DE618231C - Process for the production of pressed bodies - Google Patents
Process for the production of pressed bodiesInfo
- Publication number
- DE618231C DE618231C DEST50224D DEST050224D DE618231C DE 618231 C DE618231 C DE 618231C DE ST50224 D DEST50224 D DE ST50224D DE ST050224 D DEST050224 D DE ST050224D DE 618231 C DE618231 C DE 618231C
- Authority
- DE
- Germany
- Prior art keywords
- production
- organic bases
- coal
- pressed
- pressed bodies
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur Herstellung von Preßkörpern Die Erfindung betrifft ein Verfahren. zur Herstellung von Preßkörpern für Gebrauchsgegenstände, lsolierteile u. dgl. Das Verfahren ist dadurch gekennzeichnet, daß kohleartige Brennstoffe, wie Steinkohle, Braunkohle oder Torf, oder auch Lignin mit organischen Basen zweckmäßig in der Wärme vereinigt und die erhaltenen Massen heiß verpreßt werden. Wie sich gezeigt hat, gelingt es auf diese Weise, Preßkörper zu erhalten, die außerordentlich widerstandsfähig und praktisch geruchlos sind. Die Massen können in beliebige Formen gepreßt werden, und man kann so gemäß dem vorliegenden Verfahren Platten, Stäbe, Formstücke, Schalter, Griffe, Gebrauchsgegenstände verschiedenster Art oder Teile von solchen, kurz Formstücke der verschiedensten Form, Größe und Ausbildung herstellen. Auch kann man die Preßkörper mit Stücken aus anderem Material, z. B. Metallstücken beliebiger Form, vereinigen, indem man die Metallteile beim Pressen in die Formen der Preßkörper in geeigneter Weise einsetzt. Ebenso können den Preßmassen Materialien anderer Art, z. B. Füllkörper, Weichmachungsmittel, Fließmittel u. dgl., vor der Verp.ressung zugesetzt werden.Process for the production of compacts The invention relates to a Procedure. for the production of pressed bodies for everyday objects, insulated parts and the like. The method is characterized in that coal-like fuels such as Bituminous coal, brown coal or peat, or even lignin with organic bases, are useful combined in the heat and the masses obtained are hot-pressed. How yourself has shown, it is possible in this way to obtain compacts that extraordinarily are resistant and practically odorless. The masses can be in any shape be pressed, and you can so according to the present process plates, rods, Moldings, switches, handles, utensils of all kinds or parts of such, short fittings of various shapes, sizes and training. You can also use the compacts with pieces of other material, such. B. pieces of metal any shape, unite by pressing the metal parts into the molds the compact is used in a suitable manner. Materials can also be used for the molding compounds of another kind, e.g. B. fillers, plasticizers, superplasticizers and the like., Before Compression can be added.
Die gemäß der Erfindung erhaltenen Preßkörper lassen sich mechanisch durch Sägen, Bohren, Feilen und auf der Drehbank bearbeiten und sind in hohem Maße polierfähig. Sie besitzen ein außerordentlich starkes @elektrisches Isolationsvermögen, wie sich aus der Tatsache ergibt, daß sie durch Reiben mit Wolle sich elektrisch aufladen und diese Ladung lange Zeit behalten.The compacts obtained according to the invention can be mechanically by sawing, drilling, filing and machining on the lathe and are to a great extent polishable. They have an extremely strong @electrical insulation capacity, as can be seen from the fact that by rubbing with wool they become electric charge and keep this charge for a long time.
Man hat zwar schon vorgeschlagen, bei der Herstellung von Brennstoffbriketten den zu brikettierenden Brennstoffen ein niedrigsiedendes Lösungsmittel für die darin enthaltenen Bitumina, zuzusetzen, wie Rohbenzol. Von der Verwendung organischer Basen und insbesondere höher siedender ist dort aber keine Rede gewesen. Während die organischen Basen bei Anwendung des Verfahrens -gemäß vorliegender Erfindung reit Bestandteilen. der kohleartigen Brennstoffe in chemische Reaktion treten und dadurch erst die plastischen Massen zur Entstehung kommen, die dann zu Formkörpern für Gebrauchsgegenstände u. dgl. verpreßt werden können, kann von einer derartigen Wirkung bei Anwendung von lediglich lösenden Substanzen, wie Kohlenwasserstoffen, keine Rede sein. Abgesehen davon, lag jenem Vorschlag auch der Gedanke völlig fern, auf diese Weise an Stelle von Brennstoffbriketten für Gebrauchsgegenstände, Isolierteile u. dgl. aller Art geeignete Preßkörpex zu gewinnen.It has already been proposed in the manufacture of fuel briquettes a low-boiling solvent for the fuels to be briquetted bitumina contained in it, such as crude benzene. From using organic Bases and especially higher boiling points were not mentioned there. While the organic bases when using the method according to the present invention riding ingredients. the coal-like fuels enter into a chemical reaction and Only then do the plastic masses come into being, which then become molded bodies for everyday objects and the like. Can be pressed from such a Effect when using only dissolving substances, such as hydrocarbons, be out of the question. Apart from that, the suggestion was completely alien to the idea that in this way instead of fuel briquettes for everyday objects, insulating parts and the like of all kinds to gain suitable Preßkkörpersex.
Für das Verfahren gemäß der Erfindung können organische Basen aller Art Verwendung finden. In erster Linie kommen dafür natürlich solche in Betracht, die leicht zugänglich und nicht zu teuer sind, wie z. B. Anilin, Tolüidin, Naphthylamin, Pyridin, Piperidin und Chinolin. Auch können Mischungen verschiedenartiger organischer Basen zur Anwendung kommen: - -Bei Ausführung des neuen Verfahrens geht man beispielsweise folgendermaßen vor: Steinkohle, Braunkohle, insbesondere lignitische, oder Lignin werden in gepulverter Form mit der berechneten Menge organischer Basen oder mit einem überschuß; zweckmäßigerweise mit einem neutralen, Lösungsmittel, verdünnt, bei So' verrührt, verknetet oder in anderer Weise mechanisch in innige Berührung und so zur Reaktion gebracht. Das Lösungsmittel und gegebenenfalls der überschuß an Basen werden entweder durch Destillation, beispielsweise unter vermindertem Druck, oder durch Auswaschen entfernt. Das im Vakuum von den letzten Resten Feuchtigkeit befreite Produkt wird bei einer Temperatur von i 5o' und einem Druck von Zoo bis boo at oder noch höherem oder noch niedrigerem Druck gepreßt.For the method according to the invention, organic bases can all Kind of use. First and foremost, of course, those are to be considered which are easily accessible and not too expensive, such as B. Aniline, Toluidine, naphthylamine, pyridine, piperidine and quinoline. Mixtures can also be used different types of organic bases are used: - - When executing the new process, for example, one proceeds as follows: hard coal, lignite, especially lignitic, or lignin, are calculated in powdered form with the Amount of organic bases or with an excess; expediently with a neutral, Solvent, diluted, stirred, kneaded or otherwise mechanically at So ' brought into intimate contact and thus reacted. The solvent and optionally the excess of bases are either by distillation, for example under reduced pressure, or removed by washing. That in the vacuum of the last Residual moisture-free product is at a temperature of i 5o 'and a Pressure from zoo to boo at or even higher or lower pressure.
Als Füllstoffe kommen vor allen Dingen Fasermaterialien verschiedenster Art, wie Asbest, Holz, Fasern, Baumwollfasern u. dgl., in Frage, die eine Verfestigung bzw.. bessere Hitzebeständigkeit herbeizuführen vermögen. Als Weichmachungsmittel können die in der Kunstharz- und Kunstseideindustrie dafür gebräuchlichen und bekannten Stoffe Verwendung finden. Als Fließmittel kommen vor allen Dingen solche Stoffe in Frage, die ein Gleiten der Masse in der Form beim Preßvorgang begünstigen. Es sind dies vielfach die gleichen Mittel wie diejenigen, welche zur Weichmachung dienen. Außerdem kommt dafür vor allen Dingen auch Kautschuk in Frage, der sich hierfür als besonders geeignet erwiesen hat. Man kann zu diesem Zweck beispielsweise etwa 3 bis 5 % Kautschuk, am besten in gelöster oder emulgierter Form; der Ereßmasse zusetzen, auf Wunsch gleichzeitig- mit Vulkanisierungsmitteln, so daß bei dem in der Hitze stattfindenden Preßvorgang einerseits die Steigefähigkeit der Masse in der Förm erhöht, andererseits der K;autschulz.gegen Ende des Preßvorganges oder auch durcheine nachträgliche W ärmebebandlung dann vulkanisiert wird.A wide variety of fiber materials are primarily used as fillers Kind, such as asbestos, wood, fibers, cotton fibers and the like, in question, which a solidification or. to bring about better heat resistance. As a plasticizer can use the ones used and known for this in the synthetic resin and rayon industry Substances are used. Such substances are primarily used as superplasticizers in question, which favor a sliding of the mass in the form during the pressing process. It these are often the same agents as those used for softening. In addition, rubber comes into question above all, which is used for this has proven particularly suitable. For this purpose, for example, one can use 3 to 5% rubber, preferably in dissolved or emulsified form; the erectile mass add, if desired at the same time with vulcanizing agents, so that with the in the pressing process taking place on the one hand the ability of the mass to rise in the shape is raised, on the other hand the K; autschulz. towards the end of the pressing process or is then also vulcanized by a subsequent heat treatment.
Ausführungsbeispiele i. ioog gemahlene Braunkohle werden mit einer Lösung von io g Anilin. in Zoo ccm Benzol 3 Stunden bei; So' vexührt. Dann werden das Lösungsmittel und nicht in Reaktion getretene Anteile des Anilins durch Destillation im Vakuum entfernt und die verbleibende pulvrige Masse bei einer Temperatur von i 5o° und einem Druck von 3oo at verpreßt.Embodiments i. ioog ground brown coal are mixed with a Solution of 10 g of aniline. in zoo cc benzene for 3 hours; So vexed. Then will the solvent and unreacted portions of the aniline by distillation removed in vacuo and the remaining powdery mass at a temperature of i 50 ° and a pressure of 300 at.
2. ioog gemahlene lignitische Braunkohle werden mit einer Lösung von 15 g Triäthanolamin in Zoo ccm Benzol 3 Stunden bei So' verrührt. Weiterverarbeitung wie bei Beispiel i.2. ioog ground lignitic lignite are stirred with a solution of 1 5 g of triethanolamine in Zoo cc benzene for 3 hours at Sun '. Further processing as in example i.
3. ioog lignitische Braunkohle werden mit einer Lösung von 12 g Pyridn in 200 ccm Benzol 3 Stunden bei So' verrührt. Weiterverarbeitung wie bei Beispiel i.3. ioog lignitic lignite are mixed with a solution of 12 g of Pyridn Stirred in 200 cc of benzene for 3 hours at So '. Further processing as in the example i.
q:. ioo g gemahlenes Lignin werden mit einer Lösung von io g Naphthylamin in 200 Ccm Benzol 3 Stunden bei So' verrührt. Weiterverarbeitung wie bei Beispiel i.q :. 100 g of ground lignin are mixed with a solution of 10 g of naphthylamine Stirred in 200 cc of benzene for 3 hours at So '. Further processing as in the example i.
5. i oo g gemahlener Torf werden mit einer Lösung von i o g Toluidin in i 5o ccm Benzol 3 Stunden bei So' verknetet. Weiterv erarbeitung wie bei Beispiel i.5. 100 g of ground peat are mixed with a solution of 100 g of toluidine kneaded in 50 cc benzene for 3 hours at So '. Further processing as in the example i.
G. ioog gemahlene Steinkohle werden mit einer Lösung von io g Anilin in 200 ccm Benzol 3 Stunden bei So' verrührt. Weiterverarbeitunz wie bei Beispiel i.G. ioog ground hard coal are mixed with a solution of io g aniline Stirred in 200 cc of benzene for 3 hours at So '. Further processing as in the example i.
Claims (1)