DK180274B1 - Graphene oxide-coated PBO fibers (Zylon®) fibers; method of production and use on airship hooks and lighter-than-air vessels. - Google Patents

Graphene oxide-coated PBO fibers (Zylon®) fibers; method of production and use on airship hooks and lighter-than-air vessels. Download PDF

Info

Publication number
DK180274B1
DK180274B1 DKPA201970042A DKPA201970042A DK180274B1 DK 180274 B1 DK180274 B1 DK 180274B1 DK PA201970042 A DKPA201970042 A DK PA201970042A DK PA201970042 A DKPA201970042 A DK PA201970042A DK 180274 B1 DK180274 B1 DK 180274B1
Authority
DK
Denmark
Prior art keywords
pbo
fibers
graphene oxide
glutaraldehyde
resorcinol
Prior art date
Application number
DKPA201970042A
Other languages
Danish (da)
Inventor
Vestergaard Frandsen Mikkel
Kim David
Filleter Tobin
Parambath Mundayodan Sudeep
Original Assignee
Sceye Sarl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sceye Sarl filed Critical Sceye Sarl
Priority to DKPA201970042A priority Critical patent/DK180274B1/en
Publication of DK201970042A1 publication Critical patent/DK201970042A1/en
Application granted granted Critical
Publication of DK180274B1 publication Critical patent/DK180274B1/en

Abstract

In a method for producing a PBO fiber with increased resistance against UV-caused degradation, a coating is provided on the PBO fibers, wherein the coating comprises graphene oxide cross-linked by polymerization with glutaraldehyde and resorcinol. The fibers are useful for lighter than air vehicles.

Description

DK 180274 B1 1 Graphene-oxide grafted PBO (Zylon®) fibers; method for production and applications to airship hulls and lighter than air vehicles.
FIELD OF THE INVENTION The present invention relates to graphene-oxide coating on PBO (Zylon®) fibers; a method for production of such coated fibers, PBO fibers with such coating, an airship hull with such fibers and a lighter than air vehicle with a hull containing such fibers,
BACKGROUND OF THE INVENTION Zylon® is a trade name for a synthetic polymer material which is a thermoset liquid- crystalline polyoxazole. It was invented in the 1980s and is currently manufactured and marketed by Toyobo Corporation&. The Zylon® fibers are commonly referred to as PBO fibers due to the chemical name poly (p-phenylene-2,6-benzobisoxazole). The closest prior art is disclosed by CHEN LEI et al.: "Facile method to prepare mul- tifunctional PBO fibers: Simultaneously enhanced interfacial properties and UV re- sistance" RSC ADVANCES (2013), Vol. 3(46), pages 24664-24670. This article dis- closes a poly (p-phenylene benzobisoxazole) fiber-silica-graphene oxide (PBO-SiO2- GO) hybrid fiber. The fiber is prepared by a combined surface coating/chemical graft- ing method, resulting in an improved UV resistance. The subject matter of claim 1 of present invention differs from this article in providing a different method for improv- ing UV resistance for a graphene oxide (GO) coated poly (p-phenylene-2, 6- benzobisoxazole (PBO) fiber. In the present invention, this is done by cross-linking the GO coating by use of glutaraldehyde and resorcinol. In the article by Chen et al. it is done by a combined surface coating/chemical grafting method. The technical prob- lem solved by the present invention is thus the provision of an alternative method for providing an improved UV-resistant GO-coated PBO fiber.
PBO has remarkable strength relatively to the weight it has been proposed as material for airships, for example in the article “Tear propagation of a High-performance Air- ship Envelope Material” published by Maekawa and Yoshino in Journal of Aircraft
DK 180274 B1 2 Vol. 45, No. 5, Sept-Oct. 2008. As reported in this article, the PBO was used in a lam- inate with PBO as the base fabric.
Apart from PBO’s high specific strength as compared to other commercially available high performance fibers, it also has a high resistance to creep elongation and is there- fore especially useful for fiber reinforcement in light-weight high-strength laminate material for airships.
This is discussed by Zhai and Euler in the article “Material Chal- lenges for Lighter-Than-Air Systems in High Altitude Applications” published by the American Institute of Aeronautics and Astronautics as contribution of AIAA Sth Aviation, Technology, Integration, and Operations Conference (ATIO), 26-28 Sep- tember 2005, Arlington, Virginia.
However, PBO is also known to be very susceptible to degradation by atomic oxygen and must therefore be protected when being exposed thereto when used as a material for high-altitude airships in the stratosphere.
This is discussed in the the article “Graft- ing of silane and graphene oxide onto PBO fibers: Multifunctional interphase for fi- ber/polymer matrix composites with simultaneously improved interfacial and atomic oxygen resistant properties” published by Chen et al. in Composites Science and Technology Vol. 106, 16 January 2015, pages 32-38 and found on the following In- ternet page http://www. sciencedirect.com/science/article/pii/S0266353814003832. In this article, APTMS was used for bridging between PBO fibers and a coating contain- ing GO and silane.
It reads that "PBO-APTMS-GO showed simultaneously remarka- ble enhancement in interfacial shear strength (IFSS) and AO erosion resistance.”. These authors have also filed a Chinese patent application CN103820996, disclosing hydroxyl functional processing of the PBO fibers using treatment of the PBO fibers by lithium aluminum hydride-diethyl ether.
Graphene nanoribbon coating on PBO is also disclosed in CN105908489. Another disadvantage of PBO is rapid photo-degradation, not only by UV but also by visible light.
The presence of moisture and oxygen has been found to accelerate the photo-degradation.
In Toyobo's Technical Information brochure (Revised 2005.6) called “Pro fiber ZYLONG, available on the Internet as http://www. toyobo-global.com/seihin/kc/pbo/zylon-p/bussei-p/technical.pdf
DK 180274 B1 3 it reads that light resistance was evaluated using Xenon light weather ohmmeter. The material strength decreased sharply at the initial stage of exposure and was more than in comparative studies of Aramid fibers. The experimental result showed that the re- sidual strength after 6 months exposure to daylight is about 35%, why it is concluded therein that PBO for outdoor use have to the protected by covering material. For these reasons, despite the apparent advantages in terms of high strength and low creep, other challenges go along with this fiber material when used for stratospheric airships, where the light intensity is high and the environment chemically highly reac- tive. It would be desirable to provide a way to make the PBO more resistant against photo degradation and the reactive gases in the stratosphere in order to use it for the hull of a high altitude airship. For airships, fluorinated graphene oxide has been proposed in US9598165 for increas- ing gas tightness, another aspect important for airships. Gas tightness is also of con- cern in EP2719219 concerning graphene coating of various thermoplastic fibers. However, despite giving advantages with respect to gas tightness and resistance against atomic oxygen, graphene oxide is reported in CN102173145B that it has good transparency, which does not make it a good candidate to protect PBO against light degradation. Accordingly, for UV protection of fabrics, CN105088793 proposes mix- ing zinc oxide with the oxidized graphene. CN106087396 proposes graphene oxide slurries baked onto a polysulfonamide fabric for good mechanical properties and good anti UV performance. For Aramid fibers UV resistance has been obtained by dopa- mine modification of the fiber in combination with graphene coating.
DESCRIPTION / SUMMARY OF THE INVENTION It is therefore an objective of the invention to provide an improvement in the art. Es- pecially, it is an objective to improve light resistivity of PBO fibers. More particularly, it is an objective to provide a hull material for a high altitude airship. This objective is achieved by a method and product as set forth in the following.
DK 180274 B1 4 The inventors have found that a simple coating of graphene oxide, GO, on PBO did not protect the PBO sufficiently or satisfactory against light and UV and Ozone deg- radation. Closer study revealed not only an uneven surface coating but also openings in the coating through which light could penetrate to the fiber and degrade it. Fur- thermore, it appeared that the mere coating with GO did not provide sufficient light protection. When having the above-mentioned CN102173145B in mind about good transparency despite GO coating, this is not a surprise. However, the inventors found that a pronounced cross linking of the GO with complex molecules prior or during the coating of the PBO increased protection against light and UV degradation.
Surprisingly, a method developed for 3D structures of GO appeared to be well suited for such cross linking as well as coating procedure. A method for 3D coating of GO is disclosed in the article “Covalently Interconnected Three-Dimensional Graphene Ox- ide Solids”, published by Sudeep ef al. (one of the inventors) in ACS Nano Vol. 7 No.
8, 7034-7040, 2013. The article is available on the Internet at hup //rubs acs ore/dot/ipdE/10 102 1/nn402272u, By cross-linking graphene oxide, GO, with a cluster of glutaraldehyde, GAD, and resorcinol, Res, a three dimensional structure was created on the PBO surface. The resulting coating had a proper attachment to the otherwise inert PBO surface and had an even thickness of dimensions sufficiently thick to protect the PBO against degrada- tion.
It is pointed out that the use of glutaraldehyde instead of formaldehyde has an ad- vantage of better performance. In addition, the toxicity of formaldehyde makes the substance unattractive, as typical production facilities would not accept the use of such toxic material.
It has been found that a dry environment for the coating results in better attachment and stability. It is believed that the GO has a tendency to incorporate moisture in the coating or on the fiber surface, which results in lower quality of the coating. This was a surprising finding, seeing that moisture tend to improve the GO stability. The dry production environment is also useful for the PBO material itself, as it is sensitive to
DK 180274 B1 moisture. The influence of moisture on the PBO is also a factor that needs attention not only to the production facilities but also for the coated material when being used for an airship, as the airship, as long as it is not in the stratosphere, is exposed to hu- midity in the atmosphere. For example, the humidity in the environment during the 5 coating is less than 2 grams of water vapour in 1 kg of air, for example less than 1 g/kg or even less than 0.5g/kg. It is compared to the stratosphere, in which the air typ- ically contains 0.3 g water vapour per kg of air. The above objective is achieved with methods and products as set forth in the follow- ing. A method for producing a PBO fiber with increased resistance against UV and Ozone- caused degradation, the method comprising providing a coating on the PBO fibers, the coating comprising graphene oxide cross-linked by polymerization with glutaralde- hyde and resorcinol. A method for reducing the light degradation of PBO fibers wherein a coating is ap- plied to the PBO fibers, the coating comprising graphene oxide cross-linked by polymerization with glutaraldehyde and resorcinol.
A PBO fiber coated with graphene-oxide cross-linked with glutaraldehyde and resor- cinol. A laminate material comprising a reinforcing fiber layer, the reinforcing fiber layer comprising PBO fibers coated with graphene-oxide cross-linked with glutaraldehyde and resorcinol. An airship hull comprising a fiber layer, the fiber layer comprising PBO fibers coated with graphene-oxide that is cross-linked with glutaraldehyde and resorcinol.
A lighter-than-air vehicle comprising a hull, the hull comprising a laminate material as a gas barrier and load-bearing structure, the laminate material comprising a reinforc- ing fiber layer, the reinforcing fiber layer comprising PBO fibers coated with gra- phene-oxide cross-linked with glutaraldehyde and resorcinol.
DK 180274 B1 6 Use of PBO fibers coated with graphene-oxide cross-linked with glutaraldehyde and resorcinol for reducing degradation of PBO fibers caused by exposure to light, UV or Ozone radiation or chemical reactions.
SHORT DESCRIPTION OF THE DRAWINGS The invention will be explained in more detail with reference to the drawing, where FIG. 1 illustrates Res-GAD cross linking of GO and the modification of PBO fibers; FIG. 2 illustrates the strength measurements of Zylon® single filaments for various PBO fiber coatings in dependence of the time for UV exposure; FIG. 3 illustrates the strength retention in Zylon® single filaments in percentage for various PBO fiber coatings in dependence of the time for UV exposure; FIG. 4 illustrates experimental values for the resistance force in Newton for the measured PBO Zylon® single filaments in dependence of the time for UV ex- posure; FIG. 5 illustrates experimental values of FIG. 4, where the high intensity exposure time has been translated into estimated time of UV exposure in the strato- sphere.
FIG. 6 illustrates the strength of PBO Zylon® single filaments in dependence of the time of Ozone exposure FIG. 7 illustrates the strength retention in percentage for PBO Zylon® single fila- ments in dependence of the time of Ozone exposure.
DETAILED DESCRIPTION / PREFERRED EMBODIMENT FIG. 1 illustrates a cross-linking of graphene oxide, GO, with a cluster of glutaralde- hyde, GAD, and resorcinol, Res. The cross linking creates a three dimensional struc- ture prior or during the coating process of the coating process onto the PBO fibers.
The synthesis of GO and cross-linked GO was performed similarly as described in the article “Covalently Interconnected Three-Dimensional Graphene Oxide Solids”, pub- lished by one of the inventors Sudeep et al. in ACS Nano Vol. 7 No. 8, 7034-7040, 2013, available on the Internet at http://pubs.acs.org/doi/ipdf/10.1021/nn402272u.
DK 180274 B1 7 Synthesis of GO. Graphene oxide was synthesized as follows. A 9:1 mixture of con- centrated H2SO4/H3PO4 (360:40 mL) was added to a mixture of graphite flakes (3.0 g, 1 wt equiv) and KMnO4 (18.0 g, 6 wt equiv). The reactants were then heated to 50°C and stirred for 12 h. The reaction was cooled to room temperature and poured onto ice with 30% H202 (3 mL). The material was then washed in succession with 200 mL of water, 200 mL of 30% HCI, and 200 mL of ethanol (2 times). The material remaining after this multiple-wash process was coagulated with 200 mL of ether, and the resulting suspension was filtered over a PTFE membrane with a 0.22 um pore size.
Cross linking of GO. Dry GO was dispersed in deionized water (5 mg/mL) and treat- ed with resorcinol (11 mM), and glutaraldehyde solution (22 mM). The resulting vis- cous fluid-like material and the solution were sonicated for 3 h.
For the PBO fibers used in the experiments, Zylon® multifilaments were purchased and single filaments removed therefrom for the coating. The diameter of such fila- ments was 12 um.
In first experiments, the material was coated into the PBO single filaments by dipping the filaments into the solution and then drying the filaments. For large scale produc- tion, spray coating appears as a more feasible method.
For the UV irradiation, an apparatus was used from the company Dinies, see http://shop.dinies.com/product_info.php?info=p96 uv-chamber-m1 html, namely UV chamber M1, equipped with a UVA irradiation source providing 365 nm UVA light onto en irradiation are of 195x190mm. The intensity of the 365 nm UVA radiation at the location of the fiber was 1900 W/m2.
FIG. 2 illustrates the strength measurements for various PBO coatings in dependence of the time for UV exposure.
Four states of the PBO single filaments were used for the experiments. The lowest curve of the four curves relates to pristine (uncoated) PBO fibers. The measured data
DK 180274 B1 8 were compared to similar data from the company Toyobo, and agreement was found between the data, which proves that the results are reliable. A coating with the cross-linked GO improved the UV resistance of the PBO fibers substantially. An even further improvement could be achieved by 5 and 30 times re- peated coating. The improvement by the repeated coating is not only due to a thicker coating layer but also due to covering of defects in one layer by a subsequent layer, resulting in a more homogeneous coating and, thus, a better protection.
The exposure of the coated PBO fibers was about 100 times longer before the same reduction in strength was achieved as for the pristine PBO fibers. And after 300 hours of exposure, the coated PBO fibers had a strength about twice that of the pristine fi- bers.
FIG. 3 illustrates the strength retention in percentage of the various fiber states in de- pendence of the time for UV exposure. It is observed that the strength retention was highest for the PBO single filaments coated with cross-linked GO. Multiple coatings had a more pronounced effect than single coating.
FIG. 4 illustrates the force in Newton that had to be applied until breakage. For the PBO single filaments coated with cross-linked GO the force was 2 to 3 times as high, dependent on the number of coatings.
FIG. 5 illustrates the experimental values on a time line, in which the exposure time in hours is converted into estimated exposure times as expected in the stratosphere. Largely, 10 hours of exposure with the lamp correspond to one week of exposure in the stratosphere. It is observed that the 30 layer coating retains stability after 33 weeks for the single filament such that it can withstand about one third of the force relatively to its production state and more than three times better than for pristine PBO.
FIG. 6 illustrates the strength measurements for various PBO coatings in dependence of the time for Ozone exposure. The concentration of Ozone during the exposure was 18 ppm. This study shows that the Ozone exposure has significant effect on the strength degradation of PBO single filaments. The modified single filaments coated
DK 180274 B1 9 with cross-linked GO had an enhanced shielding effect that resulted in a three times higher strength after 100 hours of ozone exposure as compared to pristine PBO single filaments.
FIG. 7 illustrates the strength retention in percentage of pristine and cross-linked GO coated single filaments when exposed to 18 ppm ozone. It illustrates that PBO single filaments that were coated with cross-linked GO had a three times higher strength retention after 100 hours exposure to ozone.
The experiments on dingle filaments were made for having a well-defined and smooth surface. However, it is believed that the results for coated PBO multifilaments, such as Zylon® multifilaments fibers, would be even better because the coating would stick better to the surface, which is less smooth. Further, a potential weakness of one of the filaments at one position could be compensated by the strength of the others at that position so that the risk for rupture of a weakened filament is lower in a bundle of filaments than for single filaments as in the experiments.

Claims (8)

DK 180274 B1 1 PATENTKRAVDK 180274 B1 1 PATENTKRAV 1. Fremgangsmåde til fremstilling af en poly (p-phenylen-2,6-benzobisoxazol) (PBO)- fiber med øget modstand mod UV-forårsaget nedbrydning, fremgangsmåden omfatter tilvejebringelse af en coating på PBO-fibrene, coatingen omfatter grafenoxid (GO) tværbundet ved polymerisation med glutaraldehyd og resorcinol.A process for producing a poly (p-phenylene-2,6-benzobisoxazole) (PBO) fiber with increased resistance to UV-induced degradation, the process comprises providing a coating on the PBO fibers, the coating comprises graphene oxide (GO) crosslinked by polymerization with glutaraldehyde and resorcinol. 2. Fremgangsmåde ifølge krav 1, hvor coatingen omfatter GO dispergeret i deioniseret vand og behandlet med resorcinol og glutaraldehyd med et mM-forhold på 1:2.The method of claim 1, wherein the coating comprises GO dispersed in deionized water and treated with resorcinol and glutaraldehyde with a mM ratio of 1: 2. 3. Fremgangsmåde ifølge krav 2, hvor coatingen omfatter GO dispergeret i deioniseret vand og behandlet med en opløsning indeholdende 11 mM resorcinol og 22 mM glu- taraldehyd.The method of claim 2, wherein the coating comprises GO dispersed in deionized water and treated with a solution containing 11 mM resorcinol and 22 mM glutaraldehyde. 4. En PBO-fiber coatet med grafenoxid tværbundet med glutaraldehyd og resorcinol.A PBO fiber coated with graphene oxide crosslinked with glutaraldehyde and resorcinol. 5. Et laminatmateriale omfattende et armerende fiberlag, det armerende fiberlag om- fattende PBO-fibre coatet med grafenoxid, der er tværbundet med glutaraldehyd og resorcinol.A laminate material comprising a reinforcing fiber layer, the reinforcing fiber layer comprising PBO fibers coated with graphene oxide crosslinked with glutaraldehyde and resorcinol. 6. Et luftskibsskrog omfattende et fiberlag, fiberlaget omfattende PBO-fibre coatet med grafenoxid, der er tværbundet med glutaraldehyd og resorcinol.An airship hull comprising a fibrous layer, the fibrous layer comprising PBO fibers coated with graphene oxide crosslinked with glutaraldehyde and resorcinol. 7. Et lettere-end-luft-fartøj omfattende et skrog, skroget omfatter et laminatmateriale som en gasbarriere og bærende konstruktion, hvor laminatmaterialet omfatter et arme- rende fiberlag, det armerende fiberlag omfattende PBO-fibre coatet med grafenoxid tværbundet med glutaraldehyd og resorcinol.A lighter-than-air vessel comprising a hull, the hull comprising a laminate material as a gas barrier and load-bearing structure, the laminate material comprising a reinforcing fiber layer, the reinforcing fiber layer comprising PBO fibers coated with graphene oxide crosslinked with glutaraldehyde and resorcinol. DK 180274 B1 2DK 180274 B1 2 8. Anvendelse af PBO-fibre coatet med grafenoxid tværbundet med glutaraldehyd og resorcinol til reduktion af nedbrydning af PBO-fibre forårsaget af udsættelse for lys, UV-stråling eller kemiske reaktioner.Use of PBO fibers coated with graphene oxide crosslinked with glutaraldehyde and resorcinol to reduce degradation of PBO fibers caused by exposure to light, UV radiation or chemical reactions.
DKPA201970042A 2019-01-21 2019-01-21 Graphene oxide-coated PBO fibers (Zylon®) fibers; method of production and use on airship hooks and lighter-than-air vessels. DK180274B1 (en)