DE2354847B2 - SLIDING BEARING DIMENSIONS - Google Patents
SLIDING BEARING DIMENSIONSInfo
- Publication number
- DE2354847B2 DE2354847B2 DE19732354847 DE2354847A DE2354847B2 DE 2354847 B2 DE2354847 B2 DE 2354847B2 DE 19732354847 DE19732354847 DE 19732354847 DE 2354847 A DE2354847 A DE 2354847A DE 2354847 B2 DE2354847 B2 DE 2354847B2
- Authority
- DE
- Germany
- Prior art keywords
- weight
- polytetrafluoroethylene
- percent
- sliding bearing
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Gegenstand der Erfindung sind Gleitlagermassen auf der Grundlage von Polytetrafluorethylen.The invention relates to plain bearing compounds based on polytetrafluoroethylene.
Die Verwendung von Polytetrafluorethylen zur Herstellung von Gleitlagern für sich oder in Kombination mit anderen polymeren Stoffen, die ungefüllt oder mit verschiedenartigen Zusätzen (Graphit, Molybdändisulfid, Talk, Metallpulvern, Bornitrid, Pflanzenfasern, *> Glasfasern und anderen Füllstoffen) gefüllt sind, ist bekannt.The use of polytetrafluoroethylene for the production of plain bearings alone or in combination with other polymeric substances that are unfilled or with various additives (graphite, molybdenum disulfide, Talc, metal powders, boron nitride, vegetable fibers, *> Glass fibers and other fillers) are filled, is known.
Jedoch verlieren die genannten Gleitlagermassen unter schweren Betriebsbedingungen, bei erhöhten Beanspruchungen, Temperaturen und Geschwindigkeilen ihre Betriebsfähigkeit, weil infolge von bedeutenden Temperaturerhöhungen an der Reibfläche das Polytetrafluorethylen an einzelnen Punkten abgebaut wird, sich zu zersetzen beginnt, in diesem Zustand an der Oberfläche des Gegenkörpers kleben bleibt und diesen umhüllt, wobei es zu starkem Verschleiß und zum Verschweißen des Gleitpaars kommt.However, the above-mentioned plain bearing masses lose under severe operating conditions, at increased Stresses, temperatures and speed wedges their operability, because as a result of significant Temperature increases on the friction surface the polytetrafluoroethylene is broken down at individual points, begins to decompose, in this state it sticks to the surface of the counter body and this remains enveloped, which leads to heavy wear and the welding of the sliding pair.
Zweck der Erfindung ist es, die genannten Nachteile lu vermeiden.The purpose of the invention is to avoid the disadvantages mentioned lu.
Der Erfindung wurde die Aufgabe zugrunde gelegt, einen solchen Zusatz für ein Gleitlagermaterial auf. der Basis von Polytetrafluorethylen zu wählen, der das Klebenbleiben des Polytetrafluoräthylens an der Reibfläche des Gegenkörpers verhindert.The invention was based on the object of providing such an additive for a plain bearing material. the Choose the basis of polytetrafluoroethylene, which prevents the polytetrafluoroethylene from sticking to the friction surface of the counter body prevented.
Diese Aufgabe wird dadurch gelöst, daß das Gleitlagermaterial Kupfer(I)-sulfid in einer Menge von bis zu 52 Gewichtsprozent, bezogen auf das Gewicht des Polytetrafluoräthylens, enthält.This object is achieved in that the plain bearing material copper (I) sulfide in an amount of contains up to 52 percent by weight, based on the weight of the polytetrafluoroethylene.
Das Kupfersulfid übt in der Masse drei Wirkungen aus: 'The copper sulphide has three effects in bulk: '
1. Als Füllstoff erhöht es die mechanische Festigkeit der Masse und ihre Verschleißfestigkeit.1. As a filler, it increases the mechanical strength of the mass and its wear resistance.
2. Es wirkt als Schmiermittel, wodurch ein Klebenbleiben der Masse an der Oberfläche des Gegenkörpers verhindert wird. 2. It acts as a lubricant, which prevents the compound from sticking to the surface of the counter body.
3. Das Kupfersulfid tritt unter schweren Betriebsbedingungen, bei denen es durch hohe Temperaturen zum Abbau der Masse an der Reibfläche kommt und Abbauprodukte des Polytetrafluoräthylens auftreten, in chemische Reaktion mit diesen unter Bildung von Kupferfluorid, welches die Kontaktreibflächen schmiert, die Reibungskräfte vermindert und eine weitere Zersetzung des Polymerisats infolge Abfangens der Zersetzungsprodukte verhindert. 3. The copper sulfide occurs under severe operating conditions in which it is caused by high temperatures there is a breakdown of the mass on the friction surface and breakdown products of polytetrafluoroethylene occur in chemical reaction with these with the formation of copper fluoride, which the contact friction surfaces lubricates, reduces the frictional forces and further decomposition of the polymer prevented as a result of the interception of the decomposition products.
Gleitlagermassen der Erfindung, die Kupfersulfid enthalten, sind unter stärkeren Belastungen betriebsfähig als ähnliche Materialien, die kein Kupfersulfid enthalten. Sie erweitern das Anwendungsgebiet des Polytetrafluoräthylens und machen es möglich, dessen besonders wertvolle Eigenschaften wie geringe Reibungszahl, hohe chemische Beständigkeit, Korrosionsbeständigkeit, hohe Erweichungstemperatur vollständiger auszunutzen. Das Kupfersulfid kann allen Materialien, in denen Polytetrafluorethylen als Gleitkörper dient, beispielsweise reinem Polytetrafluorethylen, gefülltem Polytetrafluorethylen und Antihiktionsmehrkomponemenmaterialien auf der Basis von Polytetrafluorethylen zugegeben werden.Plain bearing compositions of the invention containing copper sulfide are operable under heavier loads than similar materials that do not contain copper sulfide. They expand the area of application of the Polytetrafluoroethylene and make it possible to use its particularly valuable properties such as low coefficient of friction, high chemical resistance, corrosion resistance, high softening temperature more complete to take advantage of. The copper sulfide can be all materials in which polytetrafluoroethylene is used as a sliding body serves, for example, pure polytetrafluoroethylene, filled polytetrafluoroethylene and anti-friction multi-component materials based on polytetrafluoroethylene can be added.
Das Kupfer(l)-sulfid kann als trockenes feines Pulver unter sorgfältigem Rühren oder in Form von Suspensionen sowie im Gemisch mit anderen Füllstoffen zugegeben werden.The copper (l) sulfide can be used as a dry fine powder with careful stirring or in the form of suspensions as well as in a mixture with other fillers be admitted.
Die folgenden Beispiele erläutern die Erfindung:The following examples illustrate the invention:
Polytetrafluorethylen
KupfersulfidPolytetrafluoroethylene
Copper sulfide
66 Gewichtsprozent 34 Gewichtsprozent66 percent by weight 34 percent by weight
In diesem Material spielt das Kupfersulfid nicht nur die Rolle eines ein Festfressen verhindernden Zusatzes, sondern dient auch als Füllstoff, der die Härte des Materials, die Beanspruchungsfähigkeit und den Temperaturenbereich desselben vergrößert und einige andere physikalisch-mechanischen Kennwerte verbessert.The copper sulfide not only plays a role in this material the role of an anti-seizure additive, but also serves as a filler that strengthens the hardness of the Material, the strength and temperature range of the same increases and some others physical-mechanical parameters improved.
1. Baumwollfasern1. Cotton fibers
2. Polytetrafluoräthylen 2. Polytetrafluoroethylene
3. Phenolformaldehyd-
und Polyvinylbutyralharz in einem
Verhältnis von 1 :23. phenol formaldehyde
and polyvinyl butyral resin in one
Ratio of 1: 2
4. Kupfersulfid4. Copper sulfide
44 Gewichtsprozent 40 Gewichtsprozent44 percent by weight 40 percent by weight
15,9 Gewichtsprozent 0,1 Gewichtsprozent15.9 percent by weight 0.1 percent by weight
1. Asbestfasern1. Asbestos fibers
2. Polytetrafluoräthylen 2. Polytetrafluoroethylene
3. Phenolformaldehydharz und Polyvinylbutyralharz in einem
Verhältnis von 1 : 23. Phenol-formaldehyde resin and polyvinyl butyral resin in one
Ratio of 1: 2
4. Molybdändisulfid4. Molybdenum disulfide
5. Kupfersulfid5. Copper sulfide
34 Gewichtsprozent 31 Gewichtsprozent34 percent by weight 31 percent by weight
20 Gewichtsprozent 9 Gewichtsprozent 6 Gewichtsprozent20 percent by weight 9 percent by weight 6 percent by weight
1. Baumwollgewebe1. Cotton fabric
2. Polytetrafluoräthylen 2. Polytetrafluoroethylene
3. Phenolformaldehydharz 3. Phenol-formaldehyde resin
4. Polyvinylbutyralharz 4. Polyvinyl butyral resin
5. Kupfersulfid5. Copper sulfide
49,3 Gewichtsprozent49.3 percent by weight
34,6 Gewichtsprozent34.6 percent by weight
4,3 Gewichtsprozent4.3 percent by weight
8,6 Gewichtsprozent 3,2 Gewichtsprozent8.6 percent by weight 3.2 percent by weight
Claims (1)