DE73004A - Process for the production of hollow cement bodies from stamped concrete with gradually molded iron framework

Info

Publication number: DE73004A
Application number: DE1892K9574
Authority: DE
Original assignee: R. KIESERLING in Hamburg und M. MÖLLER in Altona
Filing date: 1892-03-23

Description

KAISERLICHESIMPERIAL

PATENTAMT.PATENT OFFICE.

eingeformtem Eisengerippe.molded iron framework.

In manchen Fällen ist es zweckmäfsig, zur Erhöhung der Festigkeit von Cementhohlkörpern in die letzteren Eiseneinlagen einzuformen, welche von der Cementmischung vollständig umhüllt werden. Sobald aber diese Eiseneinlagen, die aus Drahtgeflecht, Drahtgewebe oder einer Reihe fest mit einander verbundener Stücke bestehen können, gleich als ein Ganzes aufgestellt werden, was bisher ausnahmslos geschah, werden die Vorzüge, welche das stufenweise Einformen des Cementhohlkörpers besitzt, sehr beschränkt, weil das Einstampfen der Cementmischung in die Form häufig fast unausführbar ist.In some cases it is useful to increase the strength of hollow cement bodies to form in the latter iron deposits, which completely from the cement mixture be enveloped. But as soon as these iron inserts, which are made of wire mesh, wire mesh or a series of firmly connected pieces, like a whole is set up, what has hitherto happened without exception, the advantages become which has the gradual molding of the hollow cement body, very limited because the tamping the cement mix in the mold is often almost impracticable.

Um nun das Einstampfen der Cementmischung in die Form, den einzigen Weg, Hohlkörper von gröfster Festigkeit und Gleichmäfsigkeit im inneren Gefüge zu erzielen, beibehalten und doch gleichzeitig den derart erzeugten Hohlkörper mit einem Eisengerippe versehen zu können, ohne das Einstampfen zu behindern, soll das nachstehend beschriebene Verfahren dienen.In order now to pound the cement mixture into the mold, the only way To achieve hollow bodies of the greatest strength and uniformity in the internal structure, retained and yet at the same time to be able to provide the hollow body produced in this way with an iron framework without tamping it in hinder, the procedure described below is intended to serve.

Dasselbe besteht im wesentlichen darin, dafs das Eisengerippe aus einzelnen Theilen zusammengesetzt wird, die nach und nach, entsprechend dem Fortgange der eigentlichen Formarbeit, in Verbindung mit einander gebracht werden.The same essentially consists in the fact that the iron framework is composed of individual parts which gradually, according to the progress of the actual formal work, are brought into connection with one another will.

Da nun im Allgemeinen aus praktischen Gründen die das Einstampfen bewirkenden Mittel in senkrechter Richtung bewegt werden, so ist nachstehend, obwohl es ja auch denkbar ist, dafs von der Seite eingestampft wird, angenommen worden, dafs das einstampfende Werkzeug in senkrechter Richtung auf- und abwärts bewegt wird. In dem Falle ist es angängig, die senkrecht oder annähernd senkrecht stehenden Theile des Eisengerippes sofort als Ganzes aufzustellen, oder aber auch dieselben aus einzelnen über einander liegenden Stücken nach und nach, dem Fortgange der Formarbeit entsprechend, zusammenzusetzen.Since now, for practical reasons, the pulping causes in general Means are moved in the vertical direction, so is below, although it is also conceivable it has been assumed that it is pulped from the side that the pulverulent Tool is moved up and down in a vertical direction. In that case it is reasonable the vertically or nearly vertically standing parts of the iron framework immediately as To set up the whole, or the same from individual pieces lying on top of one another little by little, according to the progress of the formal work.

Dieses letztere Verfahren, welches für die Herstellung von Hohlkörpern der verschiedensten Form und Gröfse anwendbar ist, soll nunmehr an einem Beispiele erläutert werden. Im engen Anschlufs an das in der Patentschrift Nr. 73003 beschriebene Verfahren der Herstellung eines Cementrohres aus Stampfbeton soll nachstehend angenommen werden, dafs es sich wieder um die Herstellung eines Cementrohres, jedoch mit Eisengerippe, handelt.This latter process, which is used for the production of hollow bodies of the most varied Shape and size are applicable, will now be explained using an example. In the close Following the process of making a Cement pipe made of stamped concrete should be assumed below that it is again a question of the production of a cement pipe, but with iron framework.

Zur Herstellung desselben verfährt man folgendermafsen:To produce it one proceeds as follows:

Nachdem in den über der Grundplatte und zwischen dem Kern und der untersten Ringschicht des Mantels bestehenden Hohlraum eine in ihrer Stärke nach der Gröfse des herzustellenden Rohres sich · richtende Lage α der Cementmischung rings um den Kern einge- After a layer α of the cement mixture around the core, which is in accordance with the size of the pipe to be manufactured, is in the cavity above the base plate and between the core and the lowest ring layer of the jacket.

stampft ist, wird auf diese Lage ein Ring b gelegt, der entweder aus einem Stück oder auch aus mehreren mit einander verbundenen oder auch unabhängig von einander bestehenden Theilen gebildet ist. Dieser Ring b bezw. diese einzelnen von einander unabhängigen Stücke werden mit senkrechten Stützen c versehen, die mit dem einen Ende unter den Ring geschoben und umgeschlagen werden, wie das in den Fig. 2 und 3 ersichtlich ist.is stamped, a ring b is placed on this layer, which is formed either from one piece or from several parts connected to one another or also existing independently of one another. This ring b respectively. these individual, mutually independent pieces are provided with vertical supports c , one end of which is pushed under the ring and turned over, as can be seen in FIGS.

Die Verbindung der Stützen c mit dem Ring b, sowie die Form dieser Stücke ist natürlich mannigfacher Abänderungen fähig, ohne dafs darum der Zweck derselben verfehlt würde Nachdem nun diese Stützen, welche wegen ihrer im Verhältnifs zur Dicke des Rohres äufserst mäfsigen Stärke das Einstampfen des Betons in keiner Weise hindern, sämmtlich aufgebracht sind, wird der noch freie Hohlraum zwischen dem Kern und der ersten Mantelschicht bis an den Rand der letzteren fest mit der Cementmischung ausgestampft und darauf auf die Betonoberfläche bezw. die Stützen c ein Ring b^l aufgelegt, der entweder schon mit Stützen c¹ versehen ist oder jetzt erst solche durch Unterführen und Umschlagen der Enden derselben um den Ring erhält. Ehe nun die zweite Mantelschicht aufgebaut und der zwischen derselben und dem Kern bestehende Hohlraum mit der Cementmischung ausgefüllt wird, werden die aus dem eingestampften Beton herausstehenden Enden der Stützen c mit dem von denselben getragenen Ring b^l in passender Weise, am einfachsten durch Umschlagen um denselben, verbunden. Darauf wird die zweite Mantelschicht aufgebaut und der von dieser Schicht einerseits, dem Kern und der Betonoberfläche der ersten Lage andererseits begrenzte Hohlraum durch Einstampfen der Cementmischung bis an den oberen Rand der Mantelschicht ausgefüllt. Nachdem dann ein neuer Ring b² aufgelegt und mit Stützen c'² versehen ist, werden die Enden der Stützen c^l, wie das vorher bei den Stützen c und dem Ring & geschah, um den Ring b² gebogen und die dritte Mantelschicht aufgebaut.The connection of the supports c with the ring b, as well as the shape of these pieces, is of course capable of manifold changes, without their purpose being missed in no way prevent all are applied, the still free cavity between the core and the first cladding layer is firmly stamped to the edge of the latter with the cement mixture and then on the concrete surface or. the supports c a ring b ^l placed, which is either already provided with supports c ¹ or only now receives such by passing under and turning the ends of the same around the ring. Before the second layer of cladding is built up and the cavity between it and the core is filled with the cement mixture, the ends of the supports c protruding from the rammed concrete with the ring b ^l carried by them are fitted in a suitable manner, the easiest way to do this by turning it around , connected. The second coat is then built up and the cavity delimited by this layer on the one hand, the core and the concrete surface of the first layer on the other hand, is filled by pounding the cement mixture up to the upper edge of the coat layer. After a new ring b ^{2 has been} placed and provided with supports c ' ² , the ends of the supports c ^{l are} bent around the ring b ² , as was the case with the supports c and the ring &, and the third cladding layer is built up.

In dieser Weise schreitet die Bildung des Rohres sowie das Einformen des Eisengerippes vor, ohne dafs durch das letztere das Einstampfen des Betons in irgend welcher Hinsicht erschwert wäre. Ist das Rohr ein muffenloses, dann wird der letzte Ring, der keine senkrechten Stützen mehr erhält, nicht in der Höhe der oberen Kante der letzten Mantelschicht gelegt, sondern einige Centimeter tiefer und in der alten Weise mit den unter demselben liegenden Stützen verbunden. Der über dem letzten Ring liegende' freie Raum der Form wird darauf ausgestampft und so erreicht, dafs das Eisengerippe von der Cementmischung allseitig umgeben ist.In this way, the formation of the tube and the molding of the iron framework proceed before, without the latter tamping the concrete in any respect would be difficult. If the pipe is sleeveless, then the last ring, which is not a vertical one Supports more, not at the level of the upper edge of the last layer of cladding but a few centimeters deeper and in the old way with those below it lying supports connected. The 'free space of form' above the last ring is then stamped out and so reached that the iron framework is removed from the cement mixture is surrounded on all sides.

Handelt es sich dagegen um die Herstellung eines Rohres mit Muffe, dann wird in gleicher Weise verfahren, jedoch aufserdem noch in Höhe des oberen Randes jener Mantelschicht, welche etwa in der Mitte der Muffe abschliefst, eine Seitenstrebe d abgezweigt, welche eine oder auch bisweilen zwei Stützen e trägt, die mit Ringen f in Verbindung stehen. Der letzte dieser Ringe besitzt natürlich auch keine Stützen. Derselbe wird vielmehr nur von solchen getragen und steht wieder einige Centimeter unterhalb des oberen Randes der Muffe, so dafs also auch dieses Nebengerippe allseitig von dem Beton umgeben ist.If it on the other hand, the method to the production of a tube with socket, then in a similar manner but the upper edge on addition or in the amount of that cladding layer which abschliefst approximately in the middle of the sleeve, one side strut d diverted containing one or also sometimes two Supports e carries, which are in communication with rings f. The last of these rings naturally has no supports either. Rather, it is only supported by such and is again a few centimeters below the upper edge of the socket, so that this secondary framework is also surrounded on all sides by the concrete.

Von dem eben geschilderten Verfahren zwar etwas abweichend, mit demselben aber in dem oben dargelegten Princip übereinstimmend, sind die in der Zeichnung noch veranschaulichten Verfahren.A little different from the procedure just described, but with the same in that In accordance with the principle set out above, those in the drawing are still illustrated Proceedings.

In den Fig. 5, 6 und 7 ist in Seitenansicht und Grundrifs ein Eisengerippe dargestellt, dessen senkrechte Stützen g aus einem oder auch mehreren mit einander verbundenen Stücken bestehen können. Diese Stützen sind je mit einer Reihe von Aussparungen versehen, in welche ein Draht /2 zu liegen kommt, welcher spiralförmig auf die Stützen, dem Fortgange der Formarbeit entsprechend, gewickelt wird. Die in jh und yc gegebenen Ausführungsformen empfehlen sich insofern, als bei Beanspruchung des Rohres auf Zug der Draht nach beiden Richtungen hin ein Widerlager findet, was bei der durch die Fig. 5 und 7 a veranschaulichten Ausführungsform nicht der "Fall ist. Das in den Fig. 8 bis 11 dargestellte Eisengerippe bedarf hinsichtlich seiner Herstellung keiner weiteren Erläuterung.In FIGS. 5, 6 and 7, an iron framework is shown in side view and outline, the vertical supports g of which can consist of one or more interconnected pieces. These supports are each provided with a row of recesses, in which a wire / 2 comes to lie, which is wound in a spiral on the supports according to the progress of the molding work. The embodiments given in jh and yc are recommended insofar as when the tube is subjected to tension, the wire finds an abutment in both directions, which is not the case in the embodiment illustrated by FIGS. 5 and 7a 8 to 11 shown iron frame needs no further explanation with regard to its manufacture.

Das in der Patentschrift Nr. 73003 beschriebene Verfahrenund dasvorliegende gleichen sich insofern aufserordentlich, als dort Theile der Form so lange fortgelassen wurden, bis dieselben unbedingt benöthigt wurden; dasselbe geschieht hier mit den einzelnen Theilen des Eisengerippes. Die Vorzüge des Verfahrens liegen, abgesehen davon, dafs das nicht genug zu schätzende Stampfverfahren beibehalten werden kann, darin, dafs durch das Eisengerippe nicht allein die Festigkeit des Hohlgegenstandes wesentlich erhöht wird, sondern auch der Cement vor und während des Abbindens einen vorzüglichen Halt gewinnt, so dafs das Abbrechen des Mantels sowohl als des Kernes sowie das Fortschaffen des Rohres von der Grundplatte früher geschehen kann, als das bei Herstellung der Rohre nach dem in der erwähnten Patentschrift beschriebenen Verfahren der Fall ist.The method described in Patent Specification No. 73003 and the present same extraordinary insofar as parts of the form were left there until they were were absolutely necessary; the same thing happens here with the individual parts of the iron framework. The advantages of the process lie apart from the fact that the tamping process, which cannot be appreciated enough, is retained can, in that the iron framework does not only increase the strength of the hollow object is increased significantly, but also the cement before and during the setting gains excellent hold, so that both the mantle and the core break off as well as the removal of the pipe from the base plate can happen earlier than that in the manufacture of the tubes according to the method described in the patent mentioned the case is.

Claims

Patent claim:

In the process described in patent no. 73003 for the production of hollow cement bodies an iron framework formed in steps of stamped concrete, the structure of which takes place in such a way that those parts of it which lie parallel or almost parallel to the direction of movement of the ramming tool, be wholly built up or gradually completed as they criss-cross these parts Pieces of the iron framework are inserted according to the progress of the form work, for the purpose of unhindered tamping of the concrete into the form.

1 sheet of drawings.