DE639794C - Process for the production of a smooth, matt surface of rubber goods from rubber milk - Google Patents

Process for the production of a smooth, matt surface of rubber goods from rubber milk

Info

Publication number
DE639794C
DE639794C DEI46925D DEI0046925D DE639794C DE 639794 C DE639794 C DE 639794C DE I46925 D DEI46925 D DE I46925D DE I0046925 D DEI0046925 D DE I0046925D DE 639794 C DE639794 C DE 639794C
Authority
DE
Germany
Prior art keywords
rubber
smooth
milk
goods
mixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEI46925D
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
International Latex Processes Ltd
Original Assignee
International Latex Processes Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by International Latex Processes Ltd filed Critical International Latex Processes Ltd
Application granted granted Critical
Publication of DE639794C publication Critical patent/DE639794C/en
Expired legal-status Critical Current

Description

Die Erfindung betrifft ein Verfahren zur Herstellung einer glatten matten Oberfläche von Kautschukwaren, die aus Kautschukmilch oder unter Verwendung von Kautschukmilch hergestellt worden sind.The invention relates to a method for producing a smooth, matt surface of rubber goods made from or using rubber milk have been manufactured.

Gemäß der Erfindung werden die Oberflächen der genannten Kautschukwaren mit einer Mischung von Stärkepulver und einem flockigen Kautschukniederschlag, der durch Koagulation einer wäßrigen Kautschukdispersion mit einem Feststoffgehalt von höchstens io°/0 hergestellt ist, überzogen oder behandelt, wobei die erwähnte Mischung so hergestellt wird, daß zuerst die wäßrigen Dispersionen aus Kautschuk in flockige Niederschläge umgewandelt und hierauf die flockigen Niederschläge mit einem Stärkepulver vermischt werden.According to the invention, the surfaces of said rubber goods with a mixture of starch powder and a flaky rubber precipitation are, which is more than io / 0 produced by coagulation of an aqueous rubber dispersion having a solids content of °, covered or treated, whereby the said mixture is prepared so that first the aqueous dispersions of rubber are converted into flaky precipitates and then the flaky precipitates are mixed with a starch powder.

Die wäßrigen Dispersionen von Kautschuk können auch in Mischung mit Stärkepulver in den flockigen Niederschlag umgewandelt werden, bevor sie auf die fertigen oder nicht fertiggestellten Gegenstände aufgebracht werden. The aqueous dispersions of rubber can also be mixed with starch powder to be converted into the flaky precipitate before being on the finished or not finished objects are applied.

Die Art der glatten Außenfläche, die gemäß der Erfindung hergestellt wird, ist der ähnlich, die nach üblicher Praxis der Kautschukoberfläche wasserdichter Gewebe gegeben wird. Es ist üblich, diese glatte Außenfläche dadurch herzustellen, daß eine klebrige Kautschukoberfläche mit Stärkepulver behandelt und das Stärkepulver hierauf durch Behandlung mit Schwefelchlorid in Dampfform oder in Form einer Lösung auf der Oberfläche festgelegt wird.The type of smooth outer surface produced according to the invention is similar to that which, according to normal practice, is given to the rubber surface of waterproof fabric. It is common to have this smooth outer surface produced by treating a sticky rubber surface with starch powder and the starch powder thereon by treatment with sulfur chloride in vapor form or is set in the form of a solution on the surface.

Die Erfindung ermöglicht es, diese Art der glatten matten Außenfläche einfacher zu erhalten. The invention makes it possible to obtain this type of smooth, matte outer surface more easily.

Es hat sich herausgestellt? daß die Oberflächen, die nach dem Verfahren gemäß der Erfindung hergestellt sind, keine Neigung zum Anhaften haben und ein Fleekigwerden verhindern. Unter Fleckigwerden wird die Musterung verstanden, die auf einer Kautschukoberfläche entsteht, nachdem diese mit Wasser in Berührung gewesen ist.It turned out? that the surfaces which are produced by the method according to the invention, have no tendency to stick and become fleecy impede. Blotchiness is understood to mean the pattern that appears on a rubber surface arises after it has been in contact with water.

Die Kautschukstärkemischungen können beispielsweise auf eine Oberfläche von Kautschukwaren aus Kautschukmilch durch Bürsten, Aufstreichen oder Spritzen mit nachfolgendem Trocknen aufgebracht werden. Gewöhnlich ist keine weitere Behandlung erforderlich. The rubber starch mixtures can, for example, be applied to a surface of rubber goods can be applied from rubber milk by brushing, painting on or spraying with subsequent drying. No further treatment is usually required.

Die genannten Mischungen von Kautschuk und Stärke können gewünschtenfalls auch auf die Kautschukoberfläche eines getauchten Gegenstandes, beispielsweise eines Kautsehukhandschuhs, aufgebracht werden, um das Anziehen und das Abstreifen von der Hand zu erleichtern.The mentioned mixtures of rubber and starch can, if desired, also the rubber surface of a dipped object, for example a chewing glove, can be applied to facilitate hand tightening and removal.

Die Mischungen von flockigen Niederschlägen von Kautschuk und einem Stärkepulver können hinsichtlich ihrer ursprünglichen Anfeuchtungseigenschaften durch den Zusatz an.-y.· feuchtender Mittel, wie z. B. Rizinusölsetfe^. und Alkohol, verbessert werden. 1--'The mixtures of flaky precipitates of rubber and a starch powder can be modified with regard to their original wetting properties by adding an.-y. · moisturizing agents, such as B. Castor oil set ^. and alcohol, to be improved. 1--'

Es ist bekannt, daß man an Stelle des üb"?;; liehen klebenden Koagulums den Kautschuk als einen flockigen Niederschlag aus Kaut-ID schukmilcli durch Anwendung bestimmter Koagulierungsmittel und durch Einstellen der Konzentration der Kautschukmilch erhalten kann, s. z.B. »Estate Rubber«, O. deVries, S. 143, I9-2O.It is known that in place of the "? ;;" sticky coagulum lent the rubber as a flaky precipitate of Kaut-ID schukmilcli by using certain coagulants and by adjusting the Concentration of the rubber milk, see e.g. "Estate Rubber", O. deVries, P. 143, 19-20.

Die bei dem vorliegenden Verfahren verwendeten flockigen Niederschläge können nach diesem bekannten Verfahren aus Kautschukmilch in regelbarer Weise durch Anwendung verschiedener Koagulierungsmjitel ao und Koagulierungsverfahren hergestellt werden, vorausgesetzt, daß die Koagulierung in Gegenwart einer einen Feststoffgehalt von höchstens io°/0 der bedingenden Wassermenge und ohne oder bei Gegenwart gewisser Mengen alkalischer oder kolloidaler Stoffe vorgenommen wird, die, wie gefunden wurde, eine hemmende Wirkung auf die Koagulierung ausüben.The fluffy precipitates used in the present process can be prepared by this known process of rubber latex in a controllable manner ao by using various Koagulierungsmjitel and coagulation be prepared, provided that the coagulation in the presence of a solid content of not more than io ° / 0 of the conditional amount of water and with or without is carried out in the presence of certain amounts of alkaline or colloidal substances which, as has been found, have an inhibiting effect on coagulation.

Die erhaltenen flockigen Niederschläge können gewünschtenfalls vor ihrer Verwendung nitriert werden; auf diese Weise wird ein großer Teil des Wassergehalts entfernt.The flaky precipitates obtained can, if desired, be removed prior to their use be nitrated; in this way a large part of the water content is removed.

Als Beispiele geeigneter Koagulierungsmit-As examples of suitable coagulation agents

tel seien genannt unlösliche, in der wäßrigen Dispersion selbst hergestellte Metallsalze, Säuren, z. B. Essigsäure, Salze, wie z. B.tel are called insoluble in water Dispersion self-made metal salts, acids, e.g. B. acetic acid, salts, such as. B.

Zinksulfat und Magnesiumsulfat.Zinc sulfate and magnesium sulfate.

Beispiele von Stoffen mit einer hemmenden Wirkung auf die Koagulierung sind Ätzkali, Casein, Natriumaluminat, Akaziengummi und Leim. Die Menge der benutzten Stoffe beeinflußt ebenfalls den Grad der Unterteilung der körnigen Dispersion.Examples of substances with an inhibiting effect on coagulation are caustic potash, Casein, sodium aluminate, acacia gum and glue. The amount of substances used affects also the degree of subdivision of the granular dispersion.

Die Emulsionen oder Dispersionen aus Kautschuk umfassen solche aus Kautschuk, Guttapercha oder Balata, die natürlich vorkommen oder künstlich erhalten werden. Derartige künstliche wäßrige Dispersionen können solche aus koaguliertem Kautschuk, vulkanisiertem Kautschuk, synthetischem Kautschuk, Kautschukabfall oder Regenerat enthalten. The emulsions or dispersions of rubber include those of rubber, Gutta-percha, or balata, which occurs naturally or is artificially preserved. Such Artificial aqueous dispersions can be those made from coagulated rubber or vulcanized rubber Contains rubber, synthetic rubber, rubber waste or reclaimed rubber.

Gewünschtenfalls kann eine der genannten Dispersionen allein oder mit anderen vermischt benutzt werden.If desired, one of the dispersions mentioned can be used alone or mixed with others to be used.

Die genannten Dispersionen können die üblichen bekannten Füll- und Vulkanisierungsmittel enthalten und bzw. oder sich zuerst in konzentrierter Form befinden. Gewünschtenfalls kann die Mischung aus Kautschuk und dem Stärkepulver durch Mahlen einer Mischung aus den flockigen Kautschukniederschlägen und dem Stärkepulver zu einer glatten Beschaffenheit in einer geeigneten Farbenmühle hergestellt werden. ^;*Pi folgenden Beispiele zeigen, wie das gemäß der Erfindung ausgeführt kann.The dispersions mentioned can contain the customary known fillers and vulcanizing agents and / or are first in concentrated form. If desired, the mixture of rubber and the starch powder can be prepared by grinding a mixture of the flaky rubber precipitates and the starch powder a smooth texture in a suitable paint mill. ^; * Pi following examples show how that can be carried out according to the invention.

Beispiel IExample I.

Eine Mischung eines flockigen Kautschukniederschlags mit Stärke, die zum Aufbringen auf Kautschukwaren aus Kautschukmilch zur Erzeugung der gewünschten glatten matten Oberfläche geeignet ist, ist die folgende:A mixture of a flaky rubber precipitate with starch necessary to apply on rubber goods made from rubber milk to produce the desired smooth matt finish Surface is suitable is the following:

Kautschuk 60 Gewichtsteile,Rubber 60 parts by weight,

Aluminiumsilikat . 40Aluminum silicate. 40

Stärke 100Strength 100

Wasser 700Water 700

Zuerst wird ein Kautschukniederschlag vonFirst there is a rubber deposit of

Kautschuk 60 Gewichtsteilen,Rubber 60 parts by weight,

Aluminiumsilikat . 40Aluminum silicate. 40

hergestellt, indem 100 Teile einer durch Zentrifugieren auf 6o°/0 gebrachten Kautschukmilch auf eine Konzentration von 5°/„ verdünnt werden, hierauf zuerst eine 5 °/oige Lösung, die 120 Teile handelsübliches Natronwasserglas enthält, und dann eine 5°/oige Lo-. sung, die 96 Teile Aluminiumsulfat enthält, eingerührt werden. Den sich ergebenden Niederschlag läßt man auf einem Filtertuch mehrere Stunden entwässern, bis eine dicke, rahmige Konsistenz mit 15 bis i6°/0 Feststoffen erhalten wird.prepared by mixing 100 parts of a 0 accommodated rubber latex are removed by centrifugation at 6o ° / diluted to a concentration of 5 ° / ", then first a 5 ° / o solution containing 120 parts of commercial sodium water glass, and then a 5 ° / o ige lo-. solution, which contains 96 parts of aluminum sulfate, are stirred in. The precipitate resulting mixture is allowed to a filter cloth for several hours to drain until a thick, creamy consistency with 15 to i6 ° / 0 solids is obtained.

Eine abgewogene Menge dieses Rahms wird in einer Stirnläufermühle oder irgendeiner anderen geeigneten Farbenmühle mit einer Menge trockenen Stärkepulvers gemahlen, die den festen Stoffen in dem Rahm gleich ist, bis sich ein gleichförmiger Rahm ergibt. Diese Mischung kann dann mit Wasser auf irgendeine gewünschte Konsistenz verdünnt werden.A weighed amount of this cream is placed in a rotary grinder or some ground with another suitable paint mill with a quantity of dry starch powder, equal to the solids in the cream until a uniform cream results. This mixture can then with Water can be diluted to any desired consistency.

Wahlweise kann die Stärke mit einer gleichen Menge Wasser in einer Stirnläufermühle gemahlen werden, bis sich eine gleichförmige schlammartige Masse ergibt, worauf zu dieser Masse der Kautschukniederschlag unter weiterem Mahlen hinzugefügt wird, so daß schließlich ein gleichförmiger Rahm erhalten wird.Alternatively, the starch can be mixed with an equal amount of water in a rotary mill be ground until a uniform sludge-like mass results, followed by this Mass of the rubber precipitate is added with further grinding, so that finally a uniform cream is obtained will.

Diese Mischung wird auf Kautschukwaren aus Kautschukmilch aufgebracht.This mixture is applied to rubber goods made from rubber milk.

Beispiel IIExample II

Eine Mischung eines flockigen Kautschukniederschlags mit einem Stärkepulver von der gleichen Zusammensetzung wie im Beispiel I wird auf folgende Weise hergestellt:A mixture of a flaky rubber precipitate with a starch powder from the the same composition as in example I is prepared in the following way:

100 Teile Stärke werden mit 100 Teilen Wasser angerührt und zu 100 Teilen 6o°/0iger100 parts of starch are mixed with 100 parts of water and 100 parts of 6o ° / 0 sodium

durch Zentrifugieren gewonnener Kautschukmilch hinzugefügt. Diese Mischung wird so verdünnt, daß sie 5 °/0 Feststoffe enthält. Hierzu werden 120 Teile Natronwasserglas als 5 °/oige Lösung und darauf 96 Teile Aluminiumsulfat als 5 °/oige Lösung zugesetzt.added rubber milk obtained by centrifugation. This mixture is diluted so that it contains 5 ° / 0 solids. For this purpose, 120 parts of sodium silicate are than 5 ° / o solution and then 96 parts of aluminum sulfate added as a 5 ° / o solution.

Der sich ergebende Niederschlag wird wie im Beispiel I weiterbehandelt und ergibt die gleichen Überzüge auf Kautschukwaren.The resulting precipitate is treated as in Example I and gives the same coatings on rubber goods.

Claims (2)

Patentansprüche: ·--Patent claims: - i. Verfahren zur Herstellung einer glat-' ten matten Oberfläche von Kautschukwaren aus Kautschukmilch, dadurch gekennzeichnet, .daß- die Oberflächen der Kautschukwaren mit einer Mischung von 'einem aus einer wäßrigen. .Dispersion von Kautschuk in Gegenwart einer einen Feststoffgehalt von höchstens io°/o bedingenden Wassermenge gewonnenen flockigen Niederschlag und Stärkepulver überzogen werden.i. Process for producing a smooth ' th matt surface of rubber goods made from rubber milk, characterized in that .that- the surfaces of the rubber goods with a mixture of 'one from a watery one. .Dispersion of rubber in the presence of a Solids content of not more than 10% of the resulting amount of flocculent water Precipitation and starch powder are coated. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die zum Überziehen ' der Oberfläche benutzte Mischung Benetzungsmittel enthält.2. The method according to claim 1, characterized in that the covering 'The mixture used on the surface contains wetting agents.
DEI46925D 1932-05-28 1933-04-07 Process for the production of a smooth, matt surface of rubber goods from rubber milk Expired DE639794C (en)