DE8127708U1 - Drive or conveyor belt - Google Patents

Drive or conveyor belt

Info

Publication number
DE8127708U1
DE8127708U1 DE8127708U DE8127708DU DE8127708U1 DE 8127708 U1 DE8127708 U1 DE 8127708U1 DE 8127708 U DE8127708 U DE 8127708U DE 8127708D U DE8127708D U DE 8127708DU DE 8127708 U1 DE8127708 U1 DE 8127708U1
Authority
DE
Germany
Prior art keywords
polyester
warp
drive
thread
conveyor belt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE8127708U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Peter BTR Gummiwerke AG
Original Assignee
Peter BTR Gummiwerke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Publication date
Publication of DE8127708U1 publication Critical patent/DE8127708U1/en
Expired legal-status Critical Current

Description

6000 Frankfurt/Main |6000 Frankfurt / Main |

H 8 P 35 K/PnH 8 P 35 K / Pn

Firma
PETER-BTR
Gummiwerke AGcompany
PETER-BTR
Gummiwerke AG

6450 Hanau 86450 Hanau 8

"Antriebs- oder Fördergurt""Drive or conveyor belt"

Die Erfindung betrifft einen Antriebs- oder Fördergurt, der aus einzelnen Teillängen, z.B. durch Verbindungshaken, zusammensetzbar ist, wobei die Teillängen mindestens eineThe invention relates to a drive or conveyor belt which is made up of individual partial lengths, e.g. by connecting hooks, Can be assembled, the partial lengths at least one

.oder dal. mit Schußfäden aus 'Polyamid/und Kettfaden aus Polyester gebildete, ggf. eine mehrlagige Gewebebindung aufweisende Gewebeeinlage aufweist, welche vorzugsweise so vorbehandelt ist, daß sie bei der Gummierung im wesentlichen längsspannungsfrei behandelbar und danach ohne Nachverstreckung vulkanisierbar ist.. or dal. with weft threads made of polyamide / and warp threads made of polyester has formed, optionally a multi-layer fabric weave exhibiting fabric insert, which is preferably pretreated in this way is that it can be treated essentially free of longitudinal tension during the gumming and then without post-stretching is vulcanizable.

Ein solcher- Antriebs- oder Fördergurt ist aus der DE-AS 22 34 915 bekannt.Such a drive or conveyor belt is known from DE-AS 22 34 915.

Für die Verwendung solcher Antriebs- oder Fördergurte im Untertagebau müssen diese einem Filterselbstrettertest der Hauptsteile für das Grubenrettungswesen genügen, welcher voraussetzt, daß beim Verschwelen des Förderbandmaterials vorgegebener Größe die Menge von den DurchgangswiderstandFor the use of such drive or conveyor belts in underground construction, they have to pass a filter self-rescue test Main parts are sufficient for the mine rescue service, which requires that when the conveyor belt material melts given size the amount of the volume resistance

Ii iiit fttiIi iiit ftti

Il HM IIl HM I

ι· imι · im

-H--H-

eines Prüffilters, beeinträchtigenden Schwelprodukten ein vorgegebenes Maß nicht überschreitet. Es ist bekannt, daß bei Antriebs- oder Fördergurten der gattungsgemäßen Art insbesondere der Polyesteranteil der Verstärkungsgewebeeinlage die Tauglichkeit hinsichtlich des SchwelVerhaltens wesentlichen mitbestimmt, d.h. je höher der Polyesteranteil des Gewebes ist, um so weniger kann das Förderbandmaterial den vorgeschriebenen Filtertest bestehen. Andererseits ist für höhere Festigkeitstypen von Antriebs- oder Fördergurten eine stärkere Gewebeeinlage erforderlich. Für die hohe Festigkeit und C. Dehnungsarmut von Antriebs- oder Fördergurten sind insbesondere die in Kettrichtung verlaufenden Polyesterfäden bestimmend. Bei der durch Erhöhung der Anzahl von Kettfäden aus Polyester angestrebten Erhöhung der Festigkeit und Dehnungsarmut von Antriebs- oder Fördergurten stößt man also im Hinblick auf den bezüglich des Schwelverhaltens zu bestehenden Filterselbstrettertest sehr bald auf vorgegebene Grenzen. Die hinsichtlich des Schwelverhaltens günstigeren Polyamidfäden werden wegen ihres ungünstigen Dehnungsverhaltens im Gegensatz zur Dehnungsarmut der Polyesterfäden bei den , gattungsgemäßen Antriebs- oder Fördergurten bisher lediglich als Schußfäden eingesetzt. Ein Ersatz von Kettfäden aus Polyester durch solche aus Polyamid zur Erhöhung der Festigkeit könnte wegen dem ungünstigen Dehnungsverhalten der » Polyamidfäden zu keinem in der Dehnungsarmut brauchbaren Antriebs- oder Fördergurt höherer Festigkeit führen.a test filter, interfering carbonization products does not exceed the specified dimension. It is known that in drive or conveyor belts of the generic type in particular the polyester content of the reinforcing fabric insert, the suitability with regard to the smoldering behavior is essential co-determined, i.e. the higher the polyester content of the fabric, the less the conveyor belt material can do the prescribed Pass the filter test. On the other hand, for higher strength types of drive or conveyor belts, a stronger one Fabric insert required. For the high strength and C. Low elongation of drive or conveyor belts are in particular determining the polyester threads running in the direction of the warp. When made by increasing the number of warp threads The aim of increasing the strength and low elongation of drive or conveyor belts is polyester With regard to the existing regarding the smoldering behavior Filter self-rescuer test very soon to given limits. The more favorable polyamide threads in terms of smoldering behavior are due to their unfavorable elongation behavior in contrast to the low elongation of the polyester threads in the , generic drive or conveyor belts have so far only been used as weft threads. A substitute made from warp threads Polyester through those made of polyamide to increase the strength could be due to the unfavorable elongation behavior of the » Polyamide threads do not lead to a drive or conveyor belt of higher strength that can be used in the low elongation.

Aufgabe der vorliegenden Erfindung ist es, einen Antriebsoder Fördergurt der gattungsgemäßen Art so weiterzubilden, daß er trotz höherer Festigkeif und hoher Dehnungsarmut auch für den Einsatz im Untertagebau geeignet ist.The object of the present invention is to develop a drive or conveyor belt of the generic type so that that it is also suitable for use in underground mining despite its higher strength and low elongation.

Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß Kettfäden aus Polyester ganz oder teilweise von Polyvinylacetat oder PolyvinylalkoholAccording to the invention, this object is achieved in that the warp threads made of polyester are wholly or partly made of polyvinyl acetate or polyvinyl alcohol

umgeben sind oder den Kettfäden aus Polyester in Kettrichtung verlaufende Polyvinylacetat- oder Polyvinylalkoholfäden zugeordnet sind. Nach der Erfindung können auch die Schußfäden aus Polyvinylacetat oder Polyvinylalkohol bestehen.are surrounded or assigned to the warp threads made of polyester running in the warp direction polyvinyl acetate or polyvinyl alcohol threads are. According to the invention, the weft threads can also consist of polyvinyl acetate or polyvinyl alcohol.

Der Erfindung liegt die überraschende Erkenntnis zugrunde, daß man bei einem gattungsgemäßen Antriebs- oder Fördergurt die Anzahl der Kettfäden aus Polyester zur Erhöhung der Festigkeit bei hohe Dehnungsarmut, ohne daß die Tauglichkeit für den Einsatz im Untertagebau im Hinblick auf den zu bestehendenThe invention is based on the surprising finding that with a generic drive or conveyor belt the number of warp threads made of polyester to increase the strength with high low elongation, without the suitability for the use in underground mining with regard to the existing ones

( ) Filterselbstrettertest beeinträchtigt wird, erhöhen kann, wenn man gleichzeitig einigen oder allen der in Kettrichtung verlaufenden Polyesterfäden eine hinreichende Menge an Polyvinylacetat oder Polyvinylalkohol in unmittelbarer Nachbarschaft zuordnet, sei es dadurch, daß die Kettfäden aus Polyester ganz oder teilweise von Polyvinylacetat oder Polyvinylalkohol umgeben sind oder sei es dadurch, daß den Kettfäden aus Polyester im wesentlichen in Kettrichtung verlaufende Polyvinylacetat- oder Polyvinylalkoholfäden zugeordnet sind. Offenbar beeinflussen sich die Zersetzungen des Polyesters und des unmittelbar benachbarten Polyvinylacetat oder Polyvinylalkohol beim Schwelvorgang in solcher Weise, daß die() Filter self-rescuer test is impaired, can increase if one simultaneously some or all of the in the warp direction running polyester threads a sufficient amount of polyvinyl acetate or polyvinyl alcohol in the immediate vicinity assigns, be it that the warp threads made of polyester wholly or partly of polyvinyl acetate or polyvinyl alcohol are surrounded or by the fact that the warp threads made of polyester run essentially in the warp direction Polyvinyl acetate or polyvinyl alcohol threads are assigned. Apparently the decomposition of the polyester influence each other and the immediately adjacent polyvinyl acetate or polyvinyl alcohol during the smoldering process in such a way that the

() Menge der entstehenden atmungsfilterschädlichen Schwelprodukte verringert wird. Der Erfindungsgedanke kann demnach Anwendung finden, wo man entweder bei durch erhöhte Zahl der in Kettrichtung verlaufenden Polyesterfäden gleichwohl ein Bestehen des Filterselbstrettertests erreichen oder bei gleichbleibender Zahl von Polyesterfäden und damit gleicher Festigkeit eines dem Filterselbstrettertests bereits genügenden Gurtes die Menge der entstehenden Schwelprodukte noch weiter herabsenken will.() Amount of carbonization products that are harmful to the respiratory filter is decreased. The idea of the invention can therefore find application where either by increasing the number of the polyester threads running in the warp direction nevertheless achieve a pass of the filter self-rescuer test or at A constant number of polyester threads and thus the same strength of one that is already sufficient in the filter self-rescue test Gurtes wants to lower the amount of carbonization products produced even further.

Es hat sich gezeigt, daß man vorteilhafterweise von einigen oder allen Kettfäden aus Polyester im Bindungsrapport jeweilsIt has been shown that it is advantageous to use some or all of the polyester warp threads in the weave repeat

ItIt I I 1 IItIt I I 1 I

wenigstens einen Kettfaden aus Polyester mit wenigstens einem Polyvinylacetat- oder Polyvinylalkoholfaden zusammen verzwirnt, vorzugsweise mehrere Kettfäden aus Polyester mit jeweils einem Polyvinylacetat- oder Polyvinylalkoholfaden. Man kann aber auch von einigen oder allen Kettfäden aus Polyester im Bindungsrapport jeweils wenigstens einen Kettfaden aus Polyester mit wenigstens einem Polyvinylacetat- oder Polyvinylalkoholfaden umzwirnen, vorzugsweise jeweils mehrere Kettfäden aus Polyester mit wenigstens einem Polyvinylacetat- oder Polyvinylalkoholfaden.at least one warp thread made of polyester twisted together with at least one polyvinyl acetate or polyvinyl alcohol thread, preferably several warp threads made of polyester, each with a polyvinyl acetate or polyvinyl alcohol thread. One can but also at least one warp thread from some or all of the polyester warp threads in the weave repeat Twist around polyester with at least one polyvinyl acetate or polyvinyl alcohol thread, preferably several warp threads in each case made of polyester with at least one polyvinyl acetate or polyvinyl alcohol thread.

Durch die Anzahl der jeweils mit einem Polyvinylacetat- oderBy the number of each with a polyvinyl acetate or

Polyvinylalkoholfaden verzwirnten oder umzwirnten und/oder ; mit Polyvinylacetat oder Polyvinylalkohol beschichteten PoIy-Polyvinyl alcohol thread twisted or twisted and / or; with polyvinyl acetate or polyvinyl alcohol coated poly-

- esterkettfäden kann das Verhältnis von Polyesteranteil zu- Ester warp threads can have the ratio of polyester to

Polyvinylacetat- oder Polyvinylalkoholanteil der in Kettrichtung verlaufenden Fäden auf einen günstigsten Wert eingestellt werden.The polyvinyl acetate or polyvinyl alcohol content of the threads running in the warp direction is set to a favorable value will.

Ein Vergleich eines herkömmlichen Gurtes mit einem erfindungsgemäßen Gurt gleicher Festigkeit von 1250 N/mm Gurtbreite -' im Filterselbstrettertest ergab beispielsweise bei dem herkömm- ! / λ liehen Gurt einen Anstieg des Einatmungswiderstandes im konstanter Luftstrom von 94 l/min von mehr als 14 mbar und bei dem erfindungsgemäßen Gurt einen Anstieg des Einatmungswiderstandes im konstanten Luftstrom von 94 l/min von lediglich 2,3 mbar. Durch die erfindungsgemäße Maßnahme der Zuordnung von Polyvinylacetat oder Polyvinylalkohol zu den in Kettrichtung verlaufenden Polyesterfäden konnte also ersichtlich aus einem bezüglich des Filterselbstretrertestes untauglichen Gurt ein in dieser Hinsicht tauglicher Gurt gleicher Festigkeit geschaffen werden.A comparison of a conventional belt with one according to the invention Belt of the same strength of 1250 N / mm belt width - 'in the filter self-rescue test, for example, with the conventional ! / λ lent belt an increase in inhalation resistance in the constant Air flow of 94 l / min of more than 14 mbar and, in the case of the belt according to the invention, an increase in inhalation resistance in a constant air flow of 94 l / min of only 2.3 mbar. By the measure according to the invention of the assignment from polyvinyl acetate or polyvinyl alcohol to the polyester threads running in the direction of the warp could thus be seen from a belt which is unsuitable for the filter self-wearer test, a belt of the same strength which is suitable in this respect be created.

Die einzige Figur zeigt schematisch im Schnitt einen in Kettrich- ;' tung verlaufenden Zwirn aus Polyesterfäden und einen PoIy-The single figure shows schematically in section a chain dash; ' thread made of polyester threads and a poly-

vinylacetat- oder Polyvinylalkoholfaden (schraffiert) nach der Erfindung.vinyl acetate or polyvinyl alcohol thread (hatched) according to the invention.

■ I fill 1 (I II.■ I fill 1 (I II.

I · · ,iif CiI · ·, iif Ci

I · · I I (I f C .I · · I I (I f C.

j · · * j · · * ς ι t ς ι t * I I* I I

l< · ι ι ι ι ι l <· ι ι ι ι ι

ti III 111 [■ (Iti III 111 [■ (I

Firma
PETER-BTR
Gummiwerke AGcompany
PETER-BTR
Gummiwerke AG

6450 Hanau 86450 Hanau 8

Antriebs- oder FördergurtDrive or conveyor belt

Zusammenfassung:Summary:

Die Erfindung bezieht sich auf einen Antriebs- oder Fördergurt, der aus einzelnen Teillängen, z.B. durch Verbindungshaken, zusammensetzbar ist, wobei die Teillängen mindestens eine mit Schußfäden aus Polyamid oder dgl. und Kettfäden aus Polyester gebildete, ggf. eine mehrlagige Gewebebindung aufweisende Gewebeeinlage aufweist, welche vorzugsweise so vorbehandelt ist, daß sie bei der Gummierung im wesentlichen längsspannungsfrei behandelbar und danch ohne Nachverstreckung vulkanisierbar ist. Zur Erhöhung der Festig- r keit und Dehnungsarmut ist bei einem für den Einsatz im Untertagebau geeigneten Gurt nach der Erfindung vorgesehen, daß Kettfäden aus Polyester ganz oder teilweise von Polyvinylacetat oder Polyvinylalkohol umgeben sind oder Kettfaden aus Polyester in Kettrichtung verlaufende Polyamidfäden zugeordnet sind.The invention relates to a drive or conveyor belt which can be assembled from individual partial lengths, for example by means of connecting hooks, the partial lengths having at least one fabric insert formed with weft threads made of polyamide or the like and warp threads made of polyester, possibly with a multilayer fabric weave, which is preferably pretreated in such a way that it can be treated essentially without longitudinal tension during the gumming and can then be vulcanized without post-stretching. To increase the strength strength r resistance and low elongation is provided with a material suitable for use in underground mining belt according to the invention is that the warp threads of polyester are completely or partially surrounded by polyvinyl acetate or polyvinyl alcohol or warp thread associated with polyester in the warp direction extending polyamide threads.

Claims (5)

Pa-trerrtÄnsprüche:Pa-trerrt claims: 1. Antriebs- oder Fördergurt, der aus einzelnen Teillängen, z.B. durch Verbindungshaken, zusammensetzbar ist, wobei die Teillängen mindestens eine mit Schußfäden aus Polyamid oder dergi. und Kettfaden aus Polyester gebildete, ggf. eine mehrlagige Gewebebindung aufweisende Gewebeeinlage aufweist, welche vorzugsweise so vorbehandelt ist, daß sie bei der Gummierung im wesentlichen längsspannungsfrei behandelbar und danach ohne Nachverstreckung vulkanisierbar ist, dadurch gekennzeichnet, daß Kettfaden aus Polyester ganz oder teilweise von Polyvinylacetat oder Polyvinylalkohol umgeben sind oder Kettfäden aus Polyester in Kettrichtung verlaufende Polyamidfäden zugeordnet, sind.1. Drive or conveyor belt, which can be put together from individual partial lengths, e.g. by connecting hooks, whereby the partial lengths at least one with weft threads made of polyamide or dergi. and warp thread made of polyester, possibly has a fabric insert having a multilayer fabric weave, which is preferably pretreated in such a way that they are essentially free of longitudinal tension during the gumming treatable and then vulcanizable without post-stretching, characterized in that warp thread from Polyester are completely or partially surrounded by polyvinyl acetate or polyvinyl alcohol or warp threads made of polyester Polyamide threads running in the warp direction are assigned. 2. Antriebs- oder Fördergurt nach Anspruch 1, dadurch gekennzeichnet, daß von einigen oder allen Kettfänden aus Polyester jeweils wenigstens ein Kettfaden aus Polyester mit wenigstens einem Polyvinylacetat- oder Polyvinylalkoholfaden zusammen verzwirnt ist.2. Drive or conveyor belt according to claim 1, characterized characterized in that of some or all of the polyester warp threads at least one polyester warp thread is twisted together with at least one polyvinyl acetate or polyvinyl alcohol thread. 3. Antriebs- oder Fördergurt nach Anspruch 2, dadurch gekennzeichnet, daß von einigen oder allen Kettfaden aus Polyester jeweils mehrere Kettfaden aus Polyester mit einem Polyvinylacetat- oder Polyvinylalkoholfaden zusammen verzwirnt sind.3. Drive or conveyor belt according to claim 2, characterized in that some or all of the warp threads Polyester several warp threads made of polyester with a polyvinyl acetate or polyvinyl alcohol thread together are twisted. 4. Antriebs- oder Fördergurt nach Anspruch 1, dadurch gekennzeichnet, daß von einigen oder allen Kettfaden aus Polyester jeweils wenigstens ein Kettfaden aus Polyester von wenigstens einem Polyvinylacetat- oder Polyvinylalkoholfaden umzwirnt ist.4. drive or conveyor belt according to claim 1, characterized characterized in that of some or all of the polyester warp threads at least one polyester warp thread is twisted around by at least one polyvinyl acetate or polyvinyl alcohol thread. 5. Antriebs- oder Fördergurt nach Anspruch 4, dadurch gekennzeichnet, daß von einigen oder allen Kettfäden aus Polyester jeweils mehrere Kettfaden aus Polyester von wenigstens einem Polyvinylacetat- oder Polyvinylalkoholfaden umzwirnt sind.5. drive or conveyor belt according to claim 4, characterized in that some or all of the warp threads made of polyester several warp threads made of polyester of at least one polyvinyl acetate or polyvinyl alcohol thread are twisted.
DE8127708U 1981-09-22 Drive or conveyor belt Expired DE8127708U1 (en)