DE944427C - Method to increase the coercive force of ª † -Fe O - Google Patents

Method to increase the coercive force of ª † -Fe O

Info

Publication number
DE944427C
DE944427C DEE4483A DEE0004483A DE944427C DE 944427 C DE944427 C DE 944427C DE E4483 A DEE4483 A DE E4483A DE E0004483 A DEE0004483 A DE E0004483A DE 944427 C DE944427 C DE 944427C
Authority
DE
Germany
Prior art keywords
oxide
coercive force
mercury
ferric oxide
oxalate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEE4483A
Other languages
German (de)
Inventor
William Soby
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EMI Ltd
Original Assignee
EMI Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EMI Ltd filed Critical EMI Ltd
Application granted granted Critical
Publication of DE944427C publication Critical patent/DE944427C/en
Expired legal-status Critical Current

Description

Verfahren zur Erhöhung der Koerzitivkraft von y-Fe203 Die Erfindung betrifft ein Verfahren zur Erhöhung der Koerzitivkraft von y-Fe@ 03, welches als Mittel für magnetische Schallaufzeichnung bei Bändern und Platten geeignet ist.Method of increasing the coercive force of y-Fe 2 O 3 The invention relates to a method for increasing the coercive force of y-Fe @ 03, which as Means for magnetic sound recording is suitable for tapes and discs.

Eines der magnetisierbaren Eisenoxyde ist das schwarze Ferro:-Ferri-Oxyd (Fe304). Ein bekanntes Herstellungsverfahren, für dieses Oxyd besteht darin, daß man Ferro@su.lfat mit einer Lösung von Ammoniak und Ammoniumnitrat mischt und die Mischung dann auf ungefähr 8o bis. 9o° C erwärmt. Ein anderes magnetisierbares Eisenoxyd ist das braune Ferri-Oxyd (y-Fe203). Es wird dies in bekannter Weise durch Oxydieren des schwarzen Ferro-Ferri-Oxyds in Luft dargestellt. Ein magne tisches Schallaufzeichnungsband oder -platte:, in der das schwarze oder braune Oxyd, nach dem obengenann.tenVerfahren hergestellt, als Schaillaufzeich,-nungsmittel zur Anwendung kommt, zeigt ein Abfallen der Wiedergabe mit ansteigender Frequenz des aufgezeichneten Schalls als Folge der verhältnismäßig geringen, Koerzitivkraft des Oxyds.One of the magnetizable iron oxides is the black ferro: ferric oxide (Fe304). A known manufacturing process for this oxide is that you mix Ferro@su.lfat with a solution of ammonia and ammonium nitrate and the Mix then to about 8o. Heated at 90 ° C. Another magnetizable iron oxide is the brown ferric oxide (y-Fe203). This is done in a known manner by oxidation of the black ferro-ferric oxide shown in air. A magnetic sound recording tape or plate: in which the black or brown oxide, according to the above-mentioned process produced, as a Schaillaufzeich, is used, shows a drop the playback with increasing frequency of the recorded sound as a result of the relatively low, coercive force of the oxide.

Der Zweck der Erfindung ist die Schaffung eines Verfahrens, um die, Koerzitivkraft von y-Ferri-Oxyd (y-Fe. 03), welches als Mittel für magner tische Schallaufzeichnung geeignet ist, zu erhöhen. Zu diesem Zweck wird eine Quecksilberverbindung in das y-Ferri-Oxyd eingebaut.The purpose of the invention is to create a method to Coercive force of y-ferric oxide (y-Fe. 03), which is used as a means for magnetic Sound recording is likely to increase. To this end, will a mercury compound built into the y-ferric oxide.

Die Erfindung soll im nachfolgenden durch Beschreibung eines Verfahrens gemäß der Erfindung im einzelnen beispielsweise näher erläutert werden..The invention is intended in the following by describing a method according to the invention are explained in detail, for example.

Eine ioo/oige wäßrige Lösung, die 845 g Am-' moniumaxalat enthält, wird mit einer ioo/oigen wäßrgen Lösung aus 1625 g Ferro-sulfat. und o,55 g Que'cksilberazetat gemischt, wobei die Lösungen eine Temperatur von 65' C haben. Dadurch entstehen feine Kristalle vom zusammengefälltem Eisenoxalat und Queclcsilberoxälat. Der Niederschlag wird filtriert, gewaschen und bei ungefähr 8o' C getrocknet. Er wird dann in 'einen Heiz-Ofen eingebracht, der auf ungefähr 380'°'C oder darüber, vorzugsweise auf ungefähr 40o bis 43o° C, gehalten wird, und dann wird Dampf von ungefähr 14o° C in den Ofen, hineingeilassen. Der Dampf dient als schwaches Oxydationsmittel, unter dessen Einfluß das Eisenoxalat zersetzt und in schwarzes Ferro,-Ferri-Oxyd (Fe. 04) umgewandelt wird. Die Dampfbehandlung wird über eine hinreichende Zeit hinweg fortgesetzt, um die Oxydation des gesamten Ferro-Oxyds (Fe0), das während der Umwandlung gebildet wird, sicherzustellen. Während die Ofentemperatur noch auf ungefähr 4oo bis 430' C gehalten wird, wird die Dampfzufuhr abgeschnitten und Luft von normaler Temperatur in dem. Ofen hineingelassen, um das. Ferro-Ferri-Oxyd durch Oxydation in das braune y-Ferri-Oxyd zu verwandeln. Diese Reaktion ist exotherm, und es ist wichtig, daß die Temperatur im Ofen nicht zu hoch ist und ungefähr 5od° C nicht übersteigt, da, falls diese Temperatur merklich überschritten wird, das ferromagnetische y-Fe2 03 in -das para_ magnetische a-Fe2 03 umgewandelt wird, das, zur Verwendung bei der Herstellung von magnetischem Tonaufz.eüchnungsmaterial ungeeignet ist.A 100% aqueous solution containing 845 g of ammonium saxalate is mixed with a 100% aqueous solution of 1625 g of ferrous sulfate. and 0.55 g of mercury acetate mixed, the solutions having a temperature of 65 ° C. This creates fine crystals of the collapsed iron oxalate and Queclc silver oxalate. The precipitate is filtered, washed and dried at about 8o'C. It is then placed in a heating oven maintained at about 380 ° C. or above, preferably about 40 ° to 43 ° C., and steam at about 140 ° C. is then blown into the oven. The steam serves as a weak oxidizing agent, under the influence of which the iron oxalate decomposes and is converted into black ferrous oxide (Fe. 04). The steam treatment is continued for a time sufficient to ensure the oxidation of all ferrous oxide (FeO) formed during the conversion. While the furnace temperature is still held at about 400 to 430 ° C, the steam supply is cut off and air of normal temperature in the. Let the oven in to convert the ferro-ferric oxide into the brown y-ferric oxide by oxidation. This reaction is exothermic, and it is important that the temperature in the furnace is not too high and does not exceed about 50 ° C., since if this temperature is noticeably exceeded, the ferromagnetic y-Fe2 03 in -the para_ magnetic a-Fe2 03 which is unsuitable for use in the manufacture of magnetic sound recording material.

y-Fe2 03, das aus einer Mischung von Eisen- und Quecksilberoxalaten nach der Erfindung hergestellt ist, hat eine Koerzitivkradt, die ungefähr dreimal größer ist als die der Oxyde, die nach den oben angegebenen bekannten Verfahren hergestellt sind. Ebenso ergibt der Einbau von Quecksilberoxalaten in Eisenoxälate die Herstellung von y-Ferri-Oxyd mit einer Koerzitivkraft, die ungefähr 4o °/o höher ist als die eines y-Ferri-Oxyds, das durch eine ähnliche Methode ohne Qüecksilberoxalate hergestellt ist.y-Fe2 03, which is made from a mixture of iron and mercury oxalates is made according to the invention, has a coercive wheel that about three times is greater than that of the oxides obtained by the known methods given above are made. The incorporation of mercury oxalates into iron oxalates also results the production of γ-ferric oxide with a coercive force about 40 per cent higher is as that of a y-ferric oxide, which by a similar method without mercury oxalate is made.

Ein Mitteil zur magnetischen. Aufzeichnung mit y-Ferri-Oxyd, das nach einem Verfahren gemäß der Erfindung hergestellt ist, hat, wie: festgestellt wurde, eineng verbesserter. Frequenzverlauf, insbesondere bei den. höheren Tonfrequenzen, infolge verbesserter Kberzitivkraft des Oxyds.A message about the magnetic. Recording with y-ferric oxide, which after produced by a method according to the invention has, as has been found: narrowly improved. Frequency response, especially with the. higher sound frequencies, as a result of the improved carbonic force of the oxide.

Claims (3)

PATENTANSPRÜCHE: i. Verfahren zur Erhöhung der Koerzitivkraft von als magnetisches Tanaufzeichnungsmittel verwendbarem y-Fe2 03, dadurch. gekennzeichnet, daß eine Quecksilberverbindung in. das Oxyd eingebaut wird. PATENT CLAIMS: i. Method for increasing the coercive force of y-Fe2 03 usable as a magnetic tan recording medium, thereby. marked, that a mercury compound is built into the oxide. 2. VexfäEren nach Anspruch i, dadurch gekennzeichnet, daß- das- Oxyd durch Wärmebehandlung von zusammengefälltem Eisenoxalat und Quecksilberoxalat hergestellt wird. 2. VexfäEren according to claim i, characterized in that the oxide by heat treatment of collapsed Iron oxalate and mercury oxalate is produced. 3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, dass der Niederschlag getrocknet und dann in Wasserdampf bei etwa 4oo bis 430°' C erhitzt wird, und das gebildete Ferro-Ferri-Oxyd bei einer Temperatur bis zu 5oo° C zu y-F% 03 oxydiert wird. Angezogene Druckschriften: Bulletin. de la societe franqaise des electricien.s, Bd. 9 (z949) -S. 3o8 bis,-318; American Journal of Science, Bd. 28 (i924), S. 143; »Berichte der deutscher, eheirr. Gesellschaft«, Bd. 42 (z909), S.2248 ff. (besonders. S. 2255 bis 2257); britische Patentschrift Nr. 596 875.3. The method according to claim 2, characterized in that the precipitate is dried and then steamed is heated at about 4oo to 430 ° 'C, and the ferro-ferric oxide formed at a Temperature up to 500 ° C is oxidized to y-F% 03. Referred publications: Bulletin. de la societe franqaise des electricien.s, vol. 9 (z949) -S. 3o8 to .318; American Journal of Science, 28: 143 (1924); “Reports from the German, eheirr. Society", Vol. 42 (z909), p.2248 ff. (Especially p. 2255 to 2257); British patent specification No. 596 875.
DEE4483A 1949-09-21 1950-09-08 Method to increase the coercive force of ª † -Fe O Expired DE944427C (en)