EA005429B1 - Thermoplastic part and method for obtaining same - Google Patents

Thermoplastic part and method for obtaining same Download PDF

Info

Publication number
EA005429B1
EA005429B1 EA200300267A EA200300267A EA005429B1 EA 005429 B1 EA005429 B1 EA 005429B1 EA 200300267 A EA200300267 A EA 200300267A EA 200300267 A EA200300267 A EA 200300267A EA 005429 B1 EA005429 B1 EA 005429B1
Authority
EA
Eurasian Patent Office
Prior art keywords
flour
thermoplastic material
product
composition
mixture
Prior art date
Application number
EA200300267A
Other languages
Russian (ru)
Other versions
EA200300267A1 (en
Inventor
Эгон Пиаиа
Арно Жобер
Original Assignee
Рехау Са (Сосьете Аноним)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Рехау Са (Сосьете Аноним) filed Critical Рехау Са (Сосьете Аноним)
Publication of EA200300267A1 publication Critical patent/EA200300267A1/en
Publication of EA005429B1 publication Critical patent/EA005429B1/en

Abstract

The invention concerns a thermoplastic part filled with fruit stone flour and a method for obtaining such a part. Said thermoplastic part is characterised in that it comprises in its volume particles of fruit stone flour, mixed as filler with said thermoplastic material(s) before the part is manufactured.

Description

Настоящее изобретение относится к изделиям из синтетических материалов и к их получению, предметом изобретения является изделие из термопластичного материала, а также способ его получения.The present invention relates to products made from synthetic materials and to their preparation, the subject of the invention is a product made from thermoplastic material, as well as a method for producing it.

Уже многие годы наблюдается тенденция к систематической замене термопластичными материалами из-за легкости их трансформации, предоставляемых ими многочисленных возможностей конфигурации, конформации, окраски, формования и состояния поверхности, их стабильности и сохранности во времени и их устойчивости к деформации и к ударам, других материалов во многих областях промышленного и бытового оборудования, в частности к замене ими натуральных материалов, таких как дерево.For many years, there has been a tendency to systematically replace thermoplastic materials due to the ease of their transformation, the numerous possibilities of configuration, conformation, color, molding and surface conditions, their stability and safety over time and their resistance to deformation and impact, other materials many areas of industrial and consumer equipment, in particular to the replacement of natural materials, such as wood.

Однако под влиянием экологических движений и т.н. «био«-течения с недавних пор отмечается отказ от т.н. «искусственных» или «синтетических» материалов и возврат к более натуральным материалам или материалам, имеющим вид натуральных, в т. ч. из эстетических соображений.However, under the influence of ecological movements and so-called. "Bio" -the flow has recently been marked by the rejection of the so-called. "Artificial" or "synthetic" materials and a return to more natural materials or materials that have the appearance of natural, including for aesthetic reasons.

Параллельно производители изделий и деталей из пластмасс стремятся к постоянному снижению их себестоимости, в частности, за счет снижения стоимости сырья.In parallel, manufacturers of products and parts made of plastics strive to constantly reduce their cost, in particular, by reducing the cost of raw materials.

Для удовлетворения этих двух требований было предложено использовать опилки или древесную муку в качестве компонентов составов, используемых для производства таких изделий и таких деталей. Такой тип решений, в частности, описан в документах И8-А-5 951 927 и ЕР-А-0 002 766.To meet these two requirements, it was proposed to use sawdust or wood flour as components of the compositions used to manufacture such products and such parts. Such type of solutions, in particular, are described in documents I8-A-5 951 927 and EP-A-0 002 766.

Однако такое использование опилок или древесной муки, в частности, когда их вводят в относительно большом количестве или когда они имеют высокую гранулометрию, существенно снижает способность к трансформации полученной композиции и требует, например, предварительного инкапсулирования муки в пластмассовые пластинки или шарики, что, в частности, затрудняет осуществление периодического способа получения.However, such use of sawdust or wood flour, in particular, when they are introduced in relatively large quantities or when they have high particle size, significantly reduces the ability to transform the resulting composition and requires, for example, pre-encapsulation of flour into plastic plates or balls, which, in particular , complicates the implementation of a periodic method of obtaining.

Кроме того, их добавление ухудшает механические свойства полученного изделия или детали.In addition, their addition affects the mechanical properties of the resulting product or part.

Наконец, полученные таким образом изделия и детали не обладают ни достаточной стабильностью размеров в случае изменения влажности окружающей среды, ни достаточной устойчивостью к разложению под действием влаги и атмосферных факторов; они также чувствительны к отрицательным температурам, что ограничивает их использование за пределами помещений, если только они не подвергаются предварительной химической обработке с целью придать им гидрофобность и непроницаемость; однако такая обработка не придает им вид натурального продукта.Finally, the products and parts thus obtained do not have sufficient dimensional stability in the event of a change in the ambient humidity, nor are they sufficiently resistant to decomposition under the action of moisture and atmospheric factors; they are also sensitive to negative temperatures, which limits their use outside the premises, unless they are subjected to preliminary chemical treatment in order to render them hydrophobic and impermeable; however, this treatment does not give them the appearance of a natural product.

В частности, задачей настоящего изобретения является устранение вышеуказанных недостатков. Неожиданно был обнаружен удивительный факт, что использование муки из ядер плодов позволяет удовлетворить вышеназванным ожиданиям и устранить большую часть из существующих ограничений условий.In particular, the present invention is to eliminate the above disadvantages. Unexpectedly, a surprising fact was discovered that the use of flour from the kernels of fruits allows one to satisfy the above-mentioned expectations and eliminate most of the existing restrictions on conditions.

Так, предметом настоящего изобретения является изделие из термопластичного(ых) материала(ов), отличающееся тем, что оно содержит в своей массе частицы муки из ядер плодов, смешанные в качестве наполнителя с указанным или указанными пластичным(и) материалом(ами) перед получением или формованием изделия, а также способ получения такого изделия или такой детали.Thus, the subject of the present invention is a product of thermoplastic (s) material (s), characterized in that it contains in its mass particles of flour from fruit kernels, mixed as a filler with the specified or specified plastic (s) material (s) before receiving or molding the product, as well as a method for producing such a product or such a part.

Композиция термопластичного материала(ов), образующая основной материал изделия, может состоять либо из одного термопластичного материала, либо из смеси нескольких термопластичных материалов, совместимых или выполненных совместимыми между собой.The composition of thermoplastic material (s) forming the main material of the product can consist either of a single thermoplastic material or of a mixture of several thermoplastic materials compatible or made compatible with each other.

Предпочтительно, муку получают главным образом из лигнифицированных эндокарпиев или скорлупы ядер, а последние берутся преимущественно из плодов масличных деревьев, предпочтительно из оливы.Preferably, flour is obtained mainly from lignified endocarpia or kernels, and the latter are taken mainly from the fruit of oil-bearing trees, preferably from olive.

Согласно предпочтительному способу осуществления изобретения, средний размер частиц муки составляет от 50 до 500 мкм, предпочтительно от 70 до 120 мкм, а содержание муки составляет от приблизительно 5 до приблизительно 50 вес.%, предпочтительно от 10 до 20 вес.%, и наиболее предпочтительно около 15 вес.% сухой муки (влажность менее 10%, предпочтительно менее 5%) в конечной композиции термопластичного материала(ов), используемой для получения изделия.According to a preferred embodiment of the invention, the average particle size of the flour is from 50 to 500 μm, preferably from 70 to 120 μm, and the flour content is from about 5 to about 50 wt.%, Preferably from 10 to 20 wt.%, And most preferably about 15 wt.% dry flour (moisture less than 10%, preferably less than 5%) in the final composition of thermoplastic material (s) used to obtain the product.

Согласно одной из характеристик изобретения, частицы, полученные тонким дроблением, высушивают и, в случае необходимости, тонируют или подвергают красящей обработке перед их смешиванием с термопластичными материалами.According to one of the characteristics of the invention, the particles obtained by fine grinding are dried and, if necessary, tinted or subjected to coloring treatment before mixing them with thermoplastic materials.

Также предметом настоящего изобретения является способ получения детали из термопластичного материала(ов), отличающийся тем, что он состоит в получении гомогенной смеси, содержащей в качестве основного компонента композицию термопластичного материала(ов) и в качестве наполнителя муку из ядер плодов, с последующей трансформацией смеси в пластичной форме с получением изделий или деталей, таких как указанные выше.The subject of the present invention is also a method for producing a part from thermoplastic material (s), characterized in that it consists in obtaining a homogeneous mixture containing as the main component a composition of thermoplastic material (s) and as a filler flour from fruit kernels, followed by transformation of the mixture in plastic form to produce products or parts, such as those listed above.

Заявленный способ может, в частности, включать получение муки из ядер сухофруктов, композиции термопластичного материала(ов) и одной или нескольких стабилизирующих, смазывающих добавок, добавок, повышающих ударостойкость и/или облегчающих трансформацию, смешивание и нагревание этих ингредиентов до температуры, превышающей приблизительно на 5-20°С (предпочтительно, на 1015°С) обычную температуру нагревания композиции термопластичного материала(ов) для идентичной трансформации в отсутствие наполнителя в форме муки, остывание полученной смеси и, в случае необходимости, оставление ее на определенное время, причем смесь сохраняет порошковую форму на протяжении всех вышеперечисленных операций, и, наконец, трансформацию смеси в одно или несколько изThe claimed method may, in particular, include the production of flour from the kernels of dried fruit, the composition of thermoplastic material (s) and one or more stabilizing, lubricating additives, additives that increase the impact resistance and / or facilitate the transformation, mixing and heating these ingredients to a temperature above approximately 5-20 ° C (preferably, at 1015 ° C) the usual temperature of heating the composition of thermoplastic material (s) for identical transformation in the absence of filler in the form of flour, cooling obtained with esi and, if necessary, leaving it for a certain time, the mix keeps powder form for all the above operations, and finally, the transformation mixture in one or more of

-1005429 делий, таких как описанные выше, с помощью подходящей операции по трансформации, в случае необходимости, после ее гранулирования.-1005429 products, such as those described above, using a suitable transformation operation, if necessary, after granulating it.

Получение смеси термопластичный материал(ы)/мука и ее возможное нагревание могут быть осуществлены в отдельном аппарате или в аппарате, встроенном в машину, в которой осуществляется трансформация полученной смеси.The preparation of a mixture of thermoplastic material (s) / flour and its possible heating can be carried out in a separate apparatus or in an apparatus embedded in the machine in which the resulting mixture is transformed.

В зависимости от требуемых внешнего вида и декоративного эффекта может быть предусмотрена операция по тонировке или пропитке красящими веществами частиц муки из ядер плодов, предпочтительно полученной из скорлупы оливковых косточек, перед ее смешением с композицией термопластичного материала(ов) и по изменению гранулометрии частиц (в случае необходимости, путем смешивания партий муки с разной гранулометрией).Depending on the desired appearance and decorative effect, an operation can be provided for tinting or impregnating with dyes particles of flour from fruit kernels, preferably obtained from the olive seed shell, before mixing it with the composition of the thermoplastic material (s) and changing the particle size distribution (if necessary, by mixing batches of flour with different granulometry).

Кроме того, в зависимости от формы или природы полученного изделия или детали, последняя(ее) может быть получена(о) экструзией, отливкой с помощью впрыскивания или выдувания, причем термопластичный материал предпочтительно выбирают из группы, состоящей из виниловых, олефиновых и стирольных полимеров и совместимых смесей этих полимеров.In addition, depending on the shape or nature of the obtained product or part, the latter (s) can be obtained (o) by extrusion, casting by injection or blowing, and the thermoplastic material is preferably selected from the group consisting of vinyl, olefin and styrene polymers and compatible blends of these polymers.

В качестве примера, не ограничивающего объем изобретения, ниже описывается получение экструдированного изделия из твердого ПВХ, содержащего в своем составе муку из оливковых косточек.As an example, not limiting the scope of the invention, the following describes the production of extruded solid PVC products, containing in its composition flour from olive pits.

Состав смеси материалов и веществ, используемый для получения изделия, представлен в нижеследующей таблице в весовых частях.The composition of the mixture of materials and substances used to obtain the product is presented in the following table in parts by weight.

Композиция смесь/состав (тип твердый ПВХ)The composition of the mixture / composition (type solid PVC)

Предпочтительное содержание Preferred content Используемый интервал значений Used interval of values ПВХ (суспензия) PVC (suspension) 100 частей 100 pieces 100 частей 100 pieces Стабилизирующий/смазывающий агент Stabilizing / Lubricating Agent 6 частей 6 pieces 4-8 частей 4-8 parts Шок-модификатор/ технологическая добавка Shock Modifier / Technological Additive 17 частей 17 parts 5-25 частей 5-25 pieces Мука из оливковых косточек Flour from olive pits 25 частей 25 pieces 10-50 частей 10-50 parts

Твердость смеси предпочтительно составляет 80±5 8ΗΌ, а удельная масса равна 1,24 г/см3.The hardness of the mixture is preferably 80 ± 5 8ΗΌ, and the specific gravity is 1.24 g / cm 3 .

В зависимости от желаемого цвета конечного изделия осуществляют добавление соответствующего красящего вещества.Depending on the desired color of the final product, add the corresponding coloring matter.

Перед стадией экструзии необходимо осуществить перемешивание для гомогенизации и предварительной пластификации всех продуктов.Before the extrusion stage, it is necessary to mix to homogenize and pre-plasticize all products.

Для этого используют мешалку, относящуюся к типу т.н. быстрых мешалок, имеющую нагревающую камеру и охлаждающую камеру.To do this, use the mixer, related to the type of so-called. rapid agitators having a heating chamber and a cooling chamber.

Температуру нагревания в нагревающей камере доводят приблизительно до 130-160°С, предпочтительно приблизительно до 150°С. По достижении этой температуры смесь перемещают в охлаждающую камеру, где оставляют остывать перед трансформацией приблизительно до 40°С.The heating temperature in the heating chamber is adjusted to approximately 130-160 ° C, preferably to approximately 150 ° C. Upon reaching this temperature, the mixture is transferred to a cooling chamber, where it is allowed to cool before transformation to approximately 40 ° C.

В результате получают гомогенную смесь с оптимальной экстракцией влаги без потери качества смеси. Эта смесь остается в форме порошка и не требует никакой другой операции перед экструзией.The result is a homogeneous mixture with optimal extraction of moisture without loss of quality of the mixture. This mixture remains in powder form and does not require any other operation before extrusion.

Перед экструдированием полученной таким образом смеси ее оставляют предпочтительно на несколько часов, преимущественно приблизительно на три часа.Before extruding the mixture thus obtained, it is preferably left for several hours, preferably approximately three hours.

Для проведения собственно экструзии, наиболее подходящими экструдерами являются двухшнековые экструдеры; что же касается вместимости и производительности экструдера в отношении объема, его выбирают соответственно метрическому весу требуемого профиля. Что касается экструзионной линии, она не отличается по структуре и функционированию от обычных известных специалисту стандартов.For extrusion itself, twin screw extruders are the most suitable extruders; as for the capacity and performance of the extruder in terms of volume, it is chosen according to the metric weight of the desired profile. As for the extrusion line, it does not differ in structure and functioning from the usual standards known to a specialist.

Установки экструзионной линии (в частности, на уровне регулировки температур, давления и аспирации) при использовании в процессе экструзии смесей, содержащих наполнитель из муки, полученной из ядер плодов масличных культур и, в частности, оливок, сходны с установками такой линии при экструзии твердого ПВХ без наполнителя.Installations of the extrusion line (in particular, at the level of temperature, pressure and aspiration adjustment) when used in the extrusion process mixtures containing a filler made from flour obtained from the kernels of oilseeds and, in particular, olives, are similar to installations of such a line during extrusion of solid PVC without filler.

Точно так же, когда термопластичный материал состоит из другого полимера или из смеси полимеров, установки по существу эквивалентны установкам, необходимым для экструзии этих полимеров без наполнителя (например: ПВХ/Полипропилен/Акрилонитрил-Бутадиен-Стирол).Similarly, when a thermoplastic material consists of another polymer or a mixture of polymers, the installations are essentially equivalent to those required for the extrusion of these polymers without filler (for example: PVC / Polypropylene / Acrylonitrile-Butadiene-Styrene).

Благодаря изобретению становится возможным получение изделий или деталей из термопластичного материала, в частности, из ПВХ или ПП (полипропилена), отличающихся от существующих аналогичных изделий или деталей с более низкой себестоимостью (использование не представляющих ценности отходов в качестве заменяющих материалов), экологичностью и значительным возможным разнообразием с точки зрения эстетического аспекта и характера поверхности (за счет варьирования содержания и гранулометрии муки из ядер, а также цвета муки, термопластичного материала или того и другого),Thanks to the invention, it becomes possible to obtain products or parts from thermoplastic material, in particular, from PVC or PP (polypropylene), differing from existing similar products or parts with lower cost (use of non-valuable waste as replacement materials), environmental friendliness and significant possible diversity in terms of the aesthetic aspect and nature of the surface (by varying the content and granulometry of the flour from the cores, as well as the color of the flour, thermoplastic material, or both),

-2005429 при сохранении механических свойств и долговечности, которые являются практически равными таким свойствам, полученным при использовании композиций термопластичных материалов без наполнителей.-2005429 while maintaining mechanical properties and durability, which are almost equal to those obtained using thermoplastic materials without fillers.

Кроме того, включение муки указанного типа в термопластичные материалы осуществляется легко и приводит к получению гомогенной смеси, причем для этого не требуется особых дополнительных операций.In addition, the inclusion of flour of the specified type in thermoplastic materials is easy and results in a homogeneous mixture, and this does not require special additional operations.

Помимо этого, и в отличие от древесной муки, мука из ядер плодов, и, в частности, оливок, имеет очень низкую гигроскопичность и в очень малой степени подвержена ферментации, что позволяет избежать, кроме всего прочего, развития бактериальной флоры (грибов). Эти свойства являются существенными для использования полученных изделий или деталей за пределами помещений. Кроме того, частицы муки из ядер имеют твердость и плотность, существенно более высокие, чем у обычной древесной муки.In addition, and unlike wood flour, flour made from the kernels of fruits, and in particular, olives, has a very low hygroscopicity and is very slightly susceptible to fermentation, which allows to avoid, among other things, the development of bacterial flora (fungi). These properties are essential for the use of the obtained products or parts outside the premises. In addition, the particles of flour from the kernels have a hardness and density that is substantially higher than that of ordinary wood flour.

Помимо этого, основные результаты проведенных тестов показали очень высокую способность смеси «термопластичное вещество(а)/мука из ядер» к трансформации, что обеспечивает также высокую стабильность размеров полученных изделий (отсутствие изменения размеров под действием влажности).In addition, the main results of the tests showed a very high ability of the mixture “thermoplastic substance (a) / flour from cores” to transform, which also ensures high dimensional stability of the obtained products (no size change due to moisture).

Действительно, жирная природа муки из ядер, используемой в настоящем изобретении, ограничивает абсорбцию воды и увеличивает ее совместимость с термопластичными материалами, способствуя также технологическим свойствам и легкости трансформации, в частности, экструзии полученной смеси.Indeed, the oily nature of the kernel meal used in the present invention limits the absorption of water and increases its compatibility with thermoplastic materials, also contributing to the technological properties and ease of transformation, in particular, the extrusion of the resulting mixture.

Изделия и детали, полученные способом согласно изобретению, находят применение как внутри помещений (например: плинтусы, псевдолепнина, мебель,...), так и снаружи (например: детали каркаса строений, двери, окна, барьеры, порталы,...), и в качестве декоративных, функциональных и/или технических элементов.Products and parts obtained by the method according to the invention, are used both indoors (for example: baseboards, pseudo-railcaps, furniture, ...), and outside (for example: building frame parts, doors, windows, barriers, portals, ...) , and as decorative, functional and / or technical elements.

Разумеется, изобретение не ограничивается описанной формой осуществления. Остается возможность модификации, в частности, с точки зрения состава различных элементов или путем взаимозаменяемости технических эквивалентов, без выхода за пределы объема изобретения.Of course, the invention is not limited to the described form of implementation. It remains possible to modify, in particular, in terms of the composition of the various elements or by the interchangeability of technical equivalents, without going beyond the scope of the invention.

Claims (11)

ФОРМУЛА ИЗОБРЕТЕНИЯCLAIM 1. Изделие из термопластичного материала(ов), отличающееся тем, что оно содержит в своей массе частицы муки из лигнифицированного эндокарпия оливковых косточек, смешанные в качестве наполнителя с указанным(и) пластичным материалом(ами) перед получением изделия, причем термопластичный материал выбран из группы, образованной виниловыми, олефиновыми и стирольными полимерами и совместимыми смесями этих полимеров, а содержание муки составляет от 5 до приблизительно 50 вес.% сухой муки в конечной композиции термопластичного материала(ов), используемой для получения изделия.1. The product of thermoplastic material (s), characterized in that it contains in its mass particles of flour from the lignified endocarp of olive seeds mixed as a filler with the specified (s) plastic material (s) before receiving the product, and the thermoplastic material is selected from the group formed by vinyl, olefin and styrene polymers and compatible mixtures of these polymers, and the flour content is from 5 to about 50 wt.% dry flour in the final composition of the thermoplastic material (s) using used to obtain the product. 2. Изделие по п.1, отличающееся тем, что средний размер частиц составляет от 50 до 500 мкм, предпочтительно от 70 до 120 мкм.2. The product according to claim 1, characterized in that the average particle size is from 50 to 500 microns, preferably from 70 to 120 microns. 3. Изделие по п.1 или 2, отличающееся тем, что содержание муки составляет от 10 до 20% сухой муки в конечной композиции термопластичного материала(ов), используемой для получения изделия.3. The product according to claim 1 or 2, characterized in that the flour content is from 10 to 20% of dry flour in the final composition of the thermoplastic material (s) used to obtain the product. 4. Изделие по п.3, отличающееся тем, что содержание муки составляет около 15 вес.% сухой муки в конечной композиции термопластичного материала(ов), используемой для получения изделия.4. The product according to claim 3, characterized in that the flour content is about 15 wt.% Dry flour in the final composition of the thermoplastic material (s) used to obtain the product. 5. Изделие по одному из пп.1-4, отличающееся тем, что частицы муки высушиваются, и/или тонируются, или подвергаются окрашиванию перед их смешиванием с термопластичными материалами.5. The product according to one of claims 1 to 4, characterized in that the flour particles are dried and / or tinted or stained before being mixed with thermoplastic materials. 6. Изделие по одному из пп.1-5, отличающееся тем, что оно получено посредством экструзии, отливки с помощью впрыскивания или выдувания.6. The product according to one of claims 1 to 5, characterized in that it is obtained by extrusion, casting by injection or blowing. 7. Способ получения изделия из термопластичного материала(ов), отличающийся тем, что он включает получение гомогенной смеси, содержащей в качестве основного компонента композицию термопластичного материала(ов), причем термопластичный материал выбирают из группы, образованной виниловыми, олефиновыми и стирольными полимерами и совместимыми смесями этих полимеров, и, в качестве наполнителя, муку из лигнифицированных эндокарпиев оливковых косточек, причем мука содержится в количестве от 5 до приблизительно 50 вес.% сухой муки в конечной композиции термопластичного материала(ов), используемой для получения изделия, с последующей трансформацией смеси в пластичной форме с получением изделия по одному из пп.1-6.7. A method of producing an article from thermoplastic material (s), characterized in that it comprises obtaining a homogeneous mixture containing as a main component a composition of thermoplastic material (s), the thermoplastic material being selected from the group formed by vinyl, olefin and styrene polymers and compatible mixtures of these polymers, and, as a filler, flour from lignified endocarpia of olive seeds, and the flour is contained in an amount of from 5 to about 50 wt.% dry flour in the final comp ozizii thermoplastic material (s) used to obtain the product, followed by transformation of the mixture in plastic form to obtain the product according to one of claims 1 to 6. 8. Способ по п.7, отличающийся тем, что он включает подготовку муки из ядер сухофруктов, композиции термопластичного материала(ов) и одной или нескольких стабилизирующих, смазывающих добавок, добавок, повышающих ударостойкость и/или облегчающих трансформацию, смешивание и нагревание этих ингредиентов до температуры, превышающей приблизительно на 5-20°С обычную температуру нагревания композиции термопластичного материала(ов) для идентичной трансформации в отсутствие наполнителя в форме муки, остывание полученной смеси и, в случае необходимости, оставление ее на определенное время, причем смесь сохраняет порошковую форму на протяжении всех вышеперечисленных операций, и, наконец, трансформацию смеси в одно или несколько изделий по одному из пп.1-6, в случае необходимости, после ее гранулирования.8. The method according to claim 7, characterized in that it comprises preparing flour from dried fruit kernels, a composition of thermoplastic material (s) and one or more stabilizing, lubricating additives, additives that increase impact resistance and / or facilitate the transformation, mixing and heating of these ingredients to a temperature that is approximately 5-20 ° C higher than the usual heating temperature of the composition of thermoplastic material (s) for identical transformation in the absence of a filler in the form of flour, cooling of the resulting mixture and, if necessary bridge, leaving it for a certain time, the mix keeps powder form for all the above operations, and finally, transforming the mixture into one or more products according to one of claims 1-6, if necessary, after granulating. -3005429-3005429 9. Способ по п.7 или 8, отличающийся тем, что он включает тонировку или пропитку красящими веществами частиц муки из оливковых косточек перед их смешением с композицией термопластичного материала(ов).9. The method according to claim 7 or 8, characterized in that it includes tinting or impregnating with coloring substances flour particles from olive seeds before mixing them with the composition of thermoplastic material (s). 10. Способ по одному из пп.7-9, отличающийся тем, что композиция термопластичного материала(ов) состоит из поливинилхлорида, а содержание сухой муки составляет от 10 до 20 вес.% в композиции.10. The method according to one of claims 7 to 9, characterized in that the composition of the thermoplastic material (s) consists of polyvinyl chloride, and the dry flour content is from 10 to 20 wt.% In the composition. 11. Способ по одному из пп.7-9 и 10, отличающийся тем, что смесь получают с помощью мешалки, имеющей нагревающую камеру и охлаждающую камеру, причем смесь нагревают до температуры от 130 до 160°С, затем она остывает приблизительно до 40°С перед трансформацией, причем операция по трансформации заключается в экструзии, проводимой в двухшнековом экструдере.11. The method according to one of claims 7 to 9 and 10, characterized in that the mixture is obtained using a stirrer having a heating chamber and a cooling chamber, the mixture being heated to a temperature of 130 to 160 ° C, then it cools to approximately 40 ° C before transformation, the transformation operation being extrusion carried out in a twin screw extruder.
EA200300267A 2000-08-16 2001-08-14 Thermoplastic part and method for obtaining same EA005429B1 (en)