DEJ0006119MA - - Google Patents
Info
- Publication number
- DEJ0006119MA DEJ0006119MA DEJ0006119MA DE J0006119M A DEJ0006119M A DE J0006119MA DE J0006119M A DEJ0006119M A DE J0006119MA
- Authority
- DE
- Germany
- Prior art keywords
- resin
- epoxy resin
- synthetic resin
- silicone putty
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
UNDESREPUBLIK DEUTSCHLANDUNDESREPUBLIC OF GERMANY
Tag der Anmeldung: 11. Juli 1952 Bekanntgemacht am 27. Oktober 1955Registration date: July 11, 1952. Advertised on October 27, 1955
DEUTSCHES PATENTAMTGERMAN PATENT OFFICE
Am elastischen Silikonkitt wurde eine besondere Hafteigenschaft festgestellt, die eine vorteilhafte Verwendung als lösungsmittelfreies und trockenes Haft-, Binde- und Klebemittel erlaubt (vgl. Patentanmeldung J 5081 IVa/221).A special one was made on the elastic silicone putty Adhesive property found that an advantageous use as a solvent-free and dry Adhesives, binders and adhesives allowed (see patent application J 5081 IVa / 221).
Weitere physikalische Eigenschaften dieses an sich bekannten Materials würden fortschrittliche Anwendungen z. B. als Dichtungsmittel, als Mittel zur Schwingungsdämpfung und als Überzugsharz gestatten, wenn nicht zwei Eigenschaften dem entgegenstünden: die starke Fließneigung und eine gewisse Wasserlöslichkeit.Further physical properties of this per se known material would become progressive Applications e.g. B. as a sealant, as a means of vibration damping and as a coating resin allow, if not two properties stand in the way: the strong tendency to flow and one certain water solubility.
Erfindungsgemäß können beide Mängel weitgebend beseitigt werden, ohne daß die erwünschten physikalischen Eigenschaften wie Plastizität, Elastizität, Haftvermögen, Alterungsbeständigkeit usw. verlorengehen. Das Ziel wird durch eine Beimischung von Epoxy'harzen erreicht, wobei ein Anteil von etwa 40 Gewichtsprozent Epoxyharz zu dem elastischen Silikonkitt besonders vorteilhaft ist. Die 'Mischung erfolgt bevorzugt bei einer Temperatur von ungefähr ioo°. Es erwies sich dabei als günstig, dem erwärmten und damit teigigen Epoxyharz den elastischen Silikonkitt unter stetem Kneten beizumischen.According to the invention, both deficiencies can be largely eliminated without the desired ones physical properties such as plasticity, elasticity, adhesiveness, resistance to aging etc. get lost. The goal is achieved by adding epoxy resins, with a A proportion of about 40 percent by weight of epoxy resin to the elastic silicone cement is particularly advantageous is. The 'mixing is preferably carried out at a temperature of approximately 100 °. It turned out It is beneficial to add the elastic silicone putty to the heated and therefore doughy epoxy resin to mix in constant kneading.
Das erzielte Kunstharz ist ebenfalls ein Elastoplast wie der bekannte elastische Silikonkitt. Das Material ist nicht härtbar, sofern der Epoxyharz-The synthetic resin obtained is also an elastoplast like the well-known elastic silicone putty. The material is not curable unless the epoxy resin
509 577/178509 577/178
J 6119 IVc/39bJ 6119 IVc / 39b
anteil etwa 401Vn und weniger beträgt. Es ist trotz seiner Plastizität im weiten Temperaturbereich .,(etwa ---50" bis 4 150") 'hoch elastisch und besitzt ungewöhnliche 1 lafteigenschaften auf fast allen bekannt/n Materialien. Ks erweist sich elektrisch isolierend, als sehr zäh, gasdicht, weitgehend druckfest, nicht alternd, wasserfest, unbrennbar, fast geruchlos und praktisch nicht fließend. Mit diesem Kunstharz, können somit u. a. ganz neuartige Haft-, Binde- und K lebe vorgänge bewerkstelligt werden. l)ie erzielten Verbindungen sind praktisch unveränderlich, sie sind gegen Zug und Druck belastbar, hoch elastisch, leicht herstellbar da nur ein Andruck der Teile unter Zwischenlage einer dünnen, trockenen und nicht schmutzenden I lar/.schicht genügt —--, nicht alK-rnd, dauerhaft, gut wännefest, wasserfest, gasdicht, elektrisch isolierend, geräusch-, er.schütterungs- und schwingiuigsdänipfend. Außerdem sind diese Kittverbindungen lösbar, wobei das Kunstharz erneut beliebig verwendet werden kann.share is around 40 1 Vn and less. Despite its plasticity, it is highly elastic in a wide temperature range, (about --- 50 "to 4 150") and has unusual properties on almost all known materials. Ks proves to be electrically insulating, very tough, gas-tight, largely pressure-resistant, non-aging, waterproof, non-flammable, almost odorless and practically non-flowing. With this synthetic resin, among other things, completely new adhesive, binding and gluing processes can be accomplished. l) The connections achieved are practically unchangeable, they can withstand tension and pressure, are highly elastic, easy to produce, since only pressing the parts with a thin, dry and non-soiling layer is sufficient ----, not alK- rnd, durable, well heat-resistant, waterproof, gas-tight, electrically insulating, noise, vibration and vibration dampening. In addition, these cement connections are detachable, whereby the synthetic resin can again be used as desired.
Das Ilarz kann ohne Veränderung beliebig lange an der Luft aufbewahrt werden, es ist bei leichter, sauberer und bequemer Handhabung immer sofort verwendbar. So ist es vor allem geeignet als lösungsinittelfreies und trockenes Haft-, Binde- und Klebemittel, unter anderem auch für .Schicht- und Verbundstoffe aller Art, ferner als stark haftendes, hochelastisches, wärmefestes, wasserfestes, gasdichtes und druekfestes Dichtungsmittel, als nicht alterndes, hochelastisches und stark haftendes Schwingungs-, Stoß- oder Erschütterungsdämpfungsmittel, als Ol>erzugsharz zur Konservierung, für Keucht igkeits- und Korrosionsschutz, Wundschutz, 1'llanzenschutz, zur Verpackung und zur elektrischen Isolierung sowie als Modell- und Kormkitt, l'Vnsterkitt, Auswuchtkitt und Vergußmasse. Darüber hinaus dürften sich viele weitere Anwendungen aus den besonderen Eigenschaften des eiTmdungsgeniäßeii Harzes ergeben.The Ilarz can be kept in the air for as long as you like without any changes. clean and convenient to use, always ready to use. So it is especially suitable as a Solvent-free and dry adhesive, binding and Adhesives, among other things also for .Layer and composite materials of all kinds, also as strongly adhesive, highly elastic, heat-resistant, waterproof, gas-tight and pressure-resistant sealant, as a non-aging, highly elastic and strongly adhesive Vibration, shock or shock absorbing agent, as an oil resin for preservation, For moisture and corrosion protection, wound protection, lanzer protection, for packaging and for electrical insulation as well as model and Kormkitt, l'Vnsterkitt, balancing putty and casting compound. In addition, many other uses are likely to arise from the special properties of the eiTmdungsgeniäßeii resin.
Versuche zeigten, dal! die genannten beiden Materialien wie Epoxyharz und Silikonkitt praktisch in jedem Verhältnis gut mischbar sind. Wird der Anteil des Epoxyharze* auf etwa 50 Gewichtsprozent und darüber erhöht, so verringert -sich die Plastizität und das Haftvermögen des erzielten Mischharzes. Die Wasserfestigkeit steigt. Ein solches Harz dürfte insbesondere als Lackharz geeignet sein. Bei einem Anteil voil etwa 30 Gewichtsprozent Epoxyharz zeiger!' sich wieder weitgehend die Eigenschaften des reinen Silikonkittes. Trotzdem ist auch dieses Mischharz noch ejtwas wasserfester und weniger fließend, jeder Anteil an Epoxyharz ist auch von wirtschaftlicher Bedeutung, da dieses Harz erheblich billiger als der elastische Silikonkitt ist. Die beachtlich gute Mischbarkeit der beiden Stoffe läßt die Verwendung des Epoxyharzes auch als vorteilhaftes Streckmittel für den elastischen Silikonkitt zu.Attempts showed dal! the mentioned two materials like epoxy resin and silicone putty come in handy are easily miscible in all proportions. If the proportion of epoxy resins * is about 50 percent by weight and if it is increased above this, the plasticity and the adhesiveness of the obtained material are reduced Mixed resin. The water resistance increases. Such a resin is particularly likely to be used as a paint resin be suitable. With a proportion of about 30 percent by weight Epoxy resin pointer! ' largely the properties of the pure silicone cement. Nevertheless, this mixed resin is still something more water-resistant and less flowing, any proportion of epoxy resin is also of economic importance, because this resin is considerably cheaper than the elastic silicone putty. The remarkably good one Miscibility of the two substances makes the use of the epoxy resin also advantageous Extender for the elastic silicone putty too.
Kin besonderes. Verarbeitungsverfahren des Kunstharzes gemäß der Erfindung besteht darin, daß das Harz im etwa auf 100 bis 1200 erwärmten Zustand mittels Preßluft u. dgl. auf die zu beschichtenden Teile aufgespritzt wird. Ein anderes Arbeitsverfahren besteht z. B. darin, daß das Kunstharz im erwärmten Zustand aufgewalzt wird.Kin special. Processing method of the resin according to the invention is that the resin is u in approximately 100 to 120 0 heated state by means of compressed air. Like sprayed onto the parts to be coated.. Another working method is e.g. B. is that the synthetic resin is rolled on in the heated state.
Claims (3)
USA.-Patentschriften Nr. 2389491, 2523037.Referred publications:
U.S. Patent Nos. 2389491, 2523037.
Family
ID=