DE2837616C2 - Heat exchanger for a fuel-heated heat source - Google Patents

Heat exchanger for a fuel-heated heat source

Info

Publication number
DE2837616C2
DE2837616C2 DE19782837616 DE2837616A DE2837616C2 DE 2837616 C2 DE2837616 C2 DE 2837616C2 DE 19782837616 DE19782837616 DE 19782837616 DE 2837616 A DE2837616 A DE 2837616A DE 2837616 C2 DE2837616 C2 DE 2837616C2
Authority
DE
Germany
Prior art keywords
lead
fuel
heat exchanger
antimony
tin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19782837616
Other languages
German (de)
Other versions
DE2837616B1 (en
Inventor
Manfred 5609 Hueckeswagen Lehnert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Vaillant GmbH
Original Assignee
Joh Vaillant GmbH and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Joh Vaillant GmbH and Co filed Critical Joh Vaillant GmbH and Co
Priority to DE19782837616 priority Critical patent/DE2837616C2/en
Publication of DE2837616B1 publication Critical patent/DE2837616B1/en
Application granted granted Critical
Publication of DE2837616C2 publication Critical patent/DE2837616C2/en
Expired legal-status Critical Current

Description

Die vorliegende Erfindung bezieht sich auf einen Wärmetauscher für eine brennstoffbeheizte Wärmequelle. The present invention relates to a heat exchanger for a fuel-heated heat source.

Solche Wärmetauscher sind bislang mit einer Überzugsschicht aus reinem Blei versehen worden. Eine derartige Bleischicht hat sich jedoch als relativ korrosionsanfällig erwiesen.Such heat exchangers have hitherto been provided with a coating layer made of pure lead. One however, such a lead layer has proven to be relatively susceptible to corrosion.

Es sind Metallegierungen mit Zinn, Antimon und Blei bekannt. Beispielsweise aus DIN 1703, Seite 20, sind als Weißmetall 5 und Weißmetall 10 Zinn-Kupfer-Antimon-Bleilegierungen bekanntgeworden, deren Zinngehalte von 4,5 % bis 5,5 % reichen, der Kupfergehalt Ibgt zwischen 0,5 bis 1,5%, der Antimongehalt von 14,5 bis 16,5% und der Rest ist Blei bzw. technisch bedingte Verunreinigung.Metal alloys with tin, antimony and lead are known. For example from DIN 1703, page 20, are known as white metal 5 and white metal 10 tin-copper-antimony-lead alloys, their Tin contents range from 4.5% to 5.5%, the copper content between 0.5 and 1.5% and the antimony content from 14.5 to 16.5% and the rest is lead or technical contamination.

Aus DIN 1741 ist eine Bleispritzgußlegierung bekanntgeworden, die einen Zinngehalt von 6% und einen Antimongehalt von 9 bis 11% enthält, der Rest ist Blei bzw. technisch bedingte Verunreinigungen. Weiterhin sind aus DIN 16512 Bleilegierungen für das graphische Gewerbe bekanntgeworden, deren Zinngehalte von 2,5 bis 3,5 % bei gleichzeitigem Antimongehalt von 3,5 bis 4,5% reichen, wobei der Rest aus Blei und technisch bedingten Verunreinigungen besteht. Weitere Legierungen für Druckzwecke weisen wesentlich höhere Antimongehalte bzw. relativ große Zinngehalte auf.A lead injection molding alloy has become known from DIN 1741, which has a tin content of 6% and an antimony content of 9 to 11%, the rest is lead or technical impurities. Furthermore, lead alloys are from DIN 16512 for the graphic trade became known, their tin contents of 2.5 to 3.5% with simultaneous antimony content from 3.5 to 4.5%, with the remainder being lead and technical impurities consists. Other alloys for printing purposes have significantly higher antimony contents or relatively large amounts of tin.

Aus Merkblatt »Stahl«, Nr. 179, ist eine Bleibadlegierung mit bis zu 2,5% Zinn und 2% Antimon bekanntgeworden, die eine bessere Haftung der Bleischicht bewirken soll. Zugleich wird die außerordentlich weiche und leicht zu beschädigende Reinbleischicht durch den Antimonzusatz härter und mechanisch widerstandsfähiger. Die Badtemperatur kann durch die Zulegierung von Zinn und Antimon um 40 bis 50° C gesenkt werden.A lead bath alloy with up to 2.5% tin and 2% antimony has become known from leaflet »Stahl«, No. 179, which should bring about a better adhesion of the lead layer. At the same time it will be extraordinary soft and easy to damage pure lead layer harder and mechanical due to the addition of antimony more resistant. The bath temperature can be increased by 40 by adding tin and antimony can be reduced to 50 ° C.

"> Der vorliegenden Erfindung liegt die Aufgabe zugrunde, einen Wärmetauscher zu schaffen, der sich durch eine extrem hohe Korrosionsbeständigkeit gegenüber Abgasen, insbesondere schwefeldioxidhaltigen Abgasen, bei einer Unterschreitung des Taupunkts auszeichnet."> The present invention is based on the object to create a heat exchanger that is extremely resistant to corrosion Exhaust gases, in particular exhaust gases containing sulfur dioxide, when the temperature falls below the dew point excels.

Erfindungsgemäß besteht die Lösung der Aufgabe bei einem Wärmetauscher der eingangs näher bezeichneten Art darin, daß er mit einer an sich bekannten Legierung aus 6 bis 10% Zinn, 4,5 bis 6,5% Anti-'> mon, Rest Blei und technisch bedingte Verunreinigungen überzogen ist. Besonders vorteilhaft ist eine Uberz"glegierung mit einem Gehalt von 8% Zinn, 5,5% Antimon, Rest Blei und technisch bedingte Verunreinigungen.According to the invention, the object is achieved in a heat exchanger of the type specified in the introduction Kind in that he is with a known alloy of 6 to 10% tin, 4.5 to 6.5% anti - '> mon, the remainder lead and technical impurities is coated. One is particularly advantageous Coating alloy with a content of 8% tin, 5.5% antimony, the remainder lead and technical reasons Impurities.

-'<> Es hat sich herausgestellt, daß sich mit diesen Bleilegierungen eine unerwartet gute Korrosionsbeständigkeit gegen feuchte schwefeldioxidhaltige Abgase ergibt.- '<> It has been found that with these lead alloys an unexpectedly good corrosion resistance against humid exhaust gases containing sulfur dioxide results.

Bei für Wärmetauscher brennstoffbeheizten Wär-For heat exchangers heated by fuel

-'■> mequellen bekannten Legierungen zur Verbleiung . handelt es sich im wesentlichen um reine Blei-Zinnlegierungen mit einem Minimum von 6% Zinn, Rest Blei, bis hin zu höheren Zinngehalten.- '■> well-known alloys for lead . it is essentially pure lead-tin alloys with a minimum of 6% tin, the rest Lead, up to higher tin contents.

Die Verwendung antimonhaltiger BleilegierungenThe use of lead alloys containing antimony

)» zum Verbleiben von kupfernen Wärmetauschern hat bei der Erfindung nicht nahegelegen, weil im einen bekannten Fall (2,5% Sn, maximal 2% Sb) das Antimon zur Härtung der Bleischicht dient und damit die Bleischicht mechanisch widerstandsfähiger wird.) »Has to keep copper heat exchangers not obvious in the invention, because in a known case (2.5% Sn, maximum 2% Sb) the antimony serves to harden the lead layer and thus make the lead layer more mechanically resistant.

η Auf diese beiden Merkmale kommt es bei der Korrosionsbeständigkeit überhaupt nicht an, da eine mechanische Einwirkung auf die Verbleiungsschicht nicht stattfindet. Auch die bekannten Antimon-Bleilegierungen für Druckzwecke können nicht ohne wei-η These two characteristics are important when it comes to corrosion resistance not at all because there is no mechanical action on the lead layer. Also the well-known antimony-lead alloys for printing purposes cannot simply

4Ii teres auf die Erfindung übertragen werden, da es bei Druckmetallegierungen nicht auf gute Korrosionsbeständigkeit ankommt, sondern nur auf leichte Gießbarkeit und guten Abdruck.4Ii teres are transferred to the invention, since it is at Pressure metal alloys do not depend on good corrosion resistance, but only on easy castability and good impression.

Das erfindungsgemäße Verfahren zum VerbleienThe method according to the invention for leading

r> eines Wärmetauschers einer brennstoffbeheizten Wärmequelle geht davon aus, daß der aus Kupferblech (99,9% Cu, 0,015-0,050% P, Rest technisch bedingte Verunreinigungen, d. h. SF-Cu) bestehende Wärmetauscher in Form eines Heizschachtes mit in-r> a heat exchanger of a fuel-heated heat source assumes that the one made of copper sheet (99.9% Cu, 0.015-0.050% P, the remainder technical impurities, i.e. SF-Cu) Heat exchanger in the form of a heating shaft with internal

-iii nenliegendem Lamellenblock, durch den eine Wasserrohrschange aus Kupfer geführt ist, zuerst in Phosphorsäure getaucht, dann in Wasser gespült und anschließend in Schwefelsäure getaucht wird, worauf eine Spülung in Wasser stattfindet, an das sich ein-iii lying lamellar block through which a water pipe coil made of copper, first dipped in phosphoric acid, then rinsed in water and is then immersed in sulfuric acid, whereupon a rinse takes place in water, to which a

v, Tauchen im Flußmittel (ZnCI2 in wäßriger Lösung) anschließt. Als nächstes folgt das Eintauchen in das Bleibald, bestehend aus einer Bleilegierung mit 8% Zinn, 5,5% Antimon, Rest Blei und technisch bedingte Verunreinigungen. Zur Entfernung der Salzre-v, immersion in the flux (ZnCl 2 in aqueous solution) follows. The next step is immersion in the lead soon, consisting of a lead alloy with 8% tin, 5.5% antimony, the remainder lead and technically-related impurities. To remove the salt residue

hii ste muß anschließend in Wasser getaucht werden. Alternativ kann nach dem Verbleien das Teil in eine 5%ige wäßrige HCI-Lösung getaucht und nachfolgend mit Wasser gespült werden.hii ste must then be immersed in water. Alternatively After the lead has been left, the part can be dipped into a 5% aqueous HCl solution and subsequently be rinsed with water.

Claims (3)

Patentansprüche:Patent claims: 1. Wärmetauscher für brennstoffbeheizte Wärmequellen, dadurch gekennzeichnet, daß er mit einer Legierung aus Zinn 6-10%, Antimon 4,5-6,5%, Rest Blei und technisch bedingte Verunreinigungen überzogen ist.1. Heat exchanger for fuel-heated heat sources, characterized in that it with an alloy of tin 6-10%, antimony 4.5-6.5%, the remainder lead and technical impurities is covered. 2. Wärmetauscher für brennstoffbeheizte Wärmequellen nach Anspruch 1, dadurch gekennzeichnet, daß er mit einer Legierung aus 8% Zinn, 5,5% Antimon, Rest Blei und technisch bedingte Verunreinigungen überzogen ist.2. Heat exchanger for fuel-heated heat sources according to claim 1, characterized in that that it was made with an alloy of 8% tin, 5.5% antimony, the remainder lead and for technical reasons Impurities is coated. 3. Verfahren zum Verbleien eines Wärmetauschers einer brennstoffbeheizten Wärmequelle unter Verwendung einer Metallegierung nach Ansprüchen 1 oder 2, gekennzeichnet durch folgende Schritte:3. Method of leading a heat exchanger of a fuel-heated heat source using a metal alloy according to claims 1 or 2, characterized by the following Steps: 1. Tauchen in H3PO4
Tauchen in H2O
Tauchen in H2SO4 1. Diving in H 3 PO 4
Diving in H 2 O
Diving in H 2 SO 4 Tauchen in H2ODiving in H 2 O Tauchen in ZnCl2 Immersion in ZnCl 2 Tauchen in das Bleibad nach Anspruch 1Dipping into the lead bath according to claim 1 oder 2or 2 Tauchen in H2ODiving in H 2 O
DE19782837616 1978-08-29 1978-08-29 Heat exchanger for a fuel-heated heat source Expired DE2837616C2 (en)