DE3541727C1 - Impregnating agent, especially for soft flat gaskets, such as cylinder head gaskets or exhaust flange gaskets - Google Patents

Impregnating agent, especially for soft flat gaskets, such as cylinder head gaskets or exhaust flange gaskets

Info

Publication number
DE3541727C1
DE3541727C1 DE3541727A DE3541727A DE3541727C1 DE 3541727 C1 DE3541727 C1 DE 3541727C1 DE 3541727 A DE3541727 A DE 3541727A DE 3541727 A DE3541727 A DE 3541727A DE 3541727 C1 DE3541727 C1 DE 3541727C1
Authority
DE
Germany
Prior art keywords
liquid
percent
impregnating agent
weight
gaskets
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE3541727A
Other languages
German (de)
Inventor
Horst Dr Beyer
Hans-Rainer Dr Zerfass
Franz-Josef Giesen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Goetze GmbH
Original Assignee
Goetze GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Goetze GmbH filed Critical Goetze GmbH
Priority to DE3541727A priority Critical patent/DE3541727C1/en
Application granted granted Critical
Publication of DE3541727C1 publication Critical patent/DE3541727C1/en
Expired legal-status Critical Current

Abstract

Published without abstract.

Description

Die Erfindung betrifft ein Imprägniermittel, insbesondere für Weichstoffflachdichtungen, wie Zylinderkopfdichtungen oder Auspuffflanschdichtungen, bestehend aus einem additionsvernetzbaren flüssigen System auf der Basis eines additionsvernetzbaren Polysiloxanharzes mit Radikalbildnerzusatz und das Verfahren zum Imprägnieren einer Weichstoffflachdichtung.The invention relates to an impregnating agent, in particular for Soft flat gaskets, such as cylinder head gaskets or Exhaust flange seals, consisting of a addition-crosslinkable liquid system based on a addition-crosslinkable polysiloxane resin with Radical generator additive and the method for impregnating one Flat soft gasket.

Weichstoffzylinderkopfdichtungen aus gegebenenfalls Faservliesen sind vor allem zur Verbesserung ihrer Medienbeständigkeit, zur Erhöhung ihrer Festigkeit und Verbesserung ihrer Abdichtgüte imprägniert. Imprägniermittel sind beispielsweise nach der US-PS 39 70 322 bevorzugt flüssige, lösungsmittelfreie Polybutadiene und Polyacrylate oder Systeme mit Isocyanaten oder Epoxiden, die beim Vernetzen in der Dichtungsplatte unter Zusatz von gegebenenfalls Vernetzungsmittel ohne Abgabe verdampfender und den Weichstoff aufblähender Substanzen vernetzen. Die mit diesen Mitteln imprägnierten Dichtungen haben sich in der Praxis inzwischen hervorragend bewährt, allerdings sind Dichtungen, welche derartige Imprägniermittel voll vernetzt enthalten, relativ spröde und in diesem Zustand nicht einbaufähig. Mit verteuernden zusätzlichen Maßnahmen müssen solche Dichtungen daher gegebenenfalls über lange Lagerzeiten bis zum Einbau vor einer völligen Vernetzung des Imprägniermittels geschützt werden.Soft cylinder head gaskets from if necessary Nonwovens are mainly used to improve their Media resistance, to increase their strength and Impregnated to improve their sealing quality. Waterproofing agent are preferred, for example, according to US Pat. No. 3,970,322 liquid, solvent-free polybutadienes and polyacrylates or systems with isocyanates or epoxides that crosslink in the sealing plate with the addition of if necessary Crosslinking agent without dispensing and evaporating the soft material Cross-linking swelling substances. The one with these means Impregnated seals have become practical in the meantime excellent proven, however seals are what contain such impregnating agents fully crosslinked, relatively brittle and cannot be installed in this condition. With costly additional measures need such seals  therefore possibly over long storage times before installation protected from complete crosslinking of the impregnating agent will.

Inzwischen sind flüssige unter Zusatz von Platinsalzkatalysatoren additionsvernetzende Silikonharze aus insbesondere flüssigem Polymethylvinylsilikonharz oder Polysilikonacrylat bekannt, die als Imprägniermittel in Flachdichtungsmaterialien nach der DE-OS 32 45 664 lagerbeständige Dichtungen mit gutem Verformungs- und Funktionsverhalten ergeben. Solche flüssigen Silikonharzsysteme sind jedoch in der Praxis schwierig zu handhaben und nur bedingt zum Imprägnieren von Faservliesstoffen geeignet. Die Faservliese müssen zur Vermeidung einer Vergiftung des Katalysators frei von Aminen, Schwefelverbindungen oder schwefelabgebenden Substanzen sein, was bei Faservliesen mit Kautschukbindemittel nur schwer möglich ist. Flüssige Silikonharzansätze mit Katalysatorzusatz vernetzen darüber hinaus, wenn auch langsam, bei Raumtemperatur unter Veränderung ihrer Viskosität, so daß sie beispielsweise nach der DE-OS 32 45 664 schon nach 16 Stunden nicht mehr verwendet werden können. Insbesondere Zylinderkopfdichtungen, bei deren Imprägnation großvolumige Imprägniermittelansätze monatelang im Einsatz sind, lassen sich so in der Massenfertigung nicht mehr wirtschaftlich imprägnieren.Meanwhile, liquid are added with Platinum salt catalysts from addition-crosslinking silicone resins in particular liquid polymethyl vinyl silicone resin or Polysilicon acrylate known as a waterproofing agent in Flat gasket materials according to DE-OS 32 45 664 storage-stable seals with good deformation and Functional behavior result. Such liquid However, silicone resin systems are difficult to apply in practice handle and only partially to impregnate Suitable for nonwoven fabrics. The nonwovens have to Avoidance of poisoning of the catalyst free of amines, Be sulfur compounds or sulfur releasing substances, which is difficult with nonwovens with rubber binders is possible. Liquid silicone resin batches with catalyst additive also network, albeit slowly, at room temperature changing their viscosity so that they, for example according to DE-OS 32 45 664 after 16 hours no longer can be used. In particular cylinder head gaskets, in their impregnation, large-volume impregnation approaches are in use for months, can be in the No longer impregnate mass production economically.

Inzwischen wurde gefunden, daß flüssige additionsvernetzende Silikonharze sich unter Radikalbildnerzusatz aus bevorzugt einem organischen Peroxid sich auch bei Abwesenheit von Platinsalzkatalysatoren vernetzen lassen. Solche flüssigen Silikonharzansätze verändern ihre Eigenschaften bei Raumtemperatur nur wenig und können praktisch zeitlich unbegrenzt wirtschaftlich zur Massenimprägnation von Zylinderkopfdichtungen verwendet werden.It has now been found that liquid addition-crosslinking Silicone resins are preferred with the addition of radical formers an organic peroxide even in the absence of Allow platinum salt catalysts to crosslink. Such liquid  Silicone resin approaches change their properties Room temperature only a little and can practically time unlimited economical for mass impregnation of Cylinder head gaskets are used.

Mit derartigen Silikonharzen imprägnierte Dichtungsmaterialien bleiben jedoch nach dem thermischen Vernetzen im Oberflächenbereich klebrig, weil offensichtlich unter dem umgebenden Lufteinfluß die völlige Vernetzung des Imprägniermittels im Oberflächenbereich beeinträchtigt wird. Damit nicht klebende und damit verwendbare Dichtungen hergestellt werden können, muß die thermische Vernetzung des Imprägniermittels unter Schutzgas oder im Vakuum vorgenommen werden, oder die Dichtungen müssen nach gegebenenfalls Auftrag einer Überzugsmasse bevorzugt mit UV-Strahlen nachvernetzt werden. Solche Maßnahmen sind aber als zusätzliche Verfahrensschritte unwirtschaftlich und die so imprägnierten Dichtungen sind letztlich zu teuer.Sealing materials impregnated with such silicone resins remain after thermal crosslinking Surface area sticky because obviously under that surrounding air influence the complete networking of the Impregnant in the surface area is impaired. So that non-adhesive and therefore usable seals can be produced, the thermal crosslinking of Impregnating agent made under protective gas or in a vacuum or the seals have to be applied if necessary a coating composition preferably crosslinked with UV rays will. However, such measures are additional Process steps uneconomical and the impregnated in this way Seals are ultimately too expensive.

Der vorliegenden Erfindung liegt daher die Aufgabe zugrunde, ein Imprägniermittel, für insbesondere Weichstoffflachdichtungen, auf der Basis eines additionsvernetzbaren flüssigen Silikonharzes zu schaffen, welches sich bevorzugt thermisch wirtschaftlich und ohne Zusatzmaßnahmen in der imprägnierten Dichtung ohne die beschriebenen Nachteile vernetzen läßt.The present invention is therefore based on the object an impregnating agent, especially for Flat gasket made of soft material, based on a to create addition-crosslinkable liquid silicone resin, which is preferred thermally economical and without Additional measures in the impregnated seal without the described disadvantages can network.

Diese Aufgabe wird durch ein flüssiges Imprägniermittel auf der Basis eines additionsvernetzbaren Silikonharzes mit Radikalbildnerzusatz gelöst, welches erfindungsgemäß mindestens 5 Gewichtsprozent eines flüssigen additionsvernetzbaren Kohlenwasserstoffes enthält. Der bevorzugt zugesetzte additionsvernetzbare flüssige Kohlenwasserstoff besteht aus einem flüssigen Polybutadien, welches in Mengen von mindestens 5 Gewichtsprozent dem Silikonharzansatz zuemulgiert ist.This task is carried out by a liquid impregnating agent the basis of an addition-crosslinkable silicone resin Radical generator additive solved, which according to the invention  at least 5 percent by weight of a liquid contains addition-crosslinkable hydrocarbon. The preferably added addition-crosslinkable liquids Hydrocarbon consists of a liquid polybutadiene, which in amounts of at least 5 percent by weight Silicone resin approach is emulsified.

Und zwar wurde überraschenderweise gefunden, daß mit der erfindungsgemäßen Zusammensetzung imprägnierte Weichstoffflachdichtungsmaterialien nach dem thermischen Vernetzen ohne besondere Zusatzmaßnahmen auch im Oberflächenbereich nicht mehr klebrig sind. Offensichtlich scheint der erfindungsgemäß zugesetzte flüssige additionsvernetzbare Kohlenwasserstoff zusammen mit dem Silikonharz beim Vernetzen ein Copolymerisat zu bilden, das von anwesenden Luftsauerstoffmengen unbeeinflußbar zu einem voll vernetzten und nicht klebrigen Produkt aushärtet. Erstaunlich war dabei, daß schon relativ kleine Mengen an vor allem flüssigen Polybutadien genügten, um den gewünschten Effekt zu erzielen. Der Zusatz an flüssigem Polybutadien verändert dabei die Verformungseigenschaften und das Verformungsverhalten der imprägnierten Dichtung gegenüber ausschließlich mit Silikonharz imprägnierten Dichtungen nicht, und es wurde sogar gefunden, daß der Polybutadienzusatz bis auf 40 Gewichtsprozent ohne wesentliche Änderung der Dichtungsqualität gesteigert werden könnte. Der Ansatz kann darüber hinaus auch zusätzlich zwischen 5 und 60 Gewichtsprozent eines flüssigen Polymethylhydrogensiloxans enthalten, ohne die Eigenschaften der Dichtung ungünstig zu beeinflussen. Hohe Zusatzmengen an preiswertem Polybutadien und preiswertem flüssigen Polymethylhydrogensiloxans verbilligen dann vor allem das Imprägniermittel gegenüber Imprägniermitteln mit hohen Anteilen an teurem additionsvernetzbarem Polysiloxan.And it was surprisingly found that with the impregnated composition according to the invention Soft gasket materials after thermal Networking without special additional measures also in Surface area are no longer sticky. Obviously seems the liquid added according to the invention addition-crosslinkable hydrocarbon together with the Silicone resin to form a copolymer during crosslinking unaffected by the amount of atmospheric oxygen present fully cross-linked and non-sticky product cures. It was astonishing that relatively small amounts of before all liquid polybutadiene was sufficient to achieve the desired To achieve effect. The addition of liquid polybutadiene changes the deformation properties and that Deformation behavior of the impregnated seal seals not only impregnated with silicone resin, and it has even been found that the polybutadiene addition up to to 40 percent by weight with no significant change in Seal quality could be increased. The approach can also between 5 and 60 Weight percent of a liquid polymethylhydrogensiloxane included without adversely affecting the properties of the seal influence. High amounts of inexpensive polybutadiene  and inexpensive liquid polymethylhydrogensiloxane then especially cheaper compared to the impregnating agent Impregnants with high proportions of expensive addition-crosslinkable polysiloxane.

Die bevorzugt eingesetzten additionsvernetzbaren Silikonharze bestehen aus flüssigem Polymethylvinylsilikonharz oder flüssigem Polysilikonacrylat und als Radikalbildner wird bevorzugt ein organisches Peroxid, wie insbesondere flüssiges Dicumylperoxid, verwendet.The preferred addition-crosslinkable silicone resins consist of liquid polymethyl vinyl silicone resin or liquid polysilicon acrylate and as a radical generator preferably an organic peroxide, such as in particular liquid Dicumyl peroxide used.

Die bevorzugten Imprägniermittelansätze bestehen dann ausThe preferred impregnating agent mixtures then consist of

  • 30 bis 70 Gewichtsprozent des flüssigen additionsvernetzbaren Polysiloxanharzes, wie Polymethylvinylsilikonharz und/oder Polysilikonacrylat,30 to 70 percent by weight the liquid addition-crosslinkable polysiloxane resin, such as Polymethyl vinyl silicone resin and / or polysilicon acrylate,
  • 5 bis 60 Gewichtsprozent des flüssigen Polymethylhydrogensiloxans,5 to 60 percent by weight the liquid polymethylhydrogensiloxane,
  • 5 bis 40 Gewichtsprozent des flüssigen additionsvernetzbaren Kohlenwasserstoffs, wie bevorzugt Polybutadien,5 to 40 weight percent the liquid addition-crosslinkable hydrocarbon, such as preferably polybutadiene,
  • 1 bis 6 Gewichtsprozent eines Radikalbildners aus bevorzugt einem organischen Peroxids und gegebenenfalls1 to 6 percent by weight of a radical generator preferably from an organic peroxide and if necessary
  • bis zu maximal 3 Gewichtsprozent eines handelsüblichen Antioxydationsmittels.up to a maximum of 3 percent by weight a commercially available antioxidant.

Durch die Erfindung ist somit eine imprägnierte Flachdichtung mit den vorteilhaften Eigenschaften einer silikonimprägnierten Flachdichtung mit guter Festigkeit, guter elastischer Verformbarkeit beim Einbau und hoher Temperatur- und Medienbeständigkeit geschaffen, die gegenüber herkömmlich imprägnierten Dichtungen vor allem zusätzlich eine besonders gute Wasserabdichtgüte und Alterungsbeständigkeit besitzt. Die imprägnierte Dichtung ist dadurch ohne zu kleben praktisch unbegrenzt lagerfähig, ohne ihre Eigenschaften zu verändern und somit ohne Zusatzmaßnahmen über längere Zeit einbaufähig lagerbar.The invention thus provides an impregnated flat gasket with the advantageous properties of a silicone impregnated  Flat gasket with good strength, good elastic Deformability during installation and high temperature and Media resistance created compared to conventional impregnated seals, especially a special one has good waterproofness and resistance to aging. The impregnated seal is therefore practical without sticking Can be stored indefinitely without changing their properties and can therefore be installed over a longer period of time without additional measures storable.

Zum Imprägnieren der Weichstoffflachdichtung mit der erfindungsgemäßen Imprägniermittelzusammensetzung wird die Dichtung mit einer Porenfüllung zwischen 60 und 100 Volumprozent imprägniert, und das Imprägniermittel wird in der einbaufähigen Dichtung thermisch auf seinen Endzustand vernetzt.For impregnating the soft flat gasket with the Impregnant composition according to the invention is the Seal with a pore filling between 60 and 100 Volume percent impregnated, and the impregnating agent is in the installable seal thermally to its final state networked.

Durch die Erfindung ist vor allem die Dichtung einfach und wirtschaftlich in der Massenfertigung herstellbar. Die erfindungsgemäße Imprägniermittelzusammensetzung ist im Betrieb über längere Zeiten verwendbar, ihre volle Vernetzung in der Dichtungsplatte ist ohne Nachteile und ohne zusätzliche Verfahrensschritte in einem einfachen thermischen Verfahren möglich und bei relativ hohen Zusatzmengen ist das Imprägniermittel ohne Nachteile kostengünstig einsetzbar.With the invention, the seal is especially simple and economically producible in mass production. The Impregnant composition according to the invention is in the Can be used for longer periods, its full networking in the sealing plate is without disadvantages and without additional Process steps in a simple thermal process possible and with relatively high additional quantities that is Impregnation agent can be used inexpensively without disadvantages.

Die Erfindung wird durch ein Ausführungsbeispiel näher erläutert. The invention is illustrated by an embodiment explained.  

Ausgegangen wird von einem Imprägniermittelansatz mitThe starting point is an impregnation agent

  • 55 Gewichtsprozent Polysilikonacrylat flüssig,
    35 Gewichtsprozent Polymethylhydrogensiloxan flüssig,
     7 Gewichtsprozent Polybutadien flüssig (Mg 1500) und
     3 Gewichtsprozent Dicumylperoxid.    55% by weight polysilicon acrylate liquid,
    35% by weight polymethylhydrogensiloxane liquid,
    7 weight percent polybutadiene liquid (Mg 1500) and
    3 percent by weight dicumyl peroxide.

Das flüssige Polybutadien ist dabei zum Ansatz unter leichtem Reiben zuemulgiert.The liquid polybutadiene is easy to approach Rubbing emulsified.

Mit diesem Imprägniermittelansatz werden Zylinderkopfdichtungen aus metallisch verstärkten Asbestfaservliesen mit einer Porenfüllung von 80 Volumprozent durch Tauchen imprägniert.With this waterproofing agent approach Cylinder head gaskets made of reinforced metal Asbestos fiber fleece with a pore filling of 80 volume percent impregnated by dipping.

Das Imprägniermittel in den Dichtungen wird 2 Minuten bei 270°C vernetzt und die Dichtungen zeigten griffige und nicht klebende Oberflächen.The impregnating agent in the seals is at 2 minutes Networked 270 ° C and the seals showed non-slip and not adhesive surfaces.

Das Funktionsverhalten der Dichtungen wurde überprüft. Es ergaben sich Werte für das Verformungsverhalten, das Abdichtvermögen und die Festigkeit, die mit herkömmlich imprägnierten Dichtungen vergleichbar sind. Die Temperaturbeständigkeit, die Wasserdichtgüte und die Beständigkeit gegenüber verschiedenen Abdichtmedien erwies sich gegenüber herkömmlich imprägnierten Dichtungen als wesentlich verbessert.The functional behavior of the seals was checked. It there were values for the deformation behavior, the Sealing ability and strength that with conventional impregnated seals are comparable. The Temperature resistance, the waterproof quality and the Resistance to various sealing media proved compared to conventionally impregnated seals as significantly improved.

Im Alterungstest durch Lagerung über 6 Monate bei 70°C wurden keine wesentlichen Änderungen der Funktionseigenschaften festgestellt.In the aging test by storage at 70 ° C for 6 months no significant changes in functional properties detected.

Claims (8)

1. Imprägniermittel, insbesondere für Weichstoffflachdichtungen für Verbrennungskraftmaschinen, wie Zylinderkopfdichtungen oder Auspuffflanschdichtungen, bestehend aus einem additionsvernetzbaren flüssigen System auf der Basis eines additionsvernetzbaren Polysiloxanharzes mit Radikalbildnerzusatz, dadurch gekennzeichnet, daß es mindestens 5 Gewichtsprozent eines flüssigen additionsvernetzbaren Kohlenwasserstoffes enthält.1. Impregnating agent, in particular for soft flat gaskets for internal combustion engines, such as cylinder head gaskets or exhaust flange gaskets, consisting of an addition-crosslinkable liquid system based on an addition-crosslinkable polysiloxane resin with radical-forming additive, characterized in that it contains at least 5 percent by weight of a liquid addition-crosslinkable hydrocarbon. 2. Imprägniermittel nach Anspruch 1, dadurch gekennzeichnet, daß der flüssige additionsvernetzbare Kohlenwasserstoff aus einem flüssigen Polybutadien besteht, welches in Mengen von 5 bis 40 Gewichtsprozent dem Imprägniermittel zuemulgiert ist.2. Impregnating agent according to claim 1, characterized in that the liquid addition-crosslinkable hydrocarbon consists of a liquid polybutadiene, which in Amounts of 5 to 40 percent by weight of the impregnating agent is emulsified. 3. Imprägniermittel nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß es zusätzlich 5 bis 60 Gewichtsprozent eines flüssigen Polymethylhydrogensiloxans enthält.3. Impregnating agent according to claim 1 or 2, characterized characterized by an additional 5 to 60 Weight percent of a liquid Contains polymethylhydrogensiloxane. 4. Imprägniermittel nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß das flüssige, additionsvernetzbare Polysiloxanharz aus einem flüssigen Polymethylvinylsilikonharz oder einem flüssigen Polysilikonacrylatharz besteht. 4. Impregnating agent according to one of claims 1 to 3, characterized in that the liquid, addition-crosslinkable polysiloxane resin from a liquid Polymethyl vinyl silicone resin or a liquid Polysilicon acrylic resin.   5. Imprägniermittel nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß der Radikalbildner aus einem organischen Peroxid besteht.5. Impregnating agent according to one of claims 1 to 4, characterized in that the radical generator from a organic peroxide. 6. Imprägniermittel nach den Ansprüchen 1 bis 5, dadurch gekennzeichnet, daß es aus
  • 30 bis 70 Gewichtsprozent des flüssigen additionsvernetzbaren Polysiloxanharzes,
  • 5 bis 60 Gewichtsprozent des flüssigen Polymethylhydrogensiloxans,
  • 5 bis 40 Gewichtsprozent des flüssigen additionsvernetzbaren Kohlenwasserstoffs,
  • 1 bis 6 Gewichtsprozent eines organischen Peroxids als Radikalbildnerzusatz und gegebenenfalls
  • bis zu 3 Gewichtsprozent eines handelsüblichen Antioxydationsmittels
6. Impregnating agent according to claims 1 to 5, characterized in that it consists of
  • 30 to 70 percent by weight of the liquid addition-crosslinkable polysiloxane resin,
  • 5 to 60 percent by weight of the liquid polymethylhydrogensiloxane,
  • 5 to 40 percent by weight of the liquid addition-crosslinkable hydrocarbon,
  • 1 to 6 percent by weight of an organic peroxide as a radical generator additive and optionally
  • up to 3 percent by weight of a commercially available antioxidant
besteht.consists. 7. Verfahren zum Imprägnieren einer Weichstoffflachdichtung, dadurch gekennzeichnet, daß die Flachdichtung bis zu einer Porenfüllung von 60 bis 100 Volumprozent mit dem Imprägniermittel nach einem der Ansprüche 1 bis 6 imprägniert wird, und daß das Imprägniermittel in der einbaufähigen Dichtung thermisch auf seinen Endzustand vernetzt wird.7. method for impregnating a soft gasket, characterized in that the flat gasket up to a pore filling of 60 to 100 percent by volume with the Impregnating agent according to one of claims 1 to 6 is impregnated, and that the impregnating agent in the built-in seal thermally to its final state is networked.
DE3541727A 1985-11-26 1985-11-26 Impregnating agent, especially for soft flat gaskets, such as cylinder head gaskets or exhaust flange gaskets Expired DE3541727C1 (en)