DE2314996A1 - FIRE-RETARDANT UPHOLSTERY CANVAS AND METHOD OF MAKING IT - Google Patents

FIRE-RETARDANT UPHOLSTERY CANVAS AND METHOD OF MAKING IT

Info

Publication number
DE2314996A1
DE2314996A1 DE19732314996 DE2314996A DE2314996A1 DE 2314996 A1 DE2314996 A1 DE 2314996A1 DE 19732314996 DE19732314996 DE 19732314996 DE 2314996 A DE2314996 A DE 2314996A DE 2314996 A1 DE2314996 A1 DE 2314996A1
Authority
DE
Germany
Prior art keywords
preparation according
canvas
phosphate
resin
aldehyde
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19732314996
Other languages
German (de)
Inventor
Albert Wayne Morgan
Roland Gregory Ribaudo
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Monsanto Co
Original Assignee
Monsanto Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Monsanto Co filed Critical Monsanto Co
Publication of DE2314996A1 publication Critical patent/DE2314996A1/en
Pending legal-status Critical Current

Description

DR. BERG DRi-.-ING. STAPFDR. BERG DRi -.- ING. STAPF

PATENTANWÄLTE 8 MÜNCHEN 86, POSTFACH 86 O2 45 9Q1 / QQß PATENTANWÄLTE 8 MÜNCHEN 86, POSTFACH 86 O2 45 9Q1 / QQß

Dr. Berg Dipl.-Ing. Stapf, 8 München 86, P.O. Box 840245Dr. Berg Dipl.-Ing. Stapf, 8 Munich 86, PO Box 840245

Ihr Zeichen Unser Zeichen 8 MÖNCHEN 80 -Your reference Our reference 8 MÖNCHEN 80 -

Your ftf. Ourref. 23 692 MAUERKIRCHERSTR. 45 26. MarZ 1973Your ftf. Ourref. 23 692 MAUERKIRCHERSTR. 45 March 26, 1973

Anwaltsakte-Nr.: 23 692Lawyer file number: 23 692

Monsanto Company St. L ο u i Sj Missouri / USAMonsanto Company St. L ο u i Sj Missouri / USA

"Feuerhemmende Po1sterleinwand und Verfahren zu ihrer Herstellung""Fire retardant upholstered canvas and method too their manufacture "

Die vorliegende Erfindung betrifft Gewebematerialien und insbesondere dünne Leinwandunterlagen, wie Polsterleinwand, die für die Herstellung von Gewebematerialien verwendet werden. Weiterhin ist die Erfindung im besonderen auf eine feuerhemmende dünne Polsterleinwand und ein Verfahren ge-The present invention relates to fabric materials and in particular to thin canvas underlays such as upholstery canvases, which are used for the manufacture of fabric materials. Furthermore, the invention is particularly based on a fire-retardant thin upholstered canvas and a process

(ββΐΐ) η tan (ββΐΐ) η tan Telegramm* BCTGSTAFfPATENT MOnchen Bankern Bayerische Verainsbank Mönchen 453100Telegram * BCTGSTAFfPATENT MOnchen Bankern Bayerische Verainsbank Mönchen 453100

H7»43 THEXi(BSiSeBERGd Bayer. Hypothekenbank MOnch« 3» 2423H7 »43 THEXi (BSiSeBERGd Bayer. Hypothekenbank MOnch« 3 »2423

9^3310 Postscheck: MOnchen «5343 9 ^ 3310 Postal check: Munich «5343

23149992314999

richtet, das eine Polsterleinwand und ähnliche Gewebematerialien feuerhemmend macht.aimed at an upholstered canvas and similar fabric materials makes fire retardant.

Bei der Herstellung von Textil- oder Gewebematerxalien, . wie z.B. Vorhängen und Draperien, Dekorationen und Fußbodenbelägen,' wie Teppiche oder Vorleger, bzw. Brücken, wird gewöhnlich eine Polsterleinwand, d.h. ein gewebtes oder nichtgewebtes Trägerteil als Träger für das Material verwendet, das die Basi's für den herzustellenden Artikel enthält. So wird gewöhnlieh ein Fußbodenbelag-Gewebe oder ein Dekorationsgewebe hergestellt, indem man ein Flormaterial entsprechend einem Noppensetζverfahren durch eine Polsterleinwand tuftet oder indem man Faservlies- oder geschmolzene Materialien auf eine oder auf beide Seiten einer Polsterleinwand zur Bildung eines Laminates aufträgt. Im Falle der Herstellung von Teppichen, insbesondere von Florteppichen, wird das Flormaterial durch eine Polsterleinwand getuftet und wird dann fest und unveränderlich mit der Polsterleinwand durch Aufbringen eines Bindemittelüberzugs aus Latex oder Harz auf die Unter- oder Rückseite der Polsterleinwand befestigt.In the manufacture of textile or Gewebematerxalien. such as curtains and draperies, decorations and floor coverings, such as carpets or rugs, or bridges, an upholstered canvas, ie a woven or non-woven carrier part, is usually used as a carrier for the material that contains the bases for the article to be manufactured. For example, a floor covering fabric or a decorative fabric is usually produced by tufting a pile material through an upholstered canvas according to a nub set method or by applying nonwoven or melted materials to one or both sides of an upholstered canvas to form a laminate. In the case of carpets, in particular pile carpets, the pile material is tufted through an upholstery canvas and is then firmly and invariably attached to the upholstery canvas by applying a binder coating made of latex or resin to the underside or back of the upholstery canvas.

Früher bestand die Polsterleinwand gewöhnlich aus einem Jute-Gewebe und ein derartiges Gewebe wurde dann durch eine Npppensetz-Maschine durchgeführt, in welcher schlingenartigIn the past, the upholstered canvas usually consisted of one Jute fabrics and such fabrics were then passed through a napkin machine, in which loop-like

309841/107Θ309841 / 107Θ

23149982314998

geformte Florelemente aus Garn durch die Polsterleinwand unter Bildung eines Flors der gewünschten Höhe auf der oberen Fläche der Polsterleinwand gebildet wurden, wobei die Garnschlaufen der Florelemente auf der Unterseite der Polsterleinwand nicht befestigt waren. Sobald die Polsterleinwand vollständig getuftet war, wurde gewöhnlich ein Latex-Bindemittel auf die exponierten Verbindungssehlaufen der unteren Fläche zur Befestigung derselben auf der Polsterieinwand aufgebracht und dadurch ein vollständiger Teppichaufbau geschaffen, in welchem die Florelemente fest in der gewünschten Höhe oberhalb der Polsterleinwand gehalten wurden. Oftmals wurde anschließend eine Papierunterlage auf die Rückseite der Latexschicht aufgeklebt, um dem Teppich die notwendige Steifheit zu verleihen.shaped pile elements of yarn through the upholstery canvas to form a pile of the desired height on the upper surface of the upholstered canvas were formed, wherein the yarn loops of the pile elements were not attached to the underside of the upholstery canvas. Once the upholstered canvas was fully tufted, a latex binder was usually applied to the exposed joint tendons the lower surface for attaching the same to the upholstery canvas applied and thereby created a complete carpet structure in which the pile elements firmly in the desired height above the upholstered canvas. Often times, a paper pad was then put on the back of the latex layer is glued on to give the carpet the necessary rigidity.

Jute oder andere Polsterleinwand-Gewebe sind jedoch kein vollständig zufriedenstellendes Basis-Gerüstmaterial und es wurde von den Herstellern von Gewebematerialien seit langem ein Bedarf für verbesserte Typen derartiger Polsterleinwand-Gewebe angemeldet.However, jute or other upholstery canvas fabrics are not A fully satisfactory basic scaffolding material and it has been used by tissue material manufacturers since There has long been a need for improved types of such upholstered canvas fabrics.

Früher wurde Polsterleinwand aus Jute oder Baumwollsegeltuch durch thermoplastische Materialien ersetzt, wie z.B. gesponnenes Nylon, Polypropylen, Polyäthylen, Polybutadien, Polystyrol und Styrol-copolymere, Acry!polymere und -co-In the past, upholstered canvas made of jute or cotton canvas was replaced by thermoplastic materials, such as woven nylon, polypropylene, polyethylene, polybutadiene, polystyrene and styrene copolymers, acrylic polymers and copolymers

309841/1076 ■ _309841/1076 ■ _

13149961314996

polymere, Äthylen-Propylen-Kautschuk, Äthylen-Propylen-Dien-Terpolymere oder andere ähnliche thermoplastische Materialien. Thermoplastische^ Polsterleinwandarten weisen eine Reihe von Vorteilen gegenüber den früheren Polsterlein-polymeric, ethylene-propylene rubber, ethylene-propylene-diene terpolymers or other similar thermoplastic materials. Thermoplastic upholstery canvas types have a A number of advantages over the earlier upholstery

wandarten auf Leinwandbasis insofern auf, als die thermoplastischen Materialien weniger kostspielig, leichter zugänglich und leichter zu verarbeiten sind.wall types based on canvas insofar as the thermoplastic Materials are less expensive, more accessible and easier to work with.

Leider schmilzt die thermoplastische Polsterleinwand, wenn Gewebematerialien auf Basis derartiger thermoplastischer Polsterleinwandarten erhitzt werden oder einer Flamme ausgesetzt sind, sehr rasch und führt zur Ausbreitung der Flamme, welche wiederum ein Auseinanderbersten der befestigten Faser- oder Filmoberflächen bewirkt und so die Entflammbarkeit des Materials außerordentlich stark steigert. Unfortunately, the thermoplastic upholstery canvas melts when Fabric materials based on such thermoplastic Upholstered canvases are heated or exposed to a flame are very rapid and lead to the spread of the flame, which in turn causes the fortified ones to burst apart Causes fiber or film surfaces and thus increases the flammability of the material extremely strongly.

Es ist daher angesichts von sehr breit angelegten Versuchen der beteiligten Industrien zur Schaffung von nichtentflammbaren Gewebematerialien das Ziel der vorliegenden Erfindung, ein Gewebematerial auf Basis einer thermoplastischen Polsterleinwand zu schaffen, die derart behandelt ist, daß eine feuerhemmende Polsterleinwand erzielt wird.It is therefore in the face of very broad attempts by the industries involved to create non-flammable Fabric materials the aim of the present invention is a fabric material based on a thermoplastic upholstery canvas to create which is treated so that a fire retardant upholstered canvas is obtained.

Gemäß der vorliegenden Erfindung werden nun GewebematerialienIn accordance with the present invention there are now fabric materials

309841/1076309841/1076

_ cc __ cc _

ob nun gewebt, faservlies-artig oder laminar, die auf der Verwendung einer Polsterleinwand als Trägerteil basieren, flammenhemmend gemacht, indem man eine Zubereitung inkorporiert, welche ein hitzhärtbares Harz und eine Phosphor-enthaltende Verbindung in dem Latex inkorporiert, der gewöhnlich auf die Polsterleinwand aufgebracht wird. Hierdurch wird bewirkt, daß eine Exposition des Gewebes gegenüber einer Flamme oder einer Erwärmung, welche die Verbrennungstemperatur -des Gewebes oder der Polsterleinwand erreichen läßt, nicht zu einem nachfolgenden Schmelzen und einer Ausbreitung der Flamme, veranlaßt durch die Polsterleinwand, führt.whether woven, fiber fleece-like or laminar, the based on the use of an upholstered canvas as a support part, Made flame retardant by incorporating a preparation containing a thermosetting resin and a phosphorus-containing one Compound incorporated into the latex that is usually applied to the upholstery canvas. This causes the tissue to be exposed to a flame or to heat which may cause the tissue to be exposed Combustion temperature of the fabric or the upholstery canvas not to a subsequent melting and spreading of the flame, caused by the upholstery, leads.

Durch die vorliegende Erfindung erfolgt nun eine Verbesserung von thermoplastischen Polsterlexnwandarten, die alle Vorteile über die früher verwendeten Gewebe-Polsterleinwandarten aufweisen, in dem Sinne, daß sie sicherer und noch vorteilhafter gestaltet werden.The present invention now provides an improvement in thermoplastic upholstery wall types, all of which Have advantages over the previously used fabric-upholstered canvas types in the sense that they are safer and even more secure be made more advantageous.

Die Ziele der vorliegenden Erfindung werden, wie bereits ganz allgemein oben ausgeführt, erreicht, indem man eine Zubereitung, enthaltend ein hitzehärtbares Harz und eine Phosphor-enthaltende Verbindung in das Latex, mit welchem man gewöhnlich eine oder beide Seiten einer Polsterleinwand beschichtet, bzw. das man auf diese aufbringt, inkorporiert .The objects of the present invention are, as already stated very generally above, achieved by using a Preparation containing a thermosetting resin and a phosphorus-containing compound in the latex, with which one or both sides of an upholstered canvas is usually coated or incorporated onto it .

309841/107&309841/107 &

13149961314996

'Die Latices, die gewöhnlich als Überzüge für Polsterleinwandsorten zum Zwecke der Adhäsion und ebenso für erhöhte Gleit- und Oberflächeneigenschaften des Gewebematerials verwendet werden, umfassen Acryl-Latices, wie z.B. PoIy-(methylmethacrylat), Äthylen/Viny!chlorid/Acrylsäure, Poly(äthylacrylat), Poly(butylacrylat), Acrylester-Copolymere und Ester/Säure-Mischungen, Polyvinylacetat-Latices und andere Latices, wie z.B. Äthylen/Vinylchlorid, Äthylen/ Vinylacetat, Vinylchlorid-Homopolymere und -Copolymere, Vinylchlorid/Acrylnitril, Naturkautschuk, SBR-Kautschuk, carboxylierter SBR-Kautschuk und ähnliche bekannte Materialien, 'The latices, commonly used as covers for upholstery canvases for the purpose of adhesion and also for increased sliding and surface properties of the fabric material used include acrylic latices such as poly (methyl methacrylate), Ethylene / vinyl chloride / acrylic acid, Poly (ethyl acrylate), poly (butyl acrylate), acrylic ester copolymers and ester / acid mixtures, polyvinyl acetate latices and other latices, such as ethylene / vinyl chloride, ethylene / Vinyl acetate, vinyl chloride homopolymers and copolymers, Vinyl chloride / acrylonitrile, natural rubber, SBR rubber, carboxylated SBR rubber and similar known materials,

Die Ausdrücke "Latex" oder "Latices", wie sie nachfolgend in der Beschreibung-und den Ansprüchen angewandt werden, sollen die vorstehend spezifisch aufgeführten Materialien und beliebige andere Latices umfassen, die als Polsterleinwandüberzüge oder Bindemittelmaterial verwendet werden.The terms "latex" or "latices" as used hereinafter are used in the description and claims, are intended to include the materials specifically listed above and any other latices used as upholstery canvas covers or binder material can be used.

Die hitzehärtbaren Harze, welche zu dem Polsterleinwandüberzugslatex zugegeben werden,' sind hitzehärtende Harze auf Aldehyd-Basis, hergestellt durch Reaktion von Aldehyden mit Stickstoff-enthaltenden Materialien, wie z.B. Amide, Sulfonamide, Amine oder phenolische Materialien.The thermosetting resins that make up the upholstery canvas cover latex are aldehyde-based thermosetting resins made by reacting aldehydes with nitrogen-containing materials such as amides, Sulfonamides, amines, or phenolic materials.

- 7 309841/1078 - 7 309841/1078

23149982314998

Erläuternde Stickstoff-enthaltende Verbindungen, die mit Aldehyden zur Herstellung der hitzehärtenden Harze, wie sie in der vorlieg enden Erfindung angewandt werden, umgesetzt wurden, umfassen Amide, wie z.B. Harnstoff und substituierte Harnstoffe, wie z.B. Monomethylharnstoff und Dimethy!harnstoff, Sulfonamide, wie z.B. p-Toluolsulfonamid und Benzolsulfonamid, Amine, wie z.B. Melamin, 1,6-Hexandiamin, Hexamethylentetraamin und ähnliche aliphatische Amine, oder phenolische Stoffe, wie z.B. Phenol, Bisphenol A5 4,4'-Dihydroxydiphenylmethan, Resorcin und ähnliche Materialien. Illustrative nitrogen-containing compounds that have been reacted with aldehydes to prepare the thermosetting resins as used in the present invention include amides such as urea and substituted ureas such as monomethyl urea and dimethyl urea, sulfonamides such as p-Toluenesulfonamide and benzenesulfonamide, amines such as melamine, 1,6-hexanediamine, hexamethylenetetraamine and similar aliphatic amines, or phenolic substances such as phenol, bisphenol A 5 4,4'-dihydroxydiphenylmethane, resorcinol and similar materials.

Erläuternde Aldehyde, welche mit den vorerwähnten Stickstoffenthaltenden Verbindungen zur Herstellung von hitzehärtbaren Harzen umgesetzt werden, schließen Formaldehyd, Acetaldehyd und Terephthaldehyd ein.Illustrative aldehydes, which with the aforementioned nitrogen-containing Compounds used to produce thermosetting resins include formaldehyde, acetaldehyde and terephthalaldehyde.

Es ist für den Fachmann klar, daß die hitzehärtbaren Harze durch Umsetzen eines Aldehyds mit einem Phenol und einem Amid, Sulfonamid oder Amin hergestellt werden können.It is clear to those skilled in the art that the thermosetting resins by reacting an aldehyde with a phenol and a Amide, sulfonamide or amine can be produced.

Phosphor-enthaltende Verbindungen, die in dem Latex für den Polsterleinwand-überzug, zusammen mit dem hitzehärtbaren Harz inkorporiert werden können, schließen ein Trialky!phosphate, z.B. Triisopropylphosphat; Triarylphosphate,Phosphorus-containing compounds in the latex for the upholstery canvas cover, along with the thermosetting Resin may be incorporated include Trialky! Phosphate, e.g., triisopropyl phosphate; Triaryl phosphates,

309841/1076309841/1076

z.B. Trikresylphosphatj Kresyldiphenylphosphat, Phenyldikresylphosphat, Triphenylphosphat, Trixylylphosphat; Alkyldiary !phosphate, z.B. Nonyldikresy!phosphat, Isodecyldipheny!phosphat, Isononyldiphenylphosphat, Isooctyldiphenylphosphat, Isopropyldiphenylphosphat, Octyldiphenylphosphat; Dialkylarylphosphate, z.B. Diisodecylphenylphosphat; Alkyldiaryl- und -dialkylarylphosphate, hergestellt aus gemischten C7-, Cq-, CL^-Alkoholen; PoIyammoniumphosphate; Diphqsphate, z.B. die Diphosphatester der 232-bis(Halogenmethyl) -I53-propylen-bis(phosphorhalidate), wie sie in der US-Patentschrift 3 192 242 beschrieben sind, auf die hier ausdrücklich Bezug genommen wird; halogenierte Phosphate, z.B. tris(ß-Chloräthyl)-phosphat, tris(2,3-Dichlorpropyl)-phosphat, tris(2,3-Dibrompropyl)-phosphat; Phosphonate und Polyphosphonate, insbesondere die halogenierten Phosphitphosphonate und halogenierten Polyphosphonate, die in den US-Patentschriften 3 014 95^ und 3 014 956, auf die hier ausdrücklich Bezug genommen wird, beschrieben sind; und Phosphoramidate. ·for example tricresyl phosphate, cresyl diphenyl phosphate, phenyl dicresyl phosphate, triphenyl phosphate, trixylyl phosphate; Alkyl diaryphosphates, for example nonyldicresylphosphate, isodecyldiphenylphosphate, isononyldiphenylphosphate, isooctyldiphenylphosphate, isopropyldiphenylphosphate, octyldiphenylphosphate; Dialkylaryl phosphates, for example diisodecylphenyl phosphate; Alkyl diaryl and dialkyl aryl phosphates prepared from mixed C 7 , Cq, CL ^ alcohols; Polyammonium phosphates; Diphosphates, for example the diphosphate esters of 2 3 2-bis (halomethyl) -I 5 3-propylenebis (phosphorus halide), as described in US Pat. No. 3,192,242, to which reference is expressly made here; halogenated phosphates, for example tris (ß-chloroethyl) phosphate, tris (2,3-dichloropropyl) phosphate, tris (2,3-dibromopropyl) phosphate; Phosphonates and polyphosphonates, in particular the halogenated Phosphitphosphonate and halogenated polyphosphonates described in US Patents 3,014 95 ^ and 3,014,956, which are expressly incorporated herein by reference; and phosphoramidates. ·

Der Anteil an Phosphor-enthaltender "Verbindung zu hitzehärtbarem Harz, wie sie in der vorliegenden Erfindung angewandt werden, kann im Bereich von etwa 1 bis 100 TEiIe phH (pro hundert Teile Harz) liegen. Vorzugsweise werden von etwa 15 bis etwa 40 phH an Phosphor-enthaltender. Verbindung eingesetzt. 309841/1076The proportion of phosphorus-containing "compound to thermosetting Resin as employed in the present invention can range from about 1 to 100 parts phH (per hundred parts of resin). Preferably from about 15 to about 40 phH of phosphorus-containing. link used. 309841/1076

Der Anteil der Mischung an hitzehärtbarem Harz und Phosphor-enthaltender Verbindung, die zu dem Latex der Polsterleinwand-Beschichtung zugegeben wirda kann im Bereich von etwa 5 bis etwa 100 Teile phH (bezogen auf den Latex) liegen. Vorzugsweise werden etwa 15 bis etwa 50 Teile der Mischung angewandt.The proportion of the mixture of thermosetting resin and phosphorus-containing compound that is added to the latex of the upholstery canvas coating a can be in the range of about 5 to about 100 parts phH (based on the latex). Preferably from about 15 to about 50 parts of the mixture are employed.

Im Rahmen der vorliegenden Erfindung wurde festgestellt 3 daß durch die Zumischung des hitzehärtbaren Harzes und der Phosphor-enthaltenden Verbindung zu dem für die Herstellung von Geweben verwendeten Latex für die Polsterleinwand-Besehiehtung nach einer Exposition gegenüber Hitze oder Plannneneinwirkung eine vollständig verkohlte Struktur gebildet wird, welche bei dem zusammengesetzten Gewebematerial in wirksamer Weise feuerhemmend ist.In the context of the present invention it has been found 3 that the addition of the thermosetting resin and the phosphorus-containing compound to the latex used for the manufacture of fabrics for the upholstery canvas cover forms a completely charred structure after exposure to heat or tarpaulin is effectively fire retardant in the composite fabric material.

Die Mischung des hitzehärtbaren Harzes und der Phosphorenthaltenden Verbindung wird durch Auflösen des Harzes in Wasser oder Wasser/Alkohol bei 50 bis 60 % Peststoffgehalt und Einrühren in Ae Phosphor-enthaltende Verbindung hergestellt. The mixture of the thermosetting resin and the phosphorus-containing compound is prepared by dissolving the resin in water or water / alcohol at 50 to 60 % pesticide content and stirring into Ae phosphorus-containing compound.

Außer/dem Einmischen des hitzehärtbaren Harzes und der Phosphor-enthaltenden Verbindung in den Latex für die Polsterleinwand-Besehichtung kann die feuerhemmende Zube-Besides / mixing in the thermosetting resin and the Phosphorus-containing compound in the latex for the upholstery canvas coating can be the fire-retardant accessories

309841/1076309841/1076

reitung der vorliegenden Erfindung auch auf anderem Wege auf die Polsterleinwand aufgebracht werden, wie z.B. durch Versprühen, Beschichten oder durch andere ähnliche Verfahren für das Aufbringen von Flüssigkeiten.·The embodiment of the present invention can also be applied to the upholstery canvas by other means, such as by Spraying, coating or other similar methods for the application of liquids.

Die feuerhemmenden Zubereitungen gemäß Erfindung können auch Kohlebildner enthalten, wie z.B. irgendein polyfunktionelles Material, z.B. Erythritol, Pentaerythritol 3 lösliche Stärke und dergl., Pigmente, Gleitmittel, Beschichtungshilfen und andere Standard-Kompoundierungsmittel.The fire retardant preparations according to the invention can also contain charcoal formers, such as any polyfunctional material, for example erythritol, pentaerythritol 3 soluble starch and the like, pigments, lubricants, coating aids and other standard compounding agents.

Die folgenden Beispiele erläutern spezifische, nicht beschränkende Ausführungsformen der Erfindung. Die in den Beispielen unter der Bezeichnung "RHOPLEX" 85, "RHOPLEX" LC40, 11CERECLOR" S52, 51RESIMENE" 8110,-"RESIMENE" 819 und · 11ACRYLOID" B82 aufgeführten Materialien können zur Zeit von den Herstellern ohne weiteres bezogen werden und wurden hinsichtlich ihrer Zusammensetzung so genau wie möglich definiert.The following examples illustrate specific, non-limiting embodiments of the invention. The materials listed in the examples under the designation "RHOPLEX" 85, "RHOPLEX" LC40, 11 CERECLOR "S52, 51 RESIMENE" 8110, - "RESIMENE" 819 and 11 ACRYLOID "B82 are currently readily available from the manufacturers and have been defined as precisely as possible in terms of their composition.

Beispiel 1example 1

Es wurden die folgenden Latices als Bindemittel für Acryl-Plorteppiche auf Polypropylen-Polsterleinwand hergestellt.The following latices have been used as binders for acrylic pile carpets made on polypropylene upholstered canvas.

309841/1076309841/1076

TabelleTabel

GewichtsteileParts by weight

BestandteileComponents ■ 1■ 1 22 33 Proben-Nr.Sample no. 55 66th 77th 100100 100100 -- 44th 100100 5050 5050 Acrylharz 'Acrylic resin ' ' 50'50 5050 100100 5050 100100 100100 OO Amin/Aldehydpv
Harz LösungAmine / aldehyde pv
Resin solution __ 1010 1515th 100100 __ __ __ co
00co
00 Phosphit- ,ν
phosphonat^'Phosphite, ν
phosphonate ^ ' __ —- __ 2525th —- 2525th Diisodecyl-
phenylphosphat
It \Diisodecyl
phenyl phosphate
It \ -- -- -- __ -- -- -- OO 4 )
Acrylharz4)
Acrylic resin __ __ -- __ 2525th __ cncn Diisodecyl- g^
pheny!phosphat 'Diisodecyl- g ^
pheny! phosphate ' __

100 100100 100

2525th

50 5050 50

Chloriertes,-χ <, Chlorinated, -χ <,

Paraffin 5;'o; - - - - 25 - - 25Paraffin 5; 'o; - - - - 25 - - 25

nat ϊ)>°)> !____! : 25 - ζ ?J nat ϊ)>°)> ! ____! : 25 - ζ ? J

2) 65 £~ige Lösung von "RESIMENE" 819 in Wasser-Isobutanol2) 65% solution of "RESIMENE" 819 in water isobutanol

3) US-Patentschrift 3 014 956 ■ YZ 3) U.S. Patent 3,014,956 ■ YZ

4) "RHOPLEX" LC-40 ~J S)11CERECLOR" S-v52 (choriertes Paraffin-52 % Chlor) j^. 6) Mischung von" 14 Teilen Phosphat, 14 Teilen chloriertes Paraffin cd4) "RHOPLEX" LC-40 ~ J S) 11 CERECLOR "S- v 52 (chlorinated paraffin-52 % chlorine) j ^. 6) Mixture of" 14 parts of phosphate, 14 parts of chlorinated paraffin cd

und 2 Teilen Phosphit-phosphonat · CDand 2 parts of phosphite phosphonate · CD

Die in der Tabelle I angegebenen Latex-Proben wurden mit der Rakel [in·verschiedenen Dicken von 3, 5 und 10 mil (0,076, 0,127 und 0,254 mm)] auf die Rückseiten von Polypropylen-Polsterleinwandstücken von Aeryl-Florteppichen aufgestrichen. Die Latexproben wurden durch Erhitzen der Teppichproben in einem Ofen getrocknet.The latex samples given in Table I were knife-coated [in different thicknesses of 3, 5 and 10 mil (0.076, 0.127 and 0.254 mm)] on the backs of polypropylene upholstery canvases from Aeryl pile carpets painted on. The latex samples were made by heating the Carpet samples dried in an oven.

Die Teppichproben wurden dann dem Prüfverfahren DOG PF 2-70 unterworfen, das ein Standard-Test zur Bestimmung der Oberflächen-Entflammbarkeit von kleinen Teppichen und Brücken ist. Das Untersuchungsver.fahren ist ganz allgemein als "Pillen"-Test bekannt und wird im Detail in Federal Register, Vol. 35, No. 74, 16. April 1970, beschrieben.The carpet samples were then subjected to test method DOG PF 2-70 subjected to a standard test for determining surface flammability of small carpets and bridges is. The investigation procedure is quite general as "Pill" test is known and is detailed in Federal Register, Vol. 35, No. 74, April 16, 1970.

Dieser Test besteht,"wie hier kurz ausgeführt wird, darin, daß man eine Teppichprobe horizontal in einen Rahmen pla-.ziert, der ein zentrales Loch aufweist. Eine kleine "Pille" von Hexamethylentetramin (eine Tablette mit zeitlich regulierter Verbrennung) wird an der Vorder- oder Rückseite des Teppichs an einem Punkt über dem Zentrum des Loches in dem Rahmen plaziert. Die "Pille" wird durch Berühren ihrer Oberfläche mit einem brennenden Zündholz entzündet. Jeder Versuch wird solange fortgesetzt, bis (1) die Flamme oder die Glut verschwindet oder (2) das Weiterglimmen oder Weiterbrennen sich über 1 inch (2,54 cm) von der Kante desThis test consists, "as will be briefly explained here, in that a carpet sample is placed horizontally in a frame, which has a central hole. A small "pill" of hexamethylenetetramine (a timed tablet Burn) will be on the front or back of the rug at a point above the center of the hole placed in the frame. The "pill" is ignited by touching its surface with a burning match. Each attempt is continued until (1) the flame or embers disappear or (2) the smoldering continues or Continue to burn about 1 inch (2.54 cm) from the edge of the

309841/1076309841/1076

Loches in dem Rahmen erstreckt.Hole in the frame extends.

Die Testergebnisse der Floroberflächen von 8 Proben von Acrylteppxchware mit Polypropylen-Polsterleinwand, welche mit den Rezepturen der Proben 1 bis 8 beschichtet war, sind in der nachstehenden Tabelle II summarisch wiedergegeben. The test results of the pile surfaces of 8 samples of acrylic carpet with polypropylene upholstery canvas, which was coated with the formulations of samples 1 to 8 are summarized in Table II below.

Tabelle IITable II

Probesample

nicht be- be- nicht be- be- be- bebestanden standen standen bestanden standen standen standen standennot passed not passed stood stood stood stood stood stood

Die Ergebnisse der Untersuchungen sind die gleichen bei Proben mit Bindemittel-Schichtdicken von 33 5 und 10 mil (0,076, 0,127 und 0,254 mm) auf der Polypropylen-PolSterleinwand. The results of the tests are the same for samples with binder layer thicknesses of 3, 3, 5 and 10 mils (0.076, 0.127 and 0.254 mm) on the polypropylene polypropylene canvas.

Beispiel 2Example 2

Die folgenden Latices wurden als feuerhemmende Bindemittel für spinn-verbundene Polsterleinwand-Arten eingesetzt:The following latices have been used as fire retardant binders used for spun-bonded upholstered canvases:

309841/1076 - 14 -309841/1076 - 14 -

Tabelle IIITable III

BestandteileComponents 11 22 GewiCertainly c h t s t e ic h t s t e i 1 e1 e 6 > 6 > II. 100100 iooioo Probe-Nr.Sample no. ■ 100 ■ 100 AcrylharzAcrylic resin 3030th 3030th 33 55 3030th II. OO Amin/Aldehyd (65%)2^ Amine / aldehyde (65%) 2 ^ 100100 100100 100100 CDCD Polyammonium-Polyammonium 55 -- ' 30'30 3030th 30 '30 ' 1515th phosphatphosphate .10 ■.10 ■ ' 10'10 1010 ~*~ * pipentaerythritol■ ^pipentaerythritol ■ ^ 5 ■'5 ■ ' 1010 -- 1515th —- 15-.15-. Polyphosphoaat 'Polyphosphoaate ' -- 1010 ©© 1515th -- 1515th GO , ■■..GO, ■■ ..

1) "RHOPLEX"1) "RHOPLEX"

2) 65 /2-ige Lösung von "RESIMENE" 819 in Wasser-Isobutanol2) 65/2 solution of "RESIMENE" 819 in water isobutanol

3) Kohle-Bildner3) charcoal maker

ij) US-Patentschrift 3 014 956ij) U.S. Patent 3,014,956

— A CT _- A CT _

23H99623H996

Die Ergebnisse des "Pillen"-Tests auf der Polsterleinwandseite des Acrylteppichs sind summarisch in der nachstehenden Tabelle IV wiedergegeben:The results of the "pill" test on the upholstery canvas side of the acrylic carpet are summarized in Table IV below:

Tabelle IV Probe-Nr. 1 2-3 4 5 ' 6 Table IV Sample No. 1 2-3 4 5 '6

be- be- be- be- be- nicht standen standen standen standen standen bestandenpassed passed passed passed passed

Beispiel 5Example 5

Die folgenden Latices wurden als feuerhemmende Bindemittel für spinn-verbundene Polypropylen-Polsterleinwandsorten hergestellt.The following latices have been used as fire retardant binders for spunbonded polypropylene upholstery canvases manufactured.

- 16 309841/1076 - 16 309841/1076

23143962314396

Tabelle. VTabel. V

BestandteileComponents

Gewich'tstei Ie Probe-Nr. Weighted sample no.

AcrylharzAcrylic resin

5050

5050

Harzresin

1010

1010

5050

1010

5050

5050

Methylethyl
ketonMethylethyl
ketone 5050 5050 5050 5050 5050 2)
Pentaerythritol ' 2)
Pentaerythritol ' 1010 1010 55 1010 Polyammonium-
phosphatPolyammonium
phosphate 55 55 1010 1010 1010 PolyphosphonatPolyphosphonate 55 -- -- 55 1010 Amin/Aldehyd- „%Amine / aldehyde- "%

1515th

1) "ACRYLOID" B-821) "ACRYLOID" B-82

2) Kohlebildner2) charcoal maker

3) US-Patentschrift 3 014"9563) U.S. Patent 3,014 "956

4) "RESIMENE" 8104) "RESIMENE" 810

Die Ergebnisse des "Pillen"-Tests an einer spinn-verbundenen Polypropylen-Polsterleinwand sind summarisch in der nachfolgenden Tabelle VI wiedergegeben.The results of the "pill" test on a spin-linked Polypropylene upholstery canvases are summary reproduced in Table VI below.

309841/1076309841/1076

23H99623H996

Tabelle VITable VI

Probe-Nr.Sample no.

bestanden bestanden bestanden bestanden bestandenpassed passed passed passed passed

Wenn die vorliegende Erfindung vorstehend auch unter Be-.zugnahme auf gewisse erläuternde spezifische Ausführungsformen beschrieben ist5 soll sie jedoch nicht auf diese Beispiele beschränkt sein, da es für den Fachmann ohne weiteres möglich ist3 entsprechende Modifikationen und Variationen durchzuführen. Es wird daher ausdrücklich darauf hingewiesen, daß die vorliegende Erfindung auch in entsprechend abgewandelter Form im Rahmen der vorlieg enden Beschreibung und der Ansprüche durchgeführt werden kann'.When the present invention is described above, even under loading .zugnahme to certain illustrative, specific embodiments 5 it should not be limited to these examples, however, since it is possible for the skilled person to carry out 3 corresponding modifications and variations. It is therefore expressly pointed out that the present invention can also be carried out in a correspondingly modified form within the scope of the present description and the claims.

-18-309841/1076 -18- 309841/1076

Claims (1)

23H99623H996 Pat e η t -a η s ρ r ü c h e : r~■"' Pat e η t -a η s ρ r ü c he : r ~ ■ "' 1. Feuerhemmende Zubereitung, enthaltend ein hitzehärtbares Harz und eine Phosphor-enthaltende Verbindung.1. Fire-retardant preparation containing a thermosetting agent Resin and a phosphorus-containing compound. 2. Zubereitung nach Anspruch 1, dadurch gekennzeichnet, daß das hitzehärtbare Harz ein Harz auf Aldehyd-Basis ist, das aus der Reaktion eines Aldehyds und einer Stickstoffenthalt enden Verbindung, oder eines Phenols, oder einer Mischung derselben., erhalten.wird.2. Preparation according to claim 1, characterized in that that the thermosetting resin is an aldehyde-based resin obtained from the reaction of an aldehyde and a nitrogen content a compound, or a phenol, or a mixture thereof., is obtained. 3. Zubereitung' nach Anspruch 2, dadurch gekennzeichnet, daß der Aldehyd Formaldehyd oder Acetaldehyd ist.·3. Preparation 'according to claim 2, characterized in that that the aldehyde is formaldehyde or acetaldehyde. 4. Zubereitung nach Anspruch 23 dadurch gekennzeichnet, daß die Stickstoff-enthaltende Verbindung ein Amid ist.4. Preparation according to claim 2 3, characterized in that the nitrogen-containing compound is an amide. 5. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß die Stickstoff--'enthaltende Verbindung ein Sulfonainid ist. - -5. Preparation according to claim 2, characterized in that that the nitrogen - 'containing compound is a sulfonainide is. - - 6. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß die Stickstoff-enthaltende Verbindung ein Amin ist.6. Preparation according to claim 2, characterized in that the nitrogen-containing compound is an amine. 7. Zubereitung nach Anspruch 23 dadurch gekennzeichnet,7. Preparation according to claim 2 3, characterized in that 309841/1076 - 19 -309841/1076 - 19 - daß das hitzehärtbare Harz ein Phenol/Aldehyd-Harz ist.that the thermosetting resin is a phenol / aldehyde resin. 8. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß das hitzehärtbare Harz ein Aldehyd/Harnstoff-Harz ist.8. Preparation according to claim 2, characterized in that the thermosetting resin is an aldehyde / urea resin. 9. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß das hitzehärtbare Harz ein Aldehyd/Sulfonamid-Harz ist.9. Preparation according to claim 2, characterized in that that the thermosetting resin is an aldehyde / sulfonamide resin. 10. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß das hitzehärtbare Harz ein Aldehyd/Melamin-Harz ist.10. Preparation according to claim 2, characterized in that the thermosetting resin is an aldehyde / melamine resin. 11. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß das hitzehärtbare Harz ein Amin/Aldehyd/Phenol-Harz ist,11. Preparation according to claim 2, characterized in that the thermosetting resin is an amine / aldehyde / phenol resin, 12. Zubereitung nach Anspruch 2, dadurch gekennzeichnet, daß das hitzehärtbare Harz ein Amid/Aldehyd/Phenol-Harz ist,12. Preparation according to claim 2, characterized in that the thermosetting resin is an amide / aldehyde / phenol resin, 13- Zubereitung nach Anspruch 1, dadurch gekennzeichnet, daß die Phosphor-enthaltende Verbindung ein Phosphat ist.13- preparation according to claim 1, characterized in that that the phosphorus-containing compound is a phosphate. lh. Zubereitung nach Anspruch 13, dadurch gekennzeichnet, daß das Phosphat ein Trialkylphosphat, Triarylphosphat, Alkyldiarylphosphat, Dialkylary!phosphat, Diphosphat, Polyammoniumphosphat und/oder ein halogeniertes Phosphat ist. lh. Preparation according to Claim 13, characterized in that the phosphate is a trialkyl phosphate, triaryl phosphate, alkyl diaryl phosphate, dialkyl aryl phosphate, diphosphate, polyammonium phosphate and / or a halogenated phosphate. 309841/1076309841/1076 - 20 -- 20 - 15· Zubereitung nach Anspruch 1, dadurch gekennzeichnet', daß die Phosphor-enthaltende Verbindung ein Phosphohat ist.15 preparation according to claim 1, characterized that the phosphorus-containing compound is a phosphate. 16. Zubereitung nach Anspruch I5 dadurch gekennzeichnet s daß die Phosphor-enthaltende Verbindung ein Phosphoröämidat ist.16. Composition according to claim I 5 characterized s that the phosphorus-containing compound is a Phosphoröämidat. 17. Zubereitung nach Anspruch I5 'dadurch gekennzeichnet, daß sie ein Kohle-bildendes Material enthält;17. Preparation according to claim I 5 ', characterized in that it contains a carbon-forming material; 18. Thermoplastische Polsterleinwand, verbunden Mt einer Zubereitung nach Anspruch i.18. Thermoplastic upholstered canvas, connected with one Preparation according to claim i. 19. Polsterleinwand- nach Anspruch 18, dadurch gekennzeichnet, daß sie ein Kohle-bildendes Material einsehließt;19. Upholstered canvas according to claim 18, characterized in that that it includes a charcoal-forming material; 20. Gewebeärtikel, enthaltend eine thermöplastischt Polster leinwand, weiche mit einer Zubereitung nach Anspruch 1 verbunden ist.20. Fabric articles containing a thermoplastic pad Canvas, soft with a preparation according to claim 1 connected is. 21. Artikel nach Anspruch 20, dadurch gekennzeichnet, daß der Artikel ein Bodenbelag oder eine Dekoration ist.21. Article according to claim 20, characterized in that that the article is a floor covering or a decoration. 309841/1076309841/1076
DE19732314996 1972-03-27 1973-03-26 FIRE-RETARDANT UPHOLSTERY CANVAS AND METHOD OF MAKING IT Pending DE2314996A1 (en)