DE2640390A1

DE2640390A1 - Hollow profiles of glass fibre-reinforced Portland cement compsn., mfr - prepd. by coating rigid plastic web with uncured compsn. then folding into shape (NL170377)

Info

Publication number: DE2640390A1
Application number: DE19762640390
Authority: DE
Inventors: Jan Hendrik Veldhoen
Original assignee: Individual
Current assignee: Individual
Priority date: 1975-09-15
Filing date: 1976-09-08
Publication date: 1977-03-24
Also published as: NL7510813A

Abstract

Mfr. of hollow profiles of polygonal cross-section comprises providing a relatively rigid plastic web, pref. of polypropylene, of which the width is equal to the desired length of the profile, with blend lines which extend in the width direction and of which the spacing is equal to the desired distances between profile edges. The web is then coated while flat with a layer of the uncured reinforced cement compsn. of which the thickness is equal to the desired wall thickness of the profile, then folded together with the cement layer along the bend lines into a shape corresponding to the finished profile and fixed in this spape. Finally the cement compsn. is allowed to cure, and the plastic web is removed. Compsn. can be extruded without breaking the glass fibres.

Description

Verfahren zur Herstellung von HohlprofilenProcess for the production of hollow profiles

Die Erfindung betrifft ein Verfahren zur Herstellung von Hohlprofilen mit im wesentlichen polygonalem Querschnitt aus einer hauptsächlich aus Portlandzement bestehenden, mit alkalibeständigen Mineralfasern, insbesondere Glasfasern armierten Zementmasse, sowie ein durch Anwendung dieses Verfahrens erhaltenes Hohlprofil. The invention relates to a method for producing hollow profiles with a substantially polygonal cross-section made from a mainly portland cement existing, reinforced with alkali-resistant mineral fibers, especially glass fibers Cement mass, as well as a hollow profile obtained by using this method.

Die Anwendung von mit alkalibeständigen Glasfasern armiertem Portlandzement als Konstruktionsmaterial ist u.a. aus den niederländischen Offenlegungsschriften 67.09510 und 68.10823 bekannt. The use of portland cement reinforced with alkali-resistant glass fibers as a construction material is, inter alia, from the Dutch Offenlegungsschrift 67.09510 and 68.10823 known.

Das genannte Material hat eine verhältnismässig grosse Festigkeit und eignet sich demzufolge zur Herstellung von Bauelementen mit niedrigem Gewicht. The material mentioned has a relatively high strength and is therefore suitable for the production of components with low weight.

Die Herstellung von Hohlprofilen mit im wesentlichen polygonalem Querschnitt aus dem erwähnten Material bringt jedoch Schwierigkeiten mit sich, weil das Material sich nicht extrudieren lässt. Bei der Extrusion brechen nämlich die Glasfasern. The production of hollow profiles with essentially polygonal However, cross-section from the material mentioned brings difficulties because the material cannot be extruded. This is because they break during extrusion Fiberglass.

Die Erfindung hat den Zweck, diesen Nachteil aufzuheben und ein zweckmässiges Verfahren zur Herstellung von Hohlprofilen mit im wesentlichen polygonalem Querschnitt aus dem genannten Material zu schaffen. The invention has the purpose of eliminating this disadvantage and an expedient Process for the production of hollow profiles with a substantially polygonal cross section to create from the said material.

Das Verfahren gemäss der Erfindung ist dadurch gekennzeichnet, dass eine verhältnismässig steife Kunststoffbahn, deren Breite der gewunschten Länge des Profils entspricht, mit in der Breitenrichtung verlaufenden Biegelinien versehen wird, deren gegenseitige Abstände den gewunschten Abständen der Profilkanten entsprechen, woraufhin die Bahn in flachem Zustand mit einer Schicht der ungehärteten armierten Zementmasse bekleidet wird, deren Dicke annähernd der gewUnschten Wandstärke des Profils entspricht, und dass die Bahn anschliessend zusammen mit der Zementschicht gemäss den Biegelinien in eine dem Profil entsprechende Gestalt gefaltet und in dieser Gestalt festgelegt wird, woraufhin man die Zementmasse aushärten lässt und die Kunststoffbahn entfernt. The method according to the invention is characterized in that a relatively stiff plastic sheet, the width of which is the desired length of the profile, provided with bending lines running in the width direction whose mutual distances correspond to the desired distances between the profile edges, whereupon the sheet in flat condition with a layer of the uncured reinforced Cement mass is covered, the thickness of which is approximately the desired wall thickness of the Profile corresponds, and that the web then together with the cement layer folded according to the bending lines in a shape corresponding to the profile and in this shape is set, whereupon the cement mass is allowed to harden and removed the plastic sheet.

Vorzugsweise wird die Kunststoffbahn mittels Klemmen in der gewünschen Gestalt festgelegt; man kann zu diesem Zweck jedoch auch andere Mittel, z.B. Klebebänder verwenden. Preferably, the plastic web is desired by means of clamps in the Shape fixed; however, other means such as adhesive tape can be used for this purpose use.

Bei einer zweckmässigen AusfUhrungsform der Erfindung besteht die Kunststoffbahn aus Polypropylen. Dieses Material hat den Vorteil, dass es sich leicht gemäss scharfen Linien umfalten lässt, so dass die Biegelinien als Gelenke wirken. Die Aushärtung der Zementmasse kann mit Dampf stattfinden. In an expedient embodiment of the invention the Plastic sheet made of polypropylene. This material has the advantage that it is light can be folded according to sharp lines so that the bending lines act as joints. The hardening of the cement mass can take place with steam.

Die Erfindung wird anhand der Zeichnung, in der ein Ausfunrungsbeispiel dargestellt ist, näher erläutert. The invention is based on the drawing, in which an exemplary embodiment is shown, explained in more detail.

Die Fig. 1 zeigt eine Kunststoffbahn, die mit Biegelinien versehen und mit einer Schicht der ungehärteten armierten Zementmasse bekleidet worden ist. Fig. 1 shows a plastic sheet provided with bending lines and has been covered with a layer of the unhardened reinforced cement compound.

Die Fig. 2 und 3 zeigen, wie die Kunststoffbahn zusammen mit der aufgebrachten Zementschicht in die gewünschte Gestalt gefaltet wird. 2 and 3 show how the plastic sheet together with the applied cement layer is folded into the desired shape.

Die Fig. 4 zeigt das fertige Profil während der Entfernung der Kunststoffbahn. 4 shows the finished profile during the removal of the plastic web.

Das in der Zeichnung dargestellte Ausführungsbeispiel bezieht sich auf die Herstellung eines Hohlprofiles 1, dessen Gestalt in der Fig. The embodiment shown in the drawing relates on the production of a hollow profile 1, the shape of which is shown in FIG.

4 dargestellt ist. Das Profil hat einen im wesentlichen polygonalen Querschnitt, wobei jedoch eine der Seiten über einen Winkelpunkt hin verlängert worden ist. Das betreffende Profil wurde willkürlich gewählt.4 is shown. The profile is essentially polygonal Cross-section, but with one of the sides extended beyond an angular point has been. The profile in question was chosen at random.

Mittels des Verfahrens gemäss der Erfindung können auch viele andere ähnliche Profile hergestellt werden.Many others can also use the method according to the invention similar profiles can be produced.

Die betreffenden Profile können u.a. als Dachränder und als Ränder für Dachhauben und Lichtkuppeln verwendet werden. The profiles in question can be used as roof edges and as edges can be used for roof hoods and skylights.

Gemäss der Fig. 1 geht man bei dem Verfahren gemäss der Erfindung von einer verhältnismisig steifen Kunststoffbahn 2 aus, deren Breite der gewünschten Profillänge entspricht und z.B. ungefähr 300 cm betragen kann. Die Kunststoffbahn wird mit mehreren in der Breitenrichtung verlaufenden Biegelinien 3 verstehen, deren gegenseitige Abstände den gewunschten Abständen der Profilkanten entsprechen. Die Bahn 2 wird nunmehr in flachem Zustand mit einer Schicht 4 der ungehärteten armierten Zementmasse bekleidet, deren Dicke annähernd der gewuflschten Wandstärke des Profils entspricht und z.B. ungefähr o,8 cm betragen kann. According to FIG. 1, the method according to the invention is used from a relatively stiff plastic sheet 2, the width of which is the desired Corresponds to the profile length and can be, for example, approximately 300 cm. The plastic sheet will understand with a plurality of bending lines 3 extending in the width direction, their mutual distances correspond to the desired distances between the profile edges. the Web 2 is now in the flat state with a layer 4 of the uncured reinforced Cement mass clad, the thickness of which approximates the desired wall thickness of the profile and can be, for example, approximately 0.8 cm.

Die Kunststoffbahn 2 wird nunmehr zusammen mit der aufgebrachten Zementschicht 4 gemäss den Biegelinien 3 umgefaltet, wie in den Fig. 2 und 3 dargestellt ist, bis man die vollständige Gestalt des Profils erhalten hat (vergl. die Fig. 4). Die Kunststoffbahn wird nunmehr mit Klemmen festgelegt; anstatt dessen kann man erwünschtenfalls auch Klebebänder verwenden. Daraufhin wird die Zementmasse, beispielsweise mit Dampf, ausgehärtet. Schliesslich wird gemäss der Fig. 4 die Kunststoffbahn entfernt, so dass das herzustellende Profil zurückbleibt. The plastic sheet 2 is now applied together with the Cement layer 4 folded over according to the bending lines 3, as shown in FIGS until the complete shape of the profile has been obtained (see Fig. 4). The plastic sheet is now fixed with clamps; instead can you can also use adhesive tapes if desired. Then the cement mass, for example with steam, cured. Finally, according to FIG. 4, the plastic sheet removed, so that the profile to be produced remains.

Die verwendete Zementmasse kann ausschliesslich aus Portlandzement bestehen; sie kann jedoch auch FUllstoffe, wie z.B. Sand enthalten. The cement mass used can only consist of Portland cement exist; however, it can also contain fillers such as sand.

Um ein an den beiden Enden geschlossenes Profil zu erhalten, kann man in jedes Ende der durch das Umfalten der Kunststoffbahn gebildeten Form eine Wand einschieben, die mit einer Schicht der ungehärteten armierten Zementmasse bekleidet worden ist und deren Gestalt dem Querschnitt des Profiles entspricht. Erwunschtenfalls kann wenigstens eine der Wände schräg in Bezug auf die Längenachse der Form angeordnet werden damit man Profile erhält, die in einer schrägen gegenseitigen Lage miteinander verbunden werden können; die Gestalt der Wand soll in diesem Fall naturgemäss der schrägen Lage angepasst werden. In der mittels der Wände abgeschlossenen Form kann ein Ueberdruck erzeugt werden um Defekte in den Profilwänden vorzubeugen. In order to obtain a profile that is closed at both ends, can one in each end of the mold formed by folding over the plastic sheet Slide in the wall, which is covered with a layer of the unhardened reinforced cement compound has been and whose shape corresponds to the cross-section of the profile. If desired at least one of the walls can be arranged obliquely with respect to the longitudinal axis of the mold are so that you get profiles that are in an inclined mutual position with each other can be connected; In this case, the shape of the wall should naturally be the inclined position can be adjusted. In the form closed by means of the walls an overpressure can be generated to prevent defects in the profile walls.

L e e r s e i t eL e r s e i t e

Claims

PATENTANS PRUECHE Process for the production of hollow profiles with substantially polygonal cross-section made from a primarily portland cement existing, reinforced with alkali-resistant mineral fibers, especially glass fibers Cement mass, characterized in that a relatively stiff plastic sheet, whose width corresponds to the desired length of the profile, with in the width direction running bending lines is provided, the mutual spacing of which is the desired Corresponding distances of the profile edges, whereupon the web in the flat state with a layer of the unhardened reinforced cement mass is covered, the thickness of which approximately corresponds to the desired wall thickness of the profile, and that the track then together with the cement layer according to the bending lines in one of the Profile corresponding shape is folded and set in this shape, whereupon the cement mass is allowed to harden and the plastic sheet is removed.

2. The method according to claim 1, characterized in that the plastic web is fixed in the desired shape by means of clamps.

3. The method according to claim 1 or 2, characterized in that the plastic sheet is made of polypropylene.

4. The method according to claim 1, 2 or 3, characterized in that the cement mass is hardened with steam.

5. The method according to claim 1, 2, 3 or 4, characterized in that that a wall in each end of the mold formed by folding over the plastic sheet is inserted, which is covered with a layer of the uncured reinforced cement paste has been dressed and whose shape corresponds to the cross-section of the profile.

6. The method according to claim 5, characterized in that at least one of the walls is arranged obliquely with respect to the longitudinal axis of the mold.

7. The method according to claim 5 or 6, characterized in that an overpressure is generated in the form closed by the walls.

8. Hollow profile made by applying the method according to a of the preceding claims.