DE2544855A1 - Raised xerographic printing - for braille produced using intumescent electroscopic tower mixture

Info

Publication number: DE2544855A1
Application number: DE19752544855
Authority: DE
Inventors: Ezekiel Jacob
Original assignee: EZEKIEL JACOB J
Current assignee: EZEKIEL JACOB J
Priority date: 1975-10-07
Filing date: 1975-10-07
Publication date: 1977-04-14
Also published as: DE2544855C2

Abstract

Raised images are produced by contacting an electrostatic latent image on a xerographic matl. with a dry, free-flowing, self-contained intumescent electroscopic toner mixture to develop the image, transferring the toner to a transfer surface and heating the transferred toner sufficiently to cause intumescence of it and provide and permanent raised image. The method is used for producing braille images, letter-heds and business cards. Raised images are produced cheaply and quickly (about 15 seconds) and faint images can be produced sharply with clean background.

Description

"Verfahren zur elektrophotographischen Herstellung erhabener"Process for the electrophotographic production of raised

Abbildungen und Tonergemisch zu seiner Durchführung" Die Erfindung betrifft ein Verfahren zur xerographischen Herstellung erhabener Abbildungen. Außerdem betrifft die Erfindung Tonergemische zur Durchführung des Verfahrens. Weiter betrifft die Erfindung die Herstellung erhabener Abbildungen mittels anderer elektrophotographischer Verfahren und Tonergemische zu deren Durchführung.Illustrations and toner mixture for its implementation "The invention relates to a method for the xerographic production of raised images. aside from that the invention relates to toner mixtures for carrying out the method. Further concerns the invention the production of raised images by means of other electrophotographic Processes and toner mixtures for their implementation.

Ein Ziel der vorliegenden Erfindung ist es, die große Menge an gedruckten Informationen auch Blinden zugänglich zu machen, indem man erhabene Kopien eines beliebigen flachgedruckten Origi.nals ohne die Erfordernis der Übertragung i.n die Braille-Blindenschrift herstellt und dafür billige, schnell arbeitende Kopiergeräte, wie ein Xerox-Bürokopiergerät, verwendet. Ein weiteres Ziel der vorliegenen Erfindung ist es, z.B. für Briefköpfe und Geschäftskarten geeignete Drucke mit Gravürtypen herzustellen und flache besch bene oder bedruckte Blätter als kopien mit erhabenem Druck zu reproduzieren. Um ein einzelnes Blatt mit erhabenem Druck herzustellen, war es bisher erforderlich, Gravür- oder auf sonstige Weise geformte Typen und dann entweder Präge- oder thermograpsehe Drucke herzustellen, wozu ein erheblicher Kostenaufwand und ein mehrstündiger Arbeitsaufwand erforderlich sind. Es wurde Jedoch nunmehr gefunden, daß es bei Verwendung von speziellen Tonergemischen möglich ist, Blätter mit erhabenem Druck auf einem elektrophotographischem Kopiergerät unter geringfügigen Kosten innerhalb von 15 Sekunden herzustellen. Ein weiteres Ziel der vorli.e genden Erfindung ist es, erhabene Schriftzeichen auf Trägermaterialen herzustellen, die sich zum weitgehenden Ersatz des heute bei Datenverarbeitungsanlagen verwendeten optischen Lesens von Schriftzeichen durch ein Kontaktlesen dieser Schriftzeichen eignen.An aim of the present invention is to reduce the amount of printed Making information accessible to the blind by making raised copies of a any flat-printed original without the requirement of transfer to the Produces Braille and uses cheap, fast-working copiers for it, like a Xerox office copier. Another object of the present invention is it, e.g. for letterheads and business cards suitable prints with engraving types manufacture and flat dam flat or printed sheets as copies reproduce with raised print. Around a single sheet of raised print manufacture, it was previously necessary to engrave or otherwise shaped Types and then either embossing or thermographe printing, including a Considerable costs and hours of work are required. However, it has now been found that when using special toner mixtures is possible, sheets with raised printing on an electrophotographic copier Manufactured in 15 seconds at a marginal cost. Another one The aim of the present invention is to create raised characters on carrier materials to produce, which is to a large extent replacement of today's data processing systems used optical reading of characters by contact reading of those characters suitable.

Wieder ein anderes Ziel der vorliegenden Erfindung ist es, einen elektrophotographischen Mehrkomponenten-Toner mit verbesserten triboelektrischen Eigenschaften zur Verfügung zustellen,der auch die schwächsten Zeichen mit großer Schärfe wiedergibt und dabei den Untergrund doch sauber und frei von Unreinheiten und Schleiern hält. Noch ein anderes Ziel der vorliegenden Erfindung ist es, einen elektrophotographischen Mehrkomponenten-Toner zur Verfügung zu stellen, der beim Erhitzen nach dem xerographischen AufbrinGen auf ein Trägermaterial sein Volumen erheblich vergrößert.Yet another object of the present invention is to provide an electrophotographic Multi-component toners with improved triboelectric properties are available that reproduces even the faintest characters with great clarity and at the same time keeps the surface clean and free of impurities and veils. Another Another object of the present invention is to provide a multicomponent electrophotographic toner to provide the heating after xerographic application on a carrier material increases its volume considerably.

Außerdem ist es Ziel der vorliegenden Erfindung, einen elektrophotographischen Mehrkomponenten-Toner zur Verfügung. zu stellen, der beim Aufblähen und während des erhitzens ein organisches @ beschriebene Material freisetzt, wodurch das in der US-PS 2 776 907/, jedoch auf andere mühevollere Weise durchgeführte Lösungsmittelfixieren eines elektrostatischen Bildes möglich wird.It is also an object of the present invention to provide an electrophotographic Multi-component toners available. to face that when puffing up and during of heating an organic @ releases described material, whereby what is done in US Pat. No. 2,776,907 /, but in a different, more laborious manner Solvent fixing of an electrostatic image becomes possible.

Die Erfindung betrifft demgemäß ein Verfahren zur elektrophotographischen Herstellung erhabener Abbildungen, das dadurch gekennzeichnet ist, daß (a) ein latentes elektrostatisches Bild auf einem xerographischen Körper hergestellt wird; (b) der xerographische Körper mit einem trockenen, frei fließenelektroskopischen den, sich selbst aufblähenden/onergemisch unter Entwicklung des latenten elektrostatischen Bildes kontaktiert wird; (c) der verteilte Toner vom xerographischen Körper auf eine Ubertragungsoberfläche überführt wird; und (d) der übertragene Toner ausreichend erwärmt wird, um ihn unter Herstellung einer permanenten erhabenen Abbildung auf der Übertragungsoberfläche aufzublähen.The invention accordingly relates to a method for electrophotographic Production of raised images, which is characterized in that (a) a latent forming an electrostatic image on a xerographic body; (b) the xerographic body with a dry, free-flowing electroscopic den, itself self-inflating / onerverbindungen with development of the latent electrostatic Image is contacted; (c) the dispersed toner from the xerographic body a transfer surface is transferred; and (d) the transferred toner is sufficient is heated to create a permanent raised image on it to inflate the transfer surface.

Weiter betrifft die Erfindung ein xerographisches Tonergemisch zur Durchführung des erfindungsgemäßen Verfahrens, das ein stabiles, trockenes, frei fließendes, sich selbst aufblähendes,elektroskopisches Pulvergemisch enthält, das im wesentlichen aus einem Thermo-Klebstoff, einem Pigment und einem Trockenblähmittel besteht.The invention further relates to a xerographic toner mixture for Implementation of the method according to the invention, which is a stable, dry, free contains flowing, self-inflating, electroscopic powder mixture that essentially of a thermal adhesive, a pigment and a dry blowing agent consists.

Gemäß einer vorzugsweisen Ausführungsform besteht das Tonergemisch aus Mikrokügelchen, die ein freisetzbares eingeschlossenes Gas enthalten.According to a preferred embodiment, the toner mixture consists of microspheres containing a releasable entrapped gas.

Gemäß einer weiterer vorzugsweisen Ausführungsform des erfindungsgemäßen Verfahrens wird ein Tonergemisch verwendet, das ein aus Einzelteilchen bestehendes Blähmittel enthält, in dem ein durch thermischen Abbau freisetzbares Gas eingeschlpssen ist.According to a further preferred embodiment of the invention Method is a toner mixture is used, which consists of a single particle Contains blowing agent in which a gas that can be released by thermal decomposition is trapped is.

Vorzugsweise wird als Bestandteil des Tonergemisches ein Thermo Klebstoff verwendet, der zumindest ein Material aus der Gruppe der Mischpolymerisate von Styrol und Methacrylester, Isopren, Polyäthylen, Phenolformaldehyd-Mischpolymerisate, Butadien-Polymerisate, Melaminharze, Bitumen und Vinylharze, enthält.A thermal adhesive is preferably used as a component of the toner mixture used, the at least one material from the group of copolymers of styrene and methacrylic ester, isoprene, polyethylene, phenol-formaldehyde copolymers, butadiene polymers, Contains melamine resins, bitumen and vinyl resins.

Das im Blähmittel bei Raumtemperaturen eingeschlossene Gas vergrößert sein Volumen vorzugsweise beim Erwärmen. Das in den Kunststoff-Mikrokügelchen bei Raumtemperatur eingeschlossene und beim Erwärmen expandierbare Gas besteht vorzugsweise aus einem Kohlenwasserstoffgas. Das Blähmittel besteht vorzugsweise aus synthetischen Kunststoff-Mikrokügelchen, die bei Raumtemperatur ein eingeschlossenes Kohlenwasserstoffgas enthalten, welches beim Erwärmen sein Volumen vergrößert. Insbesondere bestehen die Mikrokügelchen des Blähmittels aus Vinylidenchlorid-Acrylnitril-Mischpolymerisaten mit einem Durchmesser von ungefähr 0,5 bis 20 Mikron, welche als eingeschlossenes Gas vorzugsweise Isobutan enthalten.The gas trapped in the blowing agent at room temperatures is enlarged its volume preferably when heated. That in the plastic microspheres A gas enclosed at room temperature and expandable when heated is preferred from a hydrocarbon gas. The blowing agent is preferably synthetic Plastic microspheres that form an entrapped hydrocarbon gas at room temperature which increases its volume when heated. In particular, exist the microspheres of the blowing agent made of vinylidene chloride-acrylonitrile copolymers approximately 0.5 to 20 microns in diameter, which are included as included Gas preferably contain isobutane.

Insbesondere bestehen die Mikrokügelchen des Blähmittels aus Vinylidenchlorid-Acrylnitril-Mischpolymerisaten mit einem mittleren Durchmesser von ungefähr 8 Mikron, welche vorzugsweise eingeschlossenes Isobutangas enthalten. In particular, the microspheres of the blowing agent consist of vinylidene chloride-acrylonitrile copolymers having an average diameter of about 8 microns, which is preferably included Contains isobutane.

Das aus Einzelteilchen bestehende Blähmittel enthält vorzugsweise mindestens eine Verbindung aus der Gruppe N,N'-Dimethyl-N,N'-Dinitrosophthalamid, Azoisobutyrodinitril und Azodicarbonamid.The particulate blowing agent preferably contains at least a compound from the group consisting of N, N'-dimethyl-N, N'-dinitrosophthalamide, azoisobutyrodinitrile and azodicarbonamide.

Das Tonergemisch enthält das Vinylidenchlorid-Acrylnitril-Mischpolymerisa'-Blähmittel vorzugsweise in einer Menge von ungefähr 0,1 bis ungefähr 99,5 Volumprozent, bezogen auf das Volumen des gesamten Gemisches. Insbesondere enthält das Tonergemisch ungefähr 20 Volumprozent Blähmittel, bezogen auf das Volumen des gesamten Gemisches.The toner mixture contains the vinylidene chloride-acrylonitrile mixed polymerisation blowing agent preferably in an amount of from about 0.1 to about 99.5 percent by volume on the volume of the entire mixture. In particular, the toner mixture contains approximately 20 percent by volume blowing agent, based on the volume of the entire mixture.

Die Blähmittel-Nikrokügelchen weisen vorzugsweise einen hohlen Aufbau auf,undin die Hohlräume sind vorzugsweise Luft oder Stickstoff als aufblähbares Gas eingeschlossen.The blowing agent microspheres are preferably hollow in construction on, and in the cavities are preferably air or nitrogen as the inflatable Gas included.

Die erfindungsgemäß verwendeten Blähmittel enthalten als eingeschlossenes aufblähbares Gas vorzugsweise Stickstoff.The blowing agents used in the present invention contain as included inflatable gas, preferably nitrogen.

Erfindungsgemäß können zur Durchführung des Verfahrens zur elektrophotographischen Herstellung erhabener Abbildungen geeignete Tonergemische hergestellt werden, indem man 100 Volumteile eines im Handel erhältlichen Xerox-Toners zu 1/10 bis zu 200 und mehr Volumteilen aufblähbaren Mikrokügelchen zusetzt. Durch Verwendung eines für das betreffende Xerox-Gerät geeigneten Toners, zu dem man die aufschäumbaren Mikrokügelchen einfach zusetzt, erhält man unmittelbar beim Kopieren Kopien mit erhabenen Abbildungen oder Schriftzeichen, ohne daß dabei z.B. die Wärme in der Schmelzzone, die Entwicklungszeit und die Verweilzeit verändert werden müssen.According to the invention, to carry out the method for electrophotographic Production of raised images suitable toner mixtures are produced by 100 parts by volume of a commercially available Xerox toner from 1/10 up to 200 and adding more parts by volume to expandable microspheres. Using a Suitable toner for the Xerox machine in question, to which the foamable Simply adding microspheres, copies are obtained immediately when copying raised images or characters without, for example, the warmth in the Melting zone, the development time and the residence time have to be changed.

Welche Tonergemische und Temperaturen im Einzelfall verwendet werden, hängt von der thermischen Stabilität der als Trägermaterialien verwendeten Bögen ab. Die aufblähbaren Toner können gegebenenfalls ein beim Erwärmen freisetzbares Gas enthalten, blähen sich jedoch in allen Fällen beim Erwärmen erheblich auf.Which toner mixtures and temperatures are used in each individual case, depends on the thermal stability of the carrier materials used Arches off. The inflatable toners may optionally be one which is releasable upon heating Contain gas, but in all cases inflate considerably when heated.

Die nachstehenden Beispiele erläutern die Erfindung.The following examples illustrate the invention.

Beispiel 1 Toner, Xerox 813 100 Volumteile Aufschäumbare Mikrokügelehen 0,1 Volumteile Es werden aufschäumbare Mikrokügelchen der Dow Chemical Co., Midland, Michigan, verwendet. Diese aufschäumbaren Mikrokügelchen bestehen aus einem Vinylidenchlorid-Acrylnitril-Pulver mit eingeschlossenem Isobutangas, die eine Teilchengröße von ungefähr 0,5 bis 20 Mikron und eine mittlere Teilchengröße von 8 Mikron aufweisen. Es wurde gefunden, daß diese Pulver elektroskopisce Eigenschaften aufweisen und demgemäß zum Xerox-Toner unter Herabsetzung der Gesamtkosten des Toners zugemischt werden können. Der auf diese Weise hergestellte Toner führte zu Kopien mit erhabenen Schriftzeichen bzw. Abbildungen. Die Schriftzeichen sind scharf ausgebildet, und die als Unterlage verwendeten Bögen weisen ein sehr sauberes Aussehen auf. Die Druckzeichen zeigen bei 25facher Vergrößerung eine dichte erhabene Struktur mit einem gekörnten Aussehen, das vielen eng zusammengepackten braunen bis schwarzen Ballons ähnelt, wogegen die üblichen Zerox-Schriftzeichen das Aussehen von geschmolzener und verfestigter fließender Lava mit Brüchen, Sprüngen und Staubbildung aufweisen. Example 1 Toner, Xerox 813 100 parts by volume Expandable microspheres 0.1 parts by volume. Expandable microspheres from Dow Chemical Co., Midland, Michigan, used. These foamable microspheres consist of a vinylidene chloride-acrylonitrile powder with entrapped isobutane gas having a particle size of about 0.5 to 20 Microns and a mean particle size of 8 microns. It was found, that these powders have electroscopic properties and accordingly to the Xerox toner can be admixed while reducing the total cost of the toner. The on Toner produced in this way resulted in copies with raised characters or letters. Illustrations. The characters are sharp and those used as a base Arches have a very clean appearance. The print marks show at 25 times Enlargement a dense raised structure with a grainy appearance that many resembles tightly packed brown to black balloons, whereas the usual ones Zerox characters give the appearance of melted and solidified flowing Show lava with cracks, cracks and dust formation.

B e i s p i e l 2 Toner, Xerox 813 100 Volumteile Aufschäumbare MikrokUgelchen 1 Volumteil Bei Verwendung des vorstehenden Toners erhält man unter Verwendung des Xerox-Geräts 813 Kopien mit Schriftzeichen mit einer Höhe von 0,025 mm. Ex. 2 Toner, Xerox 813 100 parts by volume Foamable microspheres 1 part by volume When using the above toner, using the Xerox device 813 copies of characters 0.025 mm high.

Beispiel 3 Toner, Xerox 813 100 Volumteile Aufschäumbare Mikrokügelchen 5 Volumteile Bei Verwendung des vorgenannten Toners erhält man Kopien mit Schriftzeichen mit einer Höhe von 0,051 mm. Example 3 Toner, Xerox 813 100 parts by volume Expandable microspheres 5 parts by volume When using the aforementioned toner, copies with characters are obtained with a height of 0.051 mm.

Beispiel 4 Toner, Xerox 813 100 Volumteile Aufschäumbare Mikrokügelchen 7,5 Volumteile Bei Verwendung des vorgenannten Toners erhält man Kopien mit Schriftzeichen mit einer Höhe von 0,063 mm. Example 4 Toner, Xerox 813 100 parts by volume Expandable microspheres 7.5 parts by volume If the aforementioned toner is used, copies with characters are obtained with a height of 0.063 mm.

Beispiel 5 Toner, Xerox 813 100 Volumteile Aufschäumbare Mikrokügelchen 8 Volumteile Bei Verwendung des vorbeschriebenen Toners erhält man Kopien mit 5chriftzeichen mit einer Höhe von 0,076 mm. Example 5 Toner, Xerox 813 100 parts by volume Expandable microspheres 8 parts by volume When using the toner described above, copies with 5 characters are obtained with a height of 0.076 mm.

B e i 5 p i e 1 6 Toner, Xerox 813 100 Volumteile Aüfschäumbare Mikrokügelchen 20 Volumteile Bei Verwendung des vorbeschriebenen Toners erhält man Kopien mit Schriftzeichen mit einer Höhe von 0,152 mm, die für ein Lesen durch Blinde mittels Abtasten ausreicht. B e i 5 p i e 1 6 toner, Xerox 813 100 parts by volume Foamable microspheres 20 parts by volume When using the toner described above, copies with characters are obtained with a height of 0.152 mm, which is sufficient for reading by the blind by means of palpation.

Beispiel 7 Toner, Xerox 813 100 Volumteile Aufschäumbare Idikrokügelchen 50 Volumteile Bei Verwendung des vorbeschriebenes Toners erhält man Kopien mit Schriftzeichen mit einer Höhe von 0,152 mm mit flockigem Aussehen, die nicht gut auf der Unterlage verankert sind, was auf die kurze Zeit in der Hitzekammer des Geräts zurückgeht, die wahrscheinlich nicht zum ausreichenden Erhitzen einer solchen Masse ausreicht. Example 7 Toner, Xerox 813 100 parts by volume of foamable idicrospheres 50 parts by volume When using the toner described above, copies with characters are obtained with a height of 0.152 mm with a flaky appearance that does not sit well on the substrate are anchored, which is due to the short time in the heat chamber of the device, which is probably not sufficient to heat such a mass sufficiently.

Anschließendes Erhitzen in einem Ofen auf 1350C führt zu einer weiteren Aufblähung unmittelbar nach dem Entwickeln bis auf eine Höhe von 0,25 mm. Das Blatt mit den erhabenen Schriftzeichen wird dann mit einem klaren acrylischen Fixativ-Spray (Artists) bespniht. Subsequent heating in an oven to 1350C leads to another Bloating immediately after developing to a height of 0.25 mm. The leaf with the raised characters is then with a clear acrylic fixative spray (Artists) spotted.

Nach dem Trocknen weisen die Schriftzeichen noch eine Höhe von 0,20) mm auf, was auf die Lösungsmittelwirkung des aufgesprühten Fixativs zurückgeht. Das erhaltene Blatt eignet sich zur Verwendung als Gummistempel oder als Druckplatte für den Anilin-Druck. After drying, the characters are still 0.20) mm, which is due to the solvent effect of the sprayed fixative. The sheet obtained is suitable for use as a rubber stamp or as a printing plate for aniline printing.

13eispiel 8 Ein aufblähbarer Toner wird ohne Verwendung von aufsehäumbaren Mikrokügelchen und unter Verwendung eines thermisch instabilen ein Gas freisetzenden Vjateria2.C hergestellt. Example 8 A puffable toner is produced without using a puffable toner Microspheres and using a thermally unstable gas-releasing agent Vjateria2.C manufactured.

Der Tone weist die nachstehende Zusammensetzung auf: Staybellite Ester 10 (Hercules) *) 100 g Siliciumdioxid-Aerogel (Cabosil) 5 g Druckerschwärze, Monarch 71 5 g Gutta Percha 10 g Nitrosan (E.I. DuPont) 5g *) hydriertes Baumharz (Rosin) und Weichmacher aus dem Diäthylenglykolester eines hydrierten Baumharzes Alle vorstehenden Bestandteile mit Ausnahme des letzteren werden bei 600C in einer Gummimühle vermischt. Die Masse wird beim Vermischen von der hinteren Rolle mit einer Rakel abgeschabt und wieder zwischen die beiden Walzen zurückgeführt. Die Masse wird dann auf 400C abgekühlt und das Nitrosan zugemischt. Die Masse wird abgenommen, indem man zuerst kaltes Wasser zwischen die Walzen leitet und die Masse dann mit der Rakel von der hinteren Walze abschabt. Die Masse wird dann abgekühlt und auf eine Teilchengröße unterhalb 74 Mikron zermahlen. Der auf diese Weise hergestellte Teuer weist beim Erhitzen eine gute Anhaftung auf dem Trägerblatt auf und bläht sich dabei auf das 5- bis lOfachc eines Volumens auf. Das Gutta Percha entwickelt beim Erhitzen hohe Scherkräfte und adiabatische Wärme und ist in der Kälte auß@rordentlich brüchig, wodurch das Zermahlen erleichtert wird. Der Toner wird nach dem Zermahlen zur Aufrechterhaltung seiner freifließenden Eigenschaften zur Vermeidung einer Verklumpung mit ciumdioxid-Aerogel bestäubt. Bei Verwerldung des vorstehenden Toners erhält man Kopien mit Schriftzeichen mit einer Höhe von 0,051 mm.The clay has the following composition: Staybellite Ester 10 (Hercules) *) 100 g silicon dioxide airgel (Cabosil) 5 g printing ink, Monarch 71 5 g gutta percha 10 g nitrosan (E.I. DuPont) 5g *) hydrogenated tree resin (rosin) and hydrogenated tree resin diethylene glycol ester plasticizer All of the above Ingredients except the latter are mixed in a rubber mill at 600C. When mixing, the mass is scraped off the rear roller with a squeegee and returned again between the two rollers. The mass is then to 400C cooled and mixed in the nitrosan. The mass is taken off by first cold water is passed between the rollers and the mass is then removed with the squeegee scrapes off the rear roller. The mass is then cooled and reduced to a particle size grind below 74 microns. The expensive produced in this way points to the Heat up a good adhesion to the carrier sheet and in doing so it puffs up onto the 5- to 10-fold of a volume. The gutta percha develops high levels when heated Shear forces and adiabatic heat and is extremely brittle in the cold, which makes grinding easier. The toner will be maintained after grinding its free flowing properties to avoid clumping with cium dioxide airgel pollinated. When the above toner is used, copies with characters are obtained with a height of 0.051 mm.

Der Handelsname ?tNitrosan? kennzeichnet N,N'-Dimethyl-N,N'-dinitrosophthalamid. Nitrosan setzt beim Erhitzen auf 80 bis 1000C unter thermischer Zersetzung Stickstoffgas frei. Es können jedoch auch andere thermisch instabile Verbindungen oder Verbindungsgemische verwendet werden. Azoverbindungen, wie Azodicarbonamid, Azoisobutyrodinitril und Benzolsulfohydrazin,und Amine,wie Dinitrosopentamethylentetramin, sind ebenfalls thermisch unter Freisetzung von Stickstoff zersetzbare, erfindungsgemäß geeignete Verbindungen. Das Kunststoffmaterial, in welches das ein Gas freisetzende Mittel eingeschlossen ist, kann aus einem beliebigen bekannten Thermo-Klebstoff bestehen, welcher bei Rawmtemperatur trocken ist und frei fließt, wie aus Vinylharzen, Styrolharzen, Acrylharzen und Acryl-Mischpolymerisatharzen, Celluloseesterharzen, Polyamiden, Phenolharzen und Mischpolymerisaten von Phenolharzen, Butadien-Polymerisaten, Polyäthylen und Polyolefinen, natürlichen Harzen, wie Bitumen und Gilsonit gemäß U-PS 2 297 691. Bei der Herstellung der aufblähbaren Toner- gemäß dem vorliegenden Beispiel und zur Veränderung der Höhe der hercstellten Schriftzeichen können das Verhältnis von thermisch instabiler Komponente zum Kunststoffmaterial und ebenso die Art einer oder beider Komponenten verändert werden.The trade name? TNitrosan? denotes N, N'-dimethyl-N, N'-dinitrosophthalamide. When heated to 80 to 1000C, nitrosan releases nitrogen gas with thermal decomposition free. However, other thermally unstable compounds or mixtures of compounds can also be used be used. Azo compounds such as azodicarbonamide, azoisobutyrodinitrile and Benzenesulfohydrazine, and amines such as dinitrosopentamethylenetetramine, are also thermally decomposable with the release of nitrogen, suitable according to the invention Links. The plastic material in which the gas releasing agent may consist of any known thermal adhesive, which is dry at raw temperature and flows freely, such as from vinyl resins, styrene resins, Acrylic resins and acrylic mixed polymer resins, cellulose ester resins, polyamides, Phenolic resins and copolymers of phenolic resins, butadiene polymers, polyethylene and polyolefins, natural resins such as bitumen and gilsonite according to U-PS 2,297 691. In the manufacture of the inflatable toner according to the present example and to change the height of the characters produced, the ratio from thermally unstable component to plastic material and also the type of one or both components can be changed.

Beispiel 9 Ein verbessertes Tonergemisch zum Ersetzen des Xerox 813-Toners, sofern dieser nicht vorhanden ist, kann wie folgt hergestellt werden: In einer Gummimühle mit 2 Gummimahlwalzen mit Abmessungen von 15,24 x 30,48 cm werden bei 1130C die nachstehenden Komponenten vermischt. Example 9 An improved toner blend to replace the Xerox 813 toner, If this is not available, it can be produced as follows: In a rubber mill with 2 rubber grinding rollers with dimensions of 15.24 x 30.48 cm at 1130C the the following components mixed.

Poly-n-butyl-methacrylat 100 g Poly-isobutyl-methacrylat 100 g Tri-ortho-cresylphosphat 5 g Dibutyl-zinn-dilaurat 2 g Butylstearat 2 g Aufschäumbare Mikrokügelchen 5 g öllösliche Druckerschwärze (Irgacet, Ciba) 1 g Druckerschwärze (Monarch 71) 10 g Aluminiumoxid-hydrat 5 g Siliciumdioxid-Aerogel (Cabosil) 1 g.Poly-n-butyl methacrylate 100 g poly-isobutyl methacrylate 100 g tri-ortho-cresyl phosphate 5 g dibutyl tin dilaurate 2 g butyl stearate 2 g foamable microspheres 5 g Oil-soluble printing ink (Irgacet, Ciba) 1 g printing ink (Monarch 71) 10 g Alumina hydrate 5 g silica airgel (Cabosil) 1 g.

Die einzelnen Komponenten werden in der vorstehenden Reihenfolge zusammengemischt. Die aufschäumbaren Mikrokügelchen werden aufgeschäumt und dann mittels der beim Aufschäumen zugeführten warme geschmolzen, wodurch sie unter Verlust ihres Isobutangehalts zu einem Teil des Tonergemisches werden. Die Mikrokügeichen werden zu dem Gemisch zugemischt, um ihm eine Affinität für die später als Pulver zu dem vorgenannten zermahlenen und zerkleinerten Produkt zuzumischenden aufschäumbaren Mikrokügelchen zu verleihen.The individual components are mixed together in the above order. The foamable microspheres are foamed and then by means of the at Lathering supplied warm melted, causing them to lose their isobutane content become part of the toner mix. The microspheres become the mixture mixed in to give it an affinity for the later as a powder to the aforementioned foamable microspheres to be admixed with milled and crushed product to rent.

Aus dem vorgenannten Gemisch wird ein Blatt mit einer Dicke von 0,381 mm hergestellt, das bis auf eine Größe unterhalb 74 Mikron zerkleinert und anstelle des Xerox 813-Toners verwendet wird. Zu 100 Volumteilen des vorgenannten Toners werden 5 Volumteile der aufschäumbaren Mikrokügelchen zugesetzt. Man erhält damit sehr scharfe Kopien mit Schriftzeichen mit einer Höhe von 0,051 mm.The above mixture becomes a sheet with a thickness of 0.381 mm, which is crushed to a size below 74 microns and instead Xerox 813 toner is being used. to 100 parts by volume of the foregoing Toner is added to 5 parts by volume of the foamable microspheres. You get thus very sharp copies with characters with a height of 0.051 mm.

Durch die zugesetzte Farbe werden die Mikrokügelchen beim Aufschäumen in gewissem Maße gefärbt, wodurch die Schwärze des erhbenen Druckes verbessert wird.The added color causes the microspheres to expand when they foam colored to some extent, which improves the blackness of the raised print.

Die in den Beispielen 1 bis 9 beschriebenen aufblähbaren Tonergemische sind im Ergebnis sehr stabil und dauerhaft. Das Tonergemisch, von Beispiel 3 wird in einem Xerox 813-Gerät 6 Monate lang täglich 8 Stunden verwendet, und der Tonertank dabei routine mäßig nachbeschickt, wenn der Tonerspiegel auf eine gewisse Höhe abgesunken ist. Man erhält dabei in allen Fällen Kopien mit erhabenem Druck. Die vorerhitzten oder vorgeschäumten Mikrokügelchen aus Beispiel 9, die vor allem Luft enthalten, durch welche das Isobutan oder die anderen Gase teilweise ersetzt werden, stellen erfindungsgemäß nützliche Mikrokügelchen dar, die jedoch nicht in den Rahmen von Beispiel 9 fallen. Diese Luft enthaltenden Mikrokügelchen können wie in den Beispielen 1 bis 6 entweder als einzige Mikrokugel-Komponenten oder als Zumischung zu auSschäumbaren Mikrokügelchen verwendet werden. Der Luftgehalt reicht zur Herstellung einer ausreichenden Aufblähung des Tonergemisches aus. Mikrokügelchen, welche ein anderes Gas als Luft oder Isobutan enthalten, stellen ebenfalls erfindungsgemäß geeignete Materialien dar..So können z.B. Stickstoff enthaltende Mikrokügelchen gemäß den Beispielen 1 bis 9 unter Ausschluß der Beispiele 6 bis 7 zur Herstelausreichend lung von/auSblähbaren Tonergemischen für xerographische Drucke verwendet werden.The expandable toner mixtures described in Examples 1-9 are very stable and durable as a result. The toner mixture from Example 3 is used 8 hours a day in a Xerox 813 machine for 6 months, and the toner tank routinely replenished when the toner level has dropped to a certain level is. In all cases, copies with raised print are obtained. The preheated or pre-expanded microspheres from Example 9, which mainly contain air, by which the isobutane or the other gases are partially replaced microspheres useful in the invention, but not within the scope of Example 9 fall. These air-containing microspheres can be used as in the examples 1 to 6 can be foamed either as the only microsphere components or as an admixture Microspheres can be used. The air content is sufficient to produce a sufficient Inflation of the toner mixture. Microspheres, which are a gas other than air or contain isobutane, are also suitable materials according to the invention For example, nitrogen-containing microspheres according to Examples 1 to 9 with the exclusion of Examples 6 to 7 for the production of sufficient development of / inflatable Toner mixtures can be used for xerographic prints.

Bei ihrer Verwendung in einem Xerox-Kopiergerät weisen die aufblähbaren Tonergemische gemäß der vorliegenden Erfindung die unerwartete und vorteilhafte Wirkung zur da.) sie die weiche, amorphe photoleitende Trommel vo@ dem Verkratzen durch Komponenten des triboelektrischen, ~m Toner-Aufladungsraum verwendeten Systems bewahren. Diese Komponenten werden technisch als "Entwickler" bezeichnet. Der Entwickler entspricht nicht einem photographischen Entwickler t-.-ie er in der Photographie verwendet w.rdund photochemisch definiert ist, da er aus Glaskügelchen mit einem Durchmesser von ungefähr 0,0127 mm besteht, die miteinem in Polyvinylbutyral-Phenolformaldehyd löslichen Harzgemisch gemäß der US-PS 2 618 551 beschichtet sind. Der Entwickler verbleibt im Toner-Aufladungsraum und wird nicht verbraucht. Er vermischt sich mit dem Toner und entwickelt beim Vermischen mit den kleineren Tonerteilchen eine Aufladung des Gemisches. Wenn diese beschichteten Entwicklerkügelchen mit ihrer Komponente aus aufgeladenen Tonerteilchen huber die Oberfläche der Selen-Trommel berieselt werden, überführen sie ihre Tonerbeladung auf die elektrostatisch aufgeladenen Flächen, rollen weiter über die Oberfläche der Trommel und spülen dabei gegebenenfalls an den nicht belichteten, nicht elektrostatisch aufgeladenen Flächen, die sauber und frei von verstreutem Toner sein müssen, anhaftende schwarze Tonerteilchen von diesen Flächen. Zerkratzte Trommeln stellen ein übliches Service- und Ersatzproblem dar, obwohl die Glaskügeln wesentlich für gute elektrophotographische Drucke sind und deshalb verwendet werden müssen, obwohl sie die Trommel zerkratzen. Die Einführung dcr aufschäumbaren Mikrokügelchen-Komponente des erfindungsgemäßen Toners in das herkömmliche Xerox-Zweikomponententoner-System, nämlich Toner + Glaskügelchen-Entwickler,scheint eine Auswirkung auf das triboelektrische System zu haben, da jetzt die Glaskügelchen die Trommel nicht mehr direkt berühren und deshalb auch nicht verkratzen und trotzdem zu einem ausgezeichneten Spülen der nicht elektrostatisch aufgeladenen Flächen der Selen-Trommel führen. Es wurde während der gesamten Zeit der Verwendung der aufschäumbaren Mikrokügelchen im aufblähbaren Toner kein Zerkratzen der Selen-Trommel beobachtet. Auf diese Weise wird ein kostspieliges Service-Problem des weichen photoleitenden Materials beseitigt.When used in a Xerox copier, the inflatable Toner mixtures according to the present invention the unexpected and advantageous Effect to there.) They the soft, amorphous photoconductive drum from scratching by components of the triboelectric system used in the toner charging chamber maintain. These components are technically referred to as "developers". The developer does not correspond to a photographic developer t -.- ie he in photography used w.rdund is defined photochemically as it consists of glass beads with a Diameter of approximately 0.0127 mm, which is composed of a polyvinyl butyral-phenol-formaldehyde soluble resin mixture according to US Pat. No. 2,618,551. The developer remains in the toner charging chamber and is not used up. He mixes with the toner and develops a charge as it mixes with the smaller toner particles of the mixture. When these coated developer beads with their component from charged toner particles sprinkled over the surface of the selenium drum transfer their toner charge to the electrostatically charged surfaces, continue to roll over the surface of the drum and, if necessary, wash up the unexposed, not electrostatically charged surfaces that are clean and must be free from scattered toner, adhering black toner particles from them Surfaces. Scratched drums are a common service and replacement problem, although the glass beads are essential to good electrophotographic prints and therefore must be used even though they scratch the drum. The introduction the foamable microsphere component of the toner of the invention into the conventional Xerox two-component toner system, namely toner + glass bead developer, appears an impact to have on the triboelectric system since now the glass beads no longer touch the drum directly and therefore do not scratch it and still get an excellent rinse without being electrostatic lead charged surfaces of the selenium drum. It was going on all along the use of the foamable microspheres in the inflatable toner does not scratch observed the selenium drum. Doing this becomes a costly service problem of the soft photoconductive material is eliminated.

Das erfindungsgemäß geeignete triboelektrische System, das durch Zusetzen der Mikrokügelchen in beliebiger Form, gemäß einer vorzugsweisen Ausführungsform jedoch als aufsahäumbare Mikrokügelchen, die zuerst in nicht aufgeschäumter Form mit ihrem eingeschlossenen Material zugesetzt werden, wonach sie vom ungeschäumten in den aufgeschäumten Zustand unter gleichzeitiger Expansion oder Freisetzung des eingeschlossenen Materials überführt werden, hergestellt worden ist, führt zu dem direkten Vorteil von sauberen und scharfen erhabenen Drucken auf einem sauberen Untergrund.The triboelectric system which is suitable according to the invention and which is produced by adding the microspheres in any shape, according to a preferred embodiment however, as frothable microspheres, initially in non-frothed form with their enclosed material are added, after which they are removed from the unfoamed in the foamed state with simultaneous expansion or release of the enclosed material are transferred, has been produced, leads to the direct benefit of clean and sharp raised prints on a clean one Underground.

Diese triboelektrische Erscheinung kann unter Umstanden dadurch erklärt werden, daß der Toner während seiner xerographischen Überführung einer ausreichenden Wärme ausgesetzt wird, welche zu seinem Aufblähen und zum Anhaften auf dem Trägerblatt oder der 0herflche führt, und die Wärme bewirkt unabhängig von der Form ihrer Awendung, wobei sie mittels Strahlung, Röntgenstrahlen und Laserstrahlen zugeführt werden kann, daß sich die Mikrokügelchen relativ zu den anderen Teilchen im Toner oder relativ zueinander reibend bewegen.This triboelectric phenomenon can, under certain circumstances, be explained by this that the toner is sufficient during its xerographic transfer Heat is exposed which causes it to expand and adhere to the carrier sheet or the surface, and the heat, regardless of the form in which it is applied, being applied by means of radiation, X-rays and laser beams can that the microspheres relative to the other particles in the toner or move relative to each other by rubbing.

Triboelektrizität ist die durch Reiben ungleich geladener Oberflächen gegeneinander verursachte Elektrizität. Wenn z.B. ein Kunststoff-Haarkamm gegen ein Pelzstück geschlagen wird, führt dies zur triboelektrischen Aufladung des Kamms, der jetzt, wie ein Magnet Eisenspäne, Staubteilchen anzieht. Demgemäß wirken die erfindungsgemäßen Tonerteilchen aufgrund ihrer durch Reiben während dvr letzten Stufe des xerographischen Verfahrens erzeugten Triboelektrizitrat als Magnet, welcher die peripher verstreuten Teilchen &nzieht und zu einer sauberen, dichten kohärenten Ablagerung des Toners führt.Triboelectricity is the unevenly charged surfaces caused by rubbing electricity generated against each other. If, for example, a plastic hair comb against a piece of fur is hit, this leads to the triboelectric charging of the comb, who now like a magnet Iron filings, attracts dust particles. Accordingly act the toner particles according to the invention due to their rubbing during dvr the last stage of the xerographic process generated triboelectricity as a magnet, which draws the peripherally scattered particles and forms a clean, dense one leads to coherent deposition of the toner.

Die Freisetzung von Gas durch einen Toner stellt eine neue Eigenschaft des erfindungsgemäßen Verfahrens dar, da das Gas nur erforderlichenfalls in der Hitzebehandlungszone und während des Fixierens des thermoklebenden Toners auf das Trägerblatt freigesetzt wird Dies führt zu einer schnellen Vereinigung des Toners mit dem Trägermaterial. Die Vorteile der Lösungsmittelfixierung sind sin der US-PS 2 776 907 und in der US-PS 2 788 288 beschrieben. The release of gas by a toner is a new property of the method according to the invention, since the gas only if necessary in the Heat treatment zone and during the fixing of the thermally adhesive toner on the Carrier sheet is released This leads to a rapid amalgamation of the toner with the carrier material. The advantages of solvent fixation are disclosed in U.S. Patent 2,776,907 and U.S. Patent 2,788,288.

Die Durchführung dieser Fixierung gemäß den herkömmlichen Verfehren ist jedoch mühsam, da demgemäß das Lösungsmittel in einem gesonderten Verfahren auf mühselige und schlecht praktikable Weise verwendet wird. Die vorliegende Erfindung ermöglicht eine Gas fixierung gleichzeitig mit dem Aufblähen und der Bildung des erhabenen elektrophotographischen Druckes. Die erfindungsgemäßen aufschäumbaren Mikrokügelchen stellen in allen Beispielen trokkene, frei fließende, elektroskopische Pulver dar und sind in keiner Weise naß oder mit dem Lösungsmittel getränkt. Perform this fixation according to conventional methods however, it is troublesome because accordingly the solvent is in a separate process is used in a cumbersome and unworkable way. The present invention allows gas fixation at the same time as the expansion and formation of the raised electrophotographic printing. The foamable ones according to the invention Microspheres are dry, free flowing, electroscopic in all examples Powders and are in no way wet or soaked with the solvent.

Zur Standardisierung der Toner-Aufnahme wird der Licht-Dunkel-Regelknopf des Xerox-813-Geräts zwei Stellen unterhalb der Stellung "L" in Richtung der Stellung "D" eingerastet. The light / dark control button is used to standardize the toner uptake of the Xerox-813 two places below the "L" position in the direction of the position "D" engaged.

B e i s p i e 1 10 Es werden aufschäumbare Mikrokügelchen 100 Volumteile und öllösliche schwarze Farbe (Irgacet, Ciba) 0,5 Volumteile in 100 Volumteilen Heptan miteinander vermischt, bei Raumtemperatur auf Böden getrocknet und dann in einer Kugelmühle zu einem Pulver zermahlen. Die gefärbten Mikrokügelchen werden dann in einem Xerox-813-Gerät als einziger Toner verwendet..Sie wirken dabei als stark aufblähbare Tinte oder Toner. Die mit ihnen hergestellten Schriftzeichen weisen eine Höhe von 0-,254 mm auf und haften, da sie aus Vinylidenchlorid-Acrylnitril bestehen, aufgrund ihrer Thermo-Klebkraft auf dem Papierträgermaterial. Ein Nacherhitzen in einem Ofen bei 148,90C führt zu einer weiteren sofortigen Aufblähung und einem anschließenden Niederschmelzen unter Zunahme der Anhaftung an das Papier. EXAMPLE 1 10 Expandable microspheres become 100 parts by volume and oil-soluble black paint (Irgacet, Ciba) 0.5 parts by volume in 100 parts by volume Heptane mixed together, dried on floors at room temperature and then in grind to a powder in a ball mill. The colored microspheres are then used as the only toner in a Xerox 813 machine. They act as a highly inflatable ink or toner. The characters made with them show a height of 0.254 mm and adhere because they are made of vinylidene chloride-acrylonitrile exist, due to their thermal adhesive strength on the paper carrier material. A post-heating in an oven at 148.90C will result in another instant puff and a subsequent melting down with an increase in adhesion to the paper.

B e i s p i e l 11 100 Volumteile aufschäumbare Mikrokügelchen werden als einziger Toner in einem Xerox-813-Gerät verwendet. Man erhält bei Verwendung dieses Toners Kopien mit erhabenen weißen Schriftzeichen. EXAMPLE 11 100 parts by volume of foamable microspheres become used as the only toner in a Xerox 813 machine. You get when using copies of this toner with raised white characters.

Diese erhabenen weißen Schriftzeichen weisen eine Struktur ;.7ie dicht gepackte durchsichtige hohle Ballons auf, die mittels thermischem Kleben auf das Papiertragermaterial und die anderen aufgeblähten Teilchen aufgebracht sind. Anstelle von Trägerpapier wird - (Polyester) jetzt ein Mylan/-Film mit einer Dicke von 0,076 mm verwendet. Dabei erhält man Kopien mit weißlichen, durchsichtigen,erhabenen Schriftzeichen auf einer transparenten Kunststoff-Unterlage. Die erhabene Schrift kann jetzt densitometrisch oder elektrooptisch oder unter Verwendung von photographischen Verfahren gelesen werden. Dichte Teile des Original fi'¼ren- auf den Kopien zu Flächen mit einer entsprechend höheren Lichtstr@ung Ein für die Direirtablesung geeignetes Original wird wie vorstehend beschrieben in eine für die Direktablesung geeignete Kopie auf einem Mylar-Film auf herkömmliche Weise unter Verwendung eines herkömmlichen Xerox-813-Toners umgewandelt. Diese Kopie wird dann mit der Schriftseite nach unten in das Kopiergerät gelegt und daraus unter Verwendung des Toners gemäß dem vorliegenden Beispiel eine Kopie auf einem Mylar-Film mit einer Dicke von 0,076 mm hergestellt. Die erhaltene Kopie enthält den Text in Spiegelschrift und eignet sich für den Anilin-Druck oder als Gummistempel. Die chemische Widerstandsfähigkeit des Vinylidenchlorid-Acrylnitrils und seine Widerstandsfähigkeit gegen Lösungsmittel in Druckfarben und Gummistempelfarben sind beide außerordentlich groß, und da die aufgeblähten, erfindungsgemäß hergestelten Schriftzeichen aus dem vorgenannten Material bestehen, eignen sich die vorbeschriebenen Mylar-Druckplatten ausgezeichnet für das Drucken in hohen Auflagen. Die Widerstandsfähigkeit gegen Lösungsmittel des Xerox-Toners 813 und 914 und des xerographischen Toners der IBM sind im Vergleich zu der des aufblähbaren erfindungsgemäßen Vinylidenchlprid-Acrylnitril-Toners sehr schlecht. Das einfache Zusetzen des erfindungsgemaßen Toners zu eine schlecht Wderstandsfähigkeit gegen Lösungsmittel aufweisenden Tonern erhöht deren Widerstandsfähigkeit gegen Lösungsmittel und führt demgemäß zu einer verbesserten Widerstandsfähigkeit gegen die Verschlechterung des Druckes oder der Offset-Druckplatten aufgrundder Anlösung durch die Druckfarben. Es ist wünschenswert, auf den Mylar-Film einen Grundierungs- oder Verankerungsüberzug aufzubringen, da dies billiger als die Verwendung von aufblähbaren Mikrokügelchen mit Thermo-Klebkraft ist. Für einen Verankerungsüberzug wird erfindungsgemäß das nachstehende Gemisch verwendet: *) Acryloid A-101 (40 % Feststoffe) (Rohm & Haas, N.Y.) 100 g *) Acryloid B-72, festes Material 40 g Vinylchlorid-Acetat-Mischpolymerisat (Bakelite VYHH) 18 g Zinnmercaptid (RS 31 M&T Corp., Rahway, N.J.) 2 g Methyläthylketon 500 g Methylisobutylketon 498 g Cyclohexanon 2 g.These raised white characters have a structure; they are dense packed transparent hollow balloons that are thermally glued to the Paper carrier material and the other puffed particles are applied. Instead of from the backing paper - (polyester) is now a Mylan / film with a thickness of 0.076 mm used. This produces copies with whitish, transparent, raised characters on a transparent plastic base. The raised font can now be densitometric or read electro-optically or using photographic processes will. Dense parts of the original fi'¼ren- on the copies to areas with a corresponding higher luminous flux An original suitable for direct reading is as above written to a direct read copy on Mylar film converted in a conventional manner using a conventional Xerox 813 toner. This copy is then placed face down in the copier and a copy therefrom using the toner according to the present example made on Mylar film 0.076 mm thick. The copy received contains the text in mirror writing and is suitable for aniline printing or as a Rubber stamp. The chemical resistance of vinylidene chloride-acrylonitrile and its resistance to solvents in printing inks and rubber stamp inks are both extraordinarily large, and because the bloated ones are made according to the invention If characters consist of the aforementioned material, those described above are suitable Mylar printing plates are excellent for high volume printing. Resilience against solvents of the Xerox toner 813 and 914 and the xerographic toner the IBM compared to that of the vinylidene chloride-acrylonitrile inflatable toner of the present invention very bad. Simply adding the toner of the present invention to one bad Resistance to toners containing solvents increases their resistance against solvents and accordingly leads to an improved resistance against the deterioration of the pressure or the offset printing plates due to the dissolution by the printing inks. It is desirable to use the mylar film Apply a primer or anchor coat as it is cheaper than is the use of inflatable microspheres with thermal adhesive strength. For one According to the invention, the following mixture is used for anchoring coating: *) Acryloid A-101 (40% solids) (Rohm & Haas, N.Y.) 100 g *) Acryloid B-72, solid material 40 g vinyl chloride acetate copolymer (Bakelite VYHH) 18 g tin mercaptide (RS 31 M&T Corp., Rahway, N.J.) 2 grams of methyl ethyl ketone, 500 grams of methyl isobutyl ketone 498 g cyclohexanone 2 g.

*) Acrylesterharz Die vorstehenden Komponenten werden miteinander gelöst und mittels eines drantumwundenen Stabes ("Meyers"-Stab) auf den Nylar-Film als Überzug aufgebracht. Der Stab Nr. 3 führt zu dem geringstmöglichen geeigneten Verankerungsüberzug, während ein Mehers-Stab Nr. 30 zu dem größtmöglichen geeigneten Verankerungsüberzug unter Verwendung der vorstehenden 10 ß Feststoffe enthaltenden Lösung führt. Das Aufsprühen unter Verwendung von Freon als Treibmittel als Aerosol stellt ein zufriedenstellendes Verfahren zur Aufbringung des Verankerungsüberzugs dar. Obwohl die Aufbringung als Aerosol in Betrieben zu zufriedenstellenden Ergebnissen führt-, erhält man auf diese Weise nicht die genau abgemessenen vorbeschichteten Nylar-Filme wie bei der Aufbringung mittels der "Meyers"-Stäbe. *) Acrylic ester resin The above components are mixed together loosened and applied to the Nylar film using a rod wound around the drum ("Meyers" rod) applied as a coating. Rod # 3 leads to the least suitable Anchoring cover while a # 30 Mehers rod is the largest possible suitable Anchoring coating using the above containing 10 ß solids Solution leads. Spraying using Freon as a propellant as an aerosol provides a satisfactory method of applying the anchoring coating although the application as an aerosol in factories produces satisfactory results In this way, the precisely measured precoated material is not obtained Nylar films as when applying using the "Meyers" rods.

Auf einem solchen vorbeschichteten Mylar-Film ist die Verankerung der erhabenen elektrophotographisch aufgebrachten Schriftzeichen sehr gut, und auf diese Weise hergestellte Matrizen können über lange Zeit in den Maschinen für den Anilin- oder Offset-Druck -verwendet werden.The anchorage is on such a pre-coated Mylar film the raised electrophotographically applied characters very well, and on these Well-made matrices can be used for a long time in the machines for the aniline or offset printing can be used.

B e i s p i e l 12 Gemäß diesem Beispiel sollen farbige Reproduktionen hergestellt werden. Die aufschäumbaren Mikrokügelchen werden in den Farben rot, gelb und blau gefärbt. Der Toner weist die nachstehende Zusammensetzung auf: aufschäumbare Mikrokügelchen 100 Volumteile Heptan 100 Volumteile Farbe 1 Volumteil. Example 12 According to this example, color reproductions getting produced. The foamable microspheres are colored red, colored yellow and blue. The toner has the following composition: foamable Microspheres 100 parts by volume Heptane 100 parts by volume Color 1 part by volume.

Als rote Farbe wird "Irgacet"-Rot, als gelbe Farbe "Irgacet"-Gelb und als blaue Farbe 11lrgacet"-Blau (Hersteller Ciba Co., N.Y., N.Y.) verwendet. In allen Fällen wird das Gemisch in Luft getrocknet und dann zur originalen frei fleßenden Pulverkonsistenz pulverisiert. Es werden nacheinander die Blautöne mit dem blau gefärbten aufschäumbaren Mikrokügelchen, die Rottöne mit den rot gefärbten aufschäumbaren Nikrokügelchen und die Gelbtöne mit den gelb gefärbten aufschäumbaren Mikrokügelchen auf dem gleichen Papierträgermaterial in einem Register kopiert.The red color becomes "Irgacet" -red, the yellow color "Irgacet" becomes yellow and 11lrgacet "blue (made by Ciba Co., N.Y., N.Y.) as the blue color. In all cases, the mixture is dried in air and then released to the original powdered powder consistency. The shades of blue will appear one after the other the blue colored foamable microsphere, the red tones with the red colored ones foamable microspheres and the yellow tones with the yellow colored foamable ones Microspheres copied on the same paper support in a register.

Die Farben werden alle in erhabenem Druck wledergegeben, wobei die tieferen Töne größere Höhen aufweisen. Es wird jetzt ein "Xerox document carrier"-Raster aus einem klaren Plastikumschlag oder einer klaren Plastikhülle mit einem Rastermuster verwendet, der über das Original mit dem jeweiligen Farbton gelegt wird, wenn dieses zur Reproduktion in das Kopi ergerät überführt wird. Da die Intensität der Farbe als verschieden hohe Ablagerungen kopiert wird , ergeben sich die Vorteile des von Dessauer und Clark in Kapitel XIII, Seite 375 ihres Buches beschriebenen "Frost imaging". Diese Kunststoff-Verzerrungsmuster wirken bei Liehtprojektion als photographische Negativs, insbesondere -w.enn als Trägermaterial ein transparenter Mylar-Film verwendet wird, der mit einem thermisch anhaftenden Verankerungsüberzug gemäß Beispiel 11 beschichtet ist.The colors are all given in raised print, with the lower notes have higher heights. It now becomes a "Xerox document carrier" grid from a clear plastic envelope or a clear plastic envelope with a grid pattern is used, which is superimposed on the original with the respective color tone, if this is transferred to the copier for reproduction. As the intensity of the color when copying deposits of different heights, the advantages of Dessauer and Clark described in Chapter XIII, page 375 of their book "Frost imaging ". These plastic distortion patterns act as photographic when projected in light Negatives, especially if a transparent Mylar film is used as the carrier material which is provided with a thermally adhesive anchoring coating according to Example 11 is coated.

Die Vorteile des "Flushing" oder Verschmelzens der Farbgrenzmuster können mittels Heißpressen der erhabenen Abbildungen gegen eine glatte Druckplatte erzielt' werden. Die Höhe der farbigen Schriftzeichen führt auf diese Weise zur entsprechenden Tiefe der Farbe unter erfreulichem Vermischen der Grenzlinien der einzelnen.The advantages of "flushing" or fusing the color boundary patterns can by hot pressing the raised images against a smooth printing plate be achieved. In this way, the height of the colored characters leads to corresponding depth of color with pleasing blending of the border lines of the individual.

Farbtöne. Als Druckwalze wird eine 0,025 mm dicke halbharte Alur.iniumfolie verwendet, auf die der Papierträger mit dem in der Höhe abgestuften erhabenen Farbdruck aufgebracht wird, und die beiden Stücke werden dann zwischen der heißen Druckwalze und der heißen Stützwalze der heißen MMM-Kopiermaschine (Handelsname "Casual Copier") durchgeführt. Die beiden Stücke werden dabei in der Hitze zusammengepreßt. Nach dem Abkühlen wird die Aluminiumfolie abgezogen, und man erhält auf dem Papierträger einen Farbdruck auf einer Ebene. Dabei kann jedes Erwärmungs- und Druckverfahren vorwendet werden, und man ist nicht unbedingt auf das Casual-Kopiergerät beschränkt. Die Aluminiumfolie enthält nach dem Verlargen der Walze einen Schmiermittelüberzug und kann demgemäß leicht von dem thermisch klebenden Vinylidenchlorid-Acrylnitril-Gemisch aus dem erfindungsgemäßen, zur Herstellung von erhabenen Drucker @ neten aufgeblähten bzw. flachgewalzten elektrophotographischen Toner abgezogen werden.Shades. A 0.025 mm thick, semi-hard aluminum foil is used as the pressure roller used, on which the paper support with the raised color printing graduated in height is applied, and the two pieces are then placed between the hot pressure roller and the hot backup roller of the hot MMM copier (trade name "Casual Copier") carried out. The two pieces are pressed together in the heat. To the aluminum foil is peeled off after cooling, and the result is on the paper support a color print on one plane. Any heating and printing process can be used and one is not necessarily limited to the casual copier. After the roller has been laid, the aluminum foil contains a lubricant coating and can accordingly easily from the thermally adhesive vinylidene chloride-acrylonitrile mixture from the invention, for the production of raised printer @ neten peeled off puffed or flat-rolled electrophotographic toner.

B e i s p i e l 13 Unter Verwendung des in Beispiel 11 beschriebenen Ansatzes und des in Beispiel 12 beschriebenen Nachpreß-Verfahrens werden Seidenraster hergestellt. Example 13 Using that described in Example 11 Approach and the post-pressing process described in Example 12 are silk grids manufactured.

Demgemäß wird ein Rastermuster auf ein Gazegewebe mit einer Fadcnzahl von 120 x 80 aufgebracht. Im Xerox-813-Kopiergerät erhält man daraus Kopien mit dichten erhabenen gemusterten Flächen mit dem Aussehen von dichten weißen Flocken. Durch Heißpressen gemäß Beispiel 11 wird die erhabene Struktur flacher gewalzt, und man erhält dort> wo das Muster xerographisch abgelagert worden irt, eine lückenlose Brückenbildung der offenen Maschen des Raternetzes und damit ein saugfähiges .eidenraster, auf welches ule Druckfarbe mit freier und glatter Bewegung aufgebracht werden kann.Accordingly, a screen pattern is applied to a gauze fabric with a thread count of 120 x 80 applied. In the Xerox 813 copier you get copies of it with dense raised patterned areas with the appearance of dense white flakes. The raised structure is rolled flatter by hot pressing according to Example 11, and where the pattern has been xerographically deposited, one obtains a gapless bridging of the open meshes of the rat net and thus an absorbent one .eidenraster, on which ule printing ink is applied with free and smooth movement can be.

B. e i s p i e 1 14 Aus den nachstehenden Bestandteilen wird ein Toner hergestellt. B. e i s p i e 1 14 The following components become a Toner manufactured.

Aufschäumbare Mikrokügelchen 100 Volumteile BariumSerrit,474 74 Mikron 100 Volumteile Xerox-813-Toner 10 Volumteile.Expandable microspheres 100 parts by volume barium serite, 474-74 microns 100 parts by volume Xerox 813 toner 10 parts by volume.

Die Pulver der vorstehenden Komponenten werden in einer Trommel 30 Minuten vermischt und dann im Farbtank (Tonertank) des Xerox-813-Geräts verwendet. Man erhält damit Kopien mit Schritftzeichen mit einer Höhe von 0,025 mm. Ein weiteres 30sekündiges Erhitzen auf 148,89°C vergrößert zuerst die Höhe der erhabenen Schriftzeichen, welche dann aufgrund des Zusammenscbrnelzens teilweise zusammenfallen. Die Schriftzeichen können magnetisch oder mittels eines Lichtstrahls oberhalb der Ebene des Papierträgermaterials der in der gleichen Ebenenrichtung gerichtet ist,oder durch elektrischen Kontakt oder durch mechanischen Kontakt mittels federn dem Fasermaterial gelesen werden.The powders of the above components are placed in a drum 30 Minutes and then used in the ink tank (toner tank) of the Xerox 813 machine. Copies with characters with a height of 0.025 mm are thus obtained. Another one Heating for 30 seconds to 148.89 ° C first increases the height of the raised characters, which then partially due to the collapse coincide. The characters can be magnetic or by means of a light beam above the plane of the paper base material in the same plane direction is directed, or by electrical contact or by mechanical contact by means of feathers the fiber material can be read.

B e i s p i e l 15 Die gemäß Beispiel 14 hergestellten erhabenen Schriftzeichen auf dem Papier träger werden magnetisiert und als magnetische Druckplatte verwendet. Eine besondere Druckfarbe wird magnetisch von den magnetisierten Lettern angezogen und dann durch Kontaktieren und Erhitzen auf einen Papierträger überführt. Mittels elektrisch.er Einrichtungen ist z.B. auf elektromagnetische oder elektrostatische Weise die Übertragung der Schriftzeichen ohne NonF tieren möglich. Besondere magnetisch von der magnetischen Druckplatte anziehbare Druckfarben können die nachstehende allgemeine Zusammensetzung aufweisen: schwarzes Eisenoxid Fe3O4-FeO (Pfizer> N.Y. N.Y.) 100 Volumteile teilchenförmiges, thermisch klebendes Bindemittel mit einer Teilchengröße <74 µ 100 Volumteile (z.B. Xerox-813-Toner). EXAMPLE 15 The raised areas produced according to Example 14 Characters on the paper are magnetized and used as a magnetic printing plate used. A special printing ink becomes magnetic from the magnetized letters attracted and then transferred to a paper support by contacting and heating. By means of electrical devices, e.g. electromagnetic or electrostatic Way, the transmission of the characters without nonf animals is possible. Special magnetic Inks attractable by the magnetic printing plate may include the following general composition: black iron oxide Fe3O4-FeO (Pfizer> N.Y. N.Y.) 100 parts by volume of particulate, thermally adhesive binder with a particle size <74 µ 100 parts by volume (e.g. Xerox 813 toner).

Zur Herstellung von erhabenen Drucken werden als teilchenförmiges, thermisch klebendes Bindemittel vorzugsT..reise nicht aufgeschäumte Mikrokügelchen verwendet.For the production of raised prints, particulate, Thermally adhesive binder, preferably non-foamed microspheres used.

B e i s p i. e 1 16 Die Erscheinung der Umwandlung von nicht aufgeschäumten Mikrokügelchen zu dichten weißen Mikroballons durch Erhitzen und Riic~-gängigmachen des Aufblähens der aufgeschäumten weißen Schicht aus vielen Kügelchen durch weiteres Erhitzen mit anschließendem Schmelzen und Transparentmachen der vorgenannten weißen Schicht wird zweckmäßigerweise bei der Herstellung von Registrierpapier mittels xerographischer Verfahren eingesetzt. Die Druckfarbe au Beispiel 11 wird dabei als alleiniger Toner im Tonertank des Xerox-813-Geräts verwendet. Außerdem wird ein schwarzer Papier. B e i s p i. e 1 16 The appearance of the transformation of non-foamed Microspheres become dense white microballoons by heating and ricocheting the expansion of the foamed white layer of many spheres by further expansion Heating followed by melting and making the aforementioned white ones transparent Layer is expediently used in the production of recording paper by means of xerographic processes are used. The printing ink from Example 11 is used as Only toner used in the toner tank of the Xerox-813 machine. In addition, a black paper.

träger verwendet. Ein Rastermuster wird als zu kopierendes Original in das Kopiergerät gelegt. Als Kopie erhält man ein Raster mit dem Aussehen eines dichten weißen flockigen Überzugs aus einer Vielzahl von Kügelchen auf dem schwarzen Regiestrierpapier, das den schwarzen Untergrund mit Ausnahme der Linien für die Ordinate und die Abszisse fast bedeckt. Der weiße, erhabene xerographische Druck wird mittels eines heißen Stichels oder einer nicht kontaktierenden Wärmequelle transparent und die Aufblähung rückgängig gemacht, wobei nur die Linien transparent gemacht werden, welche der heiße Stichel entlang fährt. Auf diese Weise wird Registrierpapier für die Schreiber von elektrocardiographischen Geräten auf einfache und billige Weise hergestellt. Die Belichtung des schwarzen Hintergrundes stellt die Wiedergabe des mittels des heißen Stichels hergestellten Musters dar. carrier used. A halftone pattern is used as an original to be copied placed in the copier. As a copy you get a grid with the appearance of a dense white flaky coating of a multitude of globules on the black Director's paper that covers the black background with the exception of the lines for the Ordinate and abscissa almost covered. The white raised xerographic print is done using a hot graver or a non-contacting heat source transparent and the bloating undone, with only the lines transparent which the hot burin travels along. This way it becomes chart paper for the writers of electrocardiographic devices in a simple and cheap way Way made. The exposure of the black background represents the reproduction of the pattern made with the hot graver.

Das erfindungsgemäße Verfahren zur Herstellung von erhabenen oder Prägedrucken unter Verwendung eines Xerox-813-Geräts läßt sich auch mittels jedes beliebigen anderen Xerox-Geräts und tcde.The inventive method for producing raised or Embossing using a Xerox 813 machine can also be done using any any other Xerox device and tcde.

beliebigen anderen xerographisch bzw. elektrostatisch arbei Kopiergeräts durchführen.any other xerographic or electrostatic work Copier carry out.

Wenn als Photoleit;er ein Papierträger mit einem aufgebr eilten Überzug verwendet wird, läßt sich das erfindungsgemäße Verfahren durch elektrophoretische Ablagerung aus einer Dispersion von aufschäumbaren Mikrokügelchen in nicht polaren flüssigen Lösungsmitteln durchführen. Die Ablagerung des aufblähbaren Toners kann auch aus einem Aerosol unter Verwendung1 einer trockenen Wolke oder einer nebligen Flüssigkeit durchgeführt werden. Die erfindungsgemäß hergestellten,prägeartiges Ausschen aufweisenden Produkte können durch Pressen oder Zusammenschmelzen, entweder bbej die ganze Fläche, wie in dem Seidenraster gemäß Beispiel 13 oder nur über ausgewählte Flächen,entprägt werden. Auf diese Weise kann eine Xerokopie mit erhabenen Schriftzeichen, wie z.B. ein Briefkopf, auf dem Papierträger unter Ausschluß des Briefkopfes gepreßt werden, wodurch man eine Kopie mit verschiedener Struktur erhält, wobei der Briefkopf erhabene Schrift zeichen aufweist, während der sonstige Inhalt flach gedruckt ist. Auf diese Weise können Werbematerialien, Direct-Mail-Stücke und Etiketten mitteln des kostspielig wirkenden Aussehens des erhabenen Druckes zusammen mit der selektiven Entprägung an anderen Stellen unter Herstellung eines Erscheinungsbildes an den bedruckten Stellen, welcher, verschiedene Höhen aufweist, in werbewirksamer Weise gestaltet werden. Außerdem ist man bei der Herstellung solcher Drucke hinsichtlich des Toners nicht auf den "Xerox-813-Toner" beschränkt, @ie@-mehr wird unter "Xerox-813-Toner" in der vorliegenden Be@ @-bung ein beliebiges, pigmentiertes, thermisch klebendes, teilchenförmiges Material verstanden, das einen Schnelzpunkt im erwärmenten Bereich, die erwünschte spezifische Wärme und die erwünschte spezifische Klebkraft aufweist und das von jedem Fachmann auf einfache Weise hergestellt werden kann. Sofern ein erhabener Druck auf einem beliebigen Trägermaterial hergestellt werden soll, kann dies sowohl in graphischen als auch in elektronischen,optischen, elektrischen oder mechanischen Verfahren mittels des vorstehend eingehend beschriebenen erfindungsgemäßen Verfahrens durchgeführt werden.If used as a photoconductor, it is a paper carrier with a torn-on coating is used, the inventive method by electrophoretic Deposition from a dispersion of foamable microspheres in non-polar ones liquid solvents. The build up of the puffy toner can also from an aerosol using1 a dry cloud or misty one Liquid to be carried out. The embossed Eliminating products can be accomplished by pressing or fusing, either bbej the entire area, as in the silk grid according to example 13 or only selected above Surfaces to be debossed. In this way, a xerocopy with raised characters, such as a letterhead, pressed on the paper carrier excluding the letterhead resulting in a copy with a different structure, with the letterhead has raised characters, while the other content is printed flat. This allows promotional materials, direct mail pieces, and labels to mediate the expensive appearance of the raised print together with the selective Embossing in other places while creating an appearance on the printed areas, which has different heights, in an advertising-effective manner be designed. In addition, one is wary of making such prints of the toner is not limited to the "Xerox-813-Toner", @ ie @ -more is under "Xerox-813-Toner" in the present Be @ @ exercise any pigmented, thermally adhesive, understood particulate material that has a melting point in the heated area, the desired specific heat and the desired specific Has bond strength and which can be produced in a simple manner by any person skilled in the art can. Provided a raised print is made on any carrier material should be, this can be in graphic as well as in electronic, optical, electrical or mechanical methods by means of that described in detail above Process according to the invention are carried out.

Claims

Claims process for electrophotographic production raised images, in that (a) a latent, forming an electrostatic image on a xerographic body; (b) the xerographic body with a dry, free-flowing electroscopic den, itself self-inflating, / toner mixture with development of the latent electrostatic Image contacted wira; (c) the dispersed toner from the xerographic body a transfer surface is transferred, and (d) the transferred toner is sufficient is heated to create a permanent raised image on it to inflate the transfer surface.

2. Process for the electrophotographic production of raised images for use as Braille characters, characterized in that (a) produced an electrostatic latent image on a xerographic body is, (b) the xerographic body with a dry, free flow electroscopic the self-inflating / toner mixture with the development of the latent electrostatic Image is contacted, (c) the dispersed clays from the xerographic body a transfer surface is transferred, and (d) the transferred toner is sufficient is heated to create a permanent raised image with it to inflate the significance of a Braille character on the transmission surface.

3. Process for the electrophotographic production of raised images, characterized in that (a) a latent electrostatic image on a xerographicu Body is produced, (b) the xerographic body with a dry, free Flow electroscopic self-inflating / toner mixture under development of an electrostatic latent image, (c) the dispersed toner is transferred from the xerographic body to a transfer surface, and (d) the transferred toner is heated sufficiently to puff it up and that at the same time the transfer surface and the toner are pressed / and thereby a permanent one condensed image is produced on the transfer surface.

4. Process for the electrophotographic production of colored images% characterized in that (a) a latent electrostatic image on a xerographic Body is produced, (b) the xerographic body with a dry, free flowing, self-inflating, electroscopic toner mixture with development of the electrostatic latent image is contacted, (c) the dispersed toner is transferred from the xerographic body to a transfer surface, and (d) the transferred toner is heated sufficiently to puff 4 that the transfer surface and the toner is pressed / thereby creating a permanent, densified color image the transfer surface is established.

5. Process for electrophotographic production of raised images, characterized in that (a) a latent electrostatic image on a xerographic Body is produced, (b) the xerographic body with a dry, free flowing, self-inflating, electroscopic toner mixture with development contacting the electrostatic latent image, and (c) the dispersed toner is transferred from the xerographic body to a tissue transfer surface, and (d) the transferred toner is heated sufficiently to inflate it, wherein the transfer surface and the adhering toner are pressed at the same time, thereby producing a permanent flat raised image on the transfer surface will.

6. Process for the electrophotographic production of a silk screen printing plate, characterized in that (a) an electrostatic latent image on a xerographic Body is produced, (b) the xerographic body with a dry, free flowing, self-inflating, electroscopic toner mixture with development of the electrostatic latent image is contacted, (c) the dispersed toner is transferred from the xerographic body to a tissue transfer surface, and (d) the transferred toner is heated sufficiently to inflate it, wherein at the same time the over tragungsober surface and the toner are pressed, whereby a permanent condensed image is produced on the transfer surface.

7. Xerographic toner mixture for carrying out the procedure according to Claim 1 to 6, containing a stable, dry, free-flowing, self inflating, electroscopic powder mixture, which essentially consists of a thermal adhesive, a pigment and a dry blowing agent.

8. Xerographic toner mixture according to claim 7, containing a stable, dry, free-flowing, self-inflating, electroscopic powder mixture, that essentially consists of a thermal adhesive, a pigment and a dry one Blowing agents made from microspheres which contain an entrapped releasable gas, consists.

9. Xerographic toner mixture, containing a stable, dry, free flowing, self-inflating, electroscopic powder mixture that essentially consisting of a thermal adhesive, a pigment and a dry blowing agent from a particulate material that releases a gas upon thermal decomposition, consists.

10. Xerographic toner according to claim 7, characterized in that that it is used as a thermal adhesive at least one material from the group of copolymers of styrene and methacrylate esters, isoprene, polyethylene, phenol-formaldehyde copolymers, Contains butadiene polymers, melamine resins, bitumen and vinyl resins.

11. Xerographic toner according to claim 10, characterized in marked-4-net, that it contains plastic microspheres as a blowing agent, in which at room temperature a gas is included that is its volume at elevated temperatures expands.

12. Xerographic toner according to claim 10, characterized in that that it contains plastic microspheres as a blowing agent, in which at room temperature a hydrocarbon gas is included which increases its volume at elevated temperatures expands.

1). Xerographic toner according to claim 10, characterized in that that it contains synthetic plastic microspheres as a blowing agent, in the Room temperature a hydrocarbon gas is enclosed, which its volume at at elevated temperatures.

14. Xerographic toner according to claim 11, characterized in that that he used as a blowing agent Mikrokkxgelchen from vinylidene chloride-acrylonitrile copolymers approximately 0.5 to 20 microns in diameter, and that the entrapped Gas consists mainly of isobutane.

15. Xerographic toner according to claim 14, characterized in that the microspheres made of vinylidene chloride-acrylonitrile mixed polymers with a mean diameter of about 8 microns as included Gas mainly contain isobutane.

16. Xerographic toner according to claim 9, characterized that it has at least one compound from the class N, N'-dimethyl-N, N'-dinitrosophthalamide as particulate material, Contains azoisobutyrodinitrile and azodicarbonamide.

17. Xerographic tenor according to claim 15, characterized in that that it contains the blowing agent in an amount of about 0 to about 99.5 percent by volume, based on the volume of the total toner, discharged.

18. Xerographic toner according to claim 15, characterized in that that the microspheres make up about 20 volume percent of the total toner mix.

19. Xerographic toner according to claim 8, characterized in that that the microspheres have a hollow configuration.

20. Xerographic toner according to claim 19, characterized in that that the microspheres contain air as an entrapped gas.

21. Xerographic toner according to claim 8, characterized in that that the microspheres contain nitrogen as an entrapped gas.

22. Xerographic toner according to claim 19, characterized in that that the microspheres contain nitrogen as an entrapped gas.

27. Xerographic toner mixture, containing a stable, dry, free flowing, self-inflating, electroscopic powder mixture that consisting essentially of a thermal adhesive, a pigment and a dry blowing agent the end Plastic microspheres, in which a gas is enclosed at room temperature that expands in volume at elevated temperatures.

Toner mixture according to claim 23, characterized in that it is as enclosed gas contains a hydrocarbon gas.

25. Toner mixture according to claim 24, characterized in that it Synthetic plastic microspheres as blowing agent contains 26. Toner mixture according to claim 23, characterized in that it consists of microsphere heights as the blowing agent Vinylidene chloride-acrylonitrile copolymers with a diameter of approximately 0.5 to 20 microns and contains primarily isobutane as a trapped gas.

27. Toner mixture according to claim 26, characterized in that it as blowing agents, microspheres are made from vinylidene chloride-acrylonitrile copolymers with an average diameter of about 8 microns and as an entrapped gas contains mainly isobutane.

28. Toner mixture according to claim 27, characterized in that it the blowing agent in an amount of from about 0.1 to about 99.5 percent by volume on the volume of the entire gene: isch, contains.

29. Toner mixture according to claim 27, characterized in that it the microspheres in an amount of about 20 volume percent based on the Volume of the entire mixture.