DE3013120A1 - Solid fuel material - from waste-paper shredded and dissolved to obtain fibres for compression into logs

Info

Publication number: DE3013120A1
Application number: DE19803013120
Authority: DE
Inventors: August 7758 Meersburg Meininger
Original assignee: Individual
Current assignee: Individual
Priority date: 1980-04-03
Filing date: 1980-04-03
Publication date: 1981-10-08

Abstract

Fuel is obtained from waste paper by shredding it, mixing the shreds with water and dissolving it through agitation and water action into its fibre and size constituents. The mash is pressed in perforated vats to the shape of timber logs. The liquid from the press vats is recycled to the tanks where the mash is produced by mixing shreds and water. The resulting fuel has a high calorific value and is produced from very inexpensive material.

Description

Beschreibung Die Erfindung betrifft ein Feststoff-Heizmaterialstück. Description The invention relates to a piece of solid heating material.

Aufgabe der Erfindung ist es, ein Feststoff-Heizmaterialstück zu schaffen, das aus sehr billigem Material herstellbar ist, und einen hohen Heizwert aufweist.The object of the invention is to create a piece of solid heating material, which can be produced from very cheap material and has a high calorific value.

Erfindungsgemäß wird diese Aufgabe durch ein Feststoff-Heizmaterialstück gelöst, das so hergestellt wird, wie dies im Kennzeichen des Patentanspruches 1 definiert ist.According to the invention, this object is achieved by a piece of solid heating material solved, which is produced as shown in the characterizing part of claim 1 is defined.

Die Erfindung schafft also ein Heizmaterialstück, das aus Altpapier in extrem einfacher Weise herstellbar ist. Es entsteht ein festes, leicht und sauber handhabbares Gebilde, das langsam und kontrolliert und mit hohem Heizwert abbrennt, wobei ein Heizwert gegeben ist, der dem eines Britkettes vergleichbar ist. Man kann davon ausgehen, daß der Zentner Altpapier gegenwärtig DM 2 - 3.-- kostet. Im Vergleich dazu : der Zentner Brikett kostet ca. DM 20 - 25.--. Es entsteht also durch die Erfindung ein äußerst sauberes und in dem Heizwert Briketts vergleichbares Heizmaterial, das extrem umweltfreundlich ist, weil es aus Abfall herstellbar ist und weil es äußerst sauber - ohne Erzeugung von Kohlenmonoxyd - abbrennt.The invention thus creates a piece of heating material that is made from waste paper can be produced in an extremely simple manner. The result is a firm, light and clean manageable structure that burns down slowly and in a controlled manner and with a high calorific value, a calorific value is given which is comparable to that of a British chain. One can assume that the hundredweight of waste paper currently costs DM 2 - 3 .--. In comparison In addition: the hundredweight briquette costs around DM 20-25. So it arises through the Invention of an extremely clean heating material with comparable calorific value to briquettes, that is extremely environmentally friendly because it can be made from waste and because it Burns extremely cleanly - without producing carbon monoxide.

Ein Ausführungsbeispiel der Erfindung wird im folgenden unter Bezugnahme auf die beigefügte Zeichnung beschrieben, die schematisch den Ablauf der Herstellung darstellt.An embodiment of the invention is hereinafter referred to Described on the accompanying drawing, which schematically shows the sequence of manufacture represents.

Mehrere Stapel Altpapier 1 werden in einem Zerkleinerer 2 in Papierschnitzel 3 mechanisch zerkleinert. Diese Papierschnitzel 3 werden dann - -oße Behaiter 4 gegeben. Gleichzeitig wird diesen Behältern von einem gee''- asserzufluß 5 her Wasser zugegeben. Mit 6 ist die Wasseroberfläche bezeicnneç In dem Behälter 4 ist ein Rührwerk 7 vorgesehen, bestehend aus Rührflügeln 8 und einem Antriebsmotor 9.Several stacks of waste paper 1 are cut into shredded paper in a shredder 2 3 mechanically crushed. These shredded paper 3 then become - -oße containers 4 given. At the same time, water is supplied to these containers from a water inflow 5 admitted. With 6 the water surface is bezeicnneç In the container 4 is an agitator 7 is provided, consisting of agitator blades 8 and a drive motor 9.

In diesen Behältern 4 werden die Papierschnitzel 3 solange durch das Rührwerk 7 im Wasser bewegt, bis sich die Papierstruktur wieder in ihre Faser- und Leimbestandteile zerlegt und so eine dickflüssige Maische aus Faser-, Leimbestandteilen und Wasser entsteht. Die Wassermenge, bezogen auf das Volumen der zugeführten Papierschnitzel, und die Dauer der Vermengung bzw. mechanischen Agitation durch das Rührwerk, wird experimentell so angestimmt, daß eine solche Maische entsteht. Diese Maische ist im Behälter 4 mit dem Bezugszeichen 10 bezeichnet.In these containers 4, the shredded paper 3 as long as Agitator 7 moves in the water until the paper structure is back in its fiber and Glue components broken down and thus a viscous mash of fiber and glue components and water is created. The amount of water, based on the volume of the shredded paper, and the duration of the mixing or mechanical agitation by the agitator experimentally tuned in such a way that such a mash is produced. This mash is denoted by the reference numeral 10 in the container 4.

Danach wird die Maische 10 in einen Formpreßbehälter 11 gefüllt, der mit Löchern 12 versehen ist, durch die dünne Flüssigkeit abfließen kann, so daß die Löcher eine Art Siebwirkung zur Trennung der dünnflüssigen und der festen bzw. dickflüssigen Bestandteile hat. Dieser Effekt wird dadurch verstärkt, daß mit Hilfe eines Stempels 13, der über einen Kolben 14 von einer pneumatischen Preßeinrichtung 15 angetrieben wird, die Maische 10 im Formpreßbehälter 11 zusammengepreßt wird. Dabei wird soviel dünne Flüssigkeit, also im wesentlichen Wasser mit den Leimbestandteilen des Holzes, abgegeben, daß ein zwar noch feuchtes aber bereits in sich feststrukturiertes Gebilde entsteht. Die Zufuhr von Druckluft oder einem anderen Betätigungsmedium zu der pneumatischen Preßeinrichtung 15 erfolgt über den Anschlußschlauch 16.Thereafter, the mash 10 is filled into a compression molding container 11, the is provided with holes 12 through which the thin liquid can flow off, so that the holes act as a kind of sieve to separate the thin and solid resp. has thick components. This effect is enhanced by using a ram 13, which via a piston 14 of a pneumatic pressing device 15 is driven, the mash 10 is compressed in the compression molding container 11. There is so much thin liquid, essentially water with the glue components of the wood, given that something that is still moist but already firmly structured in itself Creation arises. The supply of compressed air or another operating medium to the pneumatic pressing device 15 takes place via the connection hose 16.

Durch diesen Vorgang des Pressens und der Flussigkeitsabtrennung entsteht aus der Maische 10 ein festes in sich zusammenhaltendes Gebilde 17, das nun aus dem Formpreßbehälter 11 entnommen werden kann. Es wird dann getrocknet, wie in der Figur dadurch schematisch dargestellt ist, daß ein Heizstrahler 18 über diesem festen Gebilde angeordnet ist.This process of pressing and separating off the liquid is created from the mash 10 a solid, cohesive structure 17, which now consists of the compression molding container 11 can be removed. It is then dried, as in that Figure is shown schematically in that a radiant heater 18 fixed above this Structure is arranged.

Durch Trocknung entsteht dann daraus ein Feststoff-Heizmaterialstück (im folgenden ebenfalls mit 17 bezeichnet), das das Endprodukt dieses Verfahrens ist. Als letzter Verfahrensschritt ist ein Stapel solcher Feststoff Heizmaterialstücke dargestellt.A solid piece of heating material is then produced from it through drying (hereinafter also referred to as 17), which is the end product of this process is. The last step in the process is a stack of such solid pieces of heating material shown.

in Diese Fe,tstoffkeizmaterialstücke halten sich nach der Trocknung fest zusammen, da ja durch die Aufweichung der Papierschnitzel auch Leimbestandteile, die im Papier ursprünglich enthalten sind, frei geworden sind, die dann aber wieder bei der Trocknung ebenfalls die Wirkung haben, die einzelnen Holzfaserbestandteile fest aneinander zu binden. Als Folge dieser Verdichtung der Faserbestandteile des Papiers ergibt sich auch, daß ein derartiges Feststoff-Heizmaterialstück langsam und kontrolliert abbrennt, und zwar unter Entfaltung eines sehr sauberen Verbrennungsvorganges, d.h. das gesamte Feststoff-Heizmaterial verbrennt zu Kohlendioxyd. Es handelt sich a5so um einen sehr sauberen Verbrennungsvorgang. These pieces of Fe, tstoffkeizmaterialstück remain after drying firmly together, because the softening of the shredded paper also has glue components, which were originally contained in the paper have become free, but which then again The individual wood fiber components also have the effect of drying to tie tightly together. As a result of this compression of the fiber components of the Paper also shows that such a piece of solid heating material is slow and burns down in a controlled manner, with the development of a very clean combustion process, i.e. all solid fuel burns to carbon dioxide. It is about a5so a very clean combustion process.

Infolge der Verdichtung ist auch die Konzentration von Heizmaterial pro Volumen so hoch, daß der Heizwert eines derartigen Feststoff-Heizmaterialstücks durchaus einem Brikett gleichen Volumens vergleichbar ist. Ein Feststoff-Heizmaterialstück der gezeigten Art kann beispielsweise die Länge von 20 cm und einen Durchmesser von 5 cm aufweisen. Bei der Handhabung ergibt sich der ganz besondere Vorteil, daß die Handhabung ohne Verschmutzung möglich ist. Es entsteht also dort, wo derartige Dinge gelagert und/oder transportiert werden müssen, keinerlei Dreck. Die Oberfläche ist einwandfrei sauber und in sich konsistent, d.h. es entsteht kein nennenswerter Abrieb, der durch mühsame Reinigungsarbeiten o.dgl.wieder beseitigt werden muß.As a result of the compression, there is also the concentration of heating material per volume so high that the calorific value of such a piece of solid heating material can be compared to a briquette of the same volume. A piece of solid fuel of the type shown, for example, the length of 20 cm and a diameter of 5 cm. When handling, there is the very special advantage that handling is possible without contamination. So it arises where such Things have to be stored and / or transported, no mess. The surface is perfectly clean and consistent in itself, i.e. there is no significant Abrasion that has to be removed again through laborious cleaning work or the like.

Bei dem Herstellungsverfahren, das anhand der beiliegenden Figur geschildert worden ist, ist noch wichtig, daß die aus den Löchern 12 des Frompreßbehälters 11 ablaufende Flüssigkeit über den Abfluß 19 des Flüssigkeitssammelbehälters 20 und den Zufluß 21 wieder dem Behälter 4 zugegeben werden kann. Damit werden wiederum die Leimbestandteile der aus dem Formpreßbehälter 11 abfließenden Flüssigkeit für die Aufbereitung der Maische 10 nutzbar gemacht.In the manufacturing process described with the aid of the attached figure Has been, it is still important that the holes 12 of the compression container 11 draining liquid via the drain 19 of the liquid collecting container 20 and the inflow 21 can be added to the container 4 again. This will in turn the glue components of the liquid flowing out of the compression molding container 11 for the preparation of the mash 10 made usable.

-ENDE DER BESCHREIBUNG- Leerseite-END OF DESCRIPTION- Blank page

Claims

Title: Solid heating material piece Patent claims 1. Solid heating material piece, characterized by the following manufacturing process: a) paper (1) is shredded; b) the shredded paper (3) produced by the shredding are in one Container (4) mixed with water and subjected to mechanical agitation and the action of water dissolved in their fiber and glue components, with the added amount of water it is determined in such a way that a thick mash (10) is produced; c) the thick one The mash (10) is placed in the compression molding container (11), the holes (12) for draining the liquid have, in which they are pressed into solid structures (17); d) the fixed Structures (17) are dried and form the finished combustible solid heating material piece (17).

2. Method for producing a piece of solid heating material according to Claim 1, characterized in that the liquid separation in the compression molding (11) outflowing liquid, in turn, the container (4) is added in the the production of the mash (10) by mixing water with the shredded paper (3) takes place.

-END OF PATENT CLAIM-