DE2700823C3 - Dental cast alloy based on silver - Google Patents
Dental cast alloy based on silverInfo
- Publication number
- DE2700823C3 DE2700823C3 DE2700823A DE2700823A DE2700823C3 DE 2700823 C3 DE2700823 C3 DE 2700823C3 DE 2700823 A DE2700823 A DE 2700823A DE 2700823 A DE2700823 A DE 2700823A DE 2700823 C3 DE2700823 C3 DE 2700823C3
- Authority
- DE
- Germany
- Prior art keywords
- silver
- palladium
- gold
- alloy
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
2020th
2525th
Die Erfindung betrifft eine Gold, Kupfer und Palladium enthaltende Dentalgußlegierung auf Silberbasis für die Herstellung von Kronen, Brücken und anderen dentalen Prothesenteilen.The invention relates to a silver-based dental casting alloy containing gold, copper and palladium for the production of crowns, bridges and other dental prosthesis parts.
Aus der US-Patentschrift 20 50 077 ist es bekannt, die Korrosionsfestigkeit von Dentallegierungen aus Silber, Palladium und Kupfer durch Zugabe von Gold zu verbessern. Dabei wird den Legierungen so viel Gold zugesetzt, daß ein Gewichtsverhältnis von Palladium zu Gold von 0,36 bis 0,74 zu 1 erreicht wird.From US patent specification 20 50 077 it is known to determine the corrosion resistance of dental alloys made of silver, To improve palladium and copper by adding gold. In doing so, the alloys become so much gold added that a weight ratio of palladium to gold of 0.36 to 0.74 to 1 is achieved.
Aufgabe der Erfindung ist es, eine Gold, Palladium, Silber und Kupfer enthaltende Dentalgußlegierung zu schaffen, die eine gute Korrosionsfestigkeit und Anlaufbeständigkeit bei homogenem, feinkrönigem Gefüge und gute mechanische Eigenschaften besitzt.The object of the invention is to provide a dental casting alloy containing gold, palladium, silver and copper create good corrosion resistance and tarnish resistance with homogeneous, fine-grained Has structure and good mechanical properties.
Die Aufgabe wird erfindungsgemäß gelöst durch eine Legierung aus 35% Gold, 10 bis 14% Kupfer, 7 bis 10,5% Palladium, 0,1 bis 2% Indium, 0,05 bis 0,5% Iridium und/oder Ruthenium und mindestens 40% Silber als Rest.The object is achieved according to the invention by an alloy of 35% gold, 10 to 14% copper, 7 to 10.5% palladium, 0.1 to 2% indium, 0.05 to 0.5% iridium and / or ruthenium and at least 40% Silver as remainder.
Diese Legierung weist ein Gewichtsverhältnis von Palladium zu Gold von 0,2 bis 0,3 zu 1 auf.This alloy has a weight ratio of palladium to gold of 0.2 to 0.3 to 1.
Der Legierung können vorteilhafterweise bis zu 5% Platin zugesetzt werden.Up to 5% platinum can advantageously be added to the alloy.
Besonders bewährt hat sich die Legierung aus 41,5% Silber, 35% Gold, 11,95% Kupfer, 10% Palladium, 0,5% Indium, 0,05% Iridium und Ruthenium und 1% Platin mit einem Gewichtsverhältnis von Palladium zu Gold von 0,28 zul.The alloy of 41.5% silver, 35% gold, 11.95% copper, 10% palladium, 0.5% has proven to be particularly effective. Indium, 0.05% iridium and ruthenium and 1% platinum with a weight ratio of palladium to gold from 0.28 perm.
Die erfindungsgemäße Lagiemng besitzt eine gelbe Farbe; ihr Schmelzbereich liegt zwischen 890 und 940° C.The Lagiemng according to the invention has a yellow color; their melting range is between 890 and 940 ° C.
Der besondere Vorteil der erfindungsgemäßen Legierung zeigt sich, wenn sie in einem Tiegel eingeschmolzen, dann in eine vorbereitete Gießform abgegossen und anschließend das erhaltene Gußstück, sobald es eine Temperatur von etwa 7000C aufweist, zusammen mit der Gießform in Wasser abgeschreckt wird.The particular advantage of the alloy according to the invention is shown when it is melted in a crucible, then poured into a prepared casting mold and then the casting obtained, as soon as it has a temperature of about 700 ° C., is quenched in water together with the casting mold.
Das durch das Abschrecken in der Gießform gebildete feinkörnige Gefüge ist homogen und weist keine heterogenen Bestandteile auf.The fine-grain structure formed by the quenching in the casting mold is homogeneous and shows no heterogeneous components.
Damit ist die wichtigste Voraussetzung für die Anlaufbeständigkeit gegeben.This is the most important prerequisite for tarnishing resistance.
Die durch das Abschrecken in der Gießform teilweise vergütete Legierung bleibt blank und kann direkt, das heißt ohne Nachbehandlung, weiterverarbeitet werden. Die sonst übliche Homogenisierungsglühung an Luft und das nachfolgende Absäuern zur Entfernung des sich bei diesem Glühen bildenden Oxidbelags werden überflüssig.The alloy, which is partially tempered by quenching in the casting mold, remains bright and can be used directly means that it can be processed further without any post-treatment. The usual homogenization annealing in air and the subsequent acidification to remove the oxide scale that forms during this annealing superfluous.
Im Gegensatz zu der erfindungsgemäßen Legierung zeigt eine Vergleichslegierung aus 35% Gold, 13% Palladium, 34% Silber, 17% Kupfer und 1% Zink mit einem Gewichtsverhältnis von Palladium zu Gold von 0,37 :1 nach dem Abschrecken in der Gießform kein homogenes Gefüge, sie muß daher zusätzlich weichgeglüht und vergütet werden.In contrast to the alloy according to the invention, a comparison alloy made of 35% gold, 13% Palladium, 34% silver, 17% copper and 1% zinc with a weight ratio of palladium to gold of 0.37: 1 after quenching in the casting mold, no homogeneous structure, it must therefore also be soft-annealed and be remunerated.
Obwohl die erfindungsgemäße Legierung im Vergleich zu der aus der US-Patentschrift 20 50 077 bekannten einen durch das niedrige Gewichtsverhältnis von Palladium zu Gold bedingten höheren Silber-Gehalt aufweist, besitzt sie eine ebenso gute Korrosionsfestigkeit Although the alloy according to the invention compared to that from US Pat. No. 20 50 077 known a higher silver content due to the low weight ratio of palladium to gold has, it has an equally good corrosion resistance
Zur Bestimmung des Korrosionsverhaltens wurden Proben aus einer Legierung gemäß der Erfindung aus 41,5% Silber, 35% Gold, 11,95% Kupfer, 10% Palladium, 0,5% Indium, 0,05% Iridium und Ruthenium und 1% Platin und aus einer Vergleichslegierung aus 35% Gold, 13% Palladium, 34% Silber, 17% Kupfer und 1% Zink unter gleichen Bedingungen in Schwefelsäure, Salpetersäure bzw. Salzsäure gelagert. Der dabei eintretende Gewichtsverlust ist bei beiden Legierungen praktisch gleich.To determine the corrosion behavior, samples were made from an alloy according to the invention 41.5% silver, 35% gold, 11.95% copper, 10% palladium, 0.5% indium, 0.05% iridium and ruthenium and 1% platinum and a comparative alloy of 35% gold, 13% palladium, 34% silver, 17% copper and 1% zinc stored under the same conditions in sulfuric acid, nitric acid or hydrochloric acid. The one with it The weight loss that occurs is practically the same for both alloys.
So besitzt die erfindungsgemäße Legierung eine derjenigen der aus der US-Patentschrift 20 50 077 bekannten Legierung entsprechende Korrosionsfestigkeit, ist aber im Vergleich zu dieser feinkörniger und homogener und somit anlaufbeständiger und läßt sich einfacher verarbeiten.The alloy according to the invention has one of those from US Pat. No. 2,050,077 known alloy corresponding corrosion resistance, but is more fine-grained and compared to this more homogeneous and therefore more tarnish-resistant and easier to process.
Auch ist sie durch den zugunsten des Silberanteils erniedrigten Palladiumgehalt preisgünstiger zu erstellen. It is also cheaper to produce because the palladium content is lowered in favor of the silver content.
Claims (4)