DE2821490A1 - Building panel composed of cementitious aggregate - has epoxy!-coated chopped glass- or steel-fibres, and is reinforced by epoxy!-impregnated glass fibre fleece - Google Patents

Building panel composed of cementitious aggregate - has epoxy!-coated chopped glass- or steel-fibres, and is reinforced by epoxy!-impregnated glass fibre fleece

Info

Publication number
DE2821490A1
DE2821490A1 DE19782821490 DE2821490A DE2821490A1 DE 2821490 A1 DE2821490 A1 DE 2821490A1 DE 19782821490 DE19782821490 DE 19782821490 DE 2821490 A DE2821490 A DE 2821490A DE 2821490 A1 DE2821490 A1 DE 2821490A1
Authority
DE
Germany
Prior art keywords
layer
building board
board according
epoxy
stone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19782821490
Other languages
German (de)
Inventor
Guenter Thumm
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Thumm & Co
Original Assignee
Thumm & Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Thumm & Co filed Critical Thumm & Co
Priority to DE19782821490 priority Critical patent/DE2821490A1/en
Publication of DE2821490A1 publication Critical patent/DE2821490A1/en
Withdrawn legal-status Critical Current

Abstract

Building component esp. for stair steps, pedestal slabs, base plates, etc., is composed of a concrete conglomerate contg. gravel and/or natural broken stones and fibres. The fibres are relatively short, high-tensile and are coated with a plastics suitably an epoxy resin. The fibres are glass or steel-fibres. They are 10-25, esp. 15 mm long. The claimed article may have a reinforcement consisting of epoxy-resin-impregnated glass-fibre-matting, embedded in it.

Description

BauplatteBuilding board

Beschreibung Die Erfindung betrifft eine Bauplatte, insbesondere für Treppenstufen, Trittstufen, Podestplatten, Sockelleisten und dergleichen, aus einem insbesondere kunststoffgebundenen Betonwerkstein, der z.B. Kies und/oder Splitt und/oder Natursteinbrocken sowie faserförmige Bestandteile enthält. Description The invention relates to a building panel, in particular for stairs, steps, platform plates, skirting boards and the like an in particular plastic-bonded artificial stone, e.g. gravel and / or chippings and / or natural stone lumps as well as fibrous components.

Konstruktiv tragende Bauplatten aus Beton und dergleichen werden mit einer Bewehrung versehen, z.B. in Form von Stahigerippen, da Beton und Betonwerkstein in der Regel keine höheren Zugkräfte aufnehmen können.Structurally load-bearing building panels made of concrete and the like are included a reinforcement, e.g. in the form of steel ribs, as concrete and cast stone usually cannot absorb higher tensile forces.

Das Anfertigen und Einbringen der Bewehrung ist aufwendig und teuer. Außerdem wird das Gewicht von Bauplatten mit Stahlbewehrung beträchtlich erhöht, wodurch Transport und Einbau erschwert und die hier anfallenden Kosten ebenfalls höher werden.The manufacture and installation of the reinforcement is complex and expensive. In addition, the weight of construction panels with steel reinforcement is considerably increased, which makes transport and installation more difficult, and so do the costs involved get higher.

Um dem abzuhelfen, ist bereits vorgeschlagen worden, Bauteile aus Betonwerkstein mit faserförmigen Bestandteilen zu versehen, die in die Betonwerksteinmasse eingebettet sind. Diese faserförmigen Bestandteile können beispielsweise aus Asbest, Kunststoff, Glas oder Stahl bestehen.In order to remedy this, it has already been proposed to use components To provide artificial stone with fibrous components, which in the artificial stone mass are embedded. These fibrous components can, for example, consist of asbestos, Made of plastic, glass or steel.

Nachteilig hierbei ist jedoch, daß Fasern aus Glas beim Mischen der Betonwerksteinmasse durch das wirken der Gesteinsbrocken zerbrochen und weitgehend pulverisiert werden, so daß sie keine Zugkräfte mehr aufnehmen können.The disadvantage here, however, is that fibers made of glass when mixing the Concrete stone mass due to the effect of the stone chunks broken and largely are pulverized so that they can no longer absorb tensile forces.

Fasern aus Kunststoff hingegen haben keine ausreichende Zugfestigkeit und Fasern aus Stahl sind rostanfällig.In contrast, fibers made of plastic do not have sufficient tensile strength and fibers made of steel are susceptible to rust.

Die Erfindung sucht hier abzuhelfen und ihr liegt daher die Aufgabe zugrunde, eine Bauplatte der eingangs genannten Art so auszubilden, daß ihre faserförmigen Bestandteile bei der herstellung der Platte nicht beschädigt werden, sondern voll funktionsfähig erhalten bleiben.The invention seeks to remedy this and it is therefore the task based on a building board of the type mentioned in such a way that its fibrous Components in the manufacture of the plate are not damaged, but full remain functional.

Erfindungsgemäß wird dies dadurch erreicht, daß die faserförmigen Bestandteile aus zugfesten kurzen Faserstücken bestehen, die mit einem Kunstharz ummantelt sind.According to the invention this is achieved in that the fibrous Components consist of tensile short pieces of fiber that are coated with a synthetic resin are sheathed.

Vorzugsweise besteht der Überzug bzw. die Mantelschicht aus Epoxydharz, während die faserförmigen Bestandteile Glasfasern oder Stahlfasern sein können.The coating or the jacket layer preferably consists of epoxy resin, while the fibrous components can be glass fibers or steel fibers.

Vorteilhafterweise haben die Faserstücke eine Länge von etwa 10 bis etwa 25 mm, insbesondere etwa 15 mm.The fiber pieces advantageously have a length of about 10 to about 25 mm, in particular about 15 mm.

Nach einer weiteren Ausgestaltung der Erfindung wird vorgeschlagen, in einen Betonwerkstein mit Zementbindung, dem zur Steigerung der Biege- und Torsionsfestigkeit gegebenenfalls ein Kunstharz beigegeben sein kann, eine Glasfaserschicht oder Glasfasermatte als Bewehrung einzubringen, die vorzugsweise mit einem Kunstharz, z.B. Epoxydharz, getränkt ist.According to a further embodiment of the invention, it is proposed that in a cement-bonded concrete block, which increases the flexural and torsional strength If necessary, a synthetic resin can be added, a glass fiber layer or glass fiber mat to be introduced as reinforcement, preferably with a synthetic resin, e.g. epoxy resin, is soaked.

Hierbei wird vorteilhafterweise auf eine noch nasse Betonwerksteinschicht, deren Festigkeit über der Klasse BII liegt, eine kunstharzgetränkte Glasfaserschicht oder Glasfasermatte aufgebracht, deren Abmessungen vorzugsweise etwas kleiner sind als die der Betonwerksteinschicht, worauf auf die Glasfaserschicht eine weitere nasse Betonwerksteinschicht aufgebracht wird, wonach man das Ganze aushärten läßt.In this case, it is advantageous to apply a layer of concrete ashlar that is still wet, whose strength is above class BII, a synthetic resin-soaked fiberglass layer or glass fiber mat, the dimensions of which are preferably somewhat smaller than that of the cast stone layer, followed by another layer on the glass fiber layer wet cast stone layer is applied, after which the whole thing is allowed to harden.

Beispielsweise Ausführungsformen der Erfindung werden nachfolgend anhand der Zeichnung erläutert, in der Fig. 1 schematisch im Schnitt eine mit faserförmigen Bestandteilen versehene Bauplatte zeigt.Exemplary embodiments of the invention are provided below explained with reference to the drawing in which Fig. 1 schematically in section shows a building board provided with fibrous components.

Fig. 2 zeigt im Schnitt eine mit einer Kunststoffschicht ummantelte Glasfaser.Fig. 2 shows in section a coated with a plastic layer Glass fiber.

Fig. 3 zeigt schematisch im Schnitt eine Bauplatte mit einer Bewehrung aus einer Glasfaserschicht oder Glasfasermatte.Fig. 3 shows schematically in section a building panel with reinforcement made of a glass fiber layer or glass fiber mat.

Fig. 1 zeigt schmatisch im Schnitt eine Bauplatte 10 aus einem tonwerkstein, die sich z.B. zur Verwendung für Treppenstufen oder Trittstufen, aber auch für Podestplatten, Sockelleisten und dergleichen eignet. Die Platte 10 kann z.B.Fig. 1 shows schematically in section a building panel 10 made of a clay stone, which can be used e.g. for stairs or treads, but also for platform plates, Skirting boards and the like are suitable. The plate 10 can e.g.

Kies 16 und/oder Splitt1ind/oder Natursteinbrocken 12 gewünschter Körnung enthalten. Das Material ist vorzugsweise kunststoffgebunden, es ist aber auch eine Zementbindung möglich. Auch kann bei Verwendung einer Zementbindung Kunstharz beigegeben werden, um die Biege- und Drehfestigkeit der Platte zu steigern.Gravel 16 and / or chippings / or natural stone chunks 12 are more desirable Grit included. The material is preferably plastic-bonded, but it is cement binding is also possible. Synthetic resin can also be used when using a cement bond added to increase the bending and torsional strength of the plate.

Die Bauplatte 10 nach Fig. 1 enthält ferner faserförmige Bestandteile 18, die wie Fig. 2 zeigt, aus einem Kern und einem Mantel bestehen. Der Eiern besteht z.B. aus einer Glasfaser mit einer Länge von etwa 10 bis 25 mm vorzugsweise etwa 15 mm, während die Überzugsschicht, die die Glasfaser 20 vollständig ummantelt, aus einem Kunstharz, vorzugsweise einem Epoxydharz besteht.The building board 10 according to FIG. 1 also contains fibrous components 18, which as FIG. 2 shows, consist of a core and a cladding. The eggs are made e.g. from a glass fiber with a length of about 10 to 25 mm, preferably about 15 mm, while the coating layer, which completely encases the glass fiber 20, consists of a synthetic resin, preferably an epoxy resin.

Die Glasfasern 20 werden mit dem Epoxydharz getränkt und das Ganze ausgehärtet, so daß sie vollständig von dem Epoxydharz-Mantel 22 umschlossen sind.The glass fibers 20 are impregnated with the epoxy resin and the whole cured so that they are completely enclosed by the epoxy resin jacket 22.

Danach werden die ummantelten Glasfasern in die Betonwerksteinmischung eingebracht bzw. die einzelnen Bestandteile, die den späteren Betonwerkstein bilden, einschließlich der Fasern 18 in üblicher Weise gemischt und in Formen gegossen, so daß die Fasern 18 wahllos in den Platten verteilt sind.Then the coated glass fibers are inserted into the concrete mix brought in or the individual components that form the later cast stone, including of fibers 18 mixed in a conventional manner and poured into molds so that the fibers 18 are randomly distributed in the plates.

Der Mantel 22 aus dem Epoxydharz schützt die Glasfasern 20 beim Mischen und Walken gegen Bruch, so daß die Fasern im fertigen Betonwerkstein unbeschädigt und funktionsfähig enthalten sind.The jacket 22 made of the epoxy resin protects the glass fibers 20 during mixing and fulling against breakage, so that the fibers in the finished cast stone are undamaged and functional are included.

Die Glasfasern geben dem Betonwerkstein bzw. der fertigen Platte die gewünschte Festigkeit, während sie, wie bereits erwähnt, während des Mischvorganges durch den Kunststoffmantel geschützt werden.The glass fibers give the artificial stone or the finished slab the desired strength while, as already mentioned, during the mixing process be protected by the plastic jacket.

Bei Versuchen hat sich gezeigt, daß die Biegefestigkeit eines auf diese Weise hergestellten und mit kurzen Fasern versehenen Steines bzw. einer Bauplatte derjenigen einer mit einer lamellierten Glasmatte versehenen Bauplatte entsprach, bezogen auf einen Mindestglasanteil von 1kg Glas auf 60 dm3 Betonwerksteinmasse.Tests have shown that the flexural strength of a this way produced and provided with short fibers stone or a building board corresponded to that of a building board provided with a laminated glass mat, based on a minimum glass content of 1kg glass per 60 dm3 cast stone mass.

Anstelle der Glasfasern können beispielsweise auch Stahlfasern oder auch andere Fasern mit ausreichender Festigkeit verwendet werden.Instead of the glass fibers, for example, steel fibers or other fibers with sufficient strength can also be used.

Die Bauplatte 10 nach Fig. 3 enthält eine Glas faserschicht 34 oder eine Glasfasermatte oder ein Glasfasergewebe, das ins Innere der Bauplatte 10 eingebettet ist.The building board 10 of FIG. 3 contains a glass fiber layer 34 or a glass fiber mat or a glass fiber fabric that is embedded in the interior of the building board 10 is.

Bei der Herstellung dieser Bauplatte wird eine untere Betonwerksteinschicht z.B. aus Kies undlbder Splitt und/oder Natursteinbrocken gebildet, wobei der Betonwerkstein zementgebunden ist, jedoch dem gemischten Naßbeton einige Prozent Kunstharz beigegeben werden können, um die Biegefestigkeit und die Torsionsfestigkeit zu steigern.A lower layer of cast stone is used in the manufacture of this construction panel e.g. formed from gravel and stone chippings and / or natural stone chunks, whereby the artificial stone is cement-bound, but the mixed wet concrete has a few percent synthetic resin added can be to increase the flexural strength and torsional strength.

Auf den noch nassen Beton bzw. auf die noch nasse Schicht 30 wird die Glasfaserschicht 34 aufgebracht, die mit einem Kunstharz, vorzugsweise einem Epoxydharz, getränkt ist.On the still wet concrete or on the still wet layer 30 is the fiberglass layer 34 applied, which is with a synthetic resin, preferably a Epoxy resin, is impregnated.

Die Abmessungen der Glasfaserschicht 34, d.h. ihre Länge und ihre Breite, sind etwas geringer als die entsprechenden Abmessungen der Betonwerksteinschicht 30, so daß die letztere an allen Seiten etwas über die Glas faserschicht 34 übersteht. Nunmehr wird auf die nasse Betonwerksteinschicht 30 und auf die getränkte Glasfaserschicht 34 eine obere nasse Betonwerksteinschicht aufgebracht, die ebenfalls z.B. aus Kies und/oder Splitt und/oder Natursteinbrocken sowie Zement besteht. Die obere Betonwerksteinschicht 32 verbindet sich vollständig mit der unteren Betonwerksteinschicht 30 und mit der Glasfaserschicht 34, wobei die letztere allseitig vollständig umschlossen wird, so daß sie voll in der späteren Bauplatte 10 eingebettet und von außen nicht sichtbar ist.The dimensions of the fiberglass layer 34, i.e. its length and its Width, are slightly smaller than the corresponding dimensions of the concrete layer 30, so that the latter protrudes slightly over the glass fiber layer 34 on all sides. Now is applied to the wet cast stone layer 30 and the soaked fiberglass layer 34 an upper wet cast stone layer is applied, which is also made of gravel, for example and / or chippings and / or natural stone chunks and cement. The upper cast stone layer 32 connects completely with the lower cast stone layer 30 and with the Glass fiber layer 34, the latter being completely enclosed on all sides, so that they are fully embedded in the later building board 10 and not visible from the outside is.

Die Schichten 30 und 32 und die Glas faserschicht 34 läßt man dann gemeinsam aushärten.Layers 30 and 32 and fiberglass layer 34 are then left cure together.

Die in der Zeichnung angedeutete Fuge 36 ist in der fertigen Bauplatte 10 nicht mehr sichtbar, da, wie erwähnt, die Abmessungen des Glasfasergewebes 34 kleiner sind als die Außenabmessungen der Bauplatte und die beiden Betonwerksteinschichten 30 und 32 sich fugenlos miteinander verbinden.The joint 36 indicated in the drawing is in the finished building board 10 no longer visible because, as mentioned, the dimensions of the glass fiber fabric 34 are smaller than the external dimensions of the building board and the two layers of cast stone 30 and 32 join together seamlessly.

Es hat sich gezeigt, daß die Glasfasermatte 34 insbesondere bei Verwendung von Epoxydharz einwandfrei aushärtet.It has been found that the fiberglass mat 34, especially when used of epoxy resin hardens perfectly.

Als Beton wird ein Material verwendet, das über der Festigkeitsklasse B II liegt, für die keine Eisenarmierung vorgeschrieben ist. Bei einem solchen Beton bietet die Glasfaserschicht eine zuverlässige und einwandfreie Bewehrung.A material is used as concrete that is above the strength class B II, for which no iron reinforcement is prescribed is. at the fiberglass layer offers such a concrete a reliable and flawless one Reinforcement.

L e e r s e i t eL e r s e i t e

Claims (8)

Ansprüche Bauplatte, insbesondere für Treppenstufen, Trittstufen, Podestplatten, Sockelleisten und dergleichen, aus einem insbesondere kunststoffgebundenen Betonwerkstein mit z.B. Kies und/oder Splitt und/oder Natursteinbrocken, sowie mit faserförmigen Bestandteilen, dadurch g e -k e n n z e i c h n e t , daß die faserförmigen Bestandteile (18) zugfeste kurze Faserstücke (20) sind, die mit Kunstharz (22) ummantelt sind. Requirements of building board, especially for stairs, steps, Platform plates, skirting boards and the like, made especially of a plastic-bonded one Concrete stone with e.g. gravel and / or chippings and / or natural stone chunks, as well as with fibrous components, in that the fibrous Components (18) are tensile short fiber pieces (20) which are coated with synthetic resin (22) are. 2. Bauplatte nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , daß die Mantelschicht (22) aus Kunstharz, insbesondere Epoxydharz besteht.2. Building board according to claim 1, characterized in that g e k e n n -z e i c h n e t that the jacket layer (22) consists of synthetic resin, in particular epoxy resin. 3. Bauplatte nach Anspruch 1 oder 2, dadurch g e k e n n -z e i c h n e t , daß die faserförmigen Bestandteile Glasfasern sind.3. Building board according to claim 1 or 2, characterized in that g e k e n n -z e i c It should be noted that the fibrous constituents are glass fibers. 4. Bauplatte nach Anspruch 1 oder 2, dadurch g e k e n n -z e i c h n e t , daß die faserförmigen Bestandteile Stahlfasern sind.4. Building board according to claim 1 or 2, characterized in that g e k e n n -z e i c It should be noted that the fibrous constituents are steel fibers. 5. Bauplatte nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , daß die Faserstücke eine Länge von etwa 10 bis 25 mm, insbesondere 15 mm, aufweisen.5. Building board according to one of the preceding claims, characterized g e it is not indicated that the fiber pieces have a length of about 10 to 25 mm, in particular 15 mm. 6. Bauplatte nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , daß sie wenigstens eine allseits von dem Betonwerkstein umschlossene Glas faserschicht oder Glasfasermatte (34) als Bewehrung enthält.6. Building board according to claim 1, characterized in that g e k e n n -z e i c h n e t that they have at least one layer of glass fibers enclosed on all sides by the cast stone or glass fiber mat (34) as reinforcement. 7. Bauplatte nach Anspruch 6, dadurch g e k e n n -z e i c h n e t , daß die Glasfaserschicht oder Glasfasermatte (34) mit einem Kunstharz, vorzugsweise Epoxydharz, getränkt ist.7. Building board according to claim 6, characterized in that g e k e n n -z e i c h n e t that the fiberglass layer or fiberglass mat (34) with a synthetic resin, preferably Epoxy resin, is impregnated. 8. Verfahren zur Herstellung einer Bauplatte nach Anspruch 6, dadurch g e k e n n z e i c h n e t , daß auf eine noch nasse Betonwerksteinschicht eine vorzugsweise kunstharzgetränkte Glas faserschicht (34) aufgebracht wird, dtEren Abmessungtn vorzugsweise etwas kleiner sind als die der Betonwerksteinschicht, daß dann auf die Betonwerksteinschicht (30) und die Glasfaserschicht (34) eine weitere nasse Betonwerksteinschicht (32) aufgebracht wird, worauf man das Ganze aushärten läßt.8. A method for producing a building board according to claim 6, characterized it is not noted that a layer of cast stone is still wet preferably synthetic resin-soaked fiberglass layer (34) is applied, dtEren Dimensions tn are preferably slightly smaller than that of the cast stone layer that then on the concrete stone layer (30) and the glass fiber layer (34) another wet cast stone layer (32) is applied, whereupon the whole thing is hardened leaves.
DE19782821490 1978-05-17 1978-05-17 Building panel composed of cementitious aggregate - has epoxy!-coated chopped glass- or steel-fibres, and is reinforced by epoxy!-impregnated glass fibre fleece Withdrawn DE2821490A1 (en)