DE2012581B - Solid propellant of the forehead burner type containing explosive oil with a superficial, combustion-inhibiting solid coating - Google Patents
Solid propellant of the forehead burner type containing explosive oil with a superficial, combustion-inhibiting solid coatingInfo
- Publication number
- DE2012581B DE2012581B DE2012581B DE 2012581 B DE2012581 B DE 2012581B DE 2012581 B DE2012581 B DE 2012581B
- Authority
- DE
- Germany
- Prior art keywords
- propellant
- nitrate
- forehead
- thickness
- superficial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Die Erfindung betrifft einen Sprengöl enthaltenden Feststofftreibsatz vom Stirnbrennertyp mit einem oberflächlichen, die Verbrennung inhibierenden festen Belag und mit verminderter Neigung zur Rauchbildung, bei dem zwischen dem Treibsatzformkörper und dem Inhibitorbelag eine Schicht aus zweibasigern Treibpulver mit einem Gehalt an anorganischem Nitrat, besonders Alkali- oder Erdalkalinitrat, vorgesehen ist.The invention relates to a solid propellant containing blasting oil of the front burner type with a superficial, burn-inhibiting solid coating and with a reduced tendency to smoke, with a layer of two-base between the propellant shaped body and the inhibitor coating Propellant powder with a content of inorganic nitrate, especially alkali or alkaline earth nitrate, is provided is.
Bei einem bekannten derartigen Treibsatz wird der Gehalt des zweibasigen Treibpulvers an anorgani- so schem Nitrat auf etwa 20 % bemessen, während die aus diesem Pulver bestehende Schicht eine Stärke aufweisen soll, die die Stärke der Inhibitorschicht um etwa 15 bis 35 °/o übertrifft.In the case of a known propellant of this type, the content of the dibasic propellant powder is inorganic Shem nitrate measured at about 20%, while the layer consisting of this powder is a starch should have, which exceeds the thickness of the inhibitor layer by about 15 to 35%.
Überraschenderweise wurde nun gefunden, daß man bei Einarbeitung von mindestens 40 %, z. B. %, eines anorganischen Nitrates in das zweibasige Pulver die Stärke dieser rauchmindernden Zwischenschicht wesentlich geringer halten kann als diejenige der Inhibitorschicht und daß die Rauchbildung noch weiter vermindert wird. Man benötigt eine Zwischenschicht, deren Stärke nur 50 % oder weniger der Stärke der Inhibitorschicht beträgt. Die Herstellung dieser um 50 % anorganischer Nitrate enthaltenden zweibasigen Pulver ist nach der bekannten Herstellungsweise auf Walzwerken ohne Schwierigkeiten möglich.Surprisingly, it has now been found that with incorporation of at least 40%, for. B. %, an inorganic nitrate in the dibasic powder the strength of this smoke-reducing intermediate layer can keep much less than that of the inhibitor layer and that the smoke formation still is further reduced. You need an intermediate layer whose thickness is only 50% or less Thickness of the inhibitor layer. The production of these containing around 50% inorganic nitrates Dibasic powder is according to the known production method on rolling mills without difficulties possible.
Gegenstand der Erfindung ist somit bei einem wie eingangs erläuterten Treibsatz die Maßnahme, daß der Gehalt an anorganischem Nitrat in der Zwischenschicht auf mindestens 40 %> bemessen und gleichzeitig deren Stärke geringer als diejenige des Inhibitorbelages gehalten istThe subject matter of the invention is therefore the measure that in a propellant charge as explained at the beginning the content of inorganic nitrate in the intermediate layer to at least 40%> dimensioned and at the same time their thickness is less than that of the inhibitor coating is held
Bei einer Ausführungsform des erfindungsgemäßen Treibsatzes ist vorgesehen, daß der Gehalt an anorganischem Nitrat etwa 50 % beträgt. Fernerhin kaun man die Dicke der nitrathaltigen Zwischenschicht mit weniger als 50% der Stärke der Inhibitorschicht bemessen.In one embodiment of the propellant charge according to the invention it is provided that the content of inorganic Nitrate is around 50%. Furthermore, you can also see the thickness of the nitrate-containing intermediate layer dimensioned less than 50% of the thickness of the inhibitor layer.
Zweckmäßig werden Folien von einer Stärke zwischen 0,4 und 0,6 mm hergestellt, die in Streifen geschnitten in bekanntem Wickelverfahren unter Verwendung von Lösungsmitteln auf die Treibsatzkörper aufgebracht werden. Auf Stirnflächen von Treibstoffsätzen können, wenn notwendig, ebenfalls durch Aufkleben Folien aufgebracht werden. Nach Aufbringen der erfindungsgemäßen Zwischenschicht werden dieIt is expedient to produce foils with a thickness between 0.4 and 0.6 mm, which are cut into strips in a known winding process using solvents on the propellant bodies be applied. If necessary, they can also be affixed to the face of fuel sets Foils are applied. After the intermediate layer according to the invention has been applied, the
Treibsätze in an sich bekannter Weise inhibiert.Propellant charges inhibited in a manner known per se.
Die folgenden Beispiele zeigen die Rauchminderung am Beispiel eines Stirnbrenners.The following examples show the smoke reduction using the example of a forehead burner.
Die Stirnbrenner wurden aus einem heißen Pulver von 1000 cal/g Explosionswärme folgender Zusammensetzung gefertigt.The forehead burners were made from a hot powder of 1000 cal / g of explosive heat of the following composition manufactured.
Nitrocellulose mit 12,8% Stickstoff .. 48,3%Nitrocellulose with 12.8% nitrogen .. 48.3%
Nitroglycerin 41 %Nitroglycerin 41%
Ballistische Additive 3%Ballistic additives 3%
Weichmacher 5,2%Plasticizer 5.2%
Stabilisatoren 2,5%Stabilizers 2.5%
Die Abmessungen der isolierten Stirnbrenner betrugen: 50 mm Durchmesser und 120 mm Länge. Die Treibsätze waren mit einer Polyester-Inhibierung versehen, deren Stärke 2 mm betrug.The dimensions of the insulated forehead burners were: 50 mm in diameter and 120 mm in length. The propellant charges were provided with a polyester inhibition, the thickness of which was 2 mm.
Zur Rauchminderung wurden aus einer Mischung zweier Pulver folgender Zusammensetzung Folien von 0,5 mm Stärke gefertigt.To reduce smoke, a mixture of two powders with the following composition was made into films made of 0.5 mm thickness.
3030th
3535
mit 12,8% Stickstoff...
Nitroglycerin
Dibutylphthalat
Satbilisatoren
Centralit I
Akardit II
Magnesiumoxid
Graphit
Bariumnitrat Nitrocellulose
with 12.8% nitrogen ...
Nitroglycerin
Dibutyl phthalate
Satbilizers
Centralit I
Akardite II
Magnesium oxide
graphite
Barium nitrate
31,50%
12,70%
2,85%
0,85%
0,05%
0,05%
15,00%37.00%
31.50%
12.70%
2.85%
0.85%
0.05%
0.05%
15.00%
18,50%
7,74%
1,70%
0,50%
0,03%
0,03%
50,00%21.50%
18.50%
7.74%
1.70%
0.50%
0.03%
0.03%
50.00%
Die Analyse der Pulver ergab bei:The analysis of the powder showed:
Feuchtigkeit, % Humidity, %
Explosionswärme, cal/g ..Heat of explosion, cal / g ..
Typ AType a
0,1
8040.1
804
Typ BType B
0,2
8650.2
865
Von den Folien wurde eine Lage mit etwa einem Drittel Überlappung auf die Treibsätze gewickeltA layer of the foils was wound onto the propellant charges with about a third overlap
unter Verwendung eines Lösungsmittelgemisches aus Butylacetat und Lactonal, so daß die Stärke der nitrathaltigen Folie auf zwei Drittel der Fläche 0,5 mm und auf ein Drittel der Fläche 1 mm betrug.using a mixed solvent Butyl acetate and lactonal, so that the thickness of the nitrate film is two thirds of the area 0.5 mm and 1 mm on a third of the area.
Zum Vergleich wurden Stionbrenner ohne nitrathaltige Zwischenschicht geprüftFor comparison, Stion burners were made without nitrates Interlayer checked
Zur Rauchmessung wurde die Extinktion über die Brennzeit mittels einer Fotozelle gemessen. Von den drei Stirnbrennertypen wurden je zehn Körper abgebrannt und ausgewertet Das Ergebnis der Rauchgasraessung betrugTo measure smoke, the extinction was measured over the burning time using a photocell. Of the three types of forehead burners were burned down for ten bodies each and evaluated The result of the smoke gas measurement was
mtrathaltigemtrates
ZwischenBetween
schichtlayer
nitrathaltigsrnitrate
ZwischenschichtIntermediate layer
nitrathaltigernitrate-containing
ZwischenschichtIntermediate layer
Claims (5)
Family
ID=