Prothese für zahnärztliche oder sonstige medizinische Zwecke Gegenstand
Lies Hauptpatentes ist eine Prothese für zahnärztliche oder sonstige medizinische
Zwecke, die aus einer plastischen Masse besteht, die im wesentlichen Celluloseäther
(Äthylcellulose) und aliphatische Dicarbonsäureester enthält.Prosthesis for dental or other medical purposes
Lie's main patent is a prosthesis for dental or other medical
Purpose, which consists of a plastic mass, which is essentially cellulose ether
(Ethyl cellulose) and aliphatic dicarboxylic acid esters.
Gegenstand der Erfindung ist eine weitere Ausbildung . der Zahnprothese
nach Patent -f99 676. Äthylcellulose ist bislang nur zu sehr hohen Preisen und in
kleinen Mengen beschaffbar, so daß die Herstellung von Zahnprothesen oder solchen
für andere medizinische Zwecke aus diesem Stoffe als Hauptbestandteil in größerem
Umfange erschwert ist.The invention relates to a further training. the denture
according to patent -f99 676. Ethyl cellulose is so far only at very high prices and in
Small quantities can be procured, so that the manufacture of dentures or such
for other medical purposes from this substance as a main component in a larger one
Scope is difficult.
Das Wesen der Prothese nach der Erfindung besteht darin, daß dieselbe
nur mit einem Überzug aus Äthylcellulose, zweckmäßig in Verbindung mit einem aliphatischen
Dicarbonsäureester (Adipinsäureester), versehen ist, während der innere Körper der
Prothese z. B. aus den üblichen Cellulosemassen, als aus Celluloseester hergestellt
ist, welcher Körper für Zahnprothesen wegen seiner verhältnismäßig hohen Bruchfestigkeit
und seiner Stärke an sich brauchbar ist, wenn er auch den Nachteil hat, gegen Alkalien
und Speichelfermente unbeständig zu sein, da solche zu. einer teilweisen Korrosion
der Celluloseestermasse führen. Die Zahnprothese nach der Erfindung verbindet also
die Vorteile einer aus reiner Äthylcellulose in Verbindung mit einem aliphatischen
Dicarbonsäureester bestehenden Prothese, insbesondere die Vorteile der Beständigkeit
gegen Alkalien und Speichelfermente, mit den Vorteilen der bekannten Äthylcelluloseesterprothesen
(der Billigkeit der Herstellung, der großen Bruchfestigkeit und -des schönen Aussehens)
Ein besonderer Vorteil der Zahnprothese nach der Erfindung und ihres Herstellungsverfahrens
besteht darin, daß eine große Zahl von im Gebrauch befindlichen Gebißplatten aus
Celluloseester auf einfache und wirtschaftliche Weise dadurch wesentlich verbessert
werden können, daß man sie nachträglich mit einem Überzug (Panzer) versieht.The essence of the prosthesis according to the invention is that the same
only with a coating of ethyl cellulose, useful in conjunction with an aliphatic one
Dicarboxylic acid ester (adipic acid ester), while the inner body of the
Prosthesis z. B. from the usual cellulose masses than made from cellulose esters
is what body for dentures because of its relatively high breaking strength
and its strength is useful in itself, even if it has the disadvantage, against alkalis
and salivary ferments to be fickle as such too. partial corrosion
the cellulose ester mass lead. The dental prosthesis according to the invention thus connects
the advantages of a pure ethyl cellulose combined with an aliphatic one
Dicarboxylic acid esters existing prosthesis, in particular the advantages of durability
against alkalis and salivary ferments, with the advantages of the well-known ethyl cellulose ester prostheses
(the cheapness of manufacture, the great breaking strength and the beautiful appearance)
A particular advantage of the dental prosthesis according to the invention and its manufacturing method
consists in the fact that a large number of denture plates in use consist of
Cellulose esters are thereby significantly improved in a simple and economical manner
that they can be subsequently provided with a coating (armor).
Zur Herstellung dieses Äthylcellulosepanzers löst man Äthylcellulose
auf, und zwar in einem Lösungsmittelgemisch, welches gleichzeitig auch ein Lösungsmittel
für Celluloseester ist. Der Lösung fügt man noch ein Elastisierurrgsmittel, z. B.
Adipinsäureester, in solcher Menge zu, daß der Elastizitäts- und Ausdehnungskoeffizient
der Überzugsmasse der gleiche ist wie der der zu überziehenden Masse. -
Das
vorher gesäuberte und getrocknete Formstück aus Celluloseester wird mittels Aufspritzens
oder Aufpinselns dünn und gleichmäßig mit der Äthylcelluloselösung überzogen und
nach zweistündigem Trocknen in mäßig erwärmter, staubfreier Atmosphäre nochmals
in gleicher Weise mit einem Überzug versehen. Gleichzeitig läßt sich durch Färben
der Äthylcelluloselösung erreichen, daß unansehnlich gewordene Prothesen eine schöne
Farbe erhalten.To make this ethyl cellulose armor, you dissolve ethyl cellulose
on, in a solvent mixture, which is also a solvent at the same time
for cellulose ester is. The solution is also added an elasticizing agent, e.g. B.
Adipic acid ester, in such an amount that the coefficient of elasticity and expansion
the coating mass is the same as that of the mass to be coated. -
That
A previously cleaned and dried shaped piece made of cellulose ester is sprayed on
Or brush it on thinly and evenly with the ethyl cellulose solution and
after two hours of drying in a moderately heated, dust-free atmosphere again
provided with a coating in the same way. At the same time can be done by dyeing
the ethyl cellulose solution that unsightly prostheses have a beautiful one
Color preserved.