DE212180C - - Google Patents
Info
- Publication number
- DE212180C DE212180C DENDAT212180D DE212180DA DE212180C DE 212180 C DE212180 C DE 212180C DE NDAT212180 D DENDAT212180 D DE NDAT212180D DE 212180D A DE212180D A DE 212180DA DE 212180 C DE212180 C DE 212180C
- Authority
- DE
- Germany
- Prior art keywords
- core thread
- execution
- colloidal
- thread
- collodion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
KAISERLICHESIMPERIAL
PATENTAMT.PATENT OFFICE.
PATENTSCHRIFTPATENT LETTERING
"-Jig 212180-KLASSE 21/. GRUPPE "-Jig 212180- CLASS 21 /. GROUP
ADOLF KROLL in LUXEMBURG und BYRAMJI SAKLATWALLA in NEW-YORK.ADOLF KROLL in LUXEMBURG and BYRAMJI SAKLATWALLA in NEW YORK.
Verfahren zur Herstellung dünner Fäden zu Beleuchtungszwecken. Patentiert im Deutschen Reiche vom 14. Dezember 1907 ab.Process for the production of thin threads for lighting purposes. Patented in the German Empire on December 14, 1907.
Die Leuchtfäden der neuen Metallfadenlampen sind bekanntlich sehr brüchig, weil das der Paste zugemengte Bindemittel das Metall verunreinigt und ein lockeres Gefüge verursacht. Die für Lampen hoher Voltzahl bei nicht zu großer Kerzenstärke erforderliche Fadendünne ist daher schwer zu erreichen. Nach der Erfindung werden durchaus reine und dünne Fäden erhalten, indem einfach dasThe filaments of the new metal filament lamps are known to be very brittle because the binder added to the paste contaminates the metal and creates a loose structure caused. The necessary for lamps with high voltages with not too large a candle strength Thinning of the thread is therefore difficult to achieve. According to the invention, they are quite pure and get thin threads by simply that
ίο Bindemittel räumlich von der Masse getrennt in Anwendung kommt. Das hierfür benutzte Verfahren stellt sich als eine Übertragung und Erweiterung des von Wollaston zur Herstellung besonders dünner Platindrähte eingeführten dar. Wollaston umgab den bereits dünnen Metalldraht mit einer Silberhülle, zog den Doppelfaden wieder durch Ziehlöcher hindurch und löste nachher den Silbermantel in Säure. Im vorliegenden Falle wird dieses Verfahren nun gleich auf das Verspritzen der Pasten übertragen.ίο Binder spatially separated from the mass comes into use. The procedure used for this turns out to be a transfer and expansion of the one introduced by Wollaston for the production of particularly thin platinum wires Wollaston surrounded the already thin metal wire with a silver sleeve and pulled the double thread through the pulling holes again and afterwards dissolved the silver coat in acid. In the present case this is Now transfer the process to the spraying of the pastes.
Zur Ausführung des Verfahrens benutzt man zweckmäßig eine Vorrichtung mit zwei ineinandergeschachtelten Düsen, von denen die äußere etwas über die innere hervortritt. Die innere Düse verspritzt die Masse, und zwar zu einem drahtförmigen Kernfaden, den die äußere Düse in einen Mantel aus Bindemittel einhüllt, wobei sie den Doppelfaden derart zusammendrückt, daß der Kernfaden an Quer-. schnitt einbüßt.A device with two is expediently used to carry out the method nested nozzles, of which the outer one protrudes slightly over the inner one. the inner nozzle injects the mass into a wire-shaped core thread, which the outer nozzle is wrapped in a jacket of binding agent, compressing the double thread in such a way that that the core thread at transverse. cut forfeit.
Als Masse für den Kernfaden eignen sich angerührte Metalloxyde u. dgl., namentlich aber kolloidale Metalle und kolloidale Metallverbindungen, da sie ein hervorragend dichtes Gefüge hinterlassen. Die Kernmasse kann beliebig wenig Klebemittel enthalten, da sie nicht plastisch zu sein braucht; sie muß aber stets genügende Nachgiebigkeit aufweisen.Mixed metal oxides and the like are particularly suitable as the mass for the core thread but colloidal metals and colloidal metal compounds, as they are extremely dense Leave a structure. The core mass can contain as little adhesive as desired, since they does not need to be plastic; but it must always be sufficiently flexible.
Mit besonderem Vorteil verwendet man kolloidale Wolframsäure, die erst durch das neue Verfahren technisch verwendbar wird. Dieses Material ist nämlich an sich zwar sehr nachgiebig, aber wenig plastisch und verliert an der Luft zu schnell das Wasser, so 'daß es steif und brüchig wird. Das läßt sich jedoch nach dem neuen Verfahren in ebenso einfacher wie wirksamer Weise verhüten, wenn man auf den Kernfaden aus kolloidaler Wolframsäure einen wasserdichten Überzug aufbringt.It is particularly advantageous to use colloidal tungstic acid, which is only produced by the new process becomes technically usable. This material is actually very much in itself yielding but not very plastic and loses water too quickly in the air, so that it becomes stiff and brittle. However, this can also be done according to the new method Easier and more effective way of preventing if you look at the core thread from colloidal Tungstic acid applies a waterproof coating.
Im allgemeinen eignen sich für den Mantel die Bindemittel der anderen Verfahren, vornehmlich aber Kollodium, das in Alkoholäther, Eisessig o. dgl. gelatiniert ist. Dem Bindemittel macht man indessen mit Vorteil solche Zusätze, die auf dem Glühfaden einen nützlichen Überzug zurücklassen, indem sie z. B. dessen Zerstäubung verringern.In general, the binders of the other processes are particularly suitable for the jacket but collodion which is gelatinized in alcohol ether, glacial acetic acid or the like. The binder however, it is advantageous to make such additives which have a useful effect on the filament Leave coating behind by z. B. reduce its atomization.
Zwecks Verwendung als Leuchtfäden für elektrische Glühlampen werden die Doppel-, fäden am besten in die später gewünschte Lage gebracht, ehe sie durch einfaches Abbrennen von ihrem Mantel befreit und einem Reduktionsverfahren unterworfen werden, das einen reinen Metalldraht zurückläßt.For use as filaments for electric light bulbs, the double, it is best to put the threads in the position you want later, before simply burning them off stripped of their sheath and subjected to a reduction process that leaves a pure metal wire.
Die neuen, oxydischen Doppelfaden lassen sich aber auch durch Weben 0. dgl. zuLet the new, oxidic double thread but also by weaving 0
Strümpfen für Gasglühlicht verarbeiten. Derartige Strümpfe sind gegen Erschütterungen ungemein widerstandsfähig. Auch ist die lichtstrahlende Oberfläche des Strumpfes, dessen Fäden außergewöhnlich fein sein können, bedeutend vergrößert.Process stockings for gas incandescent light. Such stockings are against vibrations extremely resilient. The light-emitting surface of the stocking is also its Threads can be exceptionally fine, significantly enlarged.
Zur Herstellung von Fäden für Gasglühlichtstrümpfe benutzt man zweckmäßig als Kernmasse Thoriumoxyd, das aus Oxalat hergestellt, mit Säure abgedampft und mit Wasser ■ angerührt eine firnisartige Konsistenz aufweist. Die den staubigen Fäden der üblichen Tränkungsverfahren eigentümliche große Porosität läßt sich auch hier in beliebigem Maße durch Zusatz von Bindemittel oder von pulverförmigen Thor- und Cerverbindungen erreichen. Letztere Stoffe bringt man am besten in das Bindemittel, das den äußeren Mantel bildet, um so einen festen Kern und eine poröse Oberfläche zu erhalten.For the production of threads for gas incandescent light socks one uses expediently as Core mass thorium oxide, which is made from oxalate, evaporated with acid and with water ■ has a varnish-like consistency when mixed. The dusty threads of the usual soaking processes The peculiarly large porosity can also be reduced to any desired extent by adding a binder or powder Reach Thor and Cer connections. The latter substances are best brought into the Binder that forms the outer shell, so a solid core and a porous one Surface.
Claims (4)