DE438391C - Process for separating magnesium from alloys or mixtures - Google Patents
Process for separating magnesium from alloys or mixturesInfo
- Publication number
- DE438391C DE438391C DER64194D DER0064194D DE438391C DE 438391 C DE438391 C DE 438391C DE R64194 D DER64194 D DE R64194D DE R0064194 D DER0064194 D DE R0064194D DE 438391 C DE438391 C DE 438391C
- Authority
- DE
- Germany
- Prior art keywords
- magnesium
- alloys
- zinc
- mixtures
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zum Abscheiden von Magnesium aus Legierungen oder Mischungen. Die Erfindung bezieht sich auf die- Abscheidung von Magnesium aus Legierungen oder Gemischen, die Magnesium enthalten. Wenn z. B. ein überfluß an Magnesiumlegierungen vorhanden ist, kann der Magnesiumgehalt der Legierung wertvoller, d. h. das Magnesium stärker begehrt sein als die Legierung selber. Die Erfindung erstrebt ein billiges. und zweckmäßiges Verfahren, um die Scheidung des Magnesiums von anderen Elementen, mit denen es verbunden oder gemischt ist, zu bewirken.Process for separating magnesium from alloys or mixtures. The invention relates to the deposition of magnesium from alloys or Mixtures containing magnesium. If z. B. an abundance of magnesium alloys is present, the magnesium content of the alloy may be more valuable, e.g. H. the magnesium be more in demand than the alloy itself. The invention aims for a cheap one. and expedient procedure for separating magnesium from other elements, with which it is associated or mixed to effect.
Das Verfahren hat sich besonders zweckmäßig für Magnesiumlegierungen oder -gemische erwiesen, die Zink oder ähnliche Metalle, z. B. Antimon, enthalten, und soll daher in seiner Anwendung auf solche Legierungen oder Gemische beschrieben werden.The method has proven particularly useful for magnesium alloys or mixtures have been shown to contain zinc or similar metals, e.g. B. antimony, contain, and is therefore intended to be described in its application to such alloys or mixtures will.
Magnesium widersteht auch noch oberhalb seiner Schmelztemperatur in bestimmten Grenzen vollständig dem Angriff von kaustischen Alkalien, z. B. Ätznatrium oder Ätzkalium, und bleibt von ihnen unbeeinflußt; dagegen reagieren Metalle, wie Zink und ähnliche, leicht mit einem kaustischen Alkali.Magnesium resists in even above its melting temperature certain limits completely to the attack of caustic alkalis, e.g. B. Caustic Sodium or caustic potassium, and remains unaffected by them; on the other hand, metals react, like Zinc and the like, lightly with a caustic alkali.
Kurz gesagt, besteht die Erfindung darin, die Legierung oder das Gemisch der Einwirkung von geschmolzenem kaustischen Alkali zu unterwerfen, wodurch das Zink oder ähnliche Metalle, z. B. Antimon, in der behandelten Legierung oder Mischung mit dem kaustischen Alkali reagieren und sich im Laufe der Reaktion das Magnesium selbst von dem oder den anderen Metallen trennt und unverbunden mit dem Alkali zurückbleibt.In short, the invention is the alloy or the mixture to the action of molten caustic alkali, whereby the Zinc or similar metals, e.g. B. antimony, in the alloy or mixture being treated react with the caustic alkali and in the course of the reaction the magnesium separates itself from the other metal or metals and remains unconnected with the alkali.
Es ist bekannt, zur Herstellung von aluminiumfreien Metallen und Legierungen das Aluminium von den anderen Metallen, insbesondere Zink, durch Oxydation mittels sauerstoffabgebender Körper zu entfernen. Als Sauerstoffträger wurden unter anderen Karbonate und Hydroxyde der Alkalien verwendet und das Aluminium als. Aluminat aus dem Metallbad abgeschieden. Die Menge des. zugesetzten Alkalis mußte dabei dem Aluminiumgehalt der Legierung entsprechen, um die Bildung von Zinkat zu vermeiden.It is known for the production of aluminum-free metals and alloys the aluminum from the other metals, especially zinc, by means of oxidation remove oxygen-releasing bodies. As oxygen carriers were among others Carbonates and hydroxides of the alkalis are used and the aluminum as. Aluminate deposited in the metal bath. The amount of alkali added had to correspond to the aluminum content match the alloy in order to avoid the formation of zincate.
überraschenderweise gelingt es nach der Erfindung, aus Legierungen des, Magnesiums mit Zink oder ähnlichen Metallen das Magnesium von diesen durch Behandeln mit kaustischen Alkalien zu trennen, ohne daß das Magnesium oxydiert wird.Surprisingly, according to the invention, it is possible to use alloys des, magnesium with zinc or similar metals through the magnesium of these Treat with caustic alkalis to separate without oxidizing the magnesium.
Die Arbeitsweise ist folgende: In einem Kessel aus Gußeisen oder anderem geeigneten Stoff wird eine geeignete Menge Magnesium-Zink-Legierung (95 Prozent Magnesium und 5 Prozent Zink) der Einwirkung von kaustischern Alkali im überschuß zu der vorhandenen Zinkmenge bei ungefähr 620'C ausgesetzt. Zur guten Durchmischung der Reaktionsstoffe ist ein Rührwerk vorgesehen. Die Anfangstemperatur wird so hoch gewählt, daß sie zur Einleitung der Reaktion genügt, da der Prozeß exothermisch verläuft und während der Reaktion genügend Wärme zur Durchführung des Verfahrens. geliefert wird. Das Reaktionsgefäß ist in bekannter Weise gegen Luftzutritt abgeschlossen. Für die Abführung des während der Reaktion entwickelten Wasserstoffes ist gesorgt. Nach beendigter Reaktion schwimmt Magnesium mit g9,y Prozent Reimgehalt an die Oberfläche der entstandenen Kalium-Zink-Verbindung (Kaliumzinkat) und kann in bekannter Weise aus dem Kessel abgezogen werden.The procedure is as follows: In a cauldron made of cast iron or other suitable material, a suitable amount of magnesium-zinc alloy (95 percent magnesium and 5 percent zinc) is exposed to caustic alkali in excess of the amount of zinc present at about 620 ° C. A stirrer is provided for thorough mixing of the reactants. The initial temperature is chosen so high that it is sufficient to initiate the reaction, since the process is exothermic and there is sufficient heat during the reaction to carry out the process. is delivered. The reaction vessel is sealed in a known manner against the ingress of air. The hydrogen evolved during the reaction is removed from the system. When the reaction is complete, magnesium with a concentration of 9.8 percent rime floats on the surface of the resulting potassium-zinc compound (potassium zincate) and can be withdrawn from the boiler in a known manner.
Die Legierung oder das Gemisch kann dem geschmolzenen kaustischen Alkali in festem oder in geschmolzenem Zustande zugeführt werden. Bei der eintretenden Reaktion entwickelt sich @N?asserstoff, so daß Sorge getragen werden muß, die Legierung allmählich und nicht in einer für den angewendeten Apparat übermäßigen Menge zuzuführen.The alloy or mixture may be the molten caustic Alkali can be supplied in a solid or in a molten state. When entering Reaction develops hydrogen so care must be taken with the alloy to be added gradually and not in an excessive amount for the apparatus used.
Das Zink oder sonstige, im kaustischen Alkali lösliche Metalle der Legierung reagieren sofort mit dem Alkali zu einer Zink- oder entsprechenden Verbindung und Wasserstoff, und die Neutralität des MagnesiumsgegenkaustischesAlkali bewirkt, da.ß das Magnesium in -Gegenwart des naszierenden Wasserstoffes sich in praktisch reinem Zustande abscheidet und an der Oberfläche schwimmt, wo es leicht abgenommen werden kann.The zinc or other metals soluble in the caustic alkali Alloys react immediately with the alkali to form a zinc or equivalent compound and hydrogen, and the neutrality of the magnesium counter-caustic alkali causes that the magnesium in the presence of the nascent hydrogen becomes practical in a pure state and floats on the surface where it is easily removed can be.
Da alles durch elektrolytische Zerlegung gewonnene Magnesium vor dem Verkauf als Handelsware oder vor seiner Benutzung für Legierungen gereinigt werden muß, kann es zweckmäßig sein, solchem Rohmagnesium einen kleinen Prozentsatz Zink oder ähnliches Metall zuzusetzen und dann die oben beschizebene Reinigung mit kaustischem Alkali vorzunehmen.Since all magnesium obtained by electrolytic decomposition before the Sold as a commodity or cleaned for alloys before use it may be appropriate to add a small percentage of zinc to such raw magnesium or similar metal and then the above-mentioned cleaning with caustic Make alkali.
Auf diese Z` eise kann Magnesium in sehr reinem Zustande mit sehr .einfacher Apparatur hergestellt werden.In this way, magnesium in a very pure state can be used with very .Simple apparatus can be produced.
Claims (1)