DE889588C - Process for the briquetting of hard coal using water-containing tar pitch - Google Patents

Process for the briquetting of hard coal using water-containing tar pitch

Info

Publication number
DE889588C
DE889588C DEE3983A DEE0003983A DE889588C DE 889588 C DE889588 C DE 889588C DE E3983 A DEE3983 A DE E3983A DE E0003983 A DEE0003983 A DE E0003983A DE 889588 C DE889588 C DE 889588C
Authority
DE
Germany
Prior art keywords
water
briquetting
pitch
hard coal
coal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEE3983A
Other languages
German (de)
Inventor
Johann Junker
Karl Dipl-Ing Sallmann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ESCHWEILER BERGWERKSVEREIN
Original Assignee
ESCHWEILER BERGWERKSVEREIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ESCHWEILER BERGWERKSVEREIN filed Critical ESCHWEILER BERGWERKSVEREIN
Priority to DEE3983A priority Critical patent/DE889588C/en
Application granted granted Critical
Publication of DE889588C publication Critical patent/DE889588C/en
Expired legal-status Critical Current

Description

Verfahren zur Brikettierung von Steinkohle unter Verwendung von wasserhaltigem Teerpech Es ist seit langem bekannt, feinkörnige Steinkohle unter Verwendung von Steinkohlenteerpech zu briketitieren. Die hierzu erforderliche Pechmenge schwankt ,je nach den-Verhältnissen zwischen 5 und 9% und beträgt im Mittel etwa 6,5 bis 7% v omiGewich:t der preOlfähigenK ohle-Pech-Mischunig. Blei dem, hohen Preis des Pechs. belastet ,der Aufwand für das iBin.demittel den iGesitehungspreis erheblich, etwa mit 2o %, so .daßi zahlreiche Vorschläge gemacht worden sind, das teuere Pech durch wohlfeilere Stoffe ganz oder teilweise zu ersetizen.Process for the briquetting of hard coal using hydrous Tar pitch It has long been known using fine-grained hard coal Briquetting coal tar pitch. The amount of pitch required for this varies , depending on the ratios between 5 and 9% and averages about 6.5 to 7% of the weight of the pre-oilable coal-pitch mixture. Lead to the high price of the Bad luck. burdened, the effort for the iBin.demittel the iGesitehpreis substantially, around 20%, so that numerous suggestions have been made, which is expensive bad luck to be replaced in whole or in part by cheaper materials.

Es ist bekannt, Teerpech unter Zusatz eines Öls und eines Emulgators mit größeren Mengen Wasser zu streckern. Das Wasser wurde dabei im flüssigen Pech emulgiert. Wird die Wasser-Pech-Emulsion in Ürikettierkohle eingetragen und das, Gemenge unter Umrühren im Knetwerk auf zoo° erhitzt., so verdampfen die !MTasserträpfchen unter Sprengung der sie umhüllenden, Pechschicht, wodurch eine be- sonders feine Verteilung des Bindemittels in der Kohle erreicht wird. Eine günstige Beeinflussung der Oberflächenspannungsverhältnisse durch den, ebenfalls gegenwärtigen Emulgator kann ange- nommen werden. Kleinversuche zur Brikettierung vonlSteinkohle mit einem derartigen wasserhaltigen Pech haben gezeigt., da.ß, sich tatsächlich namhafte Einsparungen an Pech erzielen lassen, worüber der -Bericht iB. 77 der Deutschen. Kohlen-1Bergbau- L:i.tung, S. 7 und 8, unterrichtet und aus- dem zu ersehen ist, daß, mit einer Peoh-Öl-1#,Vasser-IEmal- sion, deren Pech-ÖliAnteil, auf Kohle bezogen, 40/0 beträgt, die gleichen B':rilcet,tfesit.igl<eiten wie mit 60/0 fest!em,Brikettpech erreicht wurden. Die. bei der Steinkohlenbrikettierung zu beachtenden Arbeitsbedingungen beziehen sich, von der stofflichen Seite her gesehen:, :auf die Körnung der (Kohle, den Wassergehalt; des .preß.fähigen Gemisches und die Temperaturverhältnisse vor und während d-.m Preßvorgang.It is known to stretch tar pitch with the addition of an oil and an emulsifier with relatively large amounts of water. The water was emulsified in the liquid pitch. If the water-pitch emulsion is entered in Ürikettierkohle and that, mixture heated to zoo ° in the kneader while stirring., so the! MTewater droplets evaporate and explode the pitch layer that envelops them, creating a especially fine distribution of the binder in the Coal is achieved. A favorable influence the surface tension conditions through the, also present emulsifier can be be taken. Small tests for briquetting of coal with such a hydrous Bad luck have shown that they are actually well-known Allow savings in bad luck to be achieved, about what the report iB. 77 of the Germans. Coal 1 mining L: i.tung, pp. 7 and 8, instructed and from the to it can be seen that, with a Peoh-Öl-1 #, Vasser-IEmal- sion, the pitch-oil content of which, based on coal, is 40/0 is 'the same B': rilcet, tfesit.igl <eiten as with 60/0 solid! Em, briquette pitch were achieved. The. The working conditions to be observed in hard coal briquetting relate, from the material point of view, to: the grain size of the (coal, the water content; the .press.able mixture and the temperature conditions before and during the pressing process.

Für das hier zur Rede stehende Verfahren spielt die Körnung keine Rolle.The grain size does not play a role in the process under discussion here Role.

Nach den »Richtlinien für Abnahme und Überwachung von @Siteeinkohlen-,Brikettfabriken«, DIÄT 23 e8i, März 195o, Abs. 3, 436a, soll die Austrittstemperart.ur des. @B'rikettiergutes aus dem (Knetwerk beim Gebrauch voni Teerpech 88 his 98° betragen und beim Ausdampfen um nichit mehr als 5 bis io° sinken, so daß gemäß Abs. 3, 511, das Verpressen bei 85 bis go° erfolgt. Bei dieser Temperatur ist das verwendete Hartpech noch genügend. schmiegsam., um eine (Formung der Masse zuzulassen. Der Wassergehalt der Preßmasse soll 2 - bis- 4% betragen. Auch die im erwähnten ,Bierecht B, 77 beschriebcnen Versuche halten sich weitgehend an dieseArbeitsvorschriften, insbesondere an eine hohe Temperatur von ioo° im, Knetwerk, die wie oben dargelegt, verfahirensmäßig nötig ist.According to the »Guidelines for the acceptance and monitoring of @ site coal and briquette factories«, DIÄT 23 e8i, March 195o, Para. 3, 436a, should be the exit temperature only of the. @ Branded goods from the (kneading mechanism when using tar pitch 88 to 98 ° and when evaporating do not decrease by more than 5 to 10 °, so that, according to Paragraph 3, 511, the pressing at 85 to go ° takes place. At this temperature, the hard pitch used is still sufficient. supple. to allow a (shaping of the mass. The water content of the molding mass should be 2 to 4%. Also the experiments described in Bierecht B, 77 mentioned above largely adhere to these working regulations, especially high temperatures of 100 ° im, kneading mechanism, which, as explained above, is procedurally necessary.

Betriebsversuche, ein mit Wasser gestrecktes Pech zur eBrikebtierung unter den bekannten (Bedingung; n zu benutzen, verliefen jedoch nichts befriedigend, weil i. die Anfangsfestigkeit der Preßi, linge so gering ist, da;ß sie beim Austreten aus der Form zum großen Teil sofort zerfallen, und 2. die Endfestigkeit der ganz gebliebenen Preßlinge nach dem Erkalten außerordentlich schwankend isst. Beide Mängel stellt dET Bericht B 77 ebenfalls fest (S. 5, Abs. i, S. 9, Abs. i).Operational tests, a pitch diluted with water for eBrikebtierung under the known (condition; to use n, however, nothing was satisfactory, because i. the initial strength of the press is so low that it is released when it emerges disintegrate from the form for the most part immediately, and 2. the final strength of the whole the remaining pellets after cooling down extremely fluctuatingly. Both shortcomings also states dET report B 77 (p. 5, par. i, p. 9, par. i).

Es wurde gefunden, daß -die Herstellung von mit Pech#Ö1;Wasser-Emulsion gebundenen Preßlngen betrieblich unter folgenden Bedingungen möglich wird: i. müssen die großen durch die Emulsion eingetragenen und als IBrüden vorliegenden Wassermengen vor d-Im Verpressen entfernt werden, um eine Senkung .der Gesamtfeuchtigkeit auf die geforderten 2 bis 40/0 zu erzielen, 2. muß@ die Temperatur der Masse vor dem Verpressen auf weniger als- 85° gesenkte werden.It has been found that the production of pitch oil; water emulsion bound press lengths is operationally possible under the following conditions: i. have to the large amounts of water introduced by the emulsion and present as I-vapors be removed prior to pressing in order to lower the total moisture level to achieve the required 2 to 40/0, 2. must @ the temperature of the mass before the Crimping can be lowered to less than -85 °.

Die E.ntbrüdung auf 2F his 40/0 Gesamtfeuchtiigkeit ist mit den bekannten, in dien Steirnkohlenbrikettfäbriken üblichen Mitteln nicht zu erreichen. Gemäß: der Erfindung wird nun zur Durchführung der erforderlichen zusätlzlichen Entbrüdung zwischen Knetwerk und Presse eine Auflockerung ,der Preßlmasse vorgenommen, so daß(die Birüden entweichen und abgesaugt werden können.The exhaustion to 2F to 40/0 total moisture is with the well-known, not to be achieved in the conventional coal briquette factories. According to: the invention is now used to carry out the necessary additional deburring between the kneading mechanism and the press a loosening of the pressed oil is carried out so that (the Birude can escape and be sucked off.

Die Auflockerung kann z. B4 in der Weise vorgenommen werden-, daß1 in den Verteilerkopf über der Walzenpresse eine Anzahl Preßluftdüsen eingebaut werden, die Preßll.uft in, die im: Verteilerkopf befindliche Masse einblasen, und diese aufwirbeln. Durch Verwendung kalter Preßlufit kann gleich zeitig die erforderliche Abkühlung der Masse erzielt. werden.The loosening can, for. B4 are made in such a way that 1 a number of compressed air nozzles are installed in the distributor head above the roller press, the Preßll.uft in, blow in the mass located in the distributor head, and this stir up. By using cold Preßlufit can simultaneously the required Cooling of the mass achieved. will.

Folgernde Vergleichsversuche lassen die Überlegenheitun.d den Fortischritt desiVerfahrens gemäß der Erfindung erkennen. übliche Ent- zusätzliche Ent- brüdung Preß- brüdung Preß- temperatur temperatur nicht gesenkt gesenkt Wassergehalt der Masse in 0% . .. . .. . .. . . . .. 4,9 bis 6,2 3,5 Preßtemperatur in °C . . 85 6o Anfall an ganzen Preß- lingen in 0/0 . . . . . . . . 31,7 92,3- Brikettfestigkeit nach 24 Stunden in kg 51,o bis igo io6 bis 133 Pechgehalt der Preßlinge in °/0 .............. 3,5 bis 5,8 4,1 bis 5,5 The following comparative tests show the superiority and the progress of the process according to the invention. Usual Ent- additional Ent- Brüdung Press Brüdung Press temperature temperature n i t ch ese g nkt g ese nkt Water content of the mass in 0%. ... ... ... . . .. 4.9 to 6.2 3.5 Press temperature in ° C. . 85 6o Attack on whole press lingen in 0/0. . . . . . . . 31.7 92.3- Briquette strength after 24 hours in kg 51, o to igo io6 to 133 Pitch content of the pellets in ° / 0 .............. 3.5 to 5.8 4.1 to 5.5

Claims (2)

PATENTANSPRÜCHE: i. Verfahren zur Brikettierung von Steinkohlen und ähnlichen feinkörnigen Schüttgütern unter Verwendung wasserhaltiger Teer-Pech-Bindemittel, dadurch gekennzeichnet, daß zwischen Knethwerk und. Presse eine Auflockerung der Preßmasse zwecks Entfernung der großen Driidenmengen und eine Senkung der Temperatur der Prefnasse unter 8o° vorgenommen wird. PATENT CLAIMS: i. Process for the briquetting of hard coal and similar fine-grain bulk materials using water-based tar-pitch binders, characterized in that between kneading mechanism and. Press a loosening up of the Molding compound for the purpose of removing the large amounts of driids and lowering the temperature the prefwet is carried out below 80 °. 2. Verfahren nach Anspruch i, dadurch gekennzeichnet, daß, die Entbrüdung und Kühlung durch Einblasen von Luft erreicht wird.2. The method according to claim i, characterized characterized in that the evaporation and cooling achieved by blowing in air will.
DEE3983A 1951-07-04 1951-07-04 Process for the briquetting of hard coal using water-containing tar pitch Expired DE889588C (en)