DE4433626A1 - Multilayer antistatic polyolefin-based plastics film - Google Patents

Multilayer antistatic polyolefin-based plastics film

Info

Publication number
DE4433626A1
DE4433626A1 DE4433626A DE4433626A DE4433626A1 DE 4433626 A1 DE4433626 A1 DE 4433626A1 DE 4433626 A DE4433626 A DE 4433626A DE 4433626 A DE4433626 A DE 4433626A DE 4433626 A1 DE4433626 A1 DE 4433626A1
Authority
DE
Germany
Prior art keywords
plastic
plastic film
antistatic
conductive
film according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE4433626A
Other languages
German (de)
Inventor
Istvan Dr Benedek
Erich Frank
Gerd Dr Nicolaus
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
POLI FILM VERWALTUNGS GmbH
Original Assignee
POLI FILM VERWALTUNGS GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by POLI FILM VERWALTUNGS GmbH filed Critical POLI FILM VERWALTUNGS GmbH
Priority to DE4433626A priority Critical patent/DE4433626A1/en
Publication of DE4433626A1 publication Critical patent/DE4433626A1/en
Withdrawn legal-status Critical Current

Abstract

Electrically conductive multilayer polyolefin based plastics film in which the conductive additive is incorporated as a filler into the plastic of an outer layer in reticular fashion to render the outer layer penetrably conductive. Pref. conductive additive is carbon black and/or antistatics and/or conductive inorganic pigments. Suitable antistatic is a nonionic cpd. in the form of uncharged surface active molecules. The active layer contains 2-40 (pref. 20-30) wt.% carbon black and 0-5 wt.% antistatics w.r.t. 100 wt.% of the plastic. The concn. of conductive additive incorporated is adjusted to give a conductivity of \- 10<-11> 1/ohm (Siemens), esp. 10<-5>-10<-9> 1/ohm (Siemens).

Description

Die Erfindung betrifft eine elektrisch leitfähige, aus mehreren Schichten bestehende Kunststoffolie auf Polyo­ lefinebasis, wobei der Kunststoff leitfähige Additive aufweist.The invention relates to an electrically conductive multi-layer plastic film on polyo lefine basis, the plastic conductive additives having.

Derartige mehrschichtige Folien, in Form von Rollen, Bögen, Halbschläuchen und insbesondere Hauben zur Verwen­ dung als Abdeckhauben für Kraftfahrzeuge, bspw. um Lac­ kierungen durchzuführen, sind bereits bekannt. Die ther­ mischen und elektrischen Eigenschaften dieser Folien sind jedoch nicht zufriedenstellend. Insbesondere ist die Leitfähigkeit der bekannten Folien ungleichmäßig über die Folie ausgebildet, wodurch eine gleichmäßige Ableitung elektrischer Ladungen nicht sichergestellt ist.Such multilayer films, in the form of rolls, Elbows, half tubes and especially hoods for use dung as covers for motor vehicles, for example around Lac to carry out cations are already known. The ther mix and electrical properties of these foils however, are not satisfactory. In particular is the conductivity of the known films is uneven formed over the film, creating a uniform Discharge of electrical charges is not ensured.

Die Erfindung schlägt daher vor, daß die leitfähigen Additive in den Kunststoff einer äußeren Schicht als Füllstoffe netzwerkartig eingelagert sind, derart, daß die äußere Schicht durchgängig leitfähig ausgebildet ist. Eine derartige Einlagerung von elektrisch leitfähi­ gen Additiven stellt sicher, daß über diese Schicht elektrische Ladungen gleichmäßig abgeleitet werden kön­ nen. Insbesondere ist auch durch die netzwerkartige Einlagerung eine über die gesamte Folie gleichmäßig verteilte Oberflächenleitfähigkeit gesichert.The invention therefore proposes that the conductive Additives in the plastic as an outer layer Fillers are embedded in a network, such that the outer layer consistently conductive is. Such storage of electrically conductive gene additives ensures that over this layer electrical charges can be discharged evenly nen. In particular, the network-like Storage one evenly over the entire slide distributed surface conductivity ensured.

Geeignete, in den Polyolefin-Kunststoff einlagerungsfähi­ ge leitfähige Additive sind insbesondere Ruß und/oder Antistatika und/oder elektrisch leitfähige anorganische Pigmente. Überraschend wurde dabei festgestellt, daß die Kombination von Rußteilen in dem Kunststoff mit einem Antistatikum zu einer sehr deutlichen Erhöhung der Leit­ fähigkeit führt, ohne daß die mechanischen Eigenschaften der Kunststoffolie zu stark beeinträchtigt sind.Suitable, storable in the polyolefin plastic Ge conductive additives are especially carbon black and / or Antistatic and / or electrically conductive inorganic Pigments. It was surprisingly found that the Combination of soot parts in the plastic with one Antistatic to increase the lead significantly  ability leads without the mechanical properties the plastic film are too badly affected.

Die Erfindung ermöglicht in vorteilhafter Weise durch die Steuerung der Konzentration des leitfähigen Additi­ ves die Leitfähigkeit der Folie geradezu stufenweise auf eine Leitfähigkeit von bis zu 10-11 1/Ohm (Siemens), vorzugsweise jedoch auf eine Leitfähigkeit von 10-5 bis 10-9 1/Ohm (Siemens) einzustellen.The invention advantageously enables the conductivity of the film to be stepped down to a conductivity of up to 10 -11 1 / ohm (Siemens), but preferably to a conductivity of 10 -5 to 10 -9, by controlling the concentration of the conductive additive 1 / Ohm (Siemens).

Es ist vorgesehen, daß der Anteil des Antistatikums 0 bis 5 Gewichtsprozent, oder daß der Anteil des Rußes zwischen 0 und 40 Gewichtsprozent, bevorzugt bei etwa 20 bis 25 Gewichtsprozent jeweils bezogen auf 100 Gewichts­ prozent des Kunststoffes, beträgt. Bevorzugt ist weiter eine Kombination von Ruß mit Antistatika, wobei der Rußanteil etwa 25 Gewichtsprozent einschließlich etwa 2 Gewichtsprozent Antistatika, bezogen auf 100 Gewichtspro­ zent des Kunststoffes, beträgt.It is envisaged that the proportion of the antistatic 0 to 5 weight percent, or that the proportion of carbon black between 0 and 40 percent by weight, preferably around 20 up to 25 percent by weight based on 100 percent by weight percent of the plastic. Preferred is further a combination of carbon black with antistatic agents, the Soot content about 25 percent by weight including about 2 Weight percent antistatic based on 100 weight percent percent of the plastic.

Weiter ist in dem Kunststoff einer äußeren Schicht ein Farbpigment als Füllstoff eingelagert, wodurch zum einen durch unterschiedliche Farbgestaltung die leitfähige Schicht sofort erkannt werden kann und zum anderen ein bevorzugtes weißes Farbpigment die Temperaturbeständig­ keit einer erfindungsgemäßen Folie von 120 Grad Celsius über mindestens 5 Minuten weiter steigert.There is also an outer layer in the plastic Color pigment stored as a filler, which on the one hand the conductive color due to different colors Layer can be recognized immediately and the other one preferred white color pigment that is temperature resistant speed of a film according to the invention of 120 degrees Celsius increases for at least 5 minutes.

In einzelnen werden spezielle Rußkonzentrate mit beson­ deren nachbehandelten, leitfähigen Rußteilen verwendet. Diese Rußkonzentrate werden in Form eines Rußmaster­ batch, als Rußpaste, als Rußdispersion oder dgl. in das Kunststoffgranulat eingemischt, das einen Extruder durch­ setzt. Zusätzlich oder alternativ werden hierbei An­ tistatika, wie Fettsäureester, Fettsäureamin und/oder -amide, Glycerolmonostearat, -oleat usw. beigemischt. Die hierfür erforderliche Rußkonzentration ist abhängig von den verwendeten Rußen, der Matrix, der Verarbeitungs­ methode und den gestellten Anforderungen. Bei Zugabe des Rußes und/oder der mitverwendeten Antistatika, ist in der Regel ein Rußanteil von 3 bis 65% erforderlich. Vorzugsweise ein Rußanteil von 15 bis 30%, weiter vor­ zugsweise von 20 bis 25%. Die Methode der Einarbeitung und die Verteilung des Rußes in der Matrix spielen dabei eine wesentliche Rolle. Als Antistatika können im einzel­ nen zunächst kationaktive Verbindungen mit meistens einem langen Alkylrest enthaltenen Kation (ein quaternä­ res Ammonium-, Phosphonium oder Sulphoniumsalz) zum Einsatz kommen, wobei die quaternäre Gruppe auch in einem Ringsystem (z. B. Imidazol) auftreten kann.In particular, special soot concentrates are used the aftertreated, conductive carbon black parts used. These soot concentrates are in the form of a soot master batch, as a carbon black paste, as a carbon black dispersion or the like in the Plastic granules mixed through an extruder puts. In addition or as an alternative, An tistatics, such as fatty acid esters, fatty acid amine and / or  -amides, glycerol monostearate, -oleate etc. are added. The soot concentration required for this is dependent of the carbon blacks used, the matrix, the processing method and the requirements. When adding the Soot and / or the antistatic agents used is in usually a soot content of 3 to 65% is required. Preferably a soot content of 15 to 30%, further before preferably from 20 to 25%. The method of familiarization and the distribution of soot in the matrix play a role an essential role. Antistatic agents can be used individually initially cation-active compounds with mostly a long alkyl radical containing cation (a quaternary res ammonium, phosphonium or sulphonium salt) for Deployed, with the quaternary group also in a ring system (e.g. imidazole) can occur.

Weiter können die Antistatika anionaktive Verbindungen sein, hierbei meist ein Alkylsulfonat, -sulfat oder -phosphat, ein Dithiocarbamat oder Carboxylat.The antistatic agents can also contain anion-active compounds be, mostly an alkyl sulfonate, sulfate or -phosphate, a dithiocarbamate or carboxylate.

Des weiteren können die Antistatika nichtionogene Verbin­ dungen sein. Hierbei handelt es sich um ungeladene, grenzflächenaktive Moleküle von wesentlich geringerer Polarität als ionogene Verbindungen, wie bspw. Polyethy­ lenglykolester oder -ether, Fettsäureester oder -ethano­ lamide, homo- bzw. diglyzeride oder ethoxylierte Fettami­ ne.Furthermore, the antistatic can be non-ionic endings. These are uncharged, surfactant molecules of much less Polarity as ionogenic compounds, such as. Polyethy lenglycol esters or ethers, fatty acid esters or ethano lamids, homo- or diglycerides or ethoxylated fatty amines no

Weiter können auch externe Antistatika angewendet wer­ den. Hierbei sind die Antistatika nicht in dem Kunst­ stoffgranulat enthalten, sondern werden erst nachträg­ lich auf die fertige Folie aufgebracht. Bspw. handelt es sich hierbei um hygroskopische Substanzen, wie Glyzerin, Polyole oder Polyglykole, denen das Merkmal der Grenzflä­ chenaktivität fehlt. External antistatic agents can also be used the. Here, the antistatic agents are not in the art contain granulate, but will only be added later Lich applied to the finished film. E.g. it is are hygroscopic substances such as glycerin, Polyols or polyglycols which have the characteristic of the interface activity is missing.  

Während es bislang bereits bekannt ist, daß bei gleicher Rußkonzentration unterschiedliche Werte hinsichtlich der elektrischen Eigenschaften einer solchen Folie festge­ stellt werden, was bspw. auf nicht vorhersehbare Mi­ schungs- oder Nichtentmischungsvorgänge zurückgeführt wird, ist die Rußkonzentration bei einer erfindungsgemä­ ßen Folie zugleich wesentlich besser vorhersagbar. Es wird voraussehbar eine gute Dispergierung des Rußes erreicht.While it is already known that the same Soot concentration different values with regard to the festge electrical properties of such a film what, for example, on unforeseeable Wed. or demixing operations is the soot concentration in a outer film is also much more predictable. It a good dispersion of the soot is foreseeable reached.

Zusätzlich oder alternativ zu den erwähnten Rußteilen und Antistatika können auch leitfähige, anorganische Pigmente (Mischpigmente) in der Folie enthalten sein. Die zugegebene Rußmenge liegt, bezogen auf das Gewicht der Folie, bei 2 bis 40%, vorzugsweise im Bereich von 20 bis 30, weiter vorzugsweise bei 25%.In addition or as an alternative to the soot parts mentioned and antistatic agents can also be conductive, inorganic Pigments (mixed pigments) may be contained in the film. The amount of carbon black added is based on the weight the film, at 2 to 40%, preferably in the range of 20 to 30, more preferably 25%.

Die Kunststoffolien können im einzelnen aus den Kunst­ stoffen PE, PP, PB und deren Recyclaten bestehen. Sie sind frei von migrierenden Gleitmitteln.The plastic films can be individually from the art substances PE, PP, PB and their recyclates exist. she are free from migrating lubricants.

Weiter ist bevorzugt, daß mindestens eine Schicht aus PP besteht.It is further preferred that at least one layer of PP consists.

Darüber hinaus ist bevorzugt, daß eine innere Schicht der Folie Corona unvorbehandelt ist oder kleberbeschich­ tet ist. Hiermit soll eine bessere Haftung auf einer Kraftfahrzeugkarosserie etwa erreicht werden.In addition, it is preferred that an inner layer the film Corona is untreated or coated with adhesive is. This is intended to ensure better liability on a Motor vehicle body can be reached about.

Die Kleberbeschichtung kann auf Kautschukbasis vorgenom­ men sein oder auch als Acrylatkleber auf Lösemittelbasis oder Wasserbasis.The adhesive coating can be made on a rubber basis or as a solvent-based acrylic adhesive or water based.

Die Gesamtdicke der Folie beträgt mindestens 10 µm und maximal etwa 50 µm. The total thickness of the film is at least 10 µm and maximum about 50 µm.  

Die Folie kann durch Cast- oder Blasfolienherstellung erzeugt sein.The film can be made by cast or blown film be generated.

Anhand der Zeichnung wird die Erfindung weiter erläu­ tert, wobei dieThe invention will be further explained with the aid of the drawing tert, the

Fig. 1 bis 4 vergrößert die Mikrostruktur von Kunst­ stoffen mit netzwerkartig eingelagerten leitfähigen Additiven zeigen, Fig. 1 to 4 increases the microstructure of plastics with embedded network-like conductive additives show

Fig. 5 einen schematischen Schnitt durch eine Folie nach der Erfindung darstellt und Fig. 5 shows a schematic section through a film according to the invention and

Fig. 6 der Erläuterung der erfindungsgemäßen Folie dient. FIG. 6 to illustrate the inventive film is used.

In den Fig. 1 bis 4 sind vier Rasterelektronenmikro­ skop-Aufnahmen, die etwa einer hunderttausendfachen Vergrößerung entsprechen, dargestellt. Es zeigen die Fig. 1 und 2 REM-Aufnahmen einer angeätzten PP-Preß­ platte, die Fig. 3 und 4 REM-Aufnahmen einer angeätz­ ten PP-Spritzgußplatte, jeweils mit einem leitfähigen Rußcompound. Es sind Rußteilchen (schwarz) und Kunst­ stoffanteile (im wesentlichen weiß) zu unterscheiden. Durch die Einbettung des Rußes in Zwischenräume/Täler der Kunststoffteile erklärt sich die dargestellte netz­ werkartige Struktur.In Figs. 1 to 4 four scanning electron micrographs are microscope photographs, which correspond to approximately one hundred thousand times magnification is shown. There, Figs. 1 and 2 SEM micrographs of an etched press plate PP, Figs. 3 and 4 SEM micrographs of a angeätz th PP-plate injection molding, each having a conductive Rußcompound. There are soot particles (black) and plastic parts (mainly white) to be distinguished. The embedding of the soot in the spaces / valleys of the plastic parts explains the network-like structure shown.

Wie Fig. 5 zeigt, kann die Folie 1 im einzelnen drei­ schichtig sein, wobei eine erste Schicht 2 eine Dicke 3 von 7 µm aufweist, eine zweite Schicht 4 einer Dicke 5 von 11 µm und eine dritte Schicht 6 einer Dicke 7 von 7 µm. Die Schichten 2,4 und 6 sind koextrudiert oder aufeinander kaschiert. Die erste Schicht 2 ist durch Einlagerung von elektrisch leitfähigen Additiven 8 leit­ fähig und insbesondere oberflächenleitfähig ausgebildet. Die Additive 8 sind als Füllstoffe in dem Kunststoff 9 der ersten Schicht 2 netzwerkartig aneinander angela­ gert, wodurch die erfindungsgemäße gute Leitfähigkeit erreicht wird. Weiter ist es auch bevorzugt, daß die Folie 1 durch eine Einlagerung von Farbpigmenten 10 in dem Kunststoff 11 z. B. der dritten Schicht 6 farbig ausgeführt ist, so daß Vorder- 12 und Rückseite 13 unter­ schieden werden können. Es ist nämlich wesentlich, daß die leitfähige erste Schicht 2 nicht auf z. B. einer Karosserie 14 aufliegt, sondern sich im Benutzungszu­ stand außen befindet, vgl. Fig. 6. Dort ist gezeigt, wie mittels der erfindungsgemäßen Folie 1 die Karosserie 14 eines Kraftfahrzeuges 15 abgedeckt werden kann, um z. B. das Lackieren eines Kotflügels 16 zu ermöglichen. Dabei kann die Folie 1 als Hauben 17 zur Abdeckung z. B. der Reifen 18 ausgebildet sein oder aber auch als Bogen oder von einer Rolle abzuschneidendes Teilstück, um damit einzelne Fahrzeugteile wie Stoßstangen, Lampen etc. des Kraftfahrzeuges 15 abzudecken. Insbesondere für eine derartige Verwendung ist die Rückseite 13 der Folie 1 mit einem Kleber 19 beschichtet, vgl. Fig. 5, wodurch eine Selbsthaftung der Folie auf den angesprochenen Teilen der Karosserie 14 erreicht wird.As shown in FIG. 5, the film 1 can have three layers, a first layer 2 having a thickness 3 of 7 μm, a second layer 4 having a thickness 5 of 11 μm and a third layer 6 having a thickness 7 of 7 μm . The layers 2, 4 and 6 are co-extruded or laminated onto one another. The first layer 2 is formed by the incorporation of electrically conductive additives 8 and is particularly conductive. The additives 8 are added as fillers in the plastic 9 of the first layer 2 to one another in a network-like manner, as a result of which the good conductivity according to the invention is achieved. It is also preferred that the film 1 by embedding color pigments 10 in the plastic 11 z. B. the third layer 6 is colored so that the front 12 and back 13 can be distinguished. It is essential that the conductive first layer 2 not on z. B. a body 14 rests, but is in the position of use outside, see. Fig. 6. It is shown how the body 14 of a motor vehicle 15 can be covered by means of the film 1 according to the invention, for B. to allow painting of a fender 16 . The film 1 can be used as covers 17 for covering z. B. the tire 18 may be formed or as a sheet or cut from a roll to cover individual vehicle parts such as bumpers, lamps, etc. of the motor vehicle 15 . For such a use in particular, the back 13 of the film 1 is coated with an adhesive 19 , cf. Fig. 5, whereby a self-adhesion of the film on the addressed parts of the body 14 is achieved.

Die in der vorstehenden Beschreibung, der Zeichnung und den Ansprüchen offenbarten Merkmale der Erfindung können sowohl einzeln als auch in beliebiger Kombination für die Verwirklichung der Erfindung von Bedeutung sein. Alle offenbarten Merkmale sind erfindungswesentlich. In die Offenbarung der Anmeldung wird hiermit auch der Offenbarungsinhalt der zugehörigen/beigefügten Priori­ tätsunterlagen (Abschrift der Voranmeldung) vollinhalt­ lich mit einbezogen.The in the above description, the drawing and Features of the invention disclosed in the claims can both individually and in any combination for the realization of the invention may be of importance. All the features disclosed are essential to the invention. In the disclosure of the application is hereby also the Disclosure content of the associated / attached priori full documents (copy of the pre-registration) included.

Claims (15)

1. Elektrisch leitfähige, aus mehreren Schichten beste­ hende Kunststoffolie auf Polyolefinbasis, wobei der Kunststoff leitfähige Additive aufweist, dadurch gekenn­ zeichnet, daß die leitfähigen Additive (8) in den Kunst­ stoff (9) einer äußeren Schicht (2) als Füllstoffe netz­ werkartig eingelagert sind, derart, daß die äußere Schicht (2) durchgängig leitfähig ausgebildet ist.1. Electrically conductive, consisting of several layers existing polyolefin-based plastic film, the plastic having conductive additives, characterized in that the conductive additives ( 8 ) in the plastic ( 9 ) of an outer layer ( 2 ) as fillers are network-like stored are such that the outer layer ( 2 ) is continuously conductive. 2. Kunststoffolie nach Anspruch 1 oder insbesondere danach, dadurch gekennzeichnet, daß die leitfähigen Additive Ruße und/oder Antistatika und/oder leitfähige anorganische Pigmente sind.2. Plastic film according to claim 1 or in particular afterwards, characterized in that the conductive Additive carbon blacks and / or antistatic agents and / or conductive are inorganic pigments. 3. Kunststoffolie nach einem oder mehreren der Ansprüche 1 bis 2 oder insbesondere danach, dadurch gekennzeich­ net, daß durch eine Steuerung der Konzentration des leitfähigen Additivs (8) die Leitfähigkeit auf minde­ stens 10-11 1/Ohm (Siemens), vorzugsweise auf 10-5 bis 10-9 1/Ohm (Siemens) eingestellt ist.3. Plastic film according to one or more of claims 1 to 2 or in particular according thereto, characterized in that by controlling the concentration of the conductive additive ( 8 ), the conductivity to at least 10 -11 1 / ohm (Siemens), preferably to 10 -5 to 10 -9 1 / Ohm (Siemens) is set. 4. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß das Antistatikum eine nichtionogene Verbindung in Form von ungeladenen grenzflächenaktiven Molekülen ist.4. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the antistatic is a non-ionic Compound in the form of uncharged surfactant Is molecules. 5. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß der Anteil des Antistatikums 0 bis 5 Gewichtsprozent, bezogen auf 100 Gewichtsprozent des Kunststoffes, beträgt. 5. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the proportion of the antistatic 0 to 5 Weight percent, based on 100 weight percent of Plastic.   6. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß der Anteil des Rußes zwischen 0 bis 40 Gewichtsprozent, bevorzugt bei etwa 20 bis 20 Gewichts­ prozent, bezogen auf 100 Gewichtsprozent des Kunststof­ fes beträgt.6. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the proportion of soot is between 0 and 40 Weight percent, preferably at about 20 to 20 weight percent, based on 100 percent by weight of the plastic fes is. 7. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach dadurch gekenn­ zeichnet, daß der Rußanteil bei etwa 25 Gewichtsprozent einschließlich etwa 2 Gewichtsprozent Antistatika, bezo­ gen auf 100 Gewichtsprozent des Kunststoffes, beträgt.7. Plastic film according to one or more of the previous existing claims or in particular characterized thereby records that the soot content at about 25 weight percent including about 2 weight percent antistatic, bezo to 100 percent by weight of the plastic. 8. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach dadurch gekenn­ zeichnet, daß in den Kunststoff (11) einer äußeren Schicht (6) ein Farbpigment (10), bevorzugt ein weißes Farbpigment, als Füllstoff eingelagert ist.8. Plastic film according to one or more of the preceding claims or in particular characterized in that in the plastic ( 11 ) of an outer layer ( 6 ) a color pigment ( 10 ), preferably a white color pigment, is incorporated as a filler. 9. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß die der leitfähigen Schicht (2) gegen­ überliegende äußere Schicht (6) corona-unvorbehandelt und/oder mit einem Kleber (19) beschichtet ist.9. Plastic film according to one or more of the preceding claims or in particular according thereto, characterized in that the conductive layer ( 2 ) against the outer layer ( 6 ) is corona-untreated and / or coated with an adhesive ( 19 ). 10. Leitfähige mehrschichtige Kunststoffolie auf Polyo­ lefinbasis, wobei der Kunststoff Rußteile aufweist, dadurch gekennzeichnet, daß zusätzlich zu dem Ruß in dem Kunststoff ein Antistatikum enthalten ist.10. Conductive multilayer plastic film on polyo lefin basis, the plastic has soot parts, characterized in that in addition to the soot in the Plastic contains an antistatic. 11. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß das Antistatikum eine kationaktive Verbindung ist. 11. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the antistatic is a cation active Connection is.   12. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß das Antistatikum eine anionaktive Verbindung ist.12. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the antistatic is an anionic Connection is. 13. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß das Antistatikum eine nichtionogene Verbindung in Form von ungeladenen grenzflächenaktiven Molekülen ist.13. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the antistatic is a non-ionic Compound in the form of uncharged surfactant Is molecules. 14. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß das Antistatikum als externes An­ tistatikum auf die Folie aufgegeben ist.14. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the antistatic as an external An tistatic is applied to the film. 15. Kunststoffolie nach einem oder mehreren der vorherge­ henden Ansprüche oder insbesondere danach, dadurch ge­ kennzeichnet, daß das externe Antistatikum eine hygrosko­ pische Substanz ist, daß es sich bspw. um Glyzerin, Polyole oder Polyglykole handelt.15. Plastic film according to one or more of the previous existing claims or in particular according thereto, thereby ge indicates that the external antistatic is a hygrosko The chemical substance is that it is, for example, glycerol, Polyols or polyglycols.
DE4433626A 1994-02-25 1994-09-21 Multilayer antistatic polyolefin-based plastics film Withdrawn DE4433626A1 (en)