DE3048743A1

DE3048743A1 - Elastomer strip esp. for automobile bodywork - has embedded reinforcing strip of stretched zigzag form

Info

Publication number: DE3048743A1
Application number: DE19803048743
Authority: DE
Inventors: Walter Ing.(grad.) 8993 Nonnenhorn Brachmann
Original assignee: Metzeler Kautschuk GmbH; Metzeler Kautschuk AG
Current assignee: Metzeler Kautschuk GmbH; Metzeler Kautschuk AG
Priority date: 1980-12-23
Filing date: 1980-12-23
Publication date: 1982-07-22

Abstract

A profile strip of elastomer, esp. for use in automobile bodywork construction, contains a stiffening reinforcement having a clamping action. This stiffening reinforcement is composed of a strip having cuts extending in alternately from its opposite longitudinal edges, the strip is then stretched, increasing its length and opening it out into a zig-zag form. Arrangement results in comparatively light but effective reinforcement for the elastomer strip. Pref. the length of each cut is 4/5 of the width of the reinforcing strip.

Description

Profilstreifen aus elastomerem MaterialProfile strips made of elastomeric material

Die Erfindung betrifft einen Profilstreifen aus elastomerem Material mit einer als Klemmhalterung dienenden, bandförmigen Armierung.The invention relates to a profile strip made of elastomeric material with a band-shaped reinforcement serving as a clamp bracket.

Eine solche Armierung besteht beispielsweise aus einem dünnen Stahlstreifen, also einem relativ schweren Material.Such a reinforcement consists, for example, of a thin steel strip, a relatively heavy material.

Es wird jedoch angestrebt, und zwar insbesondere für den Einsatz solcher Profilstreifen in der Automobilindustrie, das Gewicht der Armierung und damit auch den Profilstreifen zu verringern. Dabei darf jedoch die Festigkeit der Armierung nicht leiden, da der feste Sitz eines solchen Profilstreifen auf einer Kante, beispielsweise als Kofferraum-Abdeckung, im wesentlichen von der Form der Armierung abhängt.However, efforts are being made, in particular for the use of such Profile strips in the automotive industry, the weight of the reinforcement and thus also to reduce the profile strip. However, the strength of the reinforcement is allowed do not suffer, as the tight fit of such a profile strip on an edge, for example as a trunk cover, depends essentially on the shape of the reinforcement.

Mit der vorliegenden Erfindung soll deshalb ein Profilstreifen der angegebenen Gattung geschaffen werden, bei dem die oben erwähnten Nachteile nicht auftreten.With the present invention is therefore a profile strip of specified genus are created in which the above-mentioned disadvantages are not appear.

Insbesondere soll ein Profilstreifen vorgeschlagen werden, der ohne Einbußen an Festigkeit ein wesentlich geringeres Gewicht als die herkömmlichen Ausführungsformen hat.In particular, a profile strip should be proposed that without Loss of strength a significantly lower weight than the conventional embodiments Has.

Dies wird erfindungsgemäß dadurch erreicht, daß die Armierung aus einem Band besteht, das von seinen beiden Längskanten her abwechselnd eingschnitten ist, und daß das eingeschnittene Band in seiner Längsrichtung gereckt ist.This is achieved according to the invention that the reinforcement from consists of a band that cut alternately from its two longitudinal edges is, and that the incised tape is stretched in its longitudinal direction.

Die Erfindung wird im folgenden anhand eines Ausführungsbeispiels unter Bezugnahme auf die beiliegenden, schematischen Zeichnungen näher erläutert. Es zeigen Fig. 1 eine Draufsicht auf ein eingeschnittenes, als Armierung verwendbares Stahlband, Fig. 2 eine Draufsicht auf das Stahlband nach Fig. 1, jedoch im gereckten Zustand, Fig. 3 einen Schnitt durch das Stahlband nach Fig. 2, das auf die Form der Armierung gebracht worden ist, und Fig. 4 einen Schnitt durch einen Profilstreifen mit eingesetzter Armierung.The invention is illustrated below using an exemplary embodiment explained in more detail with reference to the accompanying schematic drawings. 1 shows a plan view of a cut that can be used as reinforcement Steel band, FIG. 2 is a plan view of the steel band according to FIG. 1, but in the stretched position State, Fig. 3 is a section through the steel strip according to Fig. 2, which is on the form the reinforcement has been brought, and FIG. 4 shows a section through a profile strip with inserted reinforcement.

In Fig. 4 ist ein Schnitt durch einen Profilstreifen 1 dargestellt, der einen Klemmbereich 4 und Dichtlippen 2 bzw.In Fig. 4 is a section through a profile strip 1 is shown, the one clamping area 4 and sealing lips 2 or

3 aufweist. Der Klemmbereich 4 besteht aus einem elastomeren Material, in dem sich eine U-förmige Armierung 5 befindet. Ein Schnitt durch eine solche Armierung 5 ist in Fig. 3 dargestellt.3 has. The clamping area 4 consists of an elastomeric material, in which a U-shaped reinforcement 5 is located. A section through such a reinforcement 5 is shown in FIG. 3.

Der Klemmbereich 4 bildet also einen auf einer Seite offenen Bereich, der auf eine Kante aufgesteckt werden kann. Um das Herausrutschen des Klemmbereiches 4 zu erschweren, ist er auf seiner Innenfläche mit weiteren Lippen 7 versehen.The clamping area 4 thus forms an area open on one side, which can be attached to an edge. To prevent the clamping area from slipping out 4 to complicate it, it is provided with further lips 7 on its inner surface.

Der Klemmbereich 4 mit der Armierung 5 kann beispielsweise aus einem relativ harten elastomeren Material bestehen, während die Lippen 2, 3 aus einem weicherem elastomaren Material hergestellt sein können, beispielsweise aus einem Schaumstoff. Ein solcher Profilstreifen 1 wird in einem Arbeitsgang extrudiert, d.h., die Armierung 5 wird durch das relativ harte elastomere Material umspritzt und gleichzeitig auch die beiden Dichtlippen 2, 3 anetrudiert.The clamping area 4 with the reinforcement 5 can, for example, consist of a consist of relatively hard elastomeric material, while the lips 2, 3 of a softer elastomeric material can be made, for example from a Foam. Such a profile strip 1 is extruded in one operation, i.e., the reinforcement 5 is through the relatively hard elastomeric material encapsulated and at the same time also anetruded the two sealing lips 2, 3.

Zur Herstellung der Armierung 5 wird ein Stahlband verwendet, wie es in Fig. 1 in Draufsicht dargestellt ist.To produce the reinforcement 5, a steel band is used, such as it is shown in Fig. 1 in plan view.

Dieses Stahlband 5 hat in Draufsicht die Form eines rechteckigen, langgestreckten Streifens, der durch eine Stanze geführt und dabei mit Einschnitten 5' versehen wird, die senkrecht zu den Längskanten des Stahlbandes 5 nach innen verlaufen und sich möglichst weit in das Stahlband hinein erstrecken. Gleichzeitig werden in die Längskanten des Stahlbandes 5 auf der Höhe der Einschnitte 5t kleine Ausschnitte 8 eingestanzt.This steel strip 5 has the shape of a rectangular, elongated strip, which is passed through a punch and thereby with incisions 5 'is provided, which is perpendicular to the longitudinal edges of the steel strip 5 inwards and extend as far as possible into the steel strip. Simultaneously are small in the longitudinal edges of the steel strip 5 at the level of the incisions 5t Cutouts 8 punched.

Dieses eingestanzte Stahlband 5 wird dann in seiner Längsrichtung gereckt, wie in Fig. 2 dargestellt ist. Dadurch entstehen zwischen den einzelnen Stegen 9 des Stahlbandes etwa keilförmige Ausschnitte, wie man in Fig. 2 erkennen kann.This punched steel band 5 is then in its longitudinal direction stretched as shown in FIG. This creates between each Web 9 of the steel strip approximately wedge-shaped cutouts, as can be seen in FIG can.

Durch diesen Einschneid- und Reckvorgang kann also die wirksame Länge des Stahlbandes etwa verdoppelt werden, so daß sich die entsprechende Halbierung des Gewichtes der Armierung pro Längeneinheit des Profil streifens ergibt.Through this cutting and stretching process, the effective length of the steel band are roughly doubled, so that the corresponding halving the weight of the reinforcement strips per unit length of the profile results.

Dabei fällt beim Stanzen des Stahlbandes kein Abfall an, wie es beispielsweise dann der Fall wäre, wenn zur Reduzierung des Gewichtes der Armierung Ausschnitte in das Stahlband gestanzt würden.There is no waste when punching the steel strip, as is the case, for example then the case would be if cutouts were made to reduce the weight of the reinforcement would be punched into the steel band.

Die Länge der Einschnitte 5' sollte möglichst groß sein, um den anschließenden Reckvorgang zu erleichtern. Die Ausschnitte 8 unterstützen ebenfalls diesen Reckvorgang, da so die Verbindungsbereiche zwischen zwei aneinandergrenzenden Stegen 9 leichter gespreizt werden können.The length of the incisions 5 'should be as large as possible to accommodate the subsequent To facilitate the stretching process. The cutouts 8 also support this stretching process, since the connection areas between two adjacent webs 9 are lighter can be spread.

Das Recken des abwechselnd von seinen beiden Längskanten heeingeschnittenen Stahlbandes 5 kann beispielsweise dadurch erfolgen, daß das eingeschnittene Stahlband 5 zwischen zwei hintereinanderliegenden Rollenpaaren hindurchgeführt wird, von denen das in der Bewegungsrichtung hinten liegende Rollenpaar schneller läuft als das vorne liegende Rollenpaar. Dadurch übt dieses Rollenpaar eine Zugkraft auf das Band in seiner Längsrichtung aus und reckt es dadurch auf die aus Figur 2 ersichtliche Form.The stretching of the cut alternately from both of its long edges Steel band 5 can be done, for example, that the cut steel band 5 is passed between two consecutive pairs of rollers, of which the pair of rollers behind in the direction of movement runs faster than that pair of rollers at the front. As a result, this pair of rollers exerts a tensile force on the belt in its longitudinal direction and thereby stretches it to that shown in FIG Shape.

Wenn sich das Stahlband nach dem Recken etwas verformen sollte, muß es geglättet, d.h., auf die ebene Form gebracht werden. Dies kann gleichzeitig mit dem Recken geschehen, beispielsweise ebenfalls durch die erwähnten Xollenpaare.If the steel band should deform a little after stretching, it must it can be smoothed, i.e. brought to a flat shape. This can be done simultaneously with the stretching done, for example also by the mentioned Xollenpaars.

Nach dem Recken und dem Glätten wird das gereckte Stahlband 5 auf herkömmliche Weise in die aus Fig. 3 ersichtliche Form gebogen.After stretching and smoothing, the stretched steel strip 5 is opened conventionally bent into the shape shown in FIG.

Das gebogene Stahlband 5 läuft dann, durch eine Pinole geführt, durch die Austrittsdüse des Extruders, wo es durch das elastomere Material umspritzt wird. Gleichzeitig werden auch die Dichtlippen 2 und 3 anextrudiert (siehe Fig. 4).The bent steel strip 5 then runs through a quill the outlet nozzle of the extruder, where it is encapsulated by the elastomeric material. At the same time, the sealing lips 2 and 3 are also extruded on (see FIG. 4).

Damit sich die Form des gereckten Stahlbandes bei der Extrusion, aber auch bei der Vernetzung der Kautschukmischung und beim anschließenden Einsetzen des Profils nicht mehr ändert, werden Fäden 6 mitextrudiert, die sich auf beiden Seiten der Kanten der Armierung 5 befinden, wie man in Fig. 4 erkennen kann.So that the shape of the stretched steel strip is changed during extrusion, however also during the crosslinking of the rubber mixture and during the subsequent insertion of the profile no longer changes, threads 6 are coextruded, which are on both Sides of the edges of the reinforcement 5 are located, as can be seen in FIG. 4.

Diese Fäden 6 sind zugfest, d.h., ihre Länge ändert sich in Längsrichtung des Profilstreifens 1 nur wenig, so daß bei Ausübung eines Zugs auf den Profilstreifen wie er of bei der Montage erforderlich ist, sich der Profilstreifen 1 nicht verlängert, sondern seine Länge beibehält.These threads 6 are tensile strength, i.e. their length changes in the longitudinal direction of the profile strip 1 only a little, so that when a train is exercised on the profile strip how it is often required during assembly, the profile strip 1 does not lengthen, but maintains its length.

LeerseiteBlank page

Claims

claims S profile strips made of elastomeric material with a Band-shaped reinforcement serving as a clamping bracket, d a u r c h g e k e n n n shows that the band (5) forming the reinforcement is made up of its two edges is cut her alternately, and that the cut band (5) in his Is stretched longitudinally.

2. Profile strip according to claim 1, characterized in that the Incisions (5 ') run perpendicular to the longitudinal edges of the tape.

3. Profile strip according to one of claims 1 or 2, characterized in that that the incisions (5 ') are punched.

4. Profile strip according to one of claims 1 to 3, characterized in that that the length of the incisions (5 ') is about 4/5 of the width of the band (5).

5. Profile strip according to one of claims 1 to 4, characterized in that that the geredcte tape (5) is smoothed.

6. Profile strip according to claim 5, characterized in that the Band (5) is stretched during punching - and smoothed.

7. Profile strip according to claim 5, characterized in that the Band (5) is stretched and smoothed during the deformation.

8. Profile strip according to one of claims 1 to 7, characterized in that that in the vicinity of the reinforcement (5) threads (6) are in the elastomeric material.

9. Profile strip according to claim 8, characterized in that on a thread (6) is arranged on each side of an edge of the reinforcement (5).