DE202018003451U1 - eraser - Google Patents
eraser Download PDFInfo
- Publication number
- DE202018003451U1 DE202018003451U1 DE202018003451.7U DE202018003451U DE202018003451U1 DE 202018003451 U1 DE202018003451 U1 DE 202018003451U1 DE 202018003451 U DE202018003451 U DE 202018003451U DE 202018003451 U1 DE202018003451 U1 DE 202018003451U1
- Authority
- DE
- Germany
- Prior art keywords
- eraser
- plasticizer
- weight
- etcher
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Radierer zum Entfernen von Abstrichen von Schreib-, Mal- und/ oder Zeichengeräten aufweisend mindestens ein Bindemittel und mindestens einen Weichmacher, dadurch gekennzeichnet, dass der Radierer mindestens einen Weichmacher in Form von Pentaerythritoltetravalerat aufweist.An eraser for removing smears from writing, painting and / or drawing instruments comprising at least one binder and at least one plasticizer, characterized in that the eraser comprises at least one plasticizer in the form of pentaerythritol tetravalerate.
Description
Die Erfindung betrifft einen Radierer zum Entfernen von Abstrichen von Schreib-, Mal- und/oder Zeichengeräten aufweisend mindestens ein Bindemittel und mindestens einen WeichmacherThe invention relates to an eraser for removing smears from writing, painting and / or drawing instruments comprising at least one binder and at least one plasticizer
Derartige Radierer zum Entfernen von Abstrichen von Schreib-, Mal- und/oder Zeichengeräten sind prinzipiell aus dem Stand der Technik bekannt.Such erasers for removing smears from writing, painting and / or drawing devices are known in principle from the prior art.
Beispielsweise sind Weich-PVC-Systeme für Radiergummis seit den 1960er Jahren als bekannt anzusehen. Sie bestehen in der Regel aus Polyvinylchlorid (PVC) als Grundpolymer/Bindemittel, das mit Füllstoff gestreckt wird und einem Weichmacher zur Plastifizierung des Bindemittels. Darüber hinaus können noch weitere Bestandteile wie Additive, beispielsweise Farbmittel, Lösungsmittel zur Erreichung spezieller Radiereigenschaften, usw. hinzugefügt werden. Bei derartigen Radierern wurde die Weichmacherkomponente über die Jahre hin immer wieder aufgrund physiologischer Anforderungen ausgetauscht.
Die Herstellung von PVC-Radierern erfolgt in der Regel über eine Verpastung der Komponenten mit angeschlossener Gelierung und Formgebung im Extruder mittels Wärmezufuhr.For example, soft PVC systems for erasers have been known since the 1960s. They are usually made of polyvinyl chloride (PVC) as a base polymer / binder which is stretched with filler and a plasticizer for plasticizing the binder. In addition, other ingredients such as additives, such as colorants, solvents to achieve special erasing properties, etc. may be added. With erasers of this type, the plasticizer component has been replaced over the years repeatedly due to physiological requirements.
The production of PVC erasers is usually done by pasting the components with connected gelation and shaping in the extruder by means of heat.
Allgemein kann festgehalten werden, dass die eingesetzten Weichmacher physiologisch als unbedenklich eingestuft sein sollten, aber auch nach den technischen Eigenschaften, um gute Extrudierbarkeit, leichte und gute Verpastungsfähigkeit, befriedigende Radiereigenschaften und erforderliche Weichheit ausgewählt sein sollten.Generally, it can be said that the plasticizers used should be classified as physiologically safe, but should also be selected according to the technical properties, good extrudability, easy and good pasting ability, satisfactory erasing properties and required softness.
Als Beispiel von physiologisch als unbedenklich eingestuften Weichmachern sei Acetyltributylcitrat (ATBC) genannt. Jedoch hat sich beim Einsatz von ATBC herausgestellt dass die Migration derartiger Weichmacher als zu hoch einzustufen ist.An example of physiologically harmless plasticizers is acetyltributyl citrate (ATBC). However, with the use of ATBC, it has been found that the migration of such plasticizers is considered too high.
Die
Aufgabe der Erfindung ist es daher einen Radierer zu schaffen, der zum einen kostengünstig hergestellt werden kann und zum anderen eine akzeptable Migrationsneigung des Weichmachers aufweist.The object of the invention is therefore to provide an eraser, which can be produced on the one hand cost and on the other hand has an acceptable migration tendency of the plasticizer.
Weiter ist es Aufgabe der vorliegenden Erfindung, dass die technischen Eigenschaften, gute Extrudierbarkeit, leichte und gute Verpastungsfähigkeit, befriedigende Radiereigenschaften und erforderliche Weichheit sichergestellt sind.Further, it is an object of the present invention that the technical properties, good extrudability, easy and good pasting ability, satisfactory erasing properties and required softness are ensured.
Diese Aufgabe wird für einen Radierer zum Entfernen von Abstrichen von Schreib-, Mal- und/oder Zeichengeräten, der mindestens ein Bindemittel und mindestens einem Weichmacher umfasst, dadurch gelöst, dass der Radierer mindestens einen Weichmacher in Form von Pentaerythritoltetravalerat aufweist.This object is achieved for an eraser for removing smears of writing, painting and / or drawing instruments, comprising at least one binder and at least one plasticizer, characterized in that the eraser comprises at least one plasticizer in the form of pentaerythritol tetravalerate.
Die chemische Strukturformel des Pentaerythritoltetravalerat (PETV) ist in
Der Radierer weist den Vorteil auf, dass das Migrationsverhalten des Weichmachers in einem akzeptablen Bereich bleibt, was derzeit der verzweigten Form der Moleküle des PETV (siehe
Ein geeigneter Migrationstest erfolgt dergestalt, dass ein Teil eines Test-Radierers in Kontakt mit einem möglichen Reaktionspartner gebracht und gegen den Reaktionspartner gedrückt wird. Als mögliche Reaktionspartner dienen unter anderem Polystyrol, Polyethylen, Polypropylen und Bleistiftlacke. Gleichzeitig wird eine Vergleichsprobe erstellt, bei der ein Teil eines handelsüblichen Radierers mit einem Weichmacher in Form von Alkansulfonsäurephenylester ebenfalls in Kontakt mit einem gleichartigen Reaktionspartner gebracht und gegen den Reaktionspartner gedrückt wird.
Die Testanordnungen werden auf ca. 50°C erwärmt und nach unterschiedlichen Testzeiträumen die Kontaktflächen des Teils des Test-Radierers mit dem Reaktionspartner visuell auf Veränderungen begutachtet und mit den Kontaktflächen des handelsüblichen Radierers verglichen. Zeigt sich, dass die Veränderung der Kontaktfläche des Test-Radierers in etwa vergleichbar ist zu Veränderungen an den Kontaktflächen des handelsüblichen Radierers, ist der Test bestanden.A suitable migration test is performed by placing a portion of a test eraser in contact with a potential reactant and pressing it against the reactant. Possible reactants include polystyrene, polyethylene, polypropylene and pencil varnishes. At the same time, a comparative sample is prepared in which a part of a commercial eraser with a plasticizer in the form of alkanesulfonic acid phenyl ester is also brought into contact with a similar reaction partner and pressed against the reactants.
The test arrangements are heated to about 50 ° C and examined after different test periods, the contact surfaces of the part of the test eraser with the reactants visually for changes and compared with the contact surfaces of the commercial eraser. If it is found that the change in the contact area of the test eraser is roughly comparable to changes in the contact surfaces of the commercial eraser, the test is passed.
Ein Radierer enthaltend PETV als alleinigen Weichmacher erfüllt alle oben genannten Anforderungen und ist besonders kostengünstig herstellbar. An eraser containing PETV as sole plasticizer meets all the above requirements and is particularly inexpensive to produce.
Bevorzugte Ausführungsformen und vorteilhafte Weiterbildungen des Radierers sind nachfolgend erläutert.Preferred embodiments and advantageous developments of the eraser are explained below.
Insbesondere weist der Radierer einen Gehalt an dem mindestens einen Weichmachers im Bereich von 20 bis 60 Gew.-% auf, wobei mindestens 10 Gew.-% und maximal 60 Gew.-% des Radierers durch das Pentaerythritoltetravalerat gebildet sind.In particular, the eraser has a content of the at least one plasticizer in the range of 20 to 60 wt .-%, wherein at least 10 wt .-% and at most 60 wt .-% of the eraser are formed by the pentaerythritol tetravalerate.
Durch ein Verschneiden des PETV mit mindestens einem weiteren Weichmacher kann das Migrationsverhalten signifikant weiter verringert werden. Bevorzugt weist der Radierer neben dem Pentaerythritoltetravalerat mindestens einen weiteren Weichmacher in einer Menge von 0 bis 30 Gew.-% auf, wobei sich in Summe
Der mindestens eine weitere Weichmacher ist in einer besonders bevorzugten Weiterbildung des Radierers durch mindestens ein epoxidiertes Pflanzenöl gebildet. Als epoxidiertes Pflanzenöl hat sich hier insbesondere die Verwendung von epoxidiertem Sojabohnenöl (ESBO) und/oder epoxidiertem Leinöl bewährt. Die Kombination des PETV mit ESBO hat sich als besonders geeignet erwiesen, eine Migration des Weichmachers an eine Oberfläche des Radierers zu verringern.The at least one further plasticizer is formed in a particularly preferred embodiment of the eraser by at least one epoxidized vegetable oil. As epoxidized vegetable oil, the use of epoxidized soybean oil (ESBO) and / or epoxidized linseed oil has proven particularly useful. The combination of PETV with ESBO has been found to be particularly suitable for reducing migration of the plasticizer to a surface of the eraser.
Der Radierer weist weiterhin bevorzugt mindestens ein Bindemittel auf aus der Gruppe umfassend Polyvinylchlorid (PVC), Polyvinylacetat (PVAc), Polyolefine. Das PVC ist dabei eines der billigsten Polymere, die am Markt erhältlich sind.The eraser preferably further comprises at least one binder from the group comprising polyvinyl chloride (PVC), polyvinyl acetate (PVAc), polyolefins. The PVC is one of the cheapest polymers available on the market.
Weiterhin weist der Radierer vorzugsweise mindestens einen anorganischen Füllstoff auf, wie beispielsweise Kreide (Calciumcarbonat), Bimsmehl, Kaolin, Glasmehl, Ton, Talkum, usw. Dabei kann in dem Radierer lediglich ein anorganischer Füllstoff oder in Kombination können zwei oder mehrere anorganische Füllstoffe enthalten sein.Further, the eraser preferably has at least one inorganic filler such as chalk (calcium carbonate), pumice, kaolin, glass flour, clay, talc, etc. Here, the eraser may contain only an inorganic filler or in combination may contain two or more inorganic fillers ,
In einer bevorzugten Ausführungsform des Radierers weist dieser weiterhin mindestens ein Additiv auf, insbesondere aus der Gruppe umfassend Farbmittel, Wachse, Öle, Emulgatoren, Stabilisatoren, Lösemittel. Die Farbmittel können dabei anorganische Pigmente, wie Titanoxid, und/oder organische Pigmente umfassen.In a preferred embodiment of the eraser, this further comprises at least one additive, in particular from the group comprising colorants, waxes, oils, emulsifiers, stabilizers, solvents. The colorants may include inorganic pigments, such as titanium oxide, and / or organic pigments.
Besonders bewährt hat sich ein Radierer, der sich wie folgt zusammensetzt:
wobei 0 bis 30 Gew.-% des Radierers durch mindestens ein epoxidiertes Pflanzenöl gebildet sind, und
wobei sich in Summe
wherein 0 to 30 wt .-% of the eraser are formed by at least one epoxidized vegetable oil, and
in total
Bevorzugt weist der Radierer dabei Pentaerythritoltetravalerat in einer Menge von 10 bis 30 Gew.-% auf und den mindestens einen weiteren Weichmacher in Form von epoxidiertem Pflanzenöl in einer Menge von 10 bis 30 Gew.-% auf. So ist ein ausgewogenes Verhältnis zwischen geringen Kosten und ausgezeichneten Migrationseigenschaften erreicht.The eraser preferably has pentaerythritol tetravalerate in an amount of from 10 to 30% by weight and the at least one further plasticizer in the form of epoxidized vegetable oil in an amount of from 10 to 30% by weight. This achieves a balance between low costs and excellent migration characteristics.
Es hat sich in überraschender Weise gezeigt, dass durch die Verwendung von Pentaerythritoltetravalerat (PETV, CAS.no.: 15834-04-5) als erste Weichmacherkomponente, kombiniert insbesondere mit epoxidiertem Sojabohnenöl (ESBO) als zweite Weichmacherkomponente, die Aufgabe mit signifikant guten Ergebnissen gelöst wird.It has surprisingly been found that the use of pentaerythritol tetravalerate (PETV, CAS.no .: 15834-04-5) as the first plasticizer component, combined in particular with epoxidized soybean oil (ESBO) as the second plasticizer component, performs the task with significantly good results is solved.
Epoxidiertes Sojabohnenöl ist ein hochmolekularer Weichmacher, durch welchen die bestehende Migrationsneigung des Pentaerythritoltetravalerat noch deutlich verringert wird. Epoxidized soybean oil is a high-molecular-weight plasticizer, which significantly reduces the existing migration tendency of pentaerythritol tetravalerate.
Zudem hat es sich in überraschender Weise gezeigt, dass die Radiereigenschaften und damit erzielte Radierergebnisse der erfindungsgemäßen Radierer vergleichbar sind mit denen von Radierern mit wesentlich teureren Weichmachern.In addition, it has surprisingly been found that the erasing properties and thus achieved erasing results of erasers according to the invention are comparable to those of erasers with much more expensive plasticizers.
Ein wichtiger Nebeneffekt ist darin zu sehen, dass sowohl die Pastenherstellung als auch die daran angeschlossene Extrusion in gewohnter Weise bei konstanter Qualität durchgeführt werden kann.An important side effect is the fact that both the paste production and the extrusion connected to it can be carried out in the usual way with constant quality.
Als Maß für die Radierbarkeit bzw. Radierfähigkeit wird im Sinne der Erfindung die weitgehende Entfernung von Bleistiftabstrichen auf Medien verstanden, wobei die Resteinfärbung des Mediums ein Maß für die Radierleistung darstellt.As a measure of the erasability or erasability is understood in the context of the invention, the substantial removal of pencil smears on media, the residual coloring of the medium is a measure of the erasing performance.
Mit nachfolgenden Rahmenbeispielen werden bevorzugte Zusammensetzungen des erfindungsgemäßen Radierers näher erläutert.
Rahmenbeispiel 1
Mit mindestens einem den oben aufgeführten Bindemitteln in Kombination mit den Weichmachern Pentaerythritoltetravalerat und epoxidiertem Pflanzenöl, insbesondere epoxidiertem Sojabohnenöl, kann ein besonders günstiges Weichmacher- Migrationsverhalten erreicht werden. Das bevorzugt eingesetzte Bindemittel ist PVC, da mit diesem Bindemittel die besten Ergebnisse erzielt werden, um die gestellte Aufgabe zu lösen, insbesondere hinsichtlich der Radierfähigkeit und des Migrationsverhaltens des Weichmachers. Außerdem können dadurch die Herstellungskosten des Radierers minimiert werden.With at least one of the binders listed above in combination with the plasticizers pentaerythritol tetravalerate and epoxidized vegetable oil, in particular epoxidized soybean oil, a particularly favorable plasticizer migration behavior can be achieved. The preferred binder used is PVC, since with this binder the best results are achieved in order to achieve the stated object, in particular with regard to the erasability and the migration behavior of the plasticizer. In addition, the manufacturing cost of the eraser can be minimized thereby.
Der erfindungsgemäße Radierer soll nachfolgend durch folgende Rezepturbeispiele näher dargestellt werden.
Rezepturbeispiel 1
Hergestellt kann ein derartiger Radierer beispielsweise in folgender Weise werden.For example, such an eraser can be made in the following manner.
HerstellungsbeispielPreparation example
In einem Rührer werden PVC-Pulver, der Weichmacher und ggf. eingesetzte Füllstoffe und Additive zu einem homogenen Plastisol vermischt.
Das dabei erhaltene Plastisol wird mittels Doppelschneckenextruder geliert und über eine Düse zu einem endlosen Strang geformt.In a stirrer, PVC powder, the plasticizer and optionally used fillers and additives are mixed to form a homogeneous plastisol.
The resulting plastisol is gelled by means of a twin-screw extruder and formed via a nozzle to form an endless strand.
Nach Durchlaufen des Strangs durch ein Kühlbad wird der Radiererstrang auf die gewünschte Länge zu einzelnen Radierern geschnitten und ggf. bedruckt und verpackt.After passing through the strand through a cooling bath the eraser strand is cut to the desired length to individual erasers and optionally printed and packaged.
Bei der Herstellung der Radierer hat sich zudem gezeigt, dass die Härte des Radierers durch Variation des Weichmacheranteiles und Weichmacherverhältnisses leicht und genau anpass- bzw. einstellbar ist.In the production of the erasers, it has also been found that the hardness of the eraser can be easily and precisely adjusted by varying the proportion of plasticizer and plasticizer ratio.
ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- DE 102016008559 A1 [0006]DE 102016008559 A1 [0006]
Claims (10)