DE4011204A1 - Mouth-guard material with improved manipulating properties etc. - comprises mixt. of EVA copolymer and thermoplastic polycaprolactone, opt. with PVAC, pigments and perfumes - Google Patents
Mouth-guard material with improved manipulating properties etc. - comprises mixt. of EVA copolymer and thermoplastic polycaprolactone, opt. with PVAC, pigments and perfumesInfo
- Publication number
- DE4011204A1 DE4011204A1 DE19904011204 DE4011204A DE4011204A1 DE 4011204 A1 DE4011204 A1 DE 4011204A1 DE 19904011204 DE19904011204 DE 19904011204 DE 4011204 A DE4011204 A DE 4011204A DE 4011204 A1 DE4011204 A1 DE 4011204A1
- Authority
- DE
- Germany
- Prior art keywords
- polycaprolactone
- pvac
- perfumes
- mouthguard
- mouth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die vorliegende Erfindung betrifft eine Mundschutzmasse, die eine gute Verformbarkeit, Viskoelastizität und Schlagfestigkeit besitzt und sich zum Schützen der Zähne, Kieferknochen und der intraoralen Gewebe gegenüber der Einwirkung von äußeren Kräften geignet.The present invention relates to a mouthguard, the good ductility, viscoelasticity and Has impact resistance and protects the teeth, Jawbone and the intraoral tissue opposite the Suitable for external forces.
Verletzungen erfolgen häufig bei der Ausübung von sportlichen Betätigungen, wie Boxen, Rugby oder Football. Die meisten Verletzungen beruhen auf einer Fraktur der Zähne und Kieferknochen. Das Schützen des Inneren des Mundes gegenüber derartigen äußeren Einwirkungen verlangt ein Material mit einer geeigneten Festigkeit gegenüber äußeren Kräften sowie einer Pufferwirkung gegenüber der Einwirkung von äußeren Drücken.Injuries are common in the exercise of sports activities, such as boxing, rugby or football. Most injuries are due to a fracture of the teeth and jawbones. Protecting the interior of the Mouth against such external influences required a material of suitable strength external forces and a buffer effect against the Action of external pressures.
Für derartige Schutzmaterialien (Mundschutz) wurden im allgemeinen Polyvinylchlorid (PVC), insbesondere Ethylen/Vinylacetat-Copolymere (PVAc-PE) verwendet.For such protective materials (mouth protection) were in general polyvinyl chloride (PVC), in particular Ethylene / vinyl acetate copolymers (PVAc-PE) used.
Da die intraoralen Abmessungen von einer Person zu der anderen schwanken, müssen die Mundschutzmaterialien sich den verschiedenen Abmessungen anpassen und eine geeignete Elastizität besitzen sowie einen ausreichenden Schutz gegenüber äußerem Druck ausüben.Because the intraoral dimensions of a person to the other, the mouthguard materials have to vary adapt to different dimensions and appropriate Have elasticity and adequate protection to exert external pressure.
Darüber hinaus müssen die Mundschutzmaterialien in solchen Formen geliefert werden, daß es dem Zahntechniker möglich ist, in einfacher Weise einzelnen Personen den Mundschutz anzupassen, wobei der Mundschutz sauber, geschmacklich einwandfrei und dauerhaft sein muß, wobei es auch möglich sein muß, Worte klar auszudrücken.In addition, the mouthguard materials must be in such Shapes are supplied that allow the dental technician is, in a simple way, individual persons the mouthguard adjust, with the mouthguard clean, flavorful must be flawless and durable, and it is also possible must be to express words clearly.
Die Anforderungen, die an Materialien gestellt werden, die zum Schützen der Zähne, Kieferknochen etc. verwendet werden, bestehen darin, daß sie Bißdrucken widerstehen, einfach zu tragen sind, äußere Drücke zur Erzielung eines ausreichenden Schutzes abpuffern, in zuverlässiger Weise lieferbar sind, leicht herzustellen sind und eine gute Dauerhaftigkeit besitzen. Von den physikalischen Eigenschaften, die derartige Bedingungen erfüllen, seien die Elastizität, die Zugfestigkeit und die Dehnung sowie ein Entspannen nach der Einwirkung von äußeren Drücken und die Dauerhaftigkeit erwähnt. Das Ausmaß der Wasserabsorption gibt den Stabilitätsgrad der Materialien wieder. The requirements that are placed on materials that to be used for protecting the teeth, jawbones etc. are that they resist biting, just too bear external pressures to achieve adequate Buffer protection, are available in a reliable manner, are easy to produce and have a good durability have. From the physical properties, the meet such conditions are the elasticity, the Tensile strength and elongation, as well as relaxing after the Exposure to external pressures and durability mentioned. The extent of water absorption gives the Stability of the materials again.
Im allgemeinen besitzen verfügbare Produkte eine Härte von 50 bis 90, eine Zugfestigkeit von 30 bis 200 kg/cm2, eine Dehnung von 300 bis 900% und eine Wasserabsorption von 0,5 bis 2,5%.In general, available products have a hardness of 50 to 90, a tensile strength of 30 to 200 kg / cm 2 , an elongation of 300 to 900% and a water absorption of 0.5 to 2.5%.
Für Mundschutzzwecke wurden Polyvinylchlorid (PVC) oder Ethylen/Vinylacetat-Copolymere (PVAc-PE) als Komponenten erwähnt.For oral protection purposes, polyvinyl chloride (PVC) or Ethylene / vinyl acetate copolymers (PVAc-PE) as components mentioned.
PVC (Polyvinylchlorid) neigt zu einem Abbau durch Wärme, Licht etc. und besitzt keine ausreichende Dauerfestigkeit. Aus diesem Grunde enthält dieses Material gewöhnlich ein Stabilisierungsmittel und wird zusätzlich mit einem Weichmacher vermischt, um seine Erweichungstemperatur einzustellen. Derartige Regulatoren sind jedoch aufgrund der Tatsache, daß sie aus dem Material austreten, für den menschlichen Körper schädlich.PVC (polyvinyl chloride) is prone to degradation by heat, Light etc. and does not have sufficient fatigue strength. For this reason, this material usually contains one Stabilizer and is additionally with a Softener mixed to its softening temperature adjust. However, such regulators are due to the Fact that they emerge from the material for which harmful to human body.
PVAc-PE (Ethylen/Vinylacetat-Copolymere), deren Härte und Elastizität durch den Polymerisationsgrad und das Verhältnis von Polyethylen zu Polyvinylacetat gesteuert werden, werden relativ oft als Mundschutz verwendet. Jedoch kann PVAc-PE nur bei einer Temperatur von 80 bis 100°C erweicht und verformt werden, wobei der Polymerisationsgrad und das Verhältnis von Polyvinylacetat zu Polyethylen auf spezifische Bereiche begrenzt ist, damit eine gute Schlagfestigkeit und ein Schutz der Zähne und Kieferknochen sowie eine Anpassung an die Zähne gegeben ist. Ein anderes gravierendes Problem im Falle von PVAc-PE besteht darin, daß dieses Material eine schlechte Dauerfestigkeit und Festigkeit besitzt, infolge der hohen Erweichungstemperatur für die Handhabung zu heiß wird und zu einem Kleben an der Hand beim Verformen neigt. Aufgabe der vorliegenden Erfindung ist die Schaffung einer Mundschutzmasse, die thermoplastisches Polycaprolacton enthält, äußere Drücke abzupuffern vermag, die Zähne und Kieferknochen schützt, sich leicht anpassen läßt, eine gute Dauerfestigkeit und Festigkeit besitzt, sich nicht ablöst und nicht an den Händen anklebt, so daß der Verarbeiter dieses Material in einfacher Weise handhaben kann, wobei es bei einer gesteuerten tiefen Temperatur erweicht werden kann und außerdem nicht die Verwendung von Additiven erforderlich ist, die einen schädlichen Einfluß auf den menschlichen Körper ausüben, wie Weichmacher, Stabilisierungsmittel und Lösungsmittel.PVAc-PE (ethylene / vinyl acetate copolymers), their hardness and Elasticity by the degree of polymerization and the ratio be controlled from polyethylene to polyvinyl acetate relatively often used as a mouthguard. However, PVAc-PE can only softened at a temperature of 80 to 100 ° C and be deformed, the degree of polymerization and the Ratio of polyvinyl acetate to polyethylene on specific areas is limited, thus a good Impact resistance and protection of teeth and jawbones as well as an adaptation to the teeth is given. Another serious problem in the case of PVAc-PE is that This material has poor fatigue strength and Has strength, due to the high softening temperature becomes too hot for handling and sticking to the Hand when deforming tends. Task of the present Invention is the creation of a mouthguard that contains thermoplastic polycaprolactone, external pressures can buffer, protects the teeth and jawbones, easy to adapt, good fatigue life and Has strength, does not peel off and not on the Sticks hands so that the fabricator of this material in easy to handle, it is at a controlled low temperature can be softened and It also does not require the use of additives is that has a detrimental influence on the human Exercise body, such as plasticizers, stabilizers and Solvent.
Die thermoplastischen elastischen Polymeren, die für den erfindungsgemäßen Mundschutz verwendet werden können, müssen mit anderen Harzen verträglich sein und eine chemische Stabilität, Elastizität und Thermoplastizität besitzen. Geeignet für diesen Zweck sind Ethylen/Vinylacetat- Copolymere oder Mischungen davon mit Polyvinylacetat. Gegebenenfalls können derartige thermoplastische elastische Polymere durch Polycaprolacton gesteuert werden.The thermoplastic elastic polymers used for the Mouthguard according to the invention may be used be compatible with other resins and a chemical Possess stability, elasticity and thermoplasticity. Suitable for this purpose are ethylene / vinyl acetate Copolymers or blends thereof with polyvinyl acetate. Optionally, such thermoplastic elastic Polymers are controlled by polycaprolactone.
Die Ethylen/Vinylacetat-Copolymeren und das Polyvinylacetat besitzen einen derartig hohen Erweichungspunkt, daß sie zum Zeitpunkt der Preßverformung zu heiß werden. Außerdem ist ihr Haftvermögen so ausgeprägt, daß sie an der Hand ankleben. Ferner besitzen sie keine Dauerhaftigkeit und eine derartig schlechte Festigkeit, daß sie sich leicht ablösen. Daher ist es schwierig derartige Polymere in einer Qualität einzustellen, die für Mundschutzzwecke geeignet ist, so daß es bisher unmöglich war, einen Mundschutz mit zufriedenstellenden Eigenschaften zu erhalten.The ethylene / vinyl acetate copolymers and the polyvinyl acetate have such a high softening point that they Time of compression deformation to be too hot. Besides that is her grip is so pronounced that she's by the hand glue. Furthermore, they have no durability and a such poor strength that they peel off easily. Therefore, it is difficult to obtain such polymers in a quality which is suitable for oral protection purposes, so that It was previously impossible to use a surgical mask to obtain satisfactory properties.
Die Erfindung beruht auf der Feststellung, daß die vorstehenden Nachteile im wesentlichen durch den Einsatz eines thermoplastischen Polycaprolactons in Mundschutzmassen beseitigt werden können, wobei ein Polycaprolacton eingesetzt wird, das bei einer Temperatur von nur 60°C weich wird, nicht an der Hand anklebt, und eine hohe Stabilität und Festigkeit besitzt.The invention is based on the finding that the above disadvantages essentially by the use a thermoplastic polycaprolactone in mouthguards can be eliminated using a polycaprolactone is used, which softens at a temperature of only 60 ° C. does not stick to the hand, and high stability and strength.
Insbesondere wird durch die Erfindung eine Mundschutzmasse geschaffen, aus einer Kombination aus Ethylen/Vinylacetat copolymerem und einer Mischung davon mit Polyvinylacetat mit einem thermoplastischen Polycaprolacton, dessen Erweichungs punkt ungefähr 60°C und dessen durchschnittliches Molekulargewicht 10 000 bis 100 000 beträgt.In particular, the invention provides a mouthguard composition created from a combination of ethylene / vinyl acetate copolymer and a mixture thereof with polyvinyl acetate a thermoplastic polycaprolactone whose softening point about 60 ° C and its average Molecular weight is 10,000 to 100,000.
Das Polycaprolacton, das erfindungsgemäß geeignet ist, läßt sich durch die folgende Strukturformel wiedergeben:The polycaprolactone which is suitable according to the invention leaves to be represented by the following structural formula:
Damit die Vorteile des thermoplastischen Caprolactons zum Schutz der Zähne und Kieferknochen sowie zur Erzielung einer geeigneten Erweichungsverarbeitungstemperatur ausgeschöpft werden, sollte seine Menge wenigstens 4,0 Gew.-% betragen. Liegt die Menge des thermoplastischen Polycaprolactons in der Mundschutzmasse unterhalb 4,0 Gew.-%, dann ist es schwierig, die Erweichungstemperatur auf unterhalb 80°C herabzusetzen und ein Kleben der Masse an der Hand und an den Fingern zu vermeiden. Wird das thermoplastische Polycaprolacton der Mundschutzmasse in einer Menge von mehr als 50 Gew.-% zugesetzt, dann wird die Zähigkeit der Masse verbessert und die Masse läßt sich leichter erweichen, da ihr Erweichungspunkt abfällt, wobei ihr Haftvermögen verringert wird, während es andererseits schwierig wird, den Zähnen und Kieferknochen einen ausreichenden Schutz zu verleihen, da die Masse zu hart ist, um ausreichend äußere Drücke abzupuffern.So that the advantages of the thermoplastic caprolactone for Protection of teeth and jawbone and to achieve a suitable softening processing temperature exhausted should be at least 4.0 wt .-% amount. If the amount of thermoplastic polycaprolactone is in the mouthguard below 4.0 wt .-%, then it is difficult, the softening temperature below 80 ° C. minimize and gluing the earth to the hand and on to avoid the fingers. Will the thermoplastic Polycaprolactone of the mouthguard in an amount of more added as 50 wt .-%, then the toughness of the mass improved and the mass is easier to soften because their softening point drops, with their grip is reduced, while on the other hand it is difficult, the Teeth and jawbone provide adequate protection too lend because the mass is too hard to sufficiently outer To buffer pressures.
Daher liegt die maximale Menge des thermoplastischen Polycaprolactons, das erfindungsgemäß verwendet wird, in geeigneter Weise bei 50,0 Gew.-%. Dies bedeutet mit anderen Worten, daß die Menge des thermoplastischen Polycaprolactons, das erfindungsgemäß verwendet wird, auf einen Bereich von 4,0 bis 50,0 Gew.-% beschränkt ist.Therefore, the maximum amount of thermoplastic is Polycaprolactone, which is used in the invention, in Suitably at 50.0 wt .-%. This means with others Words that the amount of thermoplastic Polycaprolactone, which is used in the invention, on a range of 4.0 to 50.0 wt .-% is limited.
Der Erweichungspunkt kann bis auf 60 bis 80°C herabgesetzt werden durch Einmengung eines Polycaprolactons mit einem Molekulargewicht von 10 000 bis 100 000 und einer Menge von 4,0 bis 50,0 Gew.-%.The softening point can be reduced to 60 to 80 ° C be by mixing a polycaprolactone with a Molecular weight of 10,000 to 100,000 and an amount of 4.0 to 50.0% by weight.
Zum Färben der Mundschutzmassen gemäß vorliegender Erfindung sollten öllösliche Farbstoffe und Pigmente verwendet werden, die keine Reizwirkung ausüben und nicht toxisch sind und in Wasser unlöslich sind.For dyeing the mouth protection compositions according to the present invention oil-soluble dyes and pigments should be used, which have no irritating effect and are not toxic and in Water are insoluble.
Beispielsweise können als öllösliche Farbstoffe C.I.-Lösungsmittel-Gelb-2, -14 oder -15, C.I.-Lösungsmittel- Orange-2, C.I.-Dispersrot-9, C.I.-Lösungsmittel-Violett-13 oder -14, C.I.-Dispersviolett-1, C.I.-Lösungsmittel-Blau-12, C.I.-Lösungsmittel-Braun-37 und C.I.-Lösungsmittel-Schwarz-3 oder -5 verwendet werden.For example, as oil-soluble dyes C.I. Solvent Yellow 2, 14 or 15, C.I. Orange-2, C.I. Disperse Red-9, C.I. Solvent Violet-13 or -14, C.I. Disperse Violet 1, C.I. Solvent Blue 12, C.I. Solvent Brown-37 and C.I. Solvent Black-3 or -5 can be used.
Die verwendeten Pigmente können entweder organisch oder anorganisch sein. Geeignet als organische Pigmente sind beispielsweise anilinschwarz, naphtholgelb-S, benzidingelb, chinolingelb, anthrapyrimidingelb, sudan-I, permanentorange, indanthrenbriliantorange-GR, permanentbraun, parabraun, permanentrot-4R, pararot, feuerrot, fastviolett-B, methyl violett, dioxazinviolett, alkaliblau, pfaublau, fastskyblue, indigo und pigmentgrün-B. Die anorganischen Pigmente können beispielsweise aus Barytpulvern, Bariumcarbonat, Siliziumdioxidpulvern, Aluminiumoxidweiß, Zinkweiß, Titandioxid, Ruß, gelbem Eisenoxid, Ocker, Eisenoxid, rotem Eisenoxid, Ultramarinblau und Aluminiumpulvern bestehen.The pigments used can be either organic or be inorganic. Suitable as organic pigments for example, aniline black, naphthol yellow S, benzidine yellow, quinoline yellow, anthrapyrimidine yellow, sudan I, permanent orange, indanthrenbriliantorange-GR, permanent brown, parabraun, Permanentrot-4R, Para Red, Fire Red, Fast Violet B, methyl violet, dioxazine violet, alkali blue, peacock blue, fastskyblue, indigo and pigment green-B. The inorganic pigments can for example from barite powders, barium carbonate, Silica powders, alumina white, zinc white, Titanium dioxide, carbon black, yellow iron oxide, ocher, iron oxide, red Iron oxide, ultramarine blue and aluminum powders exist.
Eines oder zwei oder mehrere derartige Pigmente, wie sie vorstehend erwähnt wurden, können den erfindungsgemäßen Mundschutzmassen in Spurenmengen zugesetzt werden.One or two or more such pigments as they have been mentioned above, the inventive Mouthguard masses are added in trace amounts.
Jedes Parfüm, das einen Flammpunkt von 80°C oder darüber und einen Siedepunkt von 150°C oder darüber besitzt und keine Reizwirkung ausübt, kann verwendet werden.Any perfume that has a flashpoint of 80 ° C or above and has a boiling point of 150 ° C or above and none Irritating effect can be used.
Geeignete natürliche Parfüme sind beispielsweise Sinnamonöl, Anisettöl, Zimtöl, Patschuliöl, Sandelholzöl und Pfefferminzöl. Geeignete synthetische Parfüme sind beispiels weise 3-Ocentol, cis-3-Hexenol, Linaloolgeraniol, Nerol, Rosinol, Hydroxycitronellol, alpha-Terpineol, alpha-Menthol, λ-Carvon, p-Methylacetophenon, Benzylbutyrat, Benzylalkohol, Phenylethylalkohol, Cinnamylalkohol, Dimethylbenzylcarbinol, Acetylanisol, Eugenol, Aldehyd-C-14, Aldehyd-C-16, Aldehyd-C-18, Aldehyd-C-20 und dergleichen.Suitable natural perfumes are, for example, Sinnamon oil, aniseed oil, cinnamon oil, patchouli oil, sandalwood oil and peppermint oil. Suitable synthetic perfumes are, for example, 3-Ocentol, cis-3-hexenol, linaloolgeraniol, nerol, rosinol, hydroxycitronellol, alpha-terpineol, alpha-menthol, λ- carvone, p-methylacetophenone, benzyl butyrate, benzyl alcohol, phenylethyl alcohol, cinnamyl alcohol, dimethylbenzylcarbinol, Acetylanisole, eugenol, aldehyde-C-14, aldehyde-C-16, aldehyde-C-18, aldehyde-C-20 and the like.
Eines, zwei oder mehrere der vorstehend erwähnten Parfüme können vermischt und den erfindungsgemäßen Mundschutzmassen in Spurenmengen zugesetzt werden.One, two or more of the above-mentioned perfumes can be mixed and the mouthguards of the invention be added in trace amounts.
Die erfindungsgemäße Mundschutzmasse kann direkt in der Mundkavität des Verbrauchers erweicht und verpreßt und damit gut angepaßt werden. Wahlweise wird ein intraoraler Abdruck mit einem Alginatabdruckmaterial genommen und ein Gußmaterial, wie Gips, in dieser Gegenform zur Herstellung eines Gußstückes vergossen. Dann wird die Mundschutzmasse gleichmäßig bei 60 bis 80°C weich gemacht und gegen dieses Gußstück verpreßt und ausgeformt, wobei ein gut an die Abmessung der Mundkavität der jeweiligen Person angepaßter Mundschutz leicht herstellbar ist.The mouth protection composition according to the invention can be used directly in the The mouth cavity of the consumer softens and compresses and thus be well adjusted. Optionally, an intra-oral impression with an alginate impression material taken and one Casting material, such as gypsum, in this counterform for the production cast a casting. Then the mouthguard evenly softened at 60 to 80 ° C and against this Cast pressed and formed, with a good to the Dimension of the oral cavity of each person adapted Mouthguard is easy to produce.
In unerwarteter Weise ist der auf diese Weise erzeugte Mundschutz bezüglich der Zugfestigkeit um das 2- bis 5-fache besser als ein handelsübliches Produkt, so daß die Zähne und die Kieferknochen in hohem Ausmaße geschützt werden können. Die Wasserabsorption dieses Mundschutzes wird auf 1/2 bis 1/10 herabgesetzt, wobei daraus hervorgeht, daß die Masse sehr stabil ist.Unexpectedly, it is the one generated in this way Mouthguard regarding the tensile strength by 2 to 5 times better than a commercial product, so that the teeth and the jawbone can be protected to a great extent. The water absorption of this mouthguard will be 1/2 to 1/10 reduced, which shows that the mass is very stable.
Es ist darauf hinzuweisen, daß ein unter Einsatz der erfindungsgemäßen Mundschutzmasse hergestellter Mundschutz zur Verhinderung eines Knirschens mit den Zähnen beim Schlafen verwendet werden kann.It should be noted that one using the Mouthguard prepared according to the invention to prevent the teeth from crunching Sleeping can be used.
Nachfolgend wird die Erfindung unter Bezugnahme auf die folgenden Beispiele und Vergleichsbeispiele näher erläutert, ohne darauf eingeschränkt zu sein.Hereinafter, the invention with reference to the the following examples and comparative examples explained in more detail, without being limited to it.
In einer Knetvorrichtung mit einer Temperatur von 110°C werden das Ethylen/Vinylacetat-Copolymere und das Polycaprolacton miteinander während 30 Minuten verknetet. Wie durch die Ring- und Kugelmethode (JIS K 2531) gemessen werden kann, besitzt das verknetete Produkt einen Erweichungspunkt von 75°C. Dieses Produkt klebt nicht an der Hand an und wird beim Eintauchen in Wasser mit 75°C während einer Zeitspanne von 2 Minuten derart weich, daß es leicht auf ein Zahnmodell aufgepreßt werden kann. Verschiedene charakteristische Werte dieses Produkts gehen aus der folgenden Tabelle hervor.In a kneader with a temperature of 110 ° C become the ethylene / vinyl acetate copolymer and the polycaprolactone kneaded together for 30 minutes. How through the ring and ball method (JIS K 2531) are measured can, the kneaded product has a softening point of 75 ° C. This product does not stick to the hand and will when immersed in water at 75 ° C for a period of time of 2 minutes so soft that it is light on a dental model can be pressed. Various characteristic values This product is shown in the following table.
In einer auf 115°C eingestellten Knetvorrichtung werden das Ethylen/Vinylacetat-Copolymere, Polyvinylacetat und Polycaprolacton während 40 Minuten verknetet. Anhand der Ring- und Kugelmethode (JIS K 2531) wird ermittelt, daß das verknetete Produkt einen Erweichungspunkt von 70°C besitzt. Dieses Produkt klebt nicht an der Hand an und wird durch Eintauchen in warmes Wasser mit 70°C während einer Zeitspanne von 1 Minute derart weich, daß es leicht auf ein Zahnmodell aufgepreßt werden kann.In a kneading device set at 115 ° C, the Ethylene / vinyl acetate copolymers, polyvinyl acetate and Polycaprolactone kneaded for 40 minutes. Based on Ring and ball method (JIS K 2531) is determined that the kneaded product has a softening point of 70 ° C. This product does not stick to the hand and gets through Immerse in warm water at 70 ° C during one Period of 1 minute so soft that it is easy on Tooth model can be pressed.
Verschiedene Eigenschaftswerte dieses Produktes gehen aus der folgenden Tabelle hervor. Various property values of this product go out of the following table.
In einer auf 130°C eingestellten Knetvorrichtung werden das Ethylen/Vinylacetat-Copolymere und das Polycaprolacton während 50 Minuten verknetet. Wie anhand der Ring- und Kugel methode (JIS K 2531) ermittelt wird, besitzt das verknetete Produkt einen Erweichungspunkt von 75°C. Dieses Produkt klebt nicht an der Hand an und wird durch 2 Minuten dauerndes Eintauchen in warmes Wasser mit 75°C derartig weich, daß es auf ein Zahnmodell aufgepreßt werden kann. Verschiedene Eigenschaftswerte dieses Produkts gehen aus der folgenden Tabelle hervor.In a kneading device set at 130 ° C, the Ethylene / vinyl acetate copolymers and the polycaprolactone kneaded for 50 minutes. As with the ring and ball method (JIS K 2531) is determined, has the kneaded Product has a softening point of 75 ° C. This product does not stick to the hand and gets through 2 minutes continuous immersion in warm water at 75 ° C such soft, that it can be pressed onto a dental model. Various property values of this product are taken from the following table.
In einer auf 105°C eingestellten Knetvorrichtung werden das Ethylen/Vinylacetat-Copolymere und das Polycaprolacton während 30 Minuten verknetet. Wie anhand der Ring- und Kugelmethode (JIS K 2531) ermittelt wird, besitzt das verknetete Produkt einen Erweichungspunkt von 72°C. Dieses Produkt klebt nicht an der Hand an und wird durch Eintauchen in warmes Wasser mit 70°C während 1 Minute derart erweicht, daß es leicht auf ein Zahnmodell aufgebracht werden kann. In a kneading device set at 105 ° C, the Ethylene / vinyl acetate copolymers and the polycaprolactone kneaded for 30 minutes. As based on the ring and Ball method (JIS K 2531) is determined possesses the kneaded product has a softening point of 72 ° C. This Product does not stick to the hand and is dipped by soaked in warm water at 70 ° C for 1 minute, that it can be easily applied to a dental model.
Wie anhand der Ring- und Kugelmethode (JIS K 2531) ermittelt wird, besitzt diese Substanz einen Erweichungspunkt von 100°C. Dieses Material klebt während der Erweichung an der Hand an und ist so heiß und härtet so schnell während der Erweichung/Verpressung und Austrocknung, daß die Verformung schwierig ist.As determined by the ring and ball method (JIS K 2531) If this substance has a softening point of 100 ° C. This material sticks to the surface during softening Hand on and is so hot and hardens so fast during the Softening / compression and dehydration that deformation difficult.
Wie anhand der Ring- und Kugelmethode (JIS K 2531) ermittelt wird, besitzt diese Substanz einen Erweichungspunkt von 85°C und klebt an der Hand wenig an. Während der Erweichung/Verpressung und der Verformung ist es jedoch so heiß und härtet so schnell, daß eine Verformung schwierig ist.As determined by the ring and ball method (JIS K 2531) If this substance has a softening point of 85 ° C and does not stick to the hand. During the Softening / compression and deformation, however, it is so hot and hardens so fast that deformation is difficult is.
Erweichungspunkt: bestimmt gemäß JIS K 2531 Härte: bestimmt gemäß JIS K 6301, Federtyp außeres Druckverhältnis: Die Proben werden mit einem Autographen (hergestellt von der Shimazu Co.) und einem Oszilloskop (National VP-5730A) getestet. Das Ausmaß der Polsterwirkung wird als Prozentsatz pro 100 zum Zeitpunkt keines Schutzes gegenüber Schlageinwirkung ausgedrückt. Schlagbelastung: 100 g; Falldistanz: 100 mm; Probendicke: 3,0 mm.Softening point: determined according to JIS K 2531 Hardness: determined according to JIS K 6301, spring type external pressure ratio: The samples are taken with a Autographs (made by Shimazu Co.) and one Oscilloscope (National VP-5730A) tested. The extent of Upholstery effect is expressed as a percentage per 100 at time no protection against impact. Impact load: 100 g; Drop distance: 100 mm; Sample thickness: 3.0 mm.
Niedrigere Werte geben geringere Schläge wieder. Zugfestigkeit: bestimmt gemäß JlS K 6301, Nr. 2-Teststück.Lower values reflect lower hits. Tensile strength: determined according to JIS K 6301, No. 2 test piece.
Aus den in der vorstehenden Tabelle zusammengefaßten Werten ist ersichtlich, daß die erfindungsgemäßen Mundschutzmassen nicht an der Hand kleben und aufgrund ihrer herabgesetzten Erweichungspunkte eine gute Erweichungsmanipulierbarkeit besitzen. Aus einem Vergleich mit den Vergleichsbeispielen geht hervor, daß die nach den erfindungsgemäßen Beispielen erhaltenen Mundschutzmassen eine Härte und ein äußeres Druckverhältnis besitzen, die auf niedrigere Werte herabgesetzt sind, wobei ihre Zugfestigkeit um einen Faktor von 1,3 bis 2,7 verbessert ist. Ihre Wasserabsorption ist um 25 bis 70% vermindert und ihre Elastizität und Dehnung sind auf geeignete Werte eingestellt, wobei sie bezüglich Stabilität und Dauerhaftigkeit verbessert sind.From the values summarized in the table above It can be seen that the mouth protection compositions according to the invention do not stick to the hand and due to their degraded Softening points a good softening manipulability have. From a comparison with the comparative examples shows that the according to the inventive examples obtained masks a hardness and an external Have a pressure ratio that is lower are reduced, with their tensile strength by a factor is improved from 1.3 to 2.7. Your water absorption is over 25 to 70% less and their elasticity and elongation are adjusted to appropriate values, with respect Stability and durability are improved.
Daher stellen die erfindungsgemäßen Mundschutzmassen Materialien dar, die sich gut an die Mundkavität anpassen lassen und äußere Drücke in ausreichendem Maße abzupuffern vermögen, so daß sie sich zum Schützen der Zähne und Kieferknochen eignen.Therefore, the mouth protection compositions according to the invention Materials that adapt well to the oral cavity and buffer external pressures sufficiently so that they protect themselves from the teeth and Jawbone suitable.
Claims (3)