DE202011108100U1 - Liquid thermoplastic mass for buildings - Google Patents

Liquid thermoplastic mass for buildings Download PDF

Info

Publication number
DE202011108100U1
DE202011108100U1 DE201120108100 DE202011108100U DE202011108100U1 DE 202011108100 U1 DE202011108100 U1 DE 202011108100U1 DE 201120108100 DE201120108100 DE 201120108100 DE 202011108100 U DE202011108100 U DE 202011108100U DE 202011108100 U1 DE202011108100 U1 DE 202011108100U1
Authority
DE
Germany
Prior art keywords
weight
compound according
plastic compound
plastic
contained
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE201120108100
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BTF PRODUKTENTWICKLUNGS und VERTRIEBS GmbH
BTF PRODUKTENTWICKLUNGS- und VERTRIEBS- GmbH
Original Assignee
BTF PRODUKTENTWICKLUNGS und VERTRIEBS GmbH
BTF PRODUKTENTWICKLUNGS- und VERTRIEBS- GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BTF PRODUKTENTWICKLUNGS und VERTRIEBS GmbH, BTF PRODUKTENTWICKLUNGS- und VERTRIEBS- GmbH filed Critical BTF PRODUKTENTWICKLUNGS und VERTRIEBS GmbH
Priority to DE201120108100 priority Critical patent/DE202011108100U1/en
Publication of DE202011108100U1 publication Critical patent/DE202011108100U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Flüssige thermoplastische Kunststoff-Beschichtungsmasse zum Abdichten und/oder Schützen von Bauwerken insbesondere aus Beton und/oder Holz, wobei die Kunststoffmasse als Bindemittel ein modifiziertes thermoplastisches Polymethylmethacrylat und ein umweltverträgliches Lösungsmittel enthält, das leichter flüchtig ist als Wasser.Liquid thermoplastic plastic coating compound for sealing and / or protecting structures, in particular made of concrete and / or wood, the plastic compound containing a modified thermoplastic polymethyl methacrylate and an environmentally friendly solvent that is more volatile than water as a binder.

Description

Die Erfindung betrifft eine flüssige thermoplastische Kunststoffmasse, die zum Abdichten und/oder Schützen von Bauwerken, insbesondere aus Beton oder Holz, vorgesehen ist.The invention relates to a liquid thermoplastic polymer composition intended for sealing and / or protecting structures, in particular concrete or wood.

Die Rezeptur der erfindungsgemäßen Kunststoffmasse kann dahingehend modifiziert werden, dass sie zum Verkleben von Perimeterdämmplatten verwendet werden kann. Eine weitere Rezepturvariante ergibt eine Beschichtung, die nach dem Trocknen dampfdiffusionsoffen bleibt.The formulation of the plastic composition according to the invention can be modified so that it can be used for bonding Perimeterdämmplatten. Another recipe variant results in a coating that remains open to vapor diffusion after drying.

In der Bautechnik ist es erforderlich, Bauwerke bzw. Bauteile aus mineralischen oder organischen Baustoffen sowie Fugen und Risse in einem Bauwerk vor dem Eindringen von Wasser und Feuchtigkeit zu schützen. Bauwerksabdichtungen spielen z. B. bei der Nutzbarmachung von Kellern und Tiefgeschossen sowie bei Tunnel- und Brückenbauwerken eine wichtige Rolle. Abdichtungen sind auch bei Flachdächern, Terrassen und Balkonen sowie als Innenabdichtungen für Nassräume, wie Badezimmer, Saunen o. dgl. von Wichtigkeit.In structural engineering, it is necessary to protect buildings or components made of mineral or organic building materials as well as joints and cracks in a building from the ingress of water and moisture. Structural waterproofing play z. As in the utilization of basements and basements and in tunnel and bridge structures an important role. Seals are also important for flat roofs, terraces and balconies as well as interior waterproofing for wet rooms, such as bathrooms, saunas o. The like.

Hierfür wurden in der Vergangenheit hauptsächlich Bitumenbahnen verwendet, die zwischenzeitlich auch durch Kunststoffbahnen ersetzt werden. Ein Problem bei der Verwendung solcher Bahnen oder Folien besteht jedoch darin, dass die Abdichtung an Ecken, Kanten und Durchlässen aufwendig ist und trotz eines umsichtigen Arbeitens an diesen Stellen Undichtigkeiten oftmals nicht zuverlässig vermeidbar sind.For this purpose, mainly bitumen membranes were used in the past, which are replaced in the meantime by plastic sheets. However, a problem with the use of such webs or foils is that the sealing at corners, edges and passages is complex and despite a careful work at these points leaks are often not reliably prevented.

Mittels flüssiger Abdichtmassen lassen sich die oben genannten Probleme vermeiden, es können jedoch bei der Verarbeitung der bekannten flüssigen Abdichtmassen toxische Emissionen freigesetzt werden. Ähnliche Schwierigkeiten verursachen lösemittelhaltige Einkomponenten-Kunstharzgemische oder Zweikomponenten-Systeme, die neben den schädlichen Inhaltsstoffen für den Anwender auch noch sehr unpraktisch sind.By means of liquid sealing compounds, the abovementioned problems can be avoided, but toxic emissions can be released during the processing of the known liquid sealing compounds. Similar problems cause solvent-containing one-component synthetic resin mixtures or two-component systems, which are in addition to the harmful ingredients for the user also very impractical.

Um die zuletzt genannten Mängel dieser bekannten flüssigen Abdichtmassen zu beseitigen, wurden als Abdichtungsmaterialien auch bereits wässrigen Polymerdispersionen vorgeschlagen. Diese bekannten wässrigen Abdichtungsmaterialien trocknen jedoch nur bei Umgebungstemperaturen > 15°C ausreichend rasch ab. Bei Temperaturen > 20°C kann jedoch andererseits leicht Wasser eingeschlossen werden, was zur Blasenbildung und zu Leckagen führen kann. Der Temperaturbereich für eine optimale Verarbeitung derartiger Abdichtungsmaterialien ist also sehr klein. Zudem ist die Filmdicke dieser bekannten wässrigen Beschichtungsmassen nach dem Trocknen oftmals unzureichend, so dass mehrere Schichten übereinander aufgetragen werden müssen, um z. B. einen ausreichenden Schutz gegen Feuchtigkeit zu erzielen. Die Notwendigkeit eines solchen Mehrfach-Auftrags stellt einen weiteren Mangel dar.In order to eliminate the last-mentioned deficiencies of these known liquid sealing compounds, aqueous polymer dispersions have already been proposed as sealing materials. However, these known aqueous sealing materials dry sufficiently quickly only at ambient temperatures> 15 ° C. On the other hand, at temperatures> 20 ° C, water can be easily trapped, causing blistering and leaks. The temperature range for optimal processing of such sealing materials is therefore very small. In addition, the film thickness of these known aqueous coating compositions is often insufficient after drying, so that several layers have to be applied one above the other in order, for. B. to achieve adequate protection against moisture. The need for such a multiple contract is another shortcoming.

Bekannte einkomponentige Beschichtungsmassen auf Silikonbasis härten mit Luftfeuchtigkeit aus. Am bekanntesten sind die Acetatsysteme, welche beim Aushärten Essigsäure abspalten. Von Nachteil bei diesen Systemen sind die schlechte Haftung auf einer Vielzahl von Baumaterialien sowie die mangelnde Überlackierbarkeit. Außerdem ist ihre Bewitterungsstabilität bei Außenanwendungen oftmals nicht ausreichend.Known one-component silicone-based coating compositions cure with atmospheric moisture. Best known are the acetate systems, which release acetic acid during curing. A disadvantage of these systems are the poor adhesion to a variety of building materials and the lack of recoatability. In addition, their weathering stability in outdoor applications is often insufficient.

In Kenntnis dieser Gegebenheiten liegt der Erfindung die Aufgabe zugrunde, eine flüssige thermoplastische Kunststoffmasse zu schaffen, welche die oben aufgeführten negativen Eigenschaften zumindest auf ein Minimum reduziert oder eliminiert, und die bei einer einfachen Verarbeitbarkeit als wirksame Bauwerks-Abdichtung verwendbar ist.Knowing these facts, the invention has for its object to provide a liquid thermoplastic resin composition which reduces or eliminates the negative properties listed above at least to a minimum, and which is usable with a simple processability as an effective building seal.

Diese Aufgabe wird erfindungsgemäß durch die Merkmale des Anspruches 1 gelöst. Bevorzugte Weiterbildungen der erfindungsgemäßen Kunststoffmasse sind in den Unteransprüchen gekennzeichnet.This object is achieved by the features of claim 1. Preferred developments of the plastic composition according to the invention are characterized in the subclaims.

Die erfindungsgemäße flüssige thermoplastische Kunststoffmasse kann durch Sprühen, Spachteln oder Gießen verarbeitet werden. Geringfügig modifiziert ist die erfindungsgemäße Kunststoffmasse zum Verkleben von Perimeterdämmplatten verwendbar. Sehr dünn aufgetragen ist die erfindungsgemäße flüssige Kunststoffmasse nach dem Aushärten für Wasserdampf permeabel, d. h. seine Wasserdampf-Diffusionsstromdichte kann nach DIN EN 1062-1 (08/04) in eine von 3 Klassen eingeteilt werden.The liquid thermoplastic polymer composition according to the invention can be processed by spraying, filling or pouring. Slightly modified, the plastic composition according to the invention can be used for bonding Perimeterdämmplatten. When applied very thinly, the liquid plastic composition according to the invention is permeable to water vapor after curing, ie its water vapor diffusion current density can after DIN EN 1062-1 (08/04) be divided into one of 3 classes.

Die erfindungsgemäße flüssige thermoplastische Kunststoffmasse bildet quasi ein flüssiges Glas, das die gestellten Anforderungen erfüllt. Die Kunststoffmasse ist einkomponentig. Sie besteht aus einem modifizierten thermoplastischen Polymethylmethacrylat, das als Bindemittel eingesetzt wird, sowie einer Kombination von substituierten Carbonsäureestern, Ethanol, sekundären Alkoholen und gegebenenfalls mineralischen Füllstoffen. Die Carbonsäureester und/oder Alkohole werden als Lösungsmittel verwendet. Sie sind leichtentzündlich und flüchtig und in vorteilhafter Weise umweltverträglich.The liquid thermoplastic mass of the invention forms quasi a liquid glass that meets the requirements. The plastic compound is one-component. It consists of a modified thermoplastic polymethyl methacrylate, which is used as a binder, and a combination of substituted carboxylic acid esters, ethanol, secondary alcohols and optionally mineral Fillers. The carboxylic acid esters and / or alcohols are used as solvents. They are highly flammable and volatile and advantageously environmentally friendly.

Die Mischung ist nicht gesundheitsschädlich. Da die Lösungsmittel leichter flüchtig sind als Wasser, bildet sich in vorteilhafter Weise bereits nach kurzer Zeit eine homogene polymerisierte Schicht aus. Durch eine geeignete Kombination der Lösungsmittel kann die Trocknungszeit wunschgemäß verlängert oder verkürzt werden. Durch die Menge an Bindemittel/Kunststoff in der Mischung kann die Dicke und Plastizität der Beschichtung gesteuert werden. Da der flüssige Kunststoff im nicht ausgehärteten Zustand klebende Eigenschaften aufweist, kann er gut zum Verkleben z. B. von Perimeterdämmplatten verwendet werden. Die Perimeterdämmplatten werden dabei vom Klebstoff durchdrungen, so dass sie nach dem Ablüften der Lösungsmittel fest mit dem Mauerwerk verbunden sind. Der Zusatz eines Füllstoffs, bspw. von Kreide, führt dazu, dass das „flüssige Glas” bei entsprechend geringer Schichtstärke nach dem Härten Mikroporen aufweist und dadurch für Wasserdampf permeabel wird.The mixture is not harmful to health. Since the solvents are more volatile than water, advantageously forms after a short time a homogeneous polymerized layer. By a suitable combination of solvents, the drying time can be extended or shortened as desired. The amount of binder / plastic in the mixture can control the thickness and plasticity of the coating. Since the liquid plastic in the uncured state has adhesive properties, it can be good for bonding z. B. of Perimeterdämmplatten be used. The Perimeterdämmplatten be penetrated by the adhesive, so that they are firmly connected to the masonry after venting the solvent. The addition of a filler, for example of chalk, leads to the "liquid glass" having a correspondingly low layer thickness after hardening having micropores and thereby becoming permeable to water vapor.

Die erfindungsgemäße Beschichtung ist in vorteilhafter Weise beständig gegen Witterung, Temperaturschwankungen und Alterung, gegen Säuren und Laugen mittlerer Konzentration, sowie gegen Wasser, Benzin und Öl.The coating according to the invention is advantageously resistant to weathering, temperature fluctuations and aging, to acids and alkalis of medium concentration, as well as to water, gasoline and oil.

Die erfindungsgemäße Kunststoffmasse kann als Beschichtung zur Tunnelsanierung, als Abdichtung für Betonkeller, generell als Bauwerksabdichtung, zum Versiegeln von Wänden, Tapeten und Holz, sowie als Kleber für Perimeterdämmplatten verwendet werden; sie haftet auf allen gängigen Natursteinen. Die Untergründe benötigen in vorteilhafter Weise keine Vorbehandlung, sie müssen lediglich trocken und fett- und staubfrei sein.The plastic composition according to the invention can be used as a coating for tunnel renovation, as a seal for concrete basements, generally as a building seal, for sealing walls, wallpaper and wood, and as an adhesive for Perimeterdämmplatten; It is liable to all common natural stones. The substrates need advantageously no pretreatment, they only have to be dry and free of grease and dust.

Der weiteren Verdeutlichung der Erfindung dienen die nachfolgend angegebenen Rezepturen der flüssigen thermoplastischen Kunststoffmasse: Rahmenrezeptur für die flüssige thermoplastische Kunststoffmasse (flüssiges Glas) allgemein • Modifiziertes Polymethylmethacrylat 5 bis 60 Gew.-% • Mineralischer Füllstoff (Kreide) 0 bis 50 Gew.-% • Mineralischer Füllstoff (Kaolin) 0 bis 50 Gew.-% • Ethanol 0 bis 95 Gew.-% • Sekundärer Alkohol (z. B. 2-Propanol, 2-Butanol) 0 bis 95 Gew.-% • Acetessigsäuremethylester 0 bis 95 Gew.-% • Essigsäureethylester 0 bis 95 Gew.-% • Rahmenrezeptur für die Verwendung als Kleber für Perimeterdämmplatten • Modifiziertes Polymethylmethacrylat 5 bis 60 Gew.-% • Ethanol 0 bis 95 Gew.-% • Sekundärer Alkohol (z. B. 2-Propanol, 2-Butanol) 0 bis 95 Gew.-% • Acetessigsäuremethylester 0 bis 95 Gew.-% • Essigsäureethylester 0 bis 75 Gew.-% • Rahmenbeispiel 1 für „flüssiges Glas” zum Sprühen • Modifiziertes Polymethylmethacrylat 5 bis 25 Gew.-% • Ethanol 10 bis 55 Gew.-% • Essigsäureethylester 20 bis 95 Gew.-% • Rahmenbeispiel 2 für einen eingefärbten Kleber für Perimeterdämmplatten • Modifiziertes Polymethylmethacrylat 5 bis 60 Gew.-% • Ethanol 0 bis 60 Gew.-% • 2-Propanol 0 bis 60 Gew.-% • Essigsäureethylester 5 bis 40 Gew.-% • Eisenoxidpigment 0,5 bis 5 Gew.-% • Rahmenbeispiel 3 für einen anderen eingefärbten Perimeterdämmplatten-Kleber • Modifiziertes Polymethylmethacrylat 5 bis 60 Gew.-% • Ethanol 0 bis 60 Gew.-% • 2-Butanol 0 bis 60 Gew.-% • Essigsäureethylester 5 bis 40 Gew.-% • Eisenoxidpigment 0,5 bis 5 Gew.-% • Rahmenbeispiel 4 für „flüssiges Glas” zum Spachteln • Modifiziertes Polymethylmethacrylat 5 bis 60 Gew.-% • Acetessigsäuremethylester 0 bis 95 Gew.-% • Essigsäureethylester 0 bis 95 Gew.-% • Rahmenbeispiel 5 für „flüssiges Glas”, permeabel für Wasserdampf • Modifiziertes Polymethylmethacrylat 5 bis 45 Gew.-% • Mineralischer Füllstoff (Kreide) 5 bis 50 Gew.-% • Mineralischer Füllstoff (Kaolin) 0 bis 50 Gew.-% • Ethanol 0 bis 95 Gew.-% • Acetessigsäuremethylester 5 bis 50 Gew.-% • Essigsäureethylester 10 bis 95 Gew.-% • Rahmenbeispiel 6 für eingefärbtes „flüssiges Glas” zum Spachteln • Modifiziertes Polymethylmethacrylat 5 bis 60 Gew.-% • Acetessigsäuremethylester 0 bis 95 Gew.-% • Essigsäureethylester 0 bis 95 Gew.-% • Ethanol 0 bis 30 Gew.-% • Eisenoxidpigment 0,5 bis 5 Gew.-% The following clarifications of the invention serve the following formulations of the liquid thermoplastic resin composition: frame formulation for the liquid thermoplastic polymer composition (liquid glass) in general • Modified polymethylmethacrylate 5 to 60% by weight • mineral filler (chalk) 0 to 50% by weight Mineral filler (kaolin) 0 to 50% by weight • ethanol 0 to 95% by weight Secondary alcohol (eg 2-propanol, 2-butanol) 0 to 95% by weight • methyl acetoacetate 0 to 95% by weight • ethyl acetate 0 to 95% by weight • Frame formulation for use as adhesive for perimeter insulation panels • Modified polymethylmethacrylate 5 to 60% by weight • ethanol 0 to 95% by weight Secondary alcohol (eg 2-propanol, 2-butanol) 0 to 95% by weight • methyl acetoacetate 0 to 95% by weight • ethyl acetate 0 to 75% by weight • Frame Example 1 for "liquid glass" for spraying • Modified polymethylmethacrylate 5 to 25% by weight • ethanol 10 to 55% by weight • ethyl acetate 20 to 95% by weight • Frame example 2 for a colored adhesive for Perimeterdämmplatten • Modified polymethylmethacrylate 5 to 60% by weight • ethanol 0 to 60% by weight • 2-propanol 0 to 60% by weight • ethyl acetate 5 to 40% by weight • iron oxide pigment 0.5 to 5% by weight • Frame Example 3 for another colored Perimeterdämmplatten adhesive • Modified polymethylmethacrylate 5 to 60% by weight • ethanol 0 to 60% by weight • 2-butanol 0 to 60% by weight • ethyl acetate 5 to 40% by weight • iron oxide pigment 0.5 to 5% by weight • Frame example 4 for "liquid glass" for filling • Modified polymethylmethacrylate 5 to 60% by weight • methyl acetoacetate 0 to 95% by weight • ethyl acetate 0 to 95% by weight • Frame example 5 for "liquid glass", permeable to water vapor • Modified polymethylmethacrylate From 5 to 45% by weight • mineral filler (chalk) 5 to 50% by weight Mineral filler (kaolin) 0 to 50% by weight • ethanol 0 to 95% by weight • methyl acetoacetate 5 to 50% by weight • ethyl acetate 10 to 95% by weight • Frame Example 6 for colored "liquid glass" for filling • Modified polymethylmethacrylate 5 to 60% by weight • methyl acetoacetate 0 to 95% by weight • ethyl acetate 0 to 95% by weight • ethanol 0 to 30% by weight • iron oxide pigment 0.5 to 5% by weight

Das erfindungsgemäße „Flüssige Glas” bzw. die erfindungsgemäße flüssige thermoplastische Kunststoffmasse auf Basis von modifiziertem Polymethylmethacrylat und flüchtigen, umweltverträglichen Lösungsmitteln ist als einkomponentige Abdichtung von Tunneln, Brücken und anderen Bauwerken, sowohl für die Innen- und Außenanwendung geeignet. Die Kunststoff-Beschichtungsmasse dringt in vorteilhafter Weise in die abzudichtenden Materialien ein und verschließt Poren und Spalten dauerhaft.The inventive "liquid glass" or the liquid thermoplastic polymer composition based on modified polymethyl methacrylate and volatile, environmentally compatible solvents according to the invention is suitable as one-component sealing of tunnels, bridges and other structures, both for indoor and outdoor use. The plastic coating material penetrates advantageously into the materials to be sealed and closes pores and gaps permanently.

Nach dem Härten ist die Beschichtung glatt, trocken, sowie alterungs- und witterungsbeständig, außerdem ist sie leicht zu reinigen. After curing, the coating is smooth, dry, resistant to aging and weathering, and is easy to clean.

Dünn appliziert, ist die Beschichtung für Wasserdampf durchlässig und somit „atmungsaktiv”.Applied thinly, the coating is permeable to water vapor and thus "breathable".

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte Nicht-PatentliteraturCited non-patent literature

  • DIN EN 1062-1 (08/04) [0010] DIN EN 1062-1 (08/04) [0010]

Claims (9)

Flüssige thermoplastische Kunststoff-Beschichtungsmasse zum Abdichten und/oder Schützen von Bauwerken insbesondere aus Beton und/oder Holz, wobei die Kunststoffmasse als Bindemittel ein modifiziertes thermoplastisches Polymethylmethacrylat und ein umweltverträgliches Lösungsmittel enthält, das leichter flüchtig ist als Wasser.Liquid thermoplastic plastic coating material for sealing and / or protecting buildings, in particular of concrete and / or wood, wherein the plastic material contains as binder a modified thermoplastic polymethylmethacrylate and an environmentally friendly solvent which is more volatile than water. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass 5 bis 60 Gew.-% modifiziertes Polymethylmethacrylat enthalten sind.Plastic compound according to claim 1, characterized in that 5 to 60 wt .-% of modified polymethyl methacrylate are included. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass das Lösungsmittel substituierte Carbonsäureester und/oder sekundäre Alkohole enthält.Plastic compound according to claim 1, characterized in that the solvent contains substituted carboxylic acid esters and / or secondary alcohols. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass mindestens ein mineralischer Füllstoff enthalten ist.Plastic compound according to claim 1, characterized in that at least one mineral filler is included. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass Ethanol enthalten ist.Plastic compound according to claim 1, characterized in that ethanol is contained. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass Essigsäureethylester enthalten ist.Plastic compound according to claim 1, characterized in that ethyl acetate is contained. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass Acetessigsäuremethylester enthalten ist.Plastic compound according to claim 1, characterized in that methyl acetoacetate is contained. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass 2-Propanol oder 2-Butanol enthalten ist.Plastic compound according to claim 1, characterized in that 2-propanol or 2-butanol is included. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass mindestens ein Farbpigment enthalten ist.Plastic compound according to claim 1, characterized in that at least one color pigment is contained.
DE201120108100 2011-11-19 2011-11-19 Liquid thermoplastic mass for buildings Expired - Lifetime DE202011108100U1 (en)