DE3812340C1

DE3812340C1 - Dividable hose

Info

Publication number: DE3812340C1
Application number: DE19883812340
Authority: DE
Inventors: Des Erfinders Auf Nennung Verzicht
Original assignee: Rehau AG and Co
Current assignee: Rehau Automotive SE and Co KG
Priority date: 1988-04-14
Filing date: 1988-04-14
Publication date: 1989-05-03

Abstract

The invention relates to a dividable hose of polymeric materials. The hose wall is cross-sectionally made up predominantly of a base polymer, while at least one strip-shaped subregion of the hose wall consists of a foreign polymer which is different from the base polymer and is incompatible with it. It is regarded as the characterising feature of the invention that the strip-shaped subregion of the foreign polymer is recessed into the hose wall, from the outer circumference of the hose, in such a way that a residual wall of the base polymer towards the lumen of the hose is retained.

Description

Die Erfindung betrifft einen teilbaren Schlauch aus polymeren Werkstoffen, bei dem die Schlauchwandung im Querschnitt über wiegend aus einem Grundpolymeren aufgebaut ist, während we nigstens ein streifenförmiger Teilbereich der Schlauchwandung aus einem vom Grundpolymeren verschiedenen und mit diesem un verträglichen Fremdpolymeren besteht.The invention relates to a divisible tube made of polymer Materials in which the hose wall cross-section built up mainly from a basic polymer, while we at least a strip-shaped section of the hose wall from a different from the base polymer and with this un compatible foreign polymers.

Aus der Europäischen Patentschrift 00 21 446 ist ein teilba rer Kurzkatheter aus Kunststoff bekannt, der aus einem Polyo lefin als Basispolymer aufgebaut ist. In die Wand dieses be kannten Kopfkatheters sind wenigstens zwei parallel um 180° versetzte längsverlaufende Streifen aus einem modifizierenden Polymer eingesetzt, welches mit dem Basispolymeren unverträg lich ist. Derartige Kurzkatheter haben den Vorteil, daß sie sich zuverlässig in Längsrichtung aufreißen und teilen las sen. Da aber die über den vollen Wandquerschnitt verlaufenden Streifen des modifizierenden Polymeren, sowohl an der äußeren Oberfläche als auch an der inneren Oberfläche des Schlauches in ihrer vollen Querschnittsfläche austreten, muß sowohl das Basispolymere als auch das modifizierende Polymere mit dem Durchflußgut bzw. mit dem menschlichen Gewebe, in welches der Kurzkatheter eingesetzt werden soll, gut verträglich sein.From the European patent specification 00 21 446 is a part rer short catheter made of plastic known from a polyo lefin is built up as a base polymer. In the wall of this be Known head catheters are at least two parallel through 180 ° offset longitudinal stripes from a modifying Polymer used, which is incompatible with the base polymer is. Such short catheters have the advantage that they tore and split reliably in the longitudinal direction sen. But since those running across the full wall cross-section Strips of the modifying polymer, both on the outer Surface as well as on the inner surface of the hose emerge in their full cross-sectional area, both Base polymers as well as the modifying polymer with the Flow material or with the human tissue in which the Short catheter should be used, well tolerated.

Zum anderen ist als Nachteil festzustellen, daß aufgrund der Unverträglichkeit des Basispolymeren mit dem modifizierenden Polymeren eine homogene Verbindung an den Übergangsstellen der Streifen zur Schlauchwand nicht möglich ist. Dies bedeutet, daß die Belastungsgrenze unterhalb derer der einzelnen verwen deten Polymermaterialien liegt. Dieser Nachteil kann zu einer ungewollten Lösung des Verbundes und damit zu Schwierigkeiten bei der Arbeit mit diesem Kurzkatheter führen. On the other hand, it is a disadvantage that, due to the Incompatibility of the base polymer with the modifying Polymers a homogeneous connection at the transition points of the Strip to the hose wall is not possible. This means, that the load limit below that of the individual use Deten polymer materials. This disadvantage can lead to a unwanted solution of the network and thus to difficulties lead when working with this short catheter.

Aus der Europäischen Patentschrift 01 11 786 ist ein Venenka theter bekannt geworden, der im wesentlichen aus einer Kunst stoffkanüle besteht, welche einen Katheterschlauch umhüllt. Die Kunststoffkanüle besitzt in Längsrichtung verlaufende Rei hen von Querschnittsschwächungen oder Längstrennstellen. Über diese Querschnittsschwächungen oder Längstrennstellen ist die Kunststoffkanüle nach dem Verbringen des Katheterschlauches in seine Endposition auftrennbar gestaltet, wodurch sie von ihrem Sitz über dem Katheterschlauch entfernt werden kann.From the European patent specification 01 11 786 is a Venenka became known, essentially from an art there is a cannula which envelops a catheter tube. The plastic cannula has ri running in the longitudinal direction hen cross-sectional weakening or longitudinal separations. over this cross-sectional weakening or longitudinal separation points is the Plastic cannula after placing the catheter tube in designed its end position separable, thereby separating it from hers Seat over the catheter tube can be removed.

Diese Ausführung hat den Nachteil, daß erhebliche Kräfte auf gewendet werden müssen, um die Perforierungen bzw. Quer schnittsschwächungen der Kunststoffkanüle voneinander zu tren nen, was bei dem sensiblen Einsatzgebiet nicht in jedem Falle akzeptabel ist.This version has the disadvantage that considerable forces must be turned to the perforations or cross cutting weaknesses of the plastic cannula to separate from each other what in the sensitive field of application is not always is acceptable.

Hier setzt die Erfindung ein, die es sich zur Aufgabe gestellt hat, einen teilbaren Schlauch aus polymeren Werkstoffen zu entwickeln, welcher sich einerseits leicht teilen läßt, bei dem andererseits aber die Festigkeit des Verbundes so einge stellt werden kann, daß eine unwillkürliche Lösung des Schlauchverbundes vermieden wird. Erfindungsgemäß wird dazu vorgeschlagen, daß der streifenförmige Teilbereich des Fremd polymeren vom äußeren Umfang des Schlauches her derart in die Schlauchwandung eingelassen ist, daß zum Lumen des Schlauches hin eine Restwand des Grundpolymeren erhalten bleibt.This is where the invention comes in, which has set itself the task has a divisible hose made of polymeric materials develop, which on the one hand is easy to share, at on the other hand, however, the strength of the composite can be found that an involuntary solution of the Hose assembly is avoided. According to the invention suggested that the striped portion of the alien polymer from the outer circumference of the hose in such a way Hose wall is recessed to the lumen of the hose a residual wall of the base polymer is preserved.

Der erfindungsgemäße Schlauch kann also ohne Schwierigkeiten aus einem geschlossenen Schlauchsystem herausgenommen werden. Ein solches geschlossenes Schlauchsystem kann beispielsweise als Drainage-System eingesetzt werden. The hose according to the invention can therefore be used without difficulty can be removed from a closed hose system. Such a closed hose system can, for example can be used as a drainage system.

Hierfür wird der erfindungsgemäße Schlauch auf einem Metall- TROCAR fixiert. Mit diesem Metall-TROCAR werden beispielswei se die Haut- und Fleischschichten an der vorgegebenen Stelle eines menschlichen Körpers durchstochen und so weit durchge zogen, daß das am Ende des TROCARS fixierte Schlauchstück wie der aus dem menschlichen Körper austritt. Danach wird die TRO- CAR-Spitze entfernt, so daß ein durchgehender Einführkanal für den Drainschlauch geschaffen wird. Durch den erfindungsgemäßen Schlauch wird dann der Drainschlauch eingeschoben und danach der erfindungsgemäße Schlauch aus dem Körper entfernt. Nachdem der Drainschlauch mit einem Aufnahmebehälter fest verbunden ist, kann der erfindungsgemäße Schlauch ohne Zuhilfenahme von Schneidwerkzeugen einfach durch Überwindung der Haltekraft der Restwand des Grundpolymeren, d.h. durch Aufreißen dieser Rest wand von dem Drainschlauch entfernt werden. Die zum Lumen des erfindungsgemäßen Schlauches stehenbleibende Restwand des Grundpolymeren verhindert es beispielsweise, daß eine Trennung der Schlauchwandung durch das Einführen des Drainschlauches erfolgt, wie es beispielsweise beim Stand der Technik möglich ist, wo das mit dem Grundpolymeren unverträgliche modifizie rende Polymere des Streifens lediglich aufgrund der bei der Fertigung erzielbaren Adhäsion verbunden ist.For this purpose, the hose according to the invention is placed on a metal TROCAR fixed. With this metal TROCAR, for example se the skin and meat layers at the given place of a human body and pierced so far pulled that the piece of hose fixed at the end of the TROCARS like that comes out of the human body. Then the TRO CAR tip removed so that a continuous insertion channel for the drain hose is created. By the invention The drain hose is then pushed in and then the hose according to the invention removed from the body. After this the drain hose is firmly connected to a receptacle the hose according to the invention can be used without the aid of Cutting tools simply by overcoming the holding force of the Residual wall of the base polymer, i.e. by tearing up this rest wall can be removed from the drain hose. The lumen of the hose according to the invention remaining wall of the Base polymers, for example, prevent separation the hose wall by inserting the drain hose takes place as is possible, for example, in the prior art is where the modification incompatible with the base polymer polymers of the strip only because of the Manufacturing achievable adhesion is connected.

Es hat sich als vorteilhaft erwiesen, daß die Dicke des strei fenförmigen Teilbereichs des Fremdpolymeren wenigstens zwei Drittel der Schlauchwanddicke beträgt. Weiter scheint es zweckmäßig, daß das Grundpolymer ein Polyolefin und das Fremd polymer ein Polyurethan oder ein Polyvinylchlorid ist.It has proven advantageous that the thickness of the strip fen-shaped portion of the foreign polymer at least two Third of the tube wall thickness. It seems further expedient that the base polymer is a polyolefin and the foreign polymer is a polyurethane or a polyvinyl chloride.

Bei einer Wanddicke des erfindungsgemäßen Schlauches von ins gesamt 0,3 mm kann beispielsweise der streifenförmige Teilbe reich des Fremdpolymeren eine Dicke von 0,2 mm aufweisen, so daß die Restwand des Grundpolymeren noch 0,1 mm beträgt. With a wall thickness of the hose according to the invention from ins The strip-shaped part can be 0.3 mm in total rich of the foreign polymer have a thickness of 0.2 mm, so that the remaining wall of the base polymer is still 0.1 mm.

Dieses Dickenverhältnis dürfte für verschiedene Anwendungs beispiele ausreichend sein. Es liegt jedoch im Rahmen der Er findung, dieses Verhältnis fortlaufend derart zu sensibili sieren, daß eine produktionstechnisch eben noch realisierbare Verhältnissituation erreicht wird. Diese dürfte bei den heute gültigen Produktionsmethoden in dem gegebenen Schlauchwand dickenbeispiel von 0,3 mm bei einer Streifendicke von 0,295 mm liegen, so daß eine Restwand des Grundpolymeren von 0,005 mm stehen bliebe. Diese Beispielsangaben ergeben die Bandbreite, in der der erfindungsgemäße Schlauch hergestellt werden kann. Dabei wird das aktuell verwendete Dickenverhältnis in Abhän gigkeit vom Einsatzzweck gestellt, so daß für jeden solchen Einsatzzweck ein speziell gefertigtes Schlauchsystem erzeugt werden kann.This thickness ratio is likely for different applications examples may be sufficient. However, it is within the Er finding this relationship to be so sensitive on an ongoing basis sieren that a technically still feasible Ratio situation is reached. This should be the case today valid production methods in the given hose wall thickness example of 0.3 mm with a strip thickness of 0.295 mm lie, so that a residual wall of the base polymer of 0.005 mm would stop. This example gives the range, in which the hose according to the invention can be produced. The thickness ratio currently used depends on posed by the purpose, so that for each such Purpose created a specially manufactured hose system can be.

Das für den erfindungsgemäßen Schlauch verwendete Grundpoly mer ist vorteilhaft ein Polyolefin und hier insbesondere ein Polyethylen oder ein Polypropylen. Mit diesen Polyolefinen sind die zur Erzeugung der streifenförmigen Teilbereiche ver wendeten Fremdpolymere wie Polyurethan, Polyvinylchlorid und dgl. unverträglich, so daß in den Übergangsbereichen der Wand querschnitte vom Grundpolymeren zum Fremdpolymeren keine stoffschlüssige Verbindung erzielbar ist. Die streifenförmi gen Teilbereiche dienen in dieser Beziehung in erster Linie als Fühlbereiche der über der Restwand des Grundpolymeren ver bleibenden Querschnittsräume. Die Festigkeit des erfindungsge mäßen Schlauches ist daher auf die Restwand des Grundpolymeren in diesen Bereichen abgestellt, so daß die Variationsmöglich keiten in der Dicke dieser Restwand die Reißfestigkeit des erfindungsgemäßen Schlauches bestimmen. Diese Reißfestigkeit liegt entsprechend der eingestellten Wanddicke der Restwand oberhalb des inhomogenen Verbundes teilbarer Schläuche aus dem Stand der Technik, jedoch entsprechend unterhalb eines Schlau ches, bei dem das verwendete Grundpolymere über den gesamten Schlauchumfang in gleichbleibender Dicke verwendet wird. The basic poly used for the hose according to the invention mer is advantageously a polyolefin and in particular a Polyethylene or a polypropylene. With these polyolefins are the ver for generating the strip-shaped sections used foreign polymers such as polyurethane, polyvinyl chloride and Incompatible, so that in the transition areas of the wall cross-sections from base polymer to foreign polymer none cohesive connection can be achieved. The stripe-shaped Sub-areas serve primarily in this regard as sensing areas ver over the remaining wall of the base polymer permanent cross-sectional spaces. The strength of the fiction moderate hose is therefore on the remaining wall of the base polymer parked in these areas so that the possible variations in the thickness of this residual wall the tensile strength of the Determine hose according to the invention. This tear resistance lies according to the set wall thickness of the remaining wall above the inhomogeneous composite of divisible hoses from the State of the art, but correspondingly below a cunning ches, in which the base polymer used over the entire Hose circumference with a constant thickness is used.

Die speziell für den Anwendungszweck eingestellte Dicke der Restwand des Grundpolymeren bringt die Festigkeit gegen das Ausplatzen des erfindungsgemäßen Schlauches an den streifen förmigen Teilbereichen während der Anwendung, da die dabei auftretenden Kräfte nicht direkt auf den ungeschützten Ver bund zwischen Grundpolymeren und Fremdpolymeren wirken, son dern da hier die Restwand des Grundpolymeren mit ihrer homo genen Verbindung zur Schlauchwand einen Puffer bildet, der solche Krafteinwirkungen im Rahmen der eingestellten Wanddicke auffängt.The thickness of the Residual wall of the base polymer brings the strength against that The hose according to the invention bursts out on the strips shaped sub-areas during use, since the forces not directly on the unprotected ver bond between base polymers and foreign polymers, son but here the remaining wall of the base polymer with its homo gene connection to the hose wall forms a buffer that such force effects within the set wall thickness catches.

Da beim Anwenden des erfindungsgemäßen Schlauches dieser selbstverständlich gekrümmt, gebogen oder in sonstiger Weise deformiert wird, dient die Restwand des Grundpolymeren unter dem streifenförmigen Teilbereich des Fremdpolymeren auch da zu, daß bei einem ungewollten Lösen des streifenförmigen Teil bereiches, beispielsweise durch extreme Knickbelastung oder Deformation, dazu kommt, daß der erfindungsgemäße Schlauch ge schlossen bleibt und somit das Lumen vor einer Kontamination geschützt ist. So kann beispielsweise nach dem Entfernen des TROCARS der zum Absaugen dienende Drainschlauch in das unkonta minierte Lumen des erfindungsgemäßen Schlauches eingeführt werden. Erst wenn nach dem Erreichen der endgültigen Lage des Drainschlauches der erfindungsgemäße Schlauch aus der Wunde gezogen wird, kann der streifenförmige Teilbereich des Fremd polymeren abgezogen und dann die verbleibende dünne Wandung, die als Sollbruchstelle dient, aufgerissen werden. Der erfin dungsgemäße Schlauch kann danach ohne Schwierigkeit vom Drain schlauch entfernt werden.Because when using the hose according to the invention this of course curved, curved or in any other way is deformed, the remaining wall of the base polymer serves under the strip-shaped section of the foreign polymer there too to that in the event of an unwanted loosening of the strip-shaped part area, for example due to extreme buckling or Deformation, in addition to the fact that the hose according to the invention ge remains closed and thus the lumen from contamination is protected. For example, after removing the TROCARS the drain hose for suction into the unconta mined lumens of the tube according to the invention introduced will. Only if after reaching the final position of the Drain hose the hose according to the invention from the wound can be drawn, the strip-shaped portion of the foreign polymer and then the remaining thin wall, which serves as a predetermined breaking point. The inventor The hose according to the invention can then be removed from the drain without difficulty hose are removed.

Wichtig ist hierbei, daß selbst nach dem Entfernen des strei fenförmigen Teilbereichs der erfindungsgemäße Schlauch als ge schlossenes System bestehen bleibt und den Drainschlauch wei terhin vor Kontaminierung schützt. It is important that even after removing the streak fen-shaped portion of the hose according to the invention as ge closed system remains and the drain hose knows also protects against contamination.

Dies bringt den Vorteil hygienischer Sauberkeit auch nach Ent fernung des streifenförmigen Teilbereichs des Fremdpolyme ren.This has the advantage of hygienic cleanliness even after removal Removal of the strip-shaped section of the foreign polymer ren.

Bei der Herstellung des erfindungsgemäßen Schlauches wird zweckmäßigerweise der streifenförmige Teilbereich des Fremd polymeren wenigstens an einem freien Ende des Schlauches über stehend gefertigt. Dieser Überstand dient als Griffband für das Herauslösen des streifenförmigen Teilbereichs aus seinem Sitz in der Schlauchwand vor der beabsichtigten endgültigen Teilung durch Zerreißen der Restwand des Grundpolymeren.In the manufacture of the hose according to the invention expediently the strip-shaped portion of the foreign polymerize at least at a free end of the hose manufactured standing. This protrusion serves as a grip for removing the strip-shaped section from its Seat in the hose wall before the intended final Division by tearing the remaining wall of the base polymer.

Der streifenförmige Teilbereich des Fremdpolymeren kann axial von außen in die Schlauchwand als Einstreifenelement einge bracht sein. Bei Bedarf können jedoch auch mehrere solcher Streifen auf den Umfang der Schlauchwandung verteilt, einge bracht sein.The strip-shaped section of the foreign polymer can be axial from the outside into the hose wall as a single strip element be brought. If necessary, however, several such Stripes distributed over the circumference of the hose wall, inserted be brought.

Ein weiterer Vorteil des erfindungsgemäßen Schlauchaufbaus ist es, daß seine Fertigung endlos erfolgen kann. Hierbei wird mit zwei Extrusionsmaschinen gearbeitet, von deren eine das Grund polymere zur Bildung des Schlauches liefert, während die ande re das Fremdpolymere für die Erstellung des streifenförmigen Teilbereiches abgibt. Die Vereinigung der beiden Materialströ me zu dem gewünschten Schlauchaufbau erfolgt dann in einem ge meinsamen Werkzeug.Another advantage of the hose structure according to the invention is it that its manufacture can be endless. Here is with worked two extrusion machines, one of which is the reason polymer to form the tube, while the other re the foreign polymer for creating the striped Submits. The union of the two material flows me to the desired hose construction then takes place in a ge common tool.

In der Zeichnung ist ein Ausführungsbeispiel des erfindungsge mäßen Schlauches schematisch dargestellt. Der Schlauch 1 ist dabei im Querschnitt gezeigt und besitzt über den größten Teil der Querschnittsfläche gleiche Wanddicken. Im oberen Scheitel punkt ist ein streifenförmiger Teilbereich 2 zu erkennen, der sich in seinem Querschnitt vom äußeren Schlauchumfang 11 nach innen bis nahe zum inneren Schlauchumfang 12 erstreckt. Zum inneren Schlauchumfang 12 hin ist der streifenförmige Teilbe reich 2 durch eine Restwand 3 abgedeckt, so daß der gesamte innere Schlauchumfang nahtlos aus dem polymeren Material der Schlauchwand aufgebaut ist.In the drawing, an embodiment of the hose according erfindungsge is shown schematically. The hose 1 is shown in cross-section and has the same wall thicknesses over the largest part of the cross-sectional area. In the upper vertex, a strip-shaped section 2 can be seen, which extends in cross-section from the outer tube circumference 11 inwards to close to the inner tube circumference 12 . Towards the inner tube circumference 12 , the strip-shaped part 2 is covered by a residual wall 3 , so that the entire inner tube circumference is seamlessly constructed from the polymeric material of the tube wall.

Claims

1.Dividable hose made of polymeric materials, in which the hose wall is built up predominantly from a basic polymer in cross-section, while at least one strip-shaped partial area of the hose wall consists of a foreign polymer which is different from and compatible with the basic polymer, characterized in that the strip-shaped partial area ( 2 ) of the foreign polymer from the outer circumference ( 11 ) of the hose ( 1 ) is embedded in the hose wall in such a way that a residual wall ( 3 ) of the base polymer is retained towards the lumen of the hose.

2. Divisible hose according to claim 1, characterized in that the thickness of the strip-shaped portion ( 2 ) of the foreign polymer carries at least 2/3 of the hose wall thickness be.

3. Divisible hose according to claim 1, characterized net that the base polymer is a polyolefin and the foreign pole is always a polyurethane.

4. Divisible hose according to claim 3, characterized net that the foreign polymer is a polyvinyl chloride.