DE697770C - Process for the production of non-thickening carbon black-containing nitrocellulose solutions - Google Patents
Process for the production of non-thickening carbon black-containing nitrocellulose solutionsInfo
- Publication number
- DE697770C DE697770C DE1937W0101352 DEW0101352D DE697770C DE 697770 C DE697770 C DE 697770C DE 1937W0101352 DE1937W0101352 DE 1937W0101352 DE W0101352 D DEW0101352 D DE W0101352D DE 697770 C DE697770 C DE 697770C
- Authority
- DE
- Germany
- Prior art keywords
- carbon black
- thickening
- production
- solutions
- containing nitrocellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur Herstellung von nicht- eindickenden gasrußhaltigen Nitrocelluloselösungen Es ist eine oft beobachtete Tatsache, daß Nitrocellulosielösungen, die hochwertigen Gasruß enthalten, nach einiger Zeit Eindickungserscheinungen zeigen, die meist reversibler Natur sind und dann als Thixotropie gedeutet werden können. Derartige Verdickungen wirken sich sehr störend für die Lackverbraucher aus, da die Lösungen eine für die Verarbeitung viel zu 'hohe Zähflüssigkeit auf"veis,en, die oft bis zu gallertiger Struktur geht.Process for the production of non-thickening carbon black-containing nitrocellulose solutions It is an often observed fact that nitrocellulose solutions are the top quality Contain carbon black, show signs of thickening after some time, which are usually more reversible Are nature and can then be interpreted as thixotropy. Such thickenings are very disruptive for the paint consumer, as the solutions are one for the Processing much too 'high viscosity on "vises, s, which are often up to gelatinous Structure goes.
Die Thixotropie von Gasruß enthaltenden Nitrocellulos,elösungen, d. h. das reversible Eindicken oder Gelieren, ist eine Erscheinung, die unabhängig von'der Verteilung des Rußes in der Lösung auftritt. Sowohl s.alche: Lösungen, die Gasruß in sehr fein disp,ersibr, Form enthalten, als auch Lösungen, in denen der - Gasruß nicht so fein verteilt ist, dicken beim Stehen ein. Ebenso ist das Eindicken eitle Erscheinung, die unabhängig von der Farbe des Lackes ist. Sowohl solche Lösungen, die mit tiefschwarzer Farbe auftrocknende Anstriche haben, als auch solche Lösungen, die Anstriche von eitlem bräunlichen Ton geben, neigen zum Eindicken.The thixotropy of carbon black containing nitrocellulose solutions, i.e. H. reversible thickening, or gelling, is a phenomenon that is independent von'der distribution of the soot in the solution occurs. Both s.alche: solutions that Carbon black in very fine disp, ersibr, form, as well as solutions in which the - Carbon black is not so finely distributed, it thickens when standing. Thickening is the same vain appearance that is independent of the color of the paint. Both such solutions, which have paints that dry out with deep black paint, as well as such solutions, give the coats of vain brownish tone, tend to thicken.
Erfindungsgemäß treten solche Verdickungserscheinungen nicht auf, wenn. man der gasruß.haltigen -Lösung von vornherein, ölsaure oder leinölsa'ure Salze zusetzt. Als besonders wirksam haben sich beispielsweisse Ammoniumoleat, Nickeloleat und Kobaltlinoleat .erwiesen. Diese Wirkung war nicht vorauszusehen, da z. B. die als Zusatz beim Anreiben von Pigmenten gelegentlich verwendete ölsäure und Leinölsäure keinen derartigen Einfluß haben: Der Zusatz von Kupferoleat zur Herstellung von gasrüßhaltigen Nitrooellulosewalämassen ist zwar aus der deutschen Patep:tschrift 641 o82 bereits bekannt. Dort han4 es sich jedoch um einen zwecks Erleichterung des Anreib;ens und feinster Verteilung des Gasrußes gemachten Zusatz, der vor Herstellung der Lacklösung, nämlich beim Verkneten bzw. Verwalten der rußhaltigen Nitrocellulosemasse, gemacht wird, während nach der Erfindung das leinölsaure Salzeine ganz andere Wirkung hat und erst der fertigen, den Gasruß bereits in der gewünschten Verteilung enthaltenden Lacklösung zugesetzt wird. Nach der erwähnten Patentschrift wird vor der Herstellung des Lackes der Gasruß mit Kupferoleät o. dgl. und mit Nitrocellulose fein vermahlen. Durch dieses Verfahren wird ein Arbeitsgang nötig, der Zeit beansprucht, durch die erforderliche Kraft Kosten verursacht und :eine zusätzliche Apparatur notwendig macht. All dieses fällt bei dem Verfahren der Erfindung fort. Schon der einfache Zusatz von ölsauren oder leinölsauren Salzen genügt, um einen nichteindickenden: Schwarzlack auf der Grundlage von Gasruß zu erhalten.According to the invention, such thickening phenomena do not occur, if. The solution containing gas soot is oleic acid or linseed oil acid from the outset Adds salts. Ammonium oleate and nickel oleate, for example, have proven to be particularly effective and cobalt linoleate. This effect could not be foreseen, as z. B. the Oleic acid occasionally used as an additive when grinding pigments and Linseed oleic acid has no such influence: The addition of copper oleate for production of nitrocellulose whalemas containing gas soot is from the German patent specification 641 o82 already known. There is one there, however, for the sake of relief of the grinding and the finest distribution of the carbon black, the addition made before manufacture the paint solution, namely when kneading or managing the carbon black-containing nitrocellulose mass, is made, while according to the invention the linoleic acid salt has a completely different effect and only the finished one already containing the carbon black in the desired distribution Lacquer solution is added. According to the patent mentioned before production of the paint, the carbon black with copper oil or the like and finely ground with nitrocellulose. This process requires an operation that takes time to complete required force causes costs and: additional equipment is necessary power. All of this is omitted in the method of the invention. Even the simple one The addition of oleic or linseed salts is sufficient to produce a non-thickening: Obtain black paint on the basis of carbon black.
Natürlich können Lacklösungen nach der Erfindung außer der Kollodiumwolle und dem Gasruß noch die üblichen Lackbestandteile, wie Weichmacher, Harze, Mattierungsimittel Pigmente, Füllstaffe, enthalten.Of course, lacquer solutions according to the invention can be used in addition to the collodion wool and the carbon black, the usual paint components such as plasticizers, resins, matting agents Pigments, fillers included.
Die Erfindung macht durchaus nicht ein Vermahlen des Gasrußes mit der Nitroeellüloseerforderlich. In einzelnen Fällen mag es zweckmäßig sein, so vorzugehen; in anderen Fällen kann die gasrußhaltige Nitrocellulose-Lösung in der üblichen Weise hergestellt werden, d. h. durch einfache Zugabe des Pigmentes zur Nitrooelluloselösung und Rühren oder Vermischten der Suspension. In allen Fällen hat @es sich gezeigt, da:ß durch die erfindungsgemäße Zugabe von ölsauren oder leinölsauren Salzen das Eindicken mit Sicherheit vermieden werden kann. Beispiel Zu ioog eines schwarzen Metallackes von folgender Zusammensetzung: KollodiumwoU;e,nie,dririwiscos 9,'oo'o Trikresylphosphat ........ 3,30;0 Amylacetat: . . . . . . . . 24, 5 01b Äthylacetat . . . . . . . . . . . . . 8, o Q/o Butanol . . . . . . . . . . . . . . . . . 8,5 0710 Tolüol ... . . . . . . . . . . . . . . 44.o % Gasruß . . . . . . . . . . . . . . . 2,7% 100,o0/0 werden 0,3 g Ammoniumoleat zugegebenen, -das zweckmäßig vorher in 3 g Butylacetat Toluol (i : i) gelöst wurde.The invention does not by any means make it necessary to grind the carbon black with the nitrous oxide. In individual cases it may be appropriate to proceed in this way; in other cases, the carbon black-containing nitrocellulose solution can be prepared in the usual way, ie by simply adding the pigment to the nitrocellulose solution and stirring or mixing the suspension. In all cases it has been shown that: thickening can be avoided with certainty by adding oleic or linoleic salts according to the invention. Example For a black metallic lacquer of the following composition: collodion woU; e, nie, dririwiscos 9, 'oo'o tricresyl phosphate ........ 3.30; 0 amyl acetate:. . . . . . . . 24, 5 01b ethyl acetate. . . . . . . . . . . . . 8, o Q / o butanol. . . . . . . . . . . . . . . . . 8.5 0710 toluene .... . . . . . . . . . . . . . 44.o% carbon black. . . . . . . . . . . . . . . 2.7% 100, o0 / 0, 0.3 g of ammonium oleate are added, advantageously beforehand in 3 g of butyl acetate Toluene (i: i) was dissolved.
Eine derartige Lacklösung zeigt auch nach längerem Lagern keine Verdickungserscheinungen, während ohne Zusatz des ölsauren Salzes nach kurzer Zeit ein starkes Eindicken auftritt.Such a lacquer solution shows no signs of thickening even after prolonged storage, while, without the addition of the oleic acid salt, a strong thickening occurs after a short time.
Claims (1)