DE2014011C - Release agent for the production of cold-foamed flexible foam molded parts - Google Patents
Release agent for the production of cold-foamed flexible foam molded partsInfo
- Publication number
- DE2014011C DE2014011C DE19702014011 DE2014011A DE2014011C DE 2014011 C DE2014011 C DE 2014011C DE 19702014011 DE19702014011 DE 19702014011 DE 2014011 A DE2014011 A DE 2014011A DE 2014011 C DE2014011 C DE 2014011C
- Authority
- DE
- Germany
- Prior art keywords
- release agent
- cold
- molded parts
- production
- foam molded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung betrifft ein Trennmittel zum Verhindern des Anhaftens von Weichschaumform teilen an den Formen mit einem Gehalt an Metallseifen.The invention relates to a release agent for preventing the sticking of flexible foam mold to share the forms with a content of metallic soaps.
Bei der Herstellung von Weichschaumformteilen nach der sogenannten Kaltverschäumung von Polyurethanschaum wird das Komponentengemisch in geschlossene Formen in einer derartigen Menge eingebracht, daß es gegen Ende des drucklosen Ausschäumens gerade das Innere der Form ausfüllt, wobei geringfügige Uberschußmengen durch hierfür vorgesehene Auslaßöffnungen entweichen können. Das hierbei entstehende hautlose Kaltschaumformteil ist durch ein besonders niedriges Raumgewicht gekennzeichnet.In the production of flexible foam molded parts after the so-called cold foaming of polyurethane foam the component mixture is introduced into closed molds in such an amount, that it just fills the interior of the mold towards the end of the pressureless foaming, wherein small excess quantities can escape through outlet openings provided for this purpose. This here The resulting skinless molded cold foam part is characterized by a particularly low density.
Für die einwandfreie Entformung derartiger KaItschaumformteile stand bisher noch kein Trennmittel zur Verfügung, das alle nachstehenden Bedingungen erfüllt:For the perfect demolding of such cold foam molded parts no release agent was available that met all of the following conditions Fulfills:
Es muß leicht anwendbar sein, d. h., es muß dünnflüssig sein, so daß es in die Form, z. B. mit einer Air-Iess-Sprühapparatur, eingesprüht werden kann. Die Formlinge müssen hautlos sein, d. h., ihre Oberfläche darf nur aus offenen oder geschlossenen Bläschen bestehen, die sich glatt, ohne zu zerreißen, von der Formoberfläche gelöst haben. Das Trennmittel darf auch nach zahlreichen Entformungen nicht »aufbauen«. Es ist ferner die Verwendung nur allgemein üblicher Verdünnungsmittel erwünscht.It must be easy to use; h., It must be thin so that it can be in the form, z. B. with an Air-Iess spray device, can be sprayed. The briquettes must be skinless, i. i.e., its surface may only consist of open or closed bubbles that can be removed smoothly from the surface of the mold without tearing have solved. The release agent must not "build up" even after numerous demouldings. It the use of only generally customary diluents is also desirable.
Es ist schon eine größere Zahl von Trennmitteln für die Kaltverschäumung empfohlen worden, wobei diese Trennmittel als wirksame Stoffe meistens Wachse, Fette. Öle, zum Teil auch Gemische dieser Produkte mit Metallseifen enthalten. Jedoch erfüllt keines dieser verwendeten Trennmittel die obenstehenden Bedingungen, insbesondere kommt es dabei leicht zu einem Anhaften der äußerst dünnen Bläschenhäutschen, die allmählich zu einer Ausbildung dickerer Schichten, dem sogenannten «Aufbauen«, führen.A large number of release agents for cold foaming have already been recommended, with these Release agents as active substances mostly waxes, fats. Oils, sometimes also mixtures of these products Contains metal soaps. However, none of these release agents used meet the above conditions, in particular, the extremely thin vesicle membranes that gradually adhere easily lead to the formation of thicker layers, the so-called "build-up".
Es wurde nun überraschenderweise gefunden, daß es möglich ist, Kaltschaumformteile glatt und einwandfrei zu entformen, ohne daß es zu einem Aufbauen im Innern der Form kommt, wenn man ein Trennmittel verwendet, welches erfindungsgemäß dadurch gekennzeichnet ist, daß es aus einer Lösung von etwa 0,5 bis 4,0 Gewichtsprozent Aluminiumtristearat und 0,005 bis 0,1 Gewichtsprozent Magnesiumoleat in einem flüssigen chlorierten Kohlenwasserstoff, vorzugsweise Trichloräthylen, besteht.It has now been found, surprisingly, that it is possible to produce molded cold foam parts smoothly and perfectly to demold without there being a build-up inside the mold, if you use a release agent used, which is characterized according to the invention is that it is made from a solution of about 0.5 to 4.0 weight percent aluminum tristearate and 0.005 to 0.1 weight percent magnesium oleate in a liquid chlorinated hydrocarbon, preferably Trichlorethylene.
Eine Lösung von Aluminiumtristearat allein in einem chlorierten Kohlenwasserstoff ist als Trennmittel ungeeignet, da sie bereits bei niedrigsten Konzentrationen gelartig eindickt, wobei gleichzeitig der erzielbarc Trenneffekt noch unzureichend ist. Außerdem ist ein nur aus Aluminiumtn .tearat bestehender Film zu spröde. Löst man jedoch zusammen mit Aluminiumtristearat eine sehr geringe, genau dotierte Menge Magnesiumoleat, so erhält man eine dünnflüssige Lösung von ausreichendem Festkörpergehalt, die einen harten, festen Film von guter Trennwirkung liefert. A solution of aluminum tristearate alone in a chlorinated hydrocarbon is unsuitable as a release agent, since it thickens like a gel even at the lowest concentrations, and at the same time the achievable release effect is still inadequate. In addition, a film consisting only of aluminum tearate is too brittle. However, if a very small, precisely doped amount of magnesium oleate is dissolved together with aluminum tristearate , a thin liquid solution of sufficient solids content is obtained, which provides a hard, solid film with good separating effect.
Die nachstehende Tabelle zeigt den Einfluß verschieden hoher Zusätze, von Magnesiumoleat zu Aluminiumtristearatlösung. Hierbei wurde eine Lösung on 1,0% Aluminiumtristearat in Trichloräthylen verwendet. Versuch 1 zeigt die Eigenschaft des nach dem Verdunsten des Lösungsmittels erhaltenen Trennfilms von Aluminiumtristearat allein, ohne Zusatz von Magnesiumoleat. Die folgenden Versuche 2 bis 5 zeigen die Wirkung steigender Zusätze von Magnesiumoleat auf die Konsistenz des gebildeten Trennfilms und auf seine Trennwirkung.The table below shows the influence of different amounts of additives, from magnesium oleate to aluminum tristearate solution. A solution of 1.0% aluminum tristearate in trichlorethylene was used here. Experiment 1 shows the property of the release film obtained after evaporation of the solvent of aluminum tristearate alone, without the addition of magnesium oleate. The following experiments 2 to 5 show the effect of increasing additions of magnesium oleate on the consistency of the release film formed and on its separating effect.
Zusatz %
Magnesiumoleat Additive %
Magnesium oleate
0,0050.005
0,010.01
0,050.05
0,10.1
l.u%ige Lösung von
Aluminiumtristearat inl. u % solution of
Aluminum tristearate in
Trichloräthylen
Film TrennwirkungTrichlorethylene
Film release effect
sprödebrittle
harthard
festfixed
zähtough
zähtough
schlecht
mißig
gutbad
miserable
Well
ziemlich gut
mäßigpretty good
moderate
Hieraus ist zu ersehen, daß bei einem Zusatz von 0,01 Gewichtsprozent Magnesiumoleat auf die l,O°/oige Aluminiumtristearatlösung (Versuch 3) ein optimales Ergebnis erhalten wird, da der nach dtm Verdunsten des Lösungsmittels erhaltene Film noch hart ist und eine gute Abtrennung bewirkt. Er neigt nicht zum sogenannten »Aufbauen«.It can therefore be seen that an optimum result is obtained at an addition of 0.01 weight percent magnesium oleate on the l, O ° / o strength Aluminiumtristearatlösung (Experiment 3), since the film obtained after dtm evaporation of the solvent is still hard and good Separation causes. He is not prone to so-called "building up".
Das folgende Beispiel zeigt die Verwendung eines erfindungsgemäßen Trennmittels.The following example shows the use of a release agent according to the invention.
Ein Trennmittel, hergestellt durch Lösen von 10 g Aluminiumtristearat und 0,1 g Magnesiumoleat in 1000 g Trichlorälhylen, wird in üblicher Weise, z. B. mit einer sogenannten Airless-Apparatur, in eine für die Herstellung von Kaltschaumformteilen eingerichtete Form eingesprüht, wobei nach dem Verdunsten des Lösungsmittels ein die ganze innere Oberfläche der Form ausfüllender, sehr dünner Trennfilm erhalten wird. Dieser ist glänzend, hart und braucht nicht poliert zu werden. Eine in einer derart vorbereiteten Form in bekannter Weise durchgeführte Kaltverschäumung von Polyurethanschaum liefert hautlose Formteile mit weicher, glatter, halbgeschlossener Oberfläche.A release agent made by dissolving 10 g of aluminum tristearate and 0.1 g of magnesium oleate in 1000 g of Trichlorälhylen is used in a conventional manner, for. B. with a so-called airless apparatus, in a for sprayed the production of cold foam molded parts set up form, after the evaporation of the Solvent obtained a very thin separating film that fills the entire inner surface of the mold will. This is shiny, hard and does not need to be polished. One in such a prepared form Cold foaming of polyurethane foam carried out in a known manner provides skinless molded parts soft, smooth, semi-closed surface.
Claims (1)