DE19840397A1 - Artificial vitreous fibers - Google Patents
Artificial vitreous fibersInfo
- Publication number
- DE19840397A1 DE19840397A1 DE19840397A DE19840397A DE19840397A1 DE 19840397 A1 DE19840397 A1 DE 19840397A1 DE 19840397 A DE19840397 A DE 19840397A DE 19840397 A DE19840397 A DE 19840397A DE 19840397 A1 DE19840397 A1 DE 19840397A1
- Authority
- DE
- Germany
- Prior art keywords
- amount
- fibers
- product according
- composition
- composition comprises
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die vorliegende Erfindung betrifft künstliche glasartige Fasern (MMVF), welche eine Löslichkeit in biologischen Flüssigkeiten (Biolöslichkeit) besitzen, die als annehmbar erachtet wird, welche bei der Verwendung haltbar sind und gute Feuerfestigkeit aufweisen.The present invention relates to artificial vitreous fibers (MMVF) comprising a Have solubility in biological fluids (biosolubility) that are considered acceptable which are durable in use and good fire resistance respectively.
Es ist wohlbekannt, MMV-Fasern aus mineralischen Schmelzen herzustellen. Eine Kombination von Rohmaterialien wird in einem Ofen geschmolzen, um eine mineralische Schmelze mit der gewünschten chemischen Zusammensetzung bereitzustellen, und dann zu Fasern verarbeitet. Diese werden für verschiedene Zwecke, z. B. als Wärmeisolierung, Feuerschutz oder Schalldämmung verwendet.It is well known to make MMV fibers from mineral melts. A Combination of raw materials is melted in a furnace to a mineral melt with the desired chemical composition and then processed into fibers. These are for different Purposes, e.g. B. used as thermal insulation, fire protection or sound insulation.
Obwohl nicht wissenschaftlich nachgewiesen ist, daß mit der Herstellung und Verwendung von MMV-Fasern ein Gesundheitsrisiko verbunden ist, ist es aus kommerzieller Sicht wünschenswert, MMV-Fasern bereitzustellen, von denen behauptet werden kann, daß sie verbesserte biologische Sicherheit besitzen. Biologische Sicherheit wird gewöhnlich auf der Basis eines in vitro-Tests gemessen, der die Auflösungsgeschwindigkeit der Fasern in einer Flüssigkeit, die Lungenflüssigkeit simulieren soll, wie z. B. Gamble'scher Lösung bei etwa pH 7,5, bewertet.Although not scientifically proven that with the production and Using MMV fibers is a health risk associated with it From a commercial point of view, it is desirable to provide MMV fibers, of which It can be said that they have improved biological safety. Biological safety is usually measured on the basis of an in vitro test, the rate of dissolution of the fibers in a liquid, the Lung fluid should simulate such. B. Gamble's solution at about pH 7.5, rated.
Es wurden verschiedene Patentanmeldungen veröffentlicht, die Fasern beschreiben, von denen behauptet wird, daß sie eine verbesserte Auflösungsgeschwindigkeit in einem derartigen in vitro-Test ergeben. Diese umfassen EP-A-459897, WO92/09536, WO93/22251 und DE 44 43 022. In unseren Veröffentlichungen WO90/02713 und WO95/21799 werden ebenfalls biolösliche Fasern beschrieben.Several patent applications have been published which describe fibers, which is said to have an improved dissolution rate in such an in vitro test. These include EP-A-459897, WO92 / 09536, WO93 / 22251 and DE 44 43 022. In our publications WO90 / 02713 and WO95 / 21799 also describe biosoluble fibers.
Gemäß der Erfindung stellen wir ein Produkt bereit, welches künstliche glasartige
Fasern umfaßt, die aus einer Zusammensetzung gebildet sind, welche, bezogen auf
das Oxidgewicht,
According to the invention we provide a product comprising artificial vitreous fibers formed from a composition which, in relation to the oxide weight,
umfaßt. includes.
Es wurde gefunden, daß diese spezielle Kombination von Komponenten in den angegebenen Mengen, insbesondere den gewählten Bereichen für FeO, Al2O3 und Alkalimetall (Na2O + K2O), eine gute Kombination von Haltbarkeit bei der Verwendung und Biolöslichkeit ergibt. Es ist besonders überraschend, daß Biolöslichkeit mit den sehr geringen Konzentrationen an Alkalimetall erzielt werden kann, da diese bekanntermaßen Biolöslichkeit fördern. Außerdem können die Fasern aus leicht zugänglichen Ausgangsmaterialien hergestellt werden und die Fasern besitzen gute thermische Beständigkeit, Feuerfestigkeit und Isoliereigenschaften.It has been found that this particular combination of components in the amounts indicated, particularly the ranges chosen for FeO, Al 2 O 3 and alkali metal (Na 2 O + K 2 O), gives a good combination of durability in use and biosolubility. It is particularly surprising that biosolubility can be achieved with the very low levels of alkali metal, as these are known to promote biosolubility. In addition, the fibers can be made from readily available starting materials and the fibers have good thermal resistance, refractoriness and insulating properties.
In dieser Beschreibung sind die Mengen aller Elemente bezogen auf ihr Oxidgewicht angegeben. Der Einfachheit halber wird das gesamte Eisenoxid als FeO angegeben, obwohl ein Teil des Eisens als Fe2O3 vorliegen kann.In this description, the amounts of all elements are given in relation to their oxide weight. For the sake of simplicity, all of the iron oxide is reported as FeO, although some of the iron may be present as Fe 2 O 3 .
Die Menge an SiO2 beträgt 46 bis 58%. Gewöhnlich beträgt sie mindestens 50%, vorzugsweise mindestens 54%. In einigen Fällen kann es bevorzugt sein, daß SiO2 nicht mehr als 56% beträgt.The amount of SiO 2 is 46 to 58%. Usually it is at least 50%, preferably at least 54%. In some cases, it may be preferable that SiO 2 is not more than 56%.
Die Menge an Al2O3 beträgt 0,8 bis 3%. Gewöhnlich beträgt sie mindestens 0,9 oder mindestens 1%. In einigen Fällen kann sie mindestens 1,1% betragen. Im allgemeinen beträgt sie nicht mehr als 2,5%, vorzugsweise nicht mehr als 2%.The amount of Al 2 O 3 is 0.8 to 3%. Usually it is at least 0.9 or at least 1%. In some cases, it can be at least 1.1%. In general, it is not more than 2.5%, preferably not more than 2%.
Die Menge an FeO beträgt 5 bis 6,8%. Insbesondere beträgt sie oft mindestens 5, 5%. The amount of FeO is 5 to 6.8%. In particular, it is often at least 5, 5%.
Erfindungsgemäß ist es bevorzugt, daß das Eisen hauptsächlich im Eisen(II)- Zustand (statt im Eisen(III)-Zustand) vorliegen sollte. Vorzugsweise sind mindestens 70%, bevorzugter mindestens 80% des Eisens Eisen(II). Beispielsweise liegen in dem Produkt der Erfindung mindestens 90 oder 95 Gew.-% des Eisens als Eisen(II) vor.According to the invention it is preferred that the iron is mainly in the iron (II) - Condition (instead of in iron (III) state) should be present. Preferably, at least 70%, more preferably at least 80% of the iron iron (II). For example, lie in at least 90 or 95% by weight of the iron as iron (II) in the product of the invention in front.
Die Menge an TiO2 beträgt nicht mehr als 4%. Im allgemeinen beträgt sie mindestens 0,2%, vorzugsweise mindestens 0,5%. In einigen Zusammensetzungen kann sie mindestens 0,8 oder 1% betragen. Sie beträgt im allgemeinen nicht mehr als 2% und vorzugsweise nicht mehr als 1,5%.The amount of TiO 2 is not more than 4%. In general, it is at least 0.2%, preferably at least 0.5%. In some compositions it may be at least 0.8 or 1%. It is generally not more than 2%, and preferably not more than 1.5%.
Die Menge an CaO beträgt 0 bis 40%. Im allgemeinen beträgt sie mindestens 10%, vorzugsweise mindestens 15%. Im allgemeinen beträgt sie nicht mehr als 25% und vorzugsweise nicht mehr als 20%.The amount of CaO is 0 to 40%. In general, it is at least 10%, preferably at least 15%. In general, it is not more than 25% and preferably not more than 20%.
Die Menge an MgO beträgt 0 bis 30%. Im allgemeinen beträgt sie mindestens 8 oder 10%. Vorzugsweise beträgt sie nicht mehr als 20%, noch mehr bevorzugt nicht mehr als 18% und am meisten bevorzugt nicht mehr als 15%.The amount of MgO is 0 to 30%. In general, it is at least 8 or 10%. Preferably, it is not more than 20%, more preferably not more than 18%, and most preferably not more than 15%.
Die Gesamtmenge an Alkalimetall (Na2O + K2O) in der Erfindung ist sehr gering und liegt im Bereich von 0 bis 1%. Insbesondere beträgt sie nicht mehr als 0,8%, vorzugsweise nicht mehr als 0,6%. Im allgemeinen beträgt die Menge an Na2O + K2O mindestens 0,1%, oft mindestens 0,2%.The total amount of alkali metal (Na 2 O + K 2 O) in the invention is very small and is in the range of 0 to 1%. In particular, it is not more than 0.8%, preferably not more than 0.6%. In general, the amount of Na 2 O + K 2 O is at least 0.1%, often at least 0.2%.
In dem Produkt der Erfindung müssen die Fasern P2O5 enthalten. Es ist in einer Menge von 0,2 bis 10% vorhanden. Gewöhnlich beträgt die Menge nicht mehr als 5%, vorzugsweise nicht mehr als 4%. In einigen Fällen ist es bevorzugt, daß die Menge an P2O5 nicht mehr als 2% beträgt. In diesen Fällen ist es besonders überraschend, daß wir gute Biolöslichkeits-Eigenschaften erhalten, da in verschiedenen Veröffentlichungen angegeben wurde, daß der Einschluß einer großen Menge an P2O5 erforderlich ist, um gute Biolöslichkeit zu erzielen. Die Menge an P2O5 beträgt vorzugsweise mindestens 0,5%. In einigen Fällen kann die Menge an P2O5 0,2 bis 3% betragen.In the product of the invention, the fibers must contain P 2 O 5 . It is present in an amount of 0.2 to 10%. Usually, the amount is not more than 5%, preferably not more than 4%. In some cases, it is preferable that the amount of P 2 O 5 is not more than 2%. In these cases, it is particularly surprising that we obtain good biosolubility properties, as it has been stated in various publications that the inclusion of a large amount of P 2 O 5 is required to achieve good biosolubility. The amount of P 2 O 5 is preferably at least 0.5%. In some cases, the amount of P 2 O 5 may be 0.2 to 3%.
In der Erfindung beträgt das Verhältnis von P2O5/(Al2O3 + FeO) vorzugsweise nicht mehr als 0,45. Es ist ebenfalls überraschend, daß mit den beanspruchten Zusammensetzungen bei diesem Wert des Verhältnisses gute Biolöslichkeit erhalten wird, da in der Veröffentlichung WO92/09536 angegeben ist, daß das Verhältnis so hoch wie möglich (jedoch nicht über 6) sein sollte und es in den Beispielen der Veröffentlichung immer mindestens 0,9 beträgt. In der Erfindung kann das Verhältnis vorzugsweise unter 0,35 liegen.In the invention, the ratio of P 2 O 5 / (Al 2 O 3 + FeO) is preferably not more than 0.45. It is also surprising that good biosolubility is obtained with the claimed compositions at this value of the ratio, as it is stated in the publication WO92 / 09536 that the ratio should be as high as possible (but not above 6) and that in the examples the publication is always at least 0.9. In the invention, the ratio may preferably be below 0.35.
Es wurde auch festgestellt, daß es in der Erfindung bevorzugt ist, daß die Summe von CaO + MgO + Na2O + K2O + 2 P2O5 - 4 Al2O3 (jeweils bezogen auf Gew.-% an Oxid) mindestens 25 beträgt. Vorzugsweise beträgt sie mindestens 30, noch mehr bevorzugt mindestens 31, am meisten bevorzugt mindestens 33. Sie kann insbesondere mindestens 34 betragen. Es wurde festgestellt, daß sich die Löslichkeit der Fasern mit dem Anstieg des Wertes dieser Summe in der Regel erhöht.It has also been found that it is preferred in the invention that the sum of CaO + MgO + Na 2 O + K 2 O + 2 P 2 O 5 - 4 Al 2 O 3 (each based on wt .-% of oxide ) is at least 25. Preferably, it is at least 30, more preferably at least 31, most preferably at least 33. It may be at least 34 in particular. It has been found that the solubility of the fibers generally increases with the increase in the value of this sum.
Die Fasern in dem Produkt der Erfindung können verschiedene andere Elemente in einer Gesamtmenge von bis zu 10% enthalten. Vorzugsweise beträgt die Menge an anderen Elementen nicht mehr als 6%, noch mehr bevorzugt nicht mehr als 3% und insbesondere nicht mehr als 2%. Andere Elemente, die in den Fasern enthalten sein können, umfassen B2O3, BaO, ZrO2, MnO, ZnO, F, Cl, Cr2O3 und V2O5. Wenn B2O3 vorhanden ist, ist es gewöhnlich in einer Menge von nicht mehr als 5% vorhanden. Insbesondere ist die Menge an B2O3 vorzugsweise geringer als die Menge an P2O5.The fibers in the product of the invention may contain various other elements in a total amount of up to 10%. Preferably, the amount of other elements is not more than 6%, more preferably not more than 3% and especially not more than 2%. Other elements which may be included in the fibers include B 2 O 3 , BaO, ZrO 2 , MnO, ZnO, F, Cl, Cr 2 O 3 and V 2 O 5 . When B 2 O 3 is present, it is usually present in an amount of not more than 5%. In particular, the amount of B 2 O 3 is preferably less than the amount of P 2 O 5 .
Ein Vorteil der Zusammensetzung der Erfindung besteht darin, daß sie als mineralische Schmelze mit vorteilhafter Schmelzviskosität hergestellt werden kann. In dieser Beschreibung ist die Schmelzviskosität die Viskosität in Poise bei 1400°C, berechnet gemäß Bottinga und Weill, American Journal of Science, Band 272, Mai 1972, Seiten 455 bis 475. Da P2O5 in dieser Berechnung nicht eingeschlossen ist, wird das Vorhandensein von P2O5 berücksichtigt, indem man 1 Mol-% P2O5 mit 2 Mol-% SiO2 + 1 Mol-% CaO gleichsetzt. Labortests haben bewiesen, daß diese Näherung innerhalb der tatsächlichen chemischen Bereiche Gültigkeit hat.An advantage of the composition of the invention is that it can be prepared as a mineral melt of advantageous melt viscosity. In this specification, the melt viscosity is the viscosity in poise at 1400 ° C, calculated according to Bottinga and Weill, American Journal of Science, Vol. 272, May 1972, pages 455 to 475. Since P 2 O 5 is not included in this calculation the presence of P 2 O 5 is taken into account by equating 1 mol% P 2 O 5 with 2 mol% SiO 2 + 1 mol% CaO. Laboratory tests have proven that this approximation is valid within the actual chemical ranges.
Die Zusammensetzung der Erfindung stellt vorzugsweise eine Schmelze bereit, welche eine Viskosität bei 1400°C von mindestens 10 Poise, vorzugsweise mindestens 15 Poise und oft mindestens 17 Poise aufweist. Obwohl sie sogar 60 Poise betragen kann, beträgt sie im allgemeinen nicht mehr als 40 Poise und vorzugsweise nicht mehr als 30 Poise, noch mehr bevorzugt nicht mehr als 25 Poise und insbesondere nicht mehr als 20 Poise.The composition of the invention preferably provides a melt, which has a viscosity at 1400 ° C of at least 10 poise, preferably at least 15 poise and often at least 17 poise. Although she is even 60 Poise, it is generally not more than 40 poise and preferably not more than 30 poise, more preferably not more than 25 poise and in particular not more than 20 poise.
In dieser Beschreibung wird die Biolöslichkeit als Auflösungsgeschwindigkeit in Gamble'scher Lösung gemessen. Die Auflösungsgeschwindigkeit wird mit folgendem Durchflußverfahren bestimmt.In this specification, the biosolubility is expressed as dissolution rate in Gamble's solution measured. The dissolution rate becomes as follows Flow method determined.
Die verwendete modifizierte Gamble'sche Lösung hat die folgende
Zusammensetzung:
The modified Gamble's solution used has the following composition:
Die Faserdurchmesser-Verteilung wird für jede Probe durch Messen des Durchmessers von mindestens 200 einzelnen Fasern mit Hilfe des Linienschnittverfahrens und eines Rasterelektronenmikroskops oder eines Lichtmikroskops (100-fache Vergrößerung) bestimmt. Die abgelesenen Werte werden zur Berechnung der spezifischen Oberfläche der Faserproben verwendet, wobei die Dichte der Fasern berücksichtigt wird.The fiber diameter distribution is measured for each sample by measuring the Diameter of at least 200 individual fibers with the help of Line cutting method and a scanning electron microscope or a Light microscope (100x magnification) determined. The read values are used to calculate the specific surface area of fiber samples, taking into account the density of the fibers.
Auf der Basis der Auflösung von SiO2 (Netzwerk-Auflösung) wird die gelöste spezifische Dicke berechnet und die Auflösungsgeschwindigkeit (nm/Tag) ermittelt. Die Berechnungen basieren auf dem SiO2-Gehalt in den Fasern, der spezifischen Oberfläche und der gelösten Menge an Si.On the basis of the resolution of SiO 2 (network resolution), the dissolved specific thickness is calculated and the dissolution rate (nm / day) is determined. The calculations are based on the SiO 2 content in the fibers, the specific surface area and the dissolved amount of Si.
Die Auflösungsgeschwindigkeit mit Hilfe des Durchflußverfahrens wird wie folgt bestimmt. 10 mg Fasern werden in eine Durchflußzelle in einem Polycarbonat- Filterhalter (Durchmesser 40 mm) eingebracht. Ein 0,8 µm-Filter wird auf der Eintrittsseite (Oberseite) und ein 0,2 µm-Filter auf der Austrittsseite (Unterseite) angeordnet, um einen Verlust von Fasern während des Tests zu vermeiden. Beide Filter bestehen aus Cellulosenitrat. Die Durchflußrate der modifizierten Gamble'schen Lösung beträgt etwa 200 ml/Tag und wird mit Hilfe einer peristaltischeri Pumpe aufrechterhalten. Das Verhältnis des Flüssigkeitsdurchflusses zur Oberfläche der Fasern beträgt 1 bis 2 µm/Sekunde.The dissolution rate by the flow method becomes as follows certainly. 10 mg of fibers are placed in a flow cell in a polycarbonate Filter holder (diameter 40 mm) introduced. A 0.8 μm filter is placed on the Inlet side (top side) and a 0.2 μm filter on the outlet side (bottom side) arranged to prevent loss of fibers during the test. Both Filters are made of cellulose nitrate. The flow rate of the modified Gamble's solution is about 200 ml / day and is using a peristaltic pump maintained. The ratio of liquid flow to the surface of the fibers is 1 to 2 microns / second.
Der pH der Lösung wird durch Durchblubbern mit N2/CO2 (95/5) bei 7,6 ± 0,2 gehalten. Die gesamte Anordnung einschließlich Lagerbehältern wird bei 37 ± 0,7°C gehalten. Die abfließende Lösung wird einmal wöchentlich für eine Dauer von zwei Stunden gesammelt und auf Si und Ca analysiert. Die Analysen werden auf einem Perkin-Elmer Atomabsorptions-Spektralphotometer (AAS) durchgeführt. Weitere Einzelheiten sind in Environmental Health Perspectives, Band 102, Ergänzung 5, Oktober 1994, Seite 83 angegeben.The pH of the solution is maintained at 7.6 ± 0.2 by bubbling with N 2 / CO 2 (95/5). The entire assembly, including storage containers, is maintained at 37 ± 0.7 ° C. The effluent solution is collected once weekly for a period of two hours and analyzed for Si and Ca. The analyzes are carried out on a Perkin-Elmer Atomic Absorption Spectrophotometer (AAS). Further details are given in Environmental Health Perspectives, Volume 102, Supplement 5, October 1994, page 83.
Erfindungsgemäß weisen die Fasern vorzugsweise eine mit Hilfe dieses Tests gemessene Löslichkeit von mindestens 60 nm/Tag, noch mehr bevorzugt mindestens 80 oder 100 nm/Tag auf. Noch mehr bevorzugt beträgt die Löslichkeit mindestens 120 oder 130 nm/Tag. Sie kann sogar mindestens 150 oder 160 nm/Tag betragen.According to the invention, the fibers preferably have one with the aid of this test measured solubility of at least 60 nm / day, more preferably at least 80 or 100 nm / day. Even more preferred is the solubility at least 120 or 130 nm / day. It can even be at least 150 or 160 nm / day be.
Die Faserprodukte der Erfindung werden auf herkömmliche Weise hergestellt. Die Zusammensetzung wird gewöhnlich durch Mischen geeigneter Mengen natürlich vorkommender Rohmaterialien, wie z. B. Gesteins- und Sandmaterialien, und rückgewonnener Abfallstoffe gebildet. Diese beinhalten Konverterschlacke, andere Schlacken, Glas, Formsand, Kalkstein, Magnesit, Brucit, Talkum, Serpentinit, Pyroxenit, Apatit, Wollastonit, Quarzsand, Olivinsand, Eisenerz, Dolomit und MMVF- Abfall.The fiber products of the invention are made in a conventional manner. The Composition usually becomes natural by mixing suitable amounts occurring raw materials such. B. rock and sand materials, and recovered waste materials. These include converter slag, others Slag, glass, foundry sand, limestone, magnesite, brucite, talc, serpentinite, Pyroxenite, apatite, wollastonite, quartz sand, olivine sand, iron ore, dolomite and MMVF Waste.
Die Zusammensetzung kann auf herkömmliche Weise, z. B. durch Schmelzen der Rohmaterialien in einem Elektroofen oder in einem Kupolofen, in eine Schmelze umgewandelt werden. Die Schmelze wird vorzugsweise in einem Kupolofen hergestellt.The composition may be prepared in a conventional manner, e.g. B. by melting the Raw materials in an electric furnace or in a cupola, in a melt being transformed. The melt is preferably in a cupola manufactured.
Aus der Schmelze werden mit Hilfe herkömmlicher Verfahren, welche das Gießen der Schmelze in oder auf einen sich schnell drehenden Faserbildungsrotor und Veranlassen, daß die Schmelze vom Rand des Rotors in Form von Fasern abgeschleudert wird, umfassen, Fasern gebildet. Bei dem Rotor kann es sich um einen Rotor vom Spinnbecher-Typ oder einen Rotor mit einem festen Rand, der gewöhnlich um eine im wesentlichen horizontale Achse herum montiert ist, handeln. Rotoren dieses Typs können als Kaskadensystem angeordnet sein.The melt is melted by conventional methods, which include casting the melt in or on a fast spinning fiber forming rotor and Cause the melt from the edge of the rotor in the form of fibers is spun off, fibers formed. The rotor can be a rotor of the spinning cup type or a rotor with a fixed edge, the usually mounted around a substantially horizontal axis. Rotors of this type can be arranged as a cascade system.
Aus den Fasern können auf herkömmliche Weise MMVF-Produkte hergestellt werden, indem man die Fasern in Gegenwart eines Bindemittels, typischerweise in einer Menge von 0,5 bis 4%, oft etwa 1 bis 2 Gewichtsprozent des Produkts, schichtet. Es können herkömmliche MMVF-Bindemittel verwendet werden.The fibers can be used to produce MMVF products in a conventional manner be prepared by placing the fibers in the presence of a binder, typically in from 0.5 to 4%, often about 1 to 2% by weight of the product, coated. Conventional MMVF binders can be used.
Die Produkte können für jeden der Zwecke, für die MMVF-Produkte bekannt sind, verwendet werden. Diese umfassen Wärmeisolierung, Feuerisolierung und -schutz, Geräuschdämpfung und -regulierung, Wachstumsmedien für den Gartenbau oder als freie Fasern zur Verstärkung von Zement, Kunststoffen oder anderen Produkten, oder als Füllstoff. Sie können in jeder der herkömmlichen Formen, wie z. B. Matten oder Platten, Bögen, Rohrabschnitten oder anderen Formkörpern, bereitgestellt werden oder können zu einem granulären Produkt zerkleinert werden.The products may be used for any of the purposes for which MMVF products are known. be used. These include heat insulation, fire insulation and protection, Noise damping and regulation, growth media for horticulture or as free fibers for reinforcing cement, plastics or other products, or as a filler. You can in any of the conventional forms, such as. B. mats or plates, sheets, pipe sections or other shaped bodies be or can be crushed to a granular product.
Die Erfindung wird nun mit Bezug auf die folgenden Beispiele erläutert.The invention will now be elucidated with reference to the following examples.
In jedem der Beispiele unten werden Rohmaterialien geschmolzen, um eine Schmelze zu bilden, welche die unten in Tabelle 1 angegebene Zusammensetzung hat. Aus der Schmelze werden mit Hilfe eines Kaskadenrotorsystems Fasern gebildet. Die Fasern werden als im Luftstrom aufgebrachte Bahn gesammelt und behandelt, um ein Produkt zu bilden. Die Schmelzviskosität bei 1400°C ist unten für jede Zusammensetzung angegeben. Für jede Faserzusammensetzung ist auch die Löslichkeit unter dem oben erörterten Test angegeben. In each of the examples below, raw materials are melted to form a To form melt having the composition given in Table 1 below Has. From the melt fibers are using a cascade rotor system educated. The fibers are collected as an air-laid web and treated to form a product. The melt viscosity at 1400 ° C is below for each composition indicated. For each fiber composition is also the Solubility indicated under the test discussed above.
Claims (12)