DE202004020593U1 - Products or semi-finished products for use e.g. as seals or panels in cars, made from a thermoplastic elastomer-like composition containing rubber powder, thermoplastic, crosslinker and SEBS copolymer - Google Patents

Products or semi-finished products for use e.g. as seals or panels in cars, made from a thermoplastic elastomer-like composition containing rubber powder, thermoplastic, crosslinker and SEBS copolymer Download PDF

Info

Publication number
DE202004020593U1
DE202004020593U1 DE202004020593U DE202004020593U DE202004020593U1 DE 202004020593 U1 DE202004020593 U1 DE 202004020593U1 DE 202004020593 U DE202004020593 U DE 202004020593U DE 202004020593 U DE202004020593 U DE 202004020593U DE 202004020593 U1 DE202004020593 U1 DE 202004020593U1
Authority
DE
Germany
Prior art keywords
thermoplastic
composition
tpe
products
rubber powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202004020593U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MOELLERFLEX GmbH
Mollerflex GmbH
Original Assignee
MOELLERFLEX GmbH
Mollerflex GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MOELLERFLEX GmbH, Mollerflex GmbH filed Critical MOELLERFLEX GmbH
Priority to DE202004020593U priority Critical patent/DE202004020593U1/en
Publication of DE202004020593U1 publication Critical patent/DE202004020593U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Products (especially mouldings or semi-finished products) made from a thermoplastic elastomer (TPE)-like composition (I) made from rubber powder, thermoplastic(s) and crosslinker(s) by a melt-compounding process, in which composition (I) contains a proportion of SEBS copolymer (styrene-ethylene-butylene-styrene). An independent claim is also included for products made from a TPE-like composition containing PP/EPDM (polypropylene/ethylene-propylene-diene rubber).

Description

Die Erfindung betrifft ein Erzeugnis aus einer thermoplastischen Elastomeren (TPE) ähnlichen Zusammensetzung, die aus Gummimehl mit mindestens einem Thermoplasten und einem oder mehreren Vernetzungsmitteln im Prozeß des Schmelzmischens hergestellt ist.The The invention relates to a product made from a thermoplastic elastomer (TPE) similar Composition made of rubber powder with at least one thermoplastic and one or more crosslinking agents in the process of melt blending is made.

Ein Verfahren zum Herstellen von TPE-ähnlichen Zusammensetzungen ist beispielsweise aus dem Dokument DE 196 07 281 A1 bekannt. Bei dem bekannten Verfahren wird zum werkstofflichen Recycling von Alt- und Abfallgummi ein Gummimehl auf Basis des Alt- und Abfallgummis mit Thermoplasten und einem oder mehreren Vernetzungsmitteln in unterschiedlichen Masseverhältnissen im Prozeß des Schmelzmischens zu einer Zusammensetzung (Compound) mit TPE-ähnlichen Eigenschaften verarbeitet, wobei beim Schmelzmischen die Thermoplastkomponente aufgeschmolzen und nachfolgend die Elastomer und/oder die Thermoplastkomponente dynamisch stabilisiert werden. Beim Prozeß der dynamischen Stabilisation vernetzen die Polyme stabilisiert werden. Beim Prozeß der dynamischen Stabilisation vernetzen die Polymere durch die Dynamik des Mischprozesses, was mit einer Änderung der Morphologie der Polymere einhergeht. Das Gummimehl wird in die Thermoplastmatrix eingebunden bzw. in dieser verteilt. Es entsteht eine Zusammensetzung (Compound) aus Alt- und Abfallgummimehl, Thermoplast und Vernetzer(n). Auf Basis der Zusammensetzung können verschiedene Erzeugnisse hergestellt werden, beispielsweise Halbzeuge oder Formteile wie Manschetten und Dichtungen sowie Stoßfänger und Verkleidungen im Kraft- und Schienenfahrzeugbau. Auch Behälter, Kübel oder Abdeckungen im Straßen- und Rohrleitungsbau können mit Hilfe unterschiedlicher Verfahren und unter Verwendung der Zusammensetzung gefertigt werden, zum Beispiel mittels Spritzgießen, Extrusion, Walzen, Kalandieren oder Pressen.For example, one method of making TPE-like compositions is from the document DE 196 07 281 A1 known. In the known method, a rubber powder based on the used and waste rubber with thermoplastics and one or more crosslinking agents in different mass ratios in the process of melt blending is processed into a composition (compound) with TPE-like properties for mechanical recycling of waste and waste rubber during melt mixing, the thermoplastic component is melted and subsequently the elastomer and / or the thermoplastic component are dynamically stabilized. In the process of dynamic stabilization, the polyme crosslinks are stabilized. In the process of dynamic stabilization, the polymers crosslink through the dynamics of the mixing process, which is accompanied by a change in the morphology of the polymers. The rubber dust is incorporated into the thermoplastic matrix or distributed in this. The result is a composition (compound) of waste and waste rubber, thermoplastic and crosslinker (s). Based on the composition of various products can be produced, for example, semi-finished or molded parts such as collars and gaskets and bumpers and linings in power and rail vehicle. Even containers, buckets or covers in road and pipeline construction can be manufactured by means of different methods and using the composition, for example by means of injection molding, extrusion, rolling, calendering or pressing.

In dem Dokument EP 1 144 493 B1 wird vorgeschlagen, daß bekannte Herstellungsverfahren für die TPE-ähnliche Zusammensetzung dahingehend fortzubilden, daß zunächst wenigstens ein Polypropylen-Co-Polymerisat oder ein Gemisch dessen mit wenigstens einem Polypropylen-Typen im Mischaggregat aufgeschmolzen und danach der Schmelze dosiert Gummimehl, von dem zumindest ein Teil in einem Radikaldonator vorgequollen ist, zugegeben wird. Das Gummimehl wird durch Aufbringen hoher Scherdeformationen und unter Mischparameter abhängigem Zusatz radikalbildender Agenzien zur Phasenkopplung zwischen dem Gummimehl und dem Polypropylen-Co-Polymerisat oder dessen Gemisches in der Kunststoffmatrix dispergiert. Der dynamische Stabilisierungsprozeß erfolgt bei einer Mischguttemperatur, die oberhalb des Schmelztemperaturbereiches des Polypropylen-Co-Polymerisats oder dessen Gemisches, jedoch unterhalb des Zersetzungstemperaturbereiches des Gummimehls liegt, und bei einer Mischzeit, die eine Reaktion des Radikalbildners ermöglicht.In the document EP 1 144 493 B1 It is proposed that known manufacturing processes for the TPE-like composition further develop to the effect that first melted at least one polypropylene copolymer or a mixture thereof with at least one type of polypropylene in the mixing unit and then the melt metered rubber powder, of which at least a part in a preselected Radikaldonator is added. The rubber dust is dispersed in the plastic matrix by applying high shear deformations and mixing parameter dependent addition of free radical generating agents for phase coupling between the gum and the polypropylene copolymer or its mixture. The dynamic stabilization process is carried out at a mixed product temperature which is above the melting temperature range of the polypropylene copolymer or mixture thereof, but below the decomposition temperature range of the rubber meal, and at a mixing time allowing reaction of the radical generator.

Aufgabe der Erfindung ist es ein Erzeugnis der eingangs genannten Art dahingehend zu verbessern, daß eine Zusammensetzung mit verbesserten Materialeigenschaften zur Verfügung gestellt ist.task According to the invention, it is a product of the type mentioned in the introduction to improve that one Composition provided with improved material properties is.

Diese Aufgabe wird erfindungsgemäß durch ein Erzeugnis nach dem unabhängigen Anspruch 1 und dem nebengeordneten Anspruch 2 gelöst.These The object is achieved by a Product after the independent Claim 1 and the independent claim 2 solved.

Die Erfindung umfaßt den Gedanken, daß ein Erzeugnis aus einer thermoplastischen Elastomeren (TPE) ähnlichen Zusammensetzung (Compound) ist, bei der Gummimehl mit mindestens einem Thermoplasten und einem oder mehreren Vernetzungsmitteln im Prozeß des Schmelzmischens verarbeitet ist, wobei die Zusammensetzung einen Anteil an SEBS (Styrol-Ethylen-Butylen-Styrol) oder PP/EPDM (Polypropylen/Ethylen-Propylen-Dien-Kautschuk) enthält. Es hat sich überraschender Weise gezeigt, daß mit Hilfe des Zusatzes von SEBS oder PP/EPDM Zusammensetzungen (Compounds) herstellbar sind, die im Vergleich zu den bekannten Zusammensetzungen weicher sind. Die weichere Materialausbildung vergrößert die Möglichkeiten für die Verwendung der aus der Zusammensetzung hergestellten Erzeugnisse. Darüber hinaus wurde festgestellt, daß bei der Zusammensetzung eine unangenehme Geruchsausbildung vermindert oder sogar vollständig beseitigt ist.The Invention the thought that one Product of a thermoplastic elastomer (TPE) similar Composition (compound) is at the rubber flour with at least a thermoplastic and one or more crosslinking agents in the Process of Melt blending is processed, the composition of a Proportion of SEBS (styrene-ethylene-butylene-styrene) or PP / EPDM (polypropylene / ethylene-propylene-diene rubber) contains. It has become surprising shown that with Help the addition of SEBS or PP / EPDM compositions (compounds) produced are softer compared to the known compositions are. The softer material training increases the possibilities for use the products made from the composition. Furthermore was found at the composition reduces an unpleasant odor formation or even completely eliminated.

Es kann vorgesehen sein, daß das Gemisch von Gummimehl mit dem mindestens einen Thermoplasten und dem einen oder den mehreren Vernetzungsmitteln SEBS oder PP/EPDM als Füllstoff zugegeben ist. Des weiteren kann eine Weiterbildung vorsehen, daß SEBS oder PP/EPDM dem Gemisch von Gummimehl mit dem mindestens einen Thermoplasten und dem einen oder den mehreren Vernetzungsmitteln zugegeben ist.It can be provided that the Mixture of rubber powder with the at least one thermoplastic and the one or more crosslinking agents SEBS or PP / EPDM as a filler is added. Furthermore, a further development can provide that SEBS or PP / EPDM the mixture of rubber powder with the at least one thermoplastic and the one or more crosslinking agents.

SEBS oder PP/EPDM können in vollvernetzer, teilvernetzter oder nichtvernetzter Ausbildung verwendet sein.SEBS or PP / EPDM used in fully crosslinked, partially crosslinked or non-crosslinked training be.

Es hat sich gezeigt, daß als Thermoplast für die Mischung mit dem Gummimehl zum Ausbilden einer Thermoplast-Matrix ein weichgemachtes Polypropylen verwendet werden kann, insbesondere ein Reaktorpolypropylen.It has been shown that as Thermoplastic for the Mixture with the rubber dust to form a thermoplastic matrix a plasticized polypropylene can be used, in particular a reactor polypropylene.

Es kann vorgesehen sein, daß beim Verarbeiten ein Polyolefin-Elastomer zugegeben ist.It can be provided that the Processing a polyolefin elastomer is added.

Beim Herstellen der Zusammensetzung können SEES und/oder PP/EPDM je nach Anwendungsfall mit unterschiedlicher Härte und in unterschiedlicher Konzentration verwendet werden. Bei der Verwendung des weichlgemachten Polypropylens kann auch dieses in Abhängigkeit vom Anwendungsfall in unterschiedlicher Härte genutzt werden, um das Matrixmaterial für das Gummimehl zu bilden.When preparing the composition kön Depending on the application, SEES and / or PP / EPDM can be used with different hardness and in different concentrations. In the case of the use of the plasticized polypropylene, this too can be used to different hardness depending on the application, in order to form the matrix material for the rubber powder.

Die Zugabemengen von SEBS, PP/EPDM, dem weichgemachten Polypropylen und/oder dem Polyolefin-Elastomer im Rahmen des Compoundierprozesses können in Abhängigkeit von den gewünschten Eigenschaften der hergestellten Zusammensetzung individuell gewählt werden. Bei dem Polyolefin-Elastomer kann es sich beispielsweise um eine Verbindung auf Basis von Ethylen-Butene handeln.The Addition amounts of SEBS, PP / EPDM, the plasticized polypropylene and / or the polyolefin elastomer in the context of the compounding process can dependent on from the desired ones Properties of the composition produced are chosen individually. The polyolefin elastomer may be, for example, a Acting compound based on ethylene butenes.

Als Gummimehl wird bevorzugt ein Gummimehl aus Alt- oder Abfallgummi, beispielsweise aus Altreifen verwendet.When Rubber dust is preferably a rubber dust from waste or old gum, used for example from old tires.

Die in der vorstehenden Beschreibung und den Ansprüchen offenbarten Merkmale der Erfindung können sowohl einzeln als auch in beliebiger Kombination für die Verwirklichung der Erfindung in ihren verschiedenen Ausführungsformen von Bedeutung sein.The in the foregoing description and in the claims disclosed features of Invention can both individually and in any combination for the realization of the invention in its various embodiments of importance.

Claims (9)

Erzeugnis, insbesondere Formteil oder Halbzeug, aus einer thermoplastischen Elastomeren (TPE) ähnlichen Zusammensetzung, die aus Gummimehl mit mindestens einem Thermoplasten und einem oder mehreren Vernetzungsmitteln im Prozeß des Schmelzmischens hergestellt ist, dadurch gekennzeichnet, daß die TPE-ähnliche Zusammensetzung einen Anteil von SEBS (Styrol-Ethylen-Buthylen-Styrol) enthält.A product, in particular a molded part or a semi-finished product, of a thermoplastic elastomers (TPE) -like composition produced from rubber powder containing at least one thermoplastic and one or more crosslinking agents in the process of melt blending, characterized in that the TPE-like composition comprises a proportion of SEBS ( Styrene-ethylene-butylene-styrene). Erzeugnis, insbesondere Formteil oder Halbzeug, aus einer thermoplastischen Elastomeren (TPE) ähnlichen Zusammensetzung, die aus Gummimehl mit mindestens einem Thermoplasten und einem oder mehreren Vernetzungsmitteln im Prozeß des Schmelzmischens hergestellt ist, dadurch gekennzeichnet, daß die TPE-ähnliche Zusammensetzung einen Anteil von PP/EPDM (Polypropylen/Ethylen-Propylen-Dien-Kautschuk) enthält.Product, in particular molding or semi-finished, from a thermoplastic elastomer (TPE) -like composition, the from rubber dust with at least one thermoplastic and one or more several crosslinking agents prepared in the process of melt blending is, characterized in that the TPE-like Composition a proportion of PP / EPDM (polypropylene / ethylene-propylene-diene rubber) contains. Erzeugnis nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß in der TPE-ähnlichen Zusammensetzung das Gummimehl, welches mit dem mindestens einen Thermoplasten und einem oder mehreren Vernetzungsmitteln verarbeitet wird, SEBS und/oder PP/EPDM als Füllstoff zugegeben ist.Product according to claim 1 or 2, characterized that in the TPE-like Composition the rubber powder containing at least one Thermoplastics and one or more crosslinking agents processed is added, SEBS and / or PP / EPDM as a filler. Erzeugnis nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß in der TPE-ähnlichen Zusammensetzung SEBS und/oder PP/EPDM dem Gummimehl, welches mit dem mindestens einen Thermoplasten und einem oder mehreren Vernetzungsmitteln verarbeitet wird, als Zugabe zugegeben ist.Product according to claim 1 or 2, characterized that in the TPE-like Composition SEBS and / or PP / EPDM the rubber powder, which with the at least one thermoplastic and one or more crosslinking agents is processed, is added as an addition. Erzeugnis nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß SEBS und/oder PP/EPDM in vollvernetzter, teilvernetzter oder nicht vernetzter Ausbildung zugegeben sind.Product according to one of claims 1 to 4, characterized that SEBS and / or PP / EPDM in fully crosslinked, partially crosslinked or non-crosslinked Training are added. Erzeugnis nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß das mindestens eine Thermoplast ein weichgemachtes Polypropylen ist.Product according to one of claims 1 to 5, characterized that this at least one thermoplastic is a plasticized polypropylene. Erzeugnis nach Anspruch 6, dadurch gekennzeichnet, daß das weichgemachte Polypropylen Reaktorpolypropylen ist.Product according to claim 6, characterized that this plasticized polypropylene reactor polypropylene. Erzeugnis nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß die TPE-ähnliche Zusammensetzung einen Anteil eines Polyolefin-Elastomers enthält.Product according to one of claims 1 to 7, characterized that the TPE-like Composition contains a proportion of a polyolefin elastomer. Erzeugnis nach einem vier Ansprüche 1 bis 8, dadurch gekennzeichnet, daß die TPE-ähnliche Zusammensetzung einen Anteil an Ethylen-Buten-Elastomer enthält.Product according to one of claims 4 to 8, characterized that the TPE-like Composition contains a proportion of ethylene-butene elastomer.
DE202004020593U 2004-04-15 2004-04-15 Products or semi-finished products for use e.g. as seals or panels in cars, made from a thermoplastic elastomer-like composition containing rubber powder, thermoplastic, crosslinker and SEBS copolymer Expired - Lifetime DE202004020593U1 (en)