DE2724022A1

DE2724022A1 - Moulded core made from ferrite material in two halves - has weldable metallised sections on outside of each half aligned and joined

Info

Publication number: DE2724022A1
Application number: DE19772724022
Authority: DE
Inventors: Dagobert Dipl Ing Klein; Walter Schmidbauer
Original assignee: Standard Elektrik Lorenz AG
Current assignee: Alcatel Lucent Deutschland AG
Priority date: 1977-05-27
Filing date: 1977-05-27
Publication date: 1978-12-07
Also published as: AU3630078A

Abstract

The moulded coil core consists of two halves and is used in filter circuits or repeaters in telecommunication networks. The core is made from a ferrite material in order to increase the inductance. Each half of the core (4, 5) is made with a solderable metallised area (10) which extends to the rim (6) on an exposed side. There is one such area on each of two opposite sides of each half. The metallised areas on the two halves are aligned and soldered together. This is intended to speed up production of these components as it is not necessary to stick the parts together and wait for the bonding agent to harden.

Description

Elektrische Spule mit Massekern Electric coil with earth core

Stand der Technik Die Erfindung betrifft einen aus zwei Hälften bestehenden Massekern.Background of the Invention The invention relates to a two-halved one Ground core.

Elektrische Spulen, die als Filterspulen oder Übertrager in Netzwerken der Nachrichtentechnik verwendet werden, weisen einen Massekern aus Ferrit-Werkstoff auf, der die Induktivität erhöht. Solche Massekerne bestehen aus zwei gleichen Hälften, die erst beim Zusammenbauen der gesamten aus Spule und Massekern bestehenden Induktivität zusammengesetzt und miteinander dauerhaft verbunden werden.Electrical coils used as filter coils or transformers in networks used in communications technology have a ground core made of ferrite material on, which increases the inductance. Such mass cores consist of two equal halves, the inductance that only exists when the entire coil and ground core are assembled put together and permanently connected to each other.

Dazu ist es bekannt, die beiden Massekernhälften an den bei der Verbindung aufeinanderstoßenden Flächen miteinander zu verkleben. Ein derart klebter aus zwei Hälften bestehender Massekern hat folgende Nachteile: Die Klebverbindung ist feuchtigkeitsempfindlich. Die Klebefuge wirkt wie ein Luftspalt. Bei der Fertigung der Induktivität ist nach dem Kleben eine verhältnismäßig lange Wartezeit bis zur weiteren Verarbeitung einzuhalten.For this purpose, it is known to attach the two ground core halves to the connection to glue abutting surfaces together. Such a glued one out of two Halves of an existing mass core have the following disadvantages: The adhesive bond is sensitive to moisture. The glue joint acts like an air gap. When manufacturing the inductance is after Adhere to a relatively long waiting time before gluing until further processing.

Aufgabe Es ist daher die Aufgabe der Erfindung, einen Massekern mit zwei Hälften und eine damit hergestellte Induktivität anzugeben, bei der die Verbindung der beiden Massekernhälften von den aufgeführten Nachteilen frei ist.Task It is therefore the task of the invention to have a ground core specify two halves and an inductance produced with them, in which the connection of the two halves of the mass core is free from the disadvantages listed.

Lösung Die Aufgabe wird wie in den Patentansprüchen angegeben gelöst.Solution The object is achieved as indicated in the patent claims.

Beschreibung Die Erfindung wird nun anhand der Zeichnungen beispielsweise näher erläutert.Description The invention will now be exemplified with reference to the drawings explained in more detail.

Es zeigen: Fig.l eine Induktivität mit einem Ferrit-RM-Kern, dessen Hälften an zwei gegenüberliegenden Stellen miteinander verbunden sind; Fig.2 eine Induktivität mit einem Ferrit-RM-Kern, dessen Hälften an vier jeweils paarweise gegenüberliegenden Stellen miteinander verbunden sind.They show: Fig.l an inductance with a ferrite RM core, whose Halves are connected to each other at two opposite points; Fig.2 a Inductance with a ferrite RM core, the halves of which are connected to four in pairs opposite points are connected to each other.

Die Induktivität nacnFig.1 besteht aus einem Spulenkörper 1, auf dem die Spulenwicklung 2 aufgebracht ist, und der mit Anschlußstiften 3 versehen ist. Diese Spule befindet sich innerhalb eines Ferrit-RM-Kernes bekannter Form mit den beiden Kernhälften 4 und 5, die an der Fuge 6 zusammenstoßen. Im Inneren der Spulenwicklung 2 verläuft der durch eine Öffnung 7 angedeutete Butzen des Kerns parallel zu dessen Schenkeln, die die Spulenwicklung seitlich umgeben.The inductance according to Fig. 1 consists of a coil former 1 on which the coil winding 2 is applied, and which is provided with connecting pins 3. This coil is located within a ferrite RM core of known shape with the two core halves 4 and 5, which meet at the joint 6. Inside the coil winding 2 runs through an opening 7 indicated slugs of the core parallel to the legs that surround the coil winding laterally.

Der Kern weist an seinem Umfang zwischen den Schenkeln zwei relativ große Aussparungen 8 und 9 auf, an denen die Anschlußstifte 3 der Spule herausgeführt sind. Erfindungsgemäß sind Teile der Außenfläche der Kernhälfte 4 und Teile der Außenfläche der Kernhälfte 5, in jeweils bis zum Rand 6 der jeweiligen Kernhälfte reichenden Bereichen, die beim zusammengesetzten Kern aneinander grenzen, mit einer lötbaren Metallisierung 10 versehen.The core has two relative on its circumference between the legs large recesses 8 and 9, where the pins 3 of the coil led out are. According to the invention, parts of the outer surface of the core half 4 and parts of the Outer surface of the core half 5, in each case up to the edge 6 of the respective core half reaching areas that adjoin each other in the composite core, with a solderable metallization 10 is provided.

Zum Weichlöten eignet sich eine dünne Goldschicht, die auf einer anderen Metallschicht beispielsweise aus Chrom oder einer Nickel/Chrom-Legierung oder aus Titan aufgebracht ist. Als Diffusionssperre zwischen der unteren Metallschicht und der Goldschicht läßt sich beispielsweise Palladium verwenden.A thin gold layer on top of another is suitable for soft soldering Metal layer made, for example, of chromium or a nickel / chromium alloy or of Titanium is applied. As a diffusion barrier between the lower metal layer and Palladium, for example, can be used for the gold layer.

Zum Hartlöten eignet sich eine dünne Kupferschicht.A thin layer of copper is suitable for brazing.

Die derart metallisierten Außenflächenteile 10 der beiden Massekernhälften 4 und 5 sind im fertigen Zustand der Induktivität nach Fig.1 miteinander verlötet. Das Lot ist in der Fig.1 mit 11 bezeichnet.The outer surface parts 10 of the two ground core halves metallized in this way 4 and 5 are soldered together in the finished state of the inductance according to FIG. The solder is denoted by 11 in FIG.

Die Fig.2 zeigt schließlich eine Induktivität, die wie die in Fig.1 gezeigte aufgebaut ist. Jedoch sind hier entlang dem Umfang des Ferrit-RM-Kernes anstelle von zwei Lötstellen vier Lötstellen verteilt, von denen sich jeweils zwei bezüglich der Spule paarweise gegenüber liegen. In der Fig.2 sind lediglich die beiden Lötstellen iOa, 11a und lob, lib und nicht die beiden diesen jeweils bezüglich der Spule gegenüberliegenden Lötstellen sichtbar. Falls es aus 6Ertigungs technischen oder Stabilitätsgründen vorteilhaft oder notwendig ist, entlang dem Umfang am Rand 6 der beiden Kernhälften 4 und 5 noch weitere Lötstellen vorzusehen, so können diese ohne weiteres in der dargestellten Weise ausgebildet sein, oder es kann eine durchgehende Metallisierung und Verlötung vorhanden sein. Zur zusätzlichen Stabilisierung enthält der Ferrit-RM-Kern an seinen Ober- und Unterseiten paarweise gegenüberliegende Vertiefungen 12, in die nicht gezeigte Halteklammern eingreifen können.Finally, FIG. 2 shows an inductance which, like that in FIG shown is constructed. However, here are along the perimeter of the ferrite RM core instead of two soldering points, four soldering points are distributed, two of which are each are opposite in pairs with respect to the coil. In Figure 2 are only the both solder joints ok, 11a and lob, lib and not the two of these respectively the Coil opposite soldering points visible. If it comes from manufacturing technical or stability reasons is advantageous or necessary, along the circumference at the edge 6 of the two core halves 4 and 5 also provide further soldering points, so these can be easily formed in the manner shown, or it can be a continuous Metallization and soldering be present. Contains for additional stabilization the ferrite RM core on its upper and lower sides in pairs opposite recesses 12, can engage in the retaining clips, not shown.

LeerseiteBlank page

Claims

Patent claims 5.8U8 two equal halves existing mass core, characterized in that each half (4,5) at least on two opposite Outer surface parts up to the edge (6) of the open side with a solderable metallization (10) is provided.

2. Inductance, consisting of at least one winding and one Ground core according to Claim 1, characterized in that the metallized outer surface parts (10) of the two ground core halves (4,5) adjoin each other and soldered together (11) are.