DE4426888A1

DE4426888A1 - Aggregate for heat-insulating plaster

Info

Publication number: DE4426888A1
Application number: DE19944426888
Authority: DE
Inventors: Walter Kraemer
Original assignee: WUESTEFELD KALK GROS und EINZE
Priority date: 1994-07-29
Filing date: 1994-07-29
Publication date: 1996-02-15

Abstract

An aggregate for heat-insulating building material, esp. for structure-forming interior and exterior plaster, consists of a mixt. of expanded perlite or vermiculite particles of below 1000 microns size and a mineral filler, the mixt. being granulated with a binder of an aq. polymer (pref. polyvinyl acetate or an acrylate copolymer) dispersion. Also claimed is prodn. of the above aggregate by spraying the mixt. with the aq. polymer dispersion in a granulating drum and hardening the granulate by hot air drying to form pressure, water and alkali-resistant particles. The mixt. pref. contains 10-35 (pref. 20) wt.% perlite or vermiculite particles, pref. of below 500 microns size, and 65-90 wt.% filler. The filler may be limestone powder, chalk or a mixt. of pref. 30-40 wt.% cement and 25-60 wt.% limestone powder or chalk. The aq. polymer binder dispersion pref. has a solids content of 8-12.5%.

Description

Die Erfindung bezieht sich auf einen Zuschlagstoff für wärmedämmende Baustoffe, insbesondere für strukturbildende Innen- und Außenputze. Daneben hat die Erfindung ein Ver fahren zur Herstellung eines Zuschlagstoffes zum Gegen stand.The invention relates to an aggregate for insulating building materials, especially for structure-building Interior and exterior plasters. In addition, the invention has a ver drive to the production of an aggregate to the counter was standing.

Als Zuschlagstoffe für beispielsweise Innen- und Außen putze sind zahlreiche Leichtzuschlagstoffe wie Bimskör nungen, Porenbetonsplit, Blähton und Ziegelbruch bekannt. Derartige gebrochene Materialien haben den Nachteil, daß sie scharfkantig sind und somit z. B. als Rollkorn für Strukturputze nicht Verwendung finden können. Ein weiterer Nachteil besteht darin, daß derartige Materialien außer ordentlich flüssigkeitsaufnahmefähig sind und mithin bei der Verarbeitung eine enorme Wasserzugabe fordern. Ein kostengünstiger Ziegelsplit weist neben einer ungünstigen geometrischen Struktur auch noch schlechte Isoliereigen schaften auf.As additives for indoor and outdoor, for example plasters are numerous light aggregates such as pumice known, aerated concrete split, expanded clay and broken brick. Such broken materials have the disadvantage that they are sharp-edged and thus z. B. as rolled grain for Structural plasters cannot be used. Another Disadvantage is that such materials except are properly absorbent and therefore at request an enormous amount of water during processing. On Inexpensive brick split shows an unfavorable geometric structure also poor insulation properties create up.

Als Zuschlagstoffe sind darüber hinaus auch noch expandier tes Perlite und expandiertes Vermiculite bekannt, die zwar gute wärmedämmende Eigenschaften aufweisen, jedoch nicht über eine hinreichende mechanische Festigkeit verfü gen. Um sie gleichwohl als Zuschlagstoffe einsetzen zu können, ist es bekannt (DE-OS 31 03 111), eine geblähte Perlite-Körnung mit einer Glasur zu versehen, um dem Per litekorn durch die Glasur eine erhöhte mechanische Festigkeit zu geben. Ein derartiges glasiertes Perlite korn hat jedoch den Nachteil, daß es bei einer maschinel len Verarbeitung hoch abrasiv wirkt. Zudem ist es nur mit einem außerordentlichen und damit kostenintensiven Produktionsaufwand herstellbar.Additives are also expanding tes perlite and expanded vermiculite known to the have good thermal insulation properties, however do not have sufficient mechanical strength To use them as additives at the same time can, it is known (DE-OS 31 03 111), a blown Perlite grain with a glaze to the Per lit grain through the glaze an increased mechanical To give firmness. Such a glazed perlite However, grain has the disadvantage that it is in a machine processing is highly abrasive. In addition, it is only with an extraordinary and therefore expensive Production costs can be produced.

Der Erfindung liegt die Aufgabe zugrunde, einen Zuschlag stoff für insbesondere wärmedämmende Baustoffe zu schaf fen, der mit niedriger Schüttdichte kostengünstig her stellbar ist und über hinreichende mechanische Festig keits- und Wärmedämmungseigenschaften verfügt.The invention has for its object a surcharge Sheep for especially thermal insulation building materials fen, the low bulk density inexpensively is adjustable and has sufficient mechanical strength and thermal and insulation properties.

Zur Lösung dieser Aufgabe zeichnet sich der Zuschlagstoff nach der Erfindung durch die im kennzeichnenden Teil des Anspruchs 1 angegebenen Merkmale aus. Hinsichtlich vor teilhafter Ausgestaltungen des Zuschlagstoffes nach der Erfindung wird auf die Ansprüche 1 bis 11 verwiesen. Ein Verfahren zur Herstellung eines solchen Zuschlagstoffes ist in den Ansprüchen 12 und 13 angegeben.The aggregate excels in solving this task according to the invention by the in the characterizing part of Claim 1 specified features. Regarding before partial configurations of the aggregate after the Invention is referred to claims 1 to 11. On Process for the production of such an aggregate is specified in claims 12 and 13.

Durch die Einbindung feinteiliger Perlite - oder Vermiculitepartikel in pulverförmige Mineralstoffe und deren Verfestigung bzw. Bindung des daraus hergestellten Stoffgemisches durch ein Bindemittel aus einer wäßrigen Polymerdispersion, beispielsweise ein Bindemittel aus einer wäßrigen Vinylacetatdispersion und/oder Acrylatdis persion wurde überraschenderweise ein druckfester leichter Zuschlagstoff gefunden, der über eine hervorragende mechanische Festigkeit und darüber hinaus auch noch über sehr gute Wärmedämmungseigenschaften verfügt. Darüber hinaus ist der erfindungsgemäße Zuschlagstoff hervorragend zu verarbeiten und darüber hinaus auch noch außerordentlich kostengüstig herstellbar.By integrating finely divided perlite - or Vermiculite particles in powdered minerals and their consolidation or binding of the manufactured from it Mixture of substances by a binder from an aqueous Polymer dispersion, for example a binder an aqueous vinyl acetate dispersion and / or acrylate dis surprisingly, persion became a pressure-resistant lighter Found aggregate that has an excellent mechanical strength and beyond has very good thermal insulation properties. About that In addition, the aggregate according to the invention is excellent to process and beyond extremely inexpensive to manufacture.

Die Perlite - bzw. Vermiculitepartikel in Korngrößen < 1000 Mikron, vorzugsweise < 500 Mikron, sind zunächst mit einem mineralischen Füllstoff, beispielsweise Kalkstein mehl, Kreide und/oder Zement zu einer homogenen Mischung aufzubereiten und z. B. in einer Granuliertrommel mit einer wäßrigen Vinylacetatdispersion oder einer Acrylharzdis persion zu besprühen. Dabei bilden sich Granulate in einer gewünschten Korngröße. Das so gewonnene Naßgranulat kann in einem Heißluftstrom bei z. B. ca. 120° getrocknet wer den, wobei die Verfestigung der Granulate durch Filmbil dung aus polymerisierter Dispersion bewirkt wird. Damit können abriebfeste und quasi staubfreie Granulate in ge rundeter Kornstruktur gewonnen werden. Das auf eine Rest feuchte von ca. 2% getrocknete Granulat kann über eine Siebmaschine geleitet und in die gewollten Korngrößen fraktioniert werden. Etwa anfallendes Überkorn kann aufge mahlen und zusammen mit Unterkorn und Filterstaub als Feingut in die Ausgangsmischung zurückgeführt werden, so daß im vollautomatischen Produktionsablauf Abfall nicht entsteht.The perlite or vermiculite particles in grain sizes <1000 microns, preferably <500 microns, are initially with a mineral filler, for example limestone flour, chalk and / or cement to a homogeneous mixture prepare and z. B. in a granulating drum with a aqueous vinyl acetate dispersion or an acrylic resin dis to spray persion. Granules form in one desired grain size. The wet granules obtained in this way can in a hot air stream at z. B. dried about 120 ° the, whereby the solidification of the granules by film is effected from polymerized dispersion. In order to can be abrasion-resistant and quasi dust-free granules in ge rounded grain structure can be obtained. That on a rest moist granules of approx. 2% can be dried over a Screened machine and in the desired grain sizes be fractionated. Any oversize can accumulate grind and together with undersize and filter dust as Fines are returned to the starting mixture, see above that there is no waste in the fully automated production process arises.

Der erfindungsgemäße Leichtzuschlagstoff weist neben sei nem niedrigen Schüttgewicht und demzufolge hervorragenden wärmedämmenden Eigenschaften eine hohe Gleichmäßigkeit auf und ist gegenüber herkömmlichen Leichtzuschlagsstoffen na hezu frei von etwaigen Verunreinigungen, die im fertigen Putz zu Verfärbungen und dergleichen führen könnten.The light aggregate according to the invention has besides be low bulk density and therefore excellent thermal insulation properties a high uniformity and is na compared to conventional light aggregates so free of any impurities in the finished Plaster could lead to discoloration and the like.

Die Erfindung wird nachfolgend anhand einiger Ausführungs beispiele erläutert:The invention is described below with the aid of some embodiments examples explained:

example 1

Der Leichtzuschlagstoff besteht aus einem Stoffgemisch aus 35 Gew.-% Perlite (< 1,0 mm) und 65 Gew.-% Kreide. Dieses Stoffgemisch wird mit einer wäßrigen Dispersion, be stehend aus 10 Gew.-% Polyvinylacetat und 90% Wasser, granuliert. Die eingesetzte Dispersionsmenge beträgt dabei 60% der Stoffgemischmenge. Der getrocknete Zuschlagstoff hat eine Schüttdichte von 200 g/l.The lightweight aggregate consists of a mixture of substances 35% by weight perlite (<1.0 mm) and 65% by weight chalk. This Mixture of substances with an aqueous dispersion, be consisting of 10% by weight polyvinyl acetate and 90% water, granulated. The amount of dispersion used is 60% of the amount of substance mixture. The dried aggregate has a bulk density of 200 g / l.

Example 2

Der Zuschlagstoff besteht aus einem Stoffgemisch aus 15 Gew.-% Perlite (< 1 mm) und 85 Gew.-% Kalksteinmehl. Dieses Stoffgemisch wird mit einer wäßrigen Dispersion, bestehend aus 12,5 Gew.-% Polyvinylacetat und 87,5 Gew.-% Wasser, granuliert. Die eingesetzte Dispersionsmenge be trägt dabei 30% der Stoffgemischmenge. Der getrocknete Zuschlagstoff hat eine Schüttdichte von 400 g/l.The aggregate consists of a mixture of substances 15% by weight perlite (<1 mm) and 85% by weight limestone powder. This mixture of substances is mixed with an aqueous dispersion, consisting of 12.5% by weight polyvinyl acetate and 87.5% by weight Water, granulated. The amount of dispersion used carries 30% of the amount of substance mixture. The dried one Aggregate has a bulk density of 400 g / l.

Example 3

Der Zuschlagstoff besteht aus einem Stoffgemisch aus 22,5 Gew.-% Perlite (< 1,0 mm) und 77,5 Gew.-% Zement. Das Stoffgemisch wird granuliert mit einer wäßrigen Dis persion, bestehend aus 10 Gew.-% Acrylat-Copolimerisat und 90 Gew.-% Wasser. Der getrocknete Zuschlagstoff hat eine Schüttdichte von 250 g/l.The aggregate consists of a mixture of substances 22.5% by weight perlite (<1.0 mm) and 77.5% by weight cement. The mixture of substances is granulated with an aqueous dis persion, consisting of 10% by weight of an acrylic copolymer and 90% by weight of water. The dried aggregate has one Bulk density of 250 g / l.

Example 4

Der Zuschlagstoff besteht aus einem Stoffgemisch, 20 Gew.-% Perlite (< 1 mm) und 80 Gew.-% Kalksteinmehl. Dieses Stoffgemisch wird mit einer wäßrigen Dispersion granuliert, bestehend aus 10 Gew.-% Acrylat-Copolymerisat und 90 Gew.-% Wasser. Die eingesetzte Dispersionsmenge be trägt 40% der Stoffgemischmenge. Die getrocknete Körnung hat eine Schüttdichte von 300 g/l.The aggregate consists of a mixture of substances, 20 % By weight perlite (<1 mm) and 80% by weight limestone powder. This mixture of substances is mixed with an aqueous dispersion granulated, consisting of 10 wt .-% acrylate copolymer and 90 wt% water. The amount of dispersion used carries 40% of the amount of substance mixture. The dried grain has a bulk density of 300 g / l.

Claims

1. Additive for heat-insulating building materials, in particular for structure-forming interior and exterior plasters, characterized by a mixture of expanded perlite or vermiculite particles in grain sizes of less than 1000 microns and a mineral filler, which is bound in a granular form by a binding agent from an aqueous polymer dispersion.

2. Aggregate according to claim 1, characterized by a Mixture of substances with a perlite or vermiculite particle proportion of 10 to 35 wt .-%.

3. Aggregate according to claim 2, characterized by egg Perlite or vermiculite particle content of 20 wt .-%.

4. Aggregate according to one of claims 1 to 3, characterized characterized in that the mixture of perlite or Ver Miculite particle proportions with a grain size <500 microns having.

5. Aggregate according to one of claims 1 to 4, characterized characterized in that the mixture of substances to 65 to 90 wt .-% has a filler.

6. aggregate according to claim 5, characterized in that that the mixture of substances contains limestone powder as a filler.

7. aggregate according to claim 5, characterized in that that the mixture of substances has chalk as a filler.

8. aggregate according to claim 5, characterized in that the mixture of substances as a filler is a mixture of Ze ment and limestone flour or chalk.

9. aggregate according to claim 8, characterized in that the filler 30 to 40 wt .-% cement and 25 to 60 Wt .-% limestone flour or chalk.

10. Aggregate according to one of claims 1 to 9, there characterized in that the mixture of substances by a bandage medium from an aqueous polyvinyl acetate dispersion a solids content of 8% to 12.5% is bound.

11. Aggregate according to one of claims 1 to 9, there characterized in that the mixture of substances by an aq acrylic copolymer dispersion with a solid content of 8 to 12.5%.

12. Process for producing an aggregate for heat-insulating building materials, especially for structural interior and External plasters, preferably for the production of a Zu impact material according to claim 1, characterized in that a mixture of expanded perlite or Vermiculite particles in grain sizes <1000 microns with mineral fillers to form a mixture of substances rides and by spraying with an aqueous polymer Process dispersion into granules in a granulating drum is riding through drying in a hot air stream pressure-resistant, water and alkali-resistant grits harden.

13. The method according to claim 12, characterized in that the pelletizing takes place in a pelletizing drum variable with increasing angle to the discharge side is judgable.