DE2116037A1 - Antistatic coated photographic films - Google Patents
Antistatic coated photographic filmsInfo
- Publication number
- DE2116037A1 DE2116037A1 DE19712116037 DE2116037A DE2116037A1 DE 2116037 A1 DE2116037 A1 DE 2116037A1 DE 19712116037 DE19712116037 DE 19712116037 DE 2116037 A DE2116037 A DE 2116037A DE 2116037 A1 DE2116037 A1 DE 2116037A1
- Authority
- DE
- Germany
- Prior art keywords
- dextran sulfate
- alkali metal
- metal salt
- dextran
- photographic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
PATENTANWÄLTE L I I D U V /PATENTANWÄLTE L IIDUV /
8 MÜNCHEN 2, HILBi-ESTRASSE 2O8 MUNICH 2, HILBi-ESTRASSE 2O
Ihr Zeichen Unser Zeichen Datum \, ApfU 1971Your reference Our reference date \, ApfU 1971
Anwaltsakte 20 824
Βθ/δ Attorney file 20 824
Βθ / δ
Ilford Limited
Ilford, Essex (Großbritannien)Ilford Limited
Ilford, Essex (UK)
"Plio to graphische Filme mit antistatischer Beschichtung""Plio to graphic films with antistatic coating"
Diese Erfindung betrifft photοgraphische Filme mit antistatischer Beschichtung und die Herstellung eines solchen Filmmaterials.This invention relates to antistatic photographic films Coating and the manufacture of such a film material.
Es ist bekannt, daß photοgraphische Filme die Neigung zur elektrostatischen Aufladung während ihrer Herstellung und Gase ILF/861 109842/1693 -2- It is known that photographic films have a tendency to build up electrostatic charges during their manufacture and gases ILF / 861 109842/1693 -2-
_ ο —_ ο -
ebenso bei ihrer Verwendung bzw. weiteren Verarbeitung haben» Wenn ein elektrostatisch geladener Film entladen wird, werden so bezeichnete "statische Marken oder Störstellen" gebildete Diese Marken zeigen sich dann als Flächen örtlicher überentwicklung bei dem entwickelten Film» Es ist möglich, die Neigung des' photographischen Films zur Aufnahme von elektrostatischen Ladungen dadurch zu verringern, daß man eine Schicht, die eine relativ hohe elektrische Leitfähigkeit aufweist, vorsieht. Alle elektrostatischen Ladungen, die durch einen Film mit einer derartigen Schicht aufgenommen werden, werden schnell ohne Bewirken einer Entladung geerdet«also have with their use or further processing » When an electrostatically charged film is discharged, so-called "static marks or imperfections" These brands then show up as areas of local overdevelopment in the developed film »It is possible to reduce the tendency of the photographic film to receive electrostatic charges by a layer which has a relatively high electrical conductivity is provided. All electrostatic charges, picked up by a film having such a layer become rapidly without causing a discharge grounded"
Es ist ein Gegenstand der vorliegenden Erfindung, ein Verfahren zur Verbesserung der Oberflächenleitfähigkeit von photοgraphischem Material zur Verfügung zu stellen»It is an object of the present invention to provide a method for improving the surface conductivity of to provide photographic material »
Die vorliegende Erfindung schafft ein Verfahren zur Verbesserung der Oberflächenleitfähigkeit von photοgraphischem Filmmaterial, wozu man auf der Oberfläche des photographischen Materials eine Beschichtung mit einer Lösung aufbringt, die wenigstens 0,2 G-ew.$ eines Alkalimetallsalzes von Dextransulfat enthält und diese dann auf dem photographischen Material trocknet»The present invention provides a method for improving the surface conductivity of photographic materials Film material, for which purpose a coating with a solution is applied to the surface of the photographic material, which contains at least 0.2% by weight of an alkali metal salt of dextran sulfate and then applied this to the photographic Material dries »
Unter die Bezeichnung "photographisches Filmmaterial", wie sie hier verwendet wird, fallen photographisehe Materialien,As used herein, the term "photographic film material" includes photographic materials
—^5—- ^ 5—
109842/1693109842/1693
"bei denen der Träger ein Kunststoff-Film ist und weiterhin photοgraphische Materialien, bei denen der Träger Papier ist, das mit Oberflächenschichten von Kunststoffmaterial versehen ist."where the carrier is a plastic film and continues to do so photographic materials where the carrier is paper which is provided with surface layers of plastic material.
Das nach dem Verfahren der vorliegenden Erfindung hergestellte photοgraphische Material enthält auf einem Basisträger, der wenigstens an einer Seite mit einer einzigen Emulsionsschicht, einer einzigen Emulsionsschicht und einer .ab deckschicht, einer Vielzahl von Emulsionsschichten oder einer Vielzahl von Emulsionsschichten und einer Abdeckschicht beschichtet ist und der an der äußersten Schicht von irgendeiner dieser Schichten und/oder an der Seite des ■Trägers, die keine Emulsionsschicht trägt, wenn eine Seite nicht beschichtet oder mit einer nicht lichtempfindlichen Schicht beschichtet ist, eine Schicht, die ein Alkalimetallsalz von Dextransulfat enthält.The photographic material produced by the process of the present invention contains on a base support which is coated on at least one side with a single emulsion layer, a single emulsion layer and a cover layer, a plurality of emulsion layers or a plurality of emulsion layers and a cover layer and the on the outermost layer of any of these layers and / or on the side of the support which does not bear an emulsion layer, if one side is uncoated or coated with a non-photosensitive layer, a layer containing an alkali metal salt of dextran sulfate.
Das bevorzugte Alkalimetallsalz von Dextransulfat ist das liatriumsalz, und die Erfindung wird nachfolgend auf die Verwendung von natrium beschrieben, obwohl es klar ist, daß ebenso andere Alkalimetallsolze von Dextransulfat verwendet werden könneno The preferred alkali metal salt of dextran sulfate is the lithium salt and the invention will be described hereinafter with reference to the use of sodium, although it will be understood that other alkali metal salts of dextran sulfate can be used as well, or the like
Dextran ist ein Anhydroglukosepolymerisat, das von zahlreichen Stämmen von leuoonostoc und eng verwandten Bakterien in Saccharose enthaltenden Lösungen gebildet wird»Dextran is an anhydroglucose polymer used by numerous Strains of leuoonostoc and closely related bacteria is formed in solutions containing sucrose »
-4--4-
10984?/ 169310984? / 1693
Die meisten Glukosebindungen sind cc-D-1-6, wobei jedoch in geringerem Ausmaß 1-3 und 1-4 Bindungen ebenso gebildet werden.Most of the glucose bonds are cc-D-1-6, but in to a lesser extent 1-3 and 1-4 bonds are also formed.
Natriumdextransulfat kann dadurch hergestellt werden, daß man Dextran mit Schwefelsäure verestert und das erhaltene Produkt mit Natriumhydroxid oder Natriumcarbonat neutralisiert» Sodium dextran sulfate can be produced in that one esterified dextran with sulfuric acid and the obtained Product neutralized with sodium hydroxide or sodium carbonate »
Vorzugsweise hat das in dem Verfahren der vorliegenden Erfindung verwendete Dextransulfat in der Dextrankette wenigstens einen Sulfatrest pro Glukoseeinheit»Preferably, the dextran sulfate used in the method of the present invention has at least one in the dextran chain one sulfate residue per glucose unit »
Vorzugsweise hat das verwendete Dextransulfat ein Molekulargewicht von über 100 000. Ein Natriumdextransulfat, das besonders in dem Verfahren der vorliegenden Erfindung geeignet ist, wird von Pharmacia AoB0, Upsala, Schweden unter dem Warenzeichen 'Dextran Sulphate 500' auf den Markt gebracht. Diese Verbindung hat ein Molekulargewicht von ungefähr 500 000 und einen Substituierungsgrad in der Dextrankette von wenigstens einem Sulfatrest pro Glukoseeinheit»Preferably the dextran sulfate used has a molecular weight of over 100,000. A sodium dextran sulfate which is particularly useful in the process of the present invention is marketed by Pharmacia AoB 0 , Upsala, Sweden under the trademark 'Dextran Sulphate 500'. This compound has a molecular weight of approximately 500,000 and a degree of substitution in the dextran chain of at least one sulfate residue per glucose unit »
Natriumdextransulfat ist in Y/asser und in wäßrigen Lösungen primärer Alkohole löslich. Vorzugsweise wird jedoch das Natriumdextransulfat auf das photοgraphische Material &us einer wäßrigen Alkohollösung und insbesondere aus einer stark wäßrigen Llethanollöeung, d« h» einer Lösung, die überSodium dextran sulfate is in water and water solutions primary alcohols soluble. However, the sodium dextran sulfate is preferred on the photographic material & us an aqueous alcohol solution and in particular from a strongly aqueous Llethanollöeung, ie "h" a solution that over
BAD ORJGfNAL BAD ORJGfNAL
1 0 9 8 4 7 / 1 F 9 3 . . '1 0 9 8 4 7/1 F 9 3. . '
_ 5 —_ 5 -
80 VoIo^ Methanol enthält, aufgebrachte Es wird vorgezogen, das Hatriumdextransulfat auf das photographische Material aus einer starken wäßrigen Methanollösung zu beschichten, v/eil Wasser, wenn es auf eine Gelatine enthaltende Schicht aufgebracht wird, dazu neigt, solche GeIatineschichten aufzuquellen, und wenn die Schicht sich in einer solchen Bedingung befindet, kann Natriumdextransulfat in diese darunter liegende Schicht eindringen und daher keine ausreichend koherente Außenschicht bilden« Eine stark wäßrige Alkohollösung läßt irgendeine darunter liegende Gelatineschicht nicht in wesentlichem Ausmaß aufquellen« Natriumdextransulfat ist in reinem Methanol oder in anderen Wasser-mischbaren primären Alkoholen nicht löslich, und wenn die wäßrige Alkohollösung zu stark ist, kann das Natriumdextransulfat zur Ausfällung aus der Lösung neigen, und es kann dann eine gleichmäßige koherente Beschichtung von Natriumdextransulfat beim Trocknen nicht erhalten werden« Aus ähnlichen Gründen wird das Vorhandensein von Gelatine in der BeSchichtungszubereitung vorzugsweise vermieden« Contains 80 VoIo ^ methanol, applied It is preferred the sodium dextran sulfate on the photographic material from a strong aqueous methanol solution to coat, v / eil water, if it is on a layer containing gelatin tends to swell such gelatin layers, and when the layer is in such a condition, sodium dextran sulfate can get into it underneath penetrate the lying layer and therefore do not form a sufficiently coherent outer layer «A strongly aqueous alcohol solution does not cause any underlying gelatin layer to swell to any significant extent «Sodium dextran sulfate is in pure methanol or in other water-miscible primary alcohols are not soluble, and if the aqueous alcohol solution is too strong, the sodium dextran sulfate can be used Precipitation from solution tend to be, and there can then be an even coherent coating of sodium dextran sulfate are not obtained on drying «For similar reasons, the presence of gelatin in the coating preparation is preferably avoided«
Wenn das photographische Material auf der einen Seite nicht beschichtet ist und es auf dieser Seite mit Uatriumdextraneulfat beschichtet werden soll, kann dieses aus einer wäßrigen Lösung aufgebracht werden.If the photographic material is not coated on one side and it is coated on this side with sodium dextrane sulfate is to be coated, this can be applied from an aqueous solution.
Das nachfolgende Beispiel dient der Erläuterung der Erfindung .The following example serves to explain the invention.
-6--6-
Ein Streifen aus photοgraphischem Material, der eine einzige Grelatine-SilherhalogeniÄ-Emulsionsschicht und elxie Gelatine-Abdeckschicht an beiden Seiten eines Oellulosetriacetatträgers aufweist, wurde an jeder Abdeckschicht mit einer Lösung beschichtet, die die nachfolgenden Bestandteile enthielt:A strip of photographic material comprising a single grelatin-silver halide emulsion layer and elxie gelatin cover layer on both sides of an oil triacetate support was coated on each cover layer with a solution containing the following ingredients:
Natriumdextransulfat 5 gSodium dextran sulfate 5 g
A (Dextran Sulphate 500, hergestellt von ~ Pharmacia A0B0)A (Dextran Sulphate 500, manufactured by ~ Pharmacia A 0 B 0 )
destilliertes Wasser 100 mldistilled water 100 ml
Methanol 900 mlMethanol 900 ml
Nachdem das Material getrocknet war, erhielt man eine kohärente Schicht von Hatriumdextransulfat über jeder Abdeckschicht. Das Beschichtungsgewicht des Natriumdextransulfats betrug 3 mg/dm „After the material dried, a coherent one was obtained Layer of sodium dextran sulfate over each cover layer. The coating weight of the sodium dextran sulfate was 3 mg / dm "
Dieser beschichtete Streifen und ein ähnlicher Streifen, der nicht mit der lösung von Natriumdextransulfat beschichtet wurde, wurden auf eine relative Feuchtigkeit von 40 fi gebracht, und ihre Widerstandswerte bei- dieser Feuchtigkeit wurden bei einem aufgebrachten Potential von 10 KX gemessen».This coated strip, and a similar strip that had not been coated with the solution of sodium dextran sulfate were brought fi to a relative humidity of 40, and their resistance values examples of this moisture was measured at an applied potential of 10 KX ".
Der mit Hatriumdextran beschichtete Streifen hatte einen Widerstand von 4 x 10 Ohm/cm, während der nicht behandel— te Streifen einen viel höheren Widerstand von 10 Qhnr/em hatte»The strip coated with sodium dextran had one Resistance of 4 x 10 Ohm / cm, during the untreated te strips have a much higher resistance of 10 Qhnr / em would have"
10Ε8427Ί69310Ε8427Ί693
Claims (9)
0,2 Ge\'i.°/a Alkalimetallsalz von Dextransulfat enthält, eine v;ädrige primäre Alkohollösung verwendete6. The method according to any one of the preceding claims, aaäuroh characterized in that as a solution, the at least
0.2 ge \ 'i. % / A alkali metal salt of dextran sulfate contains, a v; v; v; v; primary alcohol solution used
wesentlichen, wit; im vorausgehenden Beispiel beschrieben«9. A method for improving the surface conductivity of photographic film materials according to claim 1, ■ im
essential, wit; described in the previous example «