DE737312C - Iron-chrome-aluminum alloys for objects subject to magnetic stress - Google Patents

Iron-chrome-aluminum alloys for objects subject to magnetic stress

Info

Publication number
DE737312C
DE737312C DEK157433D DEK0157433D DE737312C DE 737312 C DE737312 C DE 737312C DE K157433 D DEK157433 D DE K157433D DE K0157433 D DEK0157433 D DE K0157433D DE 737312 C DE737312 C DE 737312C
Authority
DE
Germany
Prior art keywords
purpose according
alloys
iron
content
specified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEK157433D
Other languages
German (de)
Inventor
Dr Phil Hermann Fahlenbrach
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Krupp Stahl AG
Original Assignee
Krupp Stahl AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Krupp Stahl AG filed Critical Krupp Stahl AG
Priority to DEK157433D priority Critical patent/DE737312C/en
Application granted granted Critical
Publication of DE737312C publication Critical patent/DE737312C/en
Expired legal-status Critical Current

Description

Eisen-Chrom-Aluminium-Legierungen für magnetisch beanspruchte Gegenstände Es ist bekannt, Eisen-Chrom-Aluminium-Legierungen der Zusammensetzung i bis i o 0 0 Cr, i bis q.0/ö Al, Rest im wesentlichen Eisen, als Werkstoffe mit hoher Permeabilität in elektrischen Stromkreisen zu verwenden. Dabei wurden Anfangspermeabilitäten bis zu 59o und spezifische elektrische Widerstände bis zu i .Q mm2,m erreicht.Iron-chromium-aluminum alloys for objects subject to magnetic stress It is known to use iron-chromium-aluminum alloys with the composition i to i o 0 0 Cr, i to q.0 / ö Al, the remainder essentially iron, as materials with high permeability to be used in electrical circuits. The initial permeabilities were up to to 59o and specific electrical resistances up to i .Q mm2, m achieved.

Den Gegenstand der Erfindung bildet die Verwendung von Fe-Cr-Al-Legierungen mit o, 5 bis i o 0,ö Cr, über 4. bis i o % r'11, Rest Fe, gegebenenfalls mit Verunreinigungen, als Werkstoff für Gegenstände, bei denen eine hohe Permeabfität, geringe Isoerzitivkraftund geringe Wirbelstromverluste erforderlich sind.The subject of the invention is the use of Fe-Cr-Al alloys with 0.5 to i o 0, ö Cr, over 4. to i o% r'11, remainder Fe, possibly with impurities, as a material for objects in which a high permeability, low isoercive force and low eddy current losses are required.

Es hat sich n'=imlich in nicht vorherzusehender Weise gezeigt, daß man weit bessere Ergebnisse erzielt, wenn man den Aluminiumgehalt der bekannten Legierungen, der teilweise durch Silicium zu ersetzen ist, höher wählt. So erreichte'man mit einer erfindungsgemäß zu verwendenden Legierung der Zusammensetzung 7,20ö Cr, 6,oo'o Al, Rest Fe und Verunreinigungen eine Anfangspermeabilität (B"=,lx/A!,"eii;'cm) von i ioo und einen spezifischen elektrischen Widerstand von i,2 S2 mm2/m gegenüber einer Anfangsperineabilität von mir 65o und einem spezifischen elektrischen Widerstand von o ,q S. mm' in bei einer Legierung mit 70'o Cr, 3,20..'o Al.It has been shown in an unforeseeable way that far better results can be obtained if one considers the aluminum content of the known Alloys, which is to be partially replaced by silicon, choose higher. This is how one achieved with an alloy to be used according to the invention and having the composition 7.20ö Cr, 6, oo'o Al, remainder Fe and impurities an initial permeability (B "=, lx / A!," Eii; 'cm) of i ioo and a specific electrical resistance of i, 2 S2 mm2 / m an initial permeability of 65o me and an electrical resistivity of o, q S. mm 'in for an alloy with 70'o Cr, 3.20 ..' o Al.

Die erfindungsgemäß zu verwendenden Legierungen sind besonders zur Verwendung als Werkstoffe für die Hochfrequenztechnik geeignet. Wegen der guten PermeabilitÜtskonstanz in kleinen Feldern, die bei dem obigen Beispiel bis o,16 Oersted praktisch vorhanden war, sind sie aber auch bei Niederfrequenz für die Anwendungszwecke geeignet, wo diese Permeabilitätskonstanz erforderlich ist. Der Kohlenstoffgehalt der erfindrnlg#sgeni'il., zu verwendenden Legierungen soll riglich@i klein sein und vorzugsweise nicht mehr 2tls o,10 ü betragen. Zur Verbesserung der Ver arbeitbarkeit empfiehlt sich ein Mang an/u- satz bis zu 20'o. Der Chromgehalt der Le rungen kann teilweise durch l@l olybdän und oder Wolfram ersetzt werden. Vorteilhaft werden die erfindungsgemäß zu verwendenden Legierungen bei T'emp°rattir,#i: zwischen goo und i 2oo", vorzugsweise ini Schutzgas, z. B. Wasserstoff, geglüht. Nach einem älteren nicht zum Stande der Technik gehörenden Vorschlage sollen Gegen- stände, bei denen konstante und stabile fernic- abilitäten gefordert werden, aus Eisen-Chrom- Legierungen mit 5 bis 4ooo Chrom und ge- gebenenfalls bis zu 81)'o Silicium, Aluminium oder weiteren Elementen hergestellt werd@ii. Diese Legierungen, die mechanisch hart sein sollen, weisen zwar isi diesem Zustand die sog. Isopermeigenschaften (Stabilität und Permeabilitätskonstanz mindestens bis zu einer Feldstärke von mehreren Oersted ), aber kein.' hohe Permeabilität im Sinne der Erfndun- auf und sind daher für den N-crvcnclungs zweck> nach der Erfindung ungeeignet. The alloys to be used according to the invention are particularly suitable for use as materials for high-frequency technology. Because of the good permeability constancy in small fields, which was practically present in the above example up to 0.16 Oersted, they are also suitable for low frequency applications where this constancy of permeability is required. The carbon content of the inventive geni'il., Alloys to be used should only be used be small and preferably no more than 2tls o, 10 ü. To improve the Ver workability, a lack of / u- rate up to 20'o. The chromium content of the Le rungen can partly by l @ l olybdenum and or tungsten. According to the invention are advantageous to alloys used at T'emp ° rattir, # i: between goo and i 2oo ", preferably ini Protective gas, e.g. B. hydrogen, annealed. After an older not to the state Proposals belonging to technology are intended to booths where constant and stable remote abilities are required, made of iron-chromium- Alloys with 5 to 4,000 chromium and possibly up to 81) o silicon, aluminum or other elements are produced @ ii. These alloys that are mechanically hard are supposed to show this state of affairs so-called isoperm properties (stability and Permeability constancy at least up to one Field strength of several oersteds), but none. ' high permeability in the sense of the invention on and are therefore for the N-crvcnclungs purpose> unsuitable according to the invention.

Claims (1)

PATENTANSPRÜCHE:
i. Die Verwendun- von Eisen-Chrom- Aluininitim-Legierungeii, die o,5 bis tot)-, Cr, über 4 bis i o 0##@1 Al, Rest Fe mit oder
ohne. -die üblichen Verunreinigungen ent- halten, als Werkstoff fär magnetisch be- anspruchte Gegenstände, bei denen eine hohe Permeabilität, geringe lsoerzitivkr:ifte und geringe Wirbelstromverluste erforder- lich sind. z. B. als Werkst«li für die Hochfrequenztechnik. Die Vertvendung der Legicrtingen nach Anspruch i, bei denen der Altuni- nitungehalt teilweise durch Si ersetzt wird, für den Zweck nach Anspruch i. ;: Die Verwendung der in Anspi-tich i oder _ angegebenen Legiertin<;eii. bei denen der Chromgehalt tcil«-cise durch 341ulv-lxlän und oder Wolfram ersetzt ist, für den Zweck nach Anspruch r. .l. Die Verwendung der in Anspruch 1. 2 oder j angegebenen Legierungen, deren Kohlenstoffgehalt weniger als 0.11,o und deren Mangangehalt weniger als Zoo be- trägt. für den Zweck nach Anspruch r. 5. Die Verwendung der in Anspruch i bis .t angegebenen Legierungen für ma-ne- tisch beanspruchte Gegenstände, bei denen eine konstante Permeabilitiit in kleinen Feldstärken erforderlich ist. 6. Die Verwendung der in den Ansprü- chen t bis .1 angegebenen Legierungen. die einer Glühbehandlung bei Tempcnituren zwischen 90o und i2oo-, vorztigstt-eise im Schutzgas, unterzogen i@nrden@ sind. für den Zweck nach Anspruch i oder
PATENT CLAIMS:
i. The use of iron-chromium Aluininitim alloy egg, the o, 5 to dead) -, Cr, over 4 to io 0 ## @ 1 Al, the remainder Fe with or
without. -the usual impurities- hold, as a material for magnetically claimed objects for which a high permeability, low isocitive forces and low eddy current losses are required. are lich. z. B. as a workshop for the High frequency technology. The use of the Legicrtingen according to claim i, in which the old university nite content is partially replaced by Si, for the purpose according to claim i. ;: The use of the in Anspi-tich i or _ specified alloy <; eii. at which the chromium content tcil «-cise through 341 ulv-lxlän and or tungsten is replaced, for the purpose according to claim r. .l. The use of the in claim 1. 2 or j specified alloys whose Carbon content less than 0.11, o and whose manganese content is less than zoo wearing. for the purpose according to claim r. 5. The use of the in claim i to .t specified alloys for man-ne- objects subject to stress, where a constant permeability in small Field strengths is required. 6. The use of the chen t to .1 specified alloys. the an annealing treatment at temperature between 90o and i2oo, vorztigstt-eise im Protective gas, are subjected to i @ nrden @. for the purpose according to claim i or
DEK157433D 1940-04-26 1940-04-26 Iron-chrome-aluminum alloys for objects subject to magnetic stress Expired DE737312C (en)