DE2355285A1

DE2355285A1 - Rubber hose with reinforcing inlays in cover layer - has embedded short reinforcing natural, synthetic, glass or metal fibres

Info

Publication number: DE2355285A1
Application number: DE19732355285
Authority: DE
Inventors: Siegmund Krone
Original assignee: Phoenix Gummiwerke AG
Current assignee: Phoenix AG
Priority date: 1973-11-06
Filing date: 1973-11-06
Publication date: 1975-05-07

Abstract

Hose of rubber or rubber-like material has a core and reinforcing inlays running in coils and longitudinally in the cover layer and consisting of embedded short natural or synthetics fibres, or glass or metal fibres. Pref. the fibres are 5-15 mm long and 0.1-0.5 mm thick, and amt. to 10-60 wt. % of the rubber or rubber mixt. Staple fibres of tyre cord waste can be used. The hose has a high resistance against rough handling; the amt. of fibre can be adjusted to suit the stresses to be applied. The strip produced in the calender is cut at 90 degrees to the length, and the strip thus obtained contains the fibres skew to the length.

Description

PHOENIX GUMMIWERKE EMPFÄNGER HAMBURG 90 ' BLATTPHOENIX GUMMIWERKE RECEIVER HAMBURG 90 'SHEET AKTIENGESELLSCHAFTSHARED COMPANY

Deur?ehes Pöv.eiji.amt 1.11.1973 i Deur? Ehes Pöv.eiji.amt 1.11.1973 i

Px München 2Px Munich 2

Schlauch aus Gummi oder gummiähnlichem MaterialHose made of rubber or similar to rubber material

Die Erfindung bezieht sich auf einen Schlauch aus Gummi oder gummiähnlichem Material mit Seele und wendeiförmigen und in Schlauchlängsrichtung verlaufenden Verstärkungseinlagen in der Deckschicht.The invention relates to a hose from Rubber or rubber-like material with a core and helical reinforcement inserts in the top layer that run in the longitudinal direction of the hose.

Schläuche dieser Bauart sind in vielen verschiedenen Variationen bekannt. Die Verstärkungseinlagen bestehen dabei aus unterschiedlichen Geweben und unterschiedlichem Material wie Textil oder Metall. Für die Seele können besondere widerstandfähige Elastomere Anwendung finden. Die VerStärkungseinlagen sind in Gummi oder gummiähnlichen Kunststoffen aller Art eingebettet. Ihre Auswahl richtet sich nach dem An- . wendungsfall.Hoses of this type are available in many different ways Known variations. The reinforcement inserts consist of different fabrics and different Material like textile or metal. Special resistant elastomers can be used for the soul Find application. The reinforcement inserts are in Rubber or rubber-like plastics of all kinds embedded. Your selection depends on the address. application.

Die Schläuche lassen sich nach verschiedenen Methoden herstellen. Diese erfordern in allen Fällen einen beträchtlichen Aufwand für die Konfektionierung.The tubes can be manufactured using various methods. In all cases, these require a considerable amount Expenditure for the assembly.

Aufgabe der Erfindung ist es einen Schlauchaufbau zu schaffen, der eine vereinfachte Herstellung ermöglicht, um deren Kosten zu senken.The object of the invention is a hose structure to create, which allows a simplified manufacture in order to reduce their costs.

Die Lösung dieser Aufgabe besteht darin, daß die Verstärkungseinlagen, aus einer Vielzahl von in Verstärkungsrichtung angeordneten, einzelnen eingebetteten, kurzen Fasern aus natürlichen oder syntetischen Fasern oder Glas- oder Metallfasern besteht. Solche Verstärkungseinlagen lassen sich durch Vermischen von Guramimaterial und Fasermaterial herstellen, indem das fertige Gemisch kalandriert oder gespritzt wird.The solution to this problem is that the reinforcement inserts, from a variety of gain direction arranged, individual embedded, short fibers made of natural or synthetic fibers or Consists of glass or metal fibers. Such reinforcement inserts can be made by mixing Gurami material and produce fiber material by adding the finished mixture is calendered or injected.

BOS8 19/0 2 28BOS8 19/0 2 28

Als Fasermaterial können Stapelfasern oder Reifen-' cordgevrebeabfälle verwendet werden. Durch diesen Verarbeitungsvorgang richten sich die Fasern aus und erbringen daher eine Verstärkung in einer vorgesehenen Richtung. Solche Verstärkungseinlagen mit ausgerichteten Fasern können mit geringem Aufwand hergestellt werden. Klöppel- und Wickelmaschinen für das Aufbringen der Festigkeitsträger entfallen. Teures Garn- und Cordmaterial werden nicht benötigtStaple fibers or tire cord-off waste can be used as the fiber material. Through this Processing process align the fibers and therefore provide a reinforcement in an intended Direction. Such reinforcement inserts with aligned fibers can be made with little effort getting produced. There is no need for lace-making and winding machines for applying the reinforcements. Expensive yarn and cord material are not required

Neben der vereinfachten Herstellung weist ein derartiger Schlauch ferner einen erhöhten Widerstand gegen rauhe Behandlung auf. Der Schlauch dieses Aufbaues hat darüberhinaus den Vorteil, daß er in wesentlich vereinfachter Form der Beanspruchung angepaßt werden kann. Dieses ist beispielsweise durch die in der Kautschukmasse enthaltenen Fasermengen möglich. Ferner ist die Einflußnahme durch die Wandstarke der den Schlauch ummantelden Lagen und durch die Längen und'Dicken des Fasermaterials möglich. Im wesentlichen wird man den Anforderungen gerecht, wenn die Faserlängen zwischen 5 und 15 mm und die Faserdicken zwischen 0,1 und 0,5 mn liegen. Die Fasermenge im Verhältnis zur Kautschukmischung liegt vorzugsweise zwischen IO und 60 Gewichtsprozent.In addition to the simplified production, such a hose also has an increased resistance against rough treatment. The hose of this structure also has the advantage that it is in Much simplified form adapted to the stress can be. This is due, for example, to the amounts of fiber contained in the rubber compound possible. Furthermore, the influence is exerted by the wall thickness of the layers encasing the hose and by the lengths and thicknesses of the fiber material are possible. Essentially, one meets the requirements when the fiber lengths are between 5 and 15 mm and the fiber thicknesses between 0.1 and 0.5 mm. the The amount of fiber in relation to the rubber mixture is preferably between 10 and 60 percent by weight.

Ein weiterer Vorteil des Erfindungsgedankens kann dadurch erhalten werden, daß der im Kalander hergestellte Streifen quer zur Längsrichtung geschnitten wird. Der dann erhaltene Streifen enthält die Fasern schräg zur Längsrichtung.Another advantage of the inventive concept can are obtained in that the strip produced in the calender is cut transversely to the longitudinal direction will. The strip then obtained contains the fibers at an angle to the longitudinal direction.

509819/0228509819/0228

;·&.■- 7355285; · &. ■ - 7355285

Beim Aufwickeln dieses Bandes auf die Schlauchseele kann dann eine Faserl&ge im Schlauch erhalten werden, bei der diese in einem Winkel von 90 zur Schlauchlängsrichtung liegen. Um die im Schlauch bei Druckbeaufschlagung entstehenden Kräfte zu kompensieren, ist·anzustreben, die Faserrichtung einerseits senkrecht zur Schlauchrichtung anzuordnen, um die radialen Kräfte zu kompensieren, andererseits sind die Fasern in Schlauchrichtung anzuordnen, um die axialen Kräfte zu kompensieren. Im Gegensatz zum konventionellen Schlauchaufbau wird das maximale Druckverhalten nicht bei einer Faserrichtung von 5^° ^O Min. erreicht, da die durch Fasern verstärkten Gummieinlagen nur in Faserrichtung Kräfte übertragen. When winding this tape onto the hose core can then get a fiber length in the tube at which they are at an angle of 90 to the longitudinal direction of the hose. To the im Hose created when pressurizing The aim is to compensate for forces To arrange the fiber direction on the one hand perpendicular to the hose direction to the radial forces compensate, on the other hand, the fibers are to be arranged in the direction of the hose to the axial Compensate forces. In contrast to the conventional hose structure, the maximum pressure behavior not achieved with a fiber direction of 5 ^ ° ^ O min., as the rubber inserts reinforced by fibers only transmit forces in the direction of the fibers.

Für bestimmte Zwecke kann ein derartiger Schlauch von erheblicher und besonderer Bedeutung sein. Bei angemessener Wandstärke der Verstärkungseinlagen können auch mehrere Lagen in verschiedenen Bahnen um den Schlauch herum aufgelegt werden. Bei der Wendelung muß ein Gleichgewicht zwischen dem links und rechts umlaufenden Fasermaterial bestehen.Such a hose can be used for certain purposes be of considerable and particular importance. With an appropriate wall thickness of the reinforcement inserts several layers can also be laid around the hose in different tracks. At the turn there must be a balance between the left and right circulating fiber material.

Die Erfindung wird in Verbindung mit den Abbildungen 1 und 2 beispielsweise beschrieben.The invention is described in conjunction with the figures 1 and 2, for example.

Nach Abb. 1 wird auf die Schlauchseele 1 aus chemikalienbeständigen Gummi ein Streifen 2 aufgebracht, der in Längsrichtung eingebettete Fasern 3 enthält. Darüber liegt eine Deckschicht 4, die Materi al aus Einzelfasern in Längsrichtung des Schlauches enthält.According to Fig. 1, the hose core 1 is made of chemical-resistant Rubber applied a strip 2 which contains fibers 3 embedded in the longitudinal direction. About that is a cover layer 4, the materi al of individual fibers contains in the longitudinal direction of the hose.

509819/0228509819/0228

Nach Abb. 2 wird ein Fasern enthaltender Kautschukstrelfen 5 auf die Schlauchseele 6 aufgebracht, der durch Diagonalschnitt aus einer am Kalander hergestellten Bahn erhalten worden ist. Die Fasern laufen daher schräg zur Längsrichtung dieses Verstärkungsstreifens 3» Im aufgewickelten Zustand sind diese Fasern senkrecht zur Schlauchachse gerichtet, so daß sie iP, Kreisform umlaufen, wenn beide Winkel in Übereinstimmung gebracht werden. In der Deckschicht 7 verlaufen die Fasern 8 in Richtung des Schlauches. Ein Schlauch dieses Aufbaues zeichnet sich durch besonderes ruhiges Verhalten bei Druckbelastungen aus.According to Fig. 2, a fiber-containing rubber strelf 5 is applied to the hose core 6, which has been obtained by diagonal cut from a web produced on the calender. The fibers therefore run obliquely to the longitudinal direction of this reinforcement strip 3 » In the wound state, these fibers are directed perpendicular to the tube axis, so that they revolve around a circle shape when both angles are brought into agreement. In the cover layer 7, the fibers 8 run in the direction of the tube. A hose of this construction is characterized by its particularly quiet behavior under pressure loads.

S09819/0228S09819 / 0228

Claims

Expectations

Θ, hose made of rubber or rubber-like material with a core and helical reinforcement inserts running in the longitudinal direction of the hose in the cover layer, characterized in that the reinforcement inserts consist of a large number of individually embedded short fibers made of natural or synthetic fibers or glass or metal fibers and arranged in the reinforcement direction. ; "

2. Hose according to claim 1, characterized in that the fiber length 5 - 15 mm and the Fiber thickness is 0.1-0.5 mm.

3. Hose according to claims 1 and 2, characterized in that the amount of fibers on a rubber or plastic mixture is 10-60 % by weight.

509819/0 228509819/0 228