DE2607568A1 - Hydrolysed ethylene-vinyl acetate copolymers - used in moulding compsns. for prodn. of hydrophilic articles, esp. building components - Google Patents
Hydrolysed ethylene-vinyl acetate copolymers - used in moulding compsns. for prodn. of hydrophilic articles, esp. building componentsInfo
- Publication number
- DE2607568A1 DE2607568A1 DE19762607568 DE2607568A DE2607568A1 DE 2607568 A1 DE2607568 A1 DE 2607568A1 DE 19762607568 DE19762607568 DE 19762607568 DE 2607568 A DE2607568 A DE 2607568A DE 2607568 A1 DE2607568 A1 DE 2607568A1
- Authority
- DE
- Germany
- Prior art keywords
- water
- vinyl acetate
- ethylene
- acetate copolymers
- esp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Kunststoffteile aus wasserbenetzbaren Kunststoffen Kunststoffe sind im allgemeinen hydrophob, d.h. sie werden son Wasser schwer oder nicht benetzt. Es gibt nur wenige Ausnahmen, z.B. Polyvinylalkohol und Polyvinylpyrolidon, doch können wegen deren sonstigen Eigenschaften aus- diesen Kunststoffen -im allgemeinen nicht Formteile hergestellt werden, die konstruktive Festigkeiten aufweisen. Plastic parts made from water-wettable plastics are plastics Generally hydrophobic, i.e. they are hardly wetted or not wetted by water. There are few exceptions such as polyvinyl alcohol and polyvinyl pyrolidone, however can because of their other properties from these plastics -in general molded parts are not produced that have structural strengths.
. .
Es hat daher an Versuchen nicht gefehlt die üblichen für konstruktive Zwecke geeigneten Kunststoffe, besonders die billigen Massenkunststoffe, wasserbenetzbar, d.h. hydrophil, zu machen.There has therefore been no lack of attempts for the usual constructive ones Plastics suitable for purposes, especially the cheap mass-produced plastics, water-wettable, i.e., hydrophilic.
So hat man beispielsweise PVC und PE oberflächlich angeätzt, angeflammt oder mit entsprechenden Überzügen versehen, um gute Benetzbarkeit zu erreichen. Die so behandelten Teile verlieren meist nach kurzer Gebrauchszeit ihr hydrophiles Verhalten.For example, the surface of PVC and PE has been etched and flamed or provided with appropriate coatings in order to achieve good wettability. The parts treated in this way usually lose their hydrophilic character after a short period of use Behavior.
Eine weitere Möglichkeit besteht darein, Kunststoffe mit großen Mengen anorganischer FEllstoffe, z.B. Kreide, zu füllen. Um gute Wasserbenetzbarkeit zu erhalten, benötigt man jedoch so große Füllstoffmengen, daß die Produkte sehr spröde werden und damit für konstruktive Zwecke unbrauchbar.Another option is to use plastics in large quantities inorganic fillers, e.g. chalk. To have good water wettability too obtained, however, you need so large amounts of filler that the products are very brittle will and thus useless for constructive purposes.
aufgabe der Erfindung Ist-es -daher, -die Forderung-nach guter Wasserbenetzbarkeit und mechanischer Festigkeit für als konstruktive Bauteile zu verwendende Formkörper zu erfüllen.The object of the invention is, therefore, the requirement for good wettability with water and mechanical strength for moldings to be used as structural components to meet.
Es hat sich nun als überraschend herausgestellt, daß eich die Forderung auf Wasserbenetzbarkeit einerseits und gute mechanische Festigkeit andererseits durch einen bestimmten -für.It has now turned out to be surprising that the requirement on water wettability on the one hand and good mechanical strength on the other by a specific -for.
dieeen Zweck bisher nicht bekannten und eingesetzten Typ von Kunststoff realisieren läßt, nämlich durch die erfindungsgemEß verwendeten unter ganz bestimmten Bedingungen hergestellten Copolymerisate aus Äthylen und Vinylacetat mit Äthylenanteilen von 15 bis 60 Mol-%, die nach der Polymerisation hydrolysiert werden und die dann einen Hydrolysegrad des Vinylacetatantells von nicht weniger als 85 Mol-% besitzen. Der Hydrolysegrad soll für zahlreiche Zwecke mindestens 98 ffi betragen. Formkörper aus diesen Kunststoffen werden mit und ohne Glasfasern ebenfalls unter bestimmten Bedingungen konditioniert, so daß sie stark bevorzugt Wassergehalte im Bereich-von 0,2 bis 3,0 Gew.-% aufweisen.The type of plastic used so far not known and used for its purpose can be realized, namely by those used according to the invention under very specific conditions Conditions produced copolymers of ethylene and vinyl acetate with ethylene content from 15 to 60 mol% which are hydrolyzed after the polymerization and which then have a degree of hydrolysis of the vinyl acetate antelle of not less than 85 mol%. The degree of hydrolysis should be at least 98 ffi for numerous purposes. Moldings These plastics are also made with and without glass fibers under certain conditions Conditions conditioned so that they strongly favor water contents in the range-of 0.2 to 3.0% by weight.
Die Herstellung und Konditionierung solcher Produkte ist nicht Gegenstand der vorliegenden Erfindung. Sie werden beispielsweise in den DT-Offenlegungsschriften 23 21 404 und 24 25 903 ausführlich beschrieben. Die bekannten Verwendungen dieser Produkte sind beispielsweise in Japan Plastics, Heft November/Dezember 1974, Seite 6 bis 12 und in der gleichen Zeitschrift vom Januar/Februar t975, Seite 13 bis t5 sowie in einer, vorhäufigen Prospekt der Firma Nippon Synthetic Chemical Industry Co. über GL-Resin vom 13.12.1974 beschrieben. Dabei wird auch die für Kunststoffe ungewöhnlich hohe Wasseraufnahme und ihre Auswirkungen auf bestimmte Eigenschaften, wie Dimesionsatabilltät und antistatisches Verhalten-erloutert und die hieraus resultierende Anwendung aufgrund des antistatischen Verhaltens für Spulen, Schalter, Ventilatorflügel u.a. vorgeschlagen.The manufacture and conditioning of such products is not an issue of the present invention. They are for example in the DT-Offenlegungsschriften 23 21 404 and 24 25 903 described in detail. The known uses of this Products are, for example, in Japan Plastics, November / December 1974 issue, page 6 to 12 and in the same journal from January / February t975, Page 13 to t5 as well as in a preliminary prospectus from Nippon Synthetic Chemical Industry Co. via GL-Resin dated December 13, 1974. It will also the unusually high water absorption for plastics and its effects on certain Properties such as dimensional stability and antistatic behavior-explained and the resulting application due to the antistatic behavior of coils, Switches, fan blades and others are proposed.
Die hohe Wasserbenetzbarkeit und die damit erstmals mögliche praktische Verwertbarkeit des beschriebenen Materials für verschiedene konstruktive Äpparateteile und Bormkörper, welche ständig oder überwiegend mit Wasser in Berührung kommen wurde erstmals in der vorlie,enden Anmeldung als Uberraschender Effekt von erheblicher technischer Bedeutung erkannt.The high wettability with water and the practicality that is possible for the first time Usability of the material described for various constructive parts of the apparatus and body bodies that would come into constant or predominant contact with water For the first time in the present application, a surprising effect of considerable recognized technical importance.
Durch die Variation des Vinylseetatantelis und den Grad der Verseifung hat man eine breite Palette von Möglichkeiten, Benetzbarkeit und Steife Je nach Verwendungszweck optimal miteinander zu kombinieren.By varying the vinyl acetate gelatin and the degree of saponification one has a wide range of possibilities, depending on wettability and stiffness The intended use can be optimally combined with one another.
Erfindungsgema-.ß hergestellte Teile aus solchen Kunststoffen haben eine große technische Bedeutung als mit Wasser in Rerührung kommende Teile, z.B. für den Bau von Apparateteilen, Kühltürmen, Luftwäschern u.s.According to the invention, parts made from such plastics have a great technical importance as parts that come into contact with water, e.g. for the construction of apparatus parts, cooling towers, air washers, etc.
Wegen der Korrosionsbeständigkeit solcher für Resktorenbau und Umweltschutz an Bedeutung ständig zunehmenden Anlagen wird dafür bisher meist PVC, PP und mit Glasfaser verstärkte Kunststoffe, besonders Polyester ( GFK ) eingesetzt; Kunststoffe, deren Wasserbenetzbarkeit sehr gering ist. Da es bei der Wirkungsweise immer auf eine große Grenzfläche zwischen Luft und Wasser ankommt, erhöht ein gut permanent benetzbarer Kunststoff den Wirkungsgrad dieser Anlagen erheblich.Because of their resistance to corrosion, they are used for construction of resectors and environmental protection plants, which are constantly increasing in importance, have so far mostly been PVC, PP and with Glass fiber reinforced plastics, especially polyester (GRP) used; Plastics whose water wettability is very low. Since it is the mode of action always depends on a large interface between air and water, increases a well permanently wettable plastic significantly increases the efficiency of these systems.
Eine weitere Verwendungsmöglichkeit besteht für Kunststoffe im Außeneinsatz, z«B. Fassaden, Verkleidungen, Rolläden, Balkonverkleidungen, BrEstungen, Sitzbände etc., wo man durch gute Wasserbenetzbarkeit einen Selbstreinigungseffekt durch Regen erreicht. Auf den bisher dafür eingesetzten Kunststoffen haftet der übliche atmosphärische Schmutz meist sehr hartnäckig und läßt die Kunststoffteile nach kurzer Zeit unansehnlich werden.Another possible use is for plastics in outdoor use, z «B. Facades, cladding, shutters, balcony cladding, parapets, seat tapes etc., where a self-cleaning effect through rain due to good water wettability achieved. The usual atmospheric sticks to the plastics previously used for this purpose Dirt is usually very stubborn and leaves the plastic parts unsightly after a short time will.
Das hydrophile Verhalten an in der Praxis eingesetzten erfindungsgemäßen Kunststoffteilen ist wesentlich größer, als durch quantitative Messungen der Benetzbarkeit, gemessen an Musterplatten, festgestellt werden kann; qualitative Unterschiede gegenüber nicht hydrophilen Kunststoffen sind durch reinen Augenschein bereits deutlich wahrnehmbar.The hydrophilic behavior of the invention used in practice Plastic parts is much larger than through quantitative measurements of wettability, measured on sample plates, can be determined; qualitative differences compared to Non-hydrophilic plastics are clearly noticeable just by looking at them.
Je nach Einsatzgebiet kann das Material auch mit Füllstoffen, insbesondere solchen aus Glas wie Glasfaser oder Glasgeweben verstärkt werden und/oder als Beschichtungen, Laminate oder Überzüge auf anderen Werkstoffen, bevorzugt Metallen, oder Kunststoffen, eingesetst werden. In üblicher Weise können auch andere gunststoffhilfsstoffe wie Verarbeitungshilfsstoffe, Wärme- und Lichtstabilisatoren zugesetzt werden.Depending on the area of application, the material can also be filled with fillers, in particular those made of glass such as fiberglass or glass fabrics are reinforced and / or as coatings, Laminates or coatings on other materials, preferably metals or plastics, be used. In the usual way, other plastic auxiliaries such as Processing aids, heat and light stabilizers are added.
Die Verarbeitung zu Fornikörpern erfolgt nach den für Kunststoffen üblichen Verfahren.The processing to form bodies is carried out in accordance with that for plastics usual procedures.
Claims (4)