DE202004008134U1 - Thermally loadable glass ceramic or glass body decorated with a color based on a silicate melt containing effect pigments useful for cooking surfaces, e.g. baking ovens, lamp coatings - Google Patents

Thermally loadable glass ceramic or glass body decorated with a color based on a silicate melt containing effect pigments useful for cooking surfaces, e.g. baking ovens, lamp coatings Download PDF

Info

Publication number
DE202004008134U1
DE202004008134U1 DE202004008134U DE202004008134U DE202004008134U1 DE 202004008134 U1 DE202004008134 U1 DE 202004008134U1 DE 202004008134 U DE202004008134 U DE 202004008134U DE 202004008134 U DE202004008134 U DE 202004008134U DE 202004008134 U1 DE202004008134 U1 DE 202004008134U1
Authority
DE
Germany
Prior art keywords
glass
glass ceramic
body according
glass body
effect pigments
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202004008134U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Schott Spezialglass GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schott Spezialglass GmbH filed Critical Schott Spezialglass GmbH
Priority to DE202004008134U priority Critical patent/DE202004008134U1/en
Priority claimed from DE102004022257A external-priority patent/DE102004022257B9/en
Publication of DE202004008134U1 publication Critical patent/DE202004008134U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

A thermally loadable glass ceramic or glass body decorated with a color based on a silicate melt containing effect pigments, i.e. special effect pigments which show a Color-Flop-Effect.

Description

Die Erfindung bezieht sich auf einen thermisch hochbelastbaren Glaskeramik- oder Glaskörper, dekoriert mit einer Farbe auf der Basis einer silikatischen Schmelze, die mit Effektpigmenten versehen ist.The invention relates to a Glass ceramic or glass body with high thermal resistance, decorated with a color based on a silicate melt that is provided with effect pigments.

Derartige Farben auf der Basis einer silikatischen Schmelze sind typischerweise keramische Farben mit einem Glasfluß als Basis. Diese Farben werden bei sehr hohen Temperaturen auf dem Trägerkörper gebrannt.Such colors based on a silicate melt are typically ceramic colors with a glass flow as Base. These colors are burned on the carrier body at very high temperatures.

Indem man dieser Farbbasis Effektpigmente beimischt, werden dem mit dieser Farbe dekorierten Glaskeramik- bzw. Glaskörper neben der Farbe zusätzliche Eigenschaften (Effekte) verliehen. Typische Effektpigmente sind die Glanzpigmente, insbesondere die Metalleffektpigmente, die einen metallähnlichen Glanz erzeugen.By using this color base effect pigments are added to the glass ceramic decorated with this color or vitreous in addition to the color additional Properties (effects) conferred. Typical effect pigments are the glossy pigments, especially the metallic effect pigments, some metal-like Create shine.

Glaskeramik- oder Glaskörper, die mit vorgenannten Farben, die Glanzpigmente enthalten, dekoriert sind, sind insbesondere als Glaskeramikplatten oder Platten aus vorgespanntem Spezialglas mit einem niedrigen thermischen Ausdehnungskoeffizienten, wie Borosilicatglas, die typischerweise als Kochflächen in Kochfeldern eingesetzt werden, d.h. thermisch hochbelastbar sind, ausgebildet. Aber auch beispielsweise Kaminsichtscheiben, Sichtfenster von Backöfen oder Lampenabdeckungen aus diesen Materialien, die ebenfalls thermisch stark belastet sind, werden im steigenden Maße mit vorgenannten Farben dekoriert.Glass ceramic or vitreous body are decorated with the aforementioned colors, which contain luster pigments, are in particular as glass ceramic plates or plates made of tempered Special glass with a low coefficient of thermal expansion, such as borosilicate glass, typically used as cooking surfaces in Hobs are used, i.e. can withstand high thermal loads, educated. But also, for example, fireplace viewing windows, viewing windows of ovens or lamp covers made from these materials, which are also thermal are heavily loaded, are increasingly with the aforementioned colors decorated.

Da insbesondere Kochflächen von Kochfeldern in modernen Küchen wegen ihrer Großflächigkeit auffällig sind und das stark kundenabhängige Design maßgebend beeinflussen, das auch von Land zu Land verschieden ist, werden in zahlreichen Schriften die unterschiedlichsten Dekorierungen beschrieben. Sie reichen von einfachen Mustern, z.B. als Firmenlogo und Kochzonenmarkierungen bis hin zu komplexen Vollflächen-Dekoren. Neben dem Design kommt es dabei auch insbesondere auf Kratzschutz gegen oberflächige Kratzer und Verminderung der Auffälligkeit gegenüber Verschmutzungen, z.B. Fingerabdrücken und Metallabrieb sowie von Gebrauchsspuren an. Derartige Dekore und ihre Aufbringung auf eine Glaskeramikplatte werden beispielsweise in der DE 44 26 234 C1 (= EP 0 693 464 B1 ) und der DE 34 33 880 C2 beschrieben. Weitere dekorierte Kochflächen zeigen die DE 197 28 881 C1 (= DE 297 11 916 U1 ), die DE 100 14 373 C2 und die DE 200 19 210 U1 . Die beiden letzteren Schriften beschreiben auch Dekore mit Sol-Gel-basierten Farben, die Metalleffekt-, Perlglanz-oder Interferenz-Pigmente, d.h. Effektpigmente enthalten, die einen Metallikeffekt in der Farbe bewirken. Aber auch mit derartigen Pigmenten versehene glasflussbasierte, d.h. keramische Metallikfarben sind Stand der Technik.Since the cooking surfaces of hobs in modern kitchens are particularly striking because of their large surface area and significantly influence the strongly customer-dependent design, which also differs from country to country, a wide variety of decorations are described in numerous fonts. They range from simple patterns, e.g. as company logos and cooking zone markings, to complex full-surface decors. In addition to the design, scratch protection against superficial scratches and reduction of the conspicuousness against dirt, such as fingerprints and metal abrasion as well as signs of wear and tear are important. Such decors and their application to a glass ceramic plate are, for example, in the DE 44 26 234 C1 (= EP 0 693 464 B1 ) and the DE 34 33 880 C2 described. More decorated cooking surfaces show the DE 197 28 881 C1 (= DE 297 11 916 U1 ), the DE 100 14 373 C2 and the DE 200 19 210 U1 , The latter two documents also describe decorations with sol-gel-based colors which contain metallic effect, pearlescent or interference pigments, ie effect pigments which bring about a metallic effect in the color. However, glass flow-based, ie ceramic metallic colors provided with such pigments are also state of the art.

Ein solches Perlglanzpigment auf der Basis beschichteter Glimmerplättchen ist beispielsweise unter der Marke IRIODIN® (Fa. Merck) auf dem Markt.Such a pearlescent pigment based on coated mica flakes is on the market, for example, under the IRIODIN ® brand (Merck).

In bestimmten Marktsegmenten, speziell zur Anpassung an Aluminium- und Edelstahlfächen in modernen Küchen, haben derartig dekorierte Glas-/Glaskeramik-Kochflächen mit einem Metallikeffekt einen hohen Stellenwert.In certain market segments, specifically to adapt to aluminum and Edelstahlfächen in modern kitchens, have such decorated glass / glass ceramic cooktops a metallic effect is very important.

Bisherige in der Praxis verwendete keramische Farben für die Dekoration von Glas- bzw. Glaskeramik-Kochflächen, Kaminsichtscheiben und anderen thermisch hochbelasteten Flachglasprodukten sind Systeme, welche ein oder mehrere Glasflüsse gemischt mit Farbpigmente(n) und ggf. Füllstoffe beinhalten. Nach dem Einbrand ergibt die Farbe eine mehr oder weniger homogene Beschichtung einer bestimmten Farbgebung. Im Falle der unter der Marke IRIODIN® bekannt gewordenen Pigmente und bei anderen Effektpigmenten wird diese Farbgebung zusätzlich durch die unterschiedliche Lichtreflexion auf den beschichteten Glimmerplättchen intensiviert, was zu den bekannten „Metallikeffekten" keramischer Farben führt.Previously used ceramic paints for the decoration of glass or glass ceramic cooktops, fireplace panes and other thermally highly stressed flat glass products are systems that contain one or more glass flows mixed with color pigments and possibly fillers. After firing, the color results in a more or less homogeneous coating of a certain color. In the case of the pigments known under the brand IRIODIN ® and other effect pigments, this coloring is additionally intensified by the different light reflection on the coated mica platelets, which leads to the known "metallic effects" of ceramic colors.

Nachteil der vorgenannten Farben ist es, daß die Auffälligkeit von Gebrauchsspuren, Kratzern, Metallabrieb von Kochtöpfen, etc. auf den Kochflächen etc. mehr oder weniger stark ausgeprägt ist, weil die intakten Farben der Dekorierung ein homogenes Bild für das menschliche Auge bieten. Jede Unterbrechung der Homogenität wird somit sofort registriert und als störend empfunden.Disadvantage of the aforementioned colors is it that the conspicuity signs of wear, scratches, metal abrasion from saucepans, etc. on the cooking surfaces etc. is more or less pronounced because of the intact colors offer a homogeneous image to the human eye for decoration. Any break in homogeneity is thus registered immediately and perceived as annoying.

Der Erfindung liegt daher die Aufgabe zugrunde, thermisch hochbelastbare Glaskeramik- oder Glaskörper mit einer solchen Farbe auf der Basis einer silikatischen Schmelze, die mit speziellen Effektpigmenten versehen ist, zu dekorieren, die eine verminderte Auffälligkeit von Gebrauchsspuren, Kratzern, Metallabrieb gegenüber den bekannten, dekorierten Glaskeramik- bzw. Glaskörpern bewirkt.The invention is therefore the object based on glass ceramic or glass body with high thermal resistance such a color based on a silicate melt, which is provided with special effect pigments, which is a reduced conspicuousness of signs of wear, scratches, metal abrasion compared to the known, decorated glass ceramic or glass bodies causes.

Die Lösung dieser Aufgabe gelingt gemäß der Erfindung dadurch, daß die silikatische Schmelze im vorgegebenen Anteil Spezial-Effektpigmente enthält, die auf dem dekorierten Glaskeramik- oder Glaskörper einen Farb-Flop-Effekt zeigen.This task is solved according to the invention in that the contains silicate melt in the specified proportion special effect pigments that a color flop effect on the decorated glass ceramic or glass body demonstrate.

Durch die Verwendung bestimmter Effektpigmente, insbesondere von speziellen Interferenz- oder Perglanzpigmenten, können Farben mit einem sogenannten Farb-Flop-Effekt, auch changierender oder Flip-Flop-Effekt genannt, hergestellt werden. Farben mit solchen Pigmenten ändern den Farbton mit dem Betrachtungswinkel. Die Hauptfarbe kommt nur bei einem bestimmten Winkel, dem Glanzwinkel, kräftig zur Geltung. Welche Farbtöne man aus anderen Betrachtungswinkeln sieht, hängt von einer Reihe von Faktoren, insbesondere von der Farbe des Träger-Untergrundes ab.By using certain effect pigments, especially of special interference or pearlescent pigments, can Colors with a so-called color flop effect, also iridescent or flip-flop effect called, are produced. Colors with such pigments change that Hue with the viewing angle. The main color only comes with at a certain angle, the glossy angle, it really stands out. What shades to choose from different viewing angles depends on a number of factors in particular on the color of the substrate.

Durch die Verwendung solcher Farben gelingt es, die Auffälligkeit der Gebrauchsspuren, Kratzer etc. auf dem Weg zu verringern, daß man einen raffinierten Farbtonwechsel je nach Betrachtungswinkel einstellt („Farb-Flop") und damit das menschliche Gehirn die Gebrauchsspuren nicht mehr wahrnimmt.By using such colors, it is possible to notice the signs of wear, scratches, etc. on the way to reduce that a subtle change of color depending on the viewing angle is set ("color flop") and thus the human brain no longer notices the signs of use.

Für die Dekoration von Glaskeramik und Spezialgläsern, speziell für die Anwendungen Kochfläche, Kaminsichtscheiben etc. werden daher im speziellen geeignete Glasflüsse mit Farb-Flop-Spezialpigmenten gemischt. Daraus ergibt sich ein Multicolor-Effekt, der z.B. von Grün zu Grau, von Grün zu Violett oder von Gold zu Altrosa wechselt, alleine durch Änderung des Betrachtungwinkels.For the decoration of glass ceramics and special glasses, especially for the applications Cooking surface, fireplace windows etc., therefore, special glass flows are mixed with special color flop pigments. This results in a multicolor effect that e.g. from green to gray, of green changes to violet or from gold to dusky pink, just by changing the viewing angle.

Diese Effektpigmente, die einen Farb-Flop-Effekt bewirken, sind zwar an sich bekannt, es lag jedoch nicht nahe, sie in Farben mit einer silikatischen Schmelze als Basis zu verwenden, weil sie nicht branchenüblich sind und ihre Temperaturbeständigkeit gemäß Herstellerangaben nicht ausreichend für den Einsatz in derartigen Farben mit einer silikatischen Schmelze als Basis ist (stabil bis 230° C gemäß Technical Data Sheet des Herstellers vom Feburar 2003 bzw. Juni 2002). Gemäß Produktinformationen vom Hersteller Merck finden sie daher stets in organischen Matrixen Verwendung, wie z.B. im Automobilbau, in Kunststoffen, in Druckfarben und Lacken.These effect pigments have a color flop effect are known per se, but it was not an obvious choice to be used in colors with a silicate melt as a base, because they are not common in the industry are and their temperature resistance according to the manufacturer's instructions not sufficient for use in such colors with a silicate melt as a basis (stable up to 230 ° C according to Technical Manufacturer's data sheet from February 2003 or June 2002). According to product information from the manufacturer Merck you will always find them in organic matrixes Use such as in automotive engineering, in plastics, in printing inks and paints.

Es war daher nicht ohne weiteres ersichtlich, daß diese Effektpigmente zum Dekorieren von thermisch hochbelastbaren Glaskeramik- oder Glaskörpern verwendbar wären. Überraschenderweise stellte sich heraus, daß durch das Einschließen der vorgenanten Pigmente in eine silikatische Schmelze, insbesondere einen Glasfluss, wie sie üblicherweise in der Dekoration von Glaskeramiken und Spezialgläsern verwendet werden, die Temperaturstabilität derart erhöht werden kann, daß sie ein völlig neues Anwendungsgebiet erhalten.It was therefore not easy evident that this Effect pigments for decorating glass ceramic or vitreous would be usable. Surprisingly it turned out that including the aforementioned pigments in a silicate melt, in particular a glass flow like they usually do used in the decoration of glass ceramics and special glasses be, the temperature stability so increased can be that she a completely get new application.

Gemäß einer Ausgestaltung der Erfindung besteht die Farb-Flop-Farbe aus einer silikatischen Schmelze als Basis, der Effektpigmente in Form von synthetisch hergestellten planparallelen Siliziumdioxid (SiO2)-Plättchen, die mit Metalloxiden belegt sind, in einem vorgegebenen Anteil zugesetzt sind.According to one embodiment of the invention, the color flop color consists of a silicate melt as a basis, the effect pigments in the form of synthetically produced plane-parallel silicon dioxide (SiO 2 ) platelets, which are coated with metal oxides, are added in a predetermined proportion.

Derartige Eftektpigmente zeigen einen ausgeprägten Farb-Flop-Effekt.Such effect pigments show one pronounced Color-flop effect.

Vorzugsweise werden dabei die entsprechenden Effektpigmente der Firma Merck, die unter der Marke Colorstream® im Handel sind, verwendet. Die hierbei verwendeten sehr dünnen und ebenen, optimal planparallelen Pigmentteilchen ermöglichen außergewöhnlich changierende Interferenzeffekte, d.h. einen Multicolor-Effekt. Selbst bei gedämpften Lichtverhältnissen kommt der Farbwechsel der Pigmente sehr gut zur Geltung. Die besondere Ästhetik ist dabei auf den weichen, fließenden Übergang der Farben zurückzuführen.Preferably while the corresponding effect pigments from Merck, which are under the brand ColorStream ® commercially used. The very thin and flat, optimally plane-parallel pigment particles used here enable extraordinarily changing interference effects, ie a multicolor effect. Even in dim lighting, the color change of the pigments comes into its own. The special aesthetics are due to the soft, flowing transition of the colors.

Durch unterschiedliche Beschichtungen der planparallelen SiO2-Colorstream®-Pigmentblättchen sind Farb-Flop-Pigmente in verschiedenen Farbtönen darstellbar, wie beispielsweise:Different coatings of the plane-parallel SiO 2 -Colorstream ® pigment flakes enable color flop pigments to be produced in different colors, such as:

  • 1. Colorstream® Autumn Mystery Die Farbe wechselt hierbei von Rot über ausdrucksstarkes Gold und Bronze bis Grün.1. Colorstream ® Autumn Mystery The color changes from red to expressive gold and bronze to green.
  • 2. Colorstream® Viola Fantasy Die Farbe wechselt hierbei von einem kräftigen Lila über Silber und Grün bis Blau.2. Colorstream ® Viola Fantasy The color changes from a strong purple to silver and green to blue.
  • 3. Colorstream® Arctic Fire Die Farbe wechselt hierbei von Türkis über brillantes Silber bis zu metallischem Rot und Gold.3. Colorstream ® Arctic Fire The color changes from turquoise to brilliant silver to metallic red and gold.

Vorzugsweise ist die Basis der keramischen Farbe mit den erfindungsgemäßen Farb-Flop-Pigmenten ein Glasfluss.Preferably the base is ceramic Color with the color flop pigments of the invention Glass river.

Vorzugsweise besitzt der Glasfluß eine Glaszusammensetzung (in Gew.-%) von: Li2O 0 – 5 Na2O 0 – 5 K2O < 2 ∑Li2O + Na2O + K2O 1 – 10 MgO 0 – 3 CaO 0 – 4 SrO 0 – 4 BaO 0 – 4 ZnO 0 – 4 B2O3 15 – 27 Al2O3 10 – 20 SiO2 43 – 58 TiO2 0 – 3 ZrO2 0 – 4 Sb2O3 0 – 2 F 0 – 3 The glass flow preferably has a glass composition (in% by weight) of: Li 2 O 0 - 5 Na 2 O 0 - 5 K 2 O <2 ∑Li 2 O + Na 2 O + K 2 O 1 - 10 MgO 0-3 CaO 0 - 4 SrO 0 - 4 BaO 0 - 4 ZnO 0 - 4 B 2 O 3 15-27 Al 2 O 3 10-20 SiO 2 43-58 TiO 2 0-3 ZrO 2 0 - 4 Sb 2 O 3 0-2 F 0-3

Diese Glaszusammensetzung des Glasflusses – im folgenden „GF1" genannt – entspricht derjenigen nach der DE 197 21 737 C1 , deren Offenbarungsinhalt durch Bezugnahme mit zum Offenbarungsumfang der vorliegenden Anmeldung gemacht wird.This glass composition of the glass flow - hereinafter referred to as "GF1" - corresponds to that after the DE 197 21 737 C1 , the disclosure content of which is made by reference to the disclosure scope of the present application.

Andere, je nach Anwendung einsetzbare Glaszusammensetzungen von Glasflüssen werden in DE 198 34 801 C2 , FR 2 732 960, EP 1 119 524 B1 , DE 42 01 286 A1 und EP 0 460 863 B1 beschrieben.Other glass compositions of glass flows that can be used depending on the application are described in DE 198 34 801 C2 , FR 2 732 960, EP 1 119 524 B1 . DE 42 01 286 A1 and EP 0 460 863 B1 described.

Neben den erfindungsgemäß dem Glasfluss zugesetzten speziellen Farb-Flop-Pigmenten können optional auch übliche Füllstoffe und/oder andere konventionelle Farbpigmente, beispielsweise Farbkörper (Spinelle) zugesetzt werden. So kommen insbesondere die Colorstream®-Effektpigmente in Kombination mit anderen Farbpigmenten, in sogenannte Stylings, erst richtig zur Geltung.In addition to the special color flop pigments added to the glass flow according to the invention, customary fillers and / or other conventional color pigments, for example colored bodies (spinels), can optionally also be added. In particular, the Colorstream ® effect pigments come into their own in combination with other color pigments, in so-called stylings.

Die Dekoration erfolgt vorzugsweise durch Siebdruck, insbesondere im Fall von Glas-/Glaskeramik-Kochflächen. Dabei waren besondere Schwierigkeiten in der Fertigungstechnik zu überwinden. Insbesondere bereitete die Anpastung/das Einstellen der richtigen Viskosität sowie die Korngröße der Pigmente für die Siebdruckanwendung besondere Probleme. Der Stand der Technik konnte hierzu keine Hinweise liefern, da die in Frage kommenden Farb-Flop-Pigmente, gelöst in organischen Lösungsmitteln, typischerweise bei ihrem Auftrag gesprüht werden, wie es insbesondere bei Autolacken der Fall ist.The decoration is preferably done by screen printing, especially in the case of glass / glass ceramic cooktops. there had to overcome special difficulties in manufacturing technology. In particular, the pasting / setting the right prepared viscosity as well as the grain size of the pigments for screen printing applications special problems. The prior art was unable to provide any information deliver because the color flop pigments in question, dissolved in organic solvents typically be sprayed on their order, as is particular is the case with car paints.

Die Dicke der erfindungsgemäßen Dekorierung liegt typischerweise im Bereich von 1,0 – 6 μm.The thickness of the decoration according to the invention is typically in the range of 1.0 - 6 μm.

Ausführungsbeispiele:EXAMPLES

  • 1. Glasfluss „GF1" (nach DE 197 21 737 C ) + 20 Effektpigmente Colorstream® T10 – 02 Arctic Fire multi color effect pigment, angepastet mit konventionellem Siebdruckmedium, bedruckt auf Gläsern/Glaskeramiken, die unter nachstehenden Markenprodukten bekannt geworden sind: a) CERAN HIGHTRANS® Kochflächen b) CERAN SUPREMA® Kochflächen c) ROBAX® Kaminsichtscheiben d) CERAN ARCTIC FIRE® Kochflächen e) CERADUR® Kochflächen ergibt jeweils einen Farb-Flop von Grün auf Violett mit verschiedenen Farbintensitäten, je nach Hintergrundfarbe des Trägers.1. Glass flow "GF1" (after DE 197 21 737 C. ) + 20 effect pigments Colorstream ® T10 - 02 Arctic Fire multi color effect pigment, pasted with conventional screen printing medium, printed on glasses / glass ceramics that have become known under the following branded products: a) CERAN HIGHTRANS ® cooktops b) CERAN SUPREMA ® cooktops c) ROBAX ® Fireplace viewing panels d) CERAN ARCTIC FIRE ® cooktops e) CERADUR ® cooktops each result in a color flop from green to violet with different color intensities, depending on the background color of the wearer.
  • 2. Glasfluss „GF1" + 20 % Effektpigmente Colorstream® F 10–00 Autumn Mystery multi color effect pigment + 3 % Schwarzpigmente M 91884 (Heraeus), angepastet mit Siebdruckmedium, bedruckt auf den gleichen Substraten wie im ersten Beispiel. Das ergibt jeweils einen Farb-Flop von Messing auf Altrosa mit verschiedenen Farbintensitäten, je nach Hintergrundfarbe des Trägers.2. Glass flow "GF1" + 20% effect pigments Colorstream ® F 10–00 Autumn Mystery multi color effect pigment + 3% black pigments M 91884 (Heraeus), pasted with screen printing medium, printed on the same substrates as in the first example. This results in one Color flop from brass to dusky pink with different color intensities, depending on the background color of the wearer.

Bei beiden Ausführungsbeispielen ist in den Substrat-Fällen a) und b) die Farbintensität am höchsten. Im Fall c) tritt der Farb-Flop-Effekt mit verminderter Farbintensität auf einer transparenten Mattierung auf bzw. in den Fällen d) und e) auf der Hintergrundfarbe „seidenweiß".In both embodiments is in the Substrate cases a) and b) the color intensity the highest. in the Case c) the color flop effect occurs with reduced color intensity transparent matting on or in cases d) and e) on the background color "silk white".

Claims (12)

Thermisch hochbelastbarer Glaskeramik- oder Glaskörper, dekoriert mit einer Farbe auf der Basis einer silikatischen Schmelze, die mit Effektpigmenten versehen ist, dadurch gekennzeichnet, daß die silikatische Schmelze im vorgegebenen Anteil Spezial-Effektpigmente enthält, die auf dem dekorierten Glaskeramik- oder Glaskörper einen Farb-Flop-Effekt zeigen.Glass ceramic or glass body that can withstand high thermal loads, decorated with a color based on a silicate melt, which is provided with effect pigments, characterized in that the silicate melt contains, in the predetermined proportion, special effect pigments which have a color on the decorated glass ceramic or glass body. Show flop effect. Glaskeramik- oder Glaskörper nach Anspruch 1, dadurch gekennzeichnet, daß die Spezial-Effektpigmente durch Pigmente in Form von synthetisch hergestellten, planparallelen Siliziumdioxid (SiO2)-Plättchen, die mit Metalloxiden belegt sind, gebildet sind.Glass ceramic or glass body according to claim 1, characterized in that the special effect pigments are formed by pigments in the form of synthetically produced, plane-parallel silicon dioxide (SiO 2 ) platelets which are coated with metal oxides. Glaskeramik- oder Glaskörper nach Anspruch 2, dadurch gekennzeichnet, daß die Speziel-Effektpigmente durch Effektpigmente der Firma Merck, die unter der Marke Colorstream® multi color effect pigments im Handel sind, gebildet sind.Glass ceramic or glass body according to claim 2, characterized in that the effect pigments through Speziel-effect pigments from Merck, which are under the trademark Colorstream ® multicolor effect pigments commercially, are formed. Glaskeramik- oder Glaskörper nach Anspruch 3, dadurch gekennzeichnet, daß das Effektpigment ein solches mit der Handelsbezeichnung Colorstream® Autumn Mystery ist.Glass ceramic or glass body according to claim 3, characterized in that the effect pigment is one with the trade name Colorstream ® Autumn Mystery. Glaskeramik- oder Glaskörper nach Anspruch 3, dadurch gekennzeichnet, daß das Effektpigment ein solches mit der Handelsbezeichnung Colorstream® Viola Fantasy ist.Glass ceramic or glass body according to claim 3, characterized in that the effect pigment is one with the trade name Colorstream ® Viola Fantasy. Glaskeramik- oder Glaskörper nach Anspruch 3, dadurch gekennzeichnet, daß das Effektpigment ein solches mit der Handelsbezeichnung Colorstream® Arctic Fire ist.Glass ceramic or glass body according to claim 3, characterized in that the effect pigment is one with the trade name Colorstream ® Arctic Fire. Glaskeramik- oder Glaskörper nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die silikatische Schmelze durch einen Glasfluß gebildet ist.Glass ceramic or glass body according to one of claims 1 to 6, characterized in that the silicate melt is formed by a glass flow. Glaskeramik- oder Glaskörper nach Anspruch 7, dadurch gekennzeichnet, daß der Glasfluß eine Glaszusammensetzung (in Gewicht-%) von Li2O 0 – 5 Na2O 0 – 5 K2O < 2 ∑Li2O + Na2O + K2O 1 – 10 MgO 0 – 3 CaO 0 – 4 SrO 0 – 4 BaO 0 – 4 ZnO 0 – 4 B2O3 15 – 27 Al2O3 10 – 20 SiO2 43 – 58 TiO2 0 – 3 ZrO2 0 – 4 Sb2O3 0 – 2 F 0 – 3
aufweist.Glass ceramic or glass body according to claim 7, characterized in that the glass flow has a glass composition (in% by weight) of Li 2 O 0 - 5 Na 2 O 0 - 5 K 2 O <2 ∑Li 2 O + Na 2 O + K 2 O 1 - 10 MgO 0-3 CaO 0 - 4 SrO 0 - 4 BaO 0 - 4 ZnO 0 - 4 B 2 O 3 15-27 Al 2 O 3 10-20 SiO 2 43-58 TiO 2 0-3 ZrO 2 0 - 4 Sb 2 O 3 0-2 F 0-3
having. Glaskeramik- oder Glaskörper nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß der silikatischen Schmelze neben den Spezial-Effektpigmenten übliche Füllstoffe und/ oder andere konventionelle Farbpigmente zugesetzt sind.Glass ceramic or glass body according to one of claims 1 to 8, characterized in that the silicate melt in addition to the special effect pigments usual fillers and / or other conventional color pigments are added. Glaskeramik- oder Glaskörper nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, daß die Dekorierung mittels Siebdruck gebildet ist.Glass ceramic or glass body according to one of claims 1 to 9, characterized in that the decoration is formed by means of screen printing. Glaskeramik- oder Glaskörper nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, daß der Pigmentanteil der Spezial-Effektpigmente im Bereich von 1 bis 30 Gew.-% liegt.Glass ceramic or glass body according to one of claims 1 to 10, characterized in that the pigment content the special effect pigments are in the range from 1 to 30% by weight. Glaskeramik- oder Glaskörper nach einem der Ansprüche 1 bis 11, ausgebildet als Kochfläche eines Kochfeldes mit der Dekorierung auf der Kochflächen-Oberseite.Glass ceramic or glass body according to one of claims 1 to 11, designed as a cooking surface of a hob with the decoration on the top of the hob.
DE202004008134U 2004-05-06 2004-05-06 Thermally loadable glass ceramic or glass body decorated with a color based on a silicate melt containing effect pigments useful for cooking surfaces, e.g. baking ovens, lamp coatings Expired - Lifetime DE202004008134U1 (en)