DE3834589A1 - Brazing process

Info

Publication number: DE3834589A1
Application number: DE19883834589
Authority: DE
Inventors: Maiken Fecht
Original assignee: Individual
Current assignee: Individual
Priority date: 1988-10-11
Filing date: 1988-10-11
Publication date: 1990-04-26

Abstract

The aim is to render unnecessary the hitherto conventional separate feeding of a flux and a brazing filler metal so that the brazing operation is substantially simplified. This is done by simultaneous feeding of brazing filler metal and flux in one operation by using a brazing filler metal, suitable for the materials to be combined, having an integrated flux, likewise suitable for these materials, in solid, powdered, pasty or liquid form.

Description

Die Erfindung betrifft ein Hartlötverfahren zum Vereinigen metallischer Werkstoffe mit Hilfe eines geschmolzenen Zusatzmetalles (Lot) und eines Fluß mittels sowie das zugehörige Lot.The invention relates to a brazing process for Combine metallic materials with the help of a molten filler metal (solder) and a river means and the associated lot.

Bei der Anwendung des bekannten Hartlötverfahrens wird die Verbindung der metallischen Teile durch eine Ober flächenlegierung hergestellt.When using the known brazing process the connection of the metallic parts by a top surface alloy manufactured.

Es ist wünschenswert, solche Oberflächenlegierungen jeweils nur in dem Bereich der Lötfuge zu erhalten, so daß die hierdurch veränderte Eigenschaft und das veränderte Aussehen der zu verbindenden Metalle nur an der Verbindungsstelle eintritt.It is desirable to have such surface alloys only available in the area of the solder joint, so that this changes the property and that changed appearance of the metals to be joined only occurs at the junction.

Die zu lötenden Metallteile müssen vor dem Löten absolut sauber und frei von Oxyden sein und müssen auch während des Lötens vor neuerlicher Oxydbildung geschützt werden.The metal parts to be soldered must absolutely before soldering be clean and free of oxides and must be kept during of soldering are protected against renewed oxide formation.

Die heute üblichen Lote werden vorwiegend in Form von Stangen oder Blechen angeboten. Nach dem die zu verbinden den Metallteile an der Lötstelle durch Auftrag von Fluß mitteln vor der Oxydbildung geschützt sind, wird das Stangenlot jeweils bei der erforderlichen Löttemperatur der Lotfuge folgend so in die Fuge eingeschmolzen, daß hier eine Legierung und somit eine Verbindung entstehen kann.The solders common today are predominantly in the form of Bars or sheets offered. After which to connect the metal parts at the solder joint by applying flux are protected against the formation of oxide, that will Pole solder at the required soldering temperature following the solder joint so melted into the joint that here an alloy and thus a connection arise can.

Hierbei können Tropfen des Stangenlots auf benachbarte Partien fallen und sich dort sowohl in Form kleiner Hügel wie auch als Mulden ausbilden. This can drop the rod solder onto adjacent ones Batches fall and there both in the form of smaller ones Form hills as well as hollows.

Lotbleche sind in Paillen zu schneiden und in geeigneter Menge an die Fuge anzuheften. Während des Lötens können einzelne Paillen wegspringen und ebensolche Beschädi gungen verursachen wie die Löttropfen.Solder plates are to be cut into pairs and are more suitable Attach the amount to the joint. Can while soldering single pills jump away and damage cause like the solder drops.

An der Fuge kann sich überschüssiges Lot in Form von Wülsten oder als Fragment der Lötpaillen in unterschied lichster Form ausbilden. Besonders an Schmuckobjekten sind solche Beschädigungen störend und daher auch durch eine Zusatzarbeit wieder zu beseitigen.Excess solder in the form of Bumps or as a fragment of the solder pads in different training in the simplest form. Especially on jewelry objects such damage is bothersome and therefore due to to eliminate additional work.

Bei zu wenig aufgetragenem Lot ist die Fuge nicht völlig geschlossen, so daß die Passung unter Umständen nicht sorg fältig ausgeführt ist und korrigiert werden muß, was gegebenenfalls die Wiederholung der Lötung erfordert.If the solder applied too little, the joint is not complete closed, so the fit may not worry is well executed and needs to be corrected what may require repeating the soldering.

Die metallischen Lote für Edelmetalle sind darüber hinaus auch so zu legieren, daß sie die gleiche Farbe wie die zu verbindenden Metallteile aufweisen. Eine Faustregel besagt, daß jeweils nur drei Lötungen mit einer Lotart an einem Objekt auszuführen sind, da bei einer vierten und weiteren Lötung mit dem gleichen Lot die zuvor her gestellten Verbindungen wieder gelöst werden können. Daher werden für die Lötung von Edelmetallen in Berücksichtigung der jeweiligen Farblegierungen in der Regel jeweils drei unterschiedliche Lotarten angeboten und verwendet. Hierbei wird zwischen einem streng fließenden Lot für die erste Lötung, einem mittelfließenden für die zweite Lötung und einem leicht fließenden Lot für die dritte Lötung unter schieden. Bei dem Legieren dieser Lote ist wiederum die Farbe der zu verbindenden Metallarten zu berücksichtigen. The metallic solders for precious metals are also beyond also alloyed so that they are the same color as the have metal parts to be connected. A rule of thumb states that only three solderings with one type of solder to be carried out on one object, since a fourth and further soldering with the same solder as before provided connections can be released again. Therefore are considered for the soldering of precious metals of the respective color alloys usually three different types of solder offered and used. Here is between a strictly flowing solder for the first Soldering, a medium flowing for the second soldering and an easy flowing solder for the third soldering underneath divorced. When alloying these solders, this is again The color of the metal types to be connected.

Da unter diesen Umständen an derartige Lotarten hohe Anforderungen gestellt werden müssen, wird ihre Weiter entwicklung in entsprechenden Fachlaboratorien betrieben.Because under these circumstances high types of solder Requirements will have to be met development carried out in appropriate specialist laboratories.

Der Erfindung liegt die Aufgabe zugrunde, die bisherige getrennte Zuführung eines Flußmittels und eines Lots ent behrlich zu machen, so daß der Arbeitsvorgang des Hart lötens wesentlich vereinfacht wird.The invention is based, the previous task separate feed of a flux and a solder ent to make dishonorable, so that the work of the Hart soldering is significantly simplified.

Erfindungsgemäß geschieht dies durch gleichzeitiges Zu führen von Lot und Flußmittel in einem Arbeitsgang mittels Verwendung eines für die zu vereinigenden Werkstoffe geeig neten Lotes mit integriertem ebenfalls für diese Werkstoffe geeignetem Flußmittel in fester, pulvriger, pastoser oder flüssiger Form.According to the invention, this is done by simultaneous closing lead solder and flux in one operation Use of a suitable for the materials to be combined solder with integrated also for these materials suitable flux in solid, powdery, pastose or liquid form.

Das hierfür infrage kommende Lot umfaßt Flußmittelanteile in Form von Glas enthaltend Silizium, Pottasche, Borax und Soda in unterschiedlichen Mengen (einschließlich Nullmengen).The solder that can be used for this includes flux components in the form of glass containing silicon, potash, borax and Soda in different amounts (including zero amounts).

Für besondere Anwendungsfälle empfiehlt sich im Lot ein Anteil eines für die zu vereinigenden Werkstoffe geeigneten Haftmittels.Lot is recommended for special applications Proportion of one suitable for the materials to be combined Adhesive.

Die vorgeschlagene Vereinigung des Lotes mit dem Flußmittel zu einem einheitlich zu handhabenden Arbeitsstoff vereinfacht den gesamten Arbeitsvorgang. Die neuartige mit einem geeigneten Flußmittel versetzte Lotsubstanz kann beispielsweise in gepulver ter oder mit Wasser zu einem Brei verrührter flüssiger Form mit einem Pinsel aufgetragen werden, so daß nach dem An trocknen der Substanz die Lötung ausgeführt werden kann. Das Auftragen mit einem Pinsel ist ein einfacher Vorgang, der zu keinerlei Oberschüssen der Lotsubstanz führt, so daß keine kleinen Hügel oder Mulden nach Beendigung des Lotvorgangs an der Lötstelle entstehen. The proposed union of the solder with the flux simplified to a uniformly handled material the whole process. The new one with a suitable one Solder added with flux can, for example, be powdered ter or mixed with water to a slurry of liquid form be applied with a brush, so that after the application drying the substance the soldering can be carried out. Applying with a brush is a simple process that does not lead to any surplus of the solder substance, so that none small hills or hollows after the soldering process has ended the solder joint arise.

Diese erleichterte Zufuhr der Lot/Flußmittelkombination ist insbesondere von großem Vorteil bei der industriellen oder handwerklichen Herstellung von Metallkonstruktionen im Flugzeugbau, Schiffsbau, in der Automobilindustrie, bei Rohrsystemen und Armaturen.This facilitates the supply of the solder / flux combination is particularly of great advantage in industrial or manual production of metal structures in aircraft construction, shipbuilding, in the automotive industry, at Pipe systems and fittings.

Es lassen sich nunmehr auch Aluminiumteile im Hartlötverfahren miteinander verbinden, wofür bisher nur ein kompliziertes Schweißverfahren zur Verfügung stand.Aluminum parts can now also be brazed connect with each other, for which so far only a complicated one Welding process was available.

Claims

1. Brazing process for combining metallic materials with the aid of a molten filler metal (solder) and a flux, characterized by

- Simultaneous supply of solder and flux in one operation
- By using a solder suitable for the materials to be combined with an integrated flux, if suitable for these materials, in solid, powdery, pasty or liquid form.

2. Lot for performing the method according to claim 1, marked by Flux content in the form of glass, containing silicon, Potash, borax and soda in different quantities (including zero quantities).

3. Lot according to claim 2, characterized by a share of one for ver unifying materials suitable adhesive.

4. Metal construction, especially aircraft and ships body, pipe system or the like, marked by Use of a solder according to claims 2 and 3.