DE2318287B2 - MELT THERMOINDICATORS - Google Patents
MELT THERMOINDICATORSInfo
- Publication number
- DE2318287B2 DE2318287B2 DE19732318287 DE2318287A DE2318287B2 DE 2318287 B2 DE2318287 B2 DE 2318287B2 DE 19732318287 DE19732318287 DE 19732318287 DE 2318287 A DE2318287 A DE 2318287A DE 2318287 B2 DE2318287 B2 DE 2318287B2
- Authority
- DE
- Germany
- Prior art keywords
- weight
- indicators
- thermal
- binder
- ethanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Die Erfindung betrifft Schmelzthennoindikatoren.The invention relates to melt holographic indicators.
Schmelzthermoindikatoren finden eine breite Anwendung in der Hütten-, Maschinenbau-, radiotechnischen und Flugzeugbauindustrie sowie in anderen Industriezweigen.Melt thermal indicators are widely used in the metallurgical, mechanical engineering, and radio-technical fields and aircraft construction industry as well as in other industries.
Es sind Schmelzthennoindikatoren bekannt, die ein Arbeitsmittel, einen Füllstoff sowie ein Bindemittel enthalten.Melting indicators are known which contain a working medium, a filler and a binder contain.
Die Arbeitsweise der bekannten Thermoindikatoren beruht auf einer Änderung der Farbe der Zusammensetzung beim Erreichen der kritischen oder Schmelztemperatur des Arbeitsmittels.The mode of operation of the known thermal indicators is based on a change in the color of the composition when the critical or melting temperature of the working medium is reached.
Es sind Schmelzthermoindikatoren bekannt, in denen als Arbeitsmittel organische und anorganische Verbindungen verschiedener Klassen in form von kristallinen Pulvern mit einer bestimmten Schmelztemperatur, als Bindemittel wasserlösliche organische Klebstoffe und als Füllstoffe verschiedene Farbstoffe verwendet werden (vgl. die US-PS 29 28 791 und 27 99 167).Melting thermal indicators are known in which organic and inorganic working media are used Compounds of different classes in the form of crystalline powders with a certain melting temperature, water-soluble organic adhesives as binders and various dyes as fillers are used (see. The US-PS 29 28 791 and 27 99 167).
Es ist auch ein Thermoindikatorüberzug bekannt, der als Arbeitsmittel 2-(p-Aminobenzolsulfamido)-5-äthylthiadiazol-l,3,4 in einer Menge von 35 bis 45 Gewichtsteilen, als Füllstoff einen Farbstoff (dunkelgrünes Kobalt, Kobaltfarbstoff CoO · 15 ZnO mit bis zu 6 % CoO) in einer Menge von 3 bis 4 Gewichtsteilen und als Bindemittel 2,04 Gewichtsteile eines Copolymeren von Butylmethacrylat mit 2,48 Gewichtsteilen Methacrylsäure sowie als Lösungsmittel Butylacetat in einer Menge von bis zu 100 Gewichtsteilen der Zusammensetzung enthält. Die Schmelztemperatur des Thermoindikators beträgt 182 ± 2°C (SU-Erfinderschein 2 89 310). Die bekannten Thermoindikatoren arbeiten zufriedenstellend bei Normaldruck in Abwesenheit von starken Gasströmen; sie sindA thermal indicator coating is also known, which contains 2- (p-aminobenzene sulfamido) -5-ethylthiadiazole-1,3,4 in an amount of 35 to 45 parts by weight, as a filler a dye (dark green cobalt, cobalt dye CoO · 15 ZnO with up to 6% CoO) in an amount of 3 to 4 parts by weight and as a binder 2.04 parts by weight of a copolymer of butyl methacrylate with 2.48 parts by weight of methacrylic acid and butyl acetate as a solvent in an amount of up to 100 parts by weight of the composition. The melting temperature of the thermal indicator is 182 ± 2 ° C (SU-Inventor's Certificate 2 89 310). The known thermal indicators work satisfactorily at normal pressure in the absence of strong gas flows; they are
ίο jedoch für die Bestimmung der Temperatur an der Oberfläche von Körpern, die sich im Vakuum befinden, nicht geeignet, weil infolge einer Sublimation und anderer Nebenerscheinungen, die das in den bekannten Thermoindikatoren enthaltene Arbeitsmittel beeinflussen, diese Thermoindikatoren keine genauen Angaben über die Temperatur zu prüfender Körper liefern, die verschiedenen Vakuumbedingungen ausgesetzt werden. Außerdem weisen sie eine schwache Adhäsion an der Oberfläche zu prüfender Körper auf,ίο, however, for determining the temperature at the The surface of bodies in a vacuum is unsuitable because it is a result of sublimation and other side effects that the working fluid contained in the known thermal indicators affect, these thermal indicators do not provide precise information about the temperature of the body to be tested that are exposed to various vacuum conditions. They also have a weak one Adhesion to the surface of the body to be tested,
ao die sich in starken Gasströmen befinden, wodurch die Thermoindikatorschicht von der Oberfläche der Körper entfernt wird.ao which are in strong gas flows, removing the thermal indicator layer from the surface of the Body is removed.
Aus der DT-OS 2018 049 sind ferner Schmelzthermoindikatoren bekannt, bei denen als Arbeitsmittel höhere Carbonsäuren und ihre Salze und als Bindemittel Äthanol und 10%iger Polyvinylbutyral-Lack verwendet werden.From DT-OS 2018 049 there are also melt thermal indicators known, in which higher carboxylic acids and their salts are used as the working medium and ethanol and 10% polyvinyl butyral lacquer are used as binders be used.
Der Erfindung liegt die Aufgabe zugrunde, Bindemittel für derartige Schmelzthermoindikatoren anzugeben, die beim Einsatz unter den Bedingungen hoher Gasgeschwindigkeiten und sowohl bei atmosphärischem Druck als auch im Vakuum bis zu 1 · 10~4 Torr eine hohe Meßgenauigkeit in einem breiten Temperaturbereich bei guter Adhäsion an der Oberfläche der unter diesen Bedingungen zu prüfenden Körper gewährleisten.The invention has the object of providing binders for such melt-type thermal indicators that when used under conditions of high gas velocities and both at atmospheric pressure or under vacuum up to 1 × 10 -4 Torr, a high measuring accuracy in a wide temperature range with good adhesion to the Ensure the surface of the bodies to be tested under these conditions.
Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß man als Bindemittel Lösungen von durch Polyvinylbutyral modifiziertem Resolphenolformalde-According to the invention, this object is achieved in that the binder used is solutions of Polyvinyl butyral modified resolphenol formalde-
hydharz in Äthanol verwendet, die vorzugsweise in einem Harz-Polyvinylbutyral-Gewichtsverhältnis von 1 : 1 oder 1 : 5,7 eingesetzt werden.hydharz used in ethanol, preferably in a resin-polyvinylbutyral weight ratio of 1: 1 or 1: 5.7 can be used.
Als Arbeitsmittel des Schmelzthermoindikators verwendet man vorteilhaft Carbonsäureester oder Carbonsäuresalze. Es werden beispielsweise folgende Arbeitsmittel zur Herstellung der Schmelzthermoindikatoren eingesetzt:Used as the working fluid of the melting thermo indicator it is advantageous to use carboxylic acid esters or carboxylic acid salts. For example, the following Equipment used to manufacture the melt temperature indicators:
Lfd. Nr.Serial No.
Bezeichnung des ArbeitsmittelsDesignation of the work equipment
Die als Arbeitsmittel des Thermomdikators ge- durch 5,7 Gewichtsteile Polyvinylbutyral modifiziernanten Carbonsäurederivate sind im Vakuum in tem Resolphenolformaldehydharz in Äthanol mit einem Bereich von 760 bis zu 1 · 10~4 Torr praktisch einem Trockensubstanzgehalt von 5 Gewichtsprozent nicht sublimierbar und lassen sich gut mit dem Binde- darstellt. Das Gemisch wird in eine Müh'e zur Naßmittel vereinigen. Zur Herstellung eines Schmelz- 5 mahiung eingebracht und innerhalb von 50 bis 70 h thermoindikators, der die Oberfläche des zu prüfenden zerkleinert.The total as the working medium of the Thermomdikators by 5.7 parts by weight of polyvinyl butyral modifiziernanten carboxylic acid derivatives are useful in vacuum in TEM Resolphenolformaldehydharz in ethanol with a range of 760 up to 1 x 10 -4 Torr a dry matter content of 5 weight percent do not sublimable and can be readily with the Connective represents. The mixture is combined in one effort to form a wet agent. For the production of a melting 5 mahiung introduced and within 50 to 70 h thermal indicator, which comminutes the surface of the to be tested.
Körpers gut bedeckt, ist es empfehlenswert das Ar- Die hergestellte Suspension wird in entsprechendeBody well covered, it is recommended that the ar- The suspension prepared is in appropriate
beitsmittel in Form eines feindispersen Pulvers in einer Verpackungsbehälter abgefüllt und bei Bedarf mitaids in the form of a finely dispersed powder in a packaging container and, if necessary, with
Menge von 20 bis 25 Gewichtsprozent, bezogen auf einem Pinsel oder einer Spritzpistole auf die mit einerAmount of 20 to 25 percent by weight, based on a brush or spray gun on that with a
das Gesamtgewicht der Zusammensetzung, zu ver- io Kontrastfarbe gefärbte Oberfläche des zu prüfendenthe total weight of the composition, as opposed to the contrasting color of the surface to be tested
wenden. Körpers aufgetragen. Bei der Erwärmung des Körpersturn around. Body applied. When warming the body
Zur Herstellung einer guten Adhäsion des Thermo- schmilzt der Thermoindikator bei einer TemperaturTo produce good adhesion of the thermal, the thermal indicator melts at a temperature
indikators an der Oberfläche des zu prüfenden Körpers von 25 ± Γ C, wobei die mit einer Kontrastfarbeindicator on the surface of the body to be tested of 25 ± Γ C, with those with a contrasting color
werden als Bindemittel Lösungen von durch Polyvinyl- gefärbte Oberfläche des zu prüfenden Körpers insolutions of polyvinyl-colored surface of the body to be tested are used as binders
butyral modifiziertem Resolphenolformaldehydharz 15 Erscheinung tritt.butyrally modified resole phenol formaldehyde resin 15 appearance occurs.
in Äthanol mit einer Konzentration der Trocken- B . 19in ethanol with a concentration of dry B. 19th
substanz von 1 bis 5 Gewichtsprozent verwendet. Beispielsubstance of 1 to 5 percent by weight used. example
Die erfindungsgemäßen Thermoindikatoren stellen 0,22 kg feinzerkleinertes durchgesiebtes Pulver von eine Suspension eines feindispersen Arbeitsmittels im Tripalmitinsäureglycerid werden mit 0,78 kg Binde-Bindemittel dar. Die Färbung der Suspension ist weiß ao mittel vermischt, das eine Lösung aus 1 Gewichtsteil bis hellbeige. Die erfindungsgemäßen Thermoindi- von durch 1 Gewichtsteil Polyvinylbutyral modikatoren gestatten es im Vergleich zu den bekannten fiziertem Resolphenolformaldehydharz in Äthanol Indikatoren, Oberflächeritemperaturen von Körpern mit einem Trockensubstanzgehalt von 3 Gewichtsmit höherer Genauigkeit im Vakuum und in starken prozent darstellt.The thermal indicators according to the invention represent 0.22 kg of finely comminuted, sieved powder of a suspension of a finely dispersed working medium in tripalmitic acid glyceride with 0.78 kg of binding agent The color of the suspension is mixed white ao medium, which is a solution of 1 part by weight to light beige. The Thermoindi- of the invention by 1 part by weight of polyvinyl butyral modikatoren allow it compared to the well known resolphenol-formaldehyde resin in ethanol Indicators, surface temperatures of bodies with a dry matter content of 3 weight with represents higher accuracy in vacuum and in strong percent.
Gasströmen zu messen; sie machen die Verwendung as Das Gemisch wird in eine Mühle zur NaßmahlungMeasure gas flows; they make use of as The mixture is put in a mill for wet grinding
von Füllstoffen als Bestandteile von Thermoindika- eingebracht und innerhalb von 50 bis 70 h zerkleinert,of fillers as components of thermal indicators and crushed within 50 to 70 h,
toren überflüssig, weil das Arbeitsmittel auch ohne Die hergestellte Suspension wird in entsprechendegates superfluous, because the work equipment is also used without The produced suspension is in the appropriate
den Füllstoff die Oberfläche des zu prüfenden Körpers Verpackungsbehälter abgefüllt und bei Bedarf mitthe filler filled the surface of the body to be tested packaging container and if necessary with
gut bedeckt. einem Pinsel oder einer Spritzpistole auf die mit einerwell covered. a paintbrush or a spray gun on the with a
Die Versendung der erfindungsgemäßen Thermo- 30 Kontrastfarbe gefärbte Oberfläche des zu prüfendenThe dispatch of the inventive thermal contrast paint colored surface of the surface to be tested
indikatoren ermöglicht es, den Bereich der Bedin- Körpers aufgetragen.indicators allows the area of the bedin- body to be plotted.
gungen wesentlich zu erweitern, unter denen aerody- Bei der Erwärmung des Körpers schmilzt dertends to expand significantly, among which aerody- When the body is heated, the melts
namische Wärmeversuche durchgeführt werden. Die Thermoindikator bei einer Temperatur von 60 ± I0C,thermal tests can be carried out. The thermal indicator at a temperature of 60 ± I 0 C,
Vorteile der erfindungsgemäßen Thermoindikatoren wobei die mit einer Kontrastfarbe gefärbte OberflächeAdvantages of the thermal indicators according to the invention wherein the surface colored with a contrasting color
im Vergleich zum üblichen Verfahren zur Bestimmung 35 des zj prüfenden Körpers in Erscheinung tritt,appears in comparison to the usual method for determining the zj test body,
von Wärmeverhältnissen mit Thermoelementen be- . .of heat conditions with thermocouples. .
stehen in der Möglichkeit, eine kontinuierliche Ver- Beispiel 3are able to use a continuous process. Example 3
teilung der Wärmeströmung über die Oberfläche des 0,25 kg zerkleinertes und durchgesiebtes Pulverdivision of the heat flow over the surface of the 0.25 kg of crushed and sieved powder
zu prüfenden Körpers zu beobachten, was die Er- von Bleimyristinat werden mit 0,75 kg Bindemittelbody to be tested to observe what the er- of lead myristinate will be with 0.75 kg of binder
mittlung hinsichtlich der Wärmeverhältnisse beson- 40 vermischt, das eine Lösung aus 1 Gewichtsteil vonaveraging with regard to the heat ratios, this is a solution of 1 part by weight of
ders gefährdeter Abschnitte ermöglicht und die Mög- durch 1 Gewichtsteil Polyvinylbutyral modifiziertemders endangered sections and the possibility of modified by 1 part by weight of polyvinyl butyral
lichkeit für genaue Temperaturmessungen an kleinen Resolphenolformaldehydharz in Äthanol mit einempossibility for accurate temperature measurements on small resole phenol formaldehyde resin in ethanol with a
Abschnitten des zu prüfenden Körpers gewährleistet. Trockensubstanzgehalt von 1 Gewichtsprozent dar-Sections of the body to be tested guaranteed. Dry matter content of 1 percent by weight
Außerdem bringt die Anwendung der erfindungsge- stellt.In addition, the application of the invention brings.
mäßen Thermoindikatoren bedeutende Einsparungen 45 Das Gemisch wird in eine Mühle zur NaßmahlungSignificant Savings with Thermal Indicators 45 The mixture is placed in a mill for wet grinding
mit sich, weil dadurch die Anwendung kostspieliger eingebracht und innerhalb von 50 bis 70 h zerkleinert.with itself, because it makes the application more expensive and comminutes within 50 to 70 hours.
Temperaturmeßgeräte vermieden wird. Die hergestellte Suspension wird in entsprechendeTemperature measuring devices is avoided. The suspension produced is in appropriate
Die Thermoindikatoren sind nicht toxisch und Verpackungsbehälter abgefüllt und bei Bedarf mitThe thermal indicators are non-toxic and are filled with packaging containers and if necessary with
lassen sich einfach verwenden. Man kann sie leicht einem Pinsel oder einer Spritzpistole auf die mit einerare easy to use. You can easily put a paintbrush or a spray gun on with a
auf die Oberfläche des zu prüfenden Körpers nach 50 Kontrastfarbe gefärbte Oberfläche des zu prüfendenon the surface of the body to be tested after 50 contrast color colored surface of the test body
üblichen Verfahren auftragen und nach der Ver- Körpers aufgetragen. Bei der Erwärmung des KörpersApply the usual method and apply after the body. When warming the body
wendung leicht abwaschen; außerdem ist ein gleich- schmilzt der Thermoindikator bei einer Temperaturwash off turn easily; in addition, the thermal indicator melts at the same temperature
zeitiges Auftragen von mehreren Thermoindikatoren von 90 ± I0C, wobei die mit einer KontrastfarbeTimely application of several thermal indicators of 90 ± I 0 C, with those with a contrasting color
auf die Oberfläche des zu, prüfenden Körpers in einem gefärbte Oberfläche des zu prüfenden Körpers inon the surface of the body to be tested in a colored surface of the body to be tested in
bestimmten Abstand voneinander möglich, was eine 55 Erscheinung tritt. Nachstehend wird die Herstellungcertain distance from each other possible, which occurs a 55 phenomenon. Below is the manufacture
gleichzeitige Messung verschiedener Temperaturen des Bindemittels erläutert:simultaneous measurement of different temperatures of the binder explained:
ermöglicht. Man vermischt eine 10%ige Lösung von Polyvinyl-enables. Mix a 10% solution of polyvinyl
Nachstehend werden konkrete Beispiele für die butyral in Äthanol mit einer 50%igen Lösung von Herstellung der Schmelzithermoindikatoren angeführt. Resolphenolformaldehydharz in Äthanol in einem Die angeführte Technologie ist für die Herstellung 60 Verhältnis von Resolphenolformaldehydharz zu Polyaller erfindungsgemäßen Thermoindikatoren geeignet. vinylbutyral von 1 : 1 oder 1 : 5,7 Gewichtsteilen undBelow are specific examples of the butyral in ethanol with a 50% solution of Manufacture of the melting thermal indicators listed. Resole phenol formaldehyde resin in ethanol in one The technology cited is for the production of 60 ratio of resol phenol formaldehyde resin to polyaller Thermal indicators according to the invention suitable. vinyl butyral of 1: 1 or 1: 5.7 parts by weight and
erwärmt die Mischung anschließend auf 50 bis 60° Cthen heats the mixture to 50 to 60 ° C
B e i s ρ i e 1 1 bis zur Erzielung einer homogenen und im durchfallenden Licht durchsichtigen Lösung. Die herge-B e i s ρ i e 1 1 to achieve a homogeneous and in the fall through Light see-through solution. The produced
0,2 kg feinzerkleinertes, durchgesiebtes Pulver von 65 stellte Lösung wird zusätzlich mit Äthanol bis zu0.2 kg finely crushed, sieved powder of 65 put solution is additionally with ethanol up to
Stearinsäurebutylester werden mit 0,8 kg Bindemittel einem Trockensubstanzgehalt der Lösung von 1 bisButyl stearate is added with 0.8 kg of binder to a dry matter content of the solution from 1 to
vermischt, das eine Lösung aus 1 Gewichtsteil von 5 Gewichtsprozent verdünnt.mixed, which dilutes a solution of 1 part by weight of 5 weight percent.
Claims (3)