DE2031130A1 - Flexible lubricant material - for use on belts - Google Patents

Flexible lubricant material - for use on belts

Info

Publication number
DE2031130A1
DE2031130A1 DE19702031130 DE2031130A DE2031130A1 DE 2031130 A1 DE2031130 A1 DE 2031130A1 DE 19702031130 DE19702031130 DE 19702031130 DE 2031130 A DE2031130 A DE 2031130A DE 2031130 A1 DE2031130 A1 DE 2031130A1
Authority
DE
Germany
Prior art keywords
weight
sliding material
sliding
frictional forces
flexible sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19702031130
Other languages
German (de)
Other versions
DE2031130C3 (en
DE2031130B2 (en
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed filed Critical
Priority to DE19702031130 priority Critical patent/DE2031130A1/en
Publication of DE2031130A1 publication Critical patent/DE2031130A1/en
Publication of DE2031130B2 publication Critical patent/DE2031130B2/de
Application granted granted Critical
Publication of DE2031130C3 publication Critical patent/DE2031130C3/de
Granted legal-status Critical Current

Abstract

flexible web-shaped lubricant materials comprises fibre support and coating consisting of lubricant and binders, i.e. of 40-80% molybdenum disulphide and/or graphite, 98% of which passes through a 0.04 mm. mesh sieve, 10-59% (co)polymers of vinylidene chloride and vinyl chloride and/or methacrylic acid and acrylic acid 1-8C alkyl esters, contg. as well as esters, 1-25 mol.% co-monomers with reactive groups, 1-30% thermosetting resins being added to the binder.

Description

Vereinigte Schmirgel-und Maschinen-Fabriken AG Flexibles GLeitband Bei zahlreichen technischen Bewegungsvorgängen treten oft erhebliche Reibungswiderstände und damit Energieverluste au£. Insbesondere bei Sohlei£mascbinen in den auf detn Markt befindLichen verschiedenen Ausführungsformen ist es erforderlich, die Reibung der Rückseite der Schleifbänder an den maschinell vorgesehenen Andruckvorrichtungen, z. B. an S¢bleifschuhen und Druckbalken, weitgehend herabzusetzen.Vereinigte Schmirgel-und Maschinen-Fabriken AG Flexible guide tape Considerable frictional resistance often occurs in numerous technical movement processes and thus energy losses from £. Especially with Sohlei £ mascbinen in the on detn In the various embodiments on the market, it is necessary to reduce the friction the back of the sanding belts on the machine-provided pressure devices, z. B. on S ¢ lead shoes and pressure bars to largely reduce.

Die Verminderung des Reibungswiderstandes an diesen kritischen Maschinenteilen gewährleistet einen störungsfreieren Maschinenlauf, eine Verlängerung der Stand zeit der verwendeten Schleifbänder, eine Herabsetzung der Energieaufnahme der MAschine, eine Verbesserung der Oberflächenbeschaffenheit der bearbeiteten Werkstücke und eine niedrigere Temperatur an den Reibungsflächen. The reduction of the frictional resistance on these critical machine parts ensures a trouble-free machine run, an extension of the stand time of the grinding belts used, a reduction in the energy consumption of the machine, an improvement in the surface finish the edited Workpieces and a lower temperature on the friction surfaces.

Zur Verminderung des Reibungswiderstandes werden deshalb an den Reibungsflächen MateriaLien eingesetzt, die einen geringen Reibungskoeffizienten besitzen oder bewirken. Solche Materialien sind entweder zwischen die Reibungsflächen eingebrachte Schmiermittel, oder man rüstet die reibenden Flächen oder wenigstens eine der reibenden Flächen, z. B. die Rückseite von Schleifbändern, mit einem Überzug aus, der einen niedrigen Reibungskoeffizienten aufweist und z. B. ganz oder teilweise aus anorganischen Verbindungen, wie Graphit, Talcum, Molybdändisulfid oder Metallstearaten, sowie aus organischen Verbindungen, z. 3. Polymeren, wie Polytetrafluoräthylen, PoLyamiden uswO besteht. To reduce the frictional resistance, therefore, on the friction surfaces Materials used that have or cause a low coefficient of friction. Such materials are either lubricants introduced between the friction surfaces, or one prepares the rubbing surfaces or at least one of the rubbing surfaces, z. B. the back of sanding belts, with a coating that has a low Has coefficient of friction and z. B. wholly or partly from inorganic compounds, such as graphite, talc, molybdenum disulfide or metal stearates, as well as organic Connections, e.g. 3. Polymers such as polytetrafluoroethylene, polyamides, etc.

Ein solcher Überzug kann in der vielfältigsten Weise aufgebracht werden, Besonders vorteilhaft ist es, den Überzug in Form eines Flächengebildes vorzunehmen, das auf die eine der aufeinander reibenden Oberflächen aufgebracht wird. Such a coating can be applied in the most varied of ways It is particularly advantageous to have the coating in the form of a sheet-like structure make that applied to one of the surfaces rubbing against each other will.

Dieses Flächengebilde kann z. B. duroh Aufspannen oder durch Aufkleben, wie z. B. aif Schleifschube oder Druckbalken befestigt werden.This fabric can, for. B. by clamping or by gluing, such as B. aif grinding pusher or pressure beam can be attached.

Als Trägermaterialien für derartige flexible Flächengebilde werden Gewebe aus natürlichen und synthetischen Basern verwendet und als Bindemittel für den eingesetzten Gleitstoff Polymerisate oder Copolymerisate. As carrier materials for such flexible flat structures Tissues made from natural and synthetic bases and used as binders for the lubricant used, polymers or copolymers.

Es hat sich gezeigt, daß die Flächengebilde zur Verminderung von Reibungskräften bei starken Belastungen, z. 3. It has been shown that the fabrics to reduce Frictional forces under heavy loads, e.g. 3.

bei Schle.ifprozessen mit hobem Andruck und insbesondere bei Dauerbelastung durch die dann auftretende stärkere Wärmeentwicklung eine verminderte Standzeit haben. Je höher die Be-Lastung der mit Gleitmittel und Bindemittel beschichteten Flächen ist, umso kürzer ist die Haltbarkeit des verwendeten Gleitbelages.for grinding processes with high pressure and especially with continuous load a reduced service life due to the stronger heat development that then occurs to have. The higher the load on those coated with lubricants and binders Surfaces, the shorter the shelf life of the sliding coating used.

Der Erfindung liegt die Aufgabe zugrunde, einen Gleitbelag mit niedrigem Reibungskoeffizienten zu schaffen, der auch unter extremen Belastungen eine verlängerte Standzeit ergibt. The invention is based on the object of a sliding coating with low To create a coefficient of friction that is extended even under extreme loads Tool life results.

Gelöst wird die Aufgabe dadurch, daß als Gleitmittel 40 bis 80 Gew.-% - vorzugsweise 50 bis 70 Gew.- - bezogen auf den Festkörpergehalt der gesamten Beschichtungsmasse -I4olybdändisuLfid- und/oder Graphitpulver in einer Korngrößenverteilung verwendet werden, die so beschaffen ist, daß 98 Gew.- durch ein Sieb mit der lichten Maschenweite von 0,04 mm (nach DIN 4188) hindurchgehen und daß als BindemitteL 10 bis 59 Gew.-% - vorzugsweise 20 bis 50 Gew.-% Polymere und/oder Copolymere des Vinylidencblorids und Vinylchloride und/oder der Methacrylsäure- und Acrylsäurealkylester mit Alkylgruppen von 1 bis 8, vorzugsweise von 2 bis 6 C-Ätomen verwendet werden, die neben den Estern 1 bis 25 Mol-% Comonomere mit reaktiven Gruppen, insbesondere mit freien Carboxyl-, Hydroxyl-, Amin- und Amidgruppen enthalten und daB dem Bindemittel 1 bis 30 Gew.-% - vorzugsweise 10 bis 20 Gew.-% - bezogen auf den Festkörpergehalt der gesamten Beschichtungsmasse - wärmehärtender Harze aus der Gruppe der Formaldehyd-Kondensationsprodukte mit Phenol, Harnstoff und Nelamin allein oder in Mischung zugesetzt werden. The object is achieved in that 40 to 80 wt .-% as a lubricant - preferably 50 to 70 wt. - based on the solids content of the entire coating composition -I4olybdenisulfid- and / or graphite powder used in a grain size distribution which is such that 98 wt .- through a sieve with the clear mesh size of 0.04 mm (according to DIN 4188) and that 10 to 59% by weight - preferably 20 to 50% by weight of polymers and / or copolymers of vinylidene chloride and vinyl chlorides and / or the methacrylic acid and acrylic acid alkyl esters with alkyl groups from 1 to 8, preferably from 2 to 6, carbon atoms are used, in addition to the esters 1 to 25 mol% comonomers with reactive groups, especially with free Contain carboxyl, hydroxyl, amine and amide groups and that the binder 1 up to 30% by weight - preferably 10 to 20% by weight - based on the solids content of the entire coating composition - thermosetting resins from the group of formaldehyde condensation products with phenol, urea and nelamine can be added alone or as a mixture.

Die verwendeten Bindemittel oder Gemische verschiedener Bindemitteltypen müssen zur Erzielung eines niedrigen Reibungswiderstandes auch ohne den Zusatz des eigentlichen Gleitmittels einen niedrigen Reibungskoeffizienten besitzen. The binders used or mixtures of different types of binders must to achieve a low frictional resistance without the addition of the actual lubricants have a low coefficient of friction.

Es wurde gefunden, daß die gewünschten günstigen Sebmiereigensohaften des Bindemittels erzielt werden, wenn man von Polymeren und/oder Oopolymeren des Vinyldenchlorids, der Nethacrylsäure oder Aorylsäure und deren Ester ausgeht, wobei vorteilhaft die wäßrigen Dispersionen bzw. deren Mischungen verwendet werden.It has been found that the desired beneficial sebum properties of the binder can be achieved if one of polymers and / or copolymers of the Vinyldene chloride, the methacrylic acid or aoryl acid and their esters starts, with the aqueous dispersions or mixtures thereof are advantageously used.

Für die Veresterung der Methacrylsäure und Acrylsäure werden primäre aliphatisobe Alkohole mit 1 bis 8 C-Atomen, vorzugsweise mit q bis 6 C-Atomen eingesetzt. For the esterification of methacrylic acid and acrylic acid are primary aliphatic alcohols with 1 to 8 carbon atoms, preferably with q to 6 carbon atoms, are used.

Die Polymerisate - ausgehend von den Monomeren -enthalten neben den Estern Comonomere mit reaktiven Gruppen, insbesondere mit freien Carboxylgruppen, freien Hydroxylgruppen sowie freien Amin- und Amidgruppen. The polymers - starting from the monomers - contain, in addition to the esters, comonomers with reactive groups, in particular with free carboxyl groups, free hydroxyl groups and free amine and amide groups.

Die geforderte bobe Wärmestandfestigkeit, die mit den thermoplastischen Polymerisaten und Copolymerisaten allein nicht zu erzielen ist, erreicht man durch den Zusatz von 1 bis 30 Gew.-%, bezogen auf die gesamte Gleitmasse von wärmehärtenden duroplastischen Harzen. Es handelt sich um Phenol-Formaldehyd-Kondensate, um Aminoplaste, vorzugsweise um Harnstoff- und Melamin-Bormaldebyd-Eondensate und verträglichen Misohungen der genannten Harze. The required bobe thermal stability that comes with the thermoplastic Polymers and copolymers alone cannot be achieved, can be achieved by the addition of 1 to 30 wt .-%, based on the total sliding mass of thermosetting thermosetting resins. These are phenol-formaldehyde condensates, aminoplasts, preferably around urea and melamine boron formaldehyde Eondensate and compatible Misohings of the resins mentioned.

Die Gleitmasse, die durob Aufmischung insbesondere der wäßrigen Dispersionen der genannten Polymeren/Copolymeren und der wärmehärtenden Harze mit den Gleitmitteln erzeugt wird, tbesteht - bezogen auf den Festkörpergehalt der Gleitmasse - zu 40 bis 80 Gew.-% aus dem Gleitmittel, zu 1 bis 30 Gew.-% aus wärmehärtenden, duroplastisohen Harzen und zu 10 bia 59 Gew.-% aus den polymeren Bindemitteln. Durch Zusatz von Lösungsmitteln - insbesondere von Wasser und von in Wasser löslichen niedrigen Alkobolen oder Ketonen - wird die gewünschte Viskosität, vorzugsweise 20-30.000 cP, eingestellt. The sliding compound, the durob mixing, especially the aqueous dispersions the said polymers / copolymers and the thermosetting resins with the lubricants is generated, t exists - based on the solids content of the sliding compound - to 40 up to 80% by weight from the lubricant, from 1 to 30% by weight from thermosetting, thermosetting plastics Resins and 10 to 59% by weight of the polymeric binders. By adding Solvents - especially water and water-soluble lower alcohols or ketones - the desired viscosity, preferably 20-30,000 cP, is set.

Die Besobicbtung des bahnförmigen Trägermaterials mit der viskosen Gleitmasse erfolgt in an sich bekannter Weise mit Hilfe geeigneter Rakelvorrichtungen oder durob Walsenauftrag. The coating of the web-like carrier material with the viscous one Slip compound is carried out in a manner known per se with the aid of suitable doctor blade devices or durob whale order.

Durch eine weitere Nachbehandlung auf einem Xalander unter Anwendung von Druck und Wärme kann das in der besobriebenen Weise mit der Gleitmasse beschichtete bahnförmige Gleitband verdichtet und geglättet werden. By applying a further follow-up treatment on a Xalander pressure and heat can do this in the described Way with the Sliding compound coated web-shaped sliding tape are compacted and smoothed.

Es wurde gefunden, daB mit dieser Nachbehandlung durch Kalandrieren eine weitere Steigerung der Standzeit (20 bis 30 %) bem industriellen Einsatz verbunden ist. It was found that with this post-treatment by calendering a further increase in service life (20 to 30%) associated with industrial use is.

Beispiel 1 Ein Baumwollgewebe mit einem Flächengewicht von 400 g/m2 wird mit einer Gleitmasse von folgender Zusammensetzung beschichtet: 100 Gew.-Teile einer 40 Gew.-%igen wäßrigen Polyvinylidenchlorid-Dispersion 10 Gew.-Teile eines wäßrigen Phenol-Formaldehyd-Kondensates (mit 78 Gew.-% Festkörpergehalt), 70 Gew.-Teile Graphitpulver (mindestens 90 Gew.-% O und mindestens 98 Gew.-% Durchgang durch ein Sieb mit 0,04 mm lNW). Example 1 A cotton fabric with a basis weight of 400 g / m2 is coated with a lubricant with the following composition: 100 parts by weight a 40 wt .-% aqueous polyvinylidene chloride dispersion 10 parts by weight of a aqueous phenol-formaldehyde condensate (with 78% by weight solids content), 70 parts by weight Graphite powder (at least 90 wt .-% O and at least 98 wt .-% passage through a Sieve with 0.04 mm lNW).

In zwei Durchgängen durch eine Beschichtungsanlage wird eine 0,8 mm dioke Schicht der beschriebenen Gleitmasse aufgebracht und anschließend unter Anwendung von Druck und Wärme in einem Kalander verdichtet und geglättet. In two passes through a coating system, a 0.8 mm dioke layer of the lubricant described and then applied under Application of pressure and heat in a calender compacted and smoothed.

Unter den gleichen Bedingungen, Sedoob unter Weglassung des Phenol-Formaldehyd-Kondensates der Gleitmasse, wurde ein weiteres Gleitband gefertigt. Under the same conditions, Sedoob omitting the phenol-formaldehyde condensate the sliding compound, another sliding tape was made.

Beide Gleitbänder wurden auf Druokbalken einer Schleifmasohine aufgeklebt und unter gleiohen industriellen 3edingungen geprüft. Both sliding tapes were glued to the pressure bar of a grinding machine and tested under the same industrial conditions.

Während mit dem ersten Gleitband auf den Druckbalken der Maschine 7.000 lfm Spanplatten einwandfrei geschliffen werden konnten, versagte das zweite Gleitband schon nach 5.200 lfm. While with the first sliding tape on the pressure beam of the machine 7,000 running meters of chipboard could be perfectly sanded, the second failed Sliding tape after 5,200 running meters.

Beispiel 2 Mit dem gleichen Aufbau und nach dem gleichen Herstellungsverfahren wie im Beispiel 1 beschrieben, Jedoch unter Weglassung der Nachbehandlung durch Kalandrieren, wurden zwei weitere Gleitbänder gefertigt und der gleichen Prüfung wie im Beispiel 1 unterworfen. Example 2 With the same structure and according to the same manufacturing process as described in Example 1, but omitting the aftertreatment Calendering, two more sliding belts were made and the same test as in Example 1 subjected.

Mit den nicht kalandrierten Gleitbändern wurden folgende Ergebnisse erzielt: Mit dem ersten Gleitband konnten nur 5.400 lfm -mit dem zweiten Gleitband konnten nur 4.000 lfm Spanplatte einwandfrei geschliffen werden. The following results were obtained with the non-calendered sliding belts Achieved: With the first sliding band only 5,400 running meters - with the second sliding band Only 4,000 running meters of chipboard could be perfectly sanded.

Beispiel 3 Ein Baumwollgewebe mit einem Flächengewicht von 300 g/m2 wird mit einer Gleitmasse folgender Zusammensetzung beschichtet: 50 Gew.-Teile einer 50 Gew.-%igen wäßrigen Diapersion eines Copolymerisates aus Polyvinylidenchlrid und Polyvinylchlorid, 50 Gew.-Teile einer 50 Gew.-%igen wäßrigen Dispersion eines Copolymerisates aus Acrylsäurebutylester und Aorylsäureamid mit einem monomeren Verhältnis von 9 : 1. Example 3 A cotton fabric with a basis weight of 300 g / m2 is coated with a lubricant of the following composition: 50 parts by weight of a 50% strength by weight aqueous diapersion of a copolymer of polyvinylidene chloride and polyvinyl chloride, 50 parts by weight of a 50% by weight aqueous dispersion of a Copolymer of butyl acrylate and aoryl amide with a monomeric Ratio of 9: 1.

75 Gew.-Teile Molybdändisulfidpulver (mindestens 98 Gew.-% Durchgang durch ein Sieb mit 0,04 mm LMW) 20 Gew.-Teile eines wäßrigen Melamin-Formaldehyd-Harzes (mit 65 Gew.-% Festkörper) Unter den gleichen Bedingungen wurde ein zweites Gleitband - Jedoch unter Weglassung des Melaminharzes in der Gleitmasse - gefertigt. 75 parts by weight of molybdenum disulfide powder (at least 98% by weight penetration through a sieve with 0.04 mm LMW) 20 parts by weight of an aqueous melamine-formaldehyde resin (with 65% by weight solids) A second sliding tape was created under the same conditions - However, with the omission of the melamine resin in the sliding compound - manufactured.

Nach dem Trocknen, Aushärten und Kalandern der beschichteten Gleitbänder wurde eine Prüfung wie im Beispiel 1 vorgenommen. Während mit dem ersten Gleitband auf den Druckbalken der Schleifmaschine 7.300 lfm Spanplatte einwandfrei geschliffen werden konnten, versagte das zweite Gleitband schon nach 4.800 lfm. After the coated sliding tapes have dried, hardened and calendered a test as in Example 1 was carried out. While with the first sliding tape 7,300 running meters of chipboard sanded perfectly on the pressure beam of the sanding machine could be, the second sliding tape failed after just 4,800 running meters.

Beispiel 4 Ein Zellwollgewebe mit einem Flächengewicht von 260 q/m² wird mit einer Gleitmasse folgender Zusammensetzung beschichtet: 100 Gew.-Teile einer 40 Gew.-%igen Dispersion eines CopolymeriSatee aus Aorylsäureestern (Methyl-, Aethyl-und Butylester im monomeren Verhältnis von 6:2:1) sowie mit Acrylsäure und Acrylsäureamid mit einem monomeren Verhältnis von 9:0,5:0,5 12 Gew.-Teile eines wäßrigen Harnstoff-Formaldehyd-Harzes (mit 75 Gew.-% Festkörpergehalt) und 60 Gew.-Teile Graphitpulver in der beschriebenen Kornverteilung und mit dem festgelegten Kohlenstoffgehalt. Example 4 A cellular wool fabric with a basis weight of 260 q / m² is coated with a lubricant of the following composition: 100 parts by weight a 40% by weight dispersion of a copolymer satee from aoryl acid esters (methyl, Ethyl and butyl esters in a monomeric ratio of 6: 2: 1) and with acrylic acid and Acrylic acid amide with a monomeric ratio of 9: 0.5: 0.5 12 parts by weight of a aqueous urea-formaldehyde resin (with 75 wt .-% solids content) and 60 parts by weight Graphite powder in the grain size distribution described and with the specified carbon content.

Unter den gleioben Bedingungen wurde ein zweites Gleitband - Jedoch unter Weglassung des Harnstoffharzes -in der Gleitmasse gefertigt. Under the same conditions, a second sliding band - However with the omission of the urea resin-manufactured in the sliding compound.

Nach dem Trocknen, Aushärten und Kalandrieren der beschichteten Bänder wurde eine Prüfung - wie im Beispiel 1 beschrieben - vorgenommen. After the coated strips have dried, hardened and calendered a test - as described in Example 1 - was carried out.

Während mit dem ersten Gleitband auf dem Druckbalken der Schleifmaschine 8.800 lfm Spanplatten einwandfrei geschliffen werden konnten, versagte das zweite Gleitband schon nach 5.500 lfm Beispiel 5 Ein Baumwollgewebe mit einem Flächengewicht von 350 g/m2 wird mit einer Gleitmasse folgender Zusammensetzung beschichtet: 100 Gew.-Teile einer 40 Gew.-%igen wäßrigen Dispersion von Polyacrylsäuremethylester (frei von Copolymeren mit reaktiven Gruppen) 12 Gew.-Teile eines wäßrigen rnstoff-Formaldehydharzes (mit 75 Gew.-% Festkörpergebalt) und 60 Gew.-Teile Graphit pulver in der beschriebenen Kornverteilung und mit dem festgelegten C-Gehalt. While with the first sliding tape on the pressure beam of the grinding machine 8,800 running meters of chipboard could be perfectly sanded, the second failed Sliding tape after 5,500 running meters. Example 5 A cotton fabric with a weight per unit area of 350 g / m2 is coated with a slip compound of the following composition: 100 Parts by weight of a 40% strength by weight aqueous dispersion of methyl polyacrylate (free of copolymers with reactive groups) 12 parts by weight of an aqueous formaldehyde resin (with 75 wt .-% solids content) and 60 parts by weight of graphite powder in the described Grain distribution and with the specified C content.

Naoh dem Trocknen, Härten und Kalandrieren wurde mit dem Gleitmaterial eine Prüfung, wie im Beispiel 1 beschrieben, vorgenommen, es konnten mit diesem Gleitband auf den Druokbalken der Schleifmaschine 4.200 lfm Spanplatten geschliffen werden. After drying, hardening and calendering, the sliding material was used a test as described in Example 1, carried out, it could with this Sliding tape sanded on the pressure bar of the sanding machine 4,200 running meters of chipboard will.

Claims (4)

P a t e n t a n s p r ü c h eP a t e n t a n s p r ü c h e 1. Flexibles bahnförmiges Gleitmaterial zur Verminderung von Reibungskräften, -bestehend aus einer Gewebeunterlage aus natürlichen oder synthetischen Fasern und einer Beschichtung aus Gleitmitteln und Bindemitteln, dadurch gekennzeichnet, daß als Gleitmittel 40 bis 80 Gew.-% - vorzugsweise 50 bis 70 Gew.-% - bezogen auf den Festkörpergehalt der gesamten Beschichtungsmasse - Molybdändisulfid- und/oder Graphitpulver in einer Korngrößenverteilung verwendet werden, die so bescbaffen ist, daß 98 Gew.- durch ein Sieb mit der lichten Masebenweite von 0,04 mm (nach DIM 4188) bindurobgeben und daß als Bindemittel 10 bis 59 Gew.-% - vorsugsweise 20 bis 50 Gew.-% Polymere und/oder Copolymere des Vinylidenchlorids und Vinylohlorids undXoder der Methacrylsäure - und Acrylsäurealkylester mit Alkylgruppen von 1 bis 8, vorzugsweise von 2 bis 6 O-Atomen verwendet werden, die neben den Estern 1 bis 25 Mol% Comonomere mit reaktiven Gruppen, insbesondere mit freien Carboxyl-, Hydroxyl-, Amin- und Amidgruppen enthalten und daß dem Bindemittel 1 bis 30 Gew.-% - vorzugsweise 10 bis 20 Gew.-% -bezogen auf den Festkörpergehalt der gesamten Besobichtungamasse - wärmehärtender Harze aus der Gruppe der Formaldehyd-Kondensationsprodukte mit Phenol, Harnstoff und Melamin allein oder in Misobung zugesetzt werden.1. Flexible sheet-like sliding material to reduce frictional forces, -consisting of a fabric backing made of natural or synthetic fibers and a coating of lubricants and binders, characterized in that as a lubricant 40 to 80 wt .-% - preferably 50 to 70 wt .-% - based on the Solid content of the entire coating material - molybdenum disulphide and / or graphite powder be used in a grain size distribution which is so designed that 98 wt. Pass through a sieve with an internal width of 0.04 mm (according to DIM 4188) and that as a binder 10 to 59% by weight - preferably 20 to 50% by weight of polymers and / or copolymers of vinylidene chloride and vinyl chloride and X or methacrylic acid - And acrylic acid alkyl esters with alkyl groups from 1 to 8, preferably from 2 to 6 O atoms are used, in addition to the esters 1 to 25 mol% comonomers with reactive Contain groups, especially with free carboxyl, hydroxyl, amine and amide groups and that the binder is 1 to 30% by weight, preferably 10 to 20% by weight on the solids content of the entire coating composition - thermosetting resins from the group of formaldehyde condensation products with phenol, urea and melamine can be added alone or in misery. 2. Flexibles bahnförmiges Gleitmaterial zur Verminderung von Reibungskräften nach Anspruch 1, dadurch gekennzeichnet, daß die Polymeren und/oder Copolymeren des Vinylidenchlorids und Vinylchlorids und/oder der vernetzbaren Polymethacrylate und Polyaorylate in Form ibrer 40 bis 60 Gew.-%igen wäßrigen Dispersionen verwendet werden.2. Flexible sheet-like sliding material to reduce frictional forces according to claim 1, characterized in that the polymers and / or copolymers of vinylidene chloride and vinyl chloride and / or crosslinkable polymethacrylates and polyaorylates are used in the form of other 40 to 60% strength by weight aqueous dispersions will. 3. Flexibles bahnförmiges Gleitmaterial zur Verminderung von Reibungskräften nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die wärmehärtenden Pbenol-, Harnstoff- und Melamin-Formaldehyd-Kondensationsprodukte mit einem Molverbältnis von 1:1,2 bis 1:2,5, vorzugsweise von 1:1,5 bis 1:2,0 in Form ihrer 40 bis 80 Gew.-%igen wäßrigen Lösungen mit einer Wasserverträglichkeit von 100 bis 500 % - vorzugsweise von 200 bis 400 % - verwendet werden.3. Flexible sheet-like sliding material to reduce frictional forces according to claim 1 and 2, characterized in that the thermosetting Pbenol-, urea- and melamine-formaldehyde condensation products with a molar ratio of 1: 1.2 up to 1: 2.5, preferably from 1: 1.5 to 1: 2.0 in the form of their 40 to 80% strength by weight aqueous Solutions with a water tolerance of 100 to 500% - preferably 200 up to 400% - can be used. 4. Flexibles bahnförmiges Gleitmaterial zur Verminderung von Reibungskräften nach Anspruch 1 bis 3, dadurob gekennzeichnet, daB das bahnförmige Gleitmaterial einer Naobbehandlung unter Anwendung von Druck und Wärme unterworfen wird.4. Flexible sheet-like sliding material to reduce frictional forces according to claim 1 to 3, characterized in that the sheet-like sliding material is subjected to Naob treatment using pressure and heat.
DE19702031130 1970-06-24 1970-06-24 Flexible lubricant material - for use on belts Granted DE2031130A1 (en)