DE2016827A1 - Coloured, blown film produced from plastic granules - Google Patents
Coloured, blown film produced from plastic granulesInfo
- Publication number
- DE2016827A1 DE2016827A1 DE19702016827 DE2016827A DE2016827A1 DE 2016827 A1 DE2016827 A1 DE 2016827A1 DE 19702016827 DE19702016827 DE 19702016827 DE 2016827 A DE2016827 A DE 2016827A DE 2016827 A1 DE2016827 A1 DE 2016827A1
- Authority
- DE
- Germany
- Prior art keywords
- plastic
- color
- mixed
- colored
- coloured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Verfahren zum Herstellen eingefärbter Blasfolien aus Kunststoffgranulat.Process for producing colored blown films from plastic granulate.
Zum Herstellen eingefärbter Blasfolien aus Kunststoffgranulaten aus z.B. Polyäthylen ist es nicht möglich, das Farbpigmentpulver direkt in das Kunststoffgranulat, aus dem die Folie in einer Blasanlage geblasen werden soll, einzumischen. Die Farbpigmente agglomerieren statt sich gleichmäßig in dem Extrudat (Schmelze) zu verteilen und das Ergebnis ist eine ungleichmäßig eingefärbte Folie mit Farbpunkten und daneben kaum eingefärbten Stellen, wobei die die Farbpunkte bildenden agglomerierten Farbpigmente außerdem eine Herabsetzung der Pgstigkeit der Folie bewirken. Hinzu kommt noch, daß das Farbpigmentpulver, wenn es frei eingemischt wird, ausstaubt und aufgrund seiner starken Einfärbkraft die Kleidung der Bedienungspersonen und auch diese selbst einfärbt, welche Färbung mangels eines Lösungsmittels nicht wieder zu entfernen ist, so daß der Umgang mit freiem Farbpigmentpulver nicht zumutbar ist. Alles in allem kann in dieser Weise daher nicht vorgegangen werden.For the production of colored blown films from plastic granules E.g. polyethylene it is not possible to put the color pigment powder directly into the plastic granulate, from which the film is to be blown in a blow molding machine. The color pigments agglomerate instead of spreading evenly in the extrudate (melt) and the result is an unevenly colored film with colored dots and next to it hardly colored areas, whereby the agglomerated color pigments forming the color dots also cause a reduction in the stability of the film. Additionally, that the color pigment powder, when freely mixed in, dusts out and due to its strong coloring power, the clothes of the operators and they themselves colors which color cannot be removed due to the lack of a solvent is, so that the handling of free color pigment powder is not reasonable. All in everything can therefore not be proceeded in this way.
Um diese Nachteile zu vermeiden und eine vollkommen gleichmäßig eingefärbte Folie mit unbeeinträchtigten Festigkeitseigenschaften zu erhalten, hat man die Farbpigmente in einem vorgeschalteten, besonderen Arbeitsgang ~in Größenordnungen von 50 und mehr % in Kunststoff in der Weise eingemischt, daß in einem eigens für diesen Vorgang konstruierten Miscliextruder oder Kneter das Farbpigment mit Kunststoffgranulat gemischt, extrudiert und in einem separaten Arbeitsgang zerschnitten wird. Wegen des Wasseranteiles des Farbpigments ist dabei eine Entgasung erforderlich, die den Vorgang noch kompliziert und verteuert. Die Farbpigmente befinden sich in den dabei erzeugten sogenannten Farbkonzentraten QM#sterbatches") in einem Prozentsatz von etwa 50 und mehr %. Dieses Farbkonzentrat, das die Struktur von Granulat besitzt, wird dann in daß zu extrudierende Kunststoffgranulat eingemischt, staubt nicht und färbt nicht mehr ab und ergibt eine zufriedenstellend eingefärbte Folie. Der Nachteil ist der hohe Preis für das Parbkonzentrat, der das Endprodukt wesentlich verteuert.In order to avoid these disadvantages and a completely evenly colored To obtain a film with unimpaired strength properties, one has to use the color pigments in an upstream, special operation ~ in the order of 50 and more% mixed in plastic in such a way that in a special way for this process Mix extruders or kneaders constructed the color pigment with plastic granulate mixed, extruded and cut in a separate operation. Because of the water content of the color pigment a degassing is necessary, which the Process still complicated and expensive. The color pigments are in the included produced so-called color concentrates QM # sterbatches ") in a percentage of about 50 and more%. This color concentrate, which has the structure of granules, will then be in that to be extruded Plastic granulate mixed in, does not dust and no longer stains and results in a satisfactorily colored Foil. The disadvantage is the high price of the parb concentrate, which is the end product much more expensive.
Der Erfindung liegt die Aufgabe zugrunde, ein qualitativ gleichwertiges Einmischverfahren für Farbpigmente anzugeben, das einfach und daher billig ist, um die Herstellungskosten für eingefärbte Kunststoffolie herabzusetzen.The invention is based on the object of a qualitatively equivalent Specify a method of mixing in color pigments that is simple and therefore cheap, in order to reduce the production costs for colored plastic film.
Zur Lösung dieser Aufgabe wird nach der Erfindung vorgeschlagen, daß das Farbpigmentpulver mit pulverisiertem Kunststoff, vorzugsweise der gleichen Art wie das zu verblasende, gemischt wird, worauf dieses Gemisch in das zu verblasende Kunststoffgranulat in an sich bekannter Weise eingemischt wird. 3i diesem vorgesehlagenen'Verfahrenist es ebenfalls möglich, die pigmentverteilenden Zusätze zuzuschlagen, die bei der Herstellung von Masterbatches angewandt werden; z.B. hochmolekulare Polyäthylen-Wachse oder aber Stearate und ähnliche Produkte.To solve this problem it is proposed according to the invention that the colored pigment powder is mixed with pulverized plastic, preferably of the same type as that to be blown, whereupon this mixture is mixed into the plastic granulate to be blown in a manner known per se. In this proposed process it is also possible to add the pigment-distributing additives that are used in the production of masterbatches; eg high molecular weight polyethylene waxes or stearates and similar products.
Hierzu sind anstelle der teueren Mischextruderanlage lediglich eine Mühle zum Mahlen von Kunststoff und ein Mischer zum homogenen Einmischen des Parbpigmentes in den gemahlenen Kunststoff erforderlich, die billig sind und auch sehr schnell große Mengen bearbeiten können, wofür beim verstellen von Masterbatche eine zur Erzielung der gleichen Leistung außerordentlich teure Anlage eingesetzt werden müßte.Instead of the expensive mixing extruder system, there is only one Mill for grinding plastic and a mixer for homogeneous mixing in of the parb pigment required in the ground plastic, which are cheap and also very quick can process large quantities, for which when adjusting masterbatches a for Extremely expensive system would have to be used to achieve the same performance.
Die Farbpigmente haften überraschenderweise so gut an den Kunststoffpulverpartikelchen, daß kein Stauben und auch kein starkes Abfärben auftritt.Surprisingly, the color pigments adhere so well to the plastic powder particles, that no dusting and also no strong staining occurs.
Anstelle eines Kunststoffes mit gleichem Schmelzindex, der für die Masse des Extrudates eingesetst wird, kann für den geringen Anteil des zu mahlenden Kunststoffes für die fierstellung des Farbkonzentrates auch ein Kunststoff mit angehobenem Schmelzindex eingesetzt werden, wn eine noch bessere Verteilung des Farbpigmentes zu gewährleisten, so wie dieses auch bei de#r Herstellung von Masterbatches geübt wird.Instead of a plastic with the same melt index, which is suitable for the Mass of the extrudate is used, can be used for the small portion of the to be ground Plastic for the setting of the color concentrate also a plastic with raised Melt index are used, wn an even better distribution of the color pigment as is practiced in the manufacture of masterbatches will.
Xas Parbpigmentpulver ist vorzugsweise in der Größenordnung mehr als 20 0 in der Mischung mit dem gemahlenen Kunststoff enthalten, um den für eine bestimmte Einfärbung erforderlichen Prozentsatz des Farbkonzentrates in wirtschaftlicher Weise zu begrenzen.Xas parb pigment powder is preferably on the order of more than 20 0 contained in the mixture with the ground plastic, around the for a certain Coloring required percentage of the color concentrate in an economical manner to limit.
Die unter Verwendung des erfindungsgemäßen Pulvergemisches erzeugte eingefärbte Folie zeigt eine gute und gleichmäßige Einfärbung und erbringt eine wesentliche Ersparnis durch die niedrigeren Herstellungskosten.The one produced using the powder mixture according to the invention colored film shows good and even coloring and produces one substantial savings due to the lower manufacturing costs.
Das erfindungsgemäße Farbpigment-Kunststoffpulver-Gemisch läßt sich auch gut in Silos einlagern und pneumatisch fördern, ohne sich zu entmischen wie dieses der Fall ist, wenn man 8+B, Kunststoffgranulat mit Farbpigmenten vermischt.The color pigment / plastic powder mixture according to the invention can be can also be stored well in silos and conveyed pneumatically without separating like this is the case when 8 + B, plastic granulate is mixed with color pigments.
Im einzelnen ist so vorzugehen, daß der Kunststoff in einer Mühle, z.B. einer bekannten Pralltellermühle, zu Pulver vermahlen wird, dessen Korngröße zwischen 60 und 400 Mii, vorzugsweise zwischen 100 und 150 fim liegt, Anschließend wird in einem bekannten Mischer mit mittleren bis hohen Drehzahlen, wie solche beispielsweise in der Backpulverindustrie verwendet werden, das gewonnene Kunststoffpulver mit dem Farbpigmentpulver das dabei einen Anteil von mindestens 20 % haben sollte, gründlich gemischt. Das so gewonnene Farbkonzentrat mischt man dem Rohgranulat im zur Erzielung der gewünschten Einfärbung erforderlichen Verhältnis von vorzugsweise 1 bis 5 %+Farbpigment im Gesamtbereich vor dem Extrudieren in an sich bekannter Weise mittels eines Schnecken-Schnellmischers oder mittels Schüttelrinnen zu.In detail, proceed in such a way that the plastic is in a mill, e.g. a known impact plate mill, is ground to powder, the grain size of which between 60 and 400 mi, preferably between 100 and 150 microns, then is used in a known mixer with medium to high speeds, such as those for example Used in the baking powder industry, the obtained plastic powder with the color pigment powder, which should have a share of at least 20% mixed. The color concentrate obtained in this way is mixed with the raw granulate in order to achieve this the required color ratio of preferably 1 to 5% + color pigment in the overall area before extrusion in a manner known per se by means of a high-speed screw mixer or by means of vibrating chutes.
Während bei der Herstellung der üblichen Farbkonzentrate des Wasseranteils der Farbpigmente wegen#mit Entgasung gearbeitet werden muß, um das Poröswerden des Brzeugnisses zu vermeiden, treten bei dem erfindungsgemäßen Verfahren keine Schwierigkeiten hinsichtlich Feuchtigkeit, Wasserdampfbildung, Notwendigkeit für die Entgasung bzw. Poröswerden des Erzeugnisses auf 0 Der Prozentsatz, mit dem sich das Farbpigmentpulver in das Kunststoffpulver einmischen läßt, kann je nach art des Pigmentes zwischen 20 und 50 % betragen. Eine Vergleichsrechnung hat aber ergeben, daß bereits bei einem Sinmischungsprozentsatz von 20 /; das erfindungsgemäße Verfahren eine Verbilligung gegenüber der Verwendung der bekannten Farbkonzentrate bringt.While in the production of the usual color concentrates the water content of the color pigments because of # degassing must be used to prevent the There are no difficulties in the process according to the invention to avoid product with regard to moisture, water vapor formation, the need for degassing or Porosity of the product to 0 The percentage with which the colored pigment powder becomes can be mixed into the plastic powder, depending on the type of pigment between 20 and 50%. A comparative calculation has shown that already at a blend percentage of 20 /; the method according to the invention is cheaper brings compared to the use of the known color concentrates.
Claims (3)