DE2544947A1

DE2544947A1 - Eliminating slivers on stainless and heat resisting steel strip - by adding titanium and boron prior to casting

Info

Publication number: DE2544947A1
Application number: DE19752544947
Authority: DE
Inventors: Horst Mozek; Kurt Dr Ing Tesche
Original assignee: Thyssen Edelstahlwerke AG
Current assignee: Thyssen Stahl AG
Priority date: 1975-09-30
Filing date: 1975-09-30
Publication date: 1977-09-22

Abstract

Prior to the casting, continuous casting, or pressure casting of ingots, slabs or billets, the molten steel was carefully de-oxidised and then 0.02-0.15% Ti added. In this addn. 0.002-0.007% boron is added with the Ti. The Ti may be partly or completely replaced by Nb-Ta, Hf, V and/or Zr, using a total of is not >0.15%. Used in stainless and similar steels formfg. decorative parts, appts. for the food industries, and domestic appliances etc., where an excellent surface finish is required. Higher hot rolling temps. can be used so the amt. of cold rolling is reduced.

Description

Verfahren zur Vermeidung von Schuppenz eilen/ Häiitchen Procedure for avoiding dandruff

auf der Oberfläche von rost-, säure- und hitzebeständigen Stahlbändern nach Patent .... (Patentanmeldung P 24 52 372.6) Die Erfindung betrifft ein Verfahren zur Vermeidung des Fehlers "Schuppenzeilen/ Häutchen" oder nachfolgend mit dem internationalen Begriff "slivers" bezeichnet, an Warm- bzw. Kaltbändern aus rost-, säure- und hitzebeständigen Stählen nach Patent III .(Patentanmeldung P 24 52 372.6). on the surface of rust-, acid- and heat-resistant steel strips according to patent .... (patent application P 24 52 372.6) The invention relates to a method to avoid the error "scales / skin" or subsequently with the international The term "slivers" refers to hot or cold strips made of rust, acid and heat-resistant Steels according to patent III. (Patent application P 24 52 372.6).

Bei slivers handelt es sich um Überlappungen (Oberflächentrennungen) unterschiedlicher Größe in Pfeilform, bevorzugt in kleinem Winkel zur Walzrichtung verlaufend, immer überwalzt und meist einen Oxydsaum (Zunder) enthaltend. Slivers treten bei rost-, säure- und hitzebeständigen Stahlgüten auf, Es handelt sich um reine Oberflächenfehler am Band.Slivers are overlaps (surface separations) different sizes in arrow shape, preferably at a small angle to the rolling direction running, always rolled over and mostly containing an oxide border (scale). Slivers occur in rust-, acid- and heat-resistant steel grades, it is about pure surface defects on the belt.

Slivers haben nachteilige Auswirkungen hinsichtlich - optisch einwandfreier Oberfläche, wie sie in den meisten Anwendungsfällen notwendig ist, z.B. für die Herstellung von Zierteilen, Geräten für die Nahrungsmittelindustrie, Haushaltsgeräten, - Rost- und Korrosionsbeständigkeit, weil die slivers leichtere Haftmöglichkeit für korrosive Medien bieten und sich zwischen den Fehlstellen und dem guten Material ein korrosionsfÖrdendè'r"Potentialunterschiedkildet sowie - Verarbeitbarkeit, weil bei allen formändernden Weiterverarbeitungen, ausgehend von den Fehlstellen, Materialtrennungen auftreten können.Slivers have detrimental effects in terms of - visually flawless Surface as it is necessary in most applications, e.g. for the Manufacture of decorative parts, devices for the food industry, household appliances, - Rust and corrosion resistance because the slivers easier adhesion for corrosive media and between the imperfections and the good material a corrosion-promoting "potential difference" forms as well - processability, because with all form-changing further processing, starting from the imperfections, Material separation can occur.

Aus den obigen Gründen kann ein mit dem Fehler "slivers" befallenes Material nicht an Weiterverarbeiter geliefert werden, vielmehr muß im Lauf der Kaltbandfertigung der Fehler beseitigt werden, Dies geschieht durch kostspielige Bandschleifoperationen, die häufig noch zusätzliche Fertigungsschritte, wie Vorwalzen, Zwischenglühen, zur Folge haben, Slivers entstehen bei der Warmbandfertigung, d.h, bei der Walzung der Vorbramme bzw. Strang- oder Druckgußbramme oder Blöcke zu Warmband, wenn die Erwärmung der Blöcke oder Brammen in einem kritischen Temperaturbereich und/oder bei einer kritischen Wärmdauer erfolgt. Diese kritischen Bedingungen sind insbesondere abhängig von der Stahlmarke und der Art der Block- und Brammenherstellung, d.h. ob aus Gußbrammen oder -blöcken gewalzte Vorbrammen oder -blöcke oder Strang-, Druckgußbrammen oder -blöcke eingesetzt werden.For the above reasons, a slivers Material must not be delivered to further processors, rather it has to be in the course of cold strip production the error is eliminated, this is done through costly belt grinding operations, which often have additional manufacturing steps, such as roughing, intermediate annealing, for As a result, slivers are created during hot strip production, i.e. during the rolling of the Pre-slab or continuous or die-cast slab or blocks for hot strip when the heating of the blocks or slabs in a critical temperature range and / or at a critical heating time takes place. These critical conditions are particularly dependent on the steel brand and the type of ingot and slab production, i.e. whether from cast slabs or blocks rolled slabs or blocks or strand, die-cast slabs or blocks are used.

Man kalm slivers vermeiden, indem man die Warmwalzung des Bandes bei nicht zu hoher Temperatur durchführt, Als weiteres Mittel zur Vermeidung von slivers wurde z. B. in der DT-AS 1 558 657 für ferritische Stähle vorgeschlagen, Bor in Mengen von 0, 001 bis 0, 01 yo im Anschluß an die Desoxdation des flüssigen Stahls z. B. mit Aluminium zuzusetzen, Bei austenitischen Stählen ist es auch bekannt, Bor in einer größeren Menge von etwa 40 ppm zuzusetzen. Es wurde jedoch festgestellt, daß jedenfalls bei höherer Warmwalztemperatur diese Bo, -us i e niellt den gewünschten I-ifolg bringen.Avoid kalm slivers by hot rolling the strip at Do not perform too high a temperature, as another means of avoiding slivers was z. B. proposed in DT-AS 1 558 657 for ferritic steels, boron in Quantities from 0.001 to 0.01 yo following deoxidation of the liquid steel z. B. to add aluminum, with austenitic steels it is also known To add boron in a larger amount of about 40 ppm. However, it was found that in any case at higher hot rolling temperature this Bo, -us i e niellt the desired I-ifolg bring.

Aufgabe der vorliegenden Erfindung ist nun, einen Weg zu finden, auf dem die Bildung von slivers auf rost-, säure- und hitzebeständigen Stahlbändern auch bei höheren Walztemperaturen wirksam vermieden werden kann.The object of the present invention is now to find a way on the formation of slivers on rust, acid and heat-resistant steel belts can be effectively avoided even at higher rolling temperatures.

In dem Hauptpatent war vorgeschlagen worden, der Stahlschmelze vor dem Vergießen zu Gußbrammen oder -blöcken bzw. Strangguß-, Druckgußbrammen oder -blöcken nach sorgfältiger Des oxydation 0, 02 bis 0, 15 % Titan zuzusetzen. Es wurde nun festgestellt, daß sich der positive Einfluß dieses Titangehalts insbesondere dann auswirkt, wenn der Schmelze zusätzlich noch 0, 002 bis 0, 007 % Bor zugegeben wird. Die angegebene Menge an Titan führt zu einem Titangehalt im Gußblock von etwa 0, 01 bis 0, 07 % und die von Bor zu einem Borgehalt von etwa 0, 002 bis 0, 005 %.In the main patent it had been suggested that the steel melt before casting into cast slabs or blocks or continuous cast slabs, die cast slabs or -Add 0.02 to 0.15% titanium to the blocks after careful deoxidation. It it has now been found that the positive influence of this titanium content in particular then has an effect if 0.002 to 0.007% boron is also added to the melt will. The specified amount of titanium leads to a titanium content in the ingot of approx 0.01 to 0.07% and that of boron to a boron content of about 0.002 to 0.005 %.

Durch die erfindungsgemäß vorgeschlagene Maßnahme wird praktisch ohne großen zusätzlichen Aufwand erreicht, daß man rost-, säure-und hitzebeständige Stahlbänder ohne die Entstehung des Fehlers slivers" auch bei höheren Temperaturen warmwalzen kann. Dadurch wird einmal die Wirtschaftlichkeit der Warmbandwalzung durch eine Mehrleistung der Warmbandstraße erhöht und außerdem eine stärkere Dickenverminderung des warmgewalzten Bandes erreicht, wodurch eine Verminderung des Walzaufwandes beim nachfolgenden Kaltwalzen entsteht, so daß sich die Wirtschaftlichkeit der Walzung nochmals erhöht. Daneben entfällt die bisher erforderlich gewesene Mehrarbeit zur Entfernung von Bandabschnitten, die von slivers befallen sind bzw.The measure proposed according to the invention is practically without Great additional effort is achieved by using rust, acid and heat-resistant steel belts Hot rolling even at higher temperatures without the occurrence of the sliver error can. This once the economic efficiency of hot strip rolling by a Increased output of the hot strip mill increased and also a greater reduction in thickness of the hot-rolled strip achieved, thereby reducing the cost of rolling subsequent cold rolling occurs, so that the profitability of the rolling increased again. In addition, the overtime previously required is no longer necessary Removal of ligament sections that are affected by slivers or

zur Entfernung dieser Oberflächenfehler.to remove these surface defects.

Der bei titanstabilisierten Stählen mit Titangehalten von mindestens 0, 20 % auftretende Bandoberflächenfehler "Titanschlieren" trat bei Zusatz von Titan in der erfindungsgemäß angegebenen Menge von 0, 02 bis 0, 15 % und von 0, 002 bis Gut 007 % Bor nicht auf. Auch eine Beeinträchtigung der Polierbarkeit sowie anderer Gebrauchseigenschaften wurde nicht beobachtet, so daß der Vorteil der Vermeidung von slivers bei Anwendung des erfindungsgemäßen Verfahrens voll zur Geltung kommt.That of titanium-stabilized steels with a titanium content of at least 0, 20% band surface defects "titanium streaks" occurred when titanium was added in the amount specified according to the invention of 0.02 to 0.15% and from 0.002 to Good 007% boron does not appear. Also an impairment of the polishability as well as other performance properties were not observed, so that the advantage the avoidance of slivers when using the method according to the invention to the full Comes into play.

Anstelle oder zusätzlich zu dem erfindungsgemäß zugesetzten Titan kann gemäß einer Abwandlung des erfindungsgemäßen Verfahrens auch Niob/Tantal, Hafnium, Vanadium und/oder Zirkonium in einer Menge bis zu insgesamt 0a 15 % einzeln oder zu mehreren zugesetzt werden.Instead of or in addition to the titanium added according to the invention according to a modification of the method according to the invention, niobium / tantalum, hafnium, Vanadium and / or zirconium in an amount up to a total of 0a 15% individually or to be added to several.

Claims

Claims 1. Method for avoiding flaky lines / membranes (slivers) on the surface of rust-, acid- and heat-resistant steel belts, in which the molten steel before pouring into cast slabs or blocks or continuous cast. Die-cast slabs or blocks after careful deoxidation 0.02 to 0.15% titanium is added, according to patent .... (patent application P 24 52 372.6-24), characterized in that that in addition 0.002 to 0.007% boron is added to the melt.

2. The method according to claim 1, characterized in that the titanium in whole or in part by one or more of the elements niobium / tantalum, hafnium, Vanadium or zirconium is replaced in an amount up to a total of 0.15%.