DE202013101921U1 - Permament flame retardant fabric and protective clothing - Google Patents

Permament flame retardant fabric and protective clothing Download PDF

Info

Publication number
DE202013101921U1
DE202013101921U1 DE202013101921U DE202013101921U DE202013101921U1 DE 202013101921 U1 DE202013101921 U1 DE 202013101921U1 DE 202013101921 U DE202013101921 U DE 202013101921U DE 202013101921 U DE202013101921 U DE 202013101921U DE 202013101921 U1 DE202013101921 U1 DE 202013101921U1
Authority
DE
Germany
Prior art keywords
fabric
flame retardant
equal
protective clothing
din
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202013101921U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SR WEBATEX GmbH
Original Assignee
SR WEBATEX GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SR WEBATEX GmbH filed Critical SR WEBATEX GmbH
Priority to DE202013101921U priority Critical patent/DE202013101921U1/en
Publication of DE202013101921U1 publication Critical patent/DE202013101921U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Permanent flammhemmendes Gewebe, aufweisend:
– ein permanent flammhemmendes cellulosisches Multifilament in Kettrichtung; und
– ein permanent flammhemmendes cellulosisches Core-Spun-Garn in Schussrichtung.Permanent flame retardant fabric, comprising:
- A permanently flame retardant cellulosic multifilament in the warp direction; and
- A permanently flame retardant cellulosic core spun yarn in the weft direction.

Description

Die Erfindung betrifft ein permanent flammhemmendes Gewebe.The invention relates to a permanently flame-retardant fabric.

Permanent flammhemmende Gewebe dienen insbesondere zur Herstellung von Schutzkleidung und/oder -ausrüstung für PSA-(Persönliche Schutzausrüstung) oder militärische Anwendungen. Vorbekannte flammhemmende Gewebe bestehen etwa aus Stapelgarnen (z.B. mit Aramidbeimischungen). Auch sind Gewebe aus Filamentviskose vorbekannt. Diese Gewebe aus Filamentviskose sind jedoch sehr glatt und besitzen für bestimmte Anwendungen, insbesondere im Industriebereich, einen zu geringen textilen Griff.Permanent flame retardant fabrics are used in particular for the production of protective clothing and / or equipment for PPE (Personal Protective Equipment) or military applications. For example, prior art flame retardant fabrics consist of staple yarns (e.g., with aramid blends). Also, fabrics of filament viscose are previously known. However, these filament viscose fabrics are very smooth and have too little textile feel for certain applications, especially in the industrial sector.

Der Erfindung liegt die Aufgabe zugrunde, ein permanent flammhemmendes Gewebe anzubieten, welches einen guten textilen Griff und zugleich ein hohe mechanische Festigkeit besitzt. Ferner ist es Aufgabe der Erfindung eine flammhemmende Schutzbekleidung mit einem hohen Tragekomfort und hoher mechanischer Festigkeit anzubieten.The invention has for its object to provide a permanently flame retardant fabric, which has a good textile feel and at the same time a high mechanical strength. It is another object of the invention to provide a flame-retardant protective clothing with a high level of comfort and high mechanical strength.

Diese Aufgabe wird durch das Gewebe mit den Merkmalen des Anspruchs 1 bzw. durch die Schutzbekleidung mit den Merkmalen des Anspruchs 7 gelöst. Vorteilhafte Ausführungsformen des Gewebes sind in den Unteransprüchen beschrieben.This object is achieved by the fabric with the features of claim 1 and by the protective clothing with the features of claim 7. Advantageous embodiments of the fabric are described in the subclaims.

Das erfindungsgemäße permanent flammhemmende Gewebe weist ein permanent flammhemmendes cellulosisches Multifilament in Kettrichtung; und ein permanent flammhemmendes cellulosisches Core-Spun-Garn in Schussrichtung auf. Es handelt es somit um ein rein cellulosisches Gewebe. The permanent flame-retardant fabric according to the invention has a permanently flame-retardant cellulosic multifilament in the warp direction; and a permanently flame retardant cellulosic core spun yarn in weft direction. It is thus a purely cellulosic tissue.

Im Vergleich zu Stapelgarnen weist das Gewebe eine höhere Festigkeit auf. Zugleich besitzt das Gewebe einen guten textilen Griff.Compared to staple yarns, the fabric has a higher strength. At the same time, the fabric has a good textile feel.

Unter einem Core-Spun-Garn wird hierbei ein mit Fasergarn umsponnener Filamentgarn verstanden.A core-spun yarn is here understood to mean a filament yarn wound with fiber yarn.

In einer vorteilhaften Ausführungsform weist das Gewebe ein Flächengewicht von größer gleich 270 g/m2 und kleiner gleich 330 g/m2 auf. Ein Flächengewicht in diesem Wertebereich ergibt besonders vorteilhafte Trageeigenschaften für Sicherheitsbekleidung, die aus dem Gewebe gefertigt wurde.In an advantageous embodiment, the fabric has a weight per unit area of greater than or equal to 270 g / m 2 and less than or equal to 330 g / m 2 . A basis weight in this range of values results in particularly advantageous wearing properties for safety clothing, which was manufactured from the fabric.

Als besonders vorteilhaftes Webverfahren hat sich die Köperbindung herausgestellt. Weist das Gewebe eine Köperbindung auf, sind besonders gute Trageeigenschaften (guter textiler Griff) gegeben.As a particularly advantageous weaving method, the twill weave has been found. If the fabric has a twill weave, particularly good wearing properties (good textile feel) are given.

In vorteilhafter Weise besitzt das Gewebe ein Höchstzugkraft in Schussrichtung von größer gleich 400 N / 5cm und kleiner gleich 1500 N / 5 cm und/oder ein Höchstzugkraft in Kettrichtung von größer gleich 400 N / 5 cm und kleiner gleich 2000 N / 5 cm.Advantageously, the fabric has a maximum tensile force in the weft direction of greater than or equal to 400 N / 5cm and less than 1500 N / 5 cm and / or a maximum tensile force in the warp direction of greater than or equal 400 N / 5 cm and less equal to 2000 N / 5 cm.

In einer bevorzugten Ausführungsform geht das Gewebe bei Hitzeeinwirkung nicht in eine flüssige Phase über. Mit anderen Worten schmilzt das Gewebe nicht, sondern verbrennt unter Zurücklassen von festen Reststoffen.In a preferred embodiment, the tissue does not change into a liquid phase when exposed to heat. In other words, the fabric does not melt but burns leaving behind solid residues.

Die erfindungsgemäße Schutzbekleidung ist aus dem erfindungsgemäßen Gewebe hergestellt. Sie besitzt eine hohe Festigkeit und aufgrund des guten textilen Griffs zugleich einen hohen Tragekomfort. Besonders geeignet ist die Schutzbekleidung für den Einsatz in persönlichen Schutzausrüstungen (feuerfeste Schutzkleidung) und/oder für militärische Anwendungen.The protective clothing according to the invention is produced from the fabric according to the invention. It has a high strength and due to the good textile feel at the same time a high wearing comfort. The protective clothing is particularly suitable for use in personal protective equipment (refractory protective clothing) and / or for military applications.

Die Erfindung ist anhand des folgenden Ausführungsbeispiels weiter erläutert.The invention is further explained with reference to the following embodiment.

Die zu dem Gewebe zu verarbeitenden Garne (permanent flammhemmendes cellulosisches Multifilament – Viscose FR Filamentgarn und permanent flammhemmendes cellulosisches Core-Spun-Garn – Viscose FR/HT Filamentgarn mit Fasergarn umsponnen) werden in einer Vorstufe zum Webprozess (Vorwerk) behandelt. Nach dieser Vorbehandlung und dem Aufbringen einer Avivage werden die Garne auf einer Webmaschine zum Gewebe verarbeitet. Nach dem Weben wird das Gewebe in der Ausrüstung hinsichtlich der Maßänderung, des Griffs und der Farbe ausgerüstet.The yarns to be processed into the fabric (permanently flame-retardant cellulosic multifilament - Viscose FR filament yarn and permanently flame retardant cellulosic core spun yarn - Viscose FR / HT filament yarn wound with fiber yarn) are treated in a preliminary stage to the weaving process (Vorwerk). After this pretreatment and the application of a finish, the yarns are processed on a weaving machine to the fabric. After weaving, the fabric in the equipment is equipped in terms of dimensional change, grip and color.

In der unten folgenden Tabelle sind die die Herstellparameter und Eigenschaften eines erfindungsgemäßen permanent flammhemmenden Gewebes zusammengefasst. Das permanent flammhemmende Gewebe weist ein permanent flammhemmendes cellulosisches Multifilament in Kettrichtung; und ein permanent flammhemmendes cellulosisches Core-Spun-Garn in Schussrichtung auf. Eigenschaft Messverfahren gemäß ... Einheit Wert Material DIN 53 840-B Kette Viscose FR Filamentgarn Schuss Viscose FR/HT Filamentgarn mit Fasergarn umsponnen Flächengewicht ausgerüstet DIN EN 12 127 g/cm2 300 ± 25 Bindung DIN ISO 9 354 Twill Fadenzahl ausgerüstet DIN EN 1 049-2 Kette Fd./cm 38,0 ± 5 Schuss Fd./cm 35,0 ± 5 Breite ausgerüstet DIN 53 851 cm ≥ 145 Höchstzugkraft ausgerüstet DIN EN ISO 13 934-1 Kette N/5cm 400 – 1500 Schuss N/5cm 400 – 2000 Dehnung ausgerüstet DIN EN ISO 13 934-1 Kette % ≥ 15 Schuss % ≥ 10 Weiterreißfestigkeit ausgerüstet DIN EN ISO 13 937-2 Kette N ≥ 15 Schuss N ≥ 15 The table below summarizes the manufacturing parameters and properties of a permanent flame-retardant fabric according to the invention. The permanent flame retardant Fabric has a permanently flame-retardant cellulosic multifilament in the warp direction; and a permanently flame retardant cellulosic core spun yarn in weft direction. property Measuring method according to ... unit value material DIN 53 840-B Chain Viscose FR filament yarn shot Viscose FR / HT filament yarn wound with fiber yarn Weight per unit area DIN EN 12 127 g / cm 2 300 ± 25 binding DIN ISO 9 354 twill Thread count equipped DIN EN 1 049-2 Chain Fd./cm 38.0 ± 5 shot Fd./cm 35.0 ± 5 Width equipped DIN 53 851 cm ≥ 145 Equipped with maximum traction DIN EN ISO 13 934-1 Chain N / 5 cm 400 - 1500 shot N / 5 cm 400 - 2000 Stretching equipped DIN EN ISO 13 934-1 Chain % ≥ 15 shot % ≥ 10 Tear strength equipped DIN EN ISO 13 937-2 Chain N ≥ 15 shot N ≥ 15

Das auf diese Weise hergestellte Gewebe besitzt eine hohe Festigkeit und zugleich einen guten textilen Griff. Außerdem erfüllt das Gewebe die Normen EN 11611 , EN ISO 11612 , EN 14116 und EN 61482 . Des Weiteren kann die Maßänderung nach der Wäsche auf ≤ 3 % in Längs- und Querrichtung reduziert sein.The fabric produced in this way has a high strength and at the same time a good textile feel. In addition, the fabric meets the Standards EN 11611 . EN ISO 11612 . EN 14116 and EN 61482 , Furthermore, the dimensional change after the wash can be reduced to ≦ 3% in the longitudinal and transverse directions.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte Nicht-PatentliteraturCited non-patent literature

  • DIN 53 840-B [0015] DIN 53 840-B [0015]
  • DIN EN 12 127 [0015] DIN EN 12 127 [0015]
  • DIN ISO 9 354 [0015] DIN ISO 9 354 [0015]
  • DIN EN 1 049-2 [0015] DIN EN 1 049-2 [0015]
  • DIN 53 851 [0015] DIN 53 851 [0015]
  • DIN EN ISO 13 934-1 [0015] DIN EN ISO 13 934-1 [0015]
  • DIN EN ISO 13 937-2 [0015] DIN EN ISO 13 937-2 [0015]
  • Normen EN 11611 [0016] Standards EN 11611 [0016]
  • EN ISO 11612 [0016] EN ISO 11612 [0016]
  • EN 14116 [0016] EN 14116 [0016]
  • EN 61482 [0016] EN 61482 [0016]

Claims (7)

Permanent flammhemmendes Gewebe, aufweisend: – ein permanent flammhemmendes cellulosisches Multifilament in Kettrichtung; und – ein permanent flammhemmendes cellulosisches Core-Spun-Garn in Schussrichtung.Permanent flame retardant fabric, comprising: - A permanently flame retardant cellulosic multifilament in the warp direction; and - A permanently flame retardant cellulosic core spun yarn in the weft direction. Gewebe nach Anspruch 1, wobei das Gewebe ein Flächengewicht von größer gleich 270 g/m2 und kleiner gleich 330 g/m2 aufweist.The fabric of claim 1, wherein the fabric has a basis weight greater than or equal to 270 g / m 2 and less than or equal to 330 g / m 2 . Gewebe nach einem der vorhergehenden Ansprüche, wobei das Gewebe eine Köperbindung aufweist.The fabric of any one of the preceding claims, wherein the fabric has a twill weave. Gewebe nach einem der vorhergehenden Ansprüche, wobei das Gewebe ein Höchstzugkraft in Schussrichtung von größer gleich 400 N / 5 cm und kleiner gleich 1500 N / 5 cm aufweist.The fabric of any one of the preceding claims, wherein the fabric has a maximum tensile force in the weft direction of greater than or equal to 400 N / 5 cm and less than or equal to 1500 N / 5 cm. Gewebe nach einem der vorhergehenden Ansprüche, wobei das Gewebe ein Höchstzugkraft in Kettrichtung von größer gleich 400 N / 5cm und kleiner gleich 2000 N / 5 cm aufweist.A fabric according to any one of the preceding claims, wherein the fabric has a maximum tensile force in the warp direction of greater than or equal to 400 N / 5cm and less than or equal to 2000 N / 5cm. Gewebe nach einem der vorhergehenden Ansprüche, wobei das Gewebe bei Hitzeeinwirkung nicht in eine flüssige Phase übergeht.A fabric according to any one of the preceding claims, wherein the fabric does not change to a liquid phase upon exposure to heat. Schutzbekleidung, hergestellt aus einem Gewebe nach einem der vorhergehenden Ansprüche.Protective clothing made of a fabric according to any one of the preceding claims.
DE202013101921U 2013-05-03 2013-05-03 Permament flame retardant fabric and protective clothing Expired - Lifetime DE202013101921U1 (en)