DE2060106A1 - Concrete building mortar - contg cellulose ether water-retaining agent and tenside wetting agents - Google Patents

Concrete building mortar - contg cellulose ether water-retaining agent and tenside wetting agents

Info

Publication number
DE2060106A1
DE2060106A1 DE19702060106 DE2060106A DE2060106A1 DE 2060106 A1 DE2060106 A1 DE 2060106A1 DE 19702060106 DE19702060106 DE 19702060106 DE 2060106 A DE2060106 A DE 2060106A DE 2060106 A1 DE2060106 A1 DE 2060106A1
Authority
DE
Germany
Prior art keywords
water
pref
content
agent
cellulose
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19702060106
Other languages
German (de)
Inventor
Claus-Peter Dipl-Chem D Dippel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BETONLEICHTBAUKOMBINAT VEB
Original Assignee
BETONLEICHTBAUKOMBINAT VEB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BETONLEICHTBAUKOMBINAT VEB filed Critical BETONLEICHTBAUKOMBINAT VEB
Publication of DE2060106A1 publication Critical patent/DE2060106A1/en
Pending legal-status Critical Current

Abstract

Water-retaining agents (I), pref. water-soluble cellulose ethers, e.g. Me-, Et-, hydroxyethyl-, benzyl-, or carboxymethyl cellulose or their alkali(ne earth) salts, and wetting agents, pref. anionactive, cationactive, amphoteric or non-ionogenic tensides, e.g. alkyl sulphates or sulphonates, alkylaryl or aryl sulphonates, or their alkali salts; fatty acid condensates, ethylene oxide adducts with fatty acids and alcohols, fatty alcohol sulphates, oil sulphates, alkylpolyglycol or alkylphenol ethers and/or polyphosphates, are present in building unit bonding compsns. contg mortar mixt. of binders, concrete aggregates and mixing water, esp. for assembly of light porous silicate concrete units. Pref. content of (I) and (II) depend on binder amt used, and pref. (II) content is less than (I) content. A pref. compsn. contains 5-25% cement, 70-90% SiO2, and 0.5-5% (I) and 0.1-1% (II) and necessary mixing water. Pref extrusion mortar contains a raised amt. binder, less aggregate and K2CO3.

Description

Verbundmasse für Bauteile, insbesondere für Fertigbauteile aus Gessilikatbeton und Verfahren zu deren Herstellung und Verarbeitung Die Erfindung betrifft eine Verbundmasse für Bauteile, insbesondere für die Verbindung von großformatigen Fertigbauteilen aus Gassilikatbeton oder anderen hochporösen Leichtbaustoffen, sowie ein Verfahren zur Herstellung und Verarbeitung dieser Verbundmasse.Composite compound for components, in particular for prefabricated components made of gessilicate concrete and methods for their manufacture and processing. The invention relates to a Composite compound for components, in particular for connecting large-format prefabricated components made of gas silicate concrete or other highly porous lightweight construction materials, as well as a process for the production and processing of this composite material.

Es ist bekannt, für die Verbindung von Bauteilen Mörtel aus Bindemitteln, Zuschlagstoffen und Anmachwasser zu verwenden. Diese bekannten Mörtel haben den Nachteil, daß der Verbund der Bauteile erst nach der Erhärtung des Mörtels eintritt und bis zu diesem Zeit-Punkt nur die Reibung der festen Mörtelbestandteile mit dem Bauteil und die Adhäsionskräfte des Anmachwassers eine gewisse Haftwirkung hervorrufen.It is known to use mortar made from binders for joining components, Use aggregates and mixing water. These well-known mortars have the Disadvantage that the bond between the components only occurs after the mortar has hardened and up to that point only the friction of the solid parts of the mortar with the Component and the adhesive forces of the mixing water cause a certain adhesive effect.

Weiterhin nachteilig ist, daß in Abhängigkeit der Masseverhältnisse des Fugenmörtels und der Bauteile in Verbindung mit deren Kapillarstruktur dem Mörtel eine erhebliche Menge des für den Hydratationsprozeß erforderlichen Anmachwessers entzogen und damit die Endfestigkeit des Mörtels nachteilig beeinflußt wird.Another disadvantage is that depending on the mass ratios the grout and the components in connection with their capillary structure the mortar a significant amount of the gauging water required for the hydration process withdrawn and thus the final strength of the mortar is adversely affected.

Es ist auch bekannt, Teile aus Gassilikatbeton mit einem Mörtel unter Verwendung von PVAC-Zusätzen zu verbinden. Dieser Mörtel weist zwar eine die Erhärtung nicht beeinträchtigende sofortige Haftwirkung auf, beseitigt aber nicht das nachteilige Abwandern des Anmachwassers. Es ist weiterhin bekannt, solche Mörtel mit Zusatzen von wasserlöslichen Celluloseäthern als Wasserrückhaltemittel zu versehen. Diese Mörtel zeigen zwar eine sofortige Haftwirkung und vermindern auch das Abwandern des Anmachwassers, besitzen aber für die Herstellung, Verarbeitung und Festigkeitsentwicklung eine Reihe Nachteile, wie die Verzögerung des Erstarrens und Erhärtens über mehrere Tage, die geringe Benetzbarkeit mit den zu verbindenden Bauteilnen, die einen zusätzlichen Anpreßdruck erforderlich ma@@t, um die Fugendicke einzuhalten, der hohe Anmachwasserbedarf, der nach dem Erstarren und Erhärten zu geringeren Festigkeiten führt sowie ein geringer Mischeffekt beim Mischen und Anmachen des Nörtels. Zur Erreichung einer festen Verbindung zwischen Bauteile und Fugenmörtel ist daher entweder eine breite Fugenausbildung mit Lastauflage oder die Verwendung eines Mörtels flüssiger Konsistenz für dünne Fugen erforderlich. Solche flüssigen Mörtel lassen sich jedoch nicht an senkrechten Fugenflächen verwenden.It is also known to place parts made of gas silicate concrete with a mortar underneath Use of PVAC additives to combine. This mortar shows a hardening immediate adhesive effect that does not impair, but does not eliminate the disadvantageous Migration of the mixing water. It is also known such mortars with Additions of water-soluble cellulose ethers as water retention agents. These mortars show an immediate adhesive effect and also reduce migration of the mixing water, but are used for production, processing and strength development a number of disadvantages, such as the delay in solidification and hardening over several Days, the low wettability with the components to be connected, the additional Contact pressure required ma @@ t in order to maintain the joint thickness, the high mixing water requirement, which after solidification and hardening leads to lower strengths and a lower one Mixing effect when mixing and applying the mortar. To achieve a solid connection there is therefore either a wide joint formation between the components and the grout with load bearing or the use of a mortar of liquid consistency for thin Joints required. However, such liquid mortars cannot be applied to vertical Use joint surfaces.

Es ist überdies bekannt, die Erstarrungs- und Erhärtungszeit solcher Mörtel mit Zusätzen wasserlöslicher Celluloseäther durch die Zugabe von wasserlöslichem Natriumsilikat als Erhärtungsbeschleuniger wieder zu vermindern-. Dadurch wird jedoch die Raumbeständigkeit des Mörtels nachteilig beeinflußt und die zur Verhinderung dieses unerwünschten Nebeneffektes mögliche weitere Zugabe von Mischpolymerisaten wie Vinylchlorid oder Vinylpropionat erhöht den Dosier- und Mischaufwand des Mörtels beträchtlich.It is also known the solidification and hardening time of such Mortar with additions of water-soluble cellulose ethers through the addition of water-soluble To reduce sodium silicate as a hardening accelerator again. This will however adversely affects the stability of the mortar and the prevention this undesirable side effect possible further addition of copolymers like vinyl chloride or vinyl propionate increases the dosing and mixing effort of the mortar considerably.

Die Herstellung solcher Verbundmassen erfolgt durch die Zugabe der im Anmachwasser gelösten fenten oder flüssigen Zusätze am Verarbeitungsort. Nachteilig ist dabei, daß die erforderliche Dosiergenauigkeit am Verarbeitungssort mit eraöhten Aufwendungen verbunden ist und Dosierfehler zu Mischungen führen können, die als Verbundmasse ungeeignet sind. Da solche Dosierfehler aelten sofort erkennbar sind, treten durch die nachträglichen Ausbesserungen aufwendige Nacharbeiten auf.Such composites are produced by adding the Fent or liquid additives dissolved in the mixing water at the place of application. Disadvantageous is while ensuring that the required dosing accuracy at the processing site is associated with increased expenses and dosing errors can lead to mixtures, which are unsuitable as a composite material. Since such dosing errors were immediately recognizable costly rework occurs due to the subsequent repairs.

Der Zweck der Erfindung ist es, die Montage von großformatigen Gassilikatbetonelementen und ähnlichen Bauteilen durch die Verwendung einer ökonomisch günstigen und handhabunssicheren Verbundmasse zu vereinfachen, den Verarbeitungsaufwand zu verringern und damit den Industrialisierungsgrad der Kompletter rungs- und Montagearbeiten zu erhöhen Der Erfindung liegt die Auf zugrunde, zur haftfesten Verbindung von Bauteilen, insbesondere von großformatigen Fertigbauteilen aus Gassilikatbeton, eine Verbundmasse zu entwickeln, die als dünne Klebfuge in jeder Montagelage aufgebracht werden kann, sofort nach dem Zusammenfügen der Bauteile eine Verbundwirkung ausübt und im weiteren einen normalen Hydratationsprozeß ohne Beeinträchtigung der geforderten Endfestigkeit durchläuft.The purpose of the invention is to facilitate the assembly of large-format gas silicate concrete elements and similar components through the use of an economically favorable and safe to handle To simplify composite mass, to reduce the processing effort and thus the To increase the degree of industrialization of the complete work and assembly work Invention is based on the adhesive connection of components, in particular of large-format prefabricated components made of gas silicate concrete to develop a composite mass, which can be applied as a thin adhesive joint in any assembly position, immediately after the joining of the components exerts a composite effect and also a normal hydration process without impairing the required final strength passes through.

Der Erfindung liegt weiterhin die Aufgabe zugrunde, ein Herstellungsverfahren für diese Verbundmasse zu finden, welches die optimale Massenzusammensetzung gewährleistet und Dosierungenauigkeiten ausschließt.The invention is also based on the object of a manufacturing method to find for this composite mass which guarantees the optimal mass composition and excludes metering inaccuracies.

Diese Aufgabe wird erfindungsgemäß wie folgt gelöst : Die Verbundmasse besteht aus einer Mörtelmischung aus Bindemittel, vorzugsweise Zement, einem Zuschlagsteff, vorzugsweise feinkörnigen @@essand, und Anmachwasser sowie einem Wasserrückhaltemittel in Verbindung mit einem Benstzungsmittel, wobei der Anteil des Benstzungsmittels geringer als der Anteil des Wasserrückhaltemittels und der Anteil beider Mittel von der verwendeten Bindemittelmenge abhängig ist.According to the invention, this object is achieved as follows: The composite mass consists of a mortar mixture of binding agent, preferably cement, an aggregate, preferably fine-grained @@ essand, and Mixing water and one Water retention agent in conjunction with a wetting agent, the proportion of the wetting agent is lower than the proportion of the water retention agent and the The proportion of both agents depends on the amount of binder used.

Als Wasserrückhaltemittel finden dabei wasserlösliche Cellulossäther wie Methylcellulose, Äthylcellulose, Oxyäthylcellulose, Benzylcellulose, Carboxymethylcellulose oder deren Alkali- oder Erdalkalisalze Verwendung.Water-soluble cellulose ethers are used as water retention agents such as methyl cellulose, ethyl cellulose, oxyethyl cellulose, benzyl cellulose, carboxymethyl cellulose or their alkali or alkaline earth salts use.

Als Benstzungsmittel finden, einzeln oder im Gemisch, anionenaktive, kationenaktive, amphotere oder nichtiogene Tenside wie Alkylsulfate, Alkylsulfonate, Alkylarylsulfonate, Arylsulfonate oder deren Alkali-Salze: Fettsäurekondensationsprodukte, Äthylenoxidaddukte mit Fettsäuren und Alkoholen, Fettalkoholsulfate, Ölsulfate, Alkylpolyglykoläther, Alkylphenoläther oder Polyphosphate Verwendung.As wetting agents, individually or in a mixture, anion-active, cation-active, amphoteric or non-ionogenic surfactants such as alkyl sulfates, alkyl sulfonates, Alkylarylsulfonates, arylsulfonates or their alkali salts: fatty acid condensation products, Ethylene oxide adducts with fatty acids and alcohols, fatty alcohol sulfates, oil sulfates, Use of alkyl polyglycol ethers, alkyl phenol ethers or polyphosphates.

Diese Verbundmasse ist bei einem erhöhten Anteil an Bindmittel, einem verringerten Anteil an Zuschlagstoff wind eine Zusatz von Kaliumcarbonat auch als Auspreßmörtel anwendbar.This composite mass is with an increased proportion of binder, a reduced proportion of aggregate wind an addition of potassium carbonate as well Grouting mortar can be used.

Die vorzugsweise Herstellung dieser Verbundmasse erfolgt durch da. trockene Mischen von Bindemittel, Zuschlagstoff, Wasserrückhaltemittel und Benetzungsmittel, den Versand disser Trockenmasse ia luftdichter Verpackung und die Augabe von Anmachwasser am Verarbeitungsort. Dem Anmachwasser können dabei den Gefrierpunkt herabsetzende chlorid- und sulfatfreie Mittel wie Methylalkohol oder Kaliumcarbonat zugesetzt worden.This composite mass is preferably produced by da. dry mixing of binder, aggregate, water retention agent and wetting agent, the dispatch of dry matter in general airtight packaging and the dispensing of mixing water at the place of processing. The mixing water can reduce the freezing point Chloride-free and sulfate-free agents such as methyl alcohol or potassium carbonate are added been.

Die erfindungsgemäße Verbundmasse erfüllt alle Voraussetzungen einer Verbundmasse für Gassilikatbetonelemente. Neben einer handhabunssichern Anwendung und der möglichen Ausbildung von der Genauigkeit solcher Elemente entsprechenden dünnen Fugen ist von besonderen Vorteil, daß die zur Anwendung kommenden Zusätze den Preis der Mörtelmischung nicht wesentlich verändert und ihre Verwendung keine besonderen arbeits- oder gesundheitsschutztechnischen Vorkehrungen erfordert.The composite mass according to the invention meets all the requirements of a Composite compound for gas silicate concrete elements. In addition to an application that is safe to use and the possible training of the accuracy of such elements thin joints is of particular advantage that the additives used the price of the mortar mix did not change significantly and its use did not change any requires special occupational health and safety precautions.

Die Erfindung soll nachstehend an einem Ausführungsbeispiel näher erläutert werden.The invention is to be described in more detail below using an exemplary embodiment explained.

Die Verbundmasse ist aus 20,0 % Zement 76,0 % Kiessand 3,2 % Carboxymethylcellulose und 0,8 % Alkylarylsulfonat zusammengesetzt.The composite mass consists of 20.0% cement 76.0% gravel sand 3.2% carboxymethyl cellulose and 0.8% alkyl aryl sulfonate.

Diese Bestandteile werden nach der Trockmung des Kiessandes dosiert und trocken gemischt. Durch eine geeignete luftdichte Verpackung ist diese Trockenmasse lange Zeit haltbar. Am Verarbeitungsort wird durch die Zagabe von Anmachwasser bis zum Erreichen der gewünschten Konsistens die Weiterverrarbeitung ermöglicht.These components are dosed after the gravel sand has dried and dry mixed. With suitable airtight packaging, this is dry matter durable for a long time. At the place of processing, mixing water is mixed up to enables further processing to achieve the desired consistency.

Unter Verwendung eines erhöhten Zementanteiles und einem Zusatzes von Kaliumcarbonat ist die Verbundmasse auch als Auspreßmärtel bei der Komplattierung von Gassilikatbetonteilen zu raumgroßen Elementen anwendbar.Using an increased proportion of cement and an additive of potassium carbonate, the composite material is also used as an extrusion material for complating Can be used from gas silicate concrete parts to room-sized elements.

Claims (9)

Patentansprüche:Patent claims: 1. Verbundmasse für Bauteile, insbesondere für Fertigbauteile aus Gassilikatbeton, unter Verwendung einer Mörtelmischung aus Bindemitteln, Zuschlagstoffen und Anmachwasser, gekennzeichnet durch einen Gehalt an Wasserrückhaltemitteln in Verbindung mit einem Benetzungsmittel.1. Composite mass for components, in particular for prefabricated components Gas silicate concrete, using a mortar mixture of binders, aggregates and mixing water, characterized by a content of water retention agents in Connection with a wetting agent. 2. Verbundmasse nach Anspruch 1, gekennzeichnet durch die Verwendung von wasserlöslichen Celluloseäthern wie Methylcellulose, Äthylcellulose, Oxyäthylcellulose, Benzylcellulose, Carboxymethylcellulose oder deren Alkali- oder Erdalkalisalze als Wasserrückhaltemittel.2. Composite composition according to claim 1, characterized by the use of water-soluble cellulose ethers such as methyl cellulose, ethyl cellulose, oxyethyl cellulose, Benzyl cellulose, carboxymethyl cellulose or their alkali or alkaline earth salts as Water retention agents. 3. Verbunden nach Anspruch 1, gekennzeichnet durch die Verwendung von anionenaktiven, kationenaktiven, amphoteren oder nichtionogenen Tensiden wie Alkylsulfate, Alkylsulfonate, Alkylarylsulfonate, Arylsulfonate bzw. deren Alkalisalze : Fettsäurekondensationsprodukte, Äthylenoxidaddukte mit Fettsäuren und Alkoholen, fettalkoholsulfate, Ölsulfate, Alkylpolyglykoläther, Alkylphenoläther oder Polyphosphate einzeln oder in Gemisch als Benetzungsmittel.3. Connected according to claim 1, characterized by the use of anion-active, cation-active, amphoteric or nonionic surfactants such as Alkyl sulfates, alkyl sulfonates, alkyl aryl sulfonates, aryl sulfonates or their alkali salts : Fatty acid condensation products, ethylene oxide adducts with fatty acids and alcohols, fatty alcohol sulfates, oil sulfates, alkyl polyglycol ethers, alkyl phenol ethers or polyphosphates individually or as a mixture as a wetting agent. 4. Verbundmasse nach Anspruch 1, dadurch gekennzeichnet, daß der Gehalt des Wasserrückhaltemittels in Verbindung mit dem Benetzungsmittel von der Menge des verwendeten Bindmittels abhängig ist. 4. Composite composition according to claim 1, characterized in that the Content of the water retention agent in connection with the wetting agent of the Amount of binder used is dependent. 5. Verbundmasse nach den Ansprüchen 1 und 4, dadurch gekennzeichnet, daß der Gehalt des Benetzungsmittels geringer als der Gehalt der Wasserrückhaltemittels ist.5. Composite mass according to claims 1 and 4, characterized in that that the content of the wetting agent is less than the content of the water retention agent is. 6. Verbundmasse nach den Ansprüchen 1 bis 5, gekennzeichnet durch eine Zusammensetzung aus 5,0 - 25,0 % Zement 70,0 " 90,0 p Kiessand 0,5 - 5,0 % Wasserrückhaltemittel 0,1 - 1,0 % Benetzungsmittel und dem erforderlichen Anmachwasser. 6. Composite mass according to claims 1 to 5, characterized by a composition of 5.0 - 25.0% cement 70.0 "90.0 p gravel sand 0.5 - 5.0% Water retention agent 0.1 - 1.0% wetting agent and the required mixing water. 7. Verbundmasse nach den Ansprüchen 1 bis 6, gekennzeichnet durch einen erhöhten Anteil an Bindemittel, einen verringerten Anteil an Zuschlagstoff, einen Zusatz von Kaliumcarbonat und die Verwendung als Auspreßmörtel.7. composite material according to claims 1 to 6, characterized by an increased proportion of binding agent, a reduced proportion of aggregate, an addition of potassium carbonate and the use as an extrusion mortar. 8. Verfahren zur Herstellung und Verarbeitung einer Verbundmasse nach den Ansprüchen 1 bis 6, dadurch gekennzeichnet, daß Bindemittel, Zuschlagstoff, Wasserrückhaltemittel und BEnetzungsmittel trocken gemischt, luftdicht verpackt versandt und am Verarbeitungsort durch die Zugabe von Anmachwasser verarbeitungsfähig gemacht wird.8. Method for the production and processing of a composite mass according to claims 1 to 6, characterized in that binding agent, aggregate, Water retention agent and wetting agent mixed dry, packed airtight dispatched and ready for use at the place of application by adding mixing water is made. 9. Verfahren nach Anspruch 8, dadurch gekennzeichnet, daß dem Anmachwasser den Gefrierpunkt herabsetzende chlorid- und sulfatfreie Mittel wie Methylalkohol, Kaliumcarbonat u. a. zugesetzt werden.9. The method according to claim 8, characterized in that the mixing water freezing point reducing agents free from chloride and sulfate such as methyl alcohol, Potassium carbonate and others can be added. In Betracht gezogene Druckschriften: DT-PS Nr. 1 158 430 DT-OS Nr. 1 471 110 Considered publications: DT-PS No. 1 158 430 DT-OS No. 1 471 110
DE19702060106 1970-09-29 1970-12-07 Concrete building mortar - contg cellulose ether water-retaining agent and tenside wetting agents Pending DE2060106A1 (en)