DE3128672A1 - Hydrophilic, pulverulent, atactic polypropylene preparations, process for their preparation, and their use - Google Patents
Hydrophilic, pulverulent, atactic polypropylene preparations, process for their preparation, and their useInfo
- Publication number
- DE3128672A1 DE3128672A1 DE19813128672 DE3128672A DE3128672A1 DE 3128672 A1 DE3128672 A1 DE 3128672A1 DE 19813128672 DE19813128672 DE 19813128672 DE 3128672 A DE3128672 A DE 3128672A DE 3128672 A1 DE3128672 A1 DE 3128672A1
- Authority
- DE
- Germany
- Prior art keywords
- polypropylene
- atactic polypropylene
- preparations
- alkali metal
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Patentansprüche und Beschreibung zur Patentanmeldung betreffend Hydrophilie pulverige ataktische Polypropylenpräparate, Verfahren zu ihrer Herstellung und ihre Verwendung Beschreibung Die Erfindung betrifft hydrophile pulverige ataktische Polypropylenpräparate, ein Verfahren zu ihrer Herstellung und ihre Verwendung.Claims and description of the patent application relating to hydrophilicity powdered atactic polypropylene preparations, processes for their manufacture and their use Description The invention relates to hydrophilic powdery Atactic polypropylene preparations, a process for their manufacture and their use.
Es ist bekannt, daß ein Nebenprodukt der Polypropylenherstellung ataktisches beziehungsweise amorphes Polypropylen, dessen Mengenanteil 5 bis 14 Gew.-O/o, bezogen auf das Polypropylen, beträgt, ist. Das ataktische Polypropylen ist ein den nicht vulkanisierten Kautschuk ähnliches nicht kristallines Material, dessen Molekulargewicht von 25 000 bis 60 000 variiert. Das ataktische Polyprolylen ist mit zahlreichen Produkten, unter anderem mit Mineralölen, Polyisobutylen, Butylkautschuk und rohem Bitumen, verträglich. Es erfolgten bereits zahlreiche Versuche zur Nutzbarmachung des in bedeutender Menge anfallenden ataktischen Polypropylenes. Eine Verwertungsmöglichkeit ist in der Bitumen- und Ölindustrie, in welchen es der Modifizierung von Fugenausfüll- und Verputzmassen, bitumenhaltigen Lacken, Mitten beziehungsweise-Elebemassen, Streich- beziehungsweise Schmiermaterialien und Ölen dient. Ein anderes wichtiges Anwendungsgebiet ist die Bauindustrie, in welcher es mit mineralischen Füllmaterialien vermischt als schallisolierendes Material, gegen Wasser abdichtendes Material, Dichtungsmaterial, Bestandteil von Fnmadenschutzüberzügen und sonstiges Bindematerial dienen kann. It is known to be a by-product of polypropylene manufacture atactic or amorphous polypropylene, the proportion of which is 5 to 14 Weight O / o, based on the polypropylene, is. The atactic polypropylene is a non-crystalline material similar to non-vulcanized rubber, the molecular weight of which varies from 25,000 to 60,000. Atactic polypropylene is with numerous products, including mineral oils, polyisobutylene, butyl rubber and raw bitumen, compatible. Numerous attempts have already been made to make it usable of the atactic polypropylene, which is produced in significant quantities. A recovery option is used in the bitumen and oil industry, where the modification of joint filling and plastering compounds, bituminous paints, middle or flooring compounds, coating or lubricating materials and oils are used. Another important area of application is the construction industry in which it is mixed with mineral fillers as sound insulating material, waterproofing material, sealing material, Can serve as part of thread protection covers and other binding material.
Ein wesentliches Hindernis gegen die technische beziehungsweise industrielle Verwertung des ataktischen Polypropylenes ist, daß es nur in großen Blöcken-zugänglich ist und sein mechanisches Zerkleinern und Schmelzen einen verhältnismäßig großen Energieaufwand erfordert. Aus diesem Grunde wird es in der Kunststoffindustrie vielfach als nicht verwertbares Nebenprodukt behandelt, dessen Vernichtung eigene Probleme mit sich bringt. Trotz der vorgeschlagenen Anwendungsgebiete ist keine regelmäßige beziehungsweise planmäßige Nutzbarmachung des ataktischen Polypropylenes erfolgt. A major obstacle to the technical or industrial Utilization of atactic polypropylene is that it is only accessible in large blocks is and its mechanical crushing and melting requires a relatively large amount of energy requires. For this reason it is often considered not to be in the plastics industry Treated usable by-product, the destruction of which poses its own problems brings. Despite the suggested areas of application, it is not a regular one, respectively Scheduled utilization of the atactic polypropylene takes place.
Der Erfindung liegt daher die Aufgabe zugrunde, ataktische Polypropylenpräparate, welche hydrophil und pulverig sind, ihren pulverigen Zustand beibehalten, nit wasserhaltigen Systemen verträglich sind und in diese ohne Schmelzen leicht eingearbeitet werden können und so erweiterme Anwendungsgebiete, insbesondere in der Bautechnik beziehungsweise Bauindustrie, haben, sowie ein Verfahren zu ihrer Herstellung, welches einfach durchführbar ist, und ihre Verwendung zu schaffen. The invention is therefore based on the object of providing atactic polypropylene preparations, which are hydrophilic and powdery, retain their powdery state, with hydrous Systems are compatible and can be easily incorporated into them without melting can and so extended areas of application, especially in construction technology or Construction industry, as well as a process for their manufacture, which can be carried out easily is, and their use to create.
Das Obige wurde überraschenderweise durch die Erfindung erreicht Es wurde nämlich überraschenderweise festgestellt, daß, wenn in der ataktischen Polypropylenschmelze Dicalciumsilikat gebildet wird, das Gemisch der beiden Materialien die Eigenschaft, von selbst zu Staub zu zerfallen, annimmt und ein neues Produkt, welches hydrophil ist, sich im puiexpn Zustand befindet, infolge des eingebauten Dicalciumsilikatmonohydrates seinen pulverigen Zustand beibehält, beim Stehen nicht aggregiert wird, homogen bleibt, mit wasserhaltigen Systemen verträglich ist und in diese ohne größeren Aufwand eingearbeitet werden kann, erhalten wird. The above has surprisingly been achieved by the invention It has been surprisingly found that when in the atactic Melt polypropylene dicalcium silicate is formed, the mixture of the two materials adopts the property of disintegrating into dust by itself and creates a new product, which is hydrophilic, is in the puiexpn state, due to the built-in Dicalcium silicate monohydrates maintains its powdery state, not when standing is aggregated, remains homogeneous, is compatible with water-containing systems and can be incorporated into these without great effort, is obtained.
Gegenstand der Erfindung sind daher hydrophile pulverige ataktische Polypropylenpräparate, welche dadurch gekennzeichnet sind, daß ihre Hauptmenge aus ataktischem Polypropylen und Dicalciumsilikatmonohydrat besteht und sie ferner 1 oder mehr Alkalisalz(e) von 1 oder mehr Fettsäure(n) mit längerer Kohlenstoffkette und gegebenenfalls 1 oder mehr Alkalimetallhydroxyd(e) enthalten. The invention therefore relates to hydrophilic powdery atactic Polypropylene preparations, which thereby are marked that their The main amount consists of atactic polypropylene and dicalcium silicate monohydrate and they also have 1 or more alkali salt (s) of 1 or more fatty acid (s) with a longer carbon chain and optionally contain 1 or more alkali metal hydroxide (s).
Vorzugsweise enthalten die erfindungsgemäßen Polypropylenpräparate das ataktische Polypropylen in Mengen von 40 bis 60 Gew.-% und das Dicalciumsilikatmonohydrat in Mengen von 15 bis 25 Gew./0. Diese Werte beziehen sich auf die erfindungsgemäßen ataktischen Polypropylenpräparate als solche, welche im allgemeinen einen gebundenen Wassergehalt von etwa 20 bis 40 Gew.-%, beispielsweise etwa 30 Gew.-%, aufweisen. Entsprechend enthalten die erfindungsgemäßen Polypropylenpräparate im trockenen Zustand vorzugsweise etwa 56 bis 72 Gew.-% ataktisches Polypropylen und etwa 21 bis 32 Gew.-% Dicalciumsilikat. The polypropylene preparations according to the invention preferably contain the atactic polypropylene in amounts of 40 to 60% by weight and the dicalcium silicate monohydrate in amounts of 15 to 25% by weight. These values relate to those according to the invention atactic polypropylene preparations as such, which generally contain a bond Water content of about 20 to 40% by weight, for example about 30% by weight. Correspondingly, the polypropylene preparations according to the invention contain in the dry Condition preferably about 56 to 72% by weight of atactic polypropylene and about 21% by weight up to 32% by weight of dicalcium silicate.
Zweckmäßig ist beziehungsweise sind das beziehungsweise die Alkalimetallsalz(e) von 1 oder mehr Fettsäure(n) ein solches beziehungsweise solche von 1 oder mehr Fettsäure(n) mit 12 bis 30 Kohlenstoffatomen. Vorzugsweise ist beziehungsweise sind das beziehungsweise die Alkalimetallsalz(e) von 1 oder mehr Fettsäure(n) Natriumstearat, Natriumoleat und/oder Natriumpalmitat. Es ist auch bevorzugt, daß in den erfindungsgemäßen Polypropylenpräparaten das beziehungsweise die Alkalimetallsalz(e) von 1 oder mehr Fettsäure(n) in Mengen von 1 bis 3 Gew.-% (entsprechend etwa 1,5 bis 4 Gew.-e/O im trockenen Zustand) vorliegt beziehungsweise vorliegen. Appropriate is or are the alkali metal salt (s) of 1 or more fatty acid (s) one or those of 1 or more Fatty acid (s) with 12 to 30 carbon atoms. Preferably is or are the alkali metal salt (s) of 1 or more fatty acid (s) sodium stearate, Sodium oleate and / or sodium palmitate. It is also preferred that in the invention Polypropylene preparations the alkali metal salt (s) of 1 or more Fatty acid (s) in amounts of 1 to 3 wt.% (Corresponding to about 1.5 to 4 wt. E / o in the dry state) is or are present.
Als gegebenenfalls vorliegendes Alkalimetallhydroxyd enthalten die erfinilun;^sgemäßen ataktischen Polypropylennr.iparnte vort1ag.wei,e Natriumhydroxyd. Es ist auch bevorzugt, daß inden erfindungsgemäßen Polypropylenpräparaten das beziehungsweise die Alkalimetallhydroxyd(e), soweit es beziehungsweise sie vorliegt beziehungsweise vorliegen, in Mengen von 2 bis 6,5 Gew,-o (entsprechend etwa 2,5 bis 8,5 Gew.-,°S im trockenen Zustand) enthalten ist beziehungsweise sind. The alkali metal hydroxide which may be present contains the In accordance with the atactic polypropylene number, the day before white sodium hydroxide. It is also preferred that in the polypropylene preparations according to the invention that or the alkali metal hydroxide (s), as far as it or they are present or are present in amounts of 2 to 6.5% by weight (corresponding to about 2.5 up to 8.5 wt .-, ° S in the dry state) is or are included.
Gegenstand der Erfindung ist auch ein Verfahren zur Herstellung der erfindungsgemäßen Polypropylenpräparate, welches dadurch gekennzeichnet ist, daß zu geschmolzenem ataktischem Polypropylen 1 oder mehr Fettsäure(n) mit längerer Kohlenstoffkette in Mengen von 1 bis 4 Gew.-%, insbesondere 1 bis 3 Gew.-%, bezogen auf das erstere zugegeben wird beziehungsweise werden, die erhaltene Gemischschmelze einer vorgewärmten wäßrigen Lösung von 1 oder mehr wasserlöslichen Salz(en), zweckmäßig Alkalimetallsalz(en), der Kieselsäure unter Rührern zugesetzt wird, danach zum erhaltenen Gemisch nach Bedarf Wasser zugegeben wird und dem homogenisierten Gemisch bis zum Eintreten des Zerfallens von selbst zu Staub Calciumhydroyyd, zweckmäßig als Kalkhydrat beziehungsweise gelöschter Kalk, und ferner nach Bedarf Wasser zugesetzt werden. The invention also provides a method for producing the Polypropylene preparations according to the invention, which is characterized in that to molten atactic polypropylene 1 or more fatty acid (s) with longer Carbon chain in amounts of 1 to 4% by weight, in particular 1 to 3% by weight, based on on the former is or are added, the mixture melt obtained a preheated aqueous solution of 1 or more water-soluble salt (s) is appropriate Alkali metal salt (s) to which silica is added with stirring, then to the obtained Water is added to the mixture as required and the homogenized mixture up to Occurrence of the disintegration to dust calcium hydroxide, expediently as hydrated lime or slaked lime, and water can also be added as required.
Nach ihrer Herstellung werden die erfindungsgemäßen ataktischen Polypropylenpräparate zweckmäßig abkuhlen gelassen. After their production, the atactic polypropylene preparations according to the invention are expediently allowed to cool.
Vorzugsweise wird beziehungsweise werden als wasserlösliches] Salz(e) der Kieselsäure Natriumsilikat und/oder Kaliumsilikat verwendet. Preferably, the water-soluble salt (s) the silica used is sodium silicate and / or potassium silicate.
Zweckmäßig wird das Molverhältnis des Natriumsillkates und/oder Kaliumsilikates zum Calciumhydroxyd zu 1 : 1,1 bis 1,2 gewählt. The molar ratio of the sodium silicate and / or potassium silicate is expedient chosen for calcium hydroxide at 1: 1.1 to 1.2.
Zweckmäßig wird beziehungsweise werden als E1'ettsaure(n) eine solche beziehungsweise solche mit 12 bis 30 Eohlenstoffatomen verwendet. Appropriate is or will be such as E1'ettsaure (s) or those with 12 to 30 carbon atoms are used.
Vorzugsweise wird beziehungsweise werden als Bettsäure(n) Stearinsäure, Ölsäure und/oder Palmitinsäure verwendet. Ein Beispiel für die Verwendung von mehr Fettsäuren ist die Verwendung von Stearin (eines Gemisches aus Stearin säure und Palmitinsäure). Is or are preferably used as bed acid (s) stearic acid, Oleic acid and / or palmitic acid are used. An example of using more Fatty acids is the use of stearic (a mixture of stearic acid and Palmitic acid).
Die erfindungsgemäßen ataktischen Polypropylenpräparate sind wie bereits erwähnt pulverig, weswegen bel ihrer Zugabe zu Schmelzen, wie von Asphalt, bitumenhaltigen Mitten und Bitumenüberzugsmassen, kein an Ort und Stelle erfolgendes Schmelzen erforderlich ist, da die pulverigen Präparate der warmen Schmelze unter Rühren zugesetzt werden können und das Rühren bis zum Homogenisieren fortgesetzt werden kann. Dies vereinfacht außerordentlich die Verwertung des schwer zu handhabenden in Blockform zur Verfügung stehenden ataktischen Polypropylenes. Die hydrophilen Eigenschaften der erfindungsgemäßen ataktischen Polypropylenpräparate sind ein beträchtlicher Vorteil, beispielsweise in der Hinsicht, daß sie mit Zement gut verträglich sind und so in Zementmörtel, Beton, Kalkmörtel und Wasserglasmörtel leicht eingemischt werden können. Gegenstand der Erfindung ist daher auch die Verwendung der erfindungsgemäßen Polypropylenpräparate als Zusatz für asphalt- oder bitumenhaltige Massen oder für Mörtel. The atactic polypropylene preparations of the present invention are like already mentioned powdery, which is why when adding them to melts, such as asphalt, bituminous centers and bituminous coatings, not on-site Melting is necessary because the powdery preparations are under the warm melt Stirring can be added and stirring continued until homogenized can be. This greatly simplifies the recovery of the difficult to handle atactic polypropylenes available in block form. The hydrophilic Properties of the atactic polypropylene preparations according to the invention are considerable Advantage, for example in that they are well compatible with cement and so easily mixed into cement mortar, concrete, lime mortar and water-glass mortar can be. The invention therefore also relates to the use of the invention Polypropylene preparations as an additive for asphalt or bituminous compounds or for Mortar.
Die Erfindung wird an Hand des folgenden Beispieles naher erläutert. The invention is explained in more detail using the following example.
Beispiel Es wurden in einer heizbaren Knetmaschine mit Z-förmigen Armen 90 kg normale Wasserglas lösung von 360Be auf 80 bis 90°C erwärmt. Der Verdampfungsverlust wurde durch Wasser ersetzt. In einem über dieser Vorrichtung angeordneten heizbaren und mit einem Rührer versehenen Behälter wurde ataktisches Polypropylen (mit einem Ring-Kugel-Erweichungspunkt von 1500C) geschmolzen und zu 145 kg Polypropylen wurden 5 kg Stearin mit einem Schmelzpunkt von 700C zugegeben. Example There were in a heatable kneading machine with Z-shaped Poor 90 kg normal water glass solution heated from 360Be to 80 to 90 ° C. The evaporation loss was replaced by water. In a heated one arranged above this device and a container equipped with a stirrer was atactic polypropylene (with a Ring and ball softening point of 1500C) and became 145 kg of polypropylene 5 kg of stearin with a melting point of 700C were added.
Die Polypropylenschmelze wurde der vorgewärmten sasserglaslösung unter ständigem Rühren mit solcher Geschwindigkeit zugesetzt, daß die Temperatur des Gemisches 1000C schnell erreichte. Dazu war eine Zugabegeschwindigkeit von etwa 1 1/Sekunde erforderlich. Nach der Zugabe des Polypropylenes wurde das Gemisch homogenisiert und der verdampfte Wassergehalt ersetzt. Bei der Masserzugabe verminderte sich gewöhnlich die Temperatur des Gemisches. Zur homogenen Mischung wurden unter ständigem Rühren 30 kg Kalkhydratpulver zugegeben, wobei die Dicalciumsilikatmonohydratbildung begann, was mit einer bedeutenden Volum.erhöhung und Wasseraufnahme einherging. The polypropylene melt became the preheated water glass solution added with constant stirring at such a rate that the temperature of the mixture quickly reached 1000C. In addition, there was an addition rate of about 1 1 / second required. After the addition of the polypropylene, the mixture was homogenized and replaces the evaporated water content. With the addition of mass it usually decreased the temperature of the mixture. The mixture was homogeneously mixed with constant stirring 30 kg of hydrated lime powder added, whereby the dicalcium silicate monohydrate formation began, which was accompanied by a significant increase in volume and water absorption.
Die Zusammensetzung des durch die Reaktion erhaltenen lockeren und nach dem Abkühlen pulverig zerfallenen Produkt tes war wie folgt: Gehalt an organischem Material 50 Gew.-% Gehalt an anorganischem Füllmaterial 20 Gew.-/o Gehalt an gebunclenetn'asser 30 Gew.-J: Die Zusammensetzung des 70 Gew.-% des ersteren betragenden trockenen Produktes war wie folgt: Ataktisches Polypropylen 69,5 Gew.-% Dicalciumsilikatnonohydrat beziehungsweise Dicalciumsilikat 24,3 Gew.-% Natriumstearat 2,0 Gew.-% Natriumhydroxyd 4,2 Gew. -;6 Dieses Präparat entzündete sich wegen seines hohen Dicalciumsilikatgehaltes nicht und hatte die Eigenschaft des erlöschen von selbst. Auf die Wirkung von offenen Flammen hin schmolz dieses Produkt zusammen und zerfloß. Es war dem Zement und Gips ähnlich transportierbar und lagerfähig. The composition of the loose and obtained by the reaction After cooling, the powdery disintegrated product was as follows: content of organic Material 50% by weight content of inorganic filler material 20% by weight content of bound moisture 30 percent by weight: The composition of the 70% by weight of the former dry product was as follows: Atactic polypropylene 69.5% by weight dicalcium silicate monohydrate or dicalcium silicate 24.3% by weight sodium stearate 2.0% by weight sodium hydroxide 4.2 wt. -; 6 This preparation ignited because of its high dicalcium silicate content not and had the property of going out by itself. On the effect of open This product melted and melted in flames. It was the cement and plaster of paris similarly transportable and storable.
Zusammenfassungsummary
Claims (8)