Verfahren zur Herstellung als Kleb-, Anstrich- oder Bindemittel geeigneter
Öle In dem Hauptpatent 539 589 und dessen Zusatzpatent 540 998 ist ein Verfahren
zur Herstellung eines als Kleb- oder Bindemittel u. dgl. geeigneten Öles beschrieben,
nach welchem man Butadien oder seine Methy lderivate zweckmäßig unter Anwendung
von erhöhtem Druck und bzw. oder Katalysatoren auf Temperaturen unterhalb der Zersetzungstemperatur
der entstehenden Öle erhitzt und die erhaltenen öligen Produkte von etwa entstandenen
nichtöligen Anteilen abtrennt.Process for the production of oils suitable as adhesives, paints or binders In the main patent 539 589 and its additional patent 540 998, a process for producing an oil suitable as an adhesive or binder and the like is described, according to which butadiene or its methyl derivatives are used expediently heated to temperatures below the decomposition temperature of the oils formed using elevated pressure and / or catalysts and the oily products obtained are separated from any non-oily fractions that have formed.
Es wurde nun gefunden, daß man bei diesem Verfahren in sehr kurzer
Zeit und in quantitativer Ausbeute zu Produkten gelangt, die in ihren Eigenschaften
den vorerwähnten gleich bzw. ähnlich sind, wenn man die Behandlung des Butadiens
usw. unter Druck in Gegenwart von Sauerstoff oder solchen enthaltenden oder abgebenden
Gasen bzw. Gasgemischen ausführt. Je nach den angewandten Bedingungen, wie Dauer
der Einwirkung und Reaktionstemperatur, Druck usw., erhält man mehr oder weniger
hochviskose Produkte.It has now been found that this method can be used in a very short time
Time and in quantitative yield to get products which in their properties
are the same or similar to those mentioned above when considering the treatment of butadiene
etc. under pressure in the presence of or containing or releasing oxygen
Executes gases or gas mixtures. Depending on the conditions used, such as duration
the action and reaction temperature, pressure, etc., one obtains more or less
highly viscous products.
M'ie bei den Verfahren gemäß der Patente 539 589 und 540 998 ist es
auch bei dem vorliegenden Verfahren mitunter vorteilhaft, die Polymerisation in
Gegenwart von Katalysatoren anorganischer oder organischer Natur, z. B. organischen
Flüssigkeiten, wie aromatischen Aminen, Kohlenwasserstoffen usw., vor sich gehen
zu lassen. Man kann dabei auch Gemische von organischen Lösungsmitteln benutzen,
die bei der Verwendung der Polymerisationsprodukte z. B. als Anstrichmittel, wie
Streich-, Tauch- oder Spritzlacke, nützlich oder mindestens nicht schädlich sind.It is the case with the processes according to patents 539,589 and 540,998
sometimes advantageous also in the present process, the polymerization in
Presence of catalysts of an inorganic or organic nature, e.g. B. organic
Liquids such as aromatic amines, hydrocarbons, etc., are going on
allow. You can also use mixtures of organic solvents,
when using the polymerization z. B. as a paint, such as
Brush, dip or spray paints are useful or at least not harmful.
Beispiel i In ein Druckgefäß werden ioo Gewichtsteile Butadien und
75 Gewichtsteile Äthenylcyclohexen eingefüllt. Durch Einpressen von Luft wird in
dem Gefäß ein Druck von 2o Atm. hergestellt. Darauf wird q. Stunden auf 195' erhitzt.
Man erhält in quantitativer Ausbeute ein hochwertiges Polymerisationsprodukt, das
sich vorzüglich für die Herstellung oder zum Kleben von Filmen, Überzügen, Kunstmassen
usw. und aJs- Grundstoff sowie als Zusatzmittel für Lacke und andere Anstrichmittel
eignet. Beispiel 2 Zoo Gewichtsteile Butadien werden mit 2oo Gewichtsteilen Benzol,
Zoo Gewichtsteilen Ligroin und 5o Gewichtsteilen Xylol vermischt,
worauf
man das Gemisch unter einem Luftdruck von 8o Atm. 4 Stunden auf 18o' erhitzt. Es
wird ein hochwertiges Polymerisationsprodukt erhalten, das ohne weiteres als Transparentlack
verwendet werden kann. Beispiel 3 ioo Gewichtsteile Isopren werden mit Zoo Gewichtsteilen
Toluol vermischt und in einem Druckgefäß unter 25 Atm. Luftdruck i Stunde auf 150
' erwärmt. Man erhält so eine Lösung eines Lackgrundstoffes in Toluol, die sich
vorzüglich zum Überziehen von Gegenständen eignet. Beispiel 4 EinGemisch aus 28o
Gewichtsteilen Butadien, 14o Gewichtsteilen Toluol, 6o Gewichtsteilen Ligroin und
6o Gewichtsteilen Butanol wird in einem geschlossenen Gefäß i1/2 Stunden bis auf
Zoo ° unter 8o Atm. Luftdruck erhitzt. Nach Ablassen des Druckes wird die Lösung
des entstandenen Polymerisationsproduktes erneut eine Stunde lang bei 8o' unter
6o Atm. Luftdruck erhitzt. Man erhält in guter Ausbeute eine Lösung eines hochwertigen
Lackes, der, auf eine Unterlage aufgebracht, sehr schnell zu einem hochelastischen
glänzenden Überzug auf= trocknet. Beispiel 5 35o Gewichtsteile Butadien, ioo Gewichtsteile
Toluol, ioo Gewichtsteile Ligroin, 8o Gewichtsteile Butanol und 2o Gewichtsteile
Xylol werden in einem geschlossenen Gefäß 4 Stunden lang bei 120 ' mit komprimierter
Luft von 8o Atm. Druck behandelt. Man erhält auf diese Weise eine Lösung eines hochwertigen
Lackes. Wird dieser Lack mit 6 °/o seines Gewichtes an Eisenrot vermischt und auf
eine Unterlage aufgespritzt, so erzielt man einen rasch trocknenden, fest haftenden
Überzug von großer Widerstandsfähigkeit.Example i 100 parts by weight of butadiene and
75 parts by weight of Ethenylcyclohexen filled. Forcing air in
the vessel a pressure of 20 atm. manufactured. Then q. Heated to 195 'for hours.
A high-quality polymerization product is obtained in quantitative yield, the
Excellent for the production or for gluing of films, coatings, art masses
etc. and aJs base material and as an additive for varnishes and other paints
suitable. Example 2 zoo parts by weight of butadiene are mixed with 200 parts by weight of benzene,
Zoo parts by weight of ligroin and 50 parts by weight of xylene mixed,
on what
the mixture under an air pressure of 8o atm. Heated to 18o 'for 4 hours. It
a high-quality polymerisation product is obtained, which is readily available as a transparent varnish
can be used. Example 3 100 parts by weight isoprene with zoo parts by weight
Toluene mixed and placed in a pressure vessel under 25 atm. Air pressure at 150 for one hour
'warmed up. This gives a solution of a paint base in toluene, which
Excellent for covering objects. Example 4 A mixture of 28o
Parts by weight of butadiene, 14o parts by weight of toluene, 6o parts by weight of ligroin and
6o parts by weight of butanol is kept in a closed vessel for i1 / 2 hours up to
Zoo ° below 8o atm. Air pressure heated. After releasing the pressure, the solution becomes
of the resulting polymerization product again for one hour at 8o 'below
6o atm. Air pressure heated. A solution of a high quality is obtained in good yield
Varnish, which, when applied to a base, very quickly becomes a highly elastic one
shiny coating = dries. Example 5 35o parts by weight of butadiene, 100 parts by weight
Toluene, 100 parts by weight of ligroin, 80 parts by weight of butanol and 20 parts by weight
Xylene are compressed in a closed vessel for 4 hours at 120 'with
Air of 8o atm. Pressure treated. A high quality solution is obtained in this way
Varnish. If this lacquer is mixed with 6% of its weight of iron red and applied
If a pad is sprayed on, a fast-drying, firmly adhering one is achieved
Very resistant coating.
Beispiel 6 i5o Gewichtsteile Butadien_uvnd i2o Gewichtsteile Toluöl
werden in einem .geschlossenen Gefäß mit einem Gemisch von Ozor-und Luft unter einem
Druck von -_3o Atm. 2 ##den erhitzt, wobei der Druck auf etwa 5o Atm, steigt. Es
wird in guter Ausbeute die Lösung eines hochwertigen Lackgrundstoffes erhalten.
Beispiel ? 4oo Gewichtsteile Dimethylbutadien, ioo Gewichtsteile Toluol, ioo Gewichtsteile
Ligroin, 6o Gewichtsteile Xylol, 6o Gewichtsteile Butanol werden unter einen Luftdruck
von 6o Atm. gebracht und sodann auf i8o ° erhitzt. Es bildet sich in guter Ausbeute
eine Lösung eines hochwertigen Lackgrundstoffes, der, auf eine Unterlage aufgespritzt,
einen dauerhaften Überzug liefert. Beispiel 8 Isopren wird in einem geschlossenen
Gefäß bei einem Luftdruck von 2o Atm. 4 Stunden auf i2o bis 130 ' erhitzt. Es wird
ein viskoses Polymerisationsprodukt mit für die Anstrichtechnik wertvollen Eigenschaften
erhalten. Beispiel 9 Butadien wird in einem geschlossenen Gefäß unter einen Luftdruck
von io Atm. gestellt und 3 Stunden auf 130 ' erhitzt. Es findet Polymerisation des
Butadiens zu einem viskosen Produkt statt, das hervorragend als Klebe- und Anstrichmittel
geeignet ist. Beispiel io Es werden mehrere Glasplatten mit einer dünnen Schicht
des nach Beispiel i erhältlichen Produktes bestrichen, aufeinandergelegt und unter
leichtem Druck, etwa io kg/qm, auf 85 bis 9o ° erwärmt, bis die Zwischenschicht
völlig erhärtet ist. Die Glasplatten haften dann fest aufeinander.Example 6 150 parts by weight of butadiene and 120 parts by weight of toluene oil
are in a closed vessel with a mixture of ozone and air under one
Pressure of -3o Atm. 2 ## den heated, whereby the pressure rises to about 50 atm. It
the solution of a high-quality paint base material is obtained in good yield.
Example ? 400 parts by weight of dimethylbutadiene, 100 parts by weight of toluene, 100 parts by weight
Ligroin, 60 parts by weight of xylene, 60 parts by weight of butanol are under atmospheric pressure
from 6o Atm. brought and then heated to 180 °. It forms in good yield
a solution of a high-quality paint base, which, sprayed onto a base,
provides a permanent coating. Example 8 Isoprene is used in a closed
Vessel at an air pressure of 20 atm. Heated for 4 hours at i2o to 130 '. It will
a viscous polymerisation product with valuable properties for painting technology
obtain. Example 9 Butadiene is placed in a closed vessel under atmospheric pressure
by io Atm. placed and heated to 130 'for 3 hours. It takes place polymerisation of the
Butadiene instead of a viscous product that is excellent as an adhesive and paint
suitable is. Example io There are several glass plates with a thin layer
of the product obtainable according to example i coated, placed on top of one another and under
light pressure, about 10 kg / m², heated to 85 to 90 ° until the intermediate layer
is completely hardened. The glass plates then adhere firmly to one another.