DE2608568A1

DE2608568A1 - Laminated co-extruded film for packaging - comprising high-temp. softening substrate and low tensile strength sealing lamina

Info

Publication number: DE2608568A1
Application number: DE19762608568
Authority: DE
Inventors: Dietmar Auch
Original assignee: Individual
Current assignee: Individual
Priority date: 1976-03-02
Filing date: 1976-03-02
Publication date: 1977-09-08

Abstract

A film laminate used in packaging applications comprises >=2 co-extruded thermoplastics film adhering together of which one, viz. the carrier lamina, has a higher softening temp. than the other lamina which serves as sealing layer. This latter is so thin that its tensile strength at break is less than the adhesion of the two laminae and also less than the tensile strength at break of the carrier lamina. More cheaply to produce than prior-art varnished packaging films. Can be folded, sealed, opened, re-folded and re-sealed.

Description

Verbundfolie für VerpackungszweckeComposite film for packaging

Die Erfindung betrifft eine Verbundfolie für Verpackungszwecke, bestehend aus mindestens zwei durch Koextrusion aneinanderhaftenden thermoplastischen Folien, von denen die eine Folie zur Bildung einer Trägerschicht eine höhere Erweichungstemperatur aufweist als die andere als Siegelschicht dienende Folie. The invention relates to a composite film for packaging purposes, consisting of of at least two thermoplastic films adhering to one another by coextrusion, of which one film to form a carrier layer has a higher softening temperature than the other film serving as a sealing layer.

Verbundfolien für Verpackungszwecke, die aus mindestens zwei durch Coextrusion aneinanderhaftenden thermoplastischen Folien mit verschiedenen Erweichungstemperaturen bestehen, sind bekannt. Bei einer bekannten Verbundfolie dieser Art besteht die Trägerschicht aus Polyamid und die Siegelschicht aus Polyäthylen. Diese bekannte Verbundfolie kann rwar versiegelt werden. Die versiegelte Stelle kann jedoch nachträglich nicht ohne Zerstörung der Folie gelöst werden. Aus diesem Grunde ist diese bekannte Verbundfolie nicht für alle Zwecke, z.B. nicht zum Herstellen von faltbaren Verpackungen, geeignet. Bei faltbaren Verpackungen, z.B. bei Verpackungen von Brot, insbesondere Toastbrotscheiben, ist es erwWnscht, daß die Siegelstellen der durch Falten verschlossenen Verpackung geöffnet und die faltbare Verpackung dadurch aufgefaltet werden kann, um z.B. aus einer Packung von Toastbrotscheiben nach dem Entnehmen von einer oder mehreren Scheiben die Verpackung wieder zusammenfalten zu können. Bei dieser bekannten Verbundfolie ist dies jedoch wegen der großen Zerreißfestigkeit der Siegelstelle nicht möglich. Laminated films for packaging purposes, which consist of at least two by Coextrusion of adhering thermoplastic films with different softening temperatures exist are known. In a known composite film of this type, there is Carrier layer made of polyamide and the sealing layer made of polyethylene. This well-known Composite film can be sealed properly. The sealed area can, however, subsequently cannot be released without destroying the foil. Because of this, this is well known Composite film not for all purposes, e.g. not for the production of foldable packaging, suitable. In the case of foldable packaging, e.g. bread packaging, in particular Slices of bread, it is desirable that the sealing points of the closed by folds The packaging can be opened and the foldable packaging can be unfolded, to e.g. from a pack of toast slices after removing one or several slices to be able to fold the packaging back together. With this well-known However, this is composite film because of the high tensile strength of the sealing point not possible.

Bei einer anderen bekannten siegelbaren Verbundfolie dieser Art besteht die Trägerschicht aus Homo-Polypropylen und die Siegelschicht aus Co-Polypropylen+)Diese bekannte Verbundfolie hat jedoch den Nachteil, daß der Unterschied zwischen den Erweichungspunkten der beiden Schichten verhältnismäßig gering ist, so daß das Versiegeln große Schwierigkeiten bereitet. Um diese Schwierigkeit nach Möglichkeit zu verringern, muß bei dieser bekannten Folie die Trägerschicht sehr dünn +) Äthylen-Polypropylen-Co-Polymer (Block- oder statistisches Co-Polymer) gewählt werden, damit die Wärme von dem Schweißbacken auf die Siegelschicht schneller übertragen wird. In another known sealable composite film of this type the carrier layer made of homo-polypropylene and the sealing layer made of co-polypropylene +) These known composite film, however, has the disadvantage that the difference between the Softening points of the two layers is relatively low, so that sealing causes great difficulties. To reduce this difficulty as much as possible, In this known film, the carrier layer must be very thin +) ethylene-polypropylene-co-polymer (Block or random co-polymer) be chosen so that the Heat is transferred from the welding jaws to the sealing layer more quickly.

Ein weiterer Nachteil dieser bekannten Verbundfolie besteht darin, daß auch sie nicht auffaltbar ist, weil die Siegelstellen, wie bei der zuerst genannten bekannten Verbundfolie, eine zu große Zerreißfestigkeit haben.Another disadvantage of this known composite film is that that it cannot be unfolded either, because the sealing points, as in the case of the first mentioned known composite film, have too great a tensile strength.

Für versiegelte und wieder auf faltbare Verpackungen ist eine Folie bekannt" deren Trägerschicht aus teurem Zellglas oder niaxiai verstrectem /Polypropylen besteht. Diese Trägerschicht ist mit einer als Siegelschicht dienenden Lackschicht aus Polyvinylidenclorid oder aus Nitrolack beschichtet. Diese bekannten Folien, bei denen die beiden Schichten im Unterschied zu der eingangs genannten Gattung nicht aus zwei coextrudierten Folien bestehen, können gefaltet, versiegelt und wieder aufgefaltet werden. Sie haben jedoch den Nachteil, daß durch den verhältnismäßig arbeitsaufwendigen Vorgang des Lackierens die Folie verhältnismäßig teuer ist.A film is used for sealed packaging that can be folded back on known "whose carrier layer is made of expensive cellulose glass or niaxiai reinforced / polypropylene consists. This carrier layer is covered with a lacquer layer serving as a sealing layer made of polyvinylidene chloride or coated with nitro lacquer. These well-known foils, in which the two layers differ from the genus mentioned at the beginning do not consist of two coextruded films, can be folded, sealed and again be unfolded. However, they have the disadvantage that due to the relatively labor-intensive process of painting the film is relatively expensive.

Der Erfindung liegt die Aufgabe zu Grunde, eine Verbundfolie, die aus mindestens zwei durch Coextrusion aneinanderhaftenden thermoplastischen Folien besteht, zu schaffen, die siegelbar und nach dem Versiegeln wieder auffaltbar ist und die mit einem minimalen Arbeitsaufwand herstellbar ist. The invention is based on the object of a composite film which of at least two thermoplastic films adhered to one another by coextrusion exists to create that is sealable and can be opened again after sealing and which can be produced with a minimum of labor.

Diese Aufgabe ist gemäß der Erfindung dadurch gelöst, daß die Siegelschicht so dünn ist, daß ihre Zerreißfestiqkeit - ohne Haftvermittler kleiner ist als die durch Coextrusion/verursachte Haftung der beiden Schichten aneinander und als die Zerreißfestigkeit der Trägerschicht. Versuche haben gezeigt, daß durch diese Maßnahme die der Erfindung zu Grunde liegende Aufgabe äußerst einfach gelöst und eine sehr billige,faltbare und wieder aufreißbare Folie geschaffen wird. In Anbetracht dessen, daß die Fachwelt bisher sich mit den teueren, lackierten Folien für auffaltbare Verpackungen begnügte, stellt die Erfindung für die Fachwelt eine große Überraschung dar. Der besondere Vorteil der Erfindung besteht nun darin, daß die Trägerfolie und die Siegelfolie in weiten Grenzen beliebig gewählt und den verschiedenen Gebrauchs zwecken angepaßt werden können.This object is achieved according to the invention in that the sealing layer is so thin that its Zerreißfestiqkeit - without adhesion promoter is less than that by coextrusion / caused adhesion of the two layers to each other and as the Tensile strength of the carrier layer. Tests have shown that this measure the problem underlying the invention solved extremely easily and a very cheap, foldable and tearable film is created. Considering that the professional world has so far dealt with the expensive, lacquered foils for If unfoldable packaging was sufficient, the invention represents a great one for experts Surprise. The particular advantage of the invention is that the The carrier film and the sealing film can be chosen arbitrarily within wide limits and the different ones Purposes of use can be adapted.

So läßt sich z.B. zum Verpacken von Brotscheiben eine äußerst billige Verbundfolie herstellen, bei der die Trägerschicht aus Polypropylen oder Co-Polypropylen und die Siegelschicht aus Polyäthylen oder Co-Polyäthylen besteht.For example, an extremely cheap one can be used for packing bread slices Produce composite film in which the carrier layer is made of polypropylene or co-polypropylene and the sealing layer consists of polyethylene or co-polyethylene.

Will man dagegen eine sehr widerstandsfähige und gasdichte Folie schaffen, dann kann bei dieser in bekannter Weise die Trägerschicht aus Polyamid und die Siegelschicht aus Polyäthylen bestehen, wobei sich diese Verbundfolie allerdings von der oben genannten bekannten Folie dadurch unterscheidet, daß die die selschicht so dünn qewählt wird, daß ihre Zerreißfestiqkeit ohne Haftvermittler -kleiner ist als die durch Coextrusion/verursachte Haftung der beiden Schichten aneinander und als die Zerreißfestigkeit der Trägerschicht.If, on the other hand, you want to create a very resistant and gas-tight film, then in this case the polyamide carrier layer and the sealing layer can be used in a known manner consist of polyethylene, although this composite film is different from the above said known film differs in that the selschicht is so thin It is chosen that its tear strength without adhesion promoter is less than that by coextrusion / caused adhesion of the two layers to each other and as the Tensile strength of the carrier layer.

Die Erfindung ist in der folgenden Beschreibung von mehreren Ausführungsbeispielen an Hand der Zeichnung im einzelnen erläutert.The invention is in the following description of several exemplary embodiments explained in detail on the basis of the drawing.

Die Zeichnung zeigt als stark vergrößerten Querschnitt den grundsätzlichen Aufbau der erfindungsgemäßen Verbundfolie.The drawing shows the basic one as a greatly enlarged cross-section Structure of the composite film according to the invention.

Jede erfindungsgemäße Verbundfolie besteht aus einer Trägerschicht 10, bei der mindestens eine Seite mit einer Siegelschicht 11 beschichtet ist, wobei die beiden Schichten dadurch hergestellt sind, daß zwei Folien durch Coextrusion ohne Haftvermittler aneinandergefügt sind.Each composite film according to the invention consists of a carrier layer 10, in which at least one side is coated with a sealing layer 11, wherein the two layers are produced in that two films are coextruded are joined together without an adhesion promoter.

Bei dem in der Zeichnung dargestellten Ausführungsbeispiel sind beide Seiten der Trägerschicht mit einer Siegelschicht 11 versehen.In the embodiment shown in the drawing, both are Sides of the carrier layer are provided with a sealing layer 11.

Die Dicke der Siegelschicht 11 ist so gewählt, daß ihre Zerohne Haftvermittler reißfestigkeit kleiner ist als die durch Coex-trusion/verursachte Haftung der beiden Schichten 10 und 11 aneinander und als die Zerreißfestigkeit der Trägerschicht 10.The thickness of the sealing layer 11 is chosen so that its without adhesion promoter tear strength is less than the coextrusion / caused adhesion of the two Layers 10 and 11 on each other and as the tensile strength of the backing layer 10.

Auch bestehen die Trägerschicht 10 auf der einen Seite und die Siegelschichten 11 auf der anderen Seite aus thermoplastischen Materialien mit verschiedenen Ertieichungstteraturen, und a.7ar so, daß die Siegelschichten 11 gegenüber der Trägerschicht 10 einen um so viel verringerten Eneichungspunkt haben, daß mit einem geeigneten Schweißbacken aufeinander liegende Verbundfolien dieser Art so erwärmt werden können, daß nur die aufeinanderliegenden Siegelschichten 11 miteinander verschweißt werden, ohne daß dabei die Grundschicht 10 aufgeweicht oder geschmolzen wird.There is also the carrier layer 10 on one side and the sealing layers 11 on the other hand made of thermoplastic materials with different calibration temperatures, and a.7ar so that the sealing layers 11 with respect to the carrier layer 10 one to have so much reduced calibration point that with a suitable welding jaw superposed composite films of this type can be heated so that only the sealing layers 11 lying on top of one another are welded to one another without that in the process the base layer 10 is softened or melted.

Wird mit der erfindungsgemäßen Folie eine Faltpackung hergestellt, z.B. Toastbrot eingepackt, dann können die an den Faltstellen aufeinanderliegenden Schichten der Verbundfolie in der oben beschriebenen Weise miteinander versiegelt werden. Dadurch, daß die Siegelschichten 11 so dünn sind, daß ihre Zerreißfestigkeit kleiner ist als die Haftung der Siegelschicht 11 an der Trägerschicht 10, wird beim Aufreißen der versiegelten Stelle, also beim Auffalten der Verpackung, nur die Siegelschicht an der Siegelstelle zerstört, ohne daß dabei die übrige Folie beschädigt oder die Siegelschicht abgeschält wird. Man kann also die aufgefaltete Stelle ohne weiteres wieder zusammenfalten.If a folding pack is produced with the film according to the invention, E.g. toast bread is packed, then the Layers of the composite film in the manner described above with each other be sealed. Because the sealing layers 11 are so thin that their tensile strength is smaller than the adhesion of the sealing layer 11 to the carrier layer 10, is used in Tearing open the sealed area, i.e. when unfolding the packaging, only the sealing layer destroyed at the sealing point without damaging the rest of the film or the Sealing layer is peeled off. So you can easily see the unfolded part fold it up again.

Die Verbundfolie kann durch besondere bekannte Behandlung beim Extrudieren als Klarsichtfolie, als verstreckte Folie und dergleichen ausgeführt und dadurch verschiedensten Verwendungszwecken angepaßt werden.The composite film can be subjected to special known treatment during extrusion executed as a transparent film, as a stretched film and the like and thereby various uses can be adapted.

Im folgenden sind mehrere Ausführungsbeispiele der erfindungsgemäßen Verbundfolie durch Angabe der für die Trägerschicht 10 und die Siegelschichten 11 verwendeten thermoplastischen Stoffe genauer erläutert.The following are several embodiments of the invention Composite film by specifying the information for the carrier layer 10 and the sealing layers 11 used thermoplastic materials explained in more detail.

Beispiel 1: Die Trägerschicht 10 besteht aus einer Polypropylenfolie, die mit als Siegelschichten 11 dienenden Polyäthylenfolien koextrudiert ist. Da der Erweichungspunkt von Polyäthylen zwischen 750 und 118°C liegt und der Erweichungspunkt von Polypropylen zwischen 1450 und 168 0C liegt, ist eine ausreichende Temperaturspanne gewährleistet, die ein einwandfreies Versiegeln ohne Beschädigung der Trägerschicht ermöglicht.Example 1: The carrier layer 10 consists of a polypropylene film, which is coextruded with serving as sealing layers 11 polyethylene films. There the softening point of polyethylene is between 750 and 118 ° C and the softening point of polypropylene is between 1450 and 168 0C, is a sufficient temperature range ensures a perfect sealing without damaging the carrier layer enables.

Beispiel 2: Als Trägerfolie 10 wird hier Homo-Polypropylen und als Siegelschichten 11 Co-Polypropylen verwendet. Da im Co-Polypropylenmolekül Athylenketten enthalten sind, ist die Verankerung der Co-Polypropylenträgerschicht mit der Co-Polyäthylensiegelschicht ohne Haftvermittler besonders widerstandsfähig, so daß die Siegelschicht etwas dicker gewählt werden. kann und hiermit eine noch aufreißbare, aber wesentlich höhere Siegelnahtfestigkeit erreicht wird als bei der Verwendung von normalem Polypropylen und Polyäthylen.Example 2: Homo-polypropylene is used here as the carrier film 10 and as Sealing layers 11 used co-polypropylene. As ethylene chains in the co-polypropylene molecule are included is the anchoring of the co-polypropylene carrier layer with the co-polyethylene sealing layer Particularly resistant without an adhesion promoter, so that the sealing layer is somewhat thicker to get voted. can and thus a still tearable, but significantly higher seal seam strength achieved than when using normal polypropylene and polyethylene.

Beispiel 3: Für spezielle Zwecke, wo insbesondere eine gasundurchlässigkeit erzielt werden soll, ist es zweckmäßig, als Trägerschicht 10 eine Polyamidfolie und als Siegelschichten 11 Polyäthylenfolien vorzusehen. Auch diese Verbundfolie läßt sich bei hoher Zerreißfestigkeit leicht versiegeln und wieder auffalten. Wegen der hohen Zerreißfestigkeit von Polyamid kann bei diesem Ausführungsbeispiel die Trägerschicht 10 auch dünner sein als die Siegelschichten 11, da auch bei einer dickeren Siegelschicht die Zerreißfestigkeit der Siegelschicht immer noch kleiner gehalten werden kann als die durch Coextrusion verursachte Haftung der beiden Schichten aneinander und als die Zerreißfestigkeit der Trägerschicht 10.Example 3: For special purposes, where in particular a gas impermeability is to be achieved, it is expedient to use a polyamide film as the carrier layer 10 and to provide 11 polyethylene films as sealing layers. Also this composite film can be easily sealed and unfolded again with high tensile strength. Because the high tensile strength of polyamide can in this embodiment Carrier layer 10 can also be thinner than the sealing layers 11, since even with one thicker sealing layer, the tensile strength of the sealing layer is still lower can be kept than the adhesion of the two layers caused by coextrusion to one another and as the tensile strength of the carrier layer 10.

Claims

Claims l) composite roll for packaging purposes, consisting from mint at least two thermoplastic films adhered to one another by coextrusion, of which one film to form a carrier layer has a higher softening temperature than the other film serving as a sealing layer, characterized in that that the sealing layer (11) is so thin that its tensile strength is less than the adhesion of the two layers (11, 12) to one another caused by coextrusion and as the tear strength of the backing layer (10).

2) composite film according to claim 1, characterized in that the carrier layer (10) made of polypropylene or co-polypropylene and the sealing layer (11) made of polyethylene or co-polyethylene.

3) composite film according to claim 1, characterized in that the carrier layer (10) consists of polyamide and the sealing layer (11) consists of polyethylene.