DE2329144A1 - THERMOGRAPHIC RECORDING PROCEDURE AND SUITABLE MATERIAL - Google Patents
THERMOGRAPHIC RECORDING PROCEDURE AND SUITABLE MATERIALInfo
- Publication number
- DE2329144A1 DE2329144A1 DE19732329144 DE2329144A DE2329144A1 DE 2329144 A1 DE2329144 A1 DE 2329144A1 DE 19732329144 DE19732329144 DE 19732329144 DE 2329144 A DE2329144 A DE 2329144A DE 2329144 A1 DE2329144 A1 DE 2329144A1
- Authority
- DE
- Germany
- Prior art keywords
- silver salt
- silver
- phenol derivative
- recording
- recording material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
AGFA-GEVAERTAGAGFA-GEVAERTAG
Thermographisches Aufzeichnungsverfahren und dafür geeignetesThermographic recording process and suitable ones
Material material
Die vorliegende Erfindung bezieht sich auf ein Verfahren für die Aufzeichnung und Reproduktion von Information durch Wärme und auf ein für das Verfahren geeignetes Aufzeichnungsmaterial.The present invention relates to a method for the recording and reproduction of information by heat and on a recording material suitable for the process.
Bei der Thermographie wird eine wärmeempfindliche Folie in bildseitigen Kontakt mit einer graphischen Vorlage gebracht, die ein aus infrarot-absorbierendem Material bestehendes Bild trägt. Wenn die Vorlage der Infrarotstrahlung ausgesetzt wird,werden ihre Bildteile selektiv erwärmt und bewirken in der benachbarten wärmeempfindlichen Folie die Entwicklung eines der Vorlage entsprechenden Farbbildes.In thermography, a heat-sensitive film is used on the image side Brought into contact with a graphic template which carries an image consisting of infrared absorbing material. If the template is exposed to infrared radiation, it will be their image parts are selectively heated and cause the development of one of the original in the adjacent heat-sensitive film corresponding color image.
Bei einer anderen Art der Aufzeichnung und Reproduktion von Information mit Wärmezufuhr, wird eine farbbildende Komponente einer Kopierfolie durch Belichtung mit kurzwelliger Strahlung inaktiv und durch Wärme nichtübertragbar gemacht. Die in den unbelichteten oder weniger belichteten Teilen zurückgebliebene farbbildende Verbindung wird durch Wärme auf eine Empfangsfolie übertragen, auf welcher sie eine Farbbildung hervorruft. Dieses letztere System hat den Vorteil, dass die endgültige Kopie nicht wärmeempfindlich ist, da die Reaktionsfähigkeit der fabbildenden Komponente bildmässig durch die kurzwellige Bestrahlung zerstört worden ist. Es ist hauptsächlich dieses System, auf das sich die vorliegende Erfindung bezieht. Another way of recording and reproducing information with heat is a color-forming component a copier film made inactive by exposure to short-wave radiation and made non-transferable by heat. The ones in the unexposed Color-forming compound remaining or less exposed parts is transferred by heat to a receiving sheet, on which it causes color formation. This latter system has the advantage that the final copy is not sensitive to heat because of its responsiveness the image-forming component has been destroyed in terms of image by the short-wave irradiation. It is primarily to this system that the present invention relates.
A-G 1143
GV 620AG 1143
GV 620
309881/0853309881/0853
Es 1st ebenfalls möglich, ein Einblattsystem anzuwenden,Indem man eine Schicht .verwendet, die reaktionsfähige Komponenten enthält, von denen eine durch Belichtung mit kurzwelliger Bestrahlung Inaktiv gemacht wird,Bekannte Systeme dieses Typs werden von Lawton und Lopex (US-Patent 3 076 707) und von Grant (US-Patent 3 094 619) beschrieben, wobei in den farbbildenden Systemen Diazoniumverbindungen bzw.oC-Naphthole eingesetzt werden. In diesen Systemen kann die Kopierfolie mit einem Kurzwellen- z.B. UV-Strahlungsbild der zu kopierenden Vorlage belichtet werden, um wenigstens eine der Komponenten inaktiv zu machen, und dann gleichmässig erwärmt werden, um Farbe in den Bereichen zu entwickeln, in denen die Komponenten reaktionsfähig geblieben sind.Andererseits kann die Kopierfolie zunächst der Infrarotstrahlung ausgesetzt werden,während sie mit der graphischen Vorlage in Kontakt ist,um eine farbbildende Reaktion in den Bereichen zu veranlassen,die sich mit den schwarzen Teilen der Vorlage in Kontakt befinden.Danach kann sie einer kurzwelligen Strahlung ausgesetzt werden,um die noch reaktionsfähigen Teile der Folie inaktiv zu machen.It is also possible to use a single sheet system by using a layer containing reactive components, one of which by exposure to short wave Irradiation is made inactive, known systems of this type are by Lawton and Lopex (U.S. Patent 3,076,707) and by Grant (US Patent 3,094,619), where diazonium compounds or oC-naphthols are used in the color-forming systems. In these systems, the copy film can be used with a shortwave, e.g. UV radiation image of the original to be copied are exposed to at least one of the components inactive, and then heated evenly in order to Developing color in the areas where the components have remained reactive. On the other hand, the copying film can initially be exposed to infrared radiation while it is in contact with the graphic template to induce a color-forming reaction in the areas that deal with the black parts of the original are in contact it can be exposed to short-wave radiation in order to make the still reactive parts of the film inactive.
Zweiblattsysteme werden von Benbrook, US-Patent 2 789 904, und Workman, US-Patent 3 094 417, beschrieben. Hierbei wird ein photoempfindlicher Reduktor, der durch Belichtung mit kurzwelliger Strahlung deaktiviert werden kann, auf eine Folie Übertragen (im Folgenden Kopierfolie genannt), die getrennt von der Foil· 1st, die das Material trägt, mit dem er in eine farbbildende Reaktion eintritt. Im Zweiblattsystem wird also die Folie, die den deaktivierbaren Redviktor enthält, zunächst mit einem kurzwelligen Strahlungsbild der zu kopierenden Vorlage belichtet, um eine Deaktivierung des Reduktors in den belichteten Teilen zu erreichen. Diese Folie wird dann mit einer Folie in Kontakt gebracht,die die anderen farbbildenden Komponenten enthält und wird erwärmt,um eine farbbildende Reaktion in den unbelichteten Bereichen auszulösen.Dieses Zweiblattsystem verlangt,dass der photoempfindliche Reduktor,wenn er erwärmtTwo-sheet systems are described by Benbrook, U.S. Patent 2,789,904, and Workman, U.S. Patent 3,094,417. Here, a photosensitive reductor, which can be deactivated by exposure to short-wave radiation, is applied to a film Transfer (hereinafter referred to as the copier foil) that is separate from the foil that carries the material with which it is in a color-forming reaction occurs. In the two-sheet system, the film that contains the deactivatable Redvector is first exposed to a short-wave radiation image of the original to be copied in order to deactivate the reductor in the exposed parts. This slide is then covered with a Foil is brought into contact which contains the other color-forming components and is heated to cause a color-forming reaction trigger in the unexposed areas. This two-sheet system requires the photosensitive reductor when it is heated
309881/0853309881/0853
-3- 2329UA-3- 2329UA
wird, in ausreichendem Masse von einer Folie zur anderen übertragen wird, um die farbbildende Reaktion zu ermöglichen.is transferred to a sufficient extent from one film to another to enable the color-forming reaction.
Es wurde nun gefunden, dassIt has now been found that
die thermische Farbbildung mittels photoempfindlicher Reduktoren, die im Zweiblattsystem anwendbar sind, und ein reduzierbares Schwermetallsalz wie eine Silberseife durch die Anwesenheit eines Hilfsreduktionsmittels verbessert werden kann, das ein sterisch gehindertes Phenolderivat ist und der folgenden Strukturformel entspricht :thermal color formation using photosensitive reductors, which are applicable in the two-leaf system, and a reducible heavy metal salt such as a silver soap by the presence of a Auxiliary reducing agent can be improved, which is a steric is a hindered phenol derivative and has the following structural formula:
CH,CH,
Dieses 2,6-Di-tert.butyl-4-hydroxymethylphenol wird z.B. gemäss J.Am.Chem.Soc, 22 "0953), 734-, oder nach dem US-Patent 3 030 4-28 hergestellt. Schmelzpunkt : 1410C.This 2,6-di-tert-butyl-4-hydroxymethylphenol is produced, for example, according to J. Am. Chem. Soc, 22 "0953), 734-, or according to US patent 3,030 4-28. Melting point: 141 0 C.
Das sterisch gehinderte Phenolderivat behält seine reduzierenden Eigenschaften sogar nach der Belichtung mit UV-Strahlung oder aktinischem Licht.The sterically hindered phenol derivative retains its reducing properties even after exposure to UV radiation or actinic light.
Es können verhältnismäßig niedrige Konzentrationen des vorliegenden Reduktionsmittels verwendet werden, so dass es eine oilbermetallseife bei normaler Reaktionstemperatur nur bei Anwesenheit eines photoempfindlichen Reduktionsmittels reduziert.There can be relatively low concentrations of the reducing agent present can be used so that there is an oilbermetallseife at normal reaction temperature only in the presence of one photosensitive reducing agent reduced.
Die Silbermetallbilder, die durch den als Hilfsreduktionsmittel verwendeten Reduktor erhalten werden, haben eine merklich verbesserte Farbdichte im Vergleich zu Bildern, die ohne das Reduktionsmittel hergestellt werden.The silver metal pictures, which are used as auxiliary reducing agents used reductor, have a markedly improved Color density compared to images made without the reducing agent.
Das erwähnte, sterisch gehinderte Phenolderivat kann in jedem bekannten, wärmeempfindlichen Kopiermaterial oder Bildempfangsmaterial in einer Menge verwendet werden, die geeignet ist, dieThe above-mentioned sterically hindered phenol derivative can be used in any known heat-sensitive copying material or image receiving material be used in an amount appropriate to the
GV.620 309881/0853GV.620 309881/0853
23291U23291U
gewünschte reduzierende Wirkung zu zeigen, z.B. bei Anwesenheit von anderen Reduktionsmitteln und in Verbindung mit reduzierbaren Verbindungen, z.B. Silbersalzen oder anderen Schwermetallsalzen, die in einem Bindemittel eingeschlossen sind, wie dies z.B- in den US-Patenten 2 910 377 und 3 218166, in den britischen Patenten 954 198, 1 068 882 und 1 110 046 und in den deutschen Offenlegungsschriften 2106577 und 2140462 beschrieben wird.To show the desired reducing effect, e.g. in the presence of other reducing agents and in connection with reducible agents Compounds, e.g., silver salts or other heavy metal salts, included in a binder such as this e.g. in U.S. Patents 2,910,377 and 3,218,166, in British Patents 954 198, 1,068,882 and 1,110,046 and in the German Offenlegungsschriften 2106577 and 2140462.
Das erwähnte sterisch gehinderte Phenol kann beispielsweise in Kombination mit den bekannten organischen Reduktionsmitteln verwendet werden, die ein aktives Wasserstoffatom enthalten, das an 0, N.oder C gebunden ist, z.B. mit o-Alkyl- oder Cycloalkylphenolen, Di- und Trihydroxyaryl-, Aminophenol-, Aminonaphthole, p-Phenylendiamin- und Hydroxylaminderivaten, Gallaten, Alkoxynaphtholen, Acetoacetonitrilen, Pyrazolidin-3-on ebenso wie Pyrazolin-5-on, Indandion-1,3-Derivaten, Hydroxytetronsäuren, Hydroxytetronimiden, Reduktonen, z.B. Anhydrodihydropyrrolidinhexosereduktion, Derivaten der Ascorbinsäure, des Hydroxychromans und des Hydroxycumarans, z.B. gemäss der deutschen Offenlegungsschrift 2031748; ο-Alkylphenole, Hydrochinon, Aminophenolderivate und Methoxynaphtholderivate, Bis-/5-naphthole, Hydroxycumaran und Hydroxychroman werden bevorzugt.The sterically hindered phenol mentioned can be used, for example, in combination with the known organic reducing agents which contain an active hydrogen atom that is bonded to 0, N or C, e.g. with o-alkyl or cycloalkyl phenols, Di- and trihydroxyaryl, aminophenol, aminonaphthols, p-phenylenediamine and hydroxylamine derivatives, gallates, alkoxynaphthols, Acetoacetonitriles, pyrazolidin-3-one as well as pyrazolin-5-one, indanedione-1,3-derivatives, hydroxytetronic acids, Hydroxytetronimides, reductones, e.g. anhydrodihydropyrrolidinehexose reduction, derivatives of ascorbic acid, of hydroxychroman and the hydroxycoumaran, e.g. according to the German Offenlegungsschrift 2031748; ο-alkylphenols, hydroquinone, aminophenol derivatives and methoxynaphthol derivatives, bis- / 5-naphthols, hydroxycoumaran and Hydroxychroman are preferred.
Geeignete photoempfindliche Reduktoren für Silbermetallseifen, die vorteilhafterweise mit den vorliegenden Hilfsreduktionsmitteln kombiniert werden, sind solche , die durch kurzwellige Strahlung inaktiv und nicht-übertragbar bei Wärmeeinwirkung gemacht werden,alsο z.B. die Naphthole, die im US-Patent 3 094 417 von Workman erwähnt werden, Pyrazolin-5-one, die in der deutschen Offenlegungsschrift 2 117 053 beschrieben werden, die Reduktionsmittel des Indan-dion-1,3-Typs, die in der deutschen Offenlegungsschrift 2 I52 6O7 beschrieben werden oder ein Acetoacetonitrilderivat, das in der deutschen Offenlegungsschrift 2 010 837 beschrieben wird, vorzugsweise ein Derivat entsprechend folgender allgemeiner Formel:Suitable photosensitive reductors for silver metal soaps, which advantageously with the present auxiliary reducing agents Combined are those that are made inactive by short-wave radiation and non-transmittable when exposed to heat as o e.g. the naphthols described in U.S. Patent 3,094,417 be mentioned by Workman, pyrazolin-5-one, which in the German Offenlegungsschrift 2 117 053 are described, the Reducing agent of the indan-dione-1,3-type, which is used in the German Offenlegungsschrift 2 I52 6O7 are described or a Acetoacetonitrile derivative, which is described in German Offenlegungsschrift 2 010 837, preferably a derivative accordingly following general formula:
GV.620 309881/0853GV.620 309881/0853
-S--S-
2329HA2329HA
O HO H
in der bedeuten :in which:
R, eine Alkylgruppe, z.B. Methyl, eine substituierte Alkylgruppe, eine Aralkylgruppe, z.B. Benzyl, eine Alkoxycarbonylgruppe, eine Alkoxygruppe, eine aromatische Gruppe, oder eine substituierte, aromatische Gruppe, z.B. eine Methoxyphenylgruppe, R2 eine gegebenenfalls substituierte, aromatische oder heterocyclische Gruppe, z.B. eine Phenyl-, Pyridyl-, Furyl- oder Thienylgruppe,R, an alkyl group, e.g. methyl, a substituted alkyl group, an aralkyl group, e.g. benzyl, an alkoxycarbonyl group, an alkoxy group, an aromatic group, or a substituted, aromatic group, e.g. a methoxyphenyl group, R 2 an optionally substituted, aromatic or heterocyclic group, e.g. a phenyl, pyridyl, furyl or thienyl group,
oder irgendeine andere Verbindung, die ein farbiges Produkt mit einem reduzierbaren Metallsalz bildet, vorzugsweise ein Silbersalz einer aliphatischen Carbonsäure, die mindestens 14 Kohlenstoffatome enthält, z.B. Silberbehenat oder Silberstearat. Geeignete reaktionsfähige Silbersalze werden z.B. im US-Patent 3 094 417 beschrieben.or any other compound which forms a colored product with a reducible metal salt, preferably a silver salt of an aliphatic carboxylic acid containing at least 14 carbon atoms, e.g., silver behenate or silver stearate. Suitable reactive silver salts are described, for example, in U.S. Patent 3,094,417.
Andere geeignete, farbbildende Reaktionspartner ausser Silbermetallsalzen,die in einer Empfangsfolie verwendet werden können, auf welche ein ursprünglicher, photoempfindlicher Reduktor durch gleichmässige Erwärmung nach der bildmässigen Photobelichtung übertragen wird, werden in der deutschen Offenlegungsschrift (DOS) 2 117 053 beschrieben.Other suitable, color-forming reactants besides silver metal salts, the can be used in a receiving film to which an original photosensitive reductor is applied uniform heating is transferred after the imagewise photo exposure, are in the German Offenlegungsschrift (DOS) 2 117 053.
Der photoempfindliche Reduktor der Kopierfolie kann durch Belichtung mit UV-Strahlung desensibilisiert werden, kann aber für längerwelligen aktinische Strahlen, beispielsweise die durch eine Wolframfadenlampe ausgestrahlten, empfindlich gemacht werden, indem man gemäss bekannter photochemischer Techniken einen Farbstoffsensibilisator einführt. Farbstoffsensibilisatoren der Erythrosinfamilie sind sehr geeignet; es können jedoch auch andere verwendet werden, z.B. diejenigen, die in der deutschen Offenlegungsschrift 2 106 577 beschrieben werden.The photosensitive reducing agent of the copying film can be exposed to light can be desensitized with UV radiation, but can be used for longer-wave actinic rays, for example the through emitted by a tungsten filament lamp, can be made sensitive by following known photochemical techniques introduces a dye sensitizer. Dye sensitizers the erythrosine family are very suitable; however, others can also be used, e.g. those written in the German Offenlegungsschrift 2 106 577 can be described.
Das vorliegende sterisch gehinderte Phenolderivat wird vorzugs-GV.62O 309881/0853The present sterically hindered phenol derivative is preferred GV . 6 2O 309881/0853
2329UA2329UA
weise mit einem reduzierbaren Silbersalz in einem geeigneten Bindemittel kombiniert, z.B. Polyvinylbutyral oder Poly-tert.-butylmethacrylat, und auf einen Papierfolienträger oder dergleichen angebracht, so dass eine Empfängsfolie gebildet wird.combined with a reducible silver salt in a suitable binder, e.g. polyvinyl butyral or poly-tert.-butyl methacrylate, and attached to a paper sheet support or the like to form a receiving sheet.
Das sterisch gehinderte Phenolderivat wird vorzugsweise in einer Menge von mindestens 10 Gew.-% im Hinblick auf das reduzierbare Silbersalz verwendet.The hindered phenol derivative is preferably used in an amount of at least 10% by weight in terms of the reducible Silver salt used.
Die zusammen mit der photoempfindlichen Kopierfolie verwendete Empfangsfolie kann zusätzlich zum farbbildenden Reaktionsteilnehmer und Hilfsreduktor ein sogenanntes Tönungsmittel enthalten, z.B. 1-(2H)-Phthalazinon, ein Phthalazinonderivat oder Phthalimid, wie es z.B. in den deutschen Offenlegungsschriften 21 40 462, 21 40 063, 22 206 18 und 22 61 739 beschrieben wird, wobei die Tönungsmittel einen neutraleren Bildfarbton ergeben.The receiving film used together with the photosensitive copying film can in addition to the color-forming reactant and auxiliary reducing agent contain a so-called tinting agent, e.g. 1- (2H) -phthalazinone, a phthalazinone derivative or phthalimide, as described e.g. in German Offenlegungsschrift 21 40 462, 21 40 063, 22 206 18 and 22 61 739, the tinting agents providing a more neutral image tone.
Um das erwünschte sichtbare Bild zu erhalten, werden die Empfangsfolie und die bildmässig belichtete Kopierfolie innerhalb des Temperaturbereichs von 50 bis 2000C erhitzt.In order to obtain the desired visible image, the receiving sheet and the image-wise exposed copy sheet within the temperature range of 50 are heated to 200 0 C.
Die folgenden Beispiele veranschaulichen die vorliegende Erfindung. Die Prozentsätze sind, wenn nicht anders angegeben, Gewichtspro zente. The following examples illustrate the present invention. Unless otherwise stated, the percentages are percentages by weight.
Auf einem Pauspapier wird die folgende Zusammensetzung in einemOn a tracing paper, the following composition is made into one
Verhältnis von 25 g/m. angebracht : Ratio of 25 g / m. appropriate :
4-Methoxy-1-naphthol 1 g4-methoxy-1-naphthol 1 g
Erythrosin 440 mgErythrosine 440 mg
Xthylcellulose 50 gEthyl cellulose 50 g
Methylethylketon zum Auffüllen auf 500 gMethyl ethyl ketone to make up to 500 g
Nach dem Trocknen wird die photoempfindliche Schicht der Kopierfolie in Reflex mit einer graphischen Vorlage mit differential lichtabsorbierenden Bild- und Hintergrundbereichen belichtet.After drying, the photosensitive layer of the copy sheet is exposed in reflection with a graphic template with differential light absorbing image and background areas.
GV.620 309881/0853GV.620 309881/0853
- 7 - 23291U- 7 - 23291U
Die beschichtete Oberfläche der Kopierfolie .wird dazu mit dem gedruckten Text der opaken Vorlage in Kontakt gebracht. Die Belichtung dauert 30 Sekunden und wird durch eine Wolframfaden-Lichtquelle von 1500 W bewirkt, die in einer Entfernung von 5 cm von der Kopierfolie aufgestellt ist.The coated surface of the copy film .wird with brought into contact with the printed text of the opaque template. The exposure lasts 30 seconds and is powered by a tungsten filament light source of 1500 W caused at a distance of 5 cm is set up by the copy film.
Daraufhin wird die bestrahlte Folie 5sec. mit ihrer photoempfindlichen Schicht mit einer Empfangsfolie bei 125°C in Kontakt gebracht, die wie folgt hergestellt wird.Thereupon the irradiated film is 5sec. with their photosensitive Layer brought into contact with a receiving film at 125 ° C., which is prepared as follows.
Die folgenden Zusätze werden 4 Stunden in einer Kugelmühle gemahlen :The following additives are ground in a ball mill for 4 hours:
Stearinsäure 2,25 gStearic acid 2.25 g
ELVACITE 2046 (ein MischpolymerisatELVACITE 2046 (a mixed polymer
aus n-Butylmethacrylat und Isobutyl-made of n-butyl methacrylate and isobutyl
methacrylat, gehandelt von E.I. dumethacrylate sold by E.I. you
Pont de Nemours & Co., Wilmington,Pont de Nemours & Co., Wilmington,
Del., USA) 12,2 gDel., USA) 12.2 g
Phthalazinon 2,9 gPhthalazinone 2.9 g
Zinkoxid 52,60 gZinc oxide 52.60 g
Silbers-earat 11,5 gSilver earat 11.5 g
Äthylacetat 245 gEthyl acetate 245 g
Daraufhin wird die folgende Lösung eines Hilfsreduktionsmittels zugegeben :Thereupon the following solution becomes an auxiliary reducing agent admitted:
2,6-Di-tert.butyl-4-hydroxymethy1-2,6-di-tert-butyl-4-hydroxymethyl
phenol 2,85 gphenol 2.85 g
Aceton 25 gAcetone 25 g
Die erhaltene Mischung, die zuvor mit 600 g Äthylacetat verdünnt worden ist, wird auf einen Papierträger im Verhältnis von 100 gThe mixture obtained, which has previously been diluted with 600 g of ethyl acetate, is applied to a paper support in the proportion of 100 g
2
pro m aufgetragen.2
applied per m.
Die getrocknete Empfangsfolie wird mit einer 3M Dual-Spectral Pink-Folie in Kontakt erwärmt und vorher belichtet, wie von Workman im US-Patent 3 094 417 beschrieben. Das Bild, das man auf der Empfangsfolie erhält, zeigt eine stark verbesserte Farbdichte im Vergleich zu einer Folie, die auf die gleiche be-The dried receiving foil is applied with a 3M Dual-Spectral Pink foil heated in contact and pre-exposed as described by Workman in US Pat. No. 3,094,417. The picture that one obtained on the receiving film shows a greatly improved color density compared to a film that is based on the same
GV.620 309881/0853GV.620 309881/0853
23291U23291U
schriebene Art und Weise gebildet und belichtet wurde, jedoch kein Hilfsreduktionsmittel enthält. Man erreicht eine verbesserte, thermische Stabilität des Empfangsfolienmaterials im Vergleich zu einer Empfangsfolie, die als Hilfsreduktionsmittel 2,6-Di-tert.butyl-4-methylphenol enthält.written way was formed and exposed, however contains no auxiliary reducing agent. An improved, thermal stability of the receiving sheet material is achieved in comparison to a receiving film which contains 2,6-di-tert-butyl-4-methylphenol as an auxiliary reducing agent.
Das gleiche Ergebnis wird erhalten, wenn anstatt Silberstearat Silberbehenat in der Empfangsfolie verwendet worden ist.The same result is obtained when silver behenate has been used in the receiving film instead of silver stearate.
Beispiel 1 wird wiederholt, jedoch mit dem Unterschied, dass "als lichtempfindliche Kopierfolie ein Folienmaterial verwendet wird, das aus dünnem Pergaminpapier besteht, das mit der folgenden, photoempfindlichen Zusammensetzung beschichtet wird : Erythrosin 0,01 gExample 1 is repeated, but with the difference that "a film material is used as the photosensitive copying film made of thin glassine paper coated with the following photosensitive composition: Erythrosine 0.01 g
2-(p-Chlorphenyl)-acetoacetonifcril 0,2 g Athylcellulose (Hercules N-10) 5 g Athylacetat 50 g2- (p-chlorophenyl) -acetoacetonifcril 0.2 g ethyl cellulose (Hercules N-10) 5 g Ethyl acetate 50 g
Die Zusammensetzung wird in einer Bedeckung von 4,9 kg pro Quadratmeter angebracht und getrocknet.The composition comes in a coverage of 4.9 kg each Square meters attached and dried.
GV.620 309881/0853GV.620 309881/0853
Claims (11)
fOH
f